In this work, the solar light-induced redox photoactivity of the ZnO semiconductor material was used to prepare at room temperature CuxO-ZnO composite catalysts with a control of the chemical state of the copper oxide phase. The preparation of Cu2(I)O-ZnO and Cu(II)O-ZnO composite catalysts was achieved by using Cu(acac)2 in THF-water and Cu(NO3)2 in water as metallic precursor, respectively. Prior to the implementation of the photo-assisted synthesis method, the most efficient photoactive ZnO material was selected among different ZnO materials prepared by the low temperature polyol method and through the precipitation method with carbonates and carbamates as precipitation agent, by taking the photocatalytic degradation of the 4-chlorophenol compound in water under simulated solar light as model reaction. The ZnO support materials were characterized by XRD, BET, TGA, SEM and TEM, and the synthesis method was strongly influencing their photoactivity in terms of 4-chlorophenol degradation and of total organic carbon removal. The most photoactive ZnO material was prepared by precipitation with carbonates and calcined at 300°C, and was taking advantage of a high specific surface area and a small mean crystallite size for achieving a complete 4-chlorophenol mineralization within 70 min of reaction, with a minimum Zn2+ released to the solution due to surface photocorrosion. Beside thermal catalysis applications, this work opened a new route for the facile synthesis of Cu2O-ZnO heterojunction photocatalysts, that could take advantage under solar light of the heterojunction built between the p-type semi-conductor Cu2O with direct visible light band gap and the ZnO semiconductor phase.

In this study we have investigated the effect of the addition of Nb2O5 (up to 5 mol%) on the structure and luminescent properties of ZnO-B2O3 glass doped with 0.5 mol % Eu2O3 by using of infrared (IR), Raman and photoluminescence (PL) spectroscopy. Physical properties as molar volume, oxygen packing density and glass transition temperature were determined using the results of differential thermal analyisis (DTA) and Archimedes principle for density. IR and Raman spectra revealed that niobium ions incorporate into the base zinc borate glass as NbO4 trtraherda and NbO6 octahedra. A strong red emission from the 5D0 level of Eu3+ ions was registered under near UV (392 nm) excitation using the sharp 7F0 - 5L6 transition of Eu3+. The integrated fluorescence intensity ratio R (5D0 → 7F2/5D0 → 7F1) was calculated to estimate the degree of asymmetry around the active ion, suggesting a location of Eu3+ in non-centrosymmetric sites. The higher Еu3+ luminescence emission observed in zinc borate glasses containing 1÷5 mol% Nb2O5 compared to the Nb2O5-free zinc borate glass evidences that Nb2O5 is suitable component for modification of host glass structure and improving the emission intensity.

The use of nanoparticles as antimicrobial agents can be one of the strategies to overcome the tendency of microbes to become resistant to antibiotics’ action. In this study, two composites ZnO/Au and ZnO/Ag, having 1% wt. of noble metal content, were synthesized by simple aqueous solution methods. The structure and morphology of the resulting nanocomposites were analyzed by standard structural and optical characterization methods. The formation of Au NPs and Ag NPs in these experiments was also discussed. The antimicrobial properties of ZnO, ZnO/Au and ZnO/Ag nanomaterials were investigated against Gram-negative bacteria (Pseudomonas aeruginosa) and Gram-positive bacteria (Staphylococcus aureus). The electrostatic interaction between ZnO and noble metals nanoparticles have contributed to a better visible light adsorption, which led to an enhanced antimicrobial activity. The photocatalytic tests indicated an improvement in photocatalytic degradation of the methylene blue (MB) under UV irradiation using ZnO/Au and ZnO/Ag nanocomposites compared to bare ZnO. The introduction of noble metallic nanoparticles in ZnO matrix proved to be an effective strategy to increase their antimicrobial activity against P. aeruginosa and S. aureus and their photocatalytic activity evaluated through the degradation of MB dye. Comparing the enhancing effects of Au and Ag, it was found that ZnO/Au was a better antimicrobial agent while ZnO/Ag was more effective photocatalyst under UV irradiation.

Nanopowders are continuously under investigation as they open new perspectives in numerous fields. There are two main challenges to stimulate their development: sufficient low-cost high throughput synthesis methods leading to a production with well-defined and reproducible properties, and for ceramics, conservation of their nanostructure after sintering. In this context, this paper presents the synthesis of a pure nanosized powder of ZnO (dv₅₀ ~ 60 nm, easily redispersable) by using a continuous Segmented Flow Tubular Reactor (SFTR), which has previously shown its versatility and its robustness, ensuring a high powder quality and reproducibility over time. A higher scale of production can be achieved based on a “scale-out” concept by replicating the tubular reactors. The sinterability of ZnO nanopowders synthesized by the SFTR was studied, by natural sintering at 900 °C and 1100 °C, and Spark Plasma Sintering (SPS) at 900 °C. The performances of the synthesized nanopowder were compared to a commercial ZnO nanopowder of high quality. The samples obtained from the synthesized nanopowder could not be densified at low temperature by traditional sintering, whereas SPS led to a fully dense material after only 5 minutes at 900 °C, while limiting the grain growth and thus leading to a nanostructured material.

ZnO has many technological applications which largely depend on its properties that can be tuned by controlled synthesis. Ideally, the most convenient ZnO synthesis is carried out at room temperature in aqueous solvent. However, the correct temperature values are often loosely defined. In the current paper we performed synthesis of ZnO in aqueous solvent, by varying reaction and drying temperature by 10°C steps and monitored the synthesis products primarily by XRD. We found out that a simple direct synthesis of ZnO, without additional surfactant, pumping of freezing, required both a reaction (TP) and a drying (TD) temperature of 40°C. Higher temperatures also afford ZnO, but lowering any of the TP or TD below the threshold value results either in the achievement of Zn(OH)2 or in a mixture of Zn(OH)2/ZnO. A more detailed Rietveld analysis of the ZnO samples reveals a density variation with the synthesis temperature and an increase of the nanoparticles average size also verified by SEM images. The optical properties of ZnO obtained by UV-Vis reflectance spectroscopy indicate a red shift of the band gap by ~0.1 eV.

Functional ZnO nanostructured surfaces are important in a wide range of applications. Here we report facile fabrication of ZnO surface structures at near room temperature with morphology resembling that of sea urchins, with densely packed, μm-long, tapered nanoneedles radiating from the urchin centre. The ZnO urchin structures were successfully formed on several different substrates with high surface density and coverage, including silicon (Si), glass, polydimethylsiloxane (PDMS), and copper (Cu) sheets, as well as Si seeded with ZnO nanocrystals. Time-resolved SEM revealed growth kinetics of the ZnO nanostructures on Si, capturing the emergence of “infant” urchins at the early growth stage and subsequent progressive increase in the urchin nanoneedle length and density, whilst the spiky nanoneedle morphology was retained throughout the growth. ε-Zn(OH)₂ orthorhombic crystals were also observed alongside the urchins. The crystal structures of the nanostructures at different growth time were confirmed by synchrotron X-ray diffraction measurements. On seeded Si substrates, a two-stage growth mechanism was identified, with a primary growth step of vertically aligned ZnO nanoneedle arrays preceding the secondary growth of the urchins atop the nanoneedle array. The antibacterial, anti-reflective, and wetting functionality of the ZnO urchins—with spiky nanoneedles and at high surface density—on Si substrates was demonstrated. First, bacteria colonisation was found to be suppressed on the surface after 24 h incubation in Gram-negative E. coli culture, in contrast to control substrates (bare Si and Si sputtered with 20 nm ZnO thin film). Secondly, the ZnO urchin surface, exhibiting superhydrophilic property with a water contact angle ~0°, could be rendered superhydrophobic with a simple silanization step, characterised by a water static contact angle θ of 159° ± 1.4° and contact angle hysteresis ∆θ < 7°. The dynamic superhydrophobicity of the surface was demonstrated by bouncing-off of a falling 10 μL water droplet, with a contact time of 15.3 milliseconds (ms), captured using a high-speed camera. Thirdly, it was shown that the presence of dense spiky ZnO nanoneedles and urchins on the seeded Si substrate exhibited a reflectance R < 1% over the wavelength range λ = 200–800 nm. The ZnO urchins with unique morphology via a facile fabrication route at room temperature, readily implementable on different substrates, may be further exploited for multifunctional surfaces and product formulations.

ZnO was synthesized by Sol gel method using zinc nitrate as precursor at different calcination temperatures. Nucleation of ZnO crystallites and their growth with rise in temperature was observed. Exciton bands and lattice imperfections affected the absorption spectra. The decrease in band gap with temperature was due to the formation of defect energy levels. Phonon assisted non-radiative transitions caused broadening of the peaks. The possibility of tuning the band gap of ZnO by changing the temperature was explored. Simulation studies showed transition to single phase with rise in temperature.

Optical materials with a tunable localized surface plasmon resonance (LSPR) are of a great interest for applications in photonics and optoelectronics. In the present study we explored the potential of generating the LSPR band with an ultra-broad range of over 1000 nm in gold nanoparticles (NPs) precipitated through the thermal treatment in ZnO-Al2O3-SiO2 glass. Using the optical absorption spectroscopy, we demonstrated that the LSPR band's position and shape can be finely controlled by varying the thermal treatment route. Comprehensive methods including Raman spectroscopy, X-ray diffraction and high-resolution transmission electron microscopy were used to study the glass structure, while computational approaches were used for the theoretical description of the absorption spectra. Obtained results allowed us to suggest a scenario responsible for such abnormal LSPR band broadening which includes possible interparticle plasmonic coupling effect taking place during the liquid-liquid phase separation of the heat-treated glass. The formation of gold NPs with an ultra-broad LSPR band in glasses holds promise for sensitizing rare earth ion luminescence for new photonics devices.

In this work, a novel heterojunction based on ZnSnO3/ZnO nanofibers was prepared using electrospinning method. The crystal, structural and surface compositional properties of sample based on ZnSnO3 and ZnSnO3/ZnO composite nanofibers were investigated by X-ray diffractometer (XRD), Scanning electron microscope (SEM), X-ray photoelectron spectrometer (XPS) and Brunauer-Emmett-Teller (BET). Compared to pure ZnSnO3 nanofibers, the ZnSnO3/ZnO heterostructure nanofibers display high sensitivity and selectivity response with fast response towards ethanol gas at low operational temperature. The sensitivity response of sensor based on ZnSnO3/ZnO composite nanofibers were 19.6 towards 50 ppm ethanol gas at 225°C, which was about 1.5 times superior than that of pure ZnSnO3 nanofibers, which can be owed mainly to the presence of oxygen vacancies and the synergistic effect between ZnSnO3 and ZnO.

Zinc oxide (ZnO) nanostructures have been studied extensively in the past years due to the novel electronic, photonic, mechanical and electrochemical properties. Recently, more attention has been paid to assemble nanoscale building blocks into three dimensional (3D) complex hierarchical structures, which not only inherit the excellent properties of the single building blocks but also provide potential applications in the bottom-up fabrication of functional devices. This review article focuses on 3D ZnO hierarchical nanostructures, and summarizes major advances in the solution phase synthesis, applications in environment, and electrical/electrochemical devices. We present the principles and growth mechanisms of ZnO nanostructures via different solution methods, with an emphasis on rational control of the morphology and assembly. We then discuss the applications of 3D ZnO hierarchical nanostructures in photocatalysis, field emission, electrochemical sensor, and lithium ion batteries. Throughout the discussion, the relationship between the device performance and the microstructures of 3D ZnO hierarchical nanostructures will be highlighted. This review concludes with a personal perspective on the current challenges and future researches.

In this work, we report the engineering of a sub-70 nm nanocomposite of ZnO/Zn2TiO4 using a low-temperature solution-phase method. Titanium isopropoxide and zinc acetate were used as precursors, and isopropyl alcohol and water were used as solvents. The investigation focused on the growth of nanocomposites by varying the concentrations of precursors and surfactants, as well as their efficiency within different pH ranges. All three ZnO/Zn2TiO4 nanocomposites consist of hexagonal wurtzite ZnO and Zn2TiO4 structures in the three nanocomposites. The crystallite size in three ZnO/Zn2TiO4 nanocomposites, with a hexagonal wurtzite ZnO structure, were measured to be 62.67, 40.34, and 39.50 nm. The crystallite size values in three ZnO/Zn2TiO4 nanocomposites were 26.15 nm, 25.36 nm, and 21.24 nm, respectively, with Zn2TiO4. Morphological observations, conducted using FESEM, reveal the formation of three ZnO/Zn2TiO4 nanocomposites across the entire sample. These nanocomposites resemble dispersed cotton packets, with sizes ranging from 18 to 350 nm. Peaks in the range of 610-1250cm-1 are attributed to Ti-O bond formation and peak located at 1350-1450 cm-1 are attributed to Zn-O bond formation. Also, EDX spectrum reveals peaks for various sample components such as Ti, O and Zn. UV spectrums confirmed the formation of three nanocomposite of ZnO/Zn2TiO4 as showing two peaks for each sample. Photocatalytic investigation carried out by analyzing the UV-Visible absorption spectra of methylene blue dye on the surface of ZnO/Zn2TiO4 nanocomposites, dye degradation at various irradiation time intervals, dye degradation at varied catalyst concentrations and the influence of pH on dye-degradation. Furthermore, the said nanocomposites were used to degrade environmental pollutant (Methylene blue dye). Different sets of experiments were conducted under ambient conditions which show an excellent photo catalytic degradation efficiency.

