Direct-to-blister copper flash smelting slag contains up to 14% of copper and 2-4% of lead. Considering this fact, this material is subjected to the high-temperature reduction process. After this, converting process is performed on the Cu-Pb-Fe alloy being the product of decopperization process in electric furnace. An alternative to the presently used processing of flash smelting slag would be its hydrometallurgical treatment and selective recovery of Pb and Cu. This paper presents the results of laboratory tests on flash smelting slag leaching with citric acid solutions. The experiments performed allowed to determine the process parameters at which the Pb concentration in the post-leaching sediment reached the value of 0.41-0.6% while the Pb content in flash smelting slag was 3.05%. Analogous values for copper were 11.5-11.8% (after leaching) and 12.44% (before). Material after leaching in citric acid solutions can be processed, in the second step, using sulfuric acid solutions, and it could lead to the recovery of almost all copper contained in it.

The commercial oxygen-free copper sheets were cold-rolled with reduction rates ranging from 20% to 87% reduction rate and annealed at 400, 500 and 600 °C. The microstructure and texture evolution during cold-rolling and annealing processes were studied using optical microscopy (OM), the scanning electron microscopy (SEM) and the electron back-scattered diffraction (EBSD). The results show that the deformation textures of {123} (S) , {112} (Copper) and {110} (Brass) were continuously enhanced with the increase of cold-rolling reduction. The orientations along the α-oriented fiber converged towards Brass and the orientation density of β fiber obviously increased when the rolling reduction exceeded 60%. The recrystallization texture was significantly affected by the cold-rolling reduction. After 60% cold-rolling reduction, Copper and S textures components gradually decreased and {011} recrystallization texture component formed with the increase of annealing temperature. After 87% cold-rolling reduction, a strong Cube texture formed and other textures were inhibited with the increase of annealing temperature. The strong Brass and S deformation texture was conducive to the formation of a strong Cube annealing texture. The density of annealing twin boundary decreased with the increase of annealing temperature, and more annealing twin boundaries formed in the oxygen-free copper sheets with the increase of cold rolling reduction.

The aim of the research was a comprehensive evaluation of concrete using the EIPI method. In the evaluation the compressive strength of concrete and its durability properties represented by sorptivity and air permeability were taken into account. Since copper slag waste with increased natural radioactivity was used in the assessed concrete, additional evaluation was carried out taking into account the influence of natural radioactivity within the performance index. Also the reference concrete, which was made without the use of copper slag waste, was evaluated for comparative purposes. In order to make the evaluation as comprehensive as possible, the concrete made with the use of three types of cement was subjected to the assessment: CEM I, CEM II and CEM III. The results show that in both approaches the best result was achieved by concrete with CEM III cement. If natural radioactivity is not taken into account in the evaluation, the best result is obtained by concrete made with copper slag waste, and if radioactivity is considered, the best result is obtained with concrete without addition of the waste. It follows from the above that although natural radioactivity has a significant impact on the EIPI evaluation result, the decisive factor is still the type of cement.

Composite fiber materials are superior materials due to their high strength and light weight. Composites reflect the properties of their constituents, which is proportional to the volume fraction of each phase. There are different fiber reinforcement types and each affects it’s flexural, tensile and compression strength. When selecting a composite for a specific application, the forces excreted on the composite must be known in order to determine the reinforcement type. Unidirectional fiber reinforcement will allow very strong load resistance but only in one direction where as a random orientated fiber reinforcement can resist less load but can maintain this quota in all directions. These materials are said to be anisotropic. Certain composite fibers, taking into consideration there weights, are physically stronger than conventional metals. This research deals with the analysis of three composite materials with different reinforcement types, volume fraction and phase content. It was found that material A (glass epoxy) was the strongest in the longitudinal direction with a flexural strength of 534 MPa in the longitudinal and 420 MPa in the transverse direction. The flexural stresses of material B (glass silicone) and material C (glass polyester) where both found in the 120 to 135 MPa range. Differences were due to their differences in matrix composition and reinforcement type.

Copper smelting slag is a solution of molten oxides created during the copper smelting and refining process, and about 1.5 million tons of copper slag is generated annually in Korea. Oxides in copper smelting slag include ferrous (FeO), ferric oxide (Fe­₂O₃), silica (SiO­₂ from flux), alumina (AI₂O₃), calcia (CaO) and magnesia (MgO). Main oxides in copper slag, which iron oxide and silica, exist in the form of fayalite (2FeO·SiO₂). Since the copper smelting slag contains high content of iron, and copper and zinc. Common applications of copper smelting slag are the value added products such as abrasive tools, roofing granules, road-base construction, railroad ballast, fine aggregate in concrete, etc., as well as the some studies have attempted to recover metal values from copper slag. This research was intended to recovery Fe-Cu alloy, raw material of zinc and produce reformed slag like a blast furnace slag for blast furnace slag cement from copper slag. As a results, it was confirmed that reduction smelting by carbon at temperatures above 1400°С is possible to recover pig iron containing copper from copper smelting slag, and CaO additives in the reduction smelting assist to reduce iron oxide in the fayalite and change the chemical and mineralogical composition of the slag. Copper oxide in the slag can be easily reduced and dissolved in the molten pig iron, and zinc oxide is also reduced to a volatile zinc, which is removed from the furnace as the fumes, by carbon during reduction process. When CaO addition is above 5wt.%, acid slag has been completely transformed to calcium silicate slag and observed like blast furnace slag.

In order to study the feasibility of copper-nickel smelting slag（CNSS） and palygorskite for large-scale consumption and utilization in the field of mine filling, gellable composite materials were prepared from copper-nickel smelting slag ,cement and palygorskite. The effects of palygorskite addition and curing time on the mechanical properties and microstructure of copper-nickel smelting slag-based cementitious materials were studied in detail. The results showed that the addition of palygorskite had a positive effect on the curing of the cemented filler of the non-ferrous smelting slag by promoting the early hydration reaction. palygorskite also affected the mechanical properties of the cementitious materials with different maintenance times and the ability to cure heavy metals. The strength of gellable composite materials reaches 23.05MPa when 1% palygorskite, 50% of copper-nickel smelting slag and 48% cement were used, which meet the standards requirements of filling materials for mine goaf. The addition of 1% palygorskite can improve the ability of cementitious materials to solidify heavy metals to realize the economic utilization of solid waste in mining areas.

The depletion of the ore reserves in the world necessitates the search for secondary sources such as waste products (tailings and slag). A smelter in Namibia has historic slag which accumulated over decades of its operating life. Analytical and mineralogical characterization of the slag was performed using the X-ray fluorescence (XRF) analysis, Atomic Absorption Spectrometer (AAS), ICP-OES, scanning electron microscopy energy dispersive spectroscopy (SEM-EDS) analysis, and optical microscopy analysis. The chemical analyses showed that the metal values contained in the slag were mainly copper, lead, and zinc whose average contents were approximately 0.3%Cu, 2.4%Pb and 3.2%Zn. About 10.5%Fe was also contained in the slag. Germanium was detected by scanning electron microscopy, but was however below detection limits of the chemical analysis equipment used. Based on the results, approximate conditions under which the different slag phases were formed were estimated and the recovery routes for the various metals were proposed. Analysis by both optical and scanning electron microscopy revealed that Zn and Fe occurred mainly in association with O as oxides, while Cu and Pb were mainly associated with S as sulphides. The slag consisted of three different phases; namely the silicate phase (slag), metallic phase and the sulphide phases. The slag phases were mainly glass, silicate phases and metallic and sulphide phases. It was observed that the metallic and sulphide phases were dominant in the finer size fractions (-75 µm) whereas the sulphide phase was also present in the coarser size fractions (+300 µm). An important finding from the microscopy examination was that the sulphide phases were interstitial and could be liberated from the slag. This finding meant that liberation and subsequent concentration of the sulphide phases was feasible using conventional processing techniques.

The effects of rare earth Ce on the microstructure and properties of cast pure copper were investigated through thermodynamic calculations, XRD analysis, mechanical testing, metallographic microscopy, and scanning electron microscopy (SEM). The experimental results demonstrate that the reaction between rare earth Ce and oxygen as well as sulfur in copper exhibits a significantly negative Gibbs free energy value, indicating a strong thermodynamic driving force for deoxidation and desulfurization reactions. Ce is capable of removing trace amounts of O and S from copper. Moreover, the maximum solid solubility of Ce in Cu falls within the range of 0.009% to 0.01%. Furthermore, Ce can refine columnar grains while enlarging equiaxed grains in as-cast copper.Upon addition of rare earth Ce, the tensile strength increased by 8.45%, elongation increased by 12.1%, and microhardness rose from 73.5HV to 81.2HV-an increase of 10.5%. Overall, rare earth Ce has been found to enhance both the microstructure and mechanical properties of cast pure copper.

In recent decades, the requirements for implantable medical devices increased, but the risks of implant rejection still exist. These issues are primarily associated with poor osseointegration, leading to biofilm formation on the implant surface. This study focuses on addressing these issues by developing a biomaterial for implant coatings. 45S5 Bioglass has been widely used in tissue engineering due to its ability to form a hydroxyapatite layer, ensuring a strong bond between the hard tissue and the bioglass. In this context, 45S5 bioglasses, modified by the incorporation of different amounts of copper oxide, from 0 to 8 mol%, were synthesized by the melt-quenching technique. The incorporation of Cu ions does not show a significant change in the glass structure. Since the bioglass exhibited the capacity of being polarized, and therefore promoting the osseointegration effectiveness, the electrical properties of the prepared samples were studied using the impedance spectroscopy method, in the frequency range of 102-106 Hz and temperature range of 200-400 K. The effects of CuO on charge transport mobility were investigated. Additionally, the bioactivity of the modified bioglasses was evaluated through immersion tests in simulated body fluid. The results revealed the initiation of a Ca-P-rich layer formation on the surface within 24 h, indicating the potential of the bioglasses to enhance the bone regeneration process.

Tailings generated by mining account for the largest proportion of global waste from industrial activities. Copper is relatively uncommon world-wide, with low concentrations in sediments and waters, yet is very elevated around mining sites. On the Keweenaw Peninsula of Michigan, USA, jutting out into Lake Superior, 140 mines extracted native copper from the Portage Lake Volcanic Series, part of an intercontinental rift system. Between 1901-1932, two mills at Gay (Mohawk, Wolverine) sluiced 22.7 million metric tonnes (MMT) of copper-rich tailings (stamp sands) into Grand (Big) Traverse Bay. Here we examine: 1) 3D coastal elevation and reef bathymetry, 2) particle dispersal, 3) copper concentrations and leaching, plus 4) shoreline toxicity. About 10 MMT of tailings created a migrating coastal beach that stretches 7 km from the Gay pile to the Traverse River Seawall. Another 10 MMT are moving underwater on the coastal shelf, threatening Buffalo Reef, an important lake trout and whitefish breeding ground. Aerial photos, ALS (plane) LiDAR, and relatively inexpensive UAS (drone) surveys characterize shoreline structure and aid initial remediation. Because sands (natural beach quartz, stamp sand basalt) are silicates of similar density, particle dispersal is similar and challenging. However, stamp sand beaches contrast greatly with natural sand beaches in both physical profile and chemistry. Dispersing particles retain copper, and release toxic concentrations. Leaching is elevated by exposure to high DOC and low pH waters. Field experiments, shoreline seining, and benthic sampling confirm serious impacts on aquatic biota, supporting tailings removal.

