This investigation mainly focused on the microstructural analysis of Al based hybrid metal matrix composites. Aluminium as base metal and reinforced with 2% B4 C, ZrO2 (2%,4%,6%), SiC (4%,8%,12%). Specimens were manufactured by using conventional stir casting technique. Hybrid metal matrix composites were examined by using Scanning electron microscope. This research explained XRD, EDS and Fractography analysis. This investigation shows the reinforced material has given better results in all aspects than pure Al6061 alloy and homogeneous dispersion of particles inside the matrix. Porosity, delamination, cracks, particle distributions were observed through microstructural analysis. Additionally determined the crystal size of pure Aluminium 6061 alloy and hybrid composites.

In this study a material based on Polyethylene (PE) and Microcrystalline Cellulose (MC) was developed as a breathable packaging film. Surface functionalization of MC with 3 aminopropyltriethoxysilane (APTES) shows to be an efficient alternative to tailor their properties and increase opportunities for the application of MC on the reinforcement of polymers such polyethylene (PE). Functionalization of MC with mentioned silane derivative was achieved using a green method and later used on the development of composites with PE in three percentages (1, 3 and 5%). All the materials were prepared by melt blending and characterized, in terms of structural properties (ATR-FTIR and FTIR in transmittance, EDX, SEM), thermal properties (DSC and TGA), thermomechanical properties (DMA), contact angle measurements and permeability to oxygen and water vapor. The materials demonstrated to have potential to be used as breathable film packaging of fresh products.

Negative temperature coefficient (NTC) materials are usually based on ceramic semiconductors and electrons are involved in their transport mechanism. A new type of NTC material, adequate for alternating current (AC) applications, is represented by zeolites. Indeed, zeolites are single-charge carrier ionic conductors with a temperature-dependent electrical conductivity. In particular, electrical transport in zeolites is due to the monovalent charge-balancing cations, like K⁺, capable of hopping between negatively charged sites in the aluminosilicate framework. Owing to the highly non-linear electrical behavior of the traditional electronic NTC materials, the possibility to have alternative types of materials, showing linearity in the electrical behavior, is very desirable. Among different zeolites, the natural clinoptilolite has been selected for investigating the NTC behavior since it is characterized by high zeolite content, convenient Si/Al atomic ratio, good mechanical strength, due to its compact microstructure, and low toxicity. Clinoptilolite has shown a rapid and quite reversible impedance change under heating, characterized by a linear dependence on temperature. X-ray diffraction (XRD) has been used to identify the natural zeolite, to establish all types of crystalline phases present in the mineral, and to investigate the thermal stability of these phases up to 150°C. X-ray photoelectron spectroscopy (XPS) analysis has been used for the chemical characterization of the natural clinoptilolite sample, providing important information on the cationic content and framework composition. In addition, since electrical transport takes place in the zeolite free-volume, a Brunauer–Emmett–Teller (BET) analysis of the mineral has been also performed.

We propose an algorithm for generating a panoramic image of a pipe’s inner surface based on inverse perspective mapping (IPM). For efficient crack detection, we used only perspective images of the pipe interior that can be obtained with a single lens camera instead of those taken with a 360-degree camera or a 3D depth camera. Frontal images taken while passing through the pipe were converted to images of the inner surface of the pipe using IPM. We derived a generalized IPM formula that considers the slope of the image plane to correct image distortion caused by the tilt of the plane; this IPM formula was derived based on the vanishing point of the perspective image, which was detected using optical flow techniques. Finally, the multiple transformed images with overlapping areas were combined via image stitching to create a panoramic image of the inner pipe surface. To validate our proposed algorithm, we restored images of pipe inner surface using a 3D pipe model and used these images for crack detection.

The design of processing routes involving the presence of the liquid phase is mainly associated with the knowledge of its surface and transport properties. Despite this need, due to experimental difficulties related to high temperature measurements of metallic melts, for many alloy systems neither thermodynamic nor thermophysical properties data are available. A good example lacking these datasets represents the Ir-Si system, although over the last fifty years, the structures and properties of its solid phases have been widely investigated. To compensate the missing data, the Gibbs free energy of mixing of the Ir-Si liquid phase was calculated combining the model predicted values for the enthalpy and entropy of mixing using Miedema’s model and Free Volume Theory, respectively. Subsequently, in the framework of statistical mechanics and thermodynamics, the surface properties were calculated using the Quasi Chemical Approximation (QCA) for the regular solution, while to obtain the viscosity, the Moelwyn-Hughes (MH) and Terzieff models were applied. Subsequently, the predicted values of the abovementioned thermophysical properties were used to model the non-reactive infiltration isotherm of Ir-Si (eutectic) / SiC system.

conclusions. The blends of ultrahigh molecular weight polyethylene/polypropylene (UHMWPE/PP) possess excellent processability, but limited by its reduced mechnical properties. Herein, the high mechanical properties and wear—resistance UHMWPE/PP composites were fabricated by the addition of silicon carbide (SiC) nanoparticles under a consecutive elongational flow without any other additives or solvents. The morphology and thermal properties, mechanical properties, wear resistance as well as scratch resistance of UHMWPE/PP/SiC composites were investigated . The mechanical properties and friction resistance of composites increase initially then decrease with the increase content of SiC. The optimum mechanical properties of UHMWPE/PP/SiC composites are achieved when the content of SiC is 3 phr. In addition, both the hardness and scratch resistance of composites improved upon increasing the content of SiC. These improved mechanical properties and wear resistance originate from the well disperison of SiC nanoparticles along with favourable interfacial adhesive under a consecutive elongational flow.

Thermoregulation is important for maintaining homeostasis of our body. It can be easily broken under anesthesia. An appropriate method to measure the core body temperature is needed, especially for elderly patients because the efficiency of thermoregulation gradually decreases with age. The aim of this study was to examine the accuracy and feasibility of using of SpotOn® sensor in lower extremity orthopedic surgery in elderly patients aged over 80 years by comparing a SpotOn® sensor with two other reliable minimal-invasive methods: a tympanic membrane thermometer and a bladder thermometer. This study enrolled 45 patients aged over 80 years who were scheduled to undergo a lower extremity surgery. Body temperature was measured using a SpotOn® sensor, tympanic membrane thermometer and bladder thermometer. Agreements between the SpotOn® sensor and the other two methods were assessed using Bland and Altman plots for repeated measures adjusted for unequal numbers of measurements per patient. Compared with TempBladder, bias and limits of agreement for TempZHF were 0.07℃ ± 0.58℃. Compared with TempTympanic, bias and limits of agreement for TempZHF were -0.28℃ ± 0.61℃. 3M SpotOn® sensor using ZHF method for patients aged over 80 years undergoing lower extremity surgery shows feasible measurement value and sensitivity.

To design properly and optimizate liquid-assisted processes such as reactive infiltration for fabricating light weight and corrosion resistant SiC/TiSi2 composites, the interfacial phenomena taking place when liquid Si-rich Si-Ti alloys are in contact with glassy carbon (GC) were investigated for the first time by wetting tests performed by both the sessile and pendant drop methods at T = 1450°C. Specifically, two different Si-rich Si-Ti alloys were selected, and the obtained results in terms of contact angle values, spreading kinetics, reactivity, and developed interface microstructures were compared with experimental observations previously obtained for the liquid Si-rich Si-Ti eutectics processed under the same operating conditions. The increase of the Si content did not affected the final contact angle values. Contrarily, the final developed microstructure at the interface as well as the spreading kinetics were observed as weakly dependent on the composition. From the practical point of view, Si-Ti alloy compositions with a Si-content falling in the simple eutectic region of the phase diagram might be potentially used as infiltrant materials of C- and SiC-based composites.

Graphene hybrid-filler polymer composites have emerged as prominent materials that revolutionize heavy industries. This study encapsulates the in-depth analysis of different influential factors such as filler/graphene type, aspect ratios, dispersion methods, filler-matrix compatibility, fiber orientation, synergistic effects, different processing techniques, and post-curing conditions that affect the processing, properties and determine the resultant applications of graphene hybrid polymer composites. Additionally, it discusses the substantial role of graphene collaboration with other fillers such as carbon nanotubes, silica, nano-clays and metal oxides to produce functionalized hybrid polymer composites with synergistically enhanced tailored properties to offer solutions for heavy industries like aerospace, automotive, electronics, and energy harvesting. The review concludes with some suggestions and outlook on the future of these composite materials by emphasizing the need for continued research to fully optimize their potential.

This paper addresses a new micromechanical model to predict biaxial tensile moduli of plain weave fabric (PWF) composites by considering the interaction between the orthogonal interlacing strands. The two orthogonal yarns in micromechanical unit cell (UC) were idealized as the curved beams with a path depicted by using sinusoidal shape functions. The biaxial tensile moduli of PWF composites were derived by means of the minimum total complementary potential energy principle founded on micromechanics. The biaxial tensile tests were respectively conducted on the RTM-made EW220/5284 PWF composites at five biaxial loading ratios of 0, 1, 2, 3 and ∞ to validate the new model. The predictions from the new model were compared with experimental data and good correlation was achieved between the predictions and actual experiments, demonstrating the practical and effective use of the proposed model. Using the new model, the biaxial tensile moduli of plain weave fabric (PWF) composites could be predicted based only on the properties of basic woven fabric.

To better understand the shape memory materials and self-healing materials, a new series of liquid-crystalline shape memory polyurethane (LC-SMPU) composites, named SMPU-OOBAm, were successfully prepared by incorporating 4-octyldecyloxybenzoic acid (OOBA) into the PEG-based SMPU. The effect of OOBA on the structure, morphology and properties has been carefully investigated. The results demonstrate that SMPU-OOBAm have liquid crystalline properties, triple-shape memory properties and self-healing properties. The incorporated OOBA promotes the crystallizability of both soft and hard segments of SMPU, and the crystallization rate of the hard segment of SMPU decreases when the OOBA-content increases. Additionally, the SMPU-OOBAm forms a two-phase separated structure (SMPU phase and OOBA phase), and it shows two-step modulus changes upon heating. Therefore, the SMPU-OOBAm shows triple-shape memory behavior, and the shape recovery ratio decreases with an increase in the OOBA content. Finally, SMPU-OOBAm shows self-healing properties. The new mechanism can be ascribed to the heating-induced “bleeding” of OOBA in the liquid crystalline state and the subsequent re-crystallization upon cooling. This successful combination of liquid crystalline properties, triple-shape memory properties and self-healing properties make the SMPU-OOBAm composites with many promise applications in smart optical devices, smart electronic devices and smart sensors.

In the present work, a predictive modelling and optimization with the adaptive network based fuzzy inference system(ANFIS) modelling of mechanical properties of laser-coated NB/SiC/Ni welds was studied based on Taguchi design by laser cladding. An ANFIS model based on a Sugeno type fuzzy inference system was developed for predicting the hardness properties of SiC/BN/Ni welds by laser cladding with experimental data required for network training and prediction. Based on analysis of variance, three important factors were taken as inputs for the fuzzy logic inferences, while the hardness properties was taken as the output of the ANFIS. The microstructure of welds were analysed using scanning electron microscopy with an energy dispersive X-Ray spectrometer. Highly developed leaf-like dendrites and eutectic crystals were found in some areas of the melting zone for the BN/SiC/Ni weld, which was significantly hardened. The ANFIS model based on Taguchi's design provides a better pattern of response because the predicted and experimental values were highly similar. As a result, a satisfactory result was achieved between the predicted and experimental values of hardness in laser-coated NB/SiC/Ni welds, whereby the success and validity of the method was verified.

Background: Fiber-reinforced composites (FRCs) have been proposed as an alternative to traditional metal alloys for the realization of frameworks in full-arch implant supported prostheses. The aim of the present in vitro study was to evaluate the deflection under load of seven prostheses endowed with frameworks made of different materials, including different types of fiber reinforced composites (FRCs). Methods: A master cast with four implant analogues in correspondence of the two lateral incisors and the two first molars was used to create full-arch fixed prostheses with the same shape and different materials. Prostheses were made in different materials (framework+veneering material): gold alloy+resin (Au+R), titanium+resin (Ti+R), FRC with multi-directional carbon fibers+resin (ICFRC+R), FRC with unidirectional carbon fibers+composite (UCFRC+C), FRC with glass fibers+resin (GFRC+R), FRC with glass fibers+composite (GFRC+C), resin (R, full-acrylic prosthesis). Flexural tests were conducted using Zwick/Roell Z 0.5 machine and the deflection of the lower surface of the prosthesis was measured in order to obtain load/deflection graphs. Results: Greater rigidity and less deflection were recorded for UCFRC+C, GFRC+C, followed by Ti+R, and Au+R. The greatest deformations were observed for resin alone, ICFRC+R and GFRC+R. The results were slightly different in the incisal region probably due to the greater amount of veneering material in this area. Conclusions: When used to realize full-arch frameworks, Au and Ti allow a predictable mechanical behavior with gradual deformations with increasing load. UCFRC also demonstrated good outcomes and less deflection than ICFRCs when loaded. The GFRC full-arch framework may be a valid alternative, however showed greater deflections. Further studies are needed in order to evaluated how different prosthesis design and material thickness might affect the outcomes.

