Fused deposition modeling (FDM) is widely applied in various fields due to its affordability and ease of use. However, it faces challenges such as achieving high surface quality, precise dimensional tolerance and overcoming anisotropic mechanical properties. This paper analyzes and compare the machinability of 3D printed PLA, PETG and carbon fiber reinforced PETG focusing on surface roughness and burr formation. A design of experiments (DoE) with a full factorial design was used, considering three factors: rotation speed, feed rate and depth of cut. Each factor had different levels: rotational speed at 3000, 5500 and 8000 rpm; feed rate at 400, 600 and 800 mm/min; and depth of cut at 0.2, 0.4, 0.6, and 0.8 mm. Machinability was evaluated by roughness and burr height using a profilometer for all the materials under the same milling conditions. To evaluate the statistical significance of the influence of various processing parameters on surface roughness and burr formation in 3D printed components made of three different materials PLA, PETG and carbon fiber reinforced PETG, an analysis of variance (ANOVA) test was conducted. This analysis investigated whether variations in rotational speed, feed rate and depth of cut resulted in measurable and significant differences in machinability results. Results showed that milling parameters significantly affect roughness and burr formation, with optimal conditions for minimizing any misalignment highlighting the trade-offs in parameter selection. These results provide insights into the post-processing of FDM-printed materials with milling, indicating the need for a balanced approach to parameter selection based on application-specific requirements.

The addition of biocarriers can improve the biological processes appearing in a bioreactor since their surface allows the immobilization, attachment, protection, and growth of microorganisms. In addition, the development of a biofilm layer allows the colonization of microorganisms in the biocarriers. The structure, composition, and roughness of the biocarriers' surface are crucial factors that affect the development of the biofilm. In the current work, the aluminosilicate zeolites 13X and ZSM-5 were examined as the main building components of the biocarrier scaffolds, using bentonite, montmorillonite, and halloysite nanotubes as inorganic binders in various combinations. 3D printing was utilized to form pastes into monoliths that underwent heat treatment. The 3d-printed biocarriers were subjected to a mechanical analysis, including density, compression, and nanoindentation tests. Furthermore, the 3d-printed biocarriers were morphologically and structurally characterized using nitrogen adsorption at 77 K (LN2), scanning electron microscopy (SEM), and X-ray diffraction (XRD). The stress-strain response of the materials being studied was obtained through nanoindentation tests combined with finite element analysis (FEA). These tests were also utilized to simulate the lattice geometries under compression loading conditions to investigate their deformation and stress distribution in relation to experimental compression testing. The results indicated that the 3d-printed biocarrier 13X/halloysite nanotubes was endowed with high specific surface area and extended mesoporous structure. Due to these assets, its bulk density was one of the lowest observed amongst the biocarriers derived from the various combinations of materials. The biocarriers based on the 13X zeolite exhibited the highest mechanical stability and appropriate morphological features. The 13X/halloysite nanotubes scaffold exhibits a moderate hardness value compared to the rest, while it presents the highest value of modulus of elasticity. In conclusion, Aluminosilicate zeolites and their combination with clays and inorganic nanotubes afford 3d-printed biocarriers of various textural and structural properties, which can be utilized to improve biological processes.

Printed oral splints are a therapeutic alternative in the treatment of functional disorders. Their mechanical properties are crucial to their clinical success and their performance can vary depending on cleaning, post-polymerization, or build orientation. This in vitro study aimed to compare the biaxial flexural strength of the chosen materials depending on the aforementioned parameters. 720 discs (n = 15 per group, 16 mm x 2 mm) were printed from splint materials. Printing was performed under 90°, 45°, or 0° orientation to the building platform with supporting structures. Specimens were either automatically or manually cleaned with isopropanol. Post-polymerization was performed with LED- or Xenon-light. Biaxial flexural strength (BFS) was determined with a piston-on-3-ball test after 24 hours or 60 days water storage (37°C). Test specimens were preloaded with 0.5 N and the load was applied by a piston of 1.6 mm in diameter at 1 mm/min crosshead speed. Statistics were performed by using descriptive statistics, ANOVA, and Levene-tests. Mean BFS after 24 hours of storage varied between 79 MPa and 157 MPa. After 60 hours the BFS significantly decreased and revealed values ranging from 72-127 MPa (mean24 113 MPa, mean60 97 MPa; p<0.001). No significant differences could be determined between the materials (p=0.103) or between the different cleaning procedures (p=0.321). Post-polymerization yielded higher means with LED- (P1: 115 MPa) than with Xenon-light (P2: 95 MPa; p<0.001). Regarding position, the mean values ranged from 101 MPa for 0°, 102 MPa for 45°, and 115 MPa for 90°, which was significantly different (p<0.001). Build orientation of 90° and post-polymerization with LED-light provided significantly higher biaxial flexural strength and should be used to guarantee optimal strength of splint materials. Aging decreased the biaxial flexural strength of the tested specimens.

This study addresses the challenge of treating skin cancer effectively, especially in visible areas like the face, where traditional methods may be undesirable. Current options, including surgery and radiation therapy, have limitations such as complexity, expense, and imprecise dose delivery. The proposed solution involves additively manufacturing personalized patches using diagnostic imaging data, offering a targeted and controlled dose of beta-emitting isotopes like Y-90. The patches, tailored to the tumor's shape and depth, aim to minimize damage to healthy tissues and structures. Through 3D printing technology we demonstrated the feasibility of creating individualized applicators filled with radioisotopes, that have the potential to deliver therapeutic doses while ensuring patient comfort and affordability. This innovative approach, based on radiation delivery simulations, offers a promising future alternative to conventional radiation therapy methods. Clinical trials are required to validate its efficacy and safety, but the potential for reduced radiation exposure and enhanced treatment precision positions this personalized and targeted therapy as a valuable advancement in skin cancer treatment.

In recent years, Additive Manufacturing (AM), commonly referred to as 3D printing, has garnered the attention of the scientific community due to its capacity to transform ordinary and traditional items into customized materials at an affordable cost, through various AM processes. Antimicrobial/antibiofilm 3D printed materials are one of the most trending research topics, owing to the growing concerns over the emergence of complex microbial structures called "biofilms" on various surfaces. The review provides an overview of the evolution of additive manufacturing (AM) technologies and their various derivatives, along with a brief description of their materials and applications. It also introduces how biofilms can represent an advantageous lifestyle for microbial populations. The primary objective of this research was to conduct a systematic review on the development of planctonic or biofilm forms of microorganisms on 3D printed materials. The article summarizes commonly studied microorganisms on these materials and presents their 3D printing process, materials, as well as the fields covered by each of the analyzed papers. To the best of our knowledge, this is the first all-inclusive systematic review that amalgamated research conducted in diverse fields to assess the development of biofilms on surfaces produced through three-dimensional printing. Most notably, this review presents a comprehensive account of sustainable approaches for producing antimicrobial materials through 3D printing. Additionally, we assess their advancements in various fields such as medicine, environment, agri-food, and other relevant sectors. The findings of our literature review can be used to recommend appropriate microorganisms, 3D printing materials, and technologies for academic and industrial research purposes focusing on the development of microbial biofilms on 3D printed surfaces. Furthermore, it highlights the potential of environmentally-friendly modified AM technologies to combat biofilms in clinical and non-clinical areas. Our goal with this review is to help readers gain a better understanding of fundamental concepts, inspire new researchers, and provide valuable insights for future empirical studies focused on eradicating biofilms from 3D printed materials.

Objective: The aim of this in vitro study was to evaluate the accuracy of resin-based fixed dental restorations, namely veneers, single crowns, and four-unit fixed partial dental prosthesis (FPDs) using two different 3D printers and polymer-based materials. Materials and Methods: A standard maxillary polyurethane jaw model containing prepared teeth was scanned using an intraoral scanner. The generated STL data were used to design the restorations virtually using CAD software. Two 3D printers were utilized for the provisional digital light processing and stereolithography for the castable resin patterns. Each printer produced 10 specimens of each type of restoration, for a total of 80 restorations. The 3d-printed restorations were then 3D scanned using the same intraoral scanner and evaluated for external and internal dimensional accuracy in terms of trueness and precision. A one-way ANOVA and Two-sample T-Test were implemented to compute the precision (variability between groups) and trueness (with the designed CAD model). A level of statistical significance of p-Value

The movement of liquid droplets on the energy gradient surface has attracted extensive attention. Inspired by biological features in nature, such as the periodic spindle-shaped nodes in spider silks and conical-like barbs of cacti, the structure-property-function relationship of multifunctional gradient surfaces. In this study, a series of specific patterns are fabricated by 3D printing technology, followed by modification via the atmospheric pressure plasma treatment and liquid phase chemical deposition, resulting in enhancing the ability of water droplets of 5μL to travel 18.47mm on a horizontal plane and 22.75mm against gravity up to 20° tilting angle. Additionally, analysis techniques have been employed including contact angle analyzer, ESCA and laser confocal microscope to evaluate the sample performance. This work could further be applied to many applications related to microfluidic devices, drug delivery and water/fog collection.

The work aims to develop an electromagnetic shielding measurement methodology and design an electromagnetic shielding effectiveness test setup for thin sheet material testing. In brief, multiple shielding effectiveness standards are described and analyzed in the thin sheet material testing framework. Two types of the developed shielding effectiveness test probe in high and low-frequency ranges are validated comprehensively. Extensive descriptions and data of developed testing methodology are also reported.

In this paper, we aim to present real implementation cases where non-visible elements of environmental impact assessments (EIA), wind flow, are visualized using a 3D digital twin technology. The conventional EIA process serves as a crucial tool in the evaluation of potential environmental impacts prior to the initiation of development projects. This evaluation helps to establish a legal and institutional framework that seeks to minimize the adverse effects on the environment. However, traditional EIA methods present challenges, particularly for non-experts, in comprehending the results of assessments involving non-visible environmental factors such as noise, air quality, and wind flow. These elements are often represented in static images or numerical tables, limiting accurate understanding and engagement. Our proposed method, termed Digital Twin based EIA, addresses these limitations by leveraging digital twin technology. This advanced methodology allows for the visualization of non-visible environmental elements in a spatio-temporal dimension, providing a more interactive and comprehensive user interface/experience for both citizens and stakeholders. In this context, we present a unique case study that focuses on visualizing wind flow using this technology. This paper serves as an example of how digital twin platforms can enhance traditional EIA processes, offering a more immersive and informative experience. The evolution of EIA into the digital realm signifies an important step forward in fostering public understanding and engagement in environmental protection efforts.

The assortment of low-cost 3D printers for “in-practice” use, e.g., for clear aligner therapies, is ever increasing. To address concerns about the accuracy of orthodontic models produced on such printers when cost efficient modes of 3D printing are employed, this study examined the effect of print model body type and print angulation on accuracy. Six printing-configuration groups were included: 2 model types (solid or hollow shell) combined with 3 print angles (0°, 70°, or 90°) with 10 models/group; all models were printed with 100-µm layer thickness using a digital light processing-based 3-dimensional printer. Eleven selected structures and distances were measured on the printed models with a digital microscope and compared to the same measures on a digitized master model. The clinically-acceptability range was set at ±0.25 mm difference from the master model for single tooth measurements (intra-tooth) and ±0.5 mm for cross-arch measurements (inter-tooth). For individual measurements across all models, 98% fell within clinical acceptability. For mean measurements within each model group, only canine height for the shell-0° model had a mean difference (0.26 mm ± 0.03) outside the clinically acceptable range for intra-tooth measurements. Standard deviations for all intra-tooth measurements were within 0.07 mm. While none of the mean inter-tooth measurements exceeded the acceptability range, the standard deviations were larger (0.04 to 0.30 mm). Accuracy of orthodontic models for clear aligner therapies was not impacted beyond the clinically acceptable range when altering model body type and print angulation to improve efficiency of 3D printing. These findings suggest greater flexibility of the practitioner to alter print settings to address time and cost efficiency in various clinical scenarios and still maintain clinically acceptable model accuracy.

In this paper, carbon nanotubes modified screen-printed electrode (CNTs/SPE) was prepared and the CNTs/SPE was employed for the electrochemical determination of antioxidant substance Chlorogenic acids (CGAs). A pair of well-defined redox peak of CGA was observed at the CNTs/SPE in 0.10 mol∙L^-1 acetic acid-sodium acetate buffer (pH 6.2) and electrode process is adsorption-controlled. Cyclic voltammetry (CV) and differential pulse voltammetry (DPV) method for the determination of CGA were proposed based on the CNTs/SPE. Under the optimal conditions, the proposed method exhibited linear ranges from 4.73×10^-7 to 4.45×10^-5 mol∙L^-1, the linear regression equation was Ipa(µA) = 4.1993 C (mol∙L^-1)+1.1039 (r = 0.9976) and the detection limit for CGA could reach 3.25×10^-6 mol∙L^-1. The recovery of matrine was 94.74~106.65% (RSD = 2.92%) in coffe beans. The proposed method is quick, sensitive, reliable, and can be used for the determination of CGA.