Cement paste backfill (CPB) is an effective waste management method allowing the storage of fine process tailings into underground mined-out voids. CPB performance generally depends on the sulfur content of the tailings and the type of binder. In recent years, there has been an in-creasing trend on the use of alkali-activated slag (AAS) to improve the performance properties of CPB. This study focuses on the ultrasonic and microstructural investigation of the effect of slag fineness on the mechanical, geochemical and durability properties of CPB made up of AAS (AAS-CPB) over 360 days. In this scope, AAS-CPB samples were prepared at three different fineness (3100-4650-6300 cm2/g). Fineness of slag significantly improved the early age- and long-term strength (~2.3 fold and ~6.6 fold, respectively) of CPB. However, further increase of slag fineness may have adverse effect on CPB microstructure and strength in the long term. Ultrasonic pulse velocity monitoring displayed very high relation with the strength evolution and durability assessment of CPB. Slag fineness at a degree was seen to improve the pore structure evolution of AAS-CPB. Microstructural studies are in good agreement with the geochemical and durability behavior of AAS-CPB. Microstructural and ultrasonic findings suggest that while slag fineness enhances the mechanical properties of AAS-CPB, further increase of the fineness of slag has no additional important technical advantages.

The objective of this study was to investigate the concentration and spatial distribution patterns of six potentially toxic heavy metal elements (Mn, Zn, Cr, Pb, Cu and Ni) in bus station dusts in the Xifeng district of Gansu province, NW China. The contents were analyzed for Mn, Zn, Cr, Pb, Cu and Ni by using S8 TIGER Brochures wavelength dispersive X-ray fluorescence spectrometry. Geoaccumulation index (Igeo ), enrichment factor (EF), pollution index (PI) and integrated pollution index(IPI) were calculated to evaluate the heavy metal contamination level of bus station dusts. The results indicate that, in comparison with the background values of local soil, bus station dusts in Xifeng have elevated metal concentrations as a whole. The concentrations of heavy metals investigated in this paper are compared with the reported data of other cities. The results show that the arithmetic means of Mn, Zn, Cr, Pb, Cu and Ni are 440.8, 137.9, 60.0, 42.8, 33.5 and 19.8mg kg−1 respectively. The mean values of Igeo reveal the order of Ni<Mn<Cr<Cu<Zn<Pb. The high Igeo and EF for Cu, Zn and Pb in bus station dusts indicate that there is a considerable Cu, Zn and Pb pollution, which mainly originate from traffic and industry activities. The Igeo and EF of Ni, Mn and Cr are low and the assessment results indicate an absence of distinct Ni, Mn and Cr pollution in bus station dusts. The assessment results of PI also support Cu, Zn and Pb in bus station dusts presented middle pollution, and IPI indicates heavy metals of bus station dusts polluted seriously.

The constant increase in current density in electrical wires leads to increasingly significant heat losses due to Joule effect. Therefore, reducing the electrical resistivity of copper wires becomes necessary. To achieve this goal, the development of a composite material incorporating a more conductive reinforcement, the graphene, is a promising way. The design of a copper/graphene composite using a powder metallurgy-based method is presented. This synthesis method allows for interface control through the growth of CuO(Cu) nanoparticles tightly bonded to the reinforcement. It also involves the dispersion of graphene through ultrasonic treatment and its alignment within the matrix using a uniaxial pressing densification method. The increase in the hardness (+12 HV) demonstrates the effective dispersion and separation of graphene layers. The impact on the electrical properties of dendritic copper (ρe = 2.30 µΩ.cm) remains limited, with a decrease in electrical resistance of approximately 1.4%. However, for copper with higher electrical resistivity, flake copper (at 2.71 µΩ.cm) and brass at (7.66 µΩ.cm), reductions of 2.7% and 10% have been achieved, respectively. With the improvement of graphene quality, there is more room to improve the electrical properties. This work paves the way for the development of composites with improved electrical resistivity.

Drosophila melanogaster serves as a important research model both for genetic investigations and for the study of metal toxicity, facilitating the elucidation of physiological mechanisms comparable to those of human organisms. In our research, we evaluated the toxicity effect resulting from exposure to various concentrations of lead and copper on the prolificity rates throughout the life cycle (egg-adult) of four genotypes of Drosophila melanogaster: wild-type (control), white, brown, and white-vestigial. During our study, the prolificity rates were examined across three repetitions under the impact of exposure to concentrations of 0.50, 1.00, 2.00, and 4.00 mM of copper (CuSO₄) and lead (Pb(C₂H₃O₂₎₂). Prolificity rates throughout the life cycle exhibited variations as a direct consequence of genetic factors, the concentration of exposure, and the specific type of metal, either copper or lead. The mutant white-vestigial genotype revealed an IC₅₀ concentration for prolificity inhibition at lower doses of 2.00 mM for copper and 4.00 mM for lead, in contrast to the control genotype (wild-type), which exhibited an inhibition concentration rate >IC₅₀ of 4.00 mM only in the case of copper. Our results concluded that the (i) dose influences the prolificity rate in a directly proportional manner, (ii) comparative analyses between copper and lead revealed that copper displayed toxicity across all genotypes within the concentration range of 0.50 mM to 2.00 mM. In contrast, lead exhibited toxicity within the concentration range of 1.00 mM to 4.00 mM, highlighting a (iii) more acute toxicity characteristic in the case of copper. Thus, the results of this research reflect the importance of using Drosophila melanogaster as a genetic model in the comparative study of the interaction between genetic factors and the toxicity of metals, offering significant insights into monitoring their impact and defining the maximum permissible doses on organisms.

Millions of people worldwide are affected by diabetes, a chronic disease that continuously grows due to abnormal glucose concentration levels present in the blood. Monitoring blood glucose concentrations is therefore an essential diabetes indicator to aid in the management of the disease. Enzymatic electrochemical glucose sensors presently account for the bulk of glucose sensors in the market. However, their disadvantages are that they are expensive and are dependent on environmental conditions, hence affecting their performance and sensitivity. To meet the increasing demand, non-enzymatic glucose sensors based on chemically modified electrodes for the direct electrocatalytic oxidation of glucose are a good alternative to the costly enzymatic-based sensors currently on the market, and the research thereof continues to grow. Nanotechnology-based biosensors have been explored for their electronic and mechanical properties, resulting in enhanced biological signalling through the direct oxidation of glucose. Copper oxide and copper sulfide exhibit attractive attributes for sensor application, due to their non-toxic nature, abundance, and their unique properties. Thus, in this review, copper oxide and copper sulfide-based materials, are evaluated based on their chemical structure, morphology, and fast electron mobility as suitable electrode materials for non-enzymatic glucose sensors. The review highlights the present challenges of non-enzymatic glucose sensors that have limited their deployment into the market.

Copper (Cu) is an essential micronutrient for the correct development of eukaryotic organisms. This metal plays a key role in many cellular and physiological activities, including enzymatic activity, oxygen transport, and cell signaling. Although the redox activity of Cu is crucial for enzymatic reactions, this property also makes it potentially toxic when found at high levels. Due to this dual action of Cu, highly regulated mechanisms are necessary to prevent both the deficiency and the accumulation of this metal since its dyshomeostasis may favor the development of multiple diseases, such as Menkes’ and Wilson’s diseases, neurodegenerative diseases, diabetes mellitus, and cancer. As the relationship between Cu and cancer has been the most studied, we analyze how this metal can affect three fundamental processes for tumor progression: cell proliferation, angiogenesis, and metastasis. Gynecological diseases are characterized by high prevalence, morbidity, and mortality, depending on the case, and mainly include benign and malignant tumors. The cellular processes that promote their progression are affected by Cu, and the mechanisms that occur may be similar. We analyze the crosstalk between Cu deregulation and gynecological diseases, focusing on therapeutic strategies derived from this metal.

With the increased use of laterite nickel ore, the impact of high Al2O3 slag on blast furnace smelting has gradually increased. In this paper, the effects of slag basicity and Al2O3 content on slag viscosity and enthalpy change under constant temperature conditions was investigated. The changes in slag structure were analyzed by activation energy and Fourier Transform Infrared (FT-IR) spectroscopy. The relationship between slag components and slag temperature and viscosity when slag heat is reduced was investigated. The results showed that the viscosity first slightly decreased and then significantly increased with increasing basicity at constant temperature. With the addition of Al2O3 content, the viscosity of the slag increases. The activation energy increases with increasing slag basicity and Al2O3. With increasing basicity, the [SiO4]4- tetrahedral unit trough depth becomes shallow, the [AlO4]5- asymmetric stretching band migrates to lower wave numbers, and the slag structure depolymerizes. With the increase of Al2O3 content, the trough of [SiO4]4- tetrahedra deepens and the center of the symmetric stretching band moves to a higher wave number. The [AlO4]5- asymmetric stretching band becomes obvious, indicating the complexity of the slag structure. When the heat decreases, the slag temperature increases as the basicity increases, and the slag thermal stability is better at the basicity of 0.95-1.05. As the Al2O3 content increases, the thermal stability of the slag becomes worse.

The carbonation of industrial calcium-rich byproducts such as steel slag demonstrates significant potential for CO2 sequestration. This technique aids in reducing carbon emissions while also promoting waste recycling. Despite its advantages, gaps remain in understanding how steel slag characteristics and operational parameters influence the carbonation process, as well as the underlying mechanism of direct aqueous carbonation. We evaluated the carbonation performance of three types of steel slag at temperatures below 100°C using a gas–liquid–solid reaction system. The slag with the highest CO2 sequestration capacity was chosen for a systematic evaluation of the effects of operating conditions on carbonation efficiency. Thermodynamic analysis indicated that the reactivity of CaO and Ca(OH)2 with CO2 exceeded that of CaO•SiO2 and 2CaO•SiO2. Under conditions of 85°C, a particle size less than 75 μm, an initial CO2 pressure of 0.5 MPa, a liquid-to-solid ratio of 5 mL/g, and a stirring speed of 200 rpm, the steel slag achieved a sequestration capacity (K) of 283.5 gCO2/kg and a carbonation efficiency (ζCa) of 51.61%. Characterization of the slag before and after carbonation using X-ray diffraction, SEM‒EDS, thermogravimetric analysis, and Fourier transform infrared spectrometry confirmed the formation of new carbonates. Mechanistic analysis revealed that the rate-limiting step initially involved the mass transfer of CO2, transitioning to Ca2+ mass transfer as time progressed. Our research provides a viable technique for CO2 capture and a beneficial approach for reutilizing waste steel slag. Furthermore, solid residues after capturing CO2 have the potential for conversion into carbon-negative building materials, offering a sustainable strategy for steel companies and other enterprises with high carbon emissions.