Nano Silicon carbide reinforced aluminum (Al/nanoSiC) metal matrix composites are attractive because of their superior properties such as high strength and stiffness, Application of aluminum in technological and structural application is growing steadily. The major limitation for metal matrix nano composites, however, is their propensity to brittle fracture. The new technologies and new materials are two basic aims for companies. In this research, the effect of addition Al/SiC nano particles on microstructure and mechanical properties of pure aluminum has been investigated. Pure aluminum powder and various fractions of SiC particles with an average diameter of 50 nm were milled by a high-energy planetary ball mill to produce nanocrystalline Al–SiC nanocomposite powders. Pressing and sintering applied to consolidate powders to tablet shape. Then the samples were rolled to cylindrical shape. The nano SiC Percentage were 0%, 2.5%, 5%, 7.5%, 10% , 12,5% and 15%. Mechanical tests such as tensile, hardness, fracture toughness and young’s modules measurement carried out to study the mechanical behavior of each alloy. Scanning electron microscopy was used to study the morphology and microstructure of nanocomposite powders and bulk samples. The role of wt% fraction of SiC nanoparticles was investigated. The results shows that the addition of SiC nano particles has significant influence on the microstructure and mechanical properties of composites and usually the optimum properties depends on wt% SiC.

SiC is a material with excellent mechanical and thermal properties, but with a high production cost. Obtaining SiC by reactive infiltration is an attractive method and at a much lower cost than the traditional sintering process. However, the reactive infiltration process presents a serious problem, which is the high residual silicon content, which decreases its range of application. The replacement of silicon with silicides is a widely used alternative. The present investigation shows the good mechanical properties of the SiC/IrSi₃ composite material obtained by reactive infiltration of SiC/C preforms with Ir-Si alloys. The thermomechanical analysis shows a high compatibility of silicide with SiC. The presence of the silicide shows a substantial improvement against the oxidation of the SiC/Si composites.

Aluminum matrix nanocomposites have been the subject of much attention due to their extraordinary mechanical properties and thermal stability. This research focuses on producing and characterizing an aluminum matrix reinforced with silicon carbide (SiC) nanometric particles. The conventional powder metallurgy route was used to produce the nanocomposites, and the dispersion and mixing process was carried out by ultrasonication. The conditions of the dispersion and the volume fraction of the SiC were evaluated in the production of the nanocomposites. Microstructural characterization was carried out using optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and electron backscatter diffraction (EBSD). Mechanical characterization was carried out using hardness and tensile tests. The dispersion agent was investigated, and isopropanol leads to better dispersion with fewer agglomerates. Increasing the volume fraction of the reinforcement improves the hardness of the nanocomposites. However, greater agglomeration of the reinforcement is observed for larger volume fractions. The greatest increase in hardness (77% increase compared to the hardness of the Al matrix) is obtained with 1.0 vol % of SiC, corresponding to the sample with the best dispersion. The mechanical characterization through tensile tests attests to the effect of the reinforcement on the Al matrix. The main strengthening mechanisms identified were the load transfer, the texture hardening, Orowan strengthening, and the increase in the density of dislocations in the nanocomposites.

In this study, the impact of the addition of high-aspect-ratio nano-ettringite to photocurable epoxy acrylate resin was explored, with a specific focus on the changes observed in viscosity, shrinkage, tensile strength, and elongation at the break of composites formed. Herein, the nano-ettringite samples were modified using KH-570. The 3 wt% or 6 wt% KH-570-modified and unmodified nano-ettringite were dispersed into the resin by ultrasonic treatment in conjunction with mechanical stirring. The grafting effects of nano-ettringite onto KH-570 were analyzed through scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric (TG) analysis, and Fourier transform infrared spectroscopy (FTIR). The results demonstrate that increased dosages of unmodified and modified nano-ettringite led to increased viscosity of the composite while reducing shrinkage. At the same dosage, the photocurable resin with modified nano-ettringite demonstrated a lower shrinkage and a higher tensile strength. Notably, when the amount of modified nano-ettringite was 3 wt%, the highest tensile strength of the composite was 64.61 MPa, presenting a 72.57% increase compared to the blank sample. Furthermore, the incorporation of modified nano-ettringite as a filler provides a new perspective for improving the performance of photocurable epoxy acrylate resin composites.

The carbonyl iron particles were dispersed in a polychloroprene rubber (CR) matrix under an external magnetic field for practical application as microwave absorption composites film. The film prepared under external magnetic field with a thickness of only 0.54 mm showed least reflection loss of -15.98 dB and the reflection loss value less than -10.0 dB over the frequency range of 11.4~14.8 GHz. In comparison with the microwave absorption properties of calculation by transmission line theory based on the tested relative complex permittivity and permeability and film prepared by general route without external magnetic field, the film made with external magnetic field exhibited more excellent microwave absorption properties, strongly depending on the increment of anisotropy and rearrangement of magnetic particles. The results indicated the composite film made under external magnetic field have excellent microwave absorption properties, which suggest that the composites thin film could be used as a thinner and lighter microwave absorber.

The thermal degradation behaviour of 10:90 and 90:10 blends of Polyethylene Terephthalate (PET) and petroleum coke has been investigated using mechanical alloying (milling) at 300 rpm and for periods up to 1-10 hours. Milled specimens were characterised using SEM and x-ray diffraction; their thermal degradation behaviour was investigated using thermo-gravimetric analyser (TGA) for temperatures up to 1200°C. Whereas PET specimens showed a tendency towards flattening out and increased surface area during collisions in ball mills, petroleum coke particles tended to break down into smaller particles. 10:90 and 90:10 blends of PET and coke showed significant microstructural evolution with increasing speeds and time including fracture, strain hardening and re-welding. X-ray diffraction results showed clear evidence for increasing amorphous component in petroleum coke without much influence on PET crystallinity. Thermo-gravimetric results showed a significant increase in the overall degradation and much higher weight losses associated with mechanical alloying. This study has shown that mechanical alloying could be used to modify the degradation behaviour of coke/plastic blends and corresponding yield during pyrolysis with implications for plastic waste management.

Concrete contributes 8% of all global carbon emissions making the need to find substitute critical for environmental sustainability. Research has indicated the potential for recycled plastics to be used as concrete substitutes. This study extends existing research by investigating the use of polycarbonate (PC) in plastic sand bricks as a mechanical equivalent to concrete. PC has high compressive strength, durability, impact strength, thermal resistivity, clarity, fatigue resistance, and UV resistance. This work provides a method and mold to produce a matrix of sand-plastic sample compositions with dimensions adhering to ASTM D695 standard for compressive properties of rigid-plastic. Compositions of 0% (control), 20%, 30%, 40%, and 50% sand by weight were tested. Samples were tested for compressive strength until yield and stress-strain behaviors plotted. The results for 100% PC demonstrated an average and maximum compressive strength of 71 MPa and 72 MPa, respectively. The 50% PC and 50% sand composition yielded an average and maximum compressive strength of 71 MPa and 73 MPa respectively with an increase in compressive stiffness, and transition to shear failure resembling cement. With a composite density of 1.86 g/cm3 against concrete’s average 2.4 g/cm3, and a compressive strength exceeding commercial concrete demands of 23.3 MPa to 30.2 MPa, this lightweight alternative meets the strength demands of concrete, reduces the need for new construction materials, and provides an additional recycling opportunity for nonbiodegradable waste plastic.

We report on metastable defects introduced in n-type 4H-SiC material by epithermal and fast neutron irradiation. The epithermal and fast neutron irradiation defects in 4H-SiC are much less explored compared to electron or proton irradiation induced defects. In addition to silicon vacancy (Vsi) and carbon antisite-carbon vacancy (CAV) complex, the neutron irradiation has introduced four deep level defects, all arising from the metastable defect, the M-center. The metastable deep level defects were investigated by deep level transient spectroscopy (DLTS), high-resolution Laplace DLTS (L-DLTS) and isothermal DLTS. The existence of the fourth deep level M4, recently observed in ion implanted 4H-SiC, has been additionally confirmed in neutron irradiated samples. The isothermal DLTS technique has been proven as a useful tool for studying the metastable defects.

This review summarizes the most recent developments of research on protozoan parasite infections ac-quired through food and drinking water and is aimed at gathering updated knowledge on the risk factors, illnesses caused, and measures for prevention. Reports included dated from 2019 to the present and regarded recent outbreaks and cases of severe infec-tions, prevalence in different population segments and food handlers, and occurrence in food and drinking water. Cryptosporidium spp., Entamoeba histolytica, Giardia intestinalis, Trypanosoma cruzi and Toxoplasma gondii were the microorganisms most frequently involved in large outbreaks and/or severe infections, while Cyclospora cayetanensis was most frequently involved in single case reports. Cystoisospora belli was implied in severe infections in immunocompromised patients, while Blastocystis homi-nis, Sarcocystis spp., Dientamoeba fragilis, Endolimax nana and Pentatrichomonas hominis appeared to be less relevant for number of symptomatic infections and pathogenic potential. A progressive improvement in surveillance of protozoan infections and infection sources was highlighted, especially in developed countries. The apparent increase in cases was concomitant with the implementa-tion of reporting systems and the application of molecular diagnostic methods that represent valuable in-struments for establishing epidemiological links and preventing or limiting outbreaks. The pathogenic role and sources of infection should be better elucidated for some species.

Polymer-derived SiC-polycrystalline fiber (Tyranno SA) shows excellent heat-resistance up to 2000^oC, and relatively high strength. Up to now, through our research, the relationship between the strength and residual defects of the fiber, which were formed during the production processes (degradation and sintering), has been clarified. In this paper, we addressed the relationship between the production condition and the surface roughness of the obtained SiC-polycrystalline fiber, using three different raw fibers (Elementary ratio: Si₁Al_0.01C_1.5O_0.4~0.5) and three different types of reactor (Open system, Partially-open system, and Closed system). With increase in the oxygen content in the raw fiber, the degradation during the production process easily proceeded. In this case, the degradation reactions (SiO+2C=SiC+CO and SiO₂+3C=SiC+2CO) in the inside of each filament become faster, and then the CO partial pressure on the surface of each filament is considered to be increased. In consequence, according to Le Chatelier’s principle, the surface degradation reaction and grain growth of formed SiC crystals would be considered to become slower. That is to say, using the raw fiber with higher oxygen content and closed system (highest CO content in the reactor), much smoother surface of the SiC-polycrystalline fiber could be achieved.

.With the increasing use of carbon fiber reinforced plastics in various area, carbon fiber composites based on prepregs have attracted attention in industries and academia research. However, prepreg manufacturing processes are costly, and the strength of structures varies depending on the orientation and defects (pores and delamination). For non-contact evaluation of internal defects, we proposed lock-in infrared thermography to investigate orientation angles after a compression test. We also conducted a drop-weight impact test to study the behaviour of the composites after impact according the fibers orientation for composite fabricated using unidirectional carbon fiber prepregs. Using CAI tests, we determined the residual compressive strength and confirmed the damage modes using a thermal camera. The results of the drop weight impact tests show that the specimen laminated at 0° suffered the largest damage because of susceptibility of the resin to impact. In contrast, the specimens oriented in of 0°/90° and +45°/–45° directions transferred more than 90% of the impact energy back to the impactor because of the lamination of fibers in the orthogonal directions. Furthermore, the specimens that underwent complete damage in the impact tests were subjected to the lock-in method and showed internal delamination and cut fibers. With the finite elements analysis, the damage of each ply could be observed. Moreover, the temperature differences in the residual compression tests were not significant.