The surface behavior of the ZnO-based films could be modulated via a postannealing and ultraviolet (UV) irradiation with different powers and time, respectively. These present results could provide modulate the microstructure related in grain-size distribution and photocatalytic behavior for potential guide in the field of wide bandgap semiconducting oxides. The ZnO films were prepared onto Corning-1737 glass substrates by using radio-frequency magnetron sputtering without supplying oxygen source at room temperature. For the purpose of obtaining modulable grain microstructures, the as-prepared ZnO films (Z0) were treated via a postannealing modification in vacuum furnace at 300°C for 30 minutes after deposition (Z300) accompanied with the adjustable internal stress. The contact angle (CA) value of ZnO film reduced from 95° to 68° was owning to the different grain microstructure accompanied by a change in size variation. In addition, the UV light with different irradiation powers could also be used to improve the hydrophilicity varied from hydrophobic status to superhydrophilic status due to the desirable surface characteristics of the photocatalytic action. In addition, the photocatalytic activity of ZnO film exhibited efficient photodegradation of methylene blue (MB) under UV irradiation, with a chemical reaction constant of 2.93×10-3 min−1. In this present work, we demonstrated that the CA value of the ZnO films not only caused from hydrophobic to hydrophilic status accompanied by a change in grain size combined with internal stress but also induced by the UV light irradiation combined with photocatalytic activity simultaneously. On the other hand, the enhanced surface plasmonic resonance could be observed that is due to couple electron and photon oscillations and can be generated at the interface between a flat, continuous Pt capping nanolayer. This designed structure could also be considered as a Pt electrode pattern onto ZnO (metal Pt/ ceramic ZnO) for multifunctional heterostructured sensors and devices in near future.

CuO-ZnO-Al2O3 catalysts are designed for the low-temperature shift conversion in the process of hydrogen and ammonia synthesis gas production. The paper presents the results of research on recovery of copper and zinc from spent catalysts using pyrometallurgical and hydrometallurgical methods. Under reducing conditions, at high temperature, having appropriately selected the composition of the slag, more than 66% of copper in metallic form and about 70% of zinc in the form of ZnO can be extracted from this material. Hydrometallurgical processing of the catalysts was carried out using two leaching solutions: alkaline and acidic. Almost 62% of the zinc contained in the catalysts has been leached to the alkaline solution and about 98% of copper has been leached to the acidic solution. After the hydrometallurgical treatment of the catalysts, insoluble residue was also obtained in the form of pure ZnAl2O4. This compound can be reused to produce catalysts, or it can be processed under reducing conditions at high temperature to recover zinc. The recovery of zinc and copper from such a material is consistent with the policy of sustainable development and helps to reduce the environmental load of stored wastes.

In this work, we report on the first attempt using size-controlled ZnO nanoparticles (NPs) to analyze role of thioacetamide (TAA) in forming ZnS nanostructures from ZnO. The size-controlled B(blue)_, G(green)_, Y(yellow)_ZnO QDs, and NC (nanocrystalline)_ZnO NPs were synthesized by sol-gel process as well as hydrothermal method, respectively and then reacted with an ethanolic TAA solution as sulfur source. After reacting with TAA, the formation of ZnS QDs was observed over time. The chemical reactions were identified using X-ray diffraction (XRD), Transmission Electron Microscope (TEM), UV-vis spectroscopy, and Photoluminescence (PL). All results indicate that ZnS formation is due to direct crystal growth and/or chemical conversion of ZnO to ZnS. Our results enable a broader understanding of the synthetic mechanisms involved in the use of TAA as a sulfur source in forming ZnS nanostructures from ZnO.

Infrared sensors incorporating suspended zinc oxide (ZnO) pyroelectric films and thermally-insulated silicon substrates are fabricated using conventional MEMS-based thin-film deposition, photolithography, and etching techniques. The responsivity of the pyroelectric film is improved through annealing at 500℃ for 4 h. The voltage response of the fabricated sensors is evaluated experimentally for a substrate thickness of 1 µm over a sensing range of 30 cm. The results show that the voltage signal varies as an inverse exponential function of the distance. A positioning system based on three infrared sensors is implemented in LabVIEW. It is shown that the position estimates obtained using the proposed system are in excellent agreement with the actual locations. In general, the results presented in this study provide a useful source of reference for the further development of MEMS-based pyroelectric infrared sensors.

Artemisia absinthium (A. absinthium) leaf extract was successfully used to create zinc oxide nanoparticles (ZnO NPs), and their properties were investigated via several techniques, including X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX), Fourier transform infrared (FTIR), and UV–Vis spectroscopy. SEM analysis confirmed the spherical and elliptical shapes of the particles. Three different zinc peaks were observed via EDX at energies of 1, 8.7, and 9.8 keV, together with a single oxygen peak at 0.5 keV. XRD analysis identified ZnO NPs as having a hexagonal wurtzite structure with a particle size that decreased from 24.39 to 18.77 nm, and with an increasing surface area (BET) from 4.003 to 6.032 m2/g for the ZnO (without extract) and green ZnO NPs, respectively. FTIR analysis confirmed the groups of molecules that were accountable for stabilizing and minimizing the ZnO NPs, which was apparent at 3400 cm. Using UV–Vis spectroscopy, the band gap energies (Egs) for the green ZnO and ZnO (without extract) NPs were estimated, and the values were 2.65 and 2.79 eV, respectively.

This study describes an eco-friendly synthesis of ZnO nanoparticles using aqueous oat extract. The advanced electrochemical and optical features of green synthesized ZnONPs displayed excellent antibacterial activity, and exhibited an important role in pharmaceutical determinations. The formation of nanoscale ZnO was confirmed using various spectroscopic and microscopic investigations. The formed nanoparticles were found to be around 100 nm. The as-prepared ZnONPs were monitored for their antibacterial potential against different bacterial strains. The inhibition zones for ZnONPs were found as E. coli (16 mm), P. aeruginosa (17 mm), S. aureus (12 mm) and B. subtilis (11 mm) using 30 µg mL-1 sample concentration. Also, ZnONPs exhibited significant antioxidant effects 58 to 67 % with an average IC50 value of 0.88 ± 0.03 scavenging activity and 53 to 71 % (IC50 value 0.73 ± 0.05) against the DPPH and ABTS scavenging free radicals, respectively. The photocatalytic potential of ZnONPs for Rhodamine B dye degradation dye under UV irradiation was performed. The photodegradation process was carried out as a function of time-dependent and the complete degradation (nearly 98 %) with color removal after 120 min. Conclusively, the synthesized ZnONPs using oat biomass might provide a great promise in the future for biomedical applications.

Ga doped ZnO thin films were formed by the Ultrasonic Chemical Spray Pyrolysis method onto substrates using zinc acetate and gallium (III) nitrate hydrate as precursors. The structural, optical, surface and electrical properties were studied as a function of increasing Ga doping concentration from 0 to 6 at %. Structural studies were shown polycrystalline with a hexagonal crystal structure. The transparency in the visible range was around 85% for thin film deposited using 6 at % Ga doping. With the aim of determining surface images and surface roughness of the films atomic force microscope images were taken. Ga doping of ZnO thin films could markedly decrease surface roughness. Electrical resistivity was determined by four point method. The resistivity 2.0% Ga doped ZnO film was the lowest resistivity of 1.7 cm. In the photoluminescence measurements of the films, existence of UV and defect emission band was observed. As a result, Ga doped ZnO films have advanced properties and promising materials for solar cells.

This work emphasizes to use silver decorative method to enhance the antibacterial activity of TiO₂ and ZnO nanoparticles. These silver decorated nanoparticles (hybrid nanoparticles) were synthesized by using sodium borohydride as a reducing agent, with the weight ratio of Ag precursors: oxide nanoparticles = 1: 30. The morphology and optical property of these hybrid nanoparticles were investigated using transmission electron microscopy (TEM) and UV–vis spectroscopy. The agar-well diffusion method was used to evaluate their antibacterial activity against both Staphylococcus aureus and Escherichia coli bacteria, with or without light irradiation. The TEM images indicated clearly that silver nanoparticles (AgNPs, 5-10 nm) were well deposited on the surface of nano-TiO₂ particles (30-60 nm). Besides, smaller AgNPs (< 2 nm) were dispersed on the surface of nano-ZnO particles (20-50 nm). UV-vis spectra confirmed that the hybridization of Ag and oxide nanoparticles led to shift the absorption edge of oxide nanoparticles to the lower energy region (visible region). The antibacterial tests indicated that both oxide pure nanoparticles did not exhibit inhibitory against bacteria, with or without light irradiation. However, the presence of AgNPs in their hybrids, even at low content (< 40 mg/mL) leads to a good antibacterial activity and the higher inhibition zones under light irradiation as compared to that in dark was observed.

Owing to fascinating applications of ZnO in modern devices, it is interesting to explore its more features for future devices. Hence, herein, we have synthesized the high quality ZnO spherical nanoparticles (SNPs) through a facile green synthesis route and robust structural and biomedical studies are carried out. Hexagonal phase with 93.2% crystallinity was confirmed through XRD analysis. ZnO nanoparticles were tested for their bioactivities both in vivo (acute cytotoxicity test) and in vitro (Anti-cancer activities on liver (HepG2) and cervical (Hela) cancer cell lines, stimulatory/inhibitory effects on normal rat splenic cells and hemolytic effects on red blood cells). Results showed that ZnO SNPs has no cytotoxic effects on vital organ like liver and has no hemolytic action on red blood cells. ZnO SNPs showed inhibitory consequence on normal rat splenic cells growth at all tested concentrations. ZnO nanoparticles showed an inhibitory effect on HepG2 cell line. While showed stimulatory effect on Hela cell line. Current study presents the synthesized ZnO SNPs as highly applicable in bio-optoelectronics.

In this paper, we present a study of various ZnO/SiO2-stacked thin film structures for flexible micro-energy harvesting devices. Two groups of micro-energy harvesting devices, SiO2/ZnO/SiO2 micro-energy generators (SZS-MGs) and ZnO/SiO2/ZnO micro-energy generators (ZSZ-MGs), were fabricated by stacking both SiO2 and ZnO thin films, and the resulting devices were characterized. With a particular interest in the fabrication of flexible devices, all the ZnO and SiO2 thin films were deposited on ITO-coated PEN substrates using an RF magnetron sputtering technique. The effects of the thickness and/or position of the SiO2 films on the device performance were investigated by observing the variations of output voltage in comparison with that of a control sample. As a result, compared to the ZnO single-layer device, all the ZSZ-MGs showed much better output voltages, while all the SZS-MG showed only slightly better output voltages. Among the ZSZ-MGs, the highest output voltages were obtained from the ZSZ-MGs where the SiO2 thin films were deposited using a deposition power of 150 W. Overall, the device performance seems to depend significantly on the position as well as the thickness of the SiO2 thin films in the ZnO/ SiO2-stacked multilayer structures, in addition to the processing conditions.

ZnO thin films with a thickness of 300 nm were deposited on Si and Al2O3 substrates using electron beam evaporation technique with the aim to be tested as low cost and low power consumption gas sensors for ozone (O3). To characterize the surface roughness and the grain size, which are the main parameters recognized to enhance gas sensitivity since they directly influence the effective sensing area, surface morphology and roughness analyses of the films were performed using scanning electron microscopy and atomic force microscopy, respectively. The crystalline structure and elemental composition were studied through Raman spectroscopy and X-ray photoelectron spectroscopy. Gas tests were conducted at room temperature and zero-bias voltage to assess the sensitivity and response as a function of time of the films to O3 pollutant. The results indicate that the films deposited on Al2O3 exhibit promising characteristics, such as high sensitivity and a very short response time (< 2 s) to the gas concentration. Additionally, it was observed that the films display pronounced degradation effects after a significant exposure to O3.

Building heterojunction is promising strategy for the achievement of highly efficient photocatalysis. In this study, a novel SnIn4S8@ZnO Z-scheme heterojunction with tight contact interface was successfully constructed through a facile two-step hydrothermal method. The phase composition, morphology, and photophysical properties of SnIn4S8@ZnO were studied through a series of characterization methods, respectively. Methylene blue (MB) was selected as the target pollutant for photocatalytic degradation and the degradation process was fitted with pseudo-first order kinetics. The as-prepared SnIn4S8@ZnO heterojunctions exhibited outstanding photocatalytic activities for the degradation of MB. The optimized sample (ZS800), in which the molar ratio of ZnO to SnIn4S8 was 800, displayed the highest photodegradation efficiency of MB (91%) within 20 min. Furthermore, the apparent rate constant of photodegradation for MB of ZS800 (0.121 min−1) was 2.2 times higher than that of pure ZnO (0.054 min−1). The improvement of photocatalytic activity could be attributed to the effective spatial separation of photogenerated charge carriers through a Z-scheme heterojunction with intimate contact interface. This work will provide a new insight into constructing excellent ZnO-based photocatalytic systems for wastewater purification.

Zinc oxide (ZnO) has been widely studied over the last decade for its remarkable properties in optoelectronic and photovoltaic devices because of its high electron mobility and excitonic properties, probably the broadest range of nanostructured forms, and their ease and low cost of synthesis by a wide variety of methods. The volume of recent work on ZnO nanostructures and their devices can potentially overshadow significant developments in the field. Therefore, there is a need for a concise description of the most recent advances in the field. In this review, we focus on the effect of ZnO nanostructure morphologies on the performance of ZnO-based solar cells sensitized using methylammonium lead iodide perovskite. We present an exhaustive discussion of the synthesis routes for different ZnO nanostructure morphologies, ways to control the morphology, and the impact of morphology on the photo-conversion efficiency of a given PSC.

Abstract The construction of a heterostructured nanowire array allows the manipulation of the interfacial, surface, charge transport, and transfer properties simultaneously, offering new opportunities to achieve multi-functionality for various applications. Herein, we developed a facile thermal evaporation and post-annealing method to synthesize ternary-Zn2SnO4/binary-ZnO radially heterostructured nanowire arrays (HNA). Vertically aligned ZnO nanowire arrays (3.5 μm in length) were grown on a ZnO-nanoparticle-seeded fluorine-doped tin oxide substrate by a hydrothermal method. Subsequently, the amorphous layer consisting of Zn-Sn-O complex was uniformly deposited on the surface of the ZnO nanowires via the thermal evaporation of the Zn and Sn powder mixture in vacuum, followed by post-annealing at 550 °C in air to oxidize and crystallize the Zn2SnO4 shell layer. The use of a powder mixture composed of elemental Zn and Sn (rather than oxides and carbon mixture) as an evaporation source ensures high vapor pressure at a low temperature (e.g., 700 °C) during thermal evaporation. The morphology, microstructure, and charge-transport properties of the Zn2SnO4/ZnO HNA were investigated by scanning electron microscopy, X-ray diffraction, Raman spectroscopy, transmission electron microscopy, and electrochemical impedance spectroscopy. Notably, the optimally synthesized Zn2SnO4/ZnO HNA shows an intimate interface, high surface roughness, and superior charge-separation and -transport properties compared with the pristine ZnO nanowire array.