Steel slag and GBFS are wastes generated during the steel and iron smelting process, characterized by their considerable production rates and extensive storage capacities. After grinding, they are often used as supplementary cementitious materials. However, the intrinsic slow hydration kinetics of steel slag-GBFS cementitious material (SGM) when exposed to a pure water environment result in prolonged setting times and diminished early-age strength development. The incorporation of modifiers such as gypsum, clinker, or alkaline activators can effectively improve the various properties of SGM. This comprehensive review delves into existing research on the utilization of SGM, examining their hydration mechanisms, workability, setting time, mechanical strengths, durability, and shrinkage. Critical parameters including the performance of base materials (water-to-cement ratio, fineness, and composition) and modifiers (type, alkali content, and dosage) are scrutinized to understand their influence on the final properties of the cementitious materials. The improvement mechanisms of various modifiers on properties are discussed. This the promotes resource utilization of industrial solid wastes and provides theoretical and technical support for the application of SGM.

As the coproduct of steelmaking, steelmaking slag, volumetrically expansive-prone without treatment, has been satisfactorily used as an aggregate base course material in highway construction. Although numerous technical reports and papers have revealed that steel slag aggreged using in rigid matrixes, the end product, paving block, non-structural concrete, for example, possesses superb strength and durability properties, the application of steel slag aggregate as a concrete aggregate is currently prohibited in highway construction. Naturally, researchers explore the practicality of use of steel slag, how to connect the laboratory experiment results to the end-product behavior, and further convert the research results into real construction? For all nontraditional or secondary materials utilization, the procedure of laboratory material examination, lab and field trial test are critical. To generalize the utilization, usability criteria establishment is necessary. This paper tries to use step-by-step method and plain language to explain how the volumetrically expansion can be simulated in lab testing apparatus, and based on the model, the mathematical deduction can result in a numerical usability criterion for steel slag use as a coarse aggregate in concrete (a rigid material). Therefore the paper is composed four main parts, laboratory test methods to examine the expansion force resulted from steel slag; converting the measured expansion force in a given volume of mass aggregate to the expansion (body) force of a single particle; modeling of slag and end material disruption; and a usability criterion from numerical deduction for the use of expansive-prone coarse slag in concrete or other rigid matrices. The paper provides the solutions to answer the above questions. Through the mathematical and mechanical modeling, provides the potential criteria that could result in specifications and guidance establishment for broad volumetric expansive-prone slags.

Copper, which can potentially be a highly toxic agent, is an essential nutrient due to its role as a co-factor for cuproenzymes and participation in signaling pathways. In mammals, the liver is a central organ that controls copper turnover throughout the body: copper absorption, distribution, and excretion. In ontogenesis, there are two types of copper metabolism: embryonic and adult, which maintain the balance of copper in each of these periods, respectively. In the liver cells, these types are characterized by specific expression patterns and activity levels of the genes encoding ceruloplasmin, which is the main extracellular ferroxidase and copper transporter and proteins mediating ceruloplasmin metalation. In newborns, the molecular-genetic mechanisms responsible for copper homeostasis and the ontogenetic switch from embryonic to adult copper metabolism are highly adapted to milk ceruloplasmin as a dietary source of copper. In the mammary gland cells, the level of ceruloplasmin gene expression and the alternative splicing of its pre-mRNA govern the amount of ceruloplasmin in milk, and thus, the amount of copper absorbed by the newborn is controlled. In the newborns, absorption, distribution, and accumulation copper are adapted to milk ceruloplasmin. In the newborns, which are not breast-fed at the early stages of postnatal development, the control for alimentary copper balance is absent. We tried to focus on the neonatal consequences of a violation of the balance of copper in the mother / newborn system. Although there is still much to be learned, the time to pay attention to this problem came because the neonatal misbalance of copper may provoke the development of copper related disorders for future life.

Copper(II), nickel(II) and zinc(II) complexes of various peptide fragments of tau protein were studied by potentiometric and spectroscopic techniques. All peptides contained one histidyl residue and represented the sequences of tau(91-97) (Ac-AQPHTEI-NH2), tau(385-390) (Ac-KTDHGA-NH2) and tau(404-409) (Ac-SPRHLS-NH2). Imidazole-N donors of histidine were the primary metal binding sites for all peptides and all metal ions but in case of copper(II) and nickel(II) the deprotonated amide groups were also involved in metal binding by increasing pH. The most stable complexes were formed with copper(II) ion but the presence of prolyl residues resulted in significant changes in the thermodynamic stability and speciation of the systems. It was also demonstrated that nickel(II) and especially zinc(II) complexes have relative low thermodynamic stability with these peptides. Copper(II) catalyzed oxidation of the peptides was also studied. In the presence of H2O2 the fragmentation of peptides can be detected in all cases. In the simultaneous presence of of H2O2 and ascorbic acid the extent of the fragmentation of the peptide is less preferred, and the formation of 2-oxo-histidine also occurs.

The heavy transition metal tantalum (Ta) offers a wide range of applications, especially in the field of electronics, e.g. Ta capacitors with a comparatively long life-time. Therefore, electronic scrap containing these components is a potentially valuable secondary source of this metal. However, the recovery of Ta, as other critical raw materials, that are lost in pyrometallurgical slags can be a challenging process. As a way of overcome this, the "engineered artificial minerals" EnAM approach is proposed by first searching for suitable host minerals and characterizing them. A favorable prerequisite is the enrichment of the desired element(s) in compounds that have particularly suitable properties for this purpose, such as morphology, crystal size, surface or magnetic properties. Subsequently, the slag system is adapted (e.g. chemism, solidification curve, cooling and holding times) to optimize this compound. This paper presents the results of mineralogical characterization of Ta-containing iron (Fe)-rich synthetic slags in reducing environment under different cooling rates, and describes and discusses the incorporation of Ta into the different compounds detected by powder X-ray diffraction (PXRD) and electron beam microanalysis (EPMA). Additionally, the speciation of Fe and Ta was accessible through X-Ray absorption near edge structure (XANES) spectroscopy. EPMA also provides a first semi-quantitative assessment of the Ta distribution in these individual compounds. According to this, depending on the cooling rate the enrichment factor is highest in tantalite/perovskite-type oxides (FexTayO6, CaxFeyTazO3) with up to 60 wt.% Ta and ‘tantalomagnetite’ (FeII(FeIII(2-5/3xTax)O4) with a maximum of ~ 30 wt.% Ta (only fast cooling). This is followed by a perovskite-like silicon containing oxide (XYO3) with 12-15 wt.-% Ta (only slow cooling), and a hedenbergite-like compound (XYZ2O6) with varying content of 0.3 - 7 wt.-%. The Ta-concentration in pure Fe, Fe(1-x)O, hercynitic spinel and hematite is negligible. Since a larger fraction of potentially amorphous hedenbergitic matrix is formed at faster cooling, in this case the main Ta is enriched in this compound despite the significantly lower Ta content.

Replacing carbon by hydrogen is a huge step towards reducing CO₂ emissions in the iron- and steel-making industry. The reduction of iron oxides using hydrogen plasma smelting reduction as an alternative to conventional steel-making routes has been studied at Montanuniversitaet Leoben, Austria. The aim of this work was to study the slag formation during the reduction process and the reduction behaviour of iron oxides. Furthermore, the reduction behaviour of iron ore during continuous feeding was assessed. Mixtures of iron ore and calcined lime with a basicity of 0, 0.8, 1.6, 2.3, and 2.9 were melted and reduced by hydrogen. The off-gas composition was measured during the operations to calculate the process parameters. The reduction parameters, namely the degree of reduction, degree of hydrogen utilisation, produced iron, and slag, are presented. The results of the batch-charged experiments showed that at the beginning of the reduction process, the degree of hydrogen utilisation was high, and then, it decreased over the operation time. In contrast, during the continuous-feeding experiment, the degree of hydrogen utilisation could be kept approximately constant. The highest degrees of reduction and hydrogen utilisation were obtained upon the application of a slag with a basicity of 2.3. The experiment showed that upon the continuous feeding of iron ore, the best conditions for the reduction process using hydrogen could be applied.

Electric arc furnace oxidizing slag (EAF) has a high density of 3.0~3.7 t/m3 and therefore has a high bulk density when mixed with concrete. Extensive research has been conducted on the use of concrete with high unit volume weight as heavyweight concrete for radiation shielding concrete. In this study, to examine the possibility of developing a radiation shielding concrete, the physical properties of normal concrete, magnetite concrete, EAF concrete, and EAF concrete with added iron powder, were compared. Also, their radiation shielding performance was assessed through shielding tests against X-rays and γ-rays. While the unit volume weight of EAF concrete (3.21 t/m3) appeared lower than that of magnetite concrete (3.5 t/m3), the compressive strength of EAF concrete was greater than those of magnetite and normal concretes. The radiation shielding ratio of magnetite concrete was observed to be 93.9% from the X-ray shielding test, followed by 91.2% of EAF concrete, and 73.7% of normal concrete, indicating a linear relationship with unit volume weight. From the γ-ray shielding test, the performance of EAF and magnetite concretes appeared to be similar. Based on the excellent physical properties and radiation shielding performance of EAF concrete, its potential applicability as radiation shielding concrete was confirmed.

Supplementation with 200% of the recommended daily dietary quantity of copper modified vascular contraction and relaxation through increased reactive oxygen species (ROS) and prostaglandin formation, which modified the antioxidant status of middle–aged rats. In this study, young (1 month old) male Wistar rats (n/group = 10) received a diet supplemented with 6.45 mg copper/kg (100%—Group A) for 8 weeks. The experimental group received 12.9 mg copper/kg of diet (200%—Group B). Experimental supplementation with 200% copper increased the copper concentration in the blood, liver, and kidneys; increased the ROS concentration in the aortic rings; and enhanced the sensitivity of the aortic rings to acetylcholine. We observed increased participation of nitric oxide (NO) derived from inducible NO synthase (iNOS) in vascular contraction and a decreased net effect of vasodilator prostanoids derived from cyclooxygenase–2 (COX–2) in vascular relaxation. Supplementation with 200% copper was less significant than expected after previous studies conducted with middle–aged rats.

There is much interest in effective copper chelators to correct copper dyshomeostasis in neurodegenerative and oncological diseases. In this study, a recombinant fusion protein for expression in E. coli cells was constructed from glutathione-S-transferase (GST) and the N-terminal domain (ectodomain) of human high affinity copper transporter CTR1 (hNdCTR1), which has three metal-bound motifs. Several biological properties of the GST-hNdCTR1 fusion protein were assessed. It was demonstrated that in cells, the protein was prone to oligomerization, formed inclusion bodies and displayed no toxicity. Treatment of E. coli cells with copper and silver ions reduced cell viability in a dose- and time-dependent manner. Cells expressing GST-hNdCTR1 protein demonstrated resistance to the metal treatments. These cells accumulated silver ions and formed nanoparticles that contained AgCl and Ag0. In this bacterial population, filamentous bacteria with length about 10 μm were often observed. The possibility for the fusion protein carrying extracellular metal binding motifs to integrate into the cell’s copper metabolism and its chelating properties are discussed.