Silicon carbide single crystal (SiC) has been widely used in the field of power devices, while it is difficult to fabricate ultra-flat surface by traditional manufacturing technologies due to its difficult-to-machine property. This paper investigates the interaction process during femtosecond laser ablation of crystalline silicon carbide based on the two-temperature model simulation and experimental study. The findings reveal that parameters such as laser pulse energy, scanning interval, and defocus amount exert significant influence on ablation depth, roughness, and surface morphology. The femtosecond laser proves effective in removing surface defects from cut SiC substrates, albeit resulting in increased surface roughness. However, subsequent polishing treatment of the laser-ablated silicon carbide surface can mitigate this roughness, underscoring the feasibility of laser surface ablation for silicon carbide single crystals.

An extension of the Stoney formula for the case of a back side metallized 8” silicon taiko wafer has been developed, in the elastic regime, within the frame of the theory of elasticity. A good correlation between the calculated warpage, determined by the stress released by a given back side metallization (BSM), and the corresponding experimental warpages of the same thick metal layers deposited on an 8” silicon taiko wafer provides evidences of the correctness of the developed theory. This development suggests the possibility to extend this approach to the case of 8” taiko wafers based on a wide band gap semiconductor such as silicon carbide (SiC).

Achieving the thermal conductivity required for efficient heat management in semiconductors and other devices requires the integration of thermally conductive ceramic fillers at concentrations of 60 vol% or higher. However, the increased filler content often negatively affects the mechanical properties of the composite matrix, limiting its practical applicability. To address this issue, in this paper, we present a new strategy to reduce the required ceramic filler content: the use of a thermally conductive ceramic composite filler with carbon nanotubes (CNT) grown on aluminum nitride (AlN). We have combined catalyst coating technology with vacuum filtration to ensure that the catalyst is uniformly applied to micrometer-sized AlN particles, followed by efficient and uniform synthesis of CNTs using a water-assisted process in a vertical furnace. By carefully controlling the number of vacuum filtration cycles and the growth time of the CNTs, we demonstrate precise control over the number and length of the CNT layers, thereby adjusting the properties of the composite to the intended specifications. When AlN/CNT hybrid fillers are incorporated into silicone rubber, while maintaining the mechanical properties of rubber, the thermal diffusivity achieved at reduced filler levels exceeds that of composites using AlN-only or simultaneous AlN and CNTs formulations. This demonstrates the critical role of CNTs on AlN surfaces. Our study represents a significant advancement in the design of thermally conductive materials with potential implications for a wide range of applications.

In this paper, the single event burnout(SEB) and reinforcement structure of 1200V SiC MOSFET (SG-SBD-MOSFET) with split gate and schottky barrier diode(SBD) embedded were studied. The device structure was established using Sentaurus TCAD, and the transient current changes of single event effect(SEE), SEB threshold voltage, as well as the regularity of electricfield peak distribution transfer were studied when heavy ions were incident from different regions of the device. Based on SEE analysis of new structural device, two reinforcement structure designs for SEB resistance were studied, namely the expansion of P+body contact area and the design of multi-layer N-type interval buffer layer. Firstly, two reinforcement schemes for SEB were analyzed separately, and then comprehensive design and analysis were carried out. The results showed that the SEB threshold voltage of heavy ions incident from the N+source region was increased by 16% when using the P+body contact area extension alone; When the device is reinforced with multi-layer N-type interval buffer layer alone, the SEB threshold voltage increases by 29%; The comprehensive use of P+body contact area expansion and multi-layer N-type interval buffer layer reinforcement increased the SEB threshold voltage by 33%. Overall, the breakdown voltage of the reinforced device decreased from 1632.935V to 1403.135V, which can be seen as reducing the remaining redundant voltage to 19%. The device performance was not significantly affected.

Intercalation of noble metals can produce giant Rashba-type spin-orbit splittings in graphene. The spin-orbit splitting more than 100 meV has not yet been achieved in graphene on a metallic or a semiconductor substrate. Here, we report the p-type graphene obtained by Pt intercalation of zero-layer graphene on SiC substrate. The spin splitting of ∼200 meV was observed at a wide range of binding energies. Comparing the results of theoretical studies of different models with the experimantal ones measured by spin-ARPES, XPS and STM methods, we came to the conclusion that inducing giant spin-orbit splitting requires not only a fairly close arrangement of graphene to Pt layer, but also the presence of graphene corrugation caused by non-flat Pt layer. This makes it possible to find a compromise between strong hybridization and increased spin-orbit interaction. In our case, this is achieved by forming Pt submonolayer ordered on a nanometer scale under graphene.

In this review paper, an overview of the application of n-type 4H-SiC Schottky barrier diodes (SBDs) as radiation detectors is given. We have chosen 4H-SiC SBDs among other semiconductor devices such as PiN diodes or metal-oxide-semiconductor (MOS) structures, as significant progress has been achieved in radiation detection applications of SBDs in the last decade. Here, we present the recent advances at all key stages in the application of 4H-SiC SBDs as radiation detectors, namely: SBDs fabrication, electrical characterization of SBDs, and their radiation response. Main achievements are highlighted, and main challenges are discussed.

In the present paper, Co-B/SiC composite coatings were obtained via electrodeposition from colloidal suspensions with different concentrations of SiC particles and subsequent heat treatments at 350 °C. The composition, morphology and structure of the Co-B/SiC composite coatings were analyzed using glow discharge spectrometry (GDS), scanning electron microscopy (SEM) coupled with energy-dispersive spectroscopy (EDS) and X-ray diffraction (XRD). Hardness and tribological properties were also studied. The results showed that an increase in the SiC concentration in the colloidal suspensions resulted in both an increase in the SiC content and a decrease in the B content in the obtained Co-B/SiC coatings. The Co-B/SiC coatings were adherent, glossy and soft and exhibited a homogeneous composition in all thicknesses. By contrast, an increase in the SiC particle content of the Co-B/SiC composite coating from 0 to 2.56 at.% SiC reduced the hardness of the film from 680 to 360 HV and decreased the wear volume values from 1180 to 23 mm³ N^-1 m^-1, respectively (that is, the wear resistance increased). Moreover, when the Co-B/SiC coatings with SiC content ranging from 0 to 2.56 at.% SiC were subjected to a heat treatment process, the obtained coating hardness values were in the range of 1200 to 1500 HV and the wear volume values were in the range of 382 to 19 mm³ N^-1 m^-1.

In this work SiC-Ti3AlC2 and TiC-Ti3AlC2 composites produced by additive manufacturing are investigated. The fused granules fabrication (FGF) method as one of the material extrusion additive manufacturing (MEAM) technology is used to obtain composite samples. Composites with different ratios between components and different powder:polymer ratios are investigated. The technological features of the additive formation of composites are investigated, as well as their structure and properties. The optimal sintering temperature to form the best mechanical properties for both composites is 1300 °C. The composites have a regulatable porosity. Ti3AlC2 content, sintering temperature, and polymer content in the feedstock are the main parameters that regulates the porosity of FGF samples.

Changes in the atomic and electronic structure of silicon carbide 3C-SiC (β-SiC), resulting from lead adsorption, have been studied within the density functional theory. The tests were conducted for three representative surfaces with varying degrees of lead coverage. Results indicate that chemisorption occurs, with the strongest binding, found on the hexagonal surface (111) in interaction with three dangling bonds. The adsorption energy rises with increasing coverage, especially as the surface approaches saturation. Analysis of the data was focused on parameters important for corrosion processes such as bond distances, binding energies, Bader charges and charge density difference.

In-situ grown C_0.3N_0.7Ti and SiC, which derived from non-oxide additives Ti₃SiC₂, are proposed to densify silicon nitride (Si₃N₄) ceramics with enhanced mechanical performance. Remarkable increase of density from 79.20% to 95.48% could be achieved for Si₃N₄ ceramics with 5vol% Ti₃SiC₂. The capillarity of decomposed Si from Ti₃SiC₂, and in-situ reaction between nonstoichiometric TiC_x and Si₃N₄ were believed to be responsible for densification of Si₃N₄ ceramics. An obvious enhancement of flexural strength and fracture toughness for Ti₃SiC₂ doped Si₃N₄ ceramics was observed. The maximum flexural strength of 795 MPa for Si₃N₄ composites with 5vol% Ti₃SiC₂ and maximum fracture toughness of 6.97 MPa^.m^1/2 for Si₃N₄ composites with 20vol% Ti₃SiC₂ are achieved when mixed powders are hot-press sintered at 1700℃. Pull out of elongated Si₃N₄ grains, crack bridging, crack branching and crack deflection were demonstrated to dominate enhance fracture toughness of Si₃N₄ composites.

Although the potential of natural minerals for purification of liquid radioactive wastes (LRW) from radionuclides has been widely studied, the use of hybrid polymer composites made of zeolite is still rather scarce. This article reports on the preparation of zeolite based hybride polymer composites using the in-situ polymerization technique in the body of mineral matrix and its intercalated with copper ferrocyanide (CuFC) forms. This hybrid polymer composites have shown unique and enhanced properties as compared to the individual mineral. The change in conventional properties of two mixed minerals such as zeolite and bentonite and their intercalated with CuFC forms were probed using technics such as scanning electron microscopy (SEM), X-ray diffraction (XRD), Mossbauer spectroscopy (MS) and FT-IR analysis. The totality of analysis showed a coexistence of intercalated and percolated zeolite phases. The hybrid polymer composites exhibited both adsorption and ion-exchangr properties in removal of radionuclides from LRW.

The present paper investigates flaw strength distributions established using various flexural tests on batches of SiC bar test specimens: 4-point bending as well as 3-point bending with different span lengths. Flaw strength is given by the elemental stress operating on the critical flaw at fracture of a test specimen. Fracture inducing flaws and their locations are identified by fractography. A single population of pores was found to dominate fracture. The construction of diagrams of p-quantile vs elemental strengths was aimed at assessing the Gaussian nature of flaw strengths. Then, empirical cumulative distributions of strengths were constructed using the normal distribution function. Weibull cumulative probability distributions were derived from the mean and the standard deviation using the first moment equation. Agreement was obtained between both Weibull and normal flaw strengths distributions. The cumulative distributions for the different bending tests were predicted satisfactorily from the flaw strength density function using the elemental strength model. Flaw strength distributions that include potential weaker flaws encountered in larger test pieces are extrapolated using the p-quantile diagrams. Implications are discussed about the pertinence of an intrinsically representative flaw strength distribution, about failure predictions, about size effects, and about the significance of flaw spatial distributions.

Power converter technologies have become increasingly vital in various applications due to their efficient management of electrical energy. With the growing prominence of renewable energy sources like solar and wind, the high penetration of power electronic converters has been justified. However, ensuring power quality has emerged as a significant challenge for grid-connected power converters. The divergence from the ideal sinusoidal waveform in terms of magnitude and frequency impacts both grid-side currents and voltages. Several studies have proposed solutions to address power quality issues at the load side. The advancement of power converters has been fueled by the development of high-performance microprocessors and the emergence of high-speed switching devices, such as SiC-MOSFETs. This paper focuses on the design of voltage source converters, particularly those based on SiC-MOSFET semiconductor devices. The article presents the design of H-Bridge cells, discusses two-level voltage source converters based on cascade H-Bridge cells in parallel configuration with experimental fault analysis, addresses the seven-level voltage source converters topology, and explores the design and experimental results of the matrix converter. The findings underscore the importance of considering the entire converter design for improved performance at high switching frequencies. The article concludes by summarizing the main outcomes and implications of this research.

The lattice reduction aided(LRA) algorithm has attracted widely attention of researchers in MIMO systems because of its low complexity to achieve full diversity. However, most lattice reduction auxiliary algorithms do not directly improve system performance. In this paper, a modified lattice reduction successive interference cancellation (SIC) algorithm is proposed for MIMO OFDM system mild changing the complexity of LRA algorithm. At present, the MMSE SQRD algorithm has the problem of regarding too much useful signals as the residual interference which cannot be cancelled by successive interference cancellation. Since the diagonal elements of useful signals are non-zero, the components of the symbols to be detected still present in the interference term, treating all the signals as interference will be resulted in performance loss. To solve this problem, the modified matrix is proposed.by moving this symbol component into the signal term, the proposed algorithm can provide the better performance than MMSE SQRD algorithm. The analysis shows that the LRA-MMSE-SIC algorithm of proposed in this paper significantly improves the system performance with mild increasing the complexity. The simulation results show that the performance of the proposed algorithm is improved by 1dB and 8dB compared with the comparison algorithm when the bit error rate is 10−3.