Metal oxide p-n heterojunction nanofibers (NFs) are among the most promising approaches to enhancing the efficiency of gas sensors. In this paper, we report the preparation of a series of p-NiO-loaded n-ZnO NFs, namely (1 − x) ZnO-xNiO (x = 0.03, 0.05, and 0.1 wt%), for hydrogen gas sensing experiments. Samples were prepared through the electrospinning technique followed by a calcination process. The sensing experiments showed that the sample with 0.05 wt% NiO loading resulted in the highest sensing performance at an optimal sensing temperature of 200 °C. The sensing mechanism is discussed in detail and contributions of the p-n heterojunctions, metallization of ZnO and catalytic effect of NiO on the sensing enhancements of an optimized gas sensor are analyzed. This study demonstrates the possibility of fabricating high-performance H₂ sensors through the optimization of p-type metal oxide loading on the surfaces of n-type metal oxides.

Managing severe bleeding, particularly in soft tissues and visceral injuries, remains a significant challenge in trauma and surgical care. Traditional hemostatic methods often fall short in wet and dynamic environments. This study addresses the critical issue of severe bleeding in soft tissues, proposing an innovative solution using a Polyethylene Glycol (PEG)-based hydrogel combined with zinc oxide (ZnO). The developed hydrogel forms a dual-network structure through amide bonds and metal ion chelation, resulting in enhanced mechanical properties and adhesion strength. The hydrogel, exhibiting excellent biocompatibility, is designed to release zinc ions, promoting coagulation and accelerating hemostasis. Comprehensive characterization, including gelation time, rheological properties, microstructure analysis, and swelling behavior, demon-strates the superior performance of the PEG/ZnO hydrogel compared to traditional PEG hydro-gels. Mechanical tests confirm increased compression strength and adhesive properties, crucial for withstanding tissue dynamics. In vitro assessments reveal excellent biocompatibility and en-hanced procoagulant ability attributed to ZnO. Moreover, in vivo experiments using rat liver and tail bleeding models demonstrate the remarkable hemostatic performance of the PEG/ZnO hy-drogel, showcasing its potential for acute bleeding treatment in both visceral and peripheral sce-narios.

Developing a biomolecular detection method that minimizes photodamage while maintaining an environment suitable for biological constituents to maintain their physiological state is expected to drive new diagnostic and mechanistic breakthroughs. In addition, ultra-sensitive diagnostic platforms are needed for rapid and point-of-care technologies for various diseases. Considering this, surface-enhanced Raman scattering (SERS) is proposed as a non-destructive and sensitive approach to address the limitations of fluorescence, electrochemical, and other optical detection techniques. However, to advance the applications of SERS, novel approaches to enhance the signal of substrate materials are needed to improve reproducibility and costs associated with manu-facture and scale-up. Due to their physical properties and synthesis, semiconductor-based nanostructures have gained increasing recognition as SERS substrates; however, low signal en-hancements have offset their widespread adoption. To address this limitation and assess the po-tential for use in biological applications, zinc oxide (ZnO) was coated with different concentra-tions (0.01-0.1 M) of gold (Au) precursor. When crystal violet (CV) was used as a model target with the synthesized substrates, the highest enhancement was obtained with ZnO coated with 0.05 M Au precursor. This substrate was subsequently applied to differentiate exosomes derived from three cell types to provide insight into their molecular diversity. We anticipate this work will serve as a platform for colloidal hybrid SERS substrates in future bio-sensing applications.

The presented work studies the processes of synthesis of nitrogen-containing structures of ZnO using atmospheric pressure microwave nitrogen plasma and investigates their photocatalytic activity in the processes of degradation of 2,4-dinitrophenol and the antibiotic ciprofloxacin when irradiated with sunlight. The work proposes an effective method for formation of photosensitive ZnO powders. Due to the features of plasma treatment in the open atmosphere of zinc metal microparticles, ZnO structures are formed with sizes from hundreds of nanometers to several micrometers with various micromorphologies. High photoactivity was demonstrated (rate constants 0.036 min-1 and 0.051 min-1) of synthesized ZnO structures during photo-degradation of 2,4-dinitrophenol and ciprofloxacin, respectively, when exposed to solar radiation. Photo-active structures of ZnO synthesized using microwave nitrogen plasma can find application in processes of mineralization of toxic organic compounds.

The electronic, optical, and magnetic properties of Nd-doped ZnO systems were calculated using the DFT/GGA+U method. According to the results, the Nd dopant causes lattice parameter expansion, negative formation energy, and bandgap narrowing, resulting in the formation of an n-type degenerate semiconductor. Overlapping of the generated impurity and Fermi levels results in a significant trap effect that prevents electron-hole recombination. The absorption spectrum demonstrates a redshift in the visible region and improved intensity, leading to enhanced photocatalytic performance. The Nd-doped ZnO system displays ferromagnetic, with FM coupling due to strong spd-f hybridization through magnetic exchange interaction between the Nd-4f state and O-2p, Zn-4s, and Zn-3p states. These findings imply that Nd-doped ZnO may be a promising material for DMS spintronic devices.

Although 4Ce4YSZ has high corrosion resistance, it faces challenges concerning sinterability and ionic conductivity. Therefore, we studied destabilization behavior caused by corrosion and oxygen vacancy ordering according to ZnO doping. The powders of (4Ce4YSZ)1-x(ZnO)x (x=0.5, 1, 2, 4 mol%) were synthesized through the sol-gel method. With the addition of ZnO, the cubic phase increased, and secondary phases were not observed. The (111) peak showed a higher angle shift in ZnO-doped 4Ce4YSZ compared to 4Ce4YSZ, and TEM-SAED revealed a reduction in the spacing of the (011)t plane, suggesting lattice contraction due to the substitution of the smaller Zn2+ (60 Å) for Zr4+ (84 Å) in the lattice. The local atomic structure analysis was conducted using EXAFS to investigate the oxygen vacancy ordering behavior. Zr K-edge Fourier-transform data revealed a decrease in the Zr-O1 peak intensity with an increasing amount o ZnO doping, indicating an increase in oxygen vacancies. The Zr-O1 peak position shifted to the right, leading to an increase in the Zr-O1 interatomic distance. In the Y K-edge Fourier-transform data, the Y-O1 peak intensity did not decrease, and there was little variation in the Y-O1 interatomic distance. These results suggest that the oxygen vacancies formed due to ZnO doping are located in the neighboring oxygen shell of Zn, rather than in the neighboring oxygen shells of Y and Zr. Impedance measurements were conducted to measure the conductivity, and as the amount of ZnO doping increased, the total conductivity increased, while the activation energy decreased. The increase in oxygen vacancies by ZnO doping contributed to the enhancement of conductivity and it is considered that these created oxygen vacancies did not interact with Zn2+ and did not form defect associations. Fluoride-based molten salts were introduced to the specimens to assess corrosion behavior in a molten salt environment. Yttrium depletion layers (YDLs) were formed on the surfaces of all specimens due to the leaching of yttrium. However, Ce remained relatively stable at the interface according to EDS line scans, suggesting a reduction in the phase transformation (cubic, tetragonal to monoclinic) typically associated with yttrium leaching in YSZ.

In this work, the adsorption and photocatalytic properties of ZnO-ZnAl2O4 nanosized composites synthesized by the polymer-salt method have been studied. To evaluate the efficiency of adsorption, experiments were carried out on the decolorization of aqueous solutions of the Chicago Sky Blue diazo dye. The adsorption process is divided into two stages, at the first stage the dye is rapidly adsorbed on the outer surface of the composite particles, at the second stage the dye diffuses into the pores of the material. It was noted that the rate of photocatalytic decomposition of the dye is higher than the rate of the adsorption process, which indicates the occurrence of photocatalytic decomposition of dye molecules both on the surface of the composites and in the liquid phase. With an increase in the light intensity, the photocatalytic process is significantly accelerated, linearly at low intensities, and at high intensities the dependence becomes a power law.

This review article provides useful information on TiO2 and ZnO photocatalysts and their derivatives in removing organic contaminants such as different types of dyes, hydrocarbons, pesticides, etc. Also, the reaction mechanism of TiO2 and ZnO photocatalysts and their derivatives was investigated. In addition, the impact of adding metallic (e.g., Ag, Co, Pt, Pd, Cu, Au, Ni) and non-metallic (e.g., C, N, O, S) dopants to their structure on the photodegradation efficiency of organic compounds was thoroughly studied. Moreover, advantages and disadvantages of various synthesis procedures of ZnO and TiO2 nanocatalysts were discussed and compared. Furthermore, the impact of photocatalyst dosage, photocatalyst structure, contaminant concentration, pH, light intensity and wavelength, temperature and reaction time on the photodegradation efficiency was studied. According to previous studies, adding metallic and non-metallic dopants to the TiO2 and ZnO structure led to a remarkable enhance in their stability and reusability. Besides, doped TiO2 and ZnO demonstrated remarkable photocatalytic efficiencies in eliminating various types of organic contaminants.

In this research work, we describe the preparation process, characterization, and photo-physical studies of an ionic liquid (IL) based semiconductor Zinc Oxide (ZnO) nanoparticles synthesized by an economical wet chemical precipitation method. For the first time, an IL was synthesized with the help of a chemical reaction between triethylamine (TEA) and bromoacetic acid (BAA). A polyamide dye was prepared by a reaction between two monomers, ethylenediamine (EDA) and trimesoylchloride (TMC), under room temperature conditions. The polyamide dye was capped on ZnO nanoparticles, and the final product was divided into three different samples, A, B, and C, according to level of concentrations of IL and Polyamide dye. These samples were characterized with X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM), Dynamic Light Scattering (DLS) spectra, Ultraviolet-Visible (UV-Vis), and Fluorescence spectroscopies. The formation of polyamide linkages in the ionic liquid has been confirmed by a spectroscopic method using Fourier Transform Infrared (FTIR) spectroscopy. The capping of polyamide dye molecules on the surface of ZnO nanoparticles revealed two things: (i) improved UV absorption spectra and (ii) enhanced luminescence in the photoluminescence spectra. Hence, during investigations, broad absorption bands were observed at peaks 263 nm, 278 nm, and 276 nm respectively for samples A, B, and C. Further, IL was used as an electrolyte or redox mediator and polyamide as a dye material in the fabrication of ZnO Dye-Sensitized Solar Cells (DSSCs). The samples A, B, and C were used in the fabrication of photo-anode assemblies for ZnO DSSCs. The ZnO DSSCs were tested under strong simulated light at Air Mass (AM) 1.5 solar irradiations. The observed photovoltaic results shown that solar cell SCB generated a maximum power conversion efficiency (η) of 5.65%, higher than the power conversion efficiencies of solar cells SCA (3.99%) and SCC (4.46%) respectively. The Incident Photon to Current Conversion Efficiency (IPCE) spectra values of ZnO DSSCs shown a significant improvement in the incident photon to current conversion efficiency of solar cell SCB (IPCE=61%) as compared to SCC (enhanced by 6%) and SCA (enhanced by 4%). Such solar cell assemblies can be suitable for green and clean energy applications.

A series of ZnO doped nitrogen-carbon materials (xZnO-N-C) with ZnO content of 5-40% are prepared by vacuum curing-carbonization strategy using polyamide-imide as N-C source and zinc nitrate as metal source for propane dehydrogenation (PDH). 20ZnO-N-C exhibits outstanding initial activity (propane conversion of 35.2% and propene yield of 24.6%) and relatively low deactivation rate (0.071 h-1) at 600 ◦C. The detailed characterization results show that small ZnO nanoparticles (5.5 nm) with high dispersion on the catalyst could be obtained by adjusting ZnO loading. Moreover, much more nitrogen-based species especially ZnNx species are formed on 20ZnO-N-C by comparison with 20ZnO-N-C-air prepared by curing-carbonization without vacuum, which may contribute for the higher product selectivity and catalytic stability of 20ZnO-N-C. The probable active sites for PDH reaction on the catalyst system are proposed to be C=O species and Zn2+ species. Moreover, the aggregation of ZnO nanoparticles is the primary reason for the activity loss on this catalyst system. The present finding not only provides the feasible construction strategy for the metal oxide doped nitrogen-carbon materials but also valuable guidance for the design of efficient catalyst in dehydrogenation of light alkane.

A comparative analysis of the features of UV- stimulated emission (SE) of various types of disorder active materials based on ZnO crystallites for a random laser (RL) was carried out. The superlinear increase in the intensity of the UV photoluminescence (PL) band of polydisperse nano- microcrystalline (PNMC) ZnO powder at a wavelength of λ = 387 nm and some narrowing of its half-width in the range of 20-15 nm with increasing pump intensity indicate random lasing with incoherent feedback (FB). Properties of similar UV PL bands under the same conditions from a thin film containing hexagonal ZnO microdisks, as well as samples of monodisperse ZnO nanopowder indicate stimulated emission with coherent feedback. It is shown that, among the studied materials, the PNMC ZnO powder with crystallites contained nano-grains with is the most suitable for creating a laser with incoherent feedback at room temperature. The dominant factor of UV SE in PNMC ZnO powder is radiation transitions under exciton - exciton scattering conditions. The possible mechanisms of this random emission with the continuous spectrum are discussed. The average optical gain coefficient αg at λ = 387 nm in this RL system is estimated, as αg ~ 150 cm-1.

This study presents of the microsphere-based fiber-optic sensor with the ZnO ALD coating thickness of 100 nm and 200 nm for temperature measurements. Metrological properties of the sensor were investigated over the temperature range of 100°C to 300°C, with a 10°C step. The interferometric signal is used to control whether the microstructure is intact. Spectrum shift of a reflected signal is used to conclude changes in measured parameter for the sensor with a 100 nm coating, while the reflected signal intensity is an indicator during measurements executed by a sensor with a 200 nm coating. With changing temperature, the peak position or intensity of a reflected signal also changes. The R2 coefficient of the presented sensors indicates a linear fit of over 0.99 to the obtained data. The sensitivity of the sensors, investigated in this study, equals 103.5 nW/°C and 0.019 nm/°C for ZnO thickness of 200 nm and 100 nm, respectively.