In article questions of development low-waste technologies of processing of steel-smelting slag are considered, gland allowing by extraction and its connections from steel-smelting slag to receive additional raw materials for production became, and the remains to use in building industry. Studying of gravitational methods of enrichment of steel-smelting slag and heat treatment the ore-fuel of pellets is the basis for work. Proceeding from it, in work modern physic-mechanical, chemical and physical and chemical methods of researches (UV-spectroscopy, electronic microscopy, the granulometric analysis) are used.

The basic oxygen furnace slag (BOF) was wide used in road construction, but there was a lack of characteristics in different asphalt mixtures. This study investigates the properties of hot-mixed asphalt (HMA) containing stone mastic asphalt (SMA), porous asphalt (PA) and dense-graded BOF as a partial substitution for natural aggregates. The purpose of this study is to evaluate various BOF slag contents in the asphalt mixtures would affect the cooling behavior after compaction. Asphalt mixture specimens contained 0%, 20%, 40% and 60% BOF slag, respectively, as coarse aggregate. Test results showed that BOF slag has a lipophilic property, so it can be adsorbed by asphalt cement, thereby reducing the cost of asphalt. The stability value of all asphalt mixtures increases with the proportion of BOF slag replacement. In addition, the voids in the mineral aggregate (VMA) value variable exhibited significant differences among asphalt mixtures, and could determine the deviation of the cooling trend of asphalt mixtures. Furthermore; it was found that the cooling procedure of the BOF slag used in dense-graded asphalt mixture takes about 100 min, and that the temperature tends to be moderate; however, it took about 120 min of cooling the SMA and PA mixture with BOF slag. In addition, the voids distribution of dense asphalt mixture was not uniform. It would result in various locations of thermal energy temperature on asphalt mixtures that were inconsistent.

Impure and pure casts have collected reasonable attentions over all the world. In this paper, Aluminum (Al) and Copper (Cu) cast alloys are considered to be studied. Multiple impure and pure Al-Cu cast alloys are established under the condition of very high temperatures. Then, all of the established alloys are examined by applying mechanical tests. More specifically, tests of hardness are exploited. Moreover, different quenching conditions are employed and analyzed. These are the water, air and oil. Consistent results are separately obtained for the impure and pure materials.

One method of creating a brass coating is through electrodeposition, which is most often completed in cyanide galvanic baths. Because of the toxicity of cyanides, many are working on the development of cyanide-free baths, which are promising but not satisfactory to replace the classic methods. The purpose of the study was to explore a new generation of non-aqueous cyanide-free baths based on 1-ethyl-3-methylimidazolium acetate ionic liquids. The study involved the formation of copper, zinc, and brass coatings. The influence of the bath composition, cathodic current density, and temperature was determined. The obtained coatings were characterized by their morphology, chemical composition, roughness, and corrosion resistance. It was found that the structure of the obtained coatings is strongly dependent on the process parameters. The three main structures observed were fine-grained, porous, and olive-like. To the best knowledge of the authors, it is the first time the olive-like structure was observed in the case of an electrodeposited coating. The Cu-Zn coatings consisted of 19–96 at.% copper and exhibited relatively strong corrosion resistance. High improvement of corrosion properties was found in the case of copper and brass coatings with an olive-like structure.

Smelting used to be less efficient in the past; therefore, wastes obtained from historical processing at smelter plants usually contain certain quantities of valuable metals. Upon the extraction of useful metal elements, metallurgical slag can be repurposed as an alternative mineral raw material in the building sector. A case study was conducted, which included an investigation of the physico-chemical, mineralogical, and microstructural properties of Pb-Zn slag found at the historic landfill near the Topilnica Veles smelter in North Macedonia. The slag was sampled using drill holes. The mineralogical and microstructural analysis revealed that the Pb-Zn slag is a very complex and inhomogeneous alternative raw material with utilizable levels of metals, specifically Pb (2.3 wt%), Zn (7.1 wt%), and Ag (27.5 ppm). Crystalline mineral phases wurtzite, sphalerite, galena, cerussite, akermanite, wüstite, monticellite, franklinite, and zincite were identified in the analyzed samples. The slag’s matrix consisted of alumino-silicates, amorphous silicates, and mixtures of spinel and silicates. Because the extraction of Pb, Zn, and Ag has economic potential, the first reutilization stage will be to convert metal concentrates into their collective concentrate, from which the maximum amount of these valuable elements may be taken out. This will include combination of gravity concentration and separation techniques. The next step is to assess the Pb-Zn slag’s potential applications in civil engineering based on its mineralogical and physico-mechanical properties. Alumino-silicates, amorphous silicates, and mixtures of spinel and silicates present in Pb-Zn slag, which contain high concentrations of SiO2, Al2O3, CaO, and Fe2O3, are suitable for use in cementitious building composites. The goal of this research is to suggest a solution for closing the circle of slag's reutilization in terms of Zero Waste principles, so it is critical to thoroughly investigate the material and establish methods and preparation processes, as well as ways of concentrating useful components into commercial products.

Smelting used to be less efficient in the past, so wastes obtained from historical processing at smelter plants usually contain certain quantities of valuable metals. A case study was conducted, which included an investigation of the physicochemical, mineralogical, and microstructural properties of raw material found at the historic slag pond near the Topilnica Veles smelter in North Macedonia. The Pb-Zn slag was sampled using traditional geophysical methods such as drill holes and pitholes. The mineralogical and microstructural analysis revealed that the Pb-Zn slag is a very complex and inhomogeneous alternative raw material with utilizable levels of metals, specifically Pb (2.24 wt%), Zn (7.10 wt%), and Ag (27.53 ppm). Amorphous phase, lead alloys, zinc alloys, wurtzite, sphalerite, galena, cerussite, elemental silver, elemental copper, elemental iron, magnetite, spinel, rutile, hematite, and troilite were also identified through qualitative mineralogical analysis. The glassy matrix composed of spinel, silicates, and mixed spinel-silicate is the most abundant constituent in slag composition. The various potential applications of the slag are possible based on its mineralogical and geochemical properties. Because the extraction of Pb, Zn, and Ag has certain economic potential, the next step, which will include gravity concentration and magnetic separation procedures, will be to form metal concentrates into their collective concentrate, from which the maximum amount of silver can be extracted. Slag's amorphous spinel, silicate, and mixed spinel-silicate phases, which contain high concentrations of SiO2, Al2O3, CaO, and Fe2O3, are suitable for use in building materials such as cement clinker, filler, or aggregate for concrete or mortar. The goal of this research is to close the circle of slag's reutilization potential in terms of Net Zero and Zero Waste principles, so it is critical to thoroughly investigate the material and establish methods and preparation processes, as well as ways of concentrating useful components into commercial products.

Most of the current methods for stabilizing electric arc furnace (EAF) slag are time-consuming and cannot be completely stabilized. In view of this, this study aimed to apply microbial‑induced calcium carbonate precipitation (MICP) technology in the stabilization of EAF reducing slag, and this was to be achieved by using the reaction between carbonate ions and free calcium oxide (f-CaO) in reducing slag to form a more stable calcium carbonate to achieve the purpose of stabilization. The test results showed that, when the EAF reducing slag aggregates (ERSAs) were immersed in Bacillus pasteurii bacteria solution or water, the f-CaO contained in it would react such that stabilization was achieved. The titration test results showed that the f-CaO content of the ERSAs immersed in the bacterial solution and water decreased. The expansion test results of the ERSAs that were subjected to hydration showed that the seven-day expansion of ERSAs after biomineralization could meet the Taiwan regulation requirement of a less than 0.5% expansion rate. The thermogravimetric analysis showed that both the experimental group and the control group might contain calcium carbonate compounds. The results of the X-ray diffraction analysis showed that the CaCO3 content in the ERSAs that were immersed in the bacterial solution was significantly higher than those that were immersed in water. Moreover, the compressive strength test results of concrete prepared with ERSAs showed that the compressive strength of the control group concrete began to decline after 28 days. In contrast, the experimental group concrete had a good stabilization effect, and there was no decline in compressive strength until the age of 180 days. At the age of 240 days, the surface cracks of the experimental group were particularly small, while the surface of the control group showed obvious cracks. These results confirmed that a mineralization reaction with B. pasteurii bacteria could be used as a stabilization technology for ERSAs.

Steel slag is a co-product of the steelmaking industry, this material is rarely used as a binder due to its low cementitious properties. Thus, it´s believed that the alkaline activation of steel slag can enable its use as a cementitious material. This work has the objective of making a systematic bibliographic review on the theme "slag melt as a precursor in activated alkali binders". To this end, the ProKnow-C method was used for the selection and analysis of relevant research on the topic. The portfolio resulted in 71 texts, mostly journals paper. Bibliometrics showed that the country with the most publications is China and the journal with the most publications is Construction and Building Materials. The critical analysis concluded that the XRD, XRF, and compressive strength tests are the most used for the characterization of the material. It is possible to establish that there are some knowledge gaps on the subject, such as better mechanical characterization and greater production of works with dosing by the one-part method.

Concrete consumption greatly exceeds the use of any other material in engineering. This is due to its good properties as construction material and the availability of its components. Nevertheless, the present worldwide construction increase and the high-energy consumption for cement production means a high environmental impact. On the other hand, one of the main problem in iron and steel industry is waste generation and by-products that must be properly processed or reused to promote the environmental sustainability. One of these by-products are blast furnace slag. Cement substitution by slag strategy achieves two goals, raw materials consumption reduction and waste management. In the present work, four different concrete mixtures are evaluated. 25% cement is substituted by different blast furnace slag. Tests are made to evaluate the advantages and drawbacks of each mixture. Depending on the origin, characteristics and treatment of the slag, concrete properties change. Certain mixtures provide proper concrete properties. Stainless steel slag produces a fluent mortar that reduces the water consumption whit a slight mechanical strength loss. Mixture with electric arc slag furnace properties are better to the reference concrete (without slag) when slag is treated similarly to the cement.

Phytopathogenic fungi are living organisms that cause plant diseases and great damage to agri-cultural products. Despite the wide range of commercial fungicide products in use, there is a clear need for new and environmentally friendly fungicides. Here we propose a new ecological fun-gicide, copper alginate microspheres prepared by ionic gelation. The microspheres were charac-terized (morphology and topography, encapsulation efficiency, load capacity, swelling behavior, rheology, kinetics and mechanism of copper ions release) and their in vitro antifungal potential against selected genera of phytopathogenic fungi was evaluated. Novel copper alginate micro-spheres inhibited spore germination of Botrytis cinerea and mycelial growth of Cercospora beticola and Phytophthora ramorum. They offer effective disease control while minimizing environmental impact and promoting sustainable agriculture practices.