AbstractWhile the technology is relatively new, low cost 3D printing has impacted many aspects of human life. 3D printers are being used as manufacturing tools for a wide variety of devices in a spectrum of applications ranging from diagnosis to implants to external prostheses. The ease of use and availability of 3D design software and low cost has made 3D printing an accessible manufacturing and fabrication tool in many research laboratories. 3D printers can print materials with varying density, optical character, strength and chemical properties providing platforms for a huge number of strategies that can be chosen for user’s needs. In this review, we focus on applications in biomedical diagnostics and how this revolutionary technique is facilitating development of low cost, sensitive and often geometrically complex tools. 3D printing in fabrication of microfluidics, supporting equipment, optical and electronic components of diagnostic devices is presented. Emerging diagnostic 3D bioprinting as a tool to incorporate living cells or biomaterials into 3D printing is also discussed.

3D printing is a non-traditional additive manufacturing process. It is different from the traditional subtractive manufacturing process. It offers exceptional rapid prototyping capabilities and results that traditional subtractive manufacturing methods cannot attain, especially in applications involving curved or intricately shaped components. Despite its advantages, metal 3D printing will face porosity, warpage, and surface roughness issues. These issues will affect the future practical application of the parts indirectly, for example, the structural strength and the parts assembly ca-pability. Therefore, this study compares the qualities of the warpage, weight, and surface rough-ness after milling and grinding processes under the same materials (316L stainless steel) between general rolled steel and 3D additive steel. Experimental results show that 3D printing parts are approximately 13% to 14% lighter than the general rolled steel. The surface roughness performance of 3D printing steel is better than general rolled steel under the same material after milling or grinding processing. The hardness of the 3D printing steel is better than that of the gen-eral rolled steel. The research verifies that 3D additive manufacturing can use surface processing to optimize surface performance and achieve the functions of lightness and hardness.

Sustainable manufacturing practices are becoming increasingly necessary due to the growing concerns regarding climate change and resource scarcity. Consequently, material recycling technologies have gradually become preferred over conventional processes. This study aimed to recycle waste polylactic acid (PLA) from household-disposed cups and lids to create 3D-printed parts and promote sustainable manufacturing practices. To achieve this, the current study utilised virgin and post-consumer PLA (sourced from household waste) blends. The PC-PLA wastes were shredded and sorted by size with the aid of a washing step, resulting in a filament with a 1.70 ± 0.5 mm diameter without fragmentation or dissolution. A 50:50 wt.% blend of virgin PLA (vPLA) and PC-PLA was selected as the standard recycling percentage based on previous research and resource conservation goals. The study investigated the impact of three 3D printing parameters (layer height (LH), infill density (I), and nozzle temperature (NT))on the quality of 3D-printed parts using a three-level L9 Taguchi orthogonal array. The findings revealed that blending PC-PLA with vPLA led to significant improvements in the tensile, flexural, and impact strengths by 18.40%, 8%, and 9.15%, respectively, compared to those of recycled PLA. This conclusion was supported by the investigation of the fracture surface area, which revealed fractographic features associated with printing parameters, such as plastic deformation and interfilament debonding. An ANOVA analysis revealed a positive influence of larger layer height and high nozzle temperature on the mechanical properties. Subsequently, the optimal printing parameters (LH: 0.3 mm, I: 100%, and NT: 215 °C) were determined using the S/N ratio, and a confirmation test using the optimum printing parameters exhibited a strong correlation with statistically predicted outcomes. Finally, the study used optimum printing parameters to fabricate 100% post-consumer recycled PLA 3D printed parts, demonstrating their potential for low-strength applications. Based on these findings, it can be concluded that virgin and post-consumer recycled PLA blended filament for fabricating 3D printed components is an effective way to support plastic recycling in the context of a circular economy.

Dielectric elastomers, such as thermoplastic polyurethanes (TPU), are widely used as dielectric layer, emulation layer and substrate of flexible and stretchable devices. To construct capacitors and actuators that work stably upon deformation, it has become an urgent need to investigate the evolution of dielectricity under stress and strain. However, the lack of effective methods for estimating the dielectric constant of elastomers under strain poses a big challenge. This article reports a device for in-situ measuring the dielectric constant of TPU under strain. It is found that upon stretching TPU to a strain of 400%, its dielectric constant decreases from 8.47 to 2.94. In addition, combined Fourier-transform infrared spectroscopy, X-ray scattering technique, and atomic force microscopy have been utilized to characterize the evolution of microstructure under strain. The investigation under tensile strain reveals that a decreased density and average size of polarized hard domains, along with a tendency of the molecular chains to align in parallel with the tensile stress. The evolution of the microstructures results in a reduction of the dielectric constant parallel to the electric field in TPU. Our work provides valuable experimental reference for improving the stability of flexible sensors and actuators based on dielectric elastomers.

With continuous increase in integration of the semiconductor devices, the requirements on size accuracy and surface quality of the etched lead frame are higher. The etchant is a key factor on etching process and etched surface quality, while effects of the difference in etchants on microscopic etched surface morphology of the Cu alloy have not been directly studied. In this study, the aqua regia, acidic FeCl3 and CuCl2 solutions were used as etchants, and the CuCrSn alloy specimens with different microstructure were etched and characterized. The results show that the etching rate in aqua regia is high, and the grain orientation, grain boundary (GB) and dislocation have significant influence on the local etching rate. The preferential etching of some atomic planes forms steps between grains with different orientations, and the preferential etching around the GB and dislocation group forms grooves, resulting in high surface roughness. For etching of the FeCl3 and CuCl2 etchants, the steps and grooves become blurred, and almost invisible on the surface etched by the CuCl2 etchant, thus the surface roughness is much lower. The CuCrSn alloy surface etched by the aqua regia is clean, with little Cr-rich particles, while high density Cr-rich particles are remained on the surfaces etched with the FeCl3 and CuCl2 etchants. For the same kind of etchant, the ion concentration can affect the etching mechanism and etching surface morphology.

A novel nano-laminated GdB2C2 material was successfully synthesized using GdH2, B4C, and C via an in-situ solid state reaction approach for the first time. The formation mechanism of GdB2C2 was revealed based on the microstructure and phase evolution investigation. A purity of 96.4 wt. % GdB2C2 was obtained at a low temperature of 1500 ℃, while a near full pure GdB2C2 can be obtained at a temperature over 1700 ℃. The as-obtained GdB2C2 presented excellent thermal stability at high temperature of 2100 ℃ in Ar atmosphere due to the stable frame work formed by the high covalent four-members and eight-members B-C rings in GdB2C2. The minimum reflection loss value (RLmin) of -47.01 dB with an effective absorption bandwidth (EAB) of 1.76 GHz at a thickness of 3.44 mm was obtained for the GdB2C2 synthesized at 1500 ℃. The possible EMWA mechanism could be ascribed to the nano-laminated structure and appropriate electrical conductivity, which facilitated to the good impedance matching, remarkable conduction loss, interfacial polarization as well as multiple interface reflection and scattering. The as-obtained GdB2C2, with excellent EMWA performance as well as remarkable ultra-high temperature thermal stability, could be a promising candidate for the EMWA materials applications in extreme ultra-high temperatures.

This paper investigates the influence of sample size and layer height on the elastic modulus of samples 3D printed by fused filament fabrication (FFF). Cubic samples of different sizes from either a stiff thermoplastic polymer (polycarbonate (PC)) or a soft polymer (thermoplastic polyurethane (TPU)) were printed at three different layer heights: 0.1 mm, 0.2 mm, and 0.4 mm. The samples were imaged using micro-computed tomography to visualize porosity and tested under compression. The results indicate that the elastic modulus of TPU varied with sample size, demonstrating size effects due to high porosity. In contrast, PC samples had a low void volume fraction and did not demonstrate statistically significant size effects on the elastic modulus. The variations in elastic modulus due to layer height were statistically significant for both materials. The highest elastic modulus was observed at 0.2 mm layer height for both materials across different sample sizes, which can be attributed to low void volume fractions. The study develops process-structure-property relations for PC and TPU samples manufactured by FFF. It provides new insights into the design guidelines for FFF based on the size effects. The results indicate that variations in mechanical properties due to size effects must be considered during the design stage for TPU to accurately predict the material’s behavior. Additionally, the locations of the printed parts that are subjected to higher loads should be printed closer to the heated print bed due to the lower void volume fraction observed in the section of the samples printed adjacent to the heated print bed.

The capacity of 3D printing (3DP) technologies to initiate speedy polymerization of solvent free resins accounts for their utility in the manufacturing of medical devices. Nonetheless, independent biological evaluation of 3D printed materials is recommended due to the unique parameters of the manufacturing process, which can influence their physical, chemical, and biological properties. In this study, E-Shell 450 material indicated for 3DP of hearing aid shells and inner ear devices was examined for biological safety using zebrafish bioassays adapted to OECD fish embryo test. In addition, the proprietary material was characterized for composition using headspace gas-chromatography mass spectrometry (GC-MS). To initiate test, newly fertilized zebrafish eggs were cultured on non-treated and ethanol-treated materials in glass petri dishes with ultrapure water, incubated at 28.5°C and assessed for developmental endpoints of toxicity at 24h interval until 96h. Data confirmed non-treated material was extremely toxic in bioassays within 24h whereas ethanol-treated material showed a relative lower toxicity possibly due to ethanoic-aqueous interactions as observed by GC-MS. With the current influx of 3D printing materials, users are urged to exercise caution. Operators must also take cognizance of the potential toxicity of the chemicals used in 3DP and implement safety measures to limit their exposure.

In this paper, a novel microwave catalyst Ni@SiC/CNFs (NSC), C/Ni (NC), and C/SiC (SC) were successfully synthesized by electrostatic spinning method, and proved to degrade methylene blue with high efficiency under microwave irradiation. The results imply that the catalyst Ni@SiC/CNFs with double shell structure gave a 99.99 % removal rate in 90 s for the degradation of methylene blue under microwave irradiation, outperformed the C/Ni and C/SiC and most other reported catalysts in similar studies. On the one hand, the possible mechanism of the methylene blue degradation should be ascribed to that double shell structure increases the polarization source of the material, resulting in excellent microwave absorption properties; and on the other, the in-situ generation of active species OH• and O2 - under microwave radiation and the synergistic coupling effect of metal plasma greatly improved the degradation efficiency of methylene blue. The findings of this study could provide a valuable reference for the green degradation of industrial dye wastewater and its sustainable development process.

Diseases in articular cartilages have affected millions of people globally. Although the biochemical and cellular composition of articular cartilages is relatively simple, there is the limitation in self-repair ability of cartilage. Therefore, developing the strategies for cartilage repair is very important. Here, we reported a new manufacturing process of water-based polyurethane based photosensitive materials with hyaluronic acid and applied the materials for 3D printed customized cartilage scaffolds. The scaffold has high cytocompatibility and is one that closely mimics the mechanical properties of articular cartilages. It is suitable for culturing human Wharton's jelly mesenchymal stem cells (hWJMSCs) and the cells showed an excellent chondrogenic differentiation capacity. We consider that the 3D printing hybrid scaffolds may have potential in customized tissue engineering and facilitate the development of cartilage tissue engineering.

The present work investigates primarily the morphology evolution of the body-centered-cubic (BCC)/B2 phases in AlxNiCoFeCr high-entropy alloys (HEAs) with increasing Al content, which has been neglected so far. There exist two types of microscopic morphologies of BCC and B2 phases in this HEA series: one is the weave-like morphology induced by the spinodal decomposition, and the other is the microstructure of a spherical disordered BCC precipitation on the ordered B2 matrix that appears in HEAs with a much higher Al content. The shape of coherent precipitates is found to be closely related to the lattice misfit between BCC and B2 phases, which is sensitive to Al. The mechanical properties, including the compressive yielding strength and microhardness of the AlxNiCoFeCr HEAs, are also discussed in light of the concept of the valence electron concentration (VEC).

We introduce optically clear and resilient free-form micro-optical of pure (non-photosensitized) organic-inorganic SZ2080 material made by femtosecond 3D laser lithography (3DLL). This is advantageous for rapid printing of 3D micro-/nanooptics, including their integration directly onto optical fibers. A systematic study on the fabrication peculiarities and quality of resultant structures is performed. Comparison of microlenses’ resiliency to CW and femtosecond pulsed exposure is determined. Experimental results prove that pure SZ2080 is ∼3 fold more resistant to high irradiance as compared with a standard photo-sensitized material and can sustain up to 1.91 GW/cm² intensity. 3DLL is a promising manufacturing approach for high-intensity micro-optics for emerging fields in astro-photonics and atto-second pulse generation. Additionally, pyrolysis is employed to shrink structures up to 40% by removing organic SZ2080 constituents. This opens a promising route towards downscaling photonic lattices and creation of mechanically robust glass-ceramic structures.

A low-cost bio-mass-derived carbon substrate has been employed to synthesize MoS₂@carbon composites through a hydrothermal method. Carbon fibers derived from natural cotton provide a three-dimensional and open framework for the uniform growth of MoS₂ nanosheets, thus constructing hierarchically coaxial architecture. The unique structure could synergistically benefit fast Li-ion and electron transport from the conductive carbon scaffold and porous MoS₂ nanostructures. As a result, the MoS₂@carbon composites, when served as anodes for Li-ion batteries, exhibit a high reversible specific capacity of 820 mAh g^-1, high-rate capability (457 mAh g^-1 at 2 A g^-1), and excellent cycling stability. The superior electrochemical performance makes the MoS₂@carbon composites to be low-cost and promising anode materials for Li-ion batteries.