The escalating demand for multifunctional and advanced materials for growing industries has turned scientific exploration to graphene-based hybrid filler polymer composites. The introduction of graphene with other fillers into polymer matrices results in astonishing properties and thus has gained significant attention in recent years. This study addresses the significance of graphene-based hybrid filler polymer composites in progressive materials science and engineering. The paper encloses some traditional and current preparation techniques employed in the fabrication of composites and a comprehensive review of successfully prepared graphene hybrid polymer composites with enhanced mechanical, thermal, and electrical properties reported in published research. The role of different factors, e.g., filler type, aspect ratios, filler-matrix compatibility, dispersion effects, homogeneity, filler orientation through polymer matrices, and curing conditions, are summarized. Finally, the applications in heavy industries, e.g., aerospace, electronics, energy storage, and automotive sectors were also analyzed. We hope this study will serve as a practical resource for new researchers and practitioners to understand and harness the full potential of these composites in various scientific and industrial fields.

In this review, we provide an overview of the most common majority and minority charge carrier traps in n-type 4H-SiC material. We focus on the results obtained by different applications of junction spectroscopy techniques. The basic principles behind the most common junction spectroscopy techniques are given. These techniques, namely, deep level transient spectroscopy (DLTS), Laplace DLTS (L-DLTS) and minority carrier transient spectroscopy (MCTS) have led to recent progress in identifying and better understanding of the charge carrier traps in n-type 4H-SiC material.

Epoxy powders offer a low-cost means of manufacturing thick section composite parts, such as those found in wind and tidal turbines. Currently, their processing cycle includes a lengthy drying stage (≥ 15 h) to remove ambient moisture. This prevents void defect formation and, thereby, a reduction in mechanical properties, however, it constitutes up to 60% of the processing time. Little research has been published on the study of this process or its optimisation. Experimental and simulated analyses are used to investigate the effects of hygroscopicity in epoxy powder composites. In particular, focus is given to the drying process, which is used to prevent void defect formation and, thereby, a reduction in mechanical properties. As such, tests are performed to quantify the void content of dried and undried laminates, and to measure its impact on transverse flexural strength. Dynamic vapour sorption analysis is used to study the sorption behaviour of the epoxy powder. Sorption data is fitted to a modified linear driving force model, and then implemented in existing process simulations tools. The drying of a thick epoxy powder composite section is simulated to investigate the influence of powder sintering on the duration required for drying. It is shown that the epoxy powder is slightly hygroscopic (1.36 wt%) and exhibits sorption behaviour that is characteristic of glassy polymers. This results in up to 4.8% voids (by volume) if processed in an undried state, leading to a 43% reduction in transverse flexural strength. Process simulations reveal that a standard drying cycle prematurely sinters the powder; inhibiting moisture release. By maintaining a powder state, simulations show that the drying cycle can be reduced to 5 h.

The present decade has witnessed numerous investigations focussed on the determination of the mechanical properties of Fly ash composites. These composites have attracted attention, especially in the form of reinforcements owing to their excellent tensile and compressive properties coupled with impact and hardness response. A number of techniques viz. in-situ deposition, hand-up lay and compo-casting techniques have been reported to fabricate these composites. However, in the context of these composites, a systematic structure-property correlation has not been established till date. The present review is aimed at highlighting the current state of research in the avenue of Fly ash composites from two different viewpoints, viz. (i) fabrication technique and (ii) mechanical properties of the fabricated composites. Moreover, the necessity of establishing systematic structure-property correlation in these materials has also been briefly discussed from the author’s viewpoint.

This review is focused on current state-of-the-art research on electroactive-based materials and their synthesis, as well as their physicochemical and biological properties. Special attention is paid to pristine intrinsically conducting polymers (ICPs) and their composites with other organic and inorganic components, well-defined micro- and nanostructures, and enhanced surface areas compared with those of conventionally prepared ICPs. Hydrogels, due to their defined porous structures and being filled with aqueous solution, offer the ability to increase the amount of immobilized chemical, biological or biochemical molecules. When other components are incorporated into ICPs, the materials form composites; in this particular case, they form conductive composites. The design and synthesis of conductive composites result in the inheritance of the advantages of each component and offer new features because of the synergistic effects between the components. The resulting structures of ICPs, conducting polymer hydrogels and their composites, as well as the unusual physicochemical properties, biocompatibility and multi-functionality of these materials, facilitate their bioapplications. The synergistic effects between constituents have made these materials particularly attractive as sensing elements for biological agents, and they also enable the immobilization of bioreceptors such as enzymes, antigen–antibodies, and nucleic acids onto their surfaces for the detection of an array of biological agents. Currently, these materials have unlimited applicability in biomedicine. In this review, we have limited discussion to three areas in which it seems that the use of ICPs and materials, including their different forms, are particularly interesting, namely, biosensors, delivery of drugs and tissue engineering.

To obtain a cost-effective and high-performance composite material of polybutylene adipate-terephthalate (PBAT), for this study we selected microcrystalline cellulose, which is inexpensive and easily available, as the reinforcing medium. Hexadecyl trimethoxysilane (HDTMS) containing a long carbon chain was chosen to silanize the microcrystalline cellulose (MCC) to obtain silanized cellulose (SG). Three types of SGs with different degrees of silanization were obtained by controlling the reaction ratio. Characterization of these three types of SGs was conducted using FTIR, TEM, and water absorption analysis. Subsequently, PBAT/SG composites were prepared through a sol-gel method, and the effects of these three types of SGs on the thermal stability, compatibility, mechanical properties, and dynamic thermomechanical properties of PBAT were evaluated. Furthermore, the mechanism behind enhancing the mechanical properties of the composite was analyzed. The results demonstrated successful synthesis of SG. As the reaction ratio between HDTMS and MCC increased, the nanoparticle size increased, while the water absorption decreased significantly. After SG was added to the PBAT composites, the yield stress increased while maintaining good thermal stability. Both the SEM and DMA results indicated good compatibility of the PBAT/SG composites. Analysis of the mechanical properties revealed that the tensile strength initially increased and then decreased with increasing blending ratio for all three composites tested; among them, the PBAT/SG2 composites exhibit superior performance, with a maximum tensile strength reaching 22 MPa at an 85/15 blending ratio—nearly 30% higher than that of pure PBAT alone. The addition of SG significantly improved the strength of the PBAT, and we speculated as to the underlying mechanism involved. This study provides a new idea for the industrial-scale development of degradable polyesters with low cost and good mechanical properties.

With the development of nuclear technology application, radiation safety has been widely concerned, and there is an urgent need for novel shielding materials. Among the various options available, non-lead organic composite shielding material has emerged as a promising solution in the field of radiation shielding due to its high strength, easy processing, and light weight. In this study, tungsten/epoxy resin (W/EP) composite samples with tungsten weight fraction from 0% to 60% were prepared. The shielding and mechanical properties of W/EP composites were investigated. The results show that the results showed that the higher the tungsten content, the greater the shielding capacity of W/EP composites, particularly for low-energy gamma ray (γ) shielding. However, the addition of tungsten reduces the impact strength and tensile properties of the material. Overall, for 300 keV γ-ray, W/EP with 30% tungsten content has comparable shielding capacity to ordinary concrete. W/EP composite materials can serve as shielding materials for low-energy γ-rays.

Poly-ether-ether ketone (PEEK) is a great potential thermoplastic in industry and medical treatment and health. In this work, the PEEK/GO and PEEK/MoS2 composites were prepared by a novel hot isostatic pressing method. The addition of GO alters the tribological behaviours mechanism, fatigue wear mechanism is predominant to PEEK/GO composites. However, the combination of abrasive and adhesive wear mechanisms is observed for PEEK/MoS2 composites and PEEK. The reason is the hardness and tensile strength of composites are increased with the appropriate addition of GO. The response time to stable friction state of PEEK/GO and PEEK/MoS2 composites reduces in compared with PEEK, which conduce to shorten running-in time, reduce energy consumption and improve the tribological performances of composites. The addition of GO and MoS2 can effectively decrease the friction coefficient and wear rate, and the optimal content of GO and MoS2 was 0.7 wt.% and 15 wt.%, respectively. The results indicate that PEEK/GO and PEEK/MoS2 are impressive composites that possess super tribological properties.

The manufacture of SiC-based composites is quite widespread, and currently different methods are employed for to produce them. The most efficient method, taking into account the cost/performance ratio, is reactive melt infiltration. It consists in infiltrating liquid silicon into a porous preform that must contain carbon, so that SiC is produced during infiltration. This chemical reaction is, in fact, the driving force of the process. In the present work, the synthesis of two SiC-based composite materials with very different applications and microstructures has been studied and optimized. In both cases, materials have been obtained with suitable properties for the selected applications. One of the materials studied is SiCp/Si for protection systems such as armor jackets, and the other one is Cf/SiC for use in braking systems. For the optimization, the dwell time and the atmosphere (Ar or primary vacuum) were used as variables. It has been found that in both preforms the optimum conditions are 1 hour dwell time and a vacuum atmosphere at 1450 °C. The effect of these parameters on microstructure and infiltration kinetics are discussed.

The article presents a method for obtaining new composites using a well-known mineral, expanded perlite (EP), and an industrial polymer, butadiene rubber (BR). For the design of composites, a joint oxidative chlorophosphorylation reaction of BR and EP (as well as BR and modified EP) was carried out, and the modifications obtained from this reaction were further hydrolyzed. The structure and morphology of the obtained samples were characterized in detail using Fourier transform infrared spectroscopy, ultraviolet-visible spectroscopy, X-ray powder diffraction, as well as scanning electron microscopy, and energy-dispersive X-ray analysis. EP and BR were separately modified with a similar reaction and characterized for data interpretation.

Biodegradable poly(ɛ-caprolactone) (PCL) and its composites or blends have gotten a lot of attention in the last decade because of their potential applications in human life and environmental remediation. As a result, there is a growing interest in the synthesis of PCL-composites/blends and their applications. Greater efforts have been made to develop biodegradable chemical materials as adsorbents that do not pollute the environment in order to replace traditional materials. Among the numerous types of degradable materials, PCL is currently the most promising, the most popular, and the best material to be developed, and it is referred to as the "green" eco-friendly material. Membranes and adsorbents for water treatment, packaging and compost bags, controlled drug carriers, biomaterials for tissues such as bone, cartilage, ligament, skeletal muscle, skin, cardiovascular and nerve tissues are just some of the applications of this biodegradable polymer (PCL). The goal of this review is to present a brief overview of PCL, its properties, syntheses of PCL, PCL composites, and PCL blends, but to provide a detailed investigation into the utility of PCL/PCL-based adsorbing agents in the removal of dyes/heavy metal ions.

The dolomite dust-emulsified asphalt composite with excellent mechanical properties was successfully prepared using alkali activation. The effects of different alkali concentrations and emulsified asphalt contents on the mechanical properties of the materials were studied. The mechanical properties and microstructure of the composites were analyzed using compressive strength tests, bending strength tests, and SEM characterization. The experimental results show that the specimens have excellent mechanical properties: the 7-day compressive strength can reach 76.67 MPa, and the bending strength is about twice that of silicate-based geopolymer-emulsified asphalt composite. With an increase in emulsified asphalt content, the compressive strength of the samples decreases, while the bending strength increases first and then decreases. When the emulsified asphalt content is 1%, the bending strength of the sample is up to 28.81 MPa, which is 25% higher than that of the sample without emulsified asphalt. This indicates that an appropriate emulsified asphalt content can play a toughening role in the system, providing a new idea for designing high-toughness alkali-activated materials.

Nano/micron-sized bioactive glass (BG) particles are attractive candidates for both soft and hard tissue engineering. They can chemically bond to the host tissues, enhance new tissue formation, activate cell proliferation, stimulate the genetic expression of proteins, and trigger unique an-ti-bacterial, anti-inflammatory, and anti-cancer functionalities. Recently, composites based on bi-opolymers and BG particles have been developed with various state-of-the-art techniques for tis-sue engineering. Gelatin, a semi-synthetic biopolymer, has attracted the attention of researchers because it is derived from the most abundant protein in the body, viz., collagen. It is a polymer that can be dissolved in water and processed to acquire different configurations, such as hydro-gels, fibers, films, scaffolds, etc. Searching "bioactive glass gelatin" in the tile on Scopus renders 80 highly relevant articles published in the last ~10 years, which signifies the importance of such composites. First, this review addresses the basic concepts of soft and hard tissue engineering, in-cluding the healing mechanisms and limitations ahead. Then, current knowledge on gelatin/BG composites including composition, processing and properties is summarized and discussed both for soft and hard tissue applications. This review explores physical, chemical and mechanical features and ion-release effects of such composites concerning osteogenic and angiogenic respons-es in vivo and in vitro. Additionally, recent developments of BG/gelatin composites using 3D/4D printing for tissue engineering are presented. Finally, the perspectives and current challenges in developing desirable composites for the regeneration of different tissues are outlined.