The accumulation of microorganisms, plants, algae, or small animals on wet surfaces that have a mechanical function causes biofouling, which can result in structural or other functional deficiencies. The maritime shipping industry must constantly manage biofouling to optimize operational performance, which is a common and long-lasting problem. It can occur in any metal structure in contact or submerged in ocean water, which represents additional costs in terms of repairs and maintenance. This study is focused on the production of antifouling coatings, made with nanoparticles of copper selenide (CuSe) modified with gum arabic, within a water-base acrylic polymeric matrix. During the curing of the acrylic resin, the CuSe NPs remain embedded in the resin but this does not prevent the release of ions. The coatings presented to release copper and selenium ions for up to 80 days, selenium was the element that was released the most. The adhesion of film coatings to metallic substrates showed good adhesion, scale 5B (ASTM D3359 standard). Antimicrobial activity tests show that the coatings have an inhibitory effect on Escherichia coli and Candida albicans. The effect being more noticeable when the coating is detached from the substrate and placed on a growing medium, than compared to the coating on a substrate. Scanning electron microscopy (SEM) observations show that nanostructured CuSe coatings are made up of rod-shaped and spherical particles whose range ranges from 12 to 25 nm. The Energy Dispersive X-ray spectroscopy (EDS) studies showed that the ratio of selenium nanoparticles is greater than that of copper and that their distribution is homogeneous

Carrageenan (car-), used in the pharmaceutical as well as food industry, is marine sulfated polysaccharides. The carrageenan blends (CB) of kappa (κ-), iota (ι-), and lambda (λ-) of 50/50 weight by weight are multipurpose and biocompatible hydrophilic polymers. They were subjected to adsorption of copper (Cu2+) ions. The aim of the study was to conduct extensive rheological and mechanical studies rendering them suitable for biological purposes. The rheology was conducted at various temperatures using a frequency curve, frequency sweep, loss modulus, and storage modulus analysis. Models of rheology like Ostwald, Bingham, and Modified Bingham models were utilized. The rheological results demonstrated non-Newtonian/pseudo-plastic behavior at various temperatures. The models of rheology demonstrated good flow properties and rheological performance of these materials. These materials could be exploited for their application in pharmaceuticals, food, and cosmetics. Thus, our study reflects that these CB can be safely exploited in the healthcare, pharmaceutical, and food industry. However, further studies should be conducted to evaluate their effectiveness in clinical studies.

Surface Plasmon Resonance (SPR) is an attracting property of certain transition metals when they are synthesized in nano-range giving rise to promising optical applications. However, most SPR and associated applications are limited to the noble metal nanoparticles, which limits their potential due to high production cost. We report surface plasmon resonance in copper-copper oxide core-shell quantum dots synthesized via chemical route studied by using UV-Visible spectrophotometry. Tuning of the plasmonic resonance with respect to the particle diameter is achieved by an inexpensive all chemical route. Photoluminescence measurements also support the data. This size reduction leads to remarkable changes in its optical response as compared to the bulk metal. The results point towards applications of these materials in tunable SPR based biosensors.

In pursuit of carbon neutrality, the demand for metals that are necessary for the development of clean energy technologies is rapidly increasing. Metallurgical waste, such as slag, presents a promising secondary source of these key metals. This research aims to develop an eco-friendly hydrometallurgical process to recover Cu, Ni, and Co from discarded copper/nickel slag. The high-pressure acid leaching (HPAL) was used to selectively leach Ni, Cu, and Co from the fayalite slag, yielding high leaching efficiencies of 99.9%, 89.4%, and 99.9%, respectively, with low Fe and Si tenors to the pregnant leach solution (PLS). The solvent extraction (SX) technique utilizing LIX 984N was used to selectively extract and enrich copper from the dilute PLS to about 23 g/L Cu with a very low Fe concentration of 0.05 g/L. Potassium amyl xanthate (PAX) solution was used to form Ni and Co xanthate complexes from the raffinate solution. Nickel was selectively recovered using ammonia solution, while cobalt xanthate complex was thermally decomposed and recovered as cobalt oxide solids of about 25 wt.% Co. A comprehensive process flowsheet is presented, furthermore, to realize the real application of the developed slag cleaning process, a preliminary economic evaluation was performed.

There is a high iron content in the nickel slag that mainly exists in fayalite phase. Basic Oxide can destroy the stable structure of fayalite which is beneficial to the treatment and comprehensive utilization of nickel slag. The reseach was based on the composition of the raw nickel slag, taking CaO-SiO₂-FeO-MgO system as the object and CaO as a modifier. The effect of basicity on the melting characteristics, viscosity and structure of CaO-SiO₂-FeO-MgO system was studied. The relationship between the viscosity and structure of CaO-SiO₂-FeO-MgO system was also explored. The results show as follows. (1) When the basicity is 0.38~0.90, the phase of primary crystal is olivine at argon atmosphere, while it is monoxide at the basicity of 0.90~1.50. The liquidus temperature, softening temperature, hemispherical temperature, and flow temperature all reach the lowest value at the basicity of 0.90. (2) With the increase of basicity, critical viscosity temperature of CaO-SiO₂-FeO-MgO system decreases first and then increases. Critical viscosity temperature is the lowest at the basicity of 0.90, which is 1263 ℃. (3) When the slag system is heterogeneous, the viscosity of the molten slag increase rapidity because of the type and quantity of solid phase precipitated from CaO-SiO₂-FeO-MgO system. And critical viscosity temperature of the slag system is also significantly affected. (4) When the slag system is in a homogeneous liquid phase, the molar fraction of O0 decreases with the increase of basicity and the mole fraction of O^- and O^2- increases continuously at the basicity of 0.38~1.50. The silicate network structure is gradually depolymerized into simple monomers, resulting in the degree of polymerization is reduced and the viscosity is reduced, too.

Information taken from David A. Scott’s book “Copper and Bronze in Art” was crucial for research on copper corrosion products in Stuttgart. Examples discussed are the nature and variability of ‘Black Spots’ (aka ‘Brown Fuzzies’); cupric hydroxide by cleaning, patination, and pigment synthesis; the wondrous phenomenon of curly malachite; chalconatronite formed by contact to soda glass; the formation of copper formates by glass-induced metal corrosion; and synthesis and X-ray diffraction of basic copper acetates (‘verdigris’).

Hybrid metal-organic compounds as relatively new and prosperous magnetoelectric multiferroics provide opportunities to improve the polarization, magnetization and magneto-electric coupling at the same time, which usually have some limitations in the common type-I and type-II multiferroics. In this work we investigate the crystal of guanidinium copper(II) formate [C(NH2)3]Cu(HCOO)3 and give novel insights concerning the structure, magnetic, electric and magneto-electric behaviour of this interesting material. Detailed analysis of crystal structure at 100 K is given. Magnetization points to the copper(II)-formate spin-chain phase that becomes ordered below 4.6 K into the canted antiferromagnetic (AFM) state, as a result of super-exchange interaction over different formate bridges. The performed ab-initio colinear density functional theory (DFT) calculation confirm the AFM-like ground state as a first approximation and explain the coupling of spin-chains into the AFM ordered lattice. In versatile measurements of magnetization of a crystal, including transverse component besides the longitudinal one, very large anisotropy is found that might originate from canting of the coordination octahedra around copper(II) in cooperation with the canted AFM order. With cooling down in zero fields the generation of spontaneous polarization is observed step-wise below 270 K and 210 K and the effect of magnetic field on its value is observed also in the paramagnetic phase. Measured polarization is somewhat smaller than the DFT value in the c-direction, possibly due to twin domains present in the crystal. The considerable magneto-electric coupling below the magnetic transition temperature is measured with different orientations of the crystal in magnetic field, giving altogether the new light onto the magneto-electric effect in this material.

Benign design of alkali-activated slag/FA geopolymer paste has intriguing increasing attention for optimizing its service performance. Therefore, the replacement of fly ash (FA) with 10 wt% silica fume (SF) is investigated by mechanical strength after freeze-thawing cycles and microstructure characterization. The results show that an appropriate dosage (30 wt%) of slag is necessary to attain alkali-activated slag/FA geopolymer paste with excellent mechanical performance, and the SF/slag/FA (SF: slag: FA= 10:30:60, wt%) geopolymer paste exerts the compressive and flexural strength of 95.2 and 3.2 MPa, respectively. Meanwhile, the doped 10 wt% SF facilitates the propagation of (N, C)-A–S–H chains, rather than the formation of C-S-H gels, evidenced by the absent exothermic peak at about 861oC from the differential scanning calorimetry (DSC) curves, leading to the increases in the pores volume with a pore diameter<20 nm and tortuosity by mercury intrusion porosimeter (MIP) results, corresponding to an improved freezing-thawing resistance with the residual compressive strength of 52.8 MPa and the weight loss of 10.5% after 300 freeze-thawing cycles. It explores a cost-effective and benign facile approach to designing heating curing-free alkali-activated slag/FA geopolymer paste with good freezing-thawing resistance.

Understanding potential uptake and biodistribution of engineered nanoparticles in soil-grown plants is imperative for toxicity and risk assessment considering the oral exposure of edibles by humans. Herein, we assessed potential influence of particle size (25, 50, and 250 nm) and concentration (0, 50, 100, 200, and 500 mg/kg-soil) of Copper oxide nanoparticles (CuONPs) on: (1) the root system architecture, and the physicochemical attributes of soil at the soil-root interface, (2) leading to Cu transport and accumulation in root, stem, leaf and seed in soybean (Glycine max cv Kowsar) grown for entire lifecycle of 120 days, and compared with soluble Cu²⁺ ions and water-only controls, and (3) performed a comparative assessment of total seed Cu levels in soybean with other valuable food sources for Cu intake and discussed its human health implications. Our findings showed particle size- and concentration-dependent influence of CuONPs on Cu uptake and tissue distribution in root, stem, leaf and seed in soybean. Alterations in root architecture (root dry weight, root length, root volume, and root area) were dependent on the Cu compound type, Cu concentrations, and their interactions (p<0.05), except for root density. Concentration-response relationships for all three sized CuONPs, and Cu²⁺ ions, were linear. CuONPs and Cu²⁺ ions had inhibitory effects on root growth and development. Overall, soybean responses to smallest size CuONPs-25 nm were higher for all parameters investigated compared to two larger sized CuONPs (50 nm, 250 nm) or Cu²⁺ ions. Cu uptake/bioaccumulation differed among soybean tissues in the order: root > leaf > stem > seed. Despite reduced root architecture and seed yield, our smallest size CuONPs-25 nm led to increased total seed Cu uptake compared to the larger sized CuONPs and Cu²⁺ ions tested. Our findings also suggest that soil amendment by CuONPs, more so by the smallest size CuONPs-25 nm, could significantly improve nutritional Cu value in soybean seed as reflected by % Daily Values (DV), and are rated “Good” to “Very Good” according to the “World’s Healthiest Foods” rating. However, until the potential toxicity and risk from consumption of soybean seed is characterized in humans, caution should be exercised when the Cu fortified seeds are used for daily human consumption when addressing Cu deficiency and associated illnesses, globally.