Synthesis of poly(o-phenylenediamine) (PoPD) and poly(o-phenylenediamine)-ZnO (PoPD-ZnO) nanocomposites on carbon steel by in-situ polymerization with HCl acid as doping acid Material coating. The composition and structure of PoPD-ZnO nanocomposites were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The corrosion protection ability of polymer coatings in 3.5% NaCl was studied by potentiodynamic polarization curves and electrochemical impedance spectroscopy. It can be seen from the electrochemical corrosion experimental data that PoPD-WPU coating (PWC) and PoPD-ZnO-WPU coating (PZWC) can effectively improve the corrosion resistance of the carbon steel substrate, and the corrosion rate is reduced by 2-3 orders of magnitude compared with carbon steel. The conclusion demontrates that PoPD can effectively extend the service life of carbon steel substrates. In addition, it is advantageous to form a compact and low-defect coating when added nano-particle ZnO, which is advantageous for the POPD film to develop its good barrier property and corrosion resistance.

In this work, we report the fabrication of the new heterojunction of two 2D hybrid layered semiconductors, ZnO(stearic acid)/V₂O₅(hexadecylamine), and its behavior in the degradation of aqueous methylene blue under visible light irradiation. The optimal photocatalyst efficiency, reached at a ZnO(stearic acid)/ V₂O₅(hexadecylamine) ratio of 1:0.25, results to be about six times higher than that of pristine zinc oxide. Reusability test shows that after three photocatalysis cycles no significant changes in neither the dye degradation efficiency loss nor photocatalyst structure occur. Visible light photocatalytic performance observed indicates there is synergetic effect between both 2D nanocomposites used in the heterojunction. The visible light absorption enhancement promoted by the narrower bandgap V₂O₅ based components; an increased photo generated charge separation favored by extensive interface area; and abundance of hydrophobic sites for dye adsorption appear as probable causes of the improved photocatalytic efficiency in this hybrid semiconductors heterojunction. Estimated band-edge positions for both conduction and valence band of semiconductors together with experiments using specific radical scavengers allow a plausible photodegradation mechanism.

Tantalum doped ZnO structures (ZnO:Ta) were synthesized and some of their characteristics were studied. ZnO material was deposited on silicon substrates by using a hot filament chemical vapor deposition (HFCVD) reactor. The raw materials were a pill made of a mixture of ZnO and Ta₂O₅ powders, and molecular hydrogen was used as a reactant gas. Percentage of tantalum was varied from 0 to 500 mg by varying the percentage of tantalum oxide in the mixture of the pill source, by holding a fixed amount of 500 mg of ZnO in all experiments. X-ray diffractograms confirmed the presence of zinc oxide in the wurtzite phase and metallic zinc with a hexagonal structure, and no other phase was detected. Displacements to lower angles of reflection peaks, compared with those from samples without contamination, were interpreted as the inclusion of the Ta atoms in the matrix of the ZnO. This fact was confirmed by EDS and XRD measurements. From SEM images from undoped samples exhibited mostly micro sized semi-spherical structures while doped samples displayed a trend to grown as nanocrystalline rods. The presence of tantalum during the synthesis affects the way of the growth. Green photoluminescence at naked eye was observed when Ta doped samples were illuminated by ultraviolet radiation and confirmed by PL spectra. PL intensity on Ta doped ZnO varied from those undoped samples up to 8 times.

The recyclable paper based on photochromic materials not only reduces the pollution in the paper manufacture process, but also reduces the pollution caused by the use of ink, which receives wide attention. In this paper, a serial of PMoA-PWA/ZnO/PVP hybrid films which had different ratio of PMoA/PWA was prepared by the ultrasonic composite method. The results indicated that the hybrid film prepared when the ratio of PMoA to PWA was 3 had the best photochromic performance. In this system, ZnO was the photosensitizer while PMoA/PWA was the chromophore. The photochromic mechanism of PMoA-PWA/ZnO/PVP hybrid film was based on the photogenerated electron transfer mechanism. ZnO generated photoelectron under the excitation of visible light, then PMoA and PWA obtained the photoelectron and produced photoreduction reaction to generate heteropolyblue. The visible light photochromic paper was prepared by loaded PMoA-PWA/ZnO/PVP hybrid film (A3) on A4 paper. Application test showed that the prepared paper had extremely stable, excellent and reversible visible light photochromic properties, whether it was printing patterns or words and could replace the ordinary paper to realize the reuse of paper.

he present experiment concerns deposition of ZnO by ALD and subsequent growth of nanowires by chemical bath. We used a novel AISI 301 steel substrate with mechanical parameters that make it suitable to use as a piezoelectric component in an energy harvesting device. We found out that a thin layer of another oxide below ZnO provides outstanding adhesion. Without it, ZnO exhibits island growth and is mechanically unstable. Such prepared samples were placed under repeated mechanical stress. They showed a piezoelectric signal which is stable after hundreds of actuations. This shows good promise for use of our device based on ZnO, an earth-abundant and non-toxic material, as an alternative to widespread in piezo components but environmentally unfriendly PZT. The piezo layers generated enough power for operations performed by a IoT chip. The designed measurement setup allowed for the demonstration of an application of AISI 301 steel substrate coated with ZnO by atomic layer and chemical bath deposition techniques as a piezoelectric component capable of generating energies usable in Internet of Things applications.

Here, we designed the composition of the coating of the paper sheets composed of chitosan, bacterial cellulose (nanofibres), and ZnO with boosted antibacterial and mechanical activity. We investigated the compositions with ZnO exhibiting two different sizes/shapes: (1) rods and (2) irregular sphere-like particles. The proposed processing of bacterial cellulose resulted in the formation of nanofibers. Antimicrobial behavior was tested using E. coli ATCC® 25922™ following ASTM E2149-13a standard. Mechanical properties of the paper sheets were measured by comparison of tearing resistance, tensile strength, and bursting strength according to ISO 5270 standard. The increased antibacterial response is assigned to the combination of chitosan and ZnO (independently of its shape and size), while the boosted mechanical behavior is due to bacterial cellulose nanofibers. Therefore, the proposed composition is an interesting multifunctional mixture for coatings in food packaging applications.

Zinc oxide is one of the most important semiconductor metal oxides and one of the most promising n-type materials, but its practical use is limited because of both its high thermal conductivity and its low electrical conductivity. Numerous studies have shown that doping with metals in ZnO structures leads to the modification of the band gap energy. In this work, Al-doped ZnO, Ni-doped ZnO, and undoped ZnO nanocrystalline powders were prepared by sol-gel method coupled with ultrasound irradiation. The doping concentration in ZnO was 1.0 at.% of Al and Ni. Influence of Al³⁺ and Ni²⁺ ions in the ZnO network are explored in this paper. X-ray Diffraction (XRD), Raman Spectroscopy, Nitrogen Adsorption (BET method), X-Ray Fluorescence (XRF) and Field Emission Scanning Electron Microscopy (FESEM) analyses demonstrated the incorporation of metal ions (aluminum and nickel) into the ZnO wurtzite structure. The crystallite size of the sample was decreased from 24.5 nm (ZnO) to 22.0 nm (ZnO-Al) and 21 nm (ZnO-Ni).

Zinc oxide (ZnO) as a semiconductor in its crystalline or amorphous form is still a promised material, especially under isobaric and isothermal ensembles. In this work, Parallel and Equilibrium Molecular Dynamics and DL_POLY_4 software are employed to predict the relationship between the behavior of ZnO chemical bonds and the phase transition literatures, using correlation function g(r) of Zn-Zn, Zn-O, and O-O pairs. Our system is composed of 5832 atoms of ZnO rocksalt structure (2916 atoms of Zn2+ and 2916 atoms of O2-), under the temperature of 300 (K) and the range of pressure 0-400 (GPa). The lengths of ZnO bonds, the standard error, standard deviation, the maximum of g(r), and the percentage of the variation of the bonds are analyzed. The interatomic interactions are modeled by the potential of Buckingham for short-range and Coulomb for long-range interactions. The calculations were run on the RAVEN Supercomputer of Cardiff University (UK). Our data are mostly in the vicinity of available information of bonds lengths; the rest can be deduced from the pressure of phase transition to use it as a new approach of phase transition confirmation. However, the rest of our results are still a prediction because of no results under extended pressure used in this work.

In this study, the effect of ZnO nanoparticles (Zn NPs) on the performance of epoxy resin composites was investigated. The new ZnO/epoxy resin composites were synthesized using halloysite nanotubes (HNT) and different types of ZnO nanoparticles (commercial ZnO and ZnO-ODTES). These ZnO nanoparticles were utilized for intending to enhance the interfacial bonding between the epoxy resin and the reinforcement. Various methods such as FTIR, TGA, DSC, TEM-EDX, and Nanoindentation analyses were used to prove that the ZnO nanoparticles can improve the properties of epoxy resin composites. The thermal properties of the epoxy resin composites were enhanced to a greater extent by the addition of ZnO NPS. DSC testing proved that the epoxy resin composites modified with ZnO NPS are more flexible and elastic than unmodified epoxy resin. It was seen that the epoxy resin modified with ZnO-ODTES shows a much improved hardness and penetration depth compared to the other samples. These findings can pave the way for the developing of ZnO-based marine coatings with improved properties.

Titanium alloys are difficult to machine and have poor tribological properties. This paper investigates the lubricating performance of γ-Al2O3/ZnO hybrid nanofluids for Ti-6Al-4V. The pure and hybrid nanofluid are compared, and the effects of γ-Al2O3/ZnO ratios are studied. The results show that γ-Al2O3/ZnO hybrid nanofluids outperform pure nanofluid in terms of lower friction coefficients and better surface quality. Moreover, the hybrid nanofluid with a mass ratio of Al2O3 to ZnO of 2:1 demonstrates the best lubrication performance with a reduced friction coefficient of up to 22.1% compared to the base solution, resulting in improved surface quality. Al2O3 nanoparticles can adhere to the surface of ZnO nanoparticles and work as a coating, which further enhances the lubrication performance of the water-based nanofluid.

In this work, zinc oxide (ZnO) nanoparticles were modified in a circulating fluidized bed through argon and hydrogen (Ar-H) alternative-current (AC) arc plasma, which shows the characteristics of non-equilibrium and equilibrium plasma at the same time. In addition, a circulating fluidized bed with two plasma jets was used for cyclic processing. The catalytic degradation performance on Rhodamine B (Rh B) by Ar-H plasma modified ZnO and pure ZnO was tested in aqueous media to identify the significant role of hydrogen atoms in Rh B degradation mechanism. Meanwhile, the effects of plasma treatment time on the morphology, size and photocatalytic performance of ZnO were also investigated. The results demonstrated that ZnO after 20 minutes-treatment by Ar-H plasma showed Rh B photocatalytic degradation rate is ten times greater than that of pure ZnO, and the reaction follows a first-kinetics for the Rh B degradation process. Furthermore, the photocatalyst cycle experiment curve exhibited that the modified ZnO still displays optimum photocatalytic activity after five cycles of experiment. The improvement of photocatalytic activity and luminescence performance attributes to the significant increase of the surface area, and the introduction of hydrogen atoms on the surface also could enhance the time of carrier existence where the hydrogen atoms act as shallow donors.

In the present work, doped ZnO (ZnO:Al) thin film has been grown on Silicon (Si) substrate by DC sputtering. The obtained thickness of the film is 230 ± 5 nm. The films were subjected to swift heavy ion (SHI) irradiation 120 MeV, Ag⁹⁺ with different fluences ranging from 3 × 10¹¹ to 3 × 10¹³ ions/cm². To study the impact of SHI, both pristine and irradiated samples were characterized to obtain the structural, surface morphological and electrical properties using X-ray diffractometry (XRD), atomic force microscopy (AFM) and hall effect measurement system respectively. From XRD results it is observed that there is change in crystallinity of the film with increase in irradiation fluence. The surface morphological studies through AFM shows the increase in surface roughness with increase in fluence. A significant change is also observed in electrical parameters viz conductivity, mobility and carrier concentration. Conductivity, mobility and carrier concentration decreases with increasing fluence.

In this study, in order to explore the failure mode of ZnO varistors under multiple lightning stroke, a 5-pulse 8/20 μs nominal lightning current with pulse intervals of 50 ms was applied to the ZnO varistors. Scanning electron microscopy (SEM) and X-ray diffractometry (XRD) were used to analyze the microstructure of the material. The failure processes of ZnO varistors caused by multiple lightning impulse current were described. The performance changes of ZnO varistors after multiple lightning impulses were analyzed from macro and micro perspectives. According to the results of this study’s experiments, the macroscopic failure mode of the ZnO varistors after multiple lightning impulse was that the electrical parameters deteriorate rapidly with the increase of the number of impulse groups, and finally destroyed by side-corner cracking. The microstructural examination indicated that after the multiple lightning strokes, the proportion of Bi in the several crystal phases had been converted, the grain size of ZnO varistors became smaller, and the white intergranular phase (Bi-rich grain boundary layer) increased significantly. The failure mechanism was thermal damage and grain boundary structure damage caused by temperature gradient thermal stress generated by multiple lightning current.

We report the influence of ammonium hydroxide (NH4OH), as growth additive, on zinc oxide nanomaterial through the optical response obtained by photoluminescence (PL). A low-temperature hydrothermal process is employed for the growth of ZnO nanowires (NWs) on seedless Au surface. A more than two order of magnitude change in ZnO NW density is demonstrated via careful addition of NH4OH in the growth solution. Further, we show by systematic experimental study and PL characterization data that the addition of NH4OH can degrade the optical response of ZnO NWs produced. The increase of growth solution basicity with the addition of NH4OH may slowly degrade the optical response of NWs by slowly etching its surfaces, increasing the point defects in ZnO NWs. The present study demonstrates the importance of growth nutrients to obtain quality controlled density tunable ZnO NWs on seedless conducting substrates.