Soft magnetic composites cores were produced by Spark Plasma Sintering (SPS) from Ni3Fe@ZnFe2O4 and NiFeMo@ZnFe2O4 pseudo-core-shell powders. In the Fe-Ni alloys@ZnFe2O4 pseudo-core-shell composite powders, the core is a large nanocrystalline Permalloy or Supermalloy particle obtained by mechanical alloying, and the shell is a pseudo continuously layer of Zn ferrite particles. The pseudo-core-shell powders have been compacted by SPS at temperatures between 500-700 ºC, with a holding time of 0 minutes. Several techniques were used for the characterisation of the powders and sintered compacts: X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy, magnetic hysteresis measurements (DC and AC) and electrical resistivity. The electrical resistivity is stabilised at values of about 7·10-3 Ω·m for sintering temperatures between 600-700 °C and this value is 3 orders of magnitude higher than the electrical resistivity of sintered Fe compacts. The best relative initial permeability was obtained for the Supermalloy/ZnFe2O4 composite compacts sintered at 600 ºC, which decreases linearly for the entire frequency range studied, from around 95 to 50. Up a frequency of 2,000 Hz the power losses are lower than 1.5 W/kg. At the frequency of 10 kHz, the power losses are larger, but they remain at a low level. In the case of Supermalloy/ZnFe2O4 composite compact SPS-ed at 700 °C, the specific power losses are even lower than 5 W/kg. The power losses decomposition proved that intra-particles losses give the main part of the losses.

An eight-sided prism sample, obtained from a hot-rolled AZ31 magnesium alloy sheet, was compressed at room temperature along the transverse direction to investigate the influence of local strain on twinning behavior using electron backscatter diffraction (EBSD) measurements. The octagonal surface of the sample was divided into distinct regions based on hardness distribution and metallographic observations. The EBSD maps of different areas show significant variations, suggesting that these areas experienced different local strain conditions. The EBSD measurements provided detailed data from three distinct regions, with the strain state known in two regions and uncertain in the third. The combined analysis of the Schmid factor (SF) and the strain compatibility factor (m') was employed to study twin variant selection. The comparison of twinning behavior in different regions showed that the strain compatibility factor offered a more comprehensive explanation for the observed twinning pattern in the region with local shear strain.

The integration of three-dimensional (3D) printed resin denture teeth represents a significant ad-vancement in digital dentistry. This study aimed to assess their ability to withstand chipping and indirect tensile fractures, comparing them with conventionally manufactured resin denture teeth. Four groups, each comprising 30 specimens, were examined: Group 1 featured 3D printed denture teeth (NextDent, 3D Systems, Soesterberg, The Netherlands), while the others included commer-cially obtained Ivostar Shade, SpofaDent Plus, and Major Super Lux teeth. Stereolithography 3D printing was utilized to produce methacrylate-based photopolymerized resin teeth models for Group 1, while the remaining groups were commercially sourced. Chipping and indirect tensile fracture tests were performed at a speed of 1 mm/min until fracture occurred. Statistical analysis was conducted using one-way analysis of variance (ANOVA) with Tukey's honestly significant difference multiple comparisons test (p < 0.05). Results indicated that 3D-printed teeth exhibited higher indirect tensile fracture resistance than Major Super Lux and Ivostar Shade but lower than SpofaDent Plus. Additionally, in the chipping test, buccal chipping occurred in 3D-printed resin teeth without distortion. In the indirect tensile test, the fracture line emerged near the loading point, extending cervically from the inner incline of both cusps. Overall, denture teeth produced via 3D printing with printable resin materials demonstrated sufficient fracture resistance, making them suitable for prosthetic applications.

This papers objective is to describe a method of in-office 3D designing and 3D printing of a tooth-borne molar distalizer and create a library to easily reproduce the needed distalizers in a private orthodontic clinic. Research objectives were to design and 3D print molar distalizers, clinically use in orthodontic treatment settings, assess the strength and frequency of debonding and or breakage. The print resin used was Dental LT Clear V2 (RS-F2-DLCL-02) from formlabs. The 3D printer used was a Formlabs 3B+printer. 16 patients were treated with these 3D printed distalizers. Patients selected were between 11 Years and 49 Years old, Class II occlusion with no skeletal Class II values. The skeletal cephalometric values of the six patients were within the range of SNA = 81± 3º , SNB = 78 ± 3º , ANB = 3 ± 2º. The mean duration of the 3D printed appliance was 14.58 ± 4.31 weeks. The aim reached, was to position molars and canines in a dental Class I position. The combined failure rate was 0.94. A library of distalizers has been made of sizes between 16mm and 29mm, they are easy to print and easy to use in office.

Fatigue analysis plays a vital role in determining the structural integrity and life of a dental implant. With the use of such implants on the rise, there is a corresponding increase in the number of implant failures. As such, the aim of this research paper is to investigate the life of 3D-printed dental implants. The dental implants considered in this study were 3D printed according to the direct metal laser sintering (DMLS) method. Additionally, a finite element model was developed to study their performance, while fatigue life was predicted using Fe-Safe software®. The model was validated experimentally by performing fatigue tests. The life of the dental implants was analysed based on Normal strain and the Brown-Miller with Morrow mean correction factor algorithm. The model revealed that there was a strong correlation between the FEA and the experimental results. The clinical success of 3D-printed dental implant experimentally is 20.51 years and computationally under Normal strain is 19.89 years and Brown-Miller with Morrow mean correction factor is 26.82 years.

Fabrication of scaffolds via 3D printing is a promising approach for tissue engineering. In this study, we combined 3D printing with cryogenic crosslinking to create biocompatible gela-tin/oxidized alginate (Gel/OxAlg) scaffolds with large pore sizes, beneficial for bone tissue re-generation. To enhance the osteogenic effects and mechanical properties of these scaffolds, we evaluated the impact of hydroxyapatite (HAp) on the rheological characteristics of the 2.86% (1:1) Gel/OxAlg ink. We investigated the morphological and mechanical properties of scaffolds with low, 5% and high 10% HAp content, as well as the resulting bio and osteogenic effects. Scanning electron microscopy revealed a reduction in pore sizes from 160-180 µm (HAp-free) to 120-140 µm for both HAp-containing scaffolds. Increased stability and higher Young’s moduli were measured for 5% and 10% HAp (18 and 21 kPa, respectively) compared to 11 kPa for HAp-free constructs. Biological assessments with mesenchymal stem cells indicated excellent cytocompati-bility and osteogenic differentiation in all scaffolds, with high degree of mineralization in HAp-containing constructs. Scaffolds with 5% HAp exhibit improved mechanical characteristics and shape fidelity, demonstrate positive osteogenic impact, and enhance bone tissue formation. Increasing the HAp content to 10% did not show any advantages in osteogenesis, offering a minor increase in mechanical strength at the cost of significantly compromised shape fidelity.

This study aims at relating the microstructural arrangement, in particular the symmetry materialised by filament sequencing in fused filament fabrication process on mechanical behaviour of printed polyamide. Dogbone structures are printed using various printing temperatures, which are combined with part orientation and raster angle that represent the in-plane and out-of-plane symmetrical arrangement of filament. Mechanical testing is conducted on both as-received filaments and printed structures to derive the effect of filament arrangement symmetry and process-generated defects on mechanical loss. In addition, microstructural analysis using scanning electron microscopy is used to share more light on the filament arrangement and their consequence on deformation mechanisms with respect to the printing conditions. The results show that 3D printed polyamide-based material exhibit remarkable tensile performance with strain stiffening behaviour and large elongation at break thanks to particular filament layout. Among the considered printing conditions, the part orientation is found to have the largest influence on tensile behaviour, which modulates the behaviour from complete restoration of the filament performance to mechanical loss.

As a member of smart materials, electrorheological elastomers (EREs) formed by pre-treating active electrorheological particles are attracting more and more attention. In this work, four Mg-doped strontium titanate particles with spherical, dendritic, flake-like and pinecone-like morphorlogies were obtained by hydrothermal and low-temperature co-precipitation. XRD, SEM, Raman and FT-IR were used to characterize the obtained products. The results showed that the sizes of Mg-doped strontium titanates are about 1.5‒2.0 μm, and the phase structure are dominated by cubic crystal. These Mg-doped strontium titanates were dispersed in a hydrogel composite elastic medium. Then, Mg-doped strontium titanate/glycerol/gelatin electrorheological composite hydrophilic elastomers were obtained with or without electric field. The electric field response properties of Mg-doped strontium titanate composite elastomers were investigated. It concluded that dendritic Mg-doped strontium titanate composite elastomers is high-performance EREs. And the maximum value of energy storage modulus of Mg-doped strontium titanate composite elastomers has achieved 8.70 MPa. This high electrorheological performance of the products is helpful for their applications in vibration control, force transducers, smart structures, dampers, and other fields.

Effects of oxygen content on microstructure and creep property of FGH96 superalloy were investigated. When oxygen content increased from 135ppm to 341ppm, prior particle boundary (PPB) rose from degree 2 to degree 3, and the size of γ′ phase on PPB enlarged from 1.07μm to 1.27μm, and MC carbide size grew from 77.4nm to 104.0nm. Meanwhile, the steady creep rate accelerated form 4.34×10-3 h-1 to 1.87×10-2 h-1, and the creep rupture life shortened from 176h to 94h, and the creep rupture mode transferred from intergranular and transgranular mixed fracture to along PPB fracture. During creep, the micro-twins formation and gliding will be restrained by ∑3 boundaries. FGH96 superalloy with higher oxygen content contains less ∑3 boundaries and its micro-twins cross slipped instead of single direction slip in lower oxygen content superalloy. Consequently, specimen with higher oxygen content creeped faster and raptured earlier.

The continuous casting process of helical fiber reinforced metal matrix composites was proposed, and the experimental equipment was designed and manufactured. The relationship model be-tween the process parameters and the helical shape of the fibers in the metal matrix is analyzed by differential geometry. Helical carbon fiber reinforced lead matrix composites were prepared under different conditions. When the melting temperature and cooling intensity were increased, the helical radius of helical carbon fiber in lead matrix was increased. When the fiber rotation speed was increased, the helical radius was decreased, and the helical pitch was de-creased proportionally. The experimental results are consistent with the process model. Carbon fiber rein-forced aluminum composites were prepared. Scanning electron microscopy showed that the infiltration between the aluminum matrix and the carbon fiber was not complete. As the volume fraction of carbon fiber which was added in composites is too small, the mechanical properties of the composites have not been significantly improved.

— Printing electronics incorporates several significant technologies, such as semiconductor devices produced by various printing techniques on flexible substrates. With growing interest in printed electronic devices, new technologies have been developed to make novel devices with inexpensive and large-area printing techniques. This review article focuses on the most recent developments in printed photonic devices. Photonics and optoelectronic systems may now be built utilizing materials with specific optical properties and 3D designs achieved through additive printing. Optical and architected materials that can be printed in their entirety are among the most promising future research topics, as are platforms for multi-material processing and printing technologies that can print enormous volumes at high resolution while also maintaining high throughput. Significant advances in innovative printable materials create new opportunities for functional devices to act efficiently, such as wearable sensors, integrated optoelectronics, and consumer electronics. This article provides an overview of printable materials, printing methods, and uses of printed electronic devices.

Three-dimensional V₂O₅ hollow structures have been prepared through a simple synthesis strategy combining solvothermal treatment and a subsequent thermal annealing. The V₂O₅ materials are composed of microspheres 2–3 μm in diameter and with a distinct hollow interior. The as-synthesized V₂O₅ hollow microspheres, when evaluated as a cathode material for lithium-ion batteries, can deliver a specific capacity as high as 273 mAh·g⁻¹ at 0.2 C. Benefiting from the hollow structures that afford fast electrolyte transport and volume accommodation, the V₂O₅ cathode also exhibits a superior rate capability and excellent cycling stability. The good Li-ion storage performance demonstrates the great potential of this unique V₂O₅ hollow material as a high-performance cathode for lithium-ion batteries.

The presented work offers a novel process scheme for valorizing historical Pb-Zn slag, which involves crushing, grinding, and then using separation techniques to concentrate valuable components (nonferrous metals). This methodology could have a significant impact on the global beneficiation of metallurgical slags since, in theory, it is significantly more simple, environmentally friendly, and cost-effective than standard pyrometallurgical or hydrometallurgical procedures. According to previous physicochemical and mineralogical studies, Pb-Zn slag from "Topilnica" Veles is a valuable secondary raw material. This inhomogeneous technogenic resource contains substantial amounts of nonferrous metals (Pb, Zn, Cu, and Ag). However, laboratory tests have indicated that the Pb-Zn slag contains a very uneven valuable metals amounts, ranging from several g/ton to several tens of g/ton. The main issue is that traditional metallurgical procedures for releasing beneficial elements are not commercially viable since the valuable elements are "trapped" within amorphous aluminosilicates or intergrowths of alloy grains and glassy phases. Gravity concentration (Wilfley 13 shaking table) and magnetic separation (Davis separator and disk separator) were used to obtain the final concentrate following comminution and grindability testing. The gravity concentration proved more effective. This streamlined approach of valorizing Pb-Zn slag can reduce the need for hazardous chemicals used in hydrometallurgical refinement operations, as well as the extremely high temperatures required for pyrometallurgical processing. This is the first investigation into the feasibility of this novel approach, which includes direct investigations of the Pb-Zn slag feed using these alternative technologies. After extracting the valuable metals, the amorphous aluminosilicate part of the Pb-Zn slag can be reapplied as an alternative raw material in the building sector, adding to the circularity of the suggested approach..