A better understanding of high temperature processes in slags contributes to facilitate knowledge based design of the solidified product. Here, a slag analogue with a nominal composition of 17 wt% LiMnO2 and 83 wt% Ca2SiO4 was synthesized encountering fairly high cooling rates. The Mn species from 1223 K to 1773 K was simulated using a thermodynamic model assuming a homogeneous melt. The micro-composition including the Mn species of the solidified slag was determined experimentally and was used as basis for molecular dynamics (MD) simulation. The MD simulation provides information on structure and viscosity at high temperatures, otherwise difficult to access. These parameters significantly influence oxidation state of redox-active elements and the solidified product. The micro-composition analyzed by electron probe micro analysis (EPMA) and synchrotron based micro-X-ray fluorescence (micro-XRF) showed that Mn-rich and Ca-Si-rich phases are separated. While the Mn-O phases did not contain noticeable Ca, the Ca2SiO4 phase had incorporated 0.6 wt% of Mn. The slag solidified into round shaped and droplet shaped grains of a Li-Mn-oxide, some Mn3O4 and Ca2SiO4. The powder X-ray diffraction (PXRD) confirmed the formation of larnite, the identity of the Li-Mn-oxide however remained inconclusive. The Mn oxidation state (OS) was identified using synchrotron based micro-X-ray absorption near edge spectroscopy (micro-XANES). The Mn-O grains, matched well with Li-Mn-oxides and a Mn OS: +3 e.g. LiMn3+O2. Small areas matching Hausmannite (Mn2+Mn23+O4) were also identified. The OS of Mn in the silicate phase could not be identified. For comparison a slowly cooled slag analogue with similar composition however higher Si content, was also subjected to micro-XANES. The slowly cooled slag formed long Mn-rich needles in a matrix of large calcium silicate crystals. The Mn-rich crystals matched well with the XANES spectrum of a Mn3+ Li-oxide like LiMn3+O2. At the rim of the needles the Mn-spectra matched well the Hausmannite (Mn2+Mn23+O4) reference. In the silicate phases Mn had a OS: +2, unambiguously. The melt structure at different temperatures of two compositions i.e. LiMn3+O2 and Ca2SiO4 was simulated using molecular dynamics (MD). They serve as model compositions assuming a heterogeneous melt. The results show significant different degrees of polymerization and viscosity. Information from MD simulations can support the identification of potentially different oxygen permeability and with that prediction of oxidation states. The bulk composition was identified by inductively coupled plasma optical emission spectrometry (ICP-OES), bulk structure by PXRD and bulk species by lab-XANES. The synchrotron micro analysis including micro-XRD were performed at the microfocus beamline I18 at the Diamond Light Source. Pure reference compounds were prepared and characterized with the same multi-modal approach.

The production of municipal solid waste incineration bottom ash (MSWIBA) is very massive and has the potential to replace cement despite the problems of complex composition, uneven particle size distribution, and low reactivity. This paper adopts sodium silicate activation of MSWIBA-slag to improve the reactivity to prepare composite cementitious materials. It explores the hydration performance study of the composite cementitious materials by isothermal calorimetric analysis, Fourier Transform Infrared (FTIR) spectroscopy, XRD physical diffraction analysis, and SEM/EDS tests. SEM/EDS tests will be used to explore the hydration properties of the composite gelling. The results showed that with the increase of MSWIBA doping, the porosity between the materials increased, the degree of Hydration decreased, and the compressive strength decreased with the rise of MSWIBA. When sodium silicate increased from 25% to 35%, too much alkaline material occurred over the alkaline effect, which inhibited the Hydration of the particles, and the degree of hydration reaction decreased, and the compressive strength decreased accordingly; the exothermic process of Hydration can be mainly divided into five stages, quartz and calcite did not participate in the hydration reaction completely, and sexual aluminum participated in the hydration reaction. The vibrational peaks of Si-O-Ti (T = Si and Al) were present in the material. The vibrational peaks of XRD, FTIR, and SEM-EDS all indicate the presence of silica-aluminate network structures in the hydration products, mainly N-A-S-H and C-A-S-H gels.

This study aims to model grinding of a Polish slag and evaluate the particle size distributions of the products obtained after different grinding times. Then, selected products were alkali activated in order to investigate the effect of particle size on the compressive strength of the produced alkali activated materials (AAMs). Other parameters affecting alkali activation, i.e. temperature, curing and ageing time were also examined. Among the different mathematical models used to simulate the particle size distribution, Rosin-Rammler (RR) was found to be the most suitable. When piecewise regression analysis was applied to experimental data it was found that the particle size distribution of the slag products exhibits multi fractal character. In addition, grinding of slag exhibits non-first-order behavior and the reduction rate of each size is time dependent. The grinding rate and consequently the grinding efficiency increases when the particle size increases, but drops sharply near zero after prolonged grinding periods. Regarding alkali activation, it is deduced that among the parameters studied, particle size (and the respective specific surface area) of the raw slag product and curing temperature have the most noticeable impact on the compressive strength of the produced AAMs.

This study explores the stability of electrodeposited copper catalysts utilized in electrochemical CO2 reduction (ECR) across various amine media. The focus is on understanding the influence of different amine types, corrosion ramifications, and the efficacy of pulse ECR methodologies. Employing a suite of electrochemical techniques including potentiodynamic polarization, linear resistance polarization, cyclic voltammetry, and chronopotentiometry, the investigation reveals useful insights. The findings show that among the tested amines, CO2-rich monoethanolamine (MEA) exhibits the highest corrosion rate. However, in most cases the rates remain within tolerable limits for ECR operations. Primary amines, notably monoethanolamine (MEA), show enhanced compatibility with ECR processes, attributable to their resistance against carbonate salt precipitation and sustained stability in potential over extended durations. Conversely, tertiary amines such as methyldiethanolamine (MDEA) present challenges due to the formation of carbonate salts during ECR, impeding their effective utilization. The study highlights the effectiveness of pulse ECR strategies in stabilizing ECR. A noticeable shift in cathodic potential and reduced deposit formation on the catalyst surface through periodic oxidation underscores the efficacy of such strategies. These findings offer insights for optimizing ECR in amine media, thereby providing promising pathways for advancements in CO2 emission reduction technologies.

Predicting copper price is essential for making decisions that can affect companies and governments dependent on the copper mining industry. Copper prices follow a time series that is non-linear, non-stationary, and which have periods that change as a result of potential growth, cyclical fluctuation and errors. Sometimes the trend and cyclical components together are referred to as a trend-cycle. In order to make predictions, it is necessary to consider the different characteristics of trend-cycle. In this paper, we study a copper price prediction method using Support Vector Regression. This work explores the potential of the Support Vector Regression with external recurrences to make predictions at 5, 10, 15, 20 and 30 days into the future in the copper closing price at the London Metal Exchanges. The best model for each forecast interval is performed using a grid search and balanced cross-validation. In experiments on real data-sets, our results obtained indicate that the parameters (C, ε, γ) of the model Support Vector Regression do not differ between the different prediction intervals. Additionally, the amount of preceding values used to make the estimates does not vary according to the predicted interval. Results show that the support vector regression model has a lower prediction error and is more robust. Our results show that the presented model is able to predict copper price volatilities near reality, being the RMSE equal or less than the 2.2% for prediction periods of 5 and 10 days.

: Dacarbazine, DAC, 5-(3,3-dimethyltriazeno)imidazol-4-carboxamideis is an imidazole-carboxamide derivative, that is structurally related to purines. DAC belongs to the triazene compounds, which are a group of alkylating agents with antitumour and mutagenic properties. DAC is a non-cell cycle specific drug, active on all phases of cellular cycle. In the frame of this work the 3d-metal complexes (cobalt and copper) with dacarbazine were synthesized. Their spectroscopic properties by the use of FT-IR, FT-Raman and 1HNMR were studied. The structures of dacarbazine and its complexes with copper(II) and cobalt(II) were calculated using DFT methods. The effect of metals on the electronic charge distribution of dacarbazine was discussed on the basis of calculated NBO atomic charges. The reactivity of metal complexes in relation to ligand alone was estimated on the basis of calculated energy of HOMO and LUMO orbitals. The aromaticity of imidazole ring in dacarbazine and the complexes was compared (on the basis of calculated geometric indices of aromaticity). Thermal stability of the investigated 3d-metal complexes with dacarbazine and the products of their thermal decomposition were analyzed.

Conobea scoparioides (Plantaginaceae) is an herbaceous plant known as "pataqueira" that grows wild in seasonally wet areas of the Amazon region. It is used for aromatic baths and anti-protozoan remedies by the Brazilian Amazon native people. The main volatile compounds identified in the essential oil of "Pataqueira" were the phenolic monoterpenes thymol and thymol methyl ether and their precursors, the monoterpene hydrocarbons α-phellandrene and p-cymene. A hydrotalcite synthesized from blast-furnace slag exhibited a 3:2 (Mg/Al) molar ratio, and this layered double hydroxide (LDH) was evaluated as a catalyst in converting the main monoterpenes of the "Pataqueira" oil. This action significantly increased thymol content, from 41% to 95%, associated with the percentual reduction of other main components, such as thymol methyl ether, α-phellandrene, and p-cymene. The LDH reaction showed a strong tendency towards producing hydroxylated derivatives, and its behavior was similar to the hypothetical plant biosynthetic pathway, which leads to the production of the monoterpenes of "Pataqueira" oil. Thymol and its derivatives are potent antiseptics applied in pharmaceutical and hygienic products as antibacterial, antifungal, and antioxidant properties, among others. The present work reports a natural source with a high thymol content in aromatic plants from the Amazon, with evident economic value.

Three-phase interactions (metal-slag-argon) in ladle stirring operations have strong effects on metal-slag mass transfer processes. Specifically, the thickness of the slag controls the fluid turbulence to an extent that once trespassing a critical thickness, increases of stirring strength have not further effects on the flow. To analyze these conditions, a physical model considering the three phases was built to study liquid turbulence in the proximities of the metal-slag interface. A velocity probe placed close to the interface permitted the continuous monitoring and statistical analyses of turbulence. The slag-eye opening was found to be strongly dependent on the stirring conditions, and the mixing times decreased with thin slag thicknesses. Slag entrainment was enhanced with thick slag layers, and high flow rates of the gas phase. A multiphase model was developed to simulate these results finding a good agreement between experimental and numerical results.

Recently many researches of EOS (Electric Arc Furnace Oxidizing Slag) on application to construction industry have been carried out with increasing its production and limited reclamation site. EOS can be used as a fine aggregate for construction material, however, its engineering properties vary with the manufacturing process and producing district, causing a quality differences in material performance. In the work, EOS is obtained from steel manufacturing plants in South Korea and the engineering properties are evaluated for EOS and the cement mortar with EOS, respectively. From the tests, EOS is mainly made up of CaO, SiO₂, and FeO with 18.2% of larnite which has a crystal structure of β-C₂S with similar cement mineral. EOS mortar shows an increasing compressive strength with more EOS content, which is affected by a considerable amount of larnite (β-C2S) in EOS. The EOS based mortar with ERS (Electric Arc Furnace Reduction Slag) shows unsatisfactory results over the criteria for rate of change, which implies that more consideration must be taken for the usage of the mixed ERS and EOS for cement mortar due to swelling effect of ERS on dimensional stability.