Rapid progress in the development of highly efficient nanoparticle-based construction technologies has not always been accompanied by a corresponding understanding of their effects on human health and ecosystems. Here, we compare toxicological effects of pristine TiO₂, ZnO and SiO₂, and coated SiO₂ nanoparticles and evaluate their suitability as additives to consolidants of weathered construction materials. First, WST-1 and LDH assays were used to determine the viability of human alveolar A549 cells at various nanoparticle concentrations (0–250 μg mL⁻¹). While the pristine TiO₂ and coated SiO₂ nanoparticles did not exhibit any cytotoxic effect up to the highest tested concentration, the pristine SiO₂ and ZnO nanoparticles significantly reduced cell viability. Second, as all the developed nanoparticle-modified consolidants increased the mechanical strength of weathered sandstone, the decisive criterion for the selection of the most suitable nanoparticle additive was as low toxicity as possible. We believe that this approach will be of high importance for industry to identify materials representing top functional properties and low toxicity at an early stage of the product development.

In this work, zinc oxide (ZnO) thin film has been fabricated on glass substrate using pulse laser ablation (PLA) technique. The effect of laser pulses of 1000, 1500, 2000 pulses at laser energy 700 mJ as well as, laser energy of 600, 700, and 800 mJ at fixed laser pulses of 1500 pulse, with methanol as a solvent on the structural properties of prepared films using XRD, SEM and EDX. XRD results revealed that the ZnO thin films have hexagonal structure with polycrystalline in nature with preferred orientation of (002). Crystalline size was increased with the increasing of the pulses and at energy of 700 mJ and pulse of 1500 pulse seemed nanostructure like tree leaf. In addition, narrow FWHM and no phase change have been observed in all cases. SEM images showed that for all cases the films were homogenous with some island and cluster then cracking started to obtain with the increasing of increase the pulse number. EDX analysis showed that the prepared films were free of defects and contaminations.

The demand for high-energy-density batteries necessitates novel anode materials. Transition metal oxides (TMOs) show promise due to their high capacity, sustainability, and cost-effectiveness. However, TMO-based anodes face challenges related to expansion and conductivity. This study presents a two-step dilution crystallization method to fabricate porous ZnO nanoflowers at a moderate temperature. In-situ integration with carbon nanotube dispersants enhances conductivity and reduces agglomeration. The resulting composite anode exhibits impressive initial discharge capacity (2314.2 mAh g-1) and cycling stability (580.5 mAh g-1 over 50 cycles). This study provides a facile approach for next-generation anode materials.

Delayed atomic layer deposition (ALD) of ZnO, i.e., area selective (AS)-ALD, was successfully achieved on silicon wafers (Si/SiO2) terminated with tris(dimethylamino)methylsilane (TDMAMS). This resist molecule was deposited in a home-built, near atmospheric pressure, flow-through , gas-phase reactor. TDMAMS has been shown to react with Si/SiO2 in a single cycle/reaction and to drastically reduce the number of silanols that remain at the surface. ZnO was deposited in a commercial ALD system using dimethylzinc (DMZ) as the zinc precursor and H2O as the coreactant. Deposition of TDMAMS was confirmed by spectroscopic ellipsometry (SE), X-ray photoelectron spectroscopy (XPS), and wetting. ALD of ZnO, including its selectivity on TDMAMS – terminated Si/SiO2 (Si/SiO2/TDMAMS), was confirmed by in situ ellipsometry, ex situ SE, XPS, and/or high sensitivity – low energy ion scattering (HS-LEIS). The thermal stability of the TDMAMS resist layer, which is an important parameter for AS-ALD, was investigated by heating Si/SiO2/TDMAMS in air and nitrogen at 330 ºC. ALD of ZnO takes place more readily on Si/SiO2/TDMAMS heated in the air than in N2, suggesting greater damage to the surface heated in the air. To better understand the in situ ALD of ZnO, the data were also plotted as the normalized growth per cycle and to show the selectivity. Even one, short pulse of TDMAMS effectively passivates Si/SiO2. TDMAMS can be an effective small molecule inhibitor of ALD of ZnO on Si/SiO2 surfaces.

The photocatalytic biohydrogen generation using ZnO with the aid of simultaneous deposition of copper from an aqueous biomass-derivative glycerol solution was investigated. The effects of concentration of glycerol solution, Cu ion concentration and reaction temperature on biohydrogen generation were investigated. The photocatalytic biohydrogen production rate increased with increasing the concentration of aqueous glycerol solution, and the observed data could be fitted to the Langmuire-Hinshelwood kinetic models. The photocatalytic H2 production efficiency with ZnO could be significantly improved by simultaneous Cu deposition. The photocatalytic biohydrogen production rate was dependent on temperature, and increased with the increasing temperature. The possible mechanisms for oxidation of glycerol solution and photocatalytic hydrogen generation were proposed.

The extensive use of engineered nanoparticles (ENPs) such as zinc oxide nanoparticles (ZnO NPs) in various commercial fields has spurred significant concern about its possible toxicological effects of ZnO NPs on human health and eco-system. Therefore, it is substantial to understand the aggregation phenomena which could attenuate this effect. This data article provides information on aggregation of ZnO NPs under the influence of various parameters of water chemistry. Moreover, Taguchi orthogonal array L27(313) design matrix was used to evaluate the effect of multiple parameters in aqueous solution. The data were obtained from single beam UV-Vis spectrophotometer (Optizen 2120 UV, Mecasys, Korea) using Optizenview 4.2.5 PC interference software, Fourier transform infrared spectrometer (FT/IR-4700, spectroscopy, JASCO Analytical Instruments, Easton, USA) and particle electrophoresis (NanoZS, Zetasizer, Malvern Instruments Ltd, Worcestershire, UK). The dataset draws attention on dominant parameters influencing aggregation of ZnO NPs in water. The analysis of variance (ANOVA) data revealed that electrolyte concentration, type and natural organic matter (NOM) concentration were the most significant parameters. Furthermore, FT-IR data presents a possible mechanism of ZnO NPs stabilization in the presence of different NOM. This data will be helpful for the development of environmental risk assessment strategies and prediction of fate and mobility of other ENPs in the aquatic environment.

Here, we report on ZnO nanoparticles (NPs) generated by nanosecond pulsed laser (Nd:YAG, 1064 nm) through ablation of metallic Zn target in water and air and their comparative analysis as potential nanomaterials for biomedical applications. The prepared nanomaterials were carefully characterized in terms of their structure, composition, morphology and defects. It was found that in addition to the main wurtzite ZnO phase, which is conventionally prepared and reported by others, the sample laser-generated in air also contained some amount of monoclinic zinc hydroxynitrate. Both nanomaterials were then used to modify model wound dressings based on biodegradable poly-L-lactic acid. The as-prepared model dressings were tested as biomedical materials with bactericidal properties towards S. aureus and E. coli strains. The advantages of the NPs prepared in air over their counterparts generated in water found in this work are discussed.

The ozonation reaction in a bubble column reactor (BCR) has been widely used in the removal of phenol from wastewater, but the phenol removal efficiency in this type of reactor is limited because of low ozone solubility and reactivity in the system. In the present study, the phenol degradation was enhanced using α-Al2O3 as a packing material and a ZnO nanocatalyst in the BCR. The reactor diameter and height were 8 cm and 180 cm, respectively. The gas distributor was designed to include 52 holes of 0.5-mm diameter. Also, the gas holdup, pressure drop, and bubble size were measured as a function of the superficial gas velocity (i.e., 0.5, 1, 1.5, 2, 2.5, and 3 cm/s). The evaluation of the hydrodynamic parameters provided a deep understanding of the ozonation process to select the optimal operating parameters in the reactor. It was found that the best superficial gas velocity was 2.5 cm/s. A complete (100%) phenol removal was achieved for phenol concentrations of 15, 20, and 25 ppm at reaction times of 80, 90, and 100 min, respectively, using α-Al2O3 packing material and a ZnO nanocatalyst in the BCR. Additionally, the results provided a clear reaction mechanism describing the ozonized BCR. Finally, the applied treatment method can be used efficiently to remove phenol from wastewater at a low cost, with little consumed energy, and a simple operation.

Here we report the effect of substrate, sonication process, and post-annealing on the structural, morphological, and optical properties of ZnO thin films grown in the presence of isopropyl alcohol (IPA) at temperature 30 – 65 ℃ by successive ionic layer adsorption and reaction (SILAR) method on both soda lime glass (SLG) and Cu foil. The X-ray diffraction (XRD) patterns confirmed the preferential growth thin films along (002) and (101) plane of wurtzite ZnO structure while grown on SLG and Cu foil substrate respectively. Both XRD and Raman spectra confirmed the ZnO and Cu-oxide phases of the deposited films. Scanning electron microscope (SEM) image of the deposited films shows compact and uniformly distributed grains for samples grown without sonication while using IPA at temperature 50 and 65 ℃. The post-annealing treatment improves the crystallinity of the films, further evident by XRD and transmission and reflection results. The estimated optical bandgaps are in the range of 3.37-3.48 eV for as-grown samples. Results revealed that high-quality ZnO thin films could be grown without sonication using IPA dispersant at 50 ℃, which is much lower than the reported results using the SILAR method. This study suggests that in the presence of IPA, the SLG substrate results in better c-axis oriented ZnO thin films than that of DI water, ethylene glycol, propylene glycol at the optimum temperature of 50 ℃. Air-annealing of the samples grown on Cu foils induced the formation of Cu_xO/ZnO junctions which is evident from the characteristic I-V curve including the structural and optical data.

An ultraviolet (UV) nanosecond pulsed laser with a wavelength of 355 nm was applied to anneal amorphous indium-gallium-zinc oxide (a-IGZO) thin-film transistors (TFT) at various laser beam powers ranging from 0 to 280 mW. Laser irradiation was selectively carried out on the a-IGZO channel area using the beam scanning method after the a-IGZO TFT was formed through indium-tin oxide (ITO) electrode patterning and a subsequent lift-off process. After laser annealing, negative shifts in the threshold voltages and enhanced on-currents were observed at laser-beam powers ranging from 54 to 120 mW. No meaningful parameters were investigated for laser beams higher than 200 mW. By extracting the energy band gap and work function of a-IGZO from the transmittance and ultraviolet photoelectron spectroscopy (UPS) results, the ITO electrode/a-IGZO channel energy band structures were established under different laser annealing conditions, and the electron injection mechanism from the ITO to the a-IGZO channel was analyzed and optimized at a laser beam power of 120 mW. The results show that the electrical characteristics of the a-IGZO TFTs can be improved without any heat damage to the substrate because of the selective annealing process.

CuO/ZnO/Al2O3 catalyst is a commonly used catalyst for rea methanol steam reforming reaction. Oxalic acid was as precipitant in preparing oxalate precursor of CuO/ZnO/Al2O3 catalyst by co-precipitation, deionized water and ethanol were as solvents, microwave irradiation and water bath were as aging heating manner respectively. It indicated that ethanol selected crystal phase composition of oxalate precursors and restricted their growth. Microwave irradiation prompted the isomorphous substitution between Cu2+ of CuC2O4 and Zn2+ of ZnC2O4 in mother liquid, forming the master phase (Cu,Zn)C2O4 in precursor, the solid solution Cu-O-Zn formed after calcination, which exhibited nano-fibriform morphology. It possessed small CuO grains, large surface area and strong synergy between CuO and ZnO, which is beneficial to improve the catalytic performance of methanol steam reforming, the STY of H2 reached 516.7 mL·g-1·h-1, and the selectivity of CO was only 0.29%.

This article describes in detail the numerical modeling of a CZTS (copper zinc tin sulfide) based kesterite solar cell. The Solar Cell Capacitance Simulator -one-dimension (SCAPS-1D) software was used to simulate MO/CZTS/CdS/ZnO/FTO structured solar cells. The parameters of different photovoltaic thin-film solar cells are estimated and analyzed using numerical modeling. The effects of various parameters on the performance of the photovoltaic cell and the conversion efficiency are discussed. Since the response of the solar cell is also contingent on its internal physical mechanism, J-V characteristic measures are insufficient to characterize the behavior of a device. Different features, as well as different potential conditions, must be considered for simulation, disregarding the belief in the modeling of a solar cell. With a conversion efficiency of 25.72%, a fill factor of 83.75%, a short-circuit current of 32.96436 mA/cm2 and an open-circuit voltage of 0.64V, promising optimized results have been achieved. The findings will be useful in determining the feasibility of fabricating high-efficiency CZTS-based photovoltaic cells. The efficiency of a CZTS-based experimental solar cell is also discussed. First, the effects of experimentally developed CZTS solar cells are simulated in the SCAPS-1D environment. The experimental results are then compared to the SCAPS-1D simulated results. The conversion efficiency of an optimized system increases after cell parameters are optimized. Using one-dimensional SCAPS-1D software, the effect of system parameters such as the thickness, acceptor and donor carrier concentration densities of absorber and electron transport layers, and the effect of temperature on the efficiency of CZTS-based photovoltaic cells is investigated. The proposed results will greatly assist engineers and researchers in determining the best method for optimizing solar cell efficiency, as well as in the development of efficient CZTS-based solar cells.

Herewith we report a facile synthesis of zinc oxide doped with (5, 10, 15, and 20 wt%) titanium oxide nanocomposites in gelatin under ultra-sonication. The X-ray diffraction (XRD) data revealed ZnO the formation in addition to a rutile phase TiO2. The ZnO phase size decreased, and the rutile TiO2 phase increased with a TiO2 loading increment. The scanning electron microscopy (SEM) displayed a combination of spherical and hexagonal particles with a 60 – 80 nm size distribution. The prepared nanostructures photocatalytic activity was assisted using Rhodamine B dye, where they showed enhanced photodegradation competence under visible light irradiation. The kinetics of photodegradation followed the first-order kinetics with the 20 % wt sample having the maximum activity. The mechanistic investigation revealed the dominance of h+ and •O2- species during the dye photodegradation. The results indicate the potential application of such gelatin stabilized nanostructures for dye illumination from aqueous solutions under sunlight.