Chemical modification of cellulose offers routes for structurally and functionally diverse biopolymer derivatives for numerous industrial applications. Among cellulose derivatives, cellulose ethers have found extensive use, such as emulsifiers, in food industries and biotechnology. Methylcellulose, one of the simplest cellulose derivatives, has been utilized for biomedical, construction materials and cell culture applications. Its improved water solubility, thermoresponsive gelation, and the ability to act as a matrix for various dopants also offer routes for cellulose-based functional materials. There has been a renewed interest in understanding the structural, mechanical, and optical properties of methylcellulose and its composites. This review focuses on the recent development in optically and mechanically tunable hydrogels derived from methylcellulose and methylcellulose-cellulose nanocrystal composites. We further discuss the application of the gels for preparing highly ductile and strong fibers. Finally, the emerging application of methylcellulose-based fibers as optical fibers and their application potentials are discussed.

Conventional pervious pavement materials (PPM) consist of cement and aggregate materials and are known for poor durability due to their brittle behavior. Herein, we fabricated polymeric PPMs from durable and abundant polyurethane (PU) to enhance the durability of the material and undertook mechanical and microscopic characterizations. PU-based PPM samples with varying aggregate sizes were produced and the compressive strength and water permeability of each were examined. The pore and tortuosity characteristics of the specimens were analyzed using X-ray micro-computed tomography (micro-CT). Through the micro-CT analysis, the morphological characteristics of the internal structures of PPM were identified and the correlations between the pore size distribution, connectivity, and tortuosity within the specimen were quantitatively analyzed. The microstructures derived from micro-CT were generated as a finite element model and the stress distribution generated inside was numerically determined.

This study investigates the nonlinearities in three-phase inverters for SiC-based systems and compares their performance to IGBT-based systems. An analytical model of inverter voltage distortion is developed, which accounts not only for dead time (td), switching delay time, switching frequency (fs), and voltage drops of power devices, but also for output parasitic capacitance (Cout). Experimental tests validate the model, which provides a more accurate estimate of the inverter’s output phase voltage distortion. The power device characteristics are obtained from datasheets, while Cout is determined through experimentation. Three-phase inverters with varying switching frequencies, fundamental frequencies, and dead-time values are used in simulations and experiments to determine the influence of nonlinearity on phase voltage deviation and current distortion. The results show that, due to SiC devices’ faster switching time, the phase voltage deviation and phase current distortion are lower in SiC-based inverters than in IGBT-based ones for high-frequency applications, as the dead time can be reduced.

Over the past decades, research has escalated on the use of polylactic acid (PLA) as replacement for petroleum-based polymers. This is due to its valuable properties, such as renewability, biodegradability, biocompatibility and good thermomechanical properties. Despite possessing good mechanical properties comparable to conventional petroleum-based polymers, PLA suffers from some shortcomings such as low thermal resistance, heat distortion temperature and rate of crystallization, thus different fillers have been used to overcome these limitations. In the frame work of environmentally friendly processes and products, there has been growing interest on the use of cellulose nanomaterials viz. cellulose nanocrystals (CNC) and nanofibers (CNF) as natural fillers for PLA towards advanced applications other than short-term packaging and biomedical. Cellulosic nanomaterials are renewable in nature, biodegradable, eco-friendless and they possess high strength and stiffness. In the case of eco-friendly processes, various conventional processing techniques, such as melt extrusion, melt-spinning, and compression moulding, have been used to produce PLA composites. This review addresses the critical factors in the manufacturing of PLA-cellulosic nanomaterials by using conventional techniques and recent advances needed to promote and improve the dispersion of the cellulosic nanomaterials. Different aspects, including morphology, mechanical behavior and thermal properties, as well as comparisons of CNC- and CNF reinforced PLA, are also discussed

This paper investigates the density, phase composition, microstructure and mechanical properties (microhardness, fracture toughness) of binderless WC + SiC ceramics obtained by conventional pressureless sintering (CPS) and Spark Plasma Sintering (SPS). α-WC nanopowders obtained by DC arc plasma chemical synthesis and β-SiC powders have been used as raw materials. The content of SiC particles was 1, 3, 5% wt. Excess graphite (0.3, 0.5% wt.) was added to α-WC nanopowders to decrease the volume fraction of W2C particles that negatively affect the mechanical properties of ceramics. WC + 1% wt. SiC + 0.3% wt. C ceramics are shown to have a homogeneous fine-grained microstructure, high relative density, increased microhardness and Palmquist fracture toughness. The CPS and SPS activation energies of WC + SiC nanopowders at an intensive shrinkage stage are determined using the Young-Cutler model. The effect of carbon and SiC particles on the CPS and SPS activation energies of tungsten carbide nanopowders has been analyzed. The CPS activation energies of WC, WC + C and WC + SiC + C nanopowders are shown to be closer to the carbon diffusion activation energy along α-WC grain boundaries. The SPS activation energies of WC and WC + SiC nanopowders turn out to be lower than the carbon grain boundary diffusion activation energy of α-WC.

Hybrid organic/inorganic conducting and magnetic composites of core–shell type have been prepared by in-situ coating of nickel microparticles with polypyrrole. Three series of syntheses have been made. In the first, pyrrole was oxidized with ammonium peroxydisulfate in water in the presence of various amounts of nickel and the composites contained up to 83 wt% of this metal. The similar syntheses in 0.1 M sulfuric acid followed. Finally, the composites with polypyrrole nanotubes were prepared in water in the presence of structure-guiding methyl orange dye. FTIR and Raman spectroscopies confirmed the formation of polypyrrole. The resistivity of composite powders of the order of tens to hundreds Ω cm was monitored as a function of pressure up to 10 MPa. The resistivity of composites slightly increased with increasing content of conducting nickel. This apparent paradox is explained by the coating of nickel particles, which prevents their contacts and generation of metallic conducting pathways. Electrical properties were practically independent of the way of composite preparation or nickel fraction and were controlled by polypyrrole phase. On the contrary, magnetic properties were determined exclusively by nickel content. The composites were used as a solid phase to prepare a magnetorheological fluid. The test showed better performance when compared with a different nickel system.

The on-state voltage of MOSFETs is a convenient and powerful temperature-sensitive electric parameter (TSEP) to determine the junction temperature, thus enabling device monitoring, protection, diagnostics and prognostics. The main hurdle in the use of the on-state voltage as a TSEP is the per-device characterization procedure, to be carried out in a controlled environment, with high costs. In this paper we compare two novel techniques for MOSFET junction temperature estimation: controlled shoot-through and direct heating by resistive heaters embedded in two Kapton (polyimide) films. Both allow in-place characterization of the TSEP curve with the device mounted in its final circuit and assembly, including the working heat sink. The two methods are also validated against the conventional procedure in a thermal chamber.

The pursuit of an environmentally sustainable manufacturing process advocates for the substitution of harmful reagents for less damaging and recyclable solutions. This study aims to assess the effectiveness of using cellulose microfibrils synthesized via different hydrolysis reactions as reinforcing agents in polyvinyl alcohol (PVA) at varying con-centrations. The investigation explores the morphology, thermal properties, and chemi-cal behavior of the cellulose particles. The cellulose microfibrils (CMF) produced using citric acid exhibited the highest yield and aspect ratio. Notably, particles from organic acids demonstrated greater thermal stability, with oxalic acid-derived particles displaying the maximum thermal degrada-tion temperature. Subsequently, cast films of PVA reinforced with the cellulose microfibrils underwent comprehensive analyses, including Fourier transfer infrared (FTIR) spectroscopy, thermal degradation temperature (Td), differential scanning calorimetry (DSC), and tensile strength tests. The thermal behavior of cast films experienced notable changes with the addition of cellulose particles, evidenced by increased melting and crystallinity temperatures, along with a rise in the degree of crystallinity. The incorporation of cellulose particles led to a substantial improvement in mechanical properties. Films containing CMF dis-played higher Young’s modulus, and the sample incorporating 5% CMF derived from citric acid exhibited the most significant increase in modulus.

Polylactic acid (PLA) was modified with three types of MVOs, which are the epoxidized soybean oil (ESBO), maleinized sunflower oil (MSO) and maleinized olive oil (MOO), at different weight fractions. A co-rotating twin screw extruder was used to produce composite materials by melt mixing process. The effect of MVOs content, from 2.5% to 10%, on the morphology, mechanical properties, density and water absorption were investigated in detail. Addition of ESBO and maleinized vegetable oils leads to a slight decrease in density of PLA from 1.252 to 1.231 g/cm3. As the concentration of MVO in PLA increases, the amount of water absorption also increased and the highest water absorption value was observed in P10MSO. In general, the elastic modulus (EM) was slightly changed by the addition of MVO to PLA, while the tensile strength (TS) decreased. Due to the plasticizing effect of MVOs, an increase in the Izod impact strength was obtained.

In this paper, single and repetitive frequency UIS characteristics of 1200 V asymmetric (AT)and double trench silicon carbide (DT-SiC) metal–oxide-semiconductor field-effect transistors (MOSFETs) under different working conditions are investigated by experiment and simulation. For asymmetric trench SiC MOSFETs, the failure mode is all thermal runaway under working conditions. However, the failure mode of double trench SiC MOSFETs mostly is gate oxide rupture, which indicates an instable avalanche robustness under UIS stress. The variations of measured parameters are recorded to evaluate typical electrical features of device failure. Furthermore, TCAD simulation is used to reveal the electro-thermal stress inside the device during avalanche. Additionally, failed devices are decapsulated to verify the location of failure point from the perspective of the semiconductor die. Finally, a new type of stepped-oxide vertical power DT MOSFET with P-type shielding and current spread layers is proposed for improvement of gate dielectric reliability.

The interfacial mechanics and electrical properties of the SiC reinforced copper matrix composites were studied via the first principles method. The work of adhesion (Wad) and the interfacial energies were calculated to evaluate the stabilities of the SiC/Cu interfacial models. The carbon terminated (CT)-SiC/Cu interfaces were predicted more stable than those of the silicon terminated (ST)-SiC/Cu from the results of the Wad and interfacial energies. The interfacial electron properties of SiC/Cu were studied via the charge density distribution, charge density difference, electron localized functions and partial density of the state. The covalent C-Cu bonds were formed based on the results of the electron properties, which further explained the fact that the interfaces of the CT-SiC/Cu are stable than those of the ST-SiC/Cu. The interfacial mechanics of the SiC/Cu were investigated via the interfacial fracture toughness and ultimate tensile stress, and the results indicate that both CT- and ST-SiC/Cu interfaces are hard to fracture. The ultimate tensile stress of the CT-SiC/Cu is nearly 23GPa, which is smaller than those of the ST-SiC/Cu of 25 GPa. The strains corresponding to their ultimate tensile stresses of the CT- and ST-SiC/Cu are about 0.28 and 0.26, respectively. The higher strains of CT-SiC/Cu indicate their stronger plastic properties on the interfaces of the composites.

Due to its distinctive chemical and biological properties, pectin has recently drawn much attention in biomedical and tissue engineering applications. Polymers like pectin with cell-instructive properties are attractive natural biomaterials for tissue repair and regeneration. Besides, bioactive pectin and pectin-based composites exhibit improved characteristics to deliver active molecules. Pectin and pectin-based composites serve as interactive matrices or scaffolds by stimulating cell adhesion and cell proliferation and enhancing tissue remodeling by forming an extracellular matrix in vivo. Several bioactive properties, such as immunoregulatory, antibacterial, anti-inflammatory, anti-tumor, and antioxidant activities, contribute to the pectin's and pectin-based composite's enhanced applications in tissue engineering and drug delivery systems.This paper reviews the promising characteristics of pectin or pectic polysaccharides and highlights its potential applications in drug delivery and tissue engineering. Tissue engineering scaffolds containing pectin and pectin-based conjugates or composites demonstrate essential features such as non-toxicity, tunable mechanical properties, biodegradability, and suitable surface properties. The design and fabrication of pectic composites are versatile for tissue engineering and drug delivery applications.