Artificial intelligence (AI) and 3D printing (3DP) play critical roles in what is known as the 4th Industrial Revolution by developing data- and machine-intelligence-based integrated production technologies. This shift has led to increasingly complex design requirements and fabrication methods, posing several challenges for implementing design, fabrication process, and architectural quality standardization. This paper systematically reviews AI techniques applied in diverse stages of 3DP production in architecture. The research goals are to (1) offer a comprehensive critical analysis of the body of literature; (2) identify and categorize approaches to integrating AI in the production of 3D-printed structures; (3) identify and discuss challenges and opportunities of AI integration in architectural production of 3DP structures; and (4) identify gap and provide recommendations for future research. The findings indicate that topics related to AI applications are current and trending, receiving increasing attention from researchers in general and particularly those working in machine and deep learning, artificial neural networks, and pattern recognition. However, the potential of the application of AI in architectural production using additive manufacturing still needs to be explored. Considering this, the paper emphasizes the necessity of redefining traditional field boundaries and opening new opportunities in the sector.

For this research, a comparative evaluation was performed in which the addition of 3D-printed biocarriers fabricated with 13X and Halloysite (13Χ-Η) and commercial Kaldnes K1 biocarriers were evaluated as opposed to the non addition of biocarriers in a semi-pilot scale MBBR-MBR unit. For the evaluation of the MBBR-MBR efficiency, various physicochemical parameters were measured while static light scattering and optical microscopy observations were additionally used. Biofilm extracted from the biocarriers was also evaluated. It was observed that in the MBBR-MBR K1 unit, the membrane filtration improved while in the MBBR-MBR 13X-H unit the membrane fouling rate was the same as in the control MBBR-MBR unit. This is due to the production of large amount of SMP which resulted from the large amount of biofilm created in the 13X-H biocarriers. An optimal biodegradation of the organic load was concluded for all three MBBR-MBR units. The nitrification and denitrification processes were improved at the MBBR-MBR units using 13X-H and K1. The dry mass produced on the 13X-H biocarriers was three orders of magnitude larger than that produced on the K1. Finally, it was observed that mostly EPS was produced in the biofilm of K1 biocarriers while in the biofilm of 13X-H mostly SMP.

3D printing with cement-based materials is a promising manufacturing technique for civil engineering applications that already allows for the design and the construction of complex and highly customized structures using a layer-by-layer deposition approach. Usually, in this type of additive manufacturing, a mixture of cement, water, aggregate and additives is extruded through a specific print head and deposited in successive layers to form the desired shape. The extrusion mechanism is one of the most expensive parts of the 3D printer. Also, for low scale 3D printers, based on the shape of the extruder and the geometry limitation of the mixing blade, the 3D mixture is often limited to a narrow range of materials due to the risk of layer splitting or blockage. Therefore, there is a need to develop affordable and feasible alternatives to the current design-fabrication-application approach of 3D printers. In this paper, various new designed mixtures of fiber reinforced mortars that can be 3D printed using only a commercially available screw pump are analyzed based on their fresh properties and mechanical characteristics. The reduced facility requirements in this approach allow 3D-printing to be more available for civil engineering applications. With further innovation in the future, this method and mixtures can be extended for sustainable and economically feasible printing of single-family housing units.

To realize the utilization of peanut shell, this study investigates the combustion behavior, chemical kinetics, and thermodynamic parameters of peanut shell using TGA under atmospheric air. Results indicate that increasing the heating rate leads to higher ignition, burnout, and peak temperatures, as observed in the TG/DTG curves shifting to the right. Analysis of combustion performance parameters suggest that higher heating rates can enhance combustion performances. Kinetic analysis using two model-free methods, KAS and FWO, shows that the activation energy (Eα) ranges from 93.30 to 109.65 kJ/mol for FWO and 89.72 to 103.88 kJ/mol for KAS. The data fit well with coefficient of determination values (R2) close to 1. Pre-exponential factors using FWO range from 2.19×106 to 8.06×107 s–1, and for KAS range from9.72×105 to 2.25×107 s–1. Thermodynamic analysis indicates a low-energy barrier (≤ ±6 kJ/mol) between activation energy and enthalpy changes, suggesting easy reaction initiation. Furthermore, variations in enthalpy (ΔH), Gibbs free energy (ΔG), and entropy (ΔS) upon conversion (α) suggest that peanut shell combustion is endothermic and non-spontaneous, with the generation of more homogeneous or well-ordered products as combustion progresses. These findings offer a theoretical basis and data support for the further utilization of agricultural biomass.

Verifying the accuracy of a 3D-printed object involves using an image processing system. This system compares images of the CAD model of the object to be printed with its 3D-printed counterparts to identify any discrepancies. It is important to note that the integrity of the accuracy measurement is heavily dependent on the image processing settings chosen. This study focuses on this issue by developing a customized image processing system. The system generates binary images of a given CAD model and its 3D-printed counterparts and then compares them pixel-by-pixel to determine the accuracy. Users can experiment with various image processing settings, such as grayscale to binary image conversion threshold, noise reduction parameters, masking parameters, and pixel-fineness adjustment parameters, to see how they affect accuracy. The study concludes that the grayscale to binary image conversion threshold has the most significant impact on accuracy and that the optimal threshold varies depending on the color of the 3D-printed object. The system can also effectively eliminate noise (filament marks) during image processing, ensuring accurate measurements. Additionally, the system can measure the accuracy of highly complex porous structures where the pores size, depth, and distribution are random. The insights gained from this study can be used to develop intelligent systems for the metrology of additive manufacturing.

The research on calcium leaching of 3D printed cement pastes (3DPC) exposed in aggressive water is limited, and the mechanism underlying its effect needs to be better understood. The performance anisotropy of degraded 3DPC due to calcium leaching is investigated in this paper. Samples with aggregate micro fines (AMF) and fly ash (FA) were prepared. A 6 mol/L NH₄Cl solution was used in the accelerated experiment. At specific leaching durations, performances were tested on the samples in different leaching directions. Results show that the performances of 3DPC in aggressive water have a significant anisotropic behavior. The evolution of pore defects and hydration products mainly governs the performance anisotropy of degraded 3DPC. The remaining hydration products of the surface of 3DPC leached in the Z direction are less than the other two directions because calcium ions leached in the Z direction are difficult to be compensated through weak interfaces between layers.

High-performance electromagnetic interference (EMI) shielding materials with ultralow density and environment friendly properties are greatly demanded to address electromagnetic radiation pollution. Herein, carbon nanotubes/polylactic acid (CNTs/PLA) materials with different CNTs contents, which exhibit characteristics of light weight, environmental protection and good chemical stability, are fabricated by 3D printing technology, where CNTs are evenly distributed and bind well with PLA. The performances of 3D printed CNTs/PLA composite are improved compared to pure 3D printed PLA composite, which include mechanical properties, conductive behaviors and electromagnetic interference (EMI) shielding. The EMI shielding effectiveness (SE) of CNTs/PLA composite could be improved when the contents of CNTs increase. When it reaches 15 wt%, the EMI SE of 3D printed CNTs/PLA composite could get up to 47.1 dB, which shields 99.998% of electromagnetic energy. Meanwhile, the EMI shielding mechanism of 3D printed CNTs/PLA composite is mainly of absorption loss, and it generally accounted for more than 80% of the total shielding loss. These excellent comprehensive performances endow the 3D printed CNTs/PLA composite with great potential for use in industrial and aerospace area.

Recently, 3D printing techniques gained much attention in solid dosage form production. Even though the methods are increasingly studied, there are still many challenges in establishing an accurate content of active ingredients in the final products. In the present study, new experimental design techniques and statistical software were developed to identify and optimize a formula to predict the mass of the tablet to be 3D printed before it actually is. The first step was to develop a virtual 3D object in the FreeCad Software, then, using a CURA slicer software, the G-code Format was obtained. The tablets were printed using a Cartesian 3D printer based on the generated data. Finally, adapting the object sequencing mode, a predicted drug mass value was obtained. As expected, the oblong tablet's scaling directly influences its mass. The software generates a correlation coefficient (r) of 0.84, confirming the directly proportional relationship between scaling and tablet weight. However, the r values progressively decreased, indicating a poor correlation between tablet weight and other factors: infill density percent (r = 0.403) and wall thickness (r = 0.185). After repeating the 3D printing with the values ​​suggested by the software, tablets with a practical value of 1066 mg were obtained. Considering that the confidence interval calculated is [834.95—1165.05] and the experimental value is 1066 mg, it can be certified that the proposed model is valid.

Introduction: The current generation of 3D printers are lighter, cheaper, and smaller, making them more accessible to the chairside digital dentist than ever before. 3D printers in general in the industrial and chairside setting can work with various types of materials including, metals, ceramics, and polymers. Evidence presented in many studies show that an ideal material used for dental restorations is characterised by several properties related to durability, cost-effectiveness, and high performance. This review is the second part in a 3D Printing series that looks at the literature on material science and applications for these materials in 3D printing as well as a discussion on the potential further development and future evolution in 3D printing materials. Conclusions: Current materials in 3D printing provide a wide range of possibilities for providing more predictable workflows as well as improving efficiency through less wasteful additive manufacturing in CAD/CAM procedures. Incorporating a 3D printer and a digital workflow into a dental practice is challenging but the wide range of manufacturing options and materials available mean that the dentist should be well prepared to treat patients with a more predictable and cost effective treatment pathway. As 3D printing continues to become a commonplace addition to chair side dental clinics, the evolution of these materials, in particular reinforced PMMA, resin incorporating zirconia and glass reinforced polymers offer increased speed and improved aesthetics that will likely replace subtractive manufacturing milling machines for most procedures.

In recent years, cerium dioxide (CeO2) has attracted considerable attention owing to its remarkable performance in various applications, including photocatalysis, fuel cells, and catalysis. This study explores the effect of nickel (Ni) doping on the structural, thermal, and chemical properties of CeO2 nanorods, particularly focusing on oxygen vacancy-related phenomena. Utilizing X-ray powder diffraction (XRD), alterations in crystal structure and peak shifts were observed, indicating successful Ni doping and the formation of Ni2O3 at higher doping levels, likely due to non-equilibrium reactions. Thermal gravimetric analysis (TGA) revealed changes in oxygen release mechanisms, with increasing Ni doping resulting in the release of lattice oxygen at lower temperatures. Raman spectroscopy corroborated these findings by identifying characteristic peaks associated with oxygen vacancies, facilitating the assessment of Ni doping levels. Overall, this study underscores the substantial impact of Ni doping on CeO2 nanorods, shedding light on tailored catalytic applications through modulation of oxygen vacancies while preserving the nanorod morphology.

A dynamic impact test was performed on as-rolled AZ31 alloy with gradient microstructure under various strains. The microstructural evolution and mechanical properties were systematically investigated. As the strain rate gradually increases, an increasing number of twins are formed, facilitating dynamic recrystallization (DRX), and the mechanical properties are also gradually improved as well. The microstructure becomes heterogeneous at higher strain rates, but the peak stress decreases. The impact process results in significantly higher performance due to microstructural refinement, work hardening by dislocations and precipitates. In addition, both the adiabatic shear band and the adjacent crack experience a temperature rise that exceeds the recrystallization temperature of the alloy. This observation also explains the presence of ultrafine recrystallized grains within the adiabatic shear band and the appearance of molten metal around the crack.

Asymmetric lithium salts, such as Lithium (difluoromethanesulfonyl)(trifluoromethanesulfonyl)imide (LiDFTFSI), have been demonstrated to surpass traditional symmetric lithium salts with improved Li+ conductivity and the capacity to generate stable solid electrolyte interphase (SEI) while maintaining compatibility with aluminum (Al0) current collector. However, the intrinsic reductive mechanism through which LiDFTFSI influences battery performance remains unclear and under debate. Herein, the detailed SEI reactions of LiDFTFSI-based electrolytes were investigated by combining density functional theory and molecular dynamics, aiming to clarify the formation process and atomic structure of SEI. Our results show that asymmetric DFTFSI– weakens the interaction between carbonate solvents and Li+, and substantially alter the solvation structure, exhibiting a well-balanced coordination capacity to bis(trifluoromethanesulfonyl)imide (TFSI–). Nanoseconds hybrid molecular dynamics simulation further reveals that the preferential decomposition of LiDFTFSI produces sufficient LiF and Li2O to facilitate a robust SEI. Moreover, the abundant F– generated from LiDFTFSI decomposition accumulates on the Al surface and subsequently combines with Al3+ from the current collector to form AlF3, potentially inhibiting corrosion of the current collector. Overall, these findings elucidate how LiDFTFSI regulates the solvation sheath and SEI structure, advancing the development of high-performance electrolytes compatible with current collector.