The 70/30 copper–nickel alloy is mainly used in critical parts with more demanding conditions in marine settings. There is a need for innovative methods that offer fast production and cost-effectiveness to supplement current copper–nickel alloy manufacturing processes. In this study, we employ wire-arc additive manufacturing (WAAM) to fabricate the 70/30 copper–nickel alloy. The as-built microstructure is characterized by columnar grains with prominent dendrites and chemical segregation in the inter-dendritic area. The aspect ratio of the columnar grain increases with increasing travel speed (TS) at the same wire feed speed (WFS). This is in contrast to an equiaxed grain structure with a more random orientation of conventional sample. The sample built with a WFS of 8 m/min, TS of 1000 mm/min, and a track distance of 3.85 mm exhibits superior corrosion properties in the 3.5 wt% NaCl solution compared to the conventional one, as evidenced by a higher film resistance and breakdown potential, along with a lower passive current density of the WAAM sample. The corrosion morphology reveals the critical roles played by the nickel element unevenly distributed between the dendrite core and inter-dendritic area.

Classical antibacterial drugs were designed to target specific bacterial properties distinct from host human cells to maximize potency and selectivity. These designs were quite effective as they could be easily derivatized to bear next generation drugs. However, the rapid mutation of bacteria and their associated acquired drug resistance have led to the rise of highly pathogenic superbug bacterial strains for which treatment with first line drugs is no match. More than ever, there is a dire need for antibacterial drug design that goes beyond conventional standards. Taking inspiration by the body’s innate immune response to employ its own supply of labile copper ions in a toxic attack against pathogenic bacteria, which have a very low Cu tolerance, this review article examines the feasibility of Cu-centric strategies for antibacterial preventative and therapeutic applications. Promising results are shown for the use of Cu-containing materials in the hospital setting to minimize patient bacterial infections. Studies directed at disrupting bacterial Cu regulatory pathways elucidate new drug targets that can enable toxic increase of Cu levels and perturb bacterial dependence on iron. Likewise, Cu intracellular chelation/prochelation strategies effectively induce bacterial Cu toxicity. Cu-based small molecules and nanoparticles demonstrate the importance of the Cu ions in their mechanism and display potential synergism with classical drugs.

The copper deposition on the platinum and palladium nanoelectrode has been studied using cyclic voltammetry. The use of nanoelectrode platinum and palladium are defined in the study of heavy metals. The noble nanoelectrode of metal has a typical silicone processing structure. In comparison to the nanoelectrodes, the geometry of the electrode series is complex and balanced. Nanoelectrodes of platinum are found effective in detecting heavy metal. There was regular analysis of the use of the sensors. The identification constraints down to the ng /L level was accomplished by refined electrode geometry and the stripping procedures. The process was used for the study of water sample determination. Another heavy metal ion attack voltammetric reaction was studied. The SEM picture clearly observed and characterized the nanoparticle electrode by X-ray diffraction and cyclic voltammetry.

Geopolymer, as a new type of solid waste-based inorganic cementitious material, exhibits outstanding Behavior in terms of physical and chemical performance, macro-mechanical properties and long-lasting stability, and features potential application development tendency in the field of repair and reinforcement of existing concrete structures. This paper investigates the interfacial Behavior of geopolymer mortar with OPC concrete substrate under different slag, fly ash and red mud mixing proportions, while cement mortar was used as a control group for the research. The interfacial bonding properties of the geopolymer mortar to the OPC concrete substrate were elaborated by carrying out split tensile test, two-sided shear test and three-point bending test. The scanning electron microscopy (SEM) and X-ray diffraction (XRD) were employed to further analyse the microstructural characteristics and physical phase components of the interfacial transition zone between the geopolymer mortar and the OPC concrete substrate. The results indicated that the compressive strength of slag-fly ash-red mud-based geopolymer mortar under different mixing ratio conditions was consistently superior to that of cement mortar. Overall, the interfacial bonding properties of the geopolymer mortar to the OPC concrete substrate gradually increased with the increment of the slag content, however, an evolutionary trend of minor enhancement followed by a gradual reduction was observed with the growth of the fly ash and red mud content.

CO2 emissions resulting from the production of cement is a major issue, but can be limited by the partial substitution of cement by low-carbon-impact additions. The aim of this study was the formulation of a ternary binder based on ordinary Portland cement (OPC), ground granulated blast-furnace slag (GGBS) and flash-calcined sediment (FCS), a dredged waste which was valorized after applying a new heat treatment: flash calcination. The used materials were physically, chemically and mineralogically characterized. The composition of the formulations was optimized using mixture designs. Five formulations, one reference formulation RM (100% OPC), one binary formulation (50% OPC/50% GGBS), and three ternary formulations with a variable FCS rate (10%, 15%, 20%), were selected and characterized fresh and hardened. Results showed that the incorporation of FCS reduced the workability and increased the density. In addition, a decrease in the initial setting time and the heat of hydration peak were observed. In the hardened state, the formulation containing 10% FCS showed 90-day mechanical strengths superior to that of RM. The use of FCS in ternary binders could reduce the environmental impact by reducing greenhouse gas emissions.

The objective of this work was to evaluate the removal of phosphorus and carbon dioxide capture of a conventional septic system upgraded with a sidestream steel slag filter used in recirculation mode. A pilot scale sidestream experiment was conducted with two septic tank and drainfield systems, one with and one without a sidestream slag filter. The experimental system was fed with real domestic wastewater. Recirculation ratios of 25%, 50% and 75% were tested. Limestone soils and silica soils were used as drainfield media. The phosphorus removal efficiency observed in the second compartment of the septic tank was 30% in the slag filter upgraded system, compared to -3% in the control system. The drainfield of silica soils achieved very high phosphorus removal in both control and upgraded systems. In the drainfield of limestone soil, the slag filtration reduced the groundwater phosphorus contamination load by up to 75%. Phosphorus removal in the septic tank with a slag filter was attributed to either sorption on newly precipitated calcium carbonate or precipitation of vivianite, or both. Recirculation ratio design criteria were proposed based on simulations. Simulations showed that the steel slag filter partly inhibited biological production of carbon dioxide in the septic tank. The influent alkalinity strongly influenced the recirculation ratio needed to raise the pH in the septic tank. The control septic tank produced carbon dioxide, whereas the slag filter upgraded septic tank was a carbon dioxide sink.

A full potential all-electron density functional method within generalized gradient approximation is used to investigate the electronic, elastic and transport properties of cubic copper sulphide and copper selenide. The electronic structure suggests metallic behavior with a zero energy band gap for both materials. Elastic property calculations suggest a stiff material with the bulk to shear modulus ratio of 0.35 and 0.44 for Cu2S and Cu2Se respectively. The transport properties were estimated using the Boltzmann transport approach. Seebeck coefficient, electrical conductivity, thermal conductivity, and power factor all suggest a potential p-type conductivity for Cu2S and n-type conductivity for Cu2Se.

Our investigations show that electrochemical corrosion of copper is faster than electrochemical corrosion of aluminium at temperatures below 100oC. Literature data analysis shows that the Al atoms diffuse faster than the Cu atoms at temperatures higher than 475oC, Al rich intermetallic compounds (IMCs) are formed faster in the Cu-Al system, and the Kirkendall plane shifts toward Al side. Electrochemical corrosion occurs due to electric current and due to diffusion. An electronic devise working time, for example, depends on initial copper cover thickness on aluminium wire, connected to the electronic devise, temperature, and volume and dislocation pipe diffusion coefficients, so copper, iron, and aluminium electrochemical corrosion rates are investigated experimentally at room temperature and at temperature 100oC. Intrinsic diffusivities ratios of copper and aluminium at different temperatures and diffusion activation energies in the Cu-Al system are calculated by proposed here methods using literature experimental data. Dislocation pipe and volume diffusion activation energies of pure iron are calculated separately by earlier proposed method using literature experimental data. Aluminium dissolved into NaCl solution as the Al3+ ions at room temperature and at temperature 100oC, iron dissolved into NaCl solution as the Fe2+ (not Fe3+) ions at room temperature and at temperature 100oC, copper dissolved into NaCl solution as the Cu+ ions at room temperature and as the Cu+ and the Cu2+ ions at temperature 100oC. It is founded experimentally that copper corrosion is higher than aluminium corrosion, and ratio of electrochemical corrosion rates, kCu/kAl>1, decreases with temperature increasing, although iron electrochemical corrosion rate doesn’t depend on temperature below 100oC. It is obvious, because melting point of iron is more higher then melting point of copper or aluminium. It is calculated that copper electrochemical corrosion rate is approximately equal to aluminium electrochemical corrosion at temperature about 300oC, so copper can dissolve into NaCl solution mostly as the Cu2+ ions at temperature about 300oC. Ratio of intrinsic diffusivities, DCu/DAl <1, increases with temperature increasing, and intrinsic diffusivity of aluminium could be approximately equal to intrinsic diffusivity of copper at temperature about 460oC.

Copper-based nanomaterials in the last decade attracted many researchers due to their extensive practical applications, unique, inexpensiveness, and wide availability. In addition to this, copper-based nanomaterials possess good thermal stability, and selectivity and also possess high activity. This review emphasis on the recent advances in the synthesis of copper nanomaterials and their wide applications in the field of environmental catalysis. This review aims to fill a significant knowledge gap in the different areas of environmental pollution management. Also, the paper concentrates on the recent applications of copper-based nanomaterials for environmental remediation, including the removal of heavy metals, and degradation of organic pollutants such as pharmaceuticals, and other environmental contaminants. Also, it will be helpful to young researchers in improving the suitability of implementing the Copper nanomaterials in the right way establishing and achieving sustainable goals for environmental remediation.

Mining is one of the main economic activities of several developing countries as Chile. Due to the progressive fall of the ore grades and the increasingly refractory composition of minerals, concentrating plants have increased that has led to an increase in the generation of tailings. Tailings, especially those obtained in the past, have remaining copper and other valuable species in quantities that can potentially be recovered, such as gold, silver, vanadium and rare earth elements. This transforms this abundant waste into a potential source of precious or strategic metals for secondary mining. One of the techniques of solid-liquid separation that allows the processing of solutions with low concentrations of metals corresponds to the adsorption, and more recently the biosorption, which is based on the use of biological matrices that do not constitute an environmental liability after application. Biosorption occurs as a consequence of the wide variety of active functional groups present in the different types of biomass. Bacterial, fungal, plant and algal biomasses have been described as biosorbents, mainly for the treatment of diluted and simple solutions. This work aims to recover copper from leached tailings using biomass of the red algae Gracilaria chilensis as a biosorbent. The tailing samples were taken from an abandoned deposit in the north of Chile and after an acid leaching copper was biosorbed, for which the kinetics of adsorption and the equilibrium isotherms were studied, applying the Freundlich and Langmuir models. Operational parameters such as adsorbent dose, pH and initial metal concentration were studied.