The paper presents the design stages of a single-phase Silicon Carbide bidirectional DC-AC converter. This includes the LCL filter design responsible to meet grid connection requirements. A 3kW laboratory prototype of the power converter is built employing a low-cost phase locked loop and its results are presented. The design of the low-cost phase locked loop and its implementation are depicted in some detail.

New biocements based on a powdered mixture of calcium phosphate/monetite (TTCPM) modified with the honey addition were prepared by mixing the powder and honey liquid components at a non-cytotoxic concentration of honey (up to 10% (w/v)). The setting process of the cements was not affected by the addition of honey, and the set-ting time of ~4 min corresponded to the fast setting calcium phosphate cements (CPC´s). The cement powder mixture was completely transformed into calcium-deficient nanohydroxyapatite after 24 hours of hardening in simulated body fluid, and columnar growth of long needle-like nanohydroxyapatite particles around the original calcium phosphate particles was observed in honey cements. The compressive strength of honey cements was reduced with the content of honey in the cement. The comparable antibacterial activity of cements with honey solutions was found on Escherichia coli, but very low antibacterial activity was found for Staphylococus aureus for all cements. The enhanced antioxidant inhibitory activity of composite extracts was verified. In vitro cytotoxicity testing verified the non-cytotoxic nature of honey cement extracts, and the addition of honey promoted alkaline phosphatase activity, calcium deposit production, and upregulation of osteogenic genes (osteopontin, osteocalcin, and osteonectin) by mesenchymal stem cells, demonstrating a positive synergistic effect of honey and CPC on the bioactivity of cements that could be promising therapeutic candidates for the repair of bone defects.

Extinction of natural resources builds up pressure on governments to invest in research to find more sustainable resources for construction sector. Earlier studies on mortar and concrete show that bottom ash and basalt fiber are independently alternative binder in the concrete sector. This study aims to use bottom ash and basalt fiber blends as alternative novel-based composites in pure cement paste. Strength and durability properties of two different percentages of bottom ash (40% and 50%) and three volume fractions of basalt fiber (0.3%, 0.75%, and 1.5%) were used at three curing periods (7, 28, and 56 days). In order to measure physical properties of the basalt-reinforced bottom ash cement paste composites flowability, dry unit weight, porosity and water absorption measurements at 7, 28, and 56 days of curing were performed. Furthermore, mechanical properties of composites determined by unconfined compressive strength and flexural strength tests. Finally, to assess the durability sulfate-resistance and seawater-resistance tests have been performed on composites at 28 and 56 days of curing. Results showed that addition of basalt fiber improves physical, mechanical and chemical stability properties of paste up to a limiting basalt fiber addition (0.3% volume fraction) where above an adverse effect have been monitored. It is clear that observed results can lead to development of sustainability strategies in the concrete industry by utilizing bottom ash and basalt fiber as an alternative binder.

Polymer nanocomposites are composed of polymer materials reinforced with nano fillers. In the present study the effective thermal conductivity of the composites filled with nanofillers has been investigated using commercially available finite element software ABAQUS 6.11. The nanofillers used were alumina particles and multi-walled carbon nanotubes (MWNTs) and the matrix was considered to be made of epoxy. For the analysis 2D and 3D Representative Volume Elements (RVEs) were generated using Random Sequential Adsorption (RSA) algorithm using MATLAB and Python scripts. Thermal conductivity was found out for 2D and 3D RVEs for different area and weight fractions respectively. Two different shapes of the alumina nanoparticles were considered: spherical (circular) and ellipsoidal (elliptical) for 3D (2D) analysis. It was found that the thermal conductivity was increased with the addition of nanofillers. The increase in thermal conductivity was approximately same for both types of inclusions at corresponding area or weight fractions in 2D or 3D analysis. The results showed that addition of MWNTs to the composites lead to a significant increase in thermal conductivity than spherical or ellipsoidal inclusions.

This review examines additive manufacturing for refractory tungsten (W) and its alloys. It emphasizes the primary challenges and determining factors involved in additive manufacturing pure W, W alloys, and composites. Our focus in this regard extends to both process and alloying strategies designed to address critical issues such as densification, micro-cracking, and mechanical properties in tungsten-based components produced through additive techniques. Throughout the review, we organize existing knowledge and insights into convenient tables, serving as valuable resources for researchers embarking on a deeper exploration of these topics.

The article offers a comprehensive overview of recent breakthroughs in eco-friendly polymers and polymer composites, underscoring their pivotal role in addressing sustainability challenges across diverse industrial sectors. Despite encountering obstacles related to performance and processability, biopolymers sourced from renewable materials emerge as promising alternatives for the plastics that are currently used by human beings. Natural fillers are highlighted as a strategic avenue for crafting sustainable composites, with residual natural fillers being particularly explored. Heightened environmental concerns propel discussions on the criticality of integrating biodegradable materials with natural fillers, underlining the urgency for clear frameworks and financial incentives to support adoption of these materials. Additionally, the article examines the potential of biodegradable polymers and polymer composites, with a specific emphasis on the utilization of polyhydroxyalkanoate (PHA) in composite materials and its market prospects. Moreover, it emphasizes the indispensable need for ongoing research and development endeavors to address environmental challenges within the polymer sector, reflecting a mounting interest in sustainable materials across industries.

The tribology behavior, tribofilm formation and structure evolution of polytetrafluoroethylene (PTFE) filled with α-Al2O3 and SiO2 nanoparticles during sliding against steel counterparts under different loads were studied. It is found that both composites exhibit good wear resistance across the pressure of 1 MPa to 10 MPa, with the α-Al2O3/PTFE composite demonstrates better performance stability compared to the SiO2/PTFE composite. The high wear resistance is attributed to the formation of tribofilms at the friction interface. For the α-Al2O3/PTFE, an island-like tribofilm is formed with a thickness ranging from 100 to 200 nm, while the tribofilm of the SiO2/PTFE composite is thinner, measuring approximately 50 to 100 nm, and manifest a striped pattern. The chemical composition, both at the surface and subsurface levels, as well as the morphology of the tribofilms were studied using FTIR spectrometry, X-Ray photoelectron spectroscopy (XPS), and FIB-TEM. It is found that the difference in thickness and microstructure of the tribofilms for the two composites is mainly due to the tribochemistry of the nanoparticles. The α-Al2O3 nanoparticle plays a "cohesion" role during the formation of the tribofilm, which facilitates the formation of a thicker, more uniform, and stronger adhered tribofilm on the metallic counterpart, making it more robust against higher shear stress.

Epoxy matrix composites reinforced with high-performance fibers such as carbon, Kevlar, and glass, exhibit excellent specific stiffness and strength in many mechanical applications. However, these composites are disappointingly non-recyclable and are usually disposed of in landfill sites, with no realistic prospect for biodegradation in reasonable time. In contrast, moldable composites with carbonized elastomeric matrices developed in the last decades possess attractive mechanical properties in final net-shape products and can also be incinerated or recycled. Many carbon and inorganic fillers have recently been evaluated to adjust the properties of carbonized elastomeric composites. Renewable organic fillers such as human or animal hair offer an attractive fibrous material with substantial potential for reinforcing composites with elastomeric matrices. Samples of unidirectional fiber composites (with hair volume fraction up to 7 %) and quasi-isotropic short fiber composites (with hair volume fraction up to 20 %) of human hair-reinforced nitrile butadiene rubbers (HH-NBR) were produced in the peroxide-cured and carbonized states. The samples were characterized using SEM, Raman spectroscopy and photoacoustic microscopy. Mechanical tests were performed in tension using a miniature universal testing machine. The expected effect of fiber reinforcement on the overall mechanical performance has been demonstrated for both cured and carbonized composites. Considerable enhancement of the elastic modulus (up to 10 times), ultimate tensile strength (up to 3 times) and damage tolerance was achieved. The evidence of satisfactory interfacial bonding between hair and rubber was confirmed by SEM imaging of fracture surfaces. The suitability of photoacoustic microscopy was assessed for 3D reconstruction of the fiber sub-system spatial distribution and non-destructive testing.

One of the drawbacks of natural fibers and their composites is their inherent hydrophilic nature. The effect of moisture on mechanical properties of a composite is irrefutable. This study deals with hygroscopic characteristics of Enset-PLA composites and its effect on the mechanical properties of the composite. To do this, injection molded composite specimens of different fiber volume fraction; plasticizer ratio, fiber length, and fiber age have been considered. The specimens are exposed to distilled water and the moisture absorption was monitored on a daily base. Subsequently, the specimens are subjected to mechanical loading to determine the effect of moisture on their Strength, Stiffness and strain at break strength. Lastly, individual and joint effects of considered factors have been scrutinized using optimal design of experiment. The result from the study shows that maximum and minimum moisture uptake is noticed for 25% and 10% fiber ratio respectively. Due to moisture effect, tensile and bending strength is decreased by 11% and 5% respectively for 15% fiber volume fraction; while 16% and 13% for 25% fiber volume fraction respectively. Increasing amount of plasticizer increases moisture resistance. The result indicate that Enset-PLA composite have competitive properties and stability when exposed to moisture.

Composites of Ag and TiO2 nanoparticles on cotton fabrics were synthetized in-situ by sono-chemical and hydrothermal methods achieving the successive formation of Ag-NPs and Ti-NPs directly on the fabric. The impregnated fabrics were characterized by ATR-FTIR spectroscopy, high resolution microscopy (HREM), scanning electron microscopy coupled with Ener-gy-dispersive X-ray spectroscopy (SEM-EDS), Raman, photoluminescence, UV-vis and DRS spectroscopies and by tension tests. Results showed the successful formation and impregnation of NPs on the cotton fabric, with a negligible leaching of NPs after several washing cycles. The photocatalytic activity of supported NPs was assessed by the degradation of methyl blue dye (MB) under solar and UV irradiation revealing improved photocatalytic activity of the Ag-TiO2/cotton composites due to a synergy of both Ag and TiO2 nanoparticles. This behavior is attributed to a diminished electron-hole recombination effect in the Ag-TiO2 cotton samples. The biocide activity of these composites on the growth inhibition of Staphylococcus aureus (Gram+) and Escherichia coli (Gram-) was confirmed, revealing interesting possibilities for the utilization of the functionalized cotton fabric as protective cloth for medical applications.

The effect of the addition of maleated polyethylene (MAPE) to compounds of natural rubber (NR) and Teline monspessulana flour (TMF) previously mercerized was investigated. Two factors were analyzed: A. concentration of MAPE with five levels 2; 4; 6; 8; 10 phr (parts per hundred rubber), B. concentration of TMF with two levels 25 and 40 phr. The effect of MAPE on compatibility between NR and HTM was evaluated by tensile testing the compounds. The mixing was performed in a laboratory scale mill. The test tubes were obtained by cutting or die-cutting crosslinked peroxide sheets, these were obtained during the compression molding process. Analysis indicate that the MAPE coupling agent improved the compatibility between HTM and NR, this effect was evidenced by the values of tensile strength and elongation at break. However, the gel content determination indicates that the addition of 10 phr of MAPE crosslinking decreases due to competition with coupling reaction MAPE - HTM.

In this review paper, an overview of radiation induced deep level defects in n-type 4H-SiC studied by junction spectroscopy techniques, is given. In addition to carbon vacancy (Vc), present in as-grown material already, we focus on the following deep level defects: silicon vacancy (VSi), carbon interstitial (Ci), and carbon antisite-carbon vacancy (Csi-Vc) pair. Recent advances in measurements by junction spectroscopy techniques that have led the progress toward better understanding of radiation induced defects are presented.

The article presents the results of research on the production of effective inorganic fillers and chemically resistant composite polymer-mineral materials based on industrial waste. The aim of the work is to develop the technological foundations for the production of inorganic fillers and highly filled filling compositions for use in chlorine-containing media. Materials with high resistance to hydrochloric acid are graphite and quartz sand. Thermal power plant (TPP) ash was used as an acid-resistant filler in the compositions. The simplex lattice planning method was used to determine the areas of compositions with the best properties. Two components were selected: formaldehyde rubber resin and mineral filler (TPP ash) as a binder. As the third component, hydrolytically active fillers were used - anhydrite, phosphogypsum and phosphorus production slag. A preliminary operation was performed to remove hygroscopic moisture from the filler.The influence of the nature of mineral fillers on the chemical stability and durability of the obtained composites is investigated. The nature of the interaction of mineral fillers with a polymer binder was determined, and chemical interaction of the hydroxyl groups of the filler and the methyl groups of the polymer took place. The mathematical planning method was used to optimize the chemical resistance and durability of the compositions of the studied substances. Based on the results of this study, optimal compositions of compositions, anhydrite, phosphogypsum and phosphoric slag were selected. These composites, with the highest possible degree of filling, have high target characteristics.