Ti and its alloys are the most commonly used materials for biomedical applications. However, bacterial infection after implant placement is still one of the significant rising complications. Therefore, the application of the antimicrobial agents into implant surfaces to prevent implant-associated infection has attracted lots of attention. Scientific papers have shown that inorganic antibacterial metal element (e.g. Ag, Cu, Zn) can be introduced to implant surfaces with the addition of metal nanoparticles or metallic compounds into electrolyte via micro-arc oxidation (MAO) technology. In this review, the effects of the composition and concentration of electrolyte and process parameters (e.g. voltage, current density, oxidation time) on morphological characteristics (e.g. surface morphology, bonding strength), antibacterial ability and biocompatibility of MAO antimicrobial coating were discussed in detail. Anti-infection and osseo-integration can be simultaneously accomplished with the selection of the proper antibacterial elements and operating parameters. Besides, MAO assisted by magnetron sputtering (MS) to endow Ti-based implant materials with superior antibacterial ability and biocompatibility was also discussed. Finally, the development trend of MAO technology in the future was forecasted.

Fe-(9, 19, 28, 37)wt.% Cr alloys were corroded at 700 and 800 ^oC for 70 h under 1 atm of N₂, 1 atm of N₂/3.2%H₂O-mixed gas, and 1 atm of N₂/3.1%H₂O/2.42%H₂S-mixed gas. The corrosion rate of Fe-9Cr alloy increased with the addition of H₂O, and furthermore with the addition of H₂S in N₂ gas. Fe-9Cr alloy was always nonprotective. In contrast, Fe-(19, 28, 37) wt.%Cr alloys were protective in N₂ and N₂/H₂O-mixed gas because of formation of the Cr₂O₃ layer. They were, however, nonprotective in N₂/H₂O/H₂S-mixed gas because sulfidation dominated to form the outer FeS layer and the inner Cr₂S₃ layer containing some FeCr₂S₄.

With the advancement of Additive Manufacturing and its applications in various industrial segments, it becomes increasingly important to investigate the processability parameters associated with nano-reinforcement. This study examines the influence of infill parameters, such as patterns (hexagonal, triangular and concentric), shape (solid and honeycomb) and concentrations by mass of Carbon Nanotubes (CNTs) at 1.0 wt% and 2.0 wt% on the mechanical compression properties of the 3D printed material. In this sense, nanocomposites based on Polylactic Acid (PLA) matrix nano-reinforced by CNTs were characterized using the Scanning Electron Microscopy -SEM, X-ray Diffraction, Raman Spectroscopy techniques and mechanical analysis. The mechanical properties of both the matrix and the nanocomposites were determined through mechanical compression tests, in accordance with [1]. SEM revealed compacted regions, voids, and detachment in the structures. XRD characterization indicated PLA predominantly amorphous nature, while CNTs exhibited characteristic diffractions of carbon nanotubes. Raman characterization showcased bands and characteristic vibrations of CNTs and PLA, nanocomposites' vibrational modes combine those of CNTs and PLA. Mechanical compression analysis indicates a direct influence of infill pattern, shape, and nano-reinforcement. The triangle pattern outperformed other patterns, exhibiting a 15.03% increase compared to concentric and 8.8% compared to hexagon infill. In nanocomposites, all showed higher compressive strength than the matrix. For PLA/1.0%CNTs, strength was 16.8%, and for PLA/2.0%CNTs, it reached 39.2%. In honeycomb shapes with infill variations, the triangular pattern excelled with a 0.97% increase over concentric and 6.12% over hexagon patterns. Honeycomb results indicate a 59.6% increase for (PLA/1.0%CNTs) and a 0.48% increase for (PLA/2.0%CNTs) compared to the matrix. This study highlights 3D printing parameters, emphasizing the effectiveness of the triangular pattern and the enhanced strength with the addition of CNTs, providing insights to enhance products manufactured through Additive Manufacturing.

Notwithstanding the advances achieved in the last decades in the field of synthetic bone substitutes, the development of biodegradable 3D scaffolds with ideal mechanical and biological properties remains an unattained challenge. In this work, a novel approach is explored to produce synthetic bone grafts mimicking the complex bone structure using additive manufacturing. For the first time, scaffolds were produced, using an extrusion technique, composed of a thermoplastic polymer, polycaprolactone (PCL), hydroxyapatite nanoparticles (HANp), and polyethylene glycol diacrylate (PEGDA). These scaffolds were further compared with two groups of scaffolds: one composed of PCL and another of PCL and HANp. After production, optimisation and characterisation of these scaffolds, an in vitro evaluation was performed using human dental pulp stem/stromal cells (hDPSCs). Through the findings it was possible to conclude that PEGDA scaffolds were successfully produced presenting networks of interconnected channels, presenting hydrophilic properties (15.15 4.06°), adequate mechanical performance (10.41MPa 0.934), and allowing a cell viability significantly superior to the other groups analysed. To conclude, findings in this study demonstrated that PCL, HANp and PEGDA scaffolds may have promising effects on bone regeneration and might open new insights for 3D tissue substitutes.

This paper presents a comparison between indirect methods for assessing the buildability of 3D printed cementitious materials, including CRV or CSR test using rotational rheometry, unconfined uniaxial compression test (UUCT), a newly proposed confined uniaxial compression test (CUCT), and fast penetration test. The experimental program was conducted on the extruded samples of six printable mortars and two printable concretes with various rheological behavior achieved by the use of different additives and admixtures. Predictions of the material failure and the stability failure in hollow cylindrical structures are provided and compared with the results of the direct printing test. Benefits and disadvantages of the employed test methods are discussed, also taking into consideration a perspective of their use for automated in-situ control of the materials’ buildability.

Metal 3D printing technology is a promising manufacturing method, especially in the case of complex shapes. The quality of the printed product is still a challenging issue for mechanical applications. The anisotropy of the microstructure, imperfections, and residual stress are some of the issues that diminish the mechanical properties of the printed sample. The simulation could be used to investigate some technical details, and this research has tried to computationally study the metal 3D printing of austenitic stainless steel to address austenite microstructure and local yield strength. Two computational codes were developed in Visual basics 2015 to simulate the local heating/cooling curve and subsequent austenite microstructure. A stochastic computational code was developed to simulate austenite grain morphology based on calculated thermal history. Then Hall-Pitch equation was used to estimate the yield strength of the printed sample. These codes were used to simulate the effect of temperature of the printer’s chamber on microstructure and subsequent yield strength. The austenite grain topology is more columnar at a lower temperature. The percentage of the equiaxed zone will be increased at a higher chamber’s temperature. Almost a fully equiaxed austenite microstructure will be achieved at 800 C chamber’s temperature, but the last printed layer, which is columnar and can be removed by cutting then. The estimated local austenite grain size and the local yield strength in the equiaxed regions are in the range of 15 to 30 μm and 270 to 330 MPa at 800 C temperature of printer’s chamber, respectively.

Hierarchical tungsten oxide assemblies such as spindle-like, flowers with sharp petals, nanowires and regular hexagonal structures are successfully synthesized via a solvothermal reduction method by simply adjusting the reaction conditions. On the basis of the experimental results, it is determined that the reaction time significantly influences the phase transition, microstructure and photocatalytic activity of the prepared samples. The possible mechanisms for the phase transition and morphology evolution process have been systematically proposed. Moreover, the as-prepared products exhibit significant morphology-depended photocatalytic activity. The flower-like W18O49 prepared at 6 h possesses large specific surface area (150.1 m²g^-1), improved separation efficiency of electron-hole pairs and decreased electron-transfer resistance by the photoelectrochemical measurements. As a result, the flower-like W₁₈O₄₉ prepared at 6 h exhibits the highest photocatalytic activity for the degradation of Methyl orange aqueous solution. The radical trap experiments showed that the degradation of MO was driven mainly by the participation of h⁺ and •O²⁻ radicals.

Surface initiated atom transfer radical polymerization (SI-ATRP) is one of the most versatile technique to modify the surface properties of material. Recent developed metal free SI-ATRP makes such technique more widely applicable. Herein photo-induced metal-free SI-ATRP of methacrylates, such as methyl methacrylate, N-isopropanyl acrylamide, and N,N- dimethylaminoethyl methacrylate, on the surface of SBA-15 was reported to fabricate organic-inorganic hybrid materials. SBA-15 based polymeric composite with adjustable graft ratio was obtained. The structure evolution during the SI-ATRP modification of SBA-15 was monitored and verified by FT-IR, XPS, TGA, BET, and TEM. The obtained polymeric composite showed enhanced adsorption ability for the model compound toluene in aqueous. This procedure provides a low cost, ready availability, and facile modification way to synthesize the polymeric composites without the contamination of metal.

Endoscopy has made a significant and noteworthy contribution to the field of medical science and technology. Nevertheless, its potential remains constrained due to the limited availability of rigid or flexible endoscopes. This paper introduces a novel hydraulic actuator based on electrorheological fluid (ERF) as a pivotal advancement in bridging the existing gap within the realm of endoscopy. Following a comprehensive introduction that briefly outlines the electrorheological effect, the subsequent section is dedicated to the elucidation of the actuator’s development process. Challenges arise, particularly in terms of miniaturization and the realization of a hydraulically sealed system with integrated valve electrodes. An internal electrorheological valve system consisting of four valves that are controlled using a pulse-width modulated high voltage was suitable for position control of the antagonistic hydraulic actuators. High-precision stereolithography (SLA) printing has proven practical for manufacturing the actuator components. For functional testing, a test bench was set up in which the actuator follows a setpoint through a PI control loop. The control deviation ranged from 0.6 to 1 degree, with a response time between 6 and 8 seconds. The experiments have demonstrated that, through the use of ERF and integrated valve electrodes, a miniaturized functional actuator can be constructed.

The radiation stability of polymer test objects fabricated by direct laser writing is studied. The two groups of 6 cubes (50×50×50 μm3) were printed on a common silicon substrate. 6 cubes were irradiated with X-rays in the synchrotron radiation beam (12 keV, 1010 photons/mm2/s), the other 6 kept non-irradiated for the reference. In each group, the fabrication parameters (laser power and slicing step) were uniformly varied from cube to cube. Each irradiated cube was exposed with the dose of 1013 X-ray photons. The calibration of this dose in the radiological units (Gy) was carried out using the tissue-equivalent thermoluminescent detectors (TLD-800). The corresponding exposition dose was estimated as 30 kGy for each cube. The radiation effects were evaluated by Raman spectroscopy and by morphological changes observed with the raster electron microscope. The primary radiation effect appears in the essential increase of the polymerization degree with consuming carbon-carbon double bonds in favor of the polymer cross-linking. Only one cube of 6 has changed the size and shape due to this effect, while the others retained the initial shape. Morphological changes are connected with the improper fabrication parameters (laser power and slicing step). Properly fabricated objects withstand the X-rays of the synchrotron radiation beam.

This study provides a contribution to the research field of 3D printed earthen buildings, focusing, for the first time, on the load-bearing capacity of these structures. The study involves the entire production and testing process of the earthen elements, from design, to the preparation of the mixture and the 3D printing, up to the uniaxial compression test on a wall segment. The results indicate that 3D printed earthen elements have a compressive strength of 2.32 MPa, comparable to that of rammed earth structures. The experimental data also made it possible to draw conclusions on the action of the infill, which seems to have the function of stopping the propagation of cracks. This has a positive effect on the overall behavior of 3D printed earthen elements, since it avoids the onset of dilative behavior in the final stages of the load test and maintains ultimate load values higher than 50% of the maximum load.

Aluminum wire is a common material for wire bonding due to its resistance to oxidation and low price. It does not melt when becoming a free air ball (FAB) during the electronic flame-off (EFO) process with wettability, and is applied by wedge bonding. This study used 20μm Zn-Coated Al-0.5wt.%Si (ZAS) wires to improve the FAB shape after the EFO process, while maintaining stability of the mechanical properties, including the interface bonding strength and hardness. In order to test circuit stability after ball bonding, the current-tensile test was performed. During the experiment, it was found that 80nm ZAS with wire bonding has lower resistance and higher fusing current. For the bias tensile test, the thicker Zn film diffused into the Al-Si matrix easily, after which the strength was reduced. The ball-bond interfaces had no change in their condition before and after the bias. Accordingly, ZAS could be a promising candidate for ball bonding in the future.

Tissue-like phantoms are widely used as a model for mimicking the optical properties of live tissue. This paper presents the results of a diffusion reflection method as well as fluorescence lifetime imaging microscopy measurements of fluorescein-conjugated gold nanorods in solution as well as inserted in solid tissue-imitating phantoms. A lack of consistency between the fluorescence lifetime results of the solutions and the phantoms raises a question about the ability of tissue-like phantoms to maintain the optical properties of inserted contrast agents.