For some decades, the scientific community has been looking for alternatives to the use of fossil fuels that allow the planet's sustainable and environmentally friendly development. To do this, attempts have been made to mimic some processes that occur in nature, among which the photosystem-II stands out, which allows water splitting operating with different steps to generate oxygen and hydrogen. This research presents promising results using synthetic catalysts, which try to simulate some natural processes, and which are based on Au@ZnO-graphene compounds. These catalysts were prepared by incorporating different amounts of gold nanoparticles (1 wt.%, 3 wt.%, 5 wt.%, 10 wt.%) and graphene (1 wt.%) on the surface of synthesized zinc oxide nanowires (ZnO NWs), and zinc oxide nanoparticles (ZnO NPs), along with a commercial form (commercial ZnO) for comparison purposes. The highest amount of hydrogen (1,127 µmol/hg) was reported by ZnO NWs with a gold and graphene loadings of 10 wt.% and 1 wt.%, respectively, under irradiation at 400 nm. Quantities of 759 µmol / hg and 709 µmol / hg were obtained with catalysts based on ZnO NPs and commercial ZnO, respectively. The photocatalytic activity of all composites increased with respect to the bare semiconductors, being 2.5 times higher in ZnO NWs, 8.8 times for ZnO NPs and 7.5 times for commercial ZnO. The high photocatalytic activity of the catalysts is attributed, mainly, to the synergism between the different amount of gold and graphene incorporated, and the surface area of the composites.

In this work, cobalt doped ZnO nanorod arrays with anticorrosion function were successfully prepared on FTO substrate by a simple aqueous solution method. XRD and EDS results indicate the doped Co2+ has successfully incorporated into the ZnO crystal lattice. Photocurrent density and open circuit potential (OCP) results indicate the photocathodic protection performance for 316 stainless steel (316 SS) and Q235 carbon steel in 3.5 wt.% NaCl solution under 300 W Xe lamp enhanced with the increase of cobalt concentration, and the photoanode with 15% Co/Zn ratio has the optimal photocathodic protection effect. The mechanism of enhancement may be result from the narrowed band gap, the lower recombination rate of photogenerated electron-holes, the intermediate impurity level and the split of the hypo-outer shell of cobalt ions.

Zinc oxide (ZnO) nanoparticles (NPs) were synthesized using Rosmarinus officinalis leaf extract at 80 ° C (ZnO-80) and 180 ° C (ZnO-180). The biosynthesized ZnO NPs were characterized and their photocatalytic activity was evaluated for the degradation of methylene blue (MB) and crystal violet (CV) under sunlight irradiation. The results of the characterizations by XRD, TEM and SEM showed that the size of the NPs of ZnO-80 was smaller than that of ZnO-180 which exhibited flakier agglomerated spherical structures. Photocatalytic tests showed ZnO-80 which was prepared by a cheap and easy procedure compared to ZnO-180 effectively degrades MB and CV dyes under sunlight. The superior performance of ZnO-80 over ZnO-180 can be explained by the differences in their textural properties. This is because ZnO-80 has a smaller crystallite size, a specific surface area and a higher pore volume than ZnO-180. Fourier-transform infrared spectroscopy (FTIR) analyzes revealed that both samples contained an adsorbed carboxylate group (COO-), and accordingly a mechanism was proposed for the formation of ZnO NPs that include the carboxyl group.

Many quantum dot light-emitting diodes (QLEDs) utilize ZnO nanoparticles (NPs) as an electron injection layer (EIL). However, the use of ZnO NP ETL material often results in charge imbalance within the quantum dot (QD) emitting layer (EML) and exciton quenching at the interface of QD EML and ZnO NP EIL. To overcome these challenges, we introduced an Arginine (Arg) interlayer (IL) onto the ZnO NP EIL. The Arg IL elevated the work function of ZnO NPs, thereby suppressing electron injection into the QD, leading to improved charge balance within the QDs, Additionally, the inherent insulating nature of the Arg IL prevented direct contact between QDs and ZnO NPs, reducing exciton quenching and consequently improving device efficiency. The inverted QLED (IQLED) utilizing a 20-nm-thick Arg IL on ZnO NP EIL exhibited a 2.22-fold increase in current efficiency and a 2.28-fold increase in EQE and compared to an IQLED without an IL. Likewise, the IQLED with a 20-nm-thick Arg IL on ZnO NP EIL demonstrated a 1.34-fold improvement in current efficiency and a 1.36-fold increase in EQE compared to IQLED with a 5-nm-thick PEI IL on ZnO NPs.

Wood plastic composite usage and demands have increased due to chemical, and mechanical properties when compared to plastic materials. However, because of the possibility of structural and mechanical changes of the material when exposed to external environment more research needs to be done. In the present study yellow birch/HDPE composites materials made by injection molding were treated by zinc oxide and exposed to fungal rots. Mechanical properties of the composites were assessed by Tensile and Izod impact test. The impact energies of the samples loaded with 30 % ZnO-treated fibers and exposed to G. trabeum and T. versicolor decreased, compared to when samples were not treated with ZnO. The mechanical properties of all samples treated with ZnO and exposed to rot decreased which were reported as a decreased Young's modulus and impact energies. ZnO prevented mycelium proliferation which was nonexistent on samples. It has been noted that the decrease in mechanical properties of treated samples was due to NaOH used to dissolve the ZnO powder.

Biodiesel is considered valuable to reduce dependency on petro-fuels. This work aimed to synthesize biodiesel from Silybum marianum using synthesized ZnO nanoparticles as a catalyst. The synthesized ZnO nanoparticles were examined by scanning electron microscopy and X-ray diffraction for confirmation. The synthesized biodiesel was confirmed by ASTM D-6751, H and C-NMR, GC-MS, and FT-IR spectroscopy. The optimal biodiesel yield of 91% was obtained in the oil-to-methanol ratio of 1:24, 15 mg of catalyst concentration, 60 0C temperature, and 45 minutes of reaction time. Fuel properties were determined according to the ASTM defined methods and found within the defined limits of ASTM D-6751. 1H-NMR and 13C-NMR showed characteristic peaks at 3.667 ppm, 2.000 to 2.060 ppm, 0.858-0.918 ppm, 5.288-5.407 ppm, 24.93-34.22 ppm, 172.71, 173.12, 130.16 ppm, and 128.14 ppm, respectively, which confirm biodiesel synthesis. The FAMEs composition of biodiesel was determined by GC-MS which recognized 19 peaks for different types of FAMEs. FT-IR spectroscopy showed two main peaks, first in the range of 1725-1750 cm-1 and second in the range of 1000-1300 cm-1, which confirmed that the transesterification process was completed successfully. The physicochemical characteristics of Silybum marianum confirm that it is a suitable source to produce biodiesel on industrial scale.

Renewable methanol, obtained from CO₂ and hydrogen provided from renewable energy, has been proposed as a way to close the CO₂ loop. In industry, methanol synthesis using the catalyst CuO/ZnO/Al₂O₃ occurs at a high pressure. We intend to make certain modification on the traditional catalyst in order to work at lower pressure, maintaining high selectivity. Therefore, three heterogeneous catalysts have been synthesized by co-precipitation in order to improve the activity and the selectivity to methanol under mild conditions of temperature and pressure. Certain modifications on the traditional catalyst Cu/Zn/Al₂O₃ were employed such as the modification of the synthesis time and the addition of Pd as a dopant agent. The most efficient catalyst among those tested was a palladium-doped catalyst, 5% Pd/Cu/Zn/Al₂O₃. This had a selectivity of 64% at 210C and 5 bar.

In this study is reported the optical, structural and dielectric properties of Poly (vinyl alcohol) thin films membranes with embedded ZnO nanoparticles (PVA/ZnO) obtained by solution casting method at low temperature of deposition. Fourier Transform Infrared spectra showed the characteristics peaks, which correspond to O-H and Zn-O bonds present in the hybrid material. The X-ray diffraction patterns indicated the presence of ZnO structure into the films. The composite material showed low absorbance and a wide band gap energy from 5.6 to 5.9 eV. The surface morphology for the thin films of PVA/ZnO was studied by Atomic Force Microscopy and Scanning Electron Microscopy. The dielectric properties of the nanocomposites were measured from low to high frequencies, the results showed a high dielectric constant (ε) in the order of 10⁴ at low frequency and values from ε ≈ 2000 to 100 in the range of 1KHz-1MHz respectively, the properties of PVA/ZnO such as the high permittivity and the low temperature of processing make it a suitable material for potential applications in the development of flexible electronic devices.

Fabrication of a nanocrystal zinc oxide (ZnO)/nitrogen-doped (N-doped) graphene composite using a novel and facile in situ sol-gel technique is demonstrated. Two-dimensional nanostructure morphology with uniform ZnO nanoparticles (average diameter of 10.25 nm) anchored on N-doped graphene nanosheets was observed via electron microscopy. Because of the polar heteroatoms on the graphene sheets, an abundance sites for polysulfide absorption were provided. More importantly, the strong chemical interaction between ZnO and polysulfides efficiently hindered the transport of polysulfides. Consequently, the lithium/sulfur (Li/S) battery with the ZnO/N-doped graphene composite-coated separator delivered enhanced performance in terms of discharge capacity and cycling stability when compared to the cell with a normal separator. With the modified separator, the battery achieved a discharge capacity as high as 942 mAh g^-1 for the first cycle and remained at 90.02 mAh g^-1 after the 100th charge/discharge test at 0.1 C. Results indicate that impeding the shuttling of polysulfides contributes to efficiently improving the behavior of the Li/S battery.

Fabrication of a nanocrystal zinc oxide (ZnO)/nitrogen-doped (N-doped) graphene composite using a novel and facile in situ sol-gel technique is demonstrated. Two-dimensional nanostructure morphology with uniform ZnO nanoparticles (average diameter of 10.25 nm) anchored on N-doped graphene nanosheets was observed via electron microscopy. Because of the polar heteroatoms on the graphene sheets, an abundance sites for polysulfide absorption were provided. More importantly, the strong chemical interaction between ZnO and polysulfides efficiently hindered the transport of polysulfides. Consequently, the lithium/sulfur (Li/S) battery with the ZnO/N-doped graphene composite-coated separator delivered enhanced performance in terms of discharge capacity and cycling stability when compared to the cell with a normal separator. With the modified separator, the battery achieved a discharge capacity as high as 942 mAh g^-1 for the first cycle and remained at 90.02 mAh g^-1 after the 100th charge/discharge test at 0.1 C. Results indicate that impeding the shuttling of polysulfides contributes to efficiently improving the behavior of the Li/S battery.

Green products have excellent potential for discovering and producing new medicinal products. In recent years, there is a growing interest towards the green synthesis of metal nanoparticles, particularly from plants sources. This eco-friendly approach was used in the recent research to biosynthesize zinc oxide nanoparticles (ZnO NPs) from Cissus antractica plant. The present study aims to examine the cell cytotoxicity, cell death, and pathways of apoptosis in lung cancer cells (A549) and inflammation properties treated with biosynthesized ZnO NPs. Additionally, synthe-sized ZnO nanoparticles were characterized using UV–vis spectroscopy, X-ray diffraction (XRD), Transmission electron microscopy (TEM), Fourier-transform infrared spectroscopy (FT-IR), and Energy-dispersive X-ray spectroscopy (EDS). The XRD and TEM analyses exhibited 31 nm as the size of synthesized nanoparticles, the pure crystal form of ZnO NPs, and the shape of the NPs as nearly spherical and hexagonal quartzite. The MTT assay used for cytotoxicity evaluation de-picted the significant toxic effect of CA-ZnONPs against the A549 lung cancer cells at concentra-tions up to 20 µg/mL than non-cancerous cells. Furthermore, we observed an elevated ROS level in cancer cells. These NPs also demonstrated dose-dependent ability to suppress colony for-mation and cell migration, which increases their potential as a lung cancer treatment. Further-more, The NPs formulation's ability to induce apoptosis in cancer cells was further supported by Hoechst and propidium iodide dye. Further, CA ZnO NPs increased the gene expression of BAX, Cyto-c, Caspase 3 and 9, but decreased the expression of Bcl-2, indicating that the nanoformulation triggered mitochondrial-mediated apoptosis. Besides, this study showed that NPs suppressed in-flammatory responses by subsequently decreasing reactive oxygen species (ROS) generation, downregulating the expression of the pro-inflammatory cytokines TNF-α, iNOS, COX-2, IL-6, IL-8, and NO. Moreover, the study's findings imply that Cissus antractica are a potential source with biosynthesize nanoparticles that can might be further investigated for the progress of an-ti-inflammatory and anti-cancer drugs with further study.

This paper studies the use of zinc oxide nanoparticles (ZnO-NPs) synthesized using an extract of convolvulus leaves and expired ZnCl₂, as an efficient inhibitor for carbon steel corrosion in 1M HCl solution. ZnO-NPs are characterized by Fourier-transform infrared spectrophotometer (FTIR) and UV–Vis analysis. The technique of weight loss, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) has also been used to investigate the prevention of carbon steel corrosion in 1M HCl. The results showed that the efficiency of restraint increased when the concentration of ZnO-NPs was raised to 91% and that the inhibition efficiency is still high despite its decrease at high temperature, and it acts as a mixed-type inhibitor A sample of carbon steel with the protective inhibitor layer on top was immersed for 20 hours and observed; an increase in the charge transfer resistance (Rct) and stability of the inhibitor was noticed after 6 hours. Adsorption isotherm models demonstrated that the inhibitor adsorption mechanism on the carbon steel surface followed Langmuir, more than Freundlich and Temkin, behavior. The thermodynamic parameters showed that the adsorption process is a mixed adsorption, spontaneous, and exothermic. The results illustrated that the acid medium was a strong inhibitor of carbon steel corrosion. Scanning electron microscope (SEM) showed that the ZnO-NPs formed a good protective film on the carbon steel surface.

Water borne pathogens present a threat to human health and their disinfection from water poses a challenge, prompting search for newer methods and newer materials. Disinfection of Gram-negative bacterium Escherichia coli and Gram-positive coccal bacterium Staphylococcus aureus in aqueous matrix was achieved within 60 and 90 minutes respectively at 35⁰C using solar-photocatalysis mediated by sonochemically synthesized Ag@ZnO core-shell nanoparticles. The efficiency of the process increased with increase in temperature and at 55⁰C the disinfection could be achieved in 45 and 60 min respectively for the two bacteria. A new ultrasound assisted chemical precipitation technique was used for the synthesis of Ag@ZnO core-shell nanoparticles. The characteristics of the synthesized material were established using physical techniques. The material remained stable even at 400o C. Disinfection efficiency of the Ag@ZnO core-shell nanoparticles was confirmed in case of real world water samples from pond, river, municipal tap and was found to be better than that of pure ZnO and TiO2 (Degussa P25). When the nanoparticle based catalyst was recycled and reused for subsequent disinfection experiments, its efficiency did not change remarkably even after three cycles. The sonochemically synthesized Ag@ZnO core-shell nanoparticles have a good potential for application in solar photocatalytic disinfection of water borne pathogens.