High temperature (HT) geothermal wells can provide green power 24h a day 7 days a week. Harsh environmental and operational conditions, long-term durability requirements of such wells require special cementitious composites for well construction. This paper reports a comprehensive assessment of geothermal cement composites in cyclic pressure function laboratory tests, field exposures in an HT geothermal well (300-350oC) as well as a numerical model to complement the experimental results. Performances of calcium-aluminate-cement (CAC)-based composites and calcium free cement were compared against reference Ordinary Portland Cement (OPC)/silica blend. The stability and degradation of the tested materials was characterized by crystalline composition, thermo-gravimetric, and elemental analyses, morphological studies, water-fillable porosity, and mechanical properties measurements. All CAC-based formulations outperformed the reference blend both in the function and exposure tests. The reference OPC/silica lost its mechanical properties during the 9-month well exposure through extensive HT carbonation, while properties of the CAC-based blends improved over that period. The Modified Cam-Clay (MCC) plasticity parameters of several HT cement formulations were extracted from triaxial and Brazilian tests and verified against the experimental results of function cyclic tests. These parameters can be used in well integrity models to predict field-scale behavior of the cement sheath under geothermal well conditions.

We present an integrable, sensor inlay for monitoring crack initiation and growth inside bondlines of structural carbon fiber reinforced plastic (CFRP) components. The sensing structures are sandwiched between crack stopping polyvinyliden fluoride (PVDF) and a thin reinforcing polyetherimide (PEI) layer. Good adhesion at all interfaces of the sensor system and to the CFRP material is crucial as weak bonds can counteract the desired crack stopping functionality. At the same time, the chosen reinforcing layer must withstand high strains, safely support the metallic measuring grids and possess outstanding fatigue strength. We show that this robust sensor system, which measures the strain at two successive fronts inside the bondline, allows to recognize cracks in the proximity of the inlay regardless of the mechanical loads. Feasibility is demonstrated by static load tests as well as cyclic long-term fatigue testing with up to 1,000,000 cycles. In addition to pure crack detection, crack distance estimation based on sensor signals is illustrated. The inlay integration process is developed with respect to industrial applicability. Thus, implementation of the proposed system will allow the potential of lightweight CFRP constructions to be better exploited by expanding the possibilities of structural adhesive bonding.

Over the years, scarcity of fresh potable water has increased the demand for clean water. Meanwhile, with the advent of nanotechnology, the use of nanomaterials for photocatalytic degradation of pollutants in wastewaters has increased. Herein, a new type of nanohybrids of La and Mn co-doped bismuth ferrite (BiFeO₃) nanoparticles embedded into transition metal carbide sheets (MXene) were prepared by a low-cost double solvent sol-gel method, and investigated for their photocatalytic activity. The photoluminescence results showed that pure BFO has highest electron hole recombination rate as compared to all the co-doped BFO/MXene nanohybrids. The larger surface area and higher electron-hole pair generation rate provides suitable environment for fast photo-degradation of organic molecules. The band gap of the prepared nanohybrids was tuned to 1.96 eV having largest BiFeO₃ surface area (147 m²g⁻¹) reported till date. Moreover, the BLFO/MXene and BLFMO-5/Mxene degraded the 92% organic pollutant from water in dark and remaining in light spectrum as compare to undoped BFO/Mxene due to enhancement of the surface area and electron-hole recombination rate upon doping. Therefore, these synthesized nanohybrids could be a promising candidate for photocatalytic applications in future.

In recent years, cancer therapy has witnessed significant advancements, with a focus on personalized and targeted treatment strategies. One promising approach involves the use of stimuli-responsive biomaterials for site-specific drug release. Among these biomaterials, pH, and redox-triggered polymer-nano composites have gained immense attention due to their ability to respond to the specific tumor microenvironment, enhancing therapeutic efficacy while reducing off-target effects. Cancer cells often exhibit anomalous biochemical properties, attributed to lower cytosolic pH (acidic) and elevated redox potential through the epitomized upregulation of undesired genes. Such biological process substantially imbalance the level ions (protons) and biological thiols glutathione (GHS) in the cytoplasm as well as in the subcellular organelles. Superfluous accumulation of ions and redox imbalance is associated with proliferation, invasion, and growth of tumor. Because of high surface area, deep tissue penetration capability, higher hydrophilicity, hydrophobic interior for drug/gene efficient loading, biocompatibility and site-specific targeting efficiency, functionalized polymer nanocomposites are superior to conventional small molecular materials. Paradoxically conventional methods of drug delivery aided therapeutics accompanied with inherent drug/genes are encapsulated in biocompatible carrier or suitable transfecting agents generally suffered with low bioavailability, uncontrolled drug release, low cellular penetration, cellular internalization, toxicity, and poor drug loading efficiency. To overcome these issues, recently various multifunctional nanomaterials were developed, based on synergistic stimuli responsive aided drug release in a specified cellular or subcellular system. High therapeutic efficacy, of nanoparticles (NPs) mainly associated with surface functionalization through biocompatible polymeric materials, site-specific targeting units accompanied with stimuli responsive components. Followed by therapeutically important drug or genetic materials were loaded into NPs either in covalent or non-covalent approach. Intriguingly, combined pH and redox dual stimuli based functional materials specially based on polymeric nanocomposites for cancer therapeutics scarcely reported. This article provides the recent progress in pH and redox-responsive polymer-nano composites for site-specific drug delivery in cancer therapy. It explores design principles, fabrication methods, mechanism of action, and prospects of these dual-stimuli responsive biomaterials.

The technological development of piezoelectric materials is crucial for developing wearable and flexible electromechanical devices. There are many inorganic materials with piezoelectric effects, such as piezoelectric ceramics, aluminum nitride, and zinc oxide. They all have very high piezoelectric coefficients and large piezoelectric response ranges. The characteristics of high hardness and low tenacity make inorganic piezoelectric materials unsuitable for flexible devices that require frequent bending. Polyvinylidene fluoride (PVDF) and its derivatives are the most popular materials used in flexible electromechanical devices in recent years and have high flexibility, high sensitivity, high ductility, and a certain piezoelectric coefficient. Owing to increasing the piezoelectric coefficient of PVDF, researchers are committed to optimizing PVDF materials and enhancing their polarity by a series of means to further improve their mechanical–electrical conversion efficiency. This paper reviews the latest PVDF-related optimization materials, related processing and polarization methods, and the applications of these materials such as those in wearable functional devices, chemical sensors, biosensors, and flexible actuator devices for flexible micro-electromechanical devices. We also discuss the challenges of wearable devices based on flexible piezoelectric polymer, consider where further practical applications could be.

Defectively manufactured and deliberately damaged composite laminates fabricated with different continuous reinforcing fibres (respectively, carbon and glass) and polymer matrices (respectively, thermoset and thermoplastic) were inspected in magnetic resonance imaging equipment. Two pulse sequences were evaluated during non-destructive examination conducted in saline solution-immersed samples to simulate load-bearing orthopaedic implants permanently in contact with biofluids. The orientation, positioning, shape, and especially the size of translaminar and delamination fractures were determined according to stringent structural assessment criteria. The spatial distribution, shape, and contours of water-filled voids were sufficiently delineated to infer the amount of absorbed water if thinner image slices than this study were used. The surface texture of composite specimens featuring roughness, waviness, indentation, crushing, and scratches was outlined, with fortuitous artefacts not impairing the image quality and interpretation. Low electromagnetic shielding glass fibres delivered the highest, while electrically conductive carbon fibres produced the poorest quality images, particularly when blended with thermoplastic polymer, though reliable image interpretation was still attainable.

In this work, effects of 20 transition element additives on the interfacial adhesion energy and electronic structure of Al (111)/6H-SiC (0001) interfaces have been studied by first principles method. For clean Al (111)/6H–SiC (0001) interfaces, both Si-terminated and C-terminated interfaces have covalent bond characteristics. The C-terminated interface has stronger binding energy, which is mainly due to the stronger covalent bond formed by the larger charge transfer between C and Al. The results show that the introduction of many transition elements, such as 3d transitional group Mn, Fe, Co, Ni, Cu, Zn and 4d transitional group Tc, Ru, Rh, Pd, Ag, can improve the interfacial adhesion energy of the Si-terminated Al (111)/6H-SiC (0001) interface. However, for the C-terminated Al (111)/6H-SiC (0001) interface, only the addition of Co element can improve the interfacial adhesion energy. Bader charge analysis shows that the increase of interfacial binding energy is mainly attributed to more charge transfer.

Many strategies have been developed for the synthesis of silicon carbide (SiC) thin films on silicon (Si) substrates by plasma-based deposition techniques, especially plasma enhanced chemical vapor deposition (PECVD) and magnetron sputtering, due to importance of these materials for microelectronics and related fields. A drawback is the large lattice mismatch between SiC and Si. The insertion of a thin aluminum nitride (AlN) buffer layer between them has been shown useful to overcome this problem. Herein, the high-power impulse magnetron sputtering (HiPIMS) technique was used to grow SiC thin films on AlN/Si substrates. Furthermore, the SiC films were also grown on Si substrates. Comparisons of the structural and chemical properties of SiC thin films grown on the two types of substrates allowed us to evaluate the influence of AlN buffer layer on such properties. The chemical composition and stoichiometry of the samples were investigated by Rutherford backscattering spectrometry (RBS) and Raman spectroscopy, while the crystallinity was characterized by grazing incidence X-ray diffraction (GIXRD). Our set of results evidenced the versatility of HiPIMS technique to produce polycrystalline SiC thin films at near room temperature only varying the discharge power. In addition, this study opens up a feasible route for the deposition of crystalline SiC films with a good structural quality using AlN buffer layer.

In this study, grit blasting pretreatment was used to improve the adhesion and corrosion resistance and microhardness of Ni-W/SiC nanocomposite coatings fabricated using conventional electrodeposition technique. Prior to deposition, grit blasting and polishing (more commonly used) pretreatment were used to prepare the surface of the substrate and the 3D morphology of the pretreated substrates was characterized using laser scanning confocal microscopy. The coatings surface and the cross section morphology were analyzed using scanning electron microscopy (SEM). The chemical composition, crystalline structure, microhardness, adhesion, and the corrosion behavior of the deposited coatings were characterized using energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), microhardness tester, scratch tester and electrochemical workstation, respectively. The results indicated that the grit blasting and SiC addition, improved the microhardness, adhesion and corrosion resistance. The Ni-W-SiC nanocomposites pretreated by grit blasting exhibited the best adhesion strength, up to 36.5 ± 0.75 N. Its hardness was the highest and increased up to 673 ± 5.47Hv and its corrosion resistance was the highest compared to the one pretreated by polishing.

This study provides an in-depth review of the available literature on metal composite material machining, focusing on traditional machining operations such as turning, milling, shaping, drilling, and grinding. The motivation for the study is that this composite type has emerged as a vital material in applications requiring functionality, resilience, cost-effective operation, low consumption of energy and lightweight. Despite its superior characteristics, the manufacturing complexity and poor machinability of metal matrix composites have been the primary barriers to its adoption. Nevertheless, there is a reduction of exceptional efficiency, increase in surface roughness, tool wear and so on in metal matrix composites throughout machining. As a result, this review gives a comprehensive investigation of metal matrix composite machining and effect on process parameters and procedures. Furthermore, this study distinguishes metal matrix composites towards sustainable manufacturing and the metals employed by the researchers, as well as the gaps discovered for future recommendations in metal-based composites.