Redox mediators comprising I–, Co3+, and Ti3C2Tx MXene were applied to dye-sensitized solar cells (DSCs). In the as-prepared DSCs (I-DSCs), wherein hole conduction occurred via the redox reaction of I−/I3− ions, the power conversion efficiency (PCE) was not altered by the addition of Ti3C2Tx MXene. The I-DSCs were exposed to light to produce Co2+/Co3+-based cells (Co-DSCs), wherein the holes were transferred via the redox reaction of Co2+/Co3+ ions. A PCE of 9.01% was achieved in a Co-DSC with Ti3C2Tx MXene (Ti3C2Tx-Co-DSC), which indicated an improvement from the PCE of a bare Co-DSC without Ti3C2Tx MXene (7.27%). It was also found that the presence of Ti3C2Tx MXene in the redox mediator increased the hole collection, dye regeneration, and electron injection efficiencies of the Ti3C2Tx-Co-DSC, leading to an improvement in both the short-circuit current and the PCE when compared with those of the bare Co-DSC without MXene.

During the last years there has been a high interest in the development of new purely-organic single-component conductors. Very recently, we have reported a new neutral radical conductor based on the perchlorotriphenylmethyl (PTM) radical moiety linked to a monopyrrolo-tetrathiafulvalene (MPTTF) unit by a -conjugated bridge (1). Interestingly, this system behaves as a semiconductor with high conductivity and small energy gap under high pressure. With the aim of developing a new material with improved conducting properties, we have designed and synthesized the radical dyad 2 which was functionalized with an ethylenedithio (EDT) group in order to improve the intermolecular interactions of the TTF subunits. The physical properties of the new radical dyad 2 were studied in detail in solution to further analyze its electronic structure as well as its potential use as radical conductor in the solid state.

Natural rocks are highly heterogeneous due to various geological processes that constantly alter their properties. The accumulation, deposition, and cementation of mineral and organic particles continuously modify the spatial characteristics of rock properties. Property variability or anisotropy is commonly observed in most rock types and influences strength, transport, and thermal conductivity behavior. This unpredictability presents a significant challenge for laboratory testing. Binder-jet additive manufacturing (3D printing) has emerged as a valuable technology for characterizing rock properties in geoscience and engineering. This study proposes a methodology to evaluate the variability and repeatability of mechanical properties of 3D-printed sandstones during binder-jet additive manufacturing. The mechanical properties were analyzed statistically for samples located in various parts of the 3D printer build volume. The results showed that the 3D-printed sandstones exhibited significant variations in their strength and stiffness properties when measured from samples produced within the same build volume during binder-jet additive manufacturing. The Uniaxial Compressive Strength (UCS) varied from 23 to 38 MPa, with an average value of 29 MPa. The Young's modulus, on the other hand, ranged from 1.5 to 4.05 GPa, with an average value of 2.33 GPa. The variability of the mechanical properties, quantified by the standard deviation, decreased when the entire population of 3D-printed sandstones was divided into smaller samples situated at different elevations of the build platform.

In the present work, a comparative evaluation of an MBBR unit performance was carried out for the following cases: when adding 3D-printed biocarriers fabricated with 13X and bentonite, when using K1 commercial biocarriers and when not adding biocarriers at all. For the evaluation of the MBBR efficiency, various physicochemical parameters were measured, while static light scattering and optical microscopy observations were additionally used. Finally, biofilm extracted from the biocarriers was evaluated. The findings suggest that there is an optimal biodegradation of the organic load in all MBBR units. The nitrification and denitrification process were improved at the 3D MBBR as compared to the control MBBR and MBBR K1. The dry mass of the biofilm in the 3D-printed biocarriers was two orders of magnitude larger than the one in the K1 biocarriers. What is more, in the K1 biocarriers the mass of the biofilm varied in relation to time, due to the fact that it could not be kept inside the holes, something that was not observed to happen with the 3D-printed biocarriers. Finally, it was observed, mostly in the 3D MBBR and less in the K1 MBBR, that the growth of nitrifying bacteria and heterotrophs inside the units increased the biomass production in the form of SMP, which in turn favored the adhesion of biomass on the surface of biocarriers.

In this paper, the characterization of 3D printed materials that are considered in the design of multirotor unmanned aerial vehicles (UAVs) for specialised purposes was carried out. The multirotor UAV system is briefly described, primarily from the aspect of system dynamics, considering that the airframe parts connect the UAV components, including the propulsion configuration, into a functional assembly. Three additive manufacturing (AM) technologies were discussed, and a brief overview was given of selective laser sintering (SLS), fused deposition modeling (FDM), and continuous fiber fabrication (CFF). Using hardware and related software, 12 series of specimens were produced which were experimentally tested utilizing a quasi-static uniaxial tensile test. The results of the experimental tests are given graphically with displacement-force characteristics. In this work, the focus is on CFF technology and the testing of materials that will be used in the production of mechanically loaded airframe parts of multirotor UAVs. Furthermore, an overview was given in such a way that the specimens were grouped, and the mean values of the maximum stress were presented, so that the tested materials could be more easily compared with conventional materials, such as aluminum alloys.

Copper(I) sulfide (Cu2S) is a low-cost, earth-abundant, and non-toxic thermoelectric material for applications in the middle-high temperature range (&gt;650 K). Although 3D printing these materials can simplify their manufacturing, elevated temperatures observed during sintering impair their crystal structure and energy conversion efficiency. In this study, we demonstrated a novel post-processing methodology to revert the thermoelectric properties of the 3D printed Cu2-xS materials back to the unimpaired state via sulfur infusion. After printing and sintering, sulfur was infused into the specimens under vacuum to optimize their crystal structure and achieve high thermoelectric efficiency. Chemical analysis and X-ray Diffraction (XRD) tests showed that after the sulfur infusion process, the Cu/S ratio was reverted close to the stoichiometric level. 3D printed Cu2-xS showed p-type thermoelectric behavior with electrical conductivity peaking at 143 S-cm-1 at 750 K and Seebeck coefficient of 175 µV-K-1 at 627 K. Figure of merit (ZT) value of 1.0 at 780 K was achieved which is the highest value ever reported for a 3D printed Cu2-xS thermoelectrics at this temperature. Fabrication of environmentally friendly thermoelectric materials with extended dimensional freedom and conversion efficiency has the potential to impact the thermoelectric industry with new energy conversion applications and lowered manufacturing costs.

The objective of this research is to conduct a comparative analysis between rectangular-shaped ASTM D3039 specimens with different angles (0°, 15°, and 90°) and various tensile test specimens based on ASTM and ISO standards, all 3D-printed using polyethylene terephthalate glycol (PETG) material through FDM. The study aimed to assesses the weak spot commonly found at the neck of the specimens. Two different printing orientations, namely flat and on-edge, were investigated, and a comprehensive examination and comparison were made regarding the variations in tensile strength, E-modulus, strain, and elongation at break among the tested samples. Additionally, the broken areas was evaluated, and a numerical study utilizing the finite element method (FEM) was conducted to identify stress risers' locations in each specimen type. The experimental results demonstrated that the ASTM D3039-0° specimen exhibited the best tensile properties when printed in the on-edge orientation, while the flat orientation yielded the best results in terms of the broken area. On the other hand, the ISO 527-2 specimens displayed the lowest tensile properties, regardless of the printing orientation. The study highlighted the enhanced tensile properties achieved with the rectangular shape. Specifically, the tensile strength of ASTM D3039-0° was 17.87% and 21% higher than that of the ISO 527 geometry shape for the flat and on-edge orientations, respectively. The numerical analysis indicated that the ISO 527-2 specimen had either no or minimal stress raisers, and the higher stresses observed in the narrow section were isolated from the gripping location.

3D-printed aluminium alloy fabrications made by selective laser melting (SLM) offer a promising route for the production of small series of custom-designed heat exchangers with complex geometry and shape and miniature size. Alloy composition and printing parameters need to be optimized to mitigate fabrication defects (pores and microcracks) and enhance the part performance. The deformation response needs to be studied with adequate characterization techniques at relevant dimensional scale capturing the peculiarities of micro-mechanical behavior relevant to the particular article and specimen dimensions. Purposefully designed Al-Si-Mg 3D-printable RS-333 alloy was investigated with a number of microscopy techniques including in situ mechanical testing with a Deben Microtest 1 kN stage integrated and synchronized with Tescan Vega3 SEM to acquire high resolution image datasets for Digital Image Correlation (DIC) analysis. Dog bone specimens were 3D-printed in different orientation of gauge zone cross-section with respect to the fast laser beam scanning and growth directions. This corresponds to varying local conditions of metal solidification and cooling. Specimens show variation in mechanical properties, namely, Young’s modulus (65…78 GPa), yield stress (80–150 MPa), ultimate tensile strength (115–225 MPa) and elongation at break (0,75–1,4 %). Furthermore, the failure localization and character was altered with the change of gauge cross-section orientation. DIC analysis allowed correct strain evaluation that overcame the load frame compliance effect and helped to identify the unevenness of deformation distribution (plasticity waves) that ultimately resulted in exceptionally high strain localization near the ultimate failure crack position.

Currently, the number of approved veterinary medicines are limited, and human medications are used off-label. These approved human medications are of too high potencies for a cat or a small dog breed. Therefore, there is a dire demand for smaller doses of veterinary medicines. This study aims to investigate the use of three semi-solid extrusion 3D printers in a pharmacy or animal clinic setting for extemporaneous manufacturing of prednisolone containing orodispersible films for veterinary use. Orodispersible films with adequate content uniformity and acceptance values defined by the European Pharmacopoeia was produced with one of the studied printers, namely, the Allevi 2 bioprinter. Smooth and flexible films, with high mechanical strength, neutral pH, and low moisture content were produced with high correlation between prepared design and obtained drug amount, indicating that the Allevi 2 printer could successfully be used to extemporaneously manufacture personalized doses for animals at the point-of-care.

The 2019 Novel Coronavirus (COVID-19) has caused an acute reduction in world supplies of personal protective equipment (PPE) due to increased demand. To combat the impending shortage of equipment including N95 masks, the George Washington University Hospital (GWUH) developed a 3D printed reusable N95 comparable respirator that can be used with multiple filtration units. We evaluated several candidate prototype respirator models, 3D printer filaments, and filtration units detailed here. Our most recent working model was based on a respirator found on an open source maker website and was developed with PLA (printer filament), a removable cap, a removable filtration unit consisting of two layers of MERV 16 sandwiched between MERV 13, and removable elastic bands to secure the mask. Our candidate mask passed our own suction test protocol to evaluate leakage and passed a qualitative Bitrix N95 fit test at employee health at GWUH. Further efforts are directed at improving the current model for seal against face, comfort, and sizing. The 3D model is available upon request and in the supplement of this paper. We welcome collaboration with other institutions and suggest other facilities consider mask fit for their own population when exploring this concept.

To better understand the shape memory materials and self-healing materials, a new series of liquid-crystalline shape memory polyurethane (LC-SMPU) composites, named SMPU-OOBAm, were successfully prepared by incorporating 4-octyldecyloxybenzoic acid (OOBA) into the PEG-based SMPU. The effect of OOBA on the structure, morphology and properties has been carefully investigated. The results demonstrate that SMPU-OOBAm have liquid crystalline properties, triple-shape memory properties and self-healing properties. The incorporated OOBA promotes the crystallizability of both soft and hard segments of SMPU, and the crystallization rate of the hard segment of SMPU decreases when the OOBA-content increases. Additionally, the SMPU-OOBAm forms a two-phase separated structure (SMPU phase and OOBA phase), and it shows two-step modulus changes upon heating. Therefore, the SMPU-OOBAm shows triple-shape memory behavior, and the shape recovery ratio decreases with an increase in the OOBA content. Finally, SMPU-OOBAm shows self-healing properties. The new mechanism can be ascribed to the heating-induced “bleeding” of OOBA in the liquid crystalline state and the subsequent re-crystallization upon cooling. This successful combination of liquid crystalline properties, triple-shape memory properties and self-healing properties make the SMPU-OOBAm composites with many promise applications in smart optical devices, smart electronic devices and smart sensors.

Additive manufacturing, commonly referred to as 3D printing, is an exciting and versatile manufacturing technology that is gaining traction and interest in both academic and industrial settings. Polymeric materials are essential components in a majority of the “inks” used across the various 3D printing technologies. As the environmental ramifications of sole or primary reliance on petrochemicals as a resource for industrial polymers continue to manifest themselves at a global scale, a transition to more sustainable bioderived alternatives could offer solutions. In particular, cellulose is promising due to its global abundance, biodegradability, excellent thermal and mechanical properties, and ability to be chemically modified to suit various applications. Thus far, cellulose has typically been incorporated in additive manufacturing applications as a substrate, filler, or reinforcement for other materials. However, due to its versatility and desirable properties, the exploration of all-cellulose 3D printing materials and associated methodologies is increasing. This review will discuss the progress and status of all-cellulose 3D printing approaches, associated challenges, and their potential as a key player in a more sustainable industrial future.

The 3D reconstruction of vermiculite-based sealing material was carried out based on CT scanning experiments and Avizo software. The precision and representation of the reconstructed digital core were tested by calculating the pore structure parameters and comparing them with the experimental results of mercury compression. Avizo is a perfect interface with Fluent software to perform micro-scale seepage simulation to explore the distribution of pressure and velocity fields during fluid transport. In this paper, a new approach is proposed to study the penetration leakage of non-metallic gaskets by using equivalent pore networks.