The development of photocatalysts with a wide spectral response and effective carrier separation capability is essential for the green degradation of tetracycline. In this work, a magnetic recyclable Z-scheme ZnO/ZnFe2O4 heterojunction (ZZF) was successfully constructed by the solid phase method using MIL-88A(Fe)@Zn as the precursor. Appropriate band gap width and Z-scheme charge transfer mechanism make ZZF have excellent visible light absorption performance, efficient charge separation and strong redox ability. Under visible light irradiation, the degradation efficiency of TCH for optimal sample ZZF2 can reach 86.3 % within 75 min in deionized water, and achieve 92.9 % within 60 min in tap water, which exhibits superior stability and reusability after five cycles. Moreover, the catalyst in the water can be conveniently recovered by magnetic force. After visible light irradiation for 70 minutes, the temperature of the reaction system increased by 21.9 °C. Its degradation constant (35.53×10-3 min-1) increases 5.1 times that at room temperature (6.95×10-3 min-1). Thermal energy perfects the kinetic driving force of the reactants and promotes carrier migration to produce more •O2- and •OH. This work provides a potential candidate and inspires the design of photocatalyst for tetracycline hydrochloride degradation.

This study describes a comparative in vitro study of the toxicity behavior of zinc oxide (ZnO) nanoparticles and micro-sized particles. The study aimed to understand the impact of particle size on ZnO toxicity by characterizing the particles in different media, including cell culture media, human plasma, and protein solutions (bovine serum albumin and fibrinogen). The study used various techniques such as atomic force microscopy (AFM), transmission electron microscopy (TEM), and dynamic light scattering (DLS) to characterize the particles and their interactions with proteins. Hemolytic activity, coagulation time, and cell viability assays were used to assess ZnO toxicity. The results highlight the complex interactions between ZnO NPs and biological systems, including their aggregation behavior, hemolytic activity, protein corona formation, coagulation effects, and cytotoxicity. Moreover, the study indicates that ZnO nanoparticles are not more toxic than micro-sized particles, and the 50 nm particles resulted in general the least toxic. Furthermore, the study found that at low concentrations, no acute toxicity was observed. Overall, this study provides important insights into the toxicity behavior of ZnO particles and highlights that no direct relationship between nanometer size and toxicity can be directly attributed.

Antibiotic residues in aquatic environment have the possibility to induce resistance in environmental bacteria, which ultimately might get transferred to pathogens making treatment of diseases difficultand poses a serious threat to public health. If antibiotic residues in the environment can be eliminated or reduced, it has the possibility to contribute antibiotic resistance. Towards this objective, water containing ciprofloxacin was treated with sunlight assisted photocatalysis using Fe doped ZnOnanoparticles for assessing the degradation potential of this system.Parameters like pH, temperature, catalytic dosage were assessed for the optimum performance of the system. To evaluate degradation of ciprofloxacin,both spectrophotometricas well as microbiological (loss of antibiotic activity)methods were employed. 100 mg/L Fe doped ZnO nanoparticle catalyst and sunlight intensity of 120,000–135,000 lux system gave optimum performance at pH 9 at 30 °C and 40 °C. At these conditions spectrophotometric analysis showed complete degradation of ciprofloxacin (10mg/L) by 210 min. Microbiological studies showed loss of antibacterial activity of the photocatalytically treated ciprofloxacin containingwater against Staphylococcus aureus (10⁸ CFU) in 60 min and for Escherichia coli (10⁸ CFU) in 75 min. Thedeveloped system, thus possess a potential for treatment of antibiotic contaminated waters for eliminating/reducing antibiotic residues from environment.

This study investigates the potential of a hybrid nanofluid composed of MoS2 and ZnO nanoparticles dispersed in engine oil, aiming to enhance the properties of lubricant's chemical reaction with the Soret effect on stretching sheet under the influence of applied magnetic field. With the growing demand for efficient lubrication systems in various industrial applications, including automotive engines, the development of novel nanofluid-based lubricants presents a promising avenue for improving engine performance and longevity. However, the synergistic effects of hybrid nanoparticles in engine oil remain relatively unexplored. This research addresses this gap by examining the thermal conductivity, viscosity, and wear resistance of the hybrid nanofluid, shedding light on its potential as an advanced lubrication solution. By analyzing the dispersion stability and interaction mechanisms between nanoparticles and base oil, valuable insights are gained into the fundamental aspects governing the entertainment of hybrid nano lubricants. Overall, the objectives of studying hybrid nano lubricant MoS2+ZnO with engine oil aim to advance the development of more efficient and durable lubrication solutions for automotive engines, contributing to improved reliability, fuel efficiency, and environmental sustainability. Governing non-linear partial differential equations are simplified as ordinary differential equations by utilizing similarity variables. MATLAB Bvp4c technique is used to solve the obtained linear ODE equations. The outputs are presented through graphs and tables for various state variables. The comparative survey in all the graphs is presented for the nanofluid (MoS2/Engine oil) with the hybrid nanofluid (MoS2+ZnO/Engine oil). These graphs show the effect of various parameters M, Q, β, Pr, Ec, Sc, Sr, Kp, Kr and (hybrid nano lubricant parameter). The velocity profile diminished against the values of M, Kp, and β. Temperature profile rising with Ec and Q. reciprocally goes down to Pr. The concentration profile incremented with the value of Sr and decremented with the value of Sc, and Kr. With the increasing value of both f′ (η) and θ(η) increases. But in θ(η) hybrid nanofluid slows down with the higher value of .

ZnO films with Ti atoms incorporated (TZO) in a wide range (0-18 at. %) have been grown by reactive co-sputtering on silicon and glass substrates. The influence of the titanium incorporation in the ZnO matrix on the structural and optical characteristics of the samples has been determined by Rutherford backscattering spectroscopy (RBS), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). The results indicate that the samples with low Ti content (< 4 at. %) exhibit the wurtzite-like structure, with the Ti+4 ions substitutionally incorporated into the ZnO structure, forming Ti-doped ZnO films. In particular, very low concentration of Ti (<0.9 at. %) leads to a significant increase of the crystallinity of the TZO samples. Higher Ti contents give rise to a progressive amorphization of the wurtzite-like structure so samples with high Ti content (≥18at. %), displays an amorphous structure indicating the XPS analysis a predominance of Ti-O-Zn mixed oxides. The energy gap, obtained from absorption spectrophotometry, increases from 3.2 eV for pure ZnO films to 3.6 eV for those with the highest Ti content. Ti incorporation in the ZnO samples below 0.9 at. % rises both, the blue (380 nm) and green (550 nm) bands of the photoluminescence (PL) emission, thereby indicating a significant improvement of PL efficiency of the samples.

Nanofibers appearing functional properties show a great promise as allowing constituents for a wide range of medical applications. In this work, Polycaprolactone (PCL), Silver Nitrate (AgNO₃) and Zinc Oxide (ZnO) were used for fabrication of nanofiber composite material by co-axial electrospinning (CAE) process. 5, 10, and 15 wt. % concentrations of PCL were utilized and different amount of AgNO₃ and ZnO were used in entire samples. Morphological analyses of the electrospun nanocomposites were done by scanning electron microscopy (SEM) and AgNO₃, ZnO and PCL materials’ functional groups were determined by Fourier Transform Infrared Spectroscopy (FTIR). Before co-axial electrospinning, physical properties such as liquid state ac conductivity, density and viscosity were measured for all solutions. Capacitance (C_p) and D-factors (tanδ) of nanocomposite materials are measured for the frequency range of 20Hz – 3MHz and the solid state alternating current (ac) conductivity, permittivity (ε’) and dielectric loss (ε’’) were calculated for all solutions after co-axial electrospinning. Effects of concentration percentages of PCL and AgNO₃ on real and imaginary parts of dielectric constant and solid state ac conductivity have been analyzed and comparisons have been made by the results obtained.

This study aimed to investigate the impact of incorporating indium tin oxide (ITO) nan particles (NPs) with zinc oxide (ZnO) NPs into flexible dye-sensitized solar cells (FDSSCs). ZnO and ITO NPs were separately prepared using the sol-gel method, followed by hybridization of ZnO NP/ITO NP and characterization using techniques such as TEM, SEM, XRD, UV-Vis spectros-copy, PL spectroscopy and cyclic voltammetry (CV). TEM analysis showed hexagonal struc-tures and small sphere-like nanoparticles with mean diameters of 15.22 ± 11 nm for ZnO NPs and 14.54 ± 16 nm for ZnO NPs/ITO NPs. SEM images revealed uniform dispersion and smooth surface morphology, while XRD confirmed the crystalline nature of both ZnO and hybrid NPs, indicating specific crystallographic planes with consistent sizes. UV-Vis spectroscopy demonstrated a redshift in wavelength upon adding ITO NPs, suggesting an impact on the bandgap of ZnO NPs. PL spectra exhibited a broad visible emission peak at 535 nm. These findings enhance our understanding of the optical behavior and interaction between ITO and ZnO NPs in hybrid nanostructures. The study concluded that the ITO NPs improve FDSSC performance by enhancing charge separation and transport, leading to increased photocurrent production, with the characterization techniques providing valuable insights for future research and applications.

Many stable water dispersions of various chemical compositions containing bioactive chemical compounds: copper silicate, titanium dioxide and zinc oxide (and other auxiliary substances) were developed and fabricated - they were used for preparation of thin hybrid coatings having very good antimicrobial properties against gram negative bacteria (Escherichia coli), gram positive bacteria (Staphylococcus aureus) and yeast fungus (Candida albicans). Polyester (PES) nonwovens were modified by dip-coating, and PES and cotton fabrics - by dip-coating and coating methods.

The paper focuses on the application of a multilevel, integrative and territorial approach to the protection of cultural heritage through planning instruments in Serbia. It points out the problems of the sectoral approach and discusses international recommendations that can be integrated into the planning methodology. The case study is the area of Djerdap National Park, which has an already established international and national importance. The research suggests that the cultural heritage in the area, with the exception of the Roman limes, is still recognized at the level of individual localities. The study emphasizes the importance of aligning all levels of governance to safeguard the whole spatial entity rather than focusing solely on its particular areas. The interna-tional and national importance of the planning area contributes to the strengthening of awareness of heritage and its institutional protection. However, the vitality of the area, which is key to its sustainable development, comes from the local level. Planning documents contribute to the inte-gration of local values and local communities into development programs and projects.

CoO-ZnO-based composites have attracted considerable attention for the development of energy storage devices because of their multifunctional characterization and ease of integration with existing components. This paper reports the synthesis of CoO@ZnO (CZ) nanostructures on Ni foam by the CBD method for facile and eco-friendly supercapacitor applications. The formation of a CoO@ZnO electrode functioned with cobalt, zinc, nickel and oxygen groups was confirmed by X-ray diffraction, X-ray photoelectron spectroscopy, low and high-resolution of scanning electron microscopy, and transmission electron microscopy. The as-synthesized hierarchical nanocorn skeleton-like structure of CoO@ZnO-3h (CZ3h) electrode delivered a higher specific capacitance of 1136 F/g at a current density of 3 A/g with outstanding cycling stability, showing 98.3% capacitance retention over 3000 cycles in an aqueous 2 M KOH electrolyte solution. This retention was significantly better than that of other prepared electrodes, such as CoO (CO), ZnO (ZO), CoO@ZnO-1h (CZ1h), and CoO@ZnO-7h (CZ7h) (274, 383, 240 and 537 F/g, respectively). This superior capacitance was attributed to the ideal surface morphology of CZ3h, which is responsible for the rapid electron/ion transfer between the electrolyte and electrode surface area. The enhanced features of the CZ3h electrode highlight potential applications in high performance supercapacitors, solar cells, photocatalysis, and electrocatalysis.

Glycosidic linkage analysis was conducted on the unfractionated polysaccharides in the alcohol-insoluble residues (AIRs) prepared from six red seaweeds (Gracilariopsis sp., Prionitis sp., Mastocarpus papillatus, Callophyllis sp., Mazzaella splendens, and Palmaria palmata) using GC-MS/FID analysis of partially methylated alditol acetates (PMAAs). The cell walls of P. palmata primarily contained mixed-linkage xylans and small amounts of sulfated galactans and cellulose. In contrast, the unfractionated polysaccharides of the other five species were rich in galactans displaying diverse 3,6-anhydro-galactose and galactose linkages with varied sulfation patterns. Different levels of cellulose were also observed. This glycosidic linkage method offers advantages for cellulose analysis over traditional monosaccharide analysis that is known for underrepresenting glucose in crystalline cellulose. Relative linkage compositions calculated from GC-MS and GC-FID measurements showed that anhydro sugar linkages generated more response in the latter detection method. This improved linkage workflow presents a useful tool for studying polysaccharide structural variations across red seaweed species. Furthermore, for the first time, relative linkage compositions from GC-MS and GC-FID measurements, along with normalized FID and total ion current (TIC) chromatograms without peak assignments, were analyzed using principal component analysis (PCA) as a proof-of-concept demonstration of the technique's potential to differentiate various red seaweed species.

Background: Educating college students about the importance of good sleep habits could lead to the adoption of healthier sleep routines, including sufficient sleep duration and sleep quality. The current pre-post study examines the impact of completing a sleep education program called “Sleep 101” on (1) sleep hygiene practices, (2) sleep quality, and (3) weekday and weekend sleep behaviors among college students. “Sleep 101” is an interactive online course developed to educate college students about the importance of sleep by addressing basic sleep physiology, the impact of sleep on mood, academic and physical performance, the interactions between sleep and various substances, and common sleep disorders. Methods: 338 college students were recruited from a midsized public university in the US and invited to participate in “Sleep 101”, of which 25 participants completed the baseline and post-intervention questionnaire. The Sleep Hygiene Index (SHI) was utilized to evaluate sleep hygiene practices, while standard questions were employed to assess weekday and weekend sleep behaviors and overall sleep quality. Results: Those who completed the study demonstrated a significant increase in weekday sleep duration and were less likely to engage in negative prior bedtime activities. In addition, 40% of those who completed baseline and post-intervention assessments noticed improvements in their sleep quality. Conclusion: These findings suggest that a brief online program is beneficial in improving sleep behaviors among college and could be a scalable approach to addressing current sleep issues and preventing future sleep problems in college students.