Synthetic materials such as Carbon, Kevlar, and Glass fibers are extensively utilized in various industries due to their superior characteristics including high stiffness, great strength, low den-sity, and high wear resistance, these advantages contributed to making them widespread in ap-plications like; aerospace, automobile, civil and electronics. This research is carried out to enhance the creep compliance of epoxy composite material by considering two types of fibers as reinforcement. A composite material is produced by combining two fibers, Kevlar fiber mixed with sika epoxy resin, along with Carbon fiber also mixed with sika epoxy resin using a Hand-Layup process. Experiments and numerical modeling are examined to offer a comprehensive understanding creep behavior of epoxy composite material in different weight ratios. Burger and Prony models are used to represent stress relaxation and creep strain of Visco-elastic material. According to the results, sika epoxy resin reinforced with Kevlar and Carbon fibers exhibits enhancement in the mechanical properties compared with pure epoxy. The use of Kev-lar/Sika epoxy composite results in higher creep compliance and modulus of elasticity compared with Carbon/Sika epoxy composite.

Organic solar cells are contributing extensively to the production of future large area and cost-effective sources of renewable energy with a compact environmental impact. Moreover, due to tunable optical properties of the active medium, the semi-transparent organic solar cell can be fabricated and become a promising nominee for building Integrated Photovoltaics (BIPV), vehicles, and mobile electronic devices. Therefore, three newly synthesized polymers used as were host materials for the active medium and blended with beetroot dye. Hence, based on BHJ structure two ternary systems have been constructed and utilized to fabricate semitransparent solar cells and characterized. The results show that the natural dye has a crucial impact on solar cell characteristic parameters. Consequently, large value of V_OC close to 1V were obtained for ternary systems and acceptor material named PINDOLE exhibits potentials for electron transport layer (ETL) and shows an improvement in both fill factor and device efficiency.

Three types of the composites were tested for electromagnetic interference (EMI) absorption shielding effectiveness, curing process and physical-mechanical properties. In the first type of composites, manganese-zinc ferrite, nickel-zinc ferrite, and both fillers in their mutual combinations were incorporated into acrylonitrile-butadiene rubber. The overall content of the filler, or fillers combinations was kept on 200 phr. Then, carbon black, or carbon fibres, respectively were incorporated into each rubber formulation in constant loading - 25 phr, while the content of magnetic fillers was unchanged - 200 phr. The work was focused on the understanding of correlation among electromagnetic shielding parameters and electrical conductivity of composites in relation to their EMI absorption shielding effectiveness. The absorption shielding ability of materials was evaluated within the frequency range from 1 MHz to 6 GHz. The study revealed good correlation among permittivity, conductivity, and EMI absorption effectiveness. Although, the absorption shielding efficiency of composites filled only with ferrites seems to be the highest, the absorption maxima of those composites were reached over 6 GHz. The application of carbon based fillers resulted in higher electrical conductivity and higher permittivity of composites, which was reflected in their lower absorption shielding performance. Though, the composites with filled with ferrites and carbon based fillers absorbed electromagnetic radiation within the desired frequency range. The presence of carbon based fillers caused the improvement in tensile behavior of composites. The study also demonstrated that the higher was the ratio of nickel-zinc ferrite in magnetic fillers combinations, the higher was the absorption shielding performance.

The paper covers the development of formulations and technology for low energy building materials based on the alkaline alumino-silicate binder and appropriate for special purposes. The microstructure of the binder was investigated using scanning electron microscopy and atomic force microscopy. The identification of the phase compositions was done by means of X-ray diffraction. By leach rate measurement and chemical analysis of pore liquid, the linkage of the alkali metal ions in water-insoluble composites was researched. The dependence of structure formation on mix design and curing conditions was investigated. Specific examples of manufacture and application of binder-based glues and adhesives have been considered, incl. ones for low-temperature insulating composite materials, heat insulation perlite-based materials, heat insulation of industrial boilers, and the fire resistant heat insulating system. The advantages of the binder-based temperature insulating composites compared to traditionally used ones are shown.

The topic of modification of magnesium oxychloride cement (MOC) via specific functional additives is very much pronounced in the research of alternative building materials. This study deals with the co-doping of MOC by 1D and 2D carbon nanomaterials in order to improve its mechanical properties while using tannic acid (TA) as a surfactant. Furthermore, the effect of TA on MOC also covers the improvement of water resistance. As a filler, three size fractions of standard quartz sand are used. The proposed types of MOC-based composites show promising results considering their mechanical, macro- and microstructural, chemical, and hygric properties. The use of 1D and 2D nanoadditives and their mixture enables the improvement of the flexural strength and most of all softening coefficient, the durability parameter characterizing the resistance of the prepared materials to water. For samples immersed in water for 24 h, the compressive strength of all modified composites tested was higher than that of the reference composite. Quantitatively, the developed co-doped composite shows mechanical parameters comparable to or even better than those of commonly used Portland cement-based materials, while maintaining high environmental efficiency. This indicates its potential use as an environmentally friendly alternative to Portland cement-based products.

This research examines the fire resistance of geopolymer composites (GCs), formulated using alka-li-activated metakaolin and aluminum powder. The production method involves spray-coating carbon steel plates with fresh GCs, followed by a 28-day curing period at room temperature. Sub-sequently, fire performance and aging tests are conducted to evaluate fire resistance. The study investigates GC properties, including apparent density, bending strength, compression strength, thermal conductivity, porosity, and production cost. Morphological changes before and after fire and aging tests are analyzed using scanning electron microscopy (SEM). Results demonstrate GC foams' outstanding thermal insulation, providing up to 75 minutes of fire resistance with a 6 mm coating, reducing temperatures by 300 °C compared to uncoated steel. GCs exhibit a density of 670 kg/m³, thermal conductivity of 0.166 W/m·K, 68% porosity, and cost efficiency at 250 dollars per cubic meter. This study underscores the potential of foamed geopolymer coatings for effective and economical surface protection.

TiC particles were prepared from Ti and C powders, and TiC-reinforced Cu-based composites were prepared by powder metallurgy with SPS sintering. The effects of SPS sintering temperature and TiC particle reinforcement phase content on the electrical and mechanical properties of Cu-based composites were investigated. The reinforcement of TiC particles by thermal mismatching at increasing sintering temperature has a significant strengthening effect on the composites, but the high temperature causes softening of the Cu matrix and the growth of grains reduces the properties of the composites. In this study, the effects of porosity and density on the composite properties were not significant.

Carbon fibers (CFs) cannot be directly used for the preparation of CF paper because of their chemically inert nature. Herein, the surface of CF was modified via the spontaneous oxidative self-polymerization of dopamine. By taking full advantage of the spontaneous oxidation and self-polymerization properties of PD to maintain the maximum strength of CFs, a polydopamine-modified CF paper (PDA-CFP) with excellent performance was prepared using PD-modified CFs (PDA-CFs), which increased the proportion of hydrophilic functional groups on the surface of carbon fibers, increased the O/C ratio on the CF surface by 6 times, and improved the bond strength between the modified CF and the adhesive by making full use of the interaction force between polydopamine and PVA fibers. In this way, the primary properties of the CF paper was improved. Overall, the results showed that the dispersion of CF was considerably improved by the dopamine modification. In addition, the primary physical properties of PDA-CFP were better than those of virgin CF paper (CFP-0). PDA-CFP exhibited a maximum tensile strength of 2.04 kN/m2, a minimum resistivity of 0.06055 Ω·cm and a minimum porosity of 72.4%. The tightness could be increased by up to 12.1%.

Finishing coatings used in the wood-based composites industry play a key role in the final appearance of the finished product. However, the use of such coatings is not only for aesthetic purposes but also to protect the product against surface damage and moisture or minimize the emission of harmful substances. The latter is an extremely important factor in terms of safety for both the manufacturer and the user, which is why the emissivity test is one of the most important tests in the case of finishing coatings. Such a role can be played by carbon-rich materials, such as those remaining from the extraction of birch bark. In this article, an attempt was made to create coatings in the form of a film by combining a biopolymer with suberinic acid residues (SAR). There were two types of biopolymers used – polylactide (PLA) and polycaprolactone (PCL), in various polymer-SAR ratios. SAR as a residue, is a material that bounds CO2 from the atmosphere and creates a possibility of further use. As part of this study, the obtained coatings were tested in terms of resistance to scratch, relative hardness, cold liquids, total volatile organic compounds (TVOC) and formaldehyde emission, surface absorption etc. Differences in the polymers used and the effect of the SAR additive on selected surface properties were demonstrated. The addition of carbon-rich SAR significantly improves the gas barrier properties of the surface finishing materials based on PLA and PCL. The relative hardness and scratch resistance has also increased with raising SAR content. However, the increasing content of SAR filler act as a limiter in the depth of penetration of deposited surface finishing materials onto the wood surface.

The use of interleaving material with viscoelastic properties is one of the most effective solutions to improve the damping capacity of CFRP laminates. Improving composite damping without threatening mechanical performance is challenging and the use of nanomaterials should lead to the target. In this paper, the effect of a nanostructured interlayer based on Graphite Nanoplatelets (GNPs) on the damping capacity and fracture toughness of CFRP laminates has been investigated. High-content GNP/Epoxy (70wt/30wt) coating was sprayed on the surface of CF/Epoxy prepregs at two different areal weight (10 and 40 g/m2) and incorporated at the middle-plane of a CFRP laminate. The effect of the GNP areal weight on viscoelastic and the mechanical behaviour of the laminates was investigated. Coupons with low-areal weight GNP interlayer showed a 25% increase in damping capacity with a trivial reduction of the elastic modulus. Moreover, a reduction in interlaminar shear strength (ILSS) and fracture toughness (both mode I and mode II) was observed in the composites with GNPs interlayer. GNPs alignment and degree of compaction reached during process were found as key parameters on material performances. By increasing the areal weight a mitigation on the mechanical performances drop was achieved (-15%).

For thermoelectric materials study and development, it is very important to measure the electrical power and efficiency of a thermoelectric generator (TEG). In this study, thermoelectric properties such as electrical conductivity, Seebeck coefficient, and thermal conductivity of cement composites with graphene nanoplatelets and metallic oxides (Fe2O3, ZnO, MnO2) are measured and subsequently used to figure out the output electrical power and efficiency. A maximum of 1.5 W power per square meter for a temperature difference of about 50 °C can be estimated using GnP-ZnO added cement composites. This paper also talks about how to make a cement composite-based structural TEG module to enhance the total output voltage, power, and efficiency of the system.

Deformation behavior of MXene based polymer composites with bioinspired brick and mortar structures is analyzed. MXene/Polymer nanocomposites are modeled at microscale using bioinspired configurations of nacre-mimetic brick-and-mortar assembly structure. MXenes (brick) with polymer matrix (mortar) are modeled using classical analytical methods and numerical methods based on Finite Elements (FE). The analytical methods provide less accurate estimation of elastic properties compared to numerical one. MXene nanocomposite models analyzed with FE method provide estimates of elastic constants in the same order of magnitude as literature reported experimental results with good consistency. Bioinspired design of MXene nanocomposites results in the effective Young’s modulus of the nanocomposite increase by 25.1 % and the strength (maximum stress capacity within elastic limits) increase by 42.3 %. The brick and mortar structure of the nanocomposites leads to interlocking mechanism between MXene fillers in polymer matrix, resulting in effective load transfer, good strength, and damage resistance. This is demonstrated in this paper by numerical analysis of MXene nanocomposites subjected to quasi-static loads.

The article describes the study of the properties of polytetrafluoroethylene, modified using natural layered silicates—serpentinite. It is shown that the introduction of a small amount of layered silicates significantly increases the tribological characteristics of the material. The additional introduction of magnesium nano-spinels facilitated the formation of an intercalated polymer-silicate nanocomposite.

In the present work, an innovative range of foams, based on flax gum-filled epoxy resin was developed, reinforced or not by flax fibers. Foams and composites with different gum and epoxy resin contents were produced and characterized for mechanical and thermal performances. To enhance the organic flax gum filler's cross-linking, we exploited the oxidized components' reactivity with the amine hardener (isophorone diamine). We compared the materials obtained with those derived from the native components. Flax gum and fibers were primarily characterized by chemical analysis, NMR, and FTIR to evaluate the mild oxidation of native materials. The formation of chemical bonds between oxidized polymer chains, epoxy resin, and hardener has been evidenced by FTIR, and the materials were then studied by SEM, X-ray computed micro-tomography (CT), and submitted to mechanical and thermal tests. The relevance of oxidation treatment was highlighted, through a significant increase in density and mechanical performances (+36% and +81%, respectively for the 100% flax gum material). The positive effect of flax fibers on homogeneity evidenced through micro-CT analysis was also clearly addressed. This set of promising results paves the way for future development of fully flax-based insulation composite materials.