Deterioration of concrete subjected to freezing and thawing climatic conditions is one of most important factors affecting the durability of concrete infrastructure in cold climates. The freeze-thaw resistance of cementitious materials like concrete and mortar can be determined by the CDF test (Capillary Suction of De-icing chemicals and Freeze-Thaw Test). Here, concrete specimens are subjected to repeated freeze-thaw cycles with simultaneous addition of de-icing salt and the amount of material weathered near the surface is determined. For concretes with adequate freeze-thaw resistance, this test method works very well. However, specimens with inadequate or unknown performance often experience increased edge weathering, which is caused by the detachment of the lateral isolation tape. The increasing edge influence thus leads to a falsification of the results and consequently to an underestimation of the actual freeze-thaw resistance of the material. In materials research in particular, however, concretes with high levels of weathering are studied in order to be able to investigate various factors of influence on the freeze-thaw resistance of concretes in a targeted manner. This paper presents a novel methodology that delivers new information regarding the weathering of CDF test samples and the associated distribution function of the height decrease using high resolution 3D scan data. The results indicate a correlation between the progression of the distribution function and the sample's maximum aggregate size. The change of the sample volume can be used to support the weathering results of the standard CDF methodology. The increase of the surface area is used to estimate the tortuosity of the sample surface. It indicates an asymptotic curve approaching a specific maximum value, which is dependent on the the weathering depth of the sample.

CoCrFeNiMn high-entropy alloy coatings were prepared on compacted graphite iron（CGI） through plasma cladding to strength the CGI substrate. The effects of heat treatment temperatures and times on the microstructure and mechanical properties of the CoCrFeNiMn coatings were investigated. After heat treatment, a single FCC phase was remained in the coating as compared to the deposited one, with smaller dendrites, larger dendritic spacing and more Cr-rich compounds precipitated between dendrites. The coatings’ microhardness was increased after heat treatment. After heat treated at 660°C for 90 minutes, the coating had the highest microhardness of 563±6.9 HV0.2, the lowest frictional coefficient of 0.71 and the smallest wear mass loss of 1.12 mg, and it had the best wear resistance.

Optimum design and accurate control of the internal structure of the laser target materials remain an important goal for various laser physics experiments, especially for generating high flux photon and neutron beams. The low-density material is considered to be one of the most difficult for X-ray study due to its high transparency and imperceptible contrast. To produce clear visualization of foam containing sparse structures we used a high-quality monochromatic X-ray beam of synchrotron radiation source PETRA-III at DESY. The X-ray beam parameters allow tomographic scanning with application of phase contrast retrieval algorithms. A series of 3D images of foam-suspended glass microsphere inside the plastic cylinder were obtained with the quality high enough to observe the internal structure and to visualize uniformity, displacement and surface roughness on both sides of the microsphere. The main object under investigation was a CH-plastic capillary including 10 mg/cc CHO-foam with the centered glass microsphere. The results of this work demonstrate that tomographic visualization based on a high quality X-ray radiation and phase contrast analysis is an effective and useful technique for development of new laser targets containing structured low density materials.

The incremental sheet forming represents a relatively recent technology that guarantees high customization, thanks to the layered manufacturing principle typical of rapid prototyping, and cost-effectiveness, because it does not require dedicated equipment. Research has initially shown that this process is effective in metal materials capable of withstanding plastic deformation but, in recent years, the interest in this technique has been increasing for the manufacture of complex polymer sheet components as an alternative to the conventional technologies, based on heating-shaping-cooling manufacturing routes. Conversely, incremental formed polymer sheets can suffer from some peculiar defects, for example twisting. To reduce the risk of this phenomenon and the occurrence of failures, a viable way is to choose toolpath strategies that make the tool/sheet contact conditions less severe, and this represents the main goal of the present research. Polycarbonate sheets were worked by incremental forming; in detail, cone frusta with a fixed wall angle were manufactured with a reference and a stair toolpath strategy, and both the forming forces and the twist angle were monitored. The analysis of the results highlighted that a stair toolpath involving an alternation of diagonal up and vertical down steps represents a useful strategy to mitigate the forming forces and, with them, the occurrence of the twisting phenomenon in incremental formed thermoplastic sheets.

Molecular detection of pathogens in clinical samples often requires pretreatment techniques, including immunomagnetic separation and magnetic silica bead (MSB)-based DNA purification to obtain the purified DNA of pathogens. These two techniques usually rely on handling small tubes containing a few millilitres of the sample and manual operation, implying that an automated system encompassing both techniques is needed for larger quantities of the samples. Here, we report a 3D-printed microfluidic platform that enables bacterial preconcentration and genomic DNA (gDNA) purification for improving the molecular detection of target pathogens in blood samples. The device consists of two microchannels and one chamber, which can be used to preconcentrate pathogens bound to antibody-conjugated magnetic nanoparticles (Ab-MNPs) and subsequently extract gDNA using magnetic silica beads (MSBs) in a sequential manner. The device was able to preconcentrate very low concentrations of pathogens and extract their genomic DNA in 10 mL of 10% blood within 30 min, and thus allowed polymerase chain reaction (PCR) and quantitative PCR to detect 1 colony forming unit of Escherichia coli O157:H7 in 10% blood. The results suggest that the 3D-printed microfluidic platform is highly useful for lowering the limitations on molecular detection in blood by preconcentrating the target pathogen and isolating its DNA in a large volume of the sample.

This study focuses on enhancing controllable fibrin-based hydrogels for tissue engineering, addressing existing weaknesses. By integrating a novel copolymer, we improve the foundation for cell-based angiogenesis with adaptable structural features. Tissue engineering often faces challenges like waste disposal and nutrient supply beyond the 200 µm diffusion limit. Angiogenesis breaks through this limitation, allowing the construction of larger constructs. Our innovative scaffold combination significantly boosts angiogenesis, resulting in longer branches and more capillary network junctions. The copolymer attached to fibrin fibers enables precise adjustment of hydrogel mechanical-dynamic properties for specific applications. Our material proves effective for angiogenesis, even under suppression factors like suramin. In our study, we prepared fibrin-based hydrogels with and without the copolymer PVP12400-co-GMA10mol%. Using a co-culture system of human umbilical vein endothelial cells (HUVEC) and mesenchymal stem cells (MSC), we analyzed angiogenetic behavior on and within the modified hydrogels. Capillary-like structures were reproducibly formed on different surfaces, demonstrating the general feasibility of three-dimensional endothelial cell networks in fibrin-based hydrogels. This highlights the biomaterial's suitability for in vitro pre-vascularization of biohybrid implants.

In this study, the impact of the addition of high-aspect-ratio nano-ettringite to photocurable epoxy acrylate resin was explored, with a specific focus on the changes observed in viscosity, shrinkage, tensile strength, and elongation at the break of composites formed. Herein, the nano-ettringite samples were modified using KH-570. The 3 wt% or 6 wt% KH-570-modified and unmodified nano-ettringite were dispersed into the resin by ultrasonic treatment in conjunction with mechanical stirring. The grafting effects of nano-ettringite onto KH-570 were analyzed through scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric (TG) analysis, and Fourier transform infrared spectroscopy (FTIR). The results demonstrate that increased dosages of unmodified and modified nano-ettringite led to increased viscosity of the composite while reducing shrinkage. At the same dosage, the photocurable resin with modified nano-ettringite demonstrated a lower shrinkage and a higher tensile strength. Notably, when the amount of modified nano-ettringite was 3 wt%, the highest tensile strength of the composite was 64.61 MPa, presenting a 72.57% increase compared to the blank sample. Furthermore, the incorporation of modified nano-ettringite as a filler provides a new perspective for improving the performance of photocurable epoxy acrylate resin composites.

Lignin is insoluble in water, limiting its use in the synthesis of adhesives. Therefore, in order to increase the amount of lignin raw materials used in the synthesis of adhesives, a kind of aminated lignin compounds was prepared through lignin amination reaction, and conducting structural analysis in this paper. The particle size of the amino lignin is about 100 nm, with the weight average molecular weight of 57,627 g/mol and a water solubility of 0.45g/100ml. The reaction mechanisms were proposed that the phenolic hydroxyl groups of lignin react with ammonia molecules, and thereby successfully introducing amino groups to generate the aminated lignin compounds. Therefore, this article enriches the scientific theory of lignin reactions and provides reference for the widespread application of lignin raw materials in the field of adhesives.

The affinity constant, also known as the equilibrium constant, binding constant, equilibrium association constant, or the reciprocal value, the equilibrium dissociation constant (K_d), can be considered as one of the most important characteristics for any antibody-antigen pair. Many methods based on different technologies have been proposed and used to determine this value. However, since a very large number of publications and commercial datasheets do not include this information, significant obstacles in performing such measurements seem to exist. In other cases where such data are reported, the results have often proved to be unreliable. This situation may indicate that most of the technologies available today require a high level of expertise that does not seem to be available in many laboratories. In this paper, we present a simple approach based on standard immunoassay technology that is easy and quick to perform. It relies on the effect that the molar IC₅₀ approaches the K_d value in the case of infinitely small concentrations of the reagent concentrations. A two-dimensional dilution of the reagents leads to an asymptotic convergence to K_d. The approach has some similarity to the well-known checkerboard titration used for the optimization of immunoassays. A well-known antibody against the FLAG peptide, clone M2, was used as a model system and the results were compared with other methods. This approach could be used in any case where a competitive assay is available or can be developed. The determination of an affinity constant should belong to the crucial parameters in any quality control of antibody-related products and assays and should be mandatory in papers using immunochemical protocols.

This work investigated the isothermal holding time dependence of the densification, microstructure, weight loss and tensile properties of Fe-Mn-Si powder compacts. Elemental Fe, Mn and Si powder mixtures with a nominal composition of Fe-28Mn-3Si (in weight percent) were ball milled for 5h and subsequently pressed under a uniaxial pressure of 400 MPa. The compacted Fe-Mn-Si powder mixtures were sintered at 1200 ℃ for 0, 1, 2 and 3 h, respectively. In general, the density, weight loss and tensile properties increased with the increase of isothermal holding time. A significant increase in density, weight loss and tensile properties occurred in the compacts isothermally holding for 1 h, as compared to those with no isothermal holding. However, further extension of isothermal holding time (2 and 3 h) only played a limited role in promoting the density and tensile properties. The weight loss of the sintered compacts was mianly caused by the sublimation of Mn in Mn depletion region on the surface layer of the sintered Fe-Mn-Si compacts. The length of the Mn depletion region increased as isothermal holding time increased. A single α-Fe phase was detected on the surface of all the sintered compacts, and the locations beyond the Mn depletion region were comprised of a dual dominant γ-austenite and minor ε-martensite.

In this work, we designed a MEMS device which allows simultaneous direct measurement of mechanical properties during deformation under external stress and characterization of the evolution of microstructure of nanomaterials within a transmission electron microscope. This MEMS device makes it easy to establish the correlation between microstructure and mechanical properties of nanomaterials. The device uses piezoresistive sensors to qualitatively measure the force and displacement of nanomaterials, e.g., in wire and thin plate forms. The device has a theoretical displacement resolution of 0.19 nm and a force resolution of 2.1 μN. The device has a theoretical displacement range limit of 2.74 μm and a load range limit of 27.75 mN.

Lap joints were friction stir welded in AA 7075-T6 at 1320 rpm and using two welding speeds: 70 mm/min and 120 mm/min. The temperature profiles of the weld zone were registered during the process; furthermore, the microhardness, tensile strength, and microstructure of the joints produced were examined. This study brings new insights into the thermomechanical behavior of the material during the process. The peak temperature obtained with the lower welding speed (70 mm/min) is 10% higher than that obtained with the higher speed (120 mm/min). Moreover, a 5% increase in microhardness and a 6% increase in tensile strength were were observed increasing the welding speed. Addition-ally, the microstructure examination demonstrated that, by decreasing the welding speed, the larger interaction between the tool and the material results in a deeper stir zone due to the increased heat diffusion downwards to the material. This heat flow affects the thermal profile and influences the resulting mechanical properties of the welded joints.

A new class of nano-cube core-shell heterostructures containing Ag coating on the top of WO₃ was fabricated. Physical vapor deposition was used to produce WO₃ based nano-heterostructures. All kind of wet toxic chemical process was avoided to make the process simple and contaminant free. Sputtering of WO₃ and a subsequent thermal annealing process was done to create nano-cubes of WO₃. After that, sputtering of Ag was performed to form the Ag-WO₃ core-shell nano-heterostructures (CSNH). The CSNHs were characterized using field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS), X-ray diffraction analysis (XRD) and UV-vis spectroscopy. The morphologies, elemental analysis, interfaces, crystallinity, phases, and chemical compositions were analyzed. The bottom-up growth of WO₃ nanocubes was studied using different time periods at 900°C. Ag coating was also studied before and after annealing. Finally, an optical property (band gap) was also analyzed using Tauc plot derive from absorption spectra. The tailoring the band gap of WO₃ from ~2.9eV to ~ 2.45 eV was observed while Ag-WO₃ CSNH formed.