The profile of secondary metabolites occurring in apple cuticular layer is not only characteristic for particular apple cultivar, but also dynamically reflects various external factors in growing environment. In this study, the possibility to authenticate apple samples based on analysis of their cuticular layer extracts was investigated. Ultra-high-performance liquid chromatography coupled to high resolution tandem mass spectrometry (UHPLC-HRMS/MS) was employed for obtaining metabolomic fingerprints. In total, 274 authentic apple samples, four cultivars harvested within the seasons 2020 to 2022 in the Czech Republic and Poland were analysed. The generated complex data processed by univariate and multivariate statistical methods enabled to build classification models for discrimination of apple cultivars as well as their geographical origin. The models showed very good performance in differentiation of Czech and Polish samples for three of four cultivars: ‘Gala’, ‘Golden Delicious’ and ‘Idared’, moreover, the validity of the models was verified over harvest seasons. The diagnostic markers, besides metabolites of triterpene biosynthetic pathway, mainly represented wax esters. ‘Jonagold’, which is known to be susceptible to mutations, was the only cultivar for which the unambiguous classification of geographical origin was not possible.

Strawberry root rot caused by Neopestalotiopsis clavispora is one of the main diseases of strawberry and significantly impacts the yield and quality of strawberry fruit. There are now no effective control techniques available except for fungicide sprays, which may directly impact consumers. Biological control is becoming an alternative method for the control of plant diseases to replace or decrease the application of traditional synthetic chemical fungicides. Trichoderma is widely used as a biological agent for controlling strawberry root rot. In order to provide resources for screening the highly effective biocontrol fungus for controlling strawberry root rot caused by Neopestalotiopsis clavispora, the biocontrol mechanism,the control effects of Trichoderma asperellum CMT10 against strawberry root rot and growth-promoting effects on strawberry seedlings were investigated by plate culture, microscopy observation and root drenching methods.The results showed that CMT10 had obvious competitive, antibiotic and hyperparasitism effects on Neopestalotiopsis clavispora CMGF3. The CMT10 could quickly occupy nutritional space, and the inhibition rates of CMT10 against CMGF3 in confrontation culture on 7 d was 65.49%. The inhibition rates of volatile metabolite and fermentation metabolite produced by CMT10 against CMGF3 were 79.67% and 69.84%, respectively. The mycelium of strain CMT10 can act as hyperparasites by making contacting, winding and penetrating hyphae of CMGF3. Pot experiment showed that the biocontrol efficacy of CMT10 on strawberry root rot caused by Neopestalotiopsis clavispora was 63.00%. CMT10 had obvious promotion effect on strawberry growth, the plant height, root length, total fresh weight, root fresh weight, stem fresh weight and root dry weight, with the promotion rates were 20.09%, 22.39%, 87.11%, 101.58%, 79.82% and 72.33%, respectively. Overall, this study showed the ability of Trichoderma asperellum CMT10 to control strawberry root rot and their potential to develop as novel biocontrol agents to replace chemical fungicides for eco-friendly, sustainable agriculture.

Apis mellifera, especially weak ones, are highly vulnerable to Carpoglyphus lactis mites, which can rapidly infest and consume stored pollen, leading to weakened colonies and potentially colony collapse. This study aimed to ascertain and investigate the prevalence of this mite in honeybee colonies across 9 provinces in the Republic of Korea (ROK). A total of 615 honeybee colonies were collected, from 66 apiaries during the spring and 58 apiaries during the summer of 2023. A 1,242 bp segment of the the Cytochrome c oxidase subunit 1 (COI) gene was amplified using the polymerase chain reaction method. The detection levels of C. lactis in the honeybees were compared between winter and summer. Based on the COI sequence analysis, the nucleotide sequence similarity of C. lactis mites isolated in the ROK with those from China (NC048990.1) was found to be 99.5%, and with those from the United Kingdom (KY922482.1) was 99.3%. This study is the first report of C. lactis in Korean apiaries. The findings in this study demonstrate a significantly higher detection rate in winter, which is 4.1 times greater than that in summer (p &lt; 0.001). Furthermore, the results underscore the usefulness of molecular diagnostic techniques for detecting C. lactis mites.

COX II containing a dual core CuA active site is one of the three core subunits of mitochondrial Cco, which plays a significant role in the physiological process. In this report, the full-length cDNA of COXⅡ gene was cloned from Sitophilus zeamais, which had an ORF of 684 bp encoding 227 amino acids residues. The predicted COXⅡ protein had a molecular mass of 26.2 kDa with pI value of 6.37, and multiple sequence alignment and phylogenetic analysis indicated that Sitophilus zeamais COXⅡ had high sequence identity 78.51% with the COXⅡ of other insect species, especially similarity to sitophilus oryzae. This gene was subcloned into the prokaryotic expression vector pET-32a, and induced by IPTG in E.coli Transetta (DE3) expression system. Finally the COXⅡ with 6-His tag was purified using affinity chromatography with Ni²⁺-NTA agarose. WB showed the recombinant COXⅡ was about 44 kD, and the concentration of fusion protein was 50μg/mL. UV-spectrophotometer and infrared spectrometer analysis showed that recombinant COXⅡ could catalyze the oxidation of substrate Cytc, and influenced by AITC. It was found that AITC could form a hydrophobic region with COXⅡ protein via molecular docking, besides, a sulfur atom of AITC structure could form a length of 2.9 Å hydrogen bond with Leu-31. These results will provide valuable information for elucidating the role of COXⅡ in Sitophilus zeamais responses to AITC, meanwhile, it will helpful to carry out a point mutation in AITC binding sites for the future research.

The properties of the annual, semiannual and triennial oscillations (AO, SAO and TO) in the middle atmosphere have been investigated using the TIMED/SABER temperature data. The Lomb-Scargle and wavelet spectra were used to determine the dominant oscillations in the background temperature field. The AO is prominent at the mid-latitudes. The AO amplitudes present an asymmetry between the two Hemispheres, being larger in the mesosphere than in the stratosphere. The SAO dominates the tropical regions, with three amplitude maxima at altitudes of 45, 75, and 85 km. The SAOs in the upper mesosphere (75 km) are out of phase with those in the mesopause (85 km) in the tropical regions, which can generate an enhancement of 11 K at each equinox, contributing to the lower mesospheric inversion layer. The TO is significant in the tropical region, with amplitude being maximum at 35, 45 and 85 km. Result shows that there may be potential interaction by the TO with SAO at 85km at the equator. The relation between ENSO and TO has also been discussed. The ENSO signal may modulate the amplitude of the TO, mainly in the lower stratosphere. The real origin of the TO may lie in the wave-mean-flow interaction.

This paper is focused on typical rural settlements in the Stara Planina Mountain area in Serbia. They are distinguished by their authenticity, identity and character, and they have still not been destroyed by inappropriate development as is the case in some other mountain areas in Serbia, where the effects of urbanization, globalization and homogenization are obvious. Consequently, there is a need to prevent these effects in mountain areas where there is a threat of disbalance between development and the inherited natural and cultural values. The paper starts from several important concepts that relate contemporary approaches to cultural heritage preservation, place morphology and planning future development. The concept definitions from recent documents from related fields are used. These concepts are then applied to the area of Stara Planina Mountain and its rural settlements. The necessity for an integrative approach to planning this area with significant natural and anthropogenic potential is pointed out, including its integration into international programs of sustainable development.

The research reported on this paper was aimed at improving the overall efficiency of a PDO certified artisanal cheese production process. Being a PDO certified foodstuff by the EU, it is considered to have properties and qualities determined by the geographical environment in which is made, with its production taking place in a specific and determined geographical location, in this case the Serra da Estrela region. In that sense, the authors conducted a mapping according to a systemic perspective of the processes involved in the context of manufacturing and distribution of certified Serra da Estrela cheese. Numerous methods were used throughout the process, such as a systemic design analysis, and techniques derived from ethnographic methods, which led to the collection of data in the field and consequently provided the immersion of the researcher in genuine work situations. Critical points were identified and emphasized in the systemic map with the purpose of encouraging initiatives to address and overcome the gaps and inefficiencies detected. The systemic design analysis triggered the development of design work. Observations following an ethnographic approach identified ergonomic risks in cheese making during the process of cutting excess chips, fostering the emergence of musculoskeletal disorders at the wrist. A tool that fits best to the task at hand was developed. A prototype of the new tool enabled collecting feedback from use in the work context, in order to inform product development. The domains of agricultural production and microbiology, considering the specific microorganisms developed trough the ripening process of the cheese, turned out to be aspects of high importance for the issue under focus, contributing to a broader understanding of the ripening process and its risks, simultaneously improving the efficiency and success of cheese production. If it were not for the systemic analysis, which served as a link between the boundaries of distinct domains such as the risk of microorganism contamination, ergonomics, energy efficiency, legislation and regulation policies, transportation challenges and economic viability, approached throughout the research. Simultaneously creating bridges between them, the various problems might not have been detected in the first place, as they are usually addressed in specialized disciplines, predetermined by the restrictions of each specific area of knowledge. As a consequence of the development of this research, which was based on an analysis that sought to establish possible connections between various disciplines and tried to constantly maintain a holistic perspective, making new connections and observing the issues from a new angle, apart from the already established methodologies. All this allowed to lay out the seeds for the development of a plan to tackle the critical points identified by the systemic analysis reported in this paper.

Promoting green development has become an important way to optimize the ecological and economic structure and promote sustainable development. The Yangtze River Economic Belt is an important economic corridor in China, and it remains to be examined whether the implementation of environmental regulations has enhanced the green total factor productivity (GTFP) of cities. This paper calculates the green total factor productivity of 107 cities within the Yangtze River Economic Belt by using the super-efficient SBM model and the GML index with Chinese city panel data from 2007-2019 and measures the intensity of environmental regulations through textual analysis. The bidirectional fixed-effects model constructed in this paper suggests an inverted U-shaped relationship between environmental regulation and GTFP, which is confirmed by a series of robustness tests. Green technology innovation and advanced industrial structure play a mechanism role in this. In regions with lower levels of green technology and industrial structure, the inverted U-shaped relationship between environmental regulation and green total factor productivity is more significant. In addition, the phenomenon of GTFP rising and then falling because of environmental regulation is more obvious in cities in the middle and upper reaches of the Yangtze River and outside the urban agglomerations. Therefore, when formulating environmental regulation policies, it is necessary to balance the relationship between economic development and environmental protection and harmonize the environment and economic development of the entire Yangtze River Basin.

The wetlands in northeastern Bangladesh are home to some of the most prolific and valuable ecosystems on the planet, offering a wide range of benefits to both the local and wider communities. A limited number of research on this topic have been carried out in various wetlands in coastal hilsa, but none have been located in the northeastern region of Bangladesh. Thus, the goal of this study was to better understand the most commercially relevant species (anadromous hilsa) in northeastern Bangladesh as well as to assess the wetland ecosystem services more thoroughly with the contribution of their fish genetic resources. In addition to laboratory studies, fieldwork was done in the fishing settlements along the Surma River, Hakaluki Haor, and Tanguar Haor. The study classified 77 fish species into 21 subcategories of ecosystem services, of which 56% were not threatened, 17% were vulnerable, and 10% were highly endangered. The species Hilsa was found to be the most economically significant, accounting for 1% of the GDP overall. The study determined if the hilsa stock of the examined wetlands maintains a single or several subpopulations in comparison to other parts of the country when they migrate from saline water to northeastern Bangladesh (freshwater). But when compared to other groups, the FST score was between 0.000 to 0.017, indicating that the populations are identical and that there is genetic material sharing between them. Additionally, these statistics imply that the Sylhet haor and adjacent river systems contain a single stock of Hilsa fish. Nevertheless, a number of stresses and risks, including overexploitation, illicit and destructive fishing, siltation, and natural disasters like flash floods, have been linked to changes in the supply of hilsa and other ecosystem services. This study also emphasizes the necessity of policy attention and research to address the concerns.

In this paper, we introduce a specialized, fully automated experimental arrangement designed for assessing the effectiveness of augmented and virtual reality technologies in healthcare setting and explore its design principles focusing on depth sensor characterization. The main goal of this project is to establish a robust benchtop platform for the quantitative evaluation of extended reality technologies in a controlled environment, emphasizing the practical assessment of augmented reality head-mounted devices. We outline a design concept and considerations for an experimental configuration aimed at creating a realistic testing environment. This apparatus comprises an observation platform mounted on a three-degree-of-freedom motorized system and a test phantom stage. Focusing on real-case scenarios, we utilized a range of sensors, including readily available range-sensing cameras and commercial augmented reality headsets, such as the Intel RealSense L515 LiDAR camera, mounted on the motion control system. The setup enabled automated data collection and facilitates controlled assessments and validation of various facets of augmented reality technologies, including object, hand, and head tracking, as well as static and dynamic image registration. This paper describes the system architecture, the process of automated data collection, and presents several evaluation studies conducted with this setup, providing insights into the quality and temporal noise associated with static or moving objects or observers in augmented reality applications.

To conduct high-precision and high-resolution numerical simulation of complex flow structures in turbomachinery, a high-order finite volume weighted essentially non-oscillatory (WENO) scheme for the large eddy simulation (LES) is improved and embedded into the three-dimensional viscous unsteady CFD solver NUAA-Turbo. Firstly, the spectral characteristics and unsteady convergence of the improved WENO scheme are studied. Compared with the classical WENO scheme, the improved WENO scheme has better dissipation and dispersion characteristics and faster convergence speed. Then, the coefficient CW of the Wall-Adapting Local Eddy-viscosity (WALE) model is calibrated by decaying homogeneous isotropic turbulence (DHIT) test case. Finally, the scheme is applied to conduct high-precision LES calculations of turbulent boundary layer flow, supersonic compression corner flow, and low-pressure turbine cascade separation flow. The numerical simulation results show that this WENO scheme has excellent shock wave capture ability and turbulence resolution and can capture more flow field details with less mesh size, greatly reducing the computational cost and laying a foundation for large-scale engineering application of LES.