In this study, an alternative method to conventional production methods involving thin section copper permanent mould casting (rapid solidification), hot rolling and heat treatment processes to manufacture AISI DC 53 cold work tool steel, has been investigated. In this new method, solidification of the AISI DC 53 was done in the thin section copper mould instead of traditional ingot casting. After solidification, thin slabs obtained was homogenized to 1150 ^oC and hold at this temperature for one hour and then hot rolling was be applied. During hot rolling process, about % 30 reduction in thickness of slab was obtained. After hot rolling, heat treatment (austenitizing, quenching and tempering) have been applied to thin slab. The samples have been taken as cast, as rolled and as heat treated (austenitized and tempered) and the microstructural analysis, hardness tests, retained austenite quantity measurement by XRD method have been performed. The heat treatment and tests have been performed for a commercially available AISI DC 53 which is manufactured by thick section ingot casting and rolling. Hardness values of the AISI DC 53 steels produced by traditional route is in the range of 52-54 HRC after austenitization at 1025 ^oC for one hour and quenched in compressed air and tempered twice at 525 ^oC for 120 mins. On contrary the permanent mould cast AISI DC 53 after homogenization at 1150 ^oC and immediately hot rolling then air cooling and austenitized at 1025 ^oC for one hour then quenched by compressed air and tempered twice at 525 ^oC for 120 mins have hardness valeus in the range of 55-57 HRC. Experiments have revealed that the properties of new rapid solidified steel in permanent copper mould are better than the commercially available steel and have a more refined microstructure than commercially produces alternative. Therefore, the new proposed method can be used as an alternative manufacturing method for cold-work tool steels.

Ledge formation presents a significant challenge in endodontic treatment. Yet, there is still a lack of educational tooth models for hands-on practice. This study aimed to create and evaluate a tooth model for ledge management practice. A natural tooth with curved roots was collected for scientific use under ethics committee approval. Following initial root canal preparation, the tooth was scanned using micro-computed tomography (μCT) and 3D reconstructed. A K-file, created via computer-aided design (CAD), was partly inserted into the root canal wall of the 3D-reconstructed tooth. By subtracting the K-file from the tooth, a tooth model with a root canal ledge was produced. The models were then 3D printed for a hands-on workshop. A seven-item Likert scale questionnaire was administered to 20 postgraduate students and 10 endodontists to assess the model's quality and training effectiveness. The feedback from both students and experts was positive, with no statistically significant differences found between the two groups (p &gt; 0.05). This novel tooth model is expected to address the existing gap in endodontic education and provide benefits for dental practitioners in future applications.

Recent years witnessed progressive broadening of the practical use of 3D-printed aluminium alloy parts, in particular for specific aerospace applications where weight saving is of great importance. Selective laser melting (SLM) is an intrinsically multi-parametric fabrication technology that offers multiple means of controlling mechanical properties (elastic moduli, yield strength, ductility) through the control over grains size, shape, and orientation. Ultimately, this approach implies that structural elements can be purposefully fabricated to reinforce specific zones and directions where higher mechanical loads are anticipated by design. Targeted control over mechanical properties is achieved through the tuning of 3D-printing parameters and may even obviate the need of heat treatment or mechanical post-processing. Systematic studies of grain structure for different printing orientation with the help of EBSD techniques in combination with mechanical testing at different dimensional levels are the necessary first steps to implement this agenda. Samples of 3D-printable Al-Mg-Si RS-333 alloy were fabricated in 3 orientations with respect to the principal build direction and the fast laser beam scanning direction. Sample structure and proper-ties were investigated using a number of techniques, including EBSD, in situ SEM tensile testing, roughness measurements and nanoindentation. The as-printed samples we found to display strong variation in Young’s modulus values from nanoindentation (from 43 to 66 GPa) and tensile tests (from 54 to 75 GPa), yield stress and ultimate tensile strength (100…195 and 130…220 MPa) in different printing orientations, and almost constant hardness of about 0.8 GPa. A further preliminary study was conducted of the effect of surface finishing on the mechanical performance. Surface polishing appears to reduce Young’s modulus and yield strength, but improves ductility, whereas the influence of sand blasting is more controversial. The experimental results are dis-cussed in connection with the grain morphology and orientation.

The aim of this study is to provide a detailed strategy for Safe-by-Design (SbD) 3D printed lab-on-a-chip (LOC) device manufacturing, using Fused Filament Fabrication (FFF) technology. At first, the applicability of FFF in lab-on-a-chip device development is briefly discussed. Subsequently, a methodology to categorize, identify and implement SbD measures for FFF is suggested. Furthermore, the most crucial health risks involved in FFF processes are examined, placing the focus on the examination of ultrafine particle (UFP) and Volatile Organic Compound (VOC) emission hazards. Thus, a SbD scheme for lab-on-a-chip manufacturing is provided, while also taking into account process optimization for obtaining satisfactory printed LOC quality. This work can serve as a guideline for the effective application of FFF technology for lab-on-a-chip manufacturing through the safest applicable way, towards a continuous effort to support sustainable development of lab-on-a-chip devices through cost-effective means.

The aim of this paper is to establish a valid procedure for better understanding all the phenomena associated with the high-speed machining of Glass Fibre Reinforced Plastic (GFRP) composites. Both rectangular and circular specimens were machined at high speeds (up to 50 m/min) in order to understand what occurred for all values of fiber orientation angles during machining operations. An innovative testing methodology was proposed and studied to investigate the phenomenon of burr formation and thus understand how to avoid it during machining operations. To this end, the forces arising during the machining process and the roughness of the resulting surface, were carefully studied and correlated with the cutting angle. Additionally, the cutting surface and chip morphology formed during cutting tests were examined using a high-speed camera. Close correlations are found between the variations of the cutting forces' signals and the trends of the roughness and the morphology of the machined surface.

Buckling defect will appear on the outer surface of the deformed ring during constrained ring rolling (CRR) of aluminum alloy thin wall conical ring with inner high ribs (AATWCRIHR), if the geometrical dimension of the ribs doesn't match the wall thickness. To avoid the buckling defect, a quantitative method for characterizing the degree of the buckling defect is proposed using the area of buckling profile. Then an orthogonal experimental scheme was designed taking the width of the middle rib, thickness of wall, and height of the middle rib as design variables and defining the area of buckling profile as optimization objective. Subsequently, a quadratic polynomial response surface model was established by combining the optimization algorithm with the finite element method (FEM), and the geometrical dimension of the middle ribs of the deformed AATWCRIHR is optimized. Also the optimal parameter combination to minimize the area of buckling profile is obtained and verified using FE simulation. Results show that the AATWCRIHR after optimization doesn’t generate the buckling defect during constrained ring rolling, and it is proved that the quantitative buckling defect representation method and the optimization design method based on the response surface model and the finite element simulation results are feasible for the constrained ring rolling process of the AATWCRIHR.

This article explores the cutting-edge advancement of gypsum and cement building boards infused with shape-stabilized n-octadecane, an organic phase change material (PCM). The primary focus is on improving energy efficiency and providing electromagnetic interference (EMI) shielding capabilities for contemporary buildings. The research investigates the integration of these materials into construction materials, using red-mud Carbon Foam as a stabilizer for n-octadecane (OD@CCF). Various analyses, including microstructural examination, porosity assessment, and additive dispersion, were conducted using X-ray microtomography and density measurements. Thermal conductivity measurements demonstrated the enhancement of composite boards as the OD@CCF content increased, while mechanical tests indicated an optimal additive content of up to 20%. The thermal-regulated capabilities of these advanced panels were evaluated in a custom-designed room model equipped with a homemade environmental chamber, illustrating a consistent temperature environment during heating and cooling cycles. The incorporation of OD@CCF into cement boards exhibited improved thermal energy storage properties. Moreover, the examined composite boards displayed efficient electromagnetic shielding performance within the frequency range of 3.2–7.0 GHz, achieving EMI values of approximately 18 and 19.5 dB for gypsum and cement boards, respectively, meeting the entry-level value required for commercial applications.

Inspired by recent developments in wave propagation and scattering experiments with parity-time (PT) symmetric materials, we discuss reciprocity and representation theorems for 3D inhomogeneous PT-symmetric materials and indicate some applications. We start with a unified matrix-vector wave equation which accounts for acoustic, quantum-mechanical, electromagnetic, elastodynamic, poroelastodynamic, piezoelectric and seismoelectric waves. Based on the symmetry properties of the operator matrix in this equation, we derive unified reciprocity theorems for wave fields in 3D arbitrary inhomogeneous media and 3D inhomogeneous media with PT-symmetry. These theorems form the basis for deriving unified wave field representations and relations between reflection and transmission responses in such media. Among the potential applications are interferometric Green’s matrix retrieval and Marchenko-type Green’s matrix retrieval in PT-symmetric materials.

The article offers a comprehensive overview of recent breakthroughs in eco-friendly polymers and polymer composites, underscoring their pivotal role in addressing sustainability challenges across diverse industrial sectors. Despite encountering obstacles related to performance and processability, biopolymers sourced from renewable materials emerge as promising alternatives for the plastics that are currently used by human beings. Natural fillers are highlighted as a strategic avenue for crafting sustainable composites, with residual natural fillers being particularly explored. Heightened environmental concerns propel discussions on the criticality of integrating biodegradable materials with natural fillers, underlining the urgency for clear frameworks and financial incentives to support adoption of these materials. Additionally, the article examines the potential of biodegradable polymers and polymer composites, with a specific emphasis on the utilization of polyhydroxyalkanoate (PHA) in composite materials and its market prospects. Moreover, it emphasizes the indispensable need for ongoing research and development endeavors to address environmental challenges within the polymer sector, reflecting a mounting interest in sustainable materials across industries.

Chitosan (CS) nanoparticles are under investigation for a wide range of applications in nanomedicine. The structural, molecular and physicochemical properties of chitosan nanoparticles have a direct bearing on their efficacy in drug conjugation and delivery, gene delivery, and tissue engineering. Herein we report on the structural, morphological and molecular properties of chitosan nanoparticles synthesized using the ionic gelation method with the intended purpose of being used for drug delivery. The chitosan nanoparticles (CS-NPs) were prepared in the 0.25 to 1.0% w/v concentration range, whereas separate samples of the 1.0% w/v CS-NPs were also functionalized with polyethylene oxide (PEO) alone and with a diblock copolymer of PEO and polypropylene glycol (PPG). The average size of the CS-NPs was determined from TEM imaging to be in the range of 11.3 to 14.8 nm. The XRD and TEM analyses show that the CS-NPs have semi-crystalline structure with the degree of crystallinity depending upon the nature of synthesis. Our results show that functionalizing the 1.0% w/v CS-NPs with PEO increases the degree of crystallinity whereas functionalizing with the diblock copolymer PEO - PPG results in a significant increase in their degree crystallinity. The CS/TPP concentration (CS:TPP fixed at 1:1 ratio) had no apparent effect on the degree of crystallinity of the CS-NPs. The results from the FTIR analysis confirm incorporation of TPP with CS in the CS-NPs. Additionally, FTIR analysis shows an enhancement of hydrogen bonding that is consistent with the increase in the degree of crystallinity of the CS-NPs.

In this paper, the synthesis of two novel luminescent Eu3+ ion complexes [Eu(TFT)3(phen) (1) and Eu(TFT)3(bpy)•Hex (2)] based on the combination of 2-(2,2,2-trifluoroethyl)-1-tetralone (TFT), containing n-donor ligands (1,10-phenanthroline or 2,2'-Bipyridine) and Eu3+ ion is reported herein, and their structural features are discussed on the basis of X-ray crystallographic and thermal analyses. We observed that the ligands transfer energy effectively to the metal center by fluorescence, IR and UV spectrograms studies. The structures and properties of complexes 1-2 were optimized by the DFT theoretical calculation, and the calculation results were consistent with the experimental X-ray structure data and spectral analysis.

This paper presents a proof-of-concept study on the biocolonization of 3D-printed hydroxyapatite scaffolds with mesenchymal stem cells (MSCs). Three-dimensional (3D) printed biomimetic bone structure made of Calcium Deficient HydroxyApatite (CDHA) intended as future bone graft was made from newly developed composite material for FDM printing. The biopolymer polyvinyl alcohol serves in this material as a thermoplastic binder for 3D molding of the printed object with a passive function and is completely removed during sintering. The study presents the material, the process of fused deposition modeling (FDM) of CDHA scaffolds and its post-processing at three temperatures (1200, 1300, 1400 °C), as well it evaluates the cytotoxicity and biocompatibility of scaffolds with MTT and LDH release assays after 14 days. The study also includes a morphological evaluation of the cellular colonization with scanning electron microscopy (SEM) in two different filament orientations (rectilinear and gyroid). The results of the MTT assay showed that the tested material was not toxic, and cells were preserved in both orientations, with most cells present on the material fired at 1300°C. Results of the LDH release assay showed a slight increase in LDH leakage from all samples. Visual evaluation of SEM confirmed the ideal post-processing temperature of the 3D-printed FDM framework for samples fired at 1300°C and 1400°C, with a porosity of 0.3 mm between filaments. In conclusion, the presented fabrication and colonization of CDHA scaffolds have great potential to be used in the tissue engineering of bones.