Copper demand for a country's copper industry has a greater pull effect. China's copper consumption in 2015 has accounted for 50% of the world. The scientific forecast of China's copper demands trend is also an important basis for analyzing its future environmental impact. This paper assumes that China's economy will be developing high, medium and low scenarios, and forecasts economic and social indicators such as total GDP, population and per capita GDP in China from 2016 to 2030. Then, predicted the demand of copper resources in China from 2016 to 2030 by the combination of system dynamics model, vector autoregressive moving average model and inverted U-type empirical model. The results show that: (1) in 2020, 2025 and 2030, China's refined copper demand will be 13 Mt, 15 Mt and 15.5 Mt. (2) China's copper demand growth slowed down significantly from 2016-2030. (3) 2025-2030, China's copper resource demand is stable, into the platform of demand growth, the highest peak value in 2027 will be 15.5 Mt. (4) 2030 years later, China's copper resource demand will enter a slow decline.

Cement production requires a significant amount of energy and natural resources, severely impacting the environment due to harmful gas emissions. Coal Bottom Ash (CBA) and Coal Boiler Slag (CBS), byproducts of coal-fired power plants, have pozzolanic properties. CBA and CBS can be mechanically ground to obtain Ground Coal Bottom Ash (GCBA) or Ground Coal Bottom Slag (GCBS), which can potentially replace cement in concrete, reducing waste in landfills, benefit the economy, preserving natural resources, and reducing health hazards. This study was performed to determine the optimum amount of GCBA and GCBS that can replace cement in concrete. The fresh, mechanical, and durability properties of the concrete containing GCBA were compared to a control mix consisting of 100% Portland cement. The optimum amount of cement replaced with GCBA and GCBS was 10% and 5%, respectively, based on compressive strength. The GCBA-based concrete's tensile strength, modulus of elasticity, and durability properties were better than the control. The compressive strength of the GCBA and GCBS-based mortars increased with an increase in fineness. GCBA and GCBS fineness should be within the limit recommended in the ASTM C618 standard to enhance concrete or mortar properties.

Geopolymer concrete (GPC) represents an innovative green and low-carbon construction material, offering a viable alternative to ordinary Portland cement concrete in building applications. However, existing studies tend to overlook the recyclability aspect of GPC for future use. Various structural applications necessitate the use of concrete with distinct strength characteristics. The recyclability of the parent concrete is influenced by these varying strengths. This study examined the recycling potential of GPC across a spectrum of strength grades (40, 60, 80 and 100 MPa, marked as C40, C60, C80 and C100) when subjected to freeze-thaw conditions. The cementitious material comprised 60% metakaolin and 40% slag, with natural gravel serving as the coarse aggregate, and the alkali activator consisting of sodium hydroxide solution and sodium silicate solution. The strength of the GPC was modulated by altering the Na/Al ratio. After 350 freeze-thaw cycles, the GPC specimens underwent crushing, washing, and sieving to produce recycled geopolymer aggregates (RGAs). Subsequently, their physical properties and microstructure were thoroughly examined. The findings indicated that GPC with strength grades of C100, C80, and C60 were capable of enduring 350 freeze-thaw cycles, in contrast to C40, which did not withstand these conditions. RGAs derived from GPC of strength grades C100 and C80 complied with the criteria for Class II recycled aggregates, whereas RGAs produced from GPC of strength grade C60 aligned with the Class III level. A higher strength grade in the parent concrete correlated with enhanced performance characteristics in the resulting recycled aggregates.

With the growing demand for personal protective equipment (PPE) in the face of the pandemic events caused by SARS-COV-2, the opportunity arises for the development of materials with characteristics such as antimicrobial, antiviral, antifungal activity, etc. The use of polymeric nanocomposites based on polyester/copper offers an alternative of great interest due to the versatility of the raw material and the high efficiency of copper as an antimicrobial additive. In this study, textile fibers prototypes with different Cu nanoparticles (CuNP) content were produced using melt-spinning to obtain bi-component multifilament fibers, and melt-blowing to obtain non-woven fabrics. The prototypes were tested against different pathogenic microorganisms such as S. aureus, E. coli, and C. albicans. It was shown that bi-component fibers offer more excellent protection against pathogens, while non-woven fabric only shows activity against E. coli. It was possible to identify that the CuNP were confined exclusively in the outer cover of the bi-component fibers, using different analytical techniques, which may be associated with the increase in antimicrobial activity, compared to the fibers present in the non-woven fabric, even when they present the same CuNP content.

Bioglasses are highly adoptable bone substitute materials, which can be combined with so-called therapeutic ions. These ions have shown to influence underlying molecular processes of the bone regeneration cascade. Moreover, it is known that bone substitutes induce an immune reaction within their implantation area involving macrophages and their pro- and anti-inflammatory subtypes dependent on their chemical composition. However, only poor knowledge exists regarding the influence of therapeutic ions onto the immune reactions and the associated bone healing. Thus, the aim of this work was to investigate the influence of strontium- and copper-doped bioglasses on the induction of M1- and M2-macrophages as well as the implant bed vascularization. (2) Methods: For this study, two alkali glasses were produced on basis of ICIE-16 bioglass via the melt-quench route with the addition of 5 wt% copper or strontium (ICIE16-Cu and ICIE16-Sr). Pure ICIE16 and 45S5 bioglasses were used as control materials. The bioactivity (ion release), chemical composition and the surface pattern were investigated, as well as an in vivo experiment was performed using the subcutaneous implantation model in rats. (3) Results: SEM imaging showed different formations of hydroxyapatite on the surfaces of the bioglass systems after submersion in simulated body fluid. EDX analysis confirmed the doping process by showing the release kinetics. Copper-doped bioglass exhibited a higher ion release than strontium-doped bioglass. Copper induced both a low immune cell migration and triggered a low number of M1- and M2-macrophages but also of blood vessels. The strontium-containing bioactive glass induced higher numbers of M1-macrophages after 30 days. Both copper- and strontium-doped bioglasses induced comparable numbers of M2-macrophages as found in the control groups. (4) Conclusions: Bioglass doping with copper and strontium did not exhibit significant influence on the foreign body response or the implantation bed vascularization in vivo. However, the prepared bioglass systems seemed to be biocompatible.

Measurements of copper and zinc in transfusion-dependent thalassemia (TDT) show contradictory results.Aim of the study: To examine serum levels of these minerals in TDT in relation to iron overload indices and erythron variables. Methods: This study recruited 60 children with TDT and 30 healthy children aged 3-12 years old.Results: Zinc was significantly higher in TDT children than in control children, whilst copper and the copper to zinc ratio were significantly lowered in TDT. Serum zinc was significantly associated with the number of blood transfusions and iron overload variables (including serum iron and TS%) and negatively with erythron variables (including hemoglobin, mean corpuscular volume, mean corpuscular hemoglobin). Serum copper was significantly and negatively associated with the same iron overload and erythron variables. The copper to zinc ratio was significantly correlated with iron, TS%, ferritin, hemoglobin, mean corpuscular volume, and mean corpuscular hemoglobin. Albumin levels were significantly higher in TDT children than in control children. Conclusion: Our results suggest that the increase in zinc in children with TDT may be explained by iron loading anemia and hemolysis and the consequent shedding of high amounts of intracellular zinc into the plasma. Increased albumin levels and treatment with Desferral may further contribute towards higher zinc levels in TDT. We suggest that the elevations in zinc in TDT are a compensatory mechanism protecting against infection, inflammation, and oxidative stress. Previous proposals for prophylactic use of zinc supplements in TDT may not be warranted.

There is an increasing interest in applying environmentally-friendly materials in wood protection technology. This include the use of less toxic active ingredients, as well as better fixation. This study investigates the formulation based on the combination of copper and Saqez resin on the physical and biological resistance properties of poplar wood. Samples were treated by either copper-ethanolamine (Cu/MEA) and/or Saqez resin at various treatment levels. A vacuum pressure procedure was applied. The retention, weight percent gain, water absorption, volumetric swelling, and decay resistance of the samples were then determined. The highest retention and weight percent gain were obtained at the samples treated with the combination of copper-based system and Saqez resin. Additionally, the combination of the copper and Saqez improved the physical properties and decay-resistance against white-rot fungus Trametes versicolor.

Behavior of supported alloyed and de-alloyed platinum-copper catalysts, which contained 14% - 27% wt. of Pt, was studied in the reactions of methanol electrooxidation (MOR) and oxygen electroreduction (ORR) in 0.1 M HClO4 solutions. Alloyed PtCux/C catalysts were prepared by a multistage sequential deposition of copper and platinum onto a Vulcan XC72 dispersed carbon support. De-alloyed PtCux-y/C catalysts were prepared by PtCux/C materials pretreatment in acid solutions. The effects of the catalysts initial composition and the acid treatment condition on their composition, structure, and catalytic activity in MOR and ORR were studied. Functional characteristics of platinum-copper catalysts were compared with those of commercial Pt/C catalysts when tested, both in an electrochemical cell and in H2/Air membrane-electrode assembly (MEA). It was shown that the acid pretreatment of platinum-copper catalysts practically does not have negative effect on their catalytic activity, but it reduces the amount of copper passing into the solution during the subsequent electrochemical study. The activity of platinum-copper catalysts in the MOR and the current-voltage characteristics of the H2/Air PEMFC MEAs measured in the process of their life tests were much higher than those of the Pt/C catalysts.

Hepcidin-25 was identified as the main iron regulator in the human body by binding to the sole iron-exporter ferroportin. Studies showed that the N-terminus of hepcidin is responsible for this interaction, the same N-terminus that encompasses a small copper(II)-binding site known as ATCUN (amino terminal Cu(II)- and Ni(II)- binding) motif. Interestingly, this copper-binding property is largely ignored in most papers dealing with hepcidin-25. In this context, detailed investigations of the formed complex of hepcidin-25 with copper could reveal insights into its biological role. The present work is mainly focused on the study of the metal-bound form of hepcidin-25, which could be considered the biologically active form. The first part is devoted to the reversed-phase chromatographic separation of copper-bound and copper-free hepcidin-25, which was achieved by applying basic mobile phases containing 0.1% ammonia. Further, mass spectrometry (tandem mass spectrometry MS/MS, high resolution mass spectrometry HRMS) and nuclear magnetic resonance (NMR) spectroscopy were employed to characterize the copper-peptide. Lastly, a 3D model of hepcidin-25 with bound copper(II) is presented. The identification of metal complexes and potential isoforms and isomers, from which the latter usually are left undetected by mass spectrometry, led to the conclusion that complementary analytical methods are needed to characterize a peptide calibrant or reference material comprehensively. Quantitative nuclear magnetic resonance (qNMR), inductively-coupled plasma mass spectrometry (ICP-MS), ion-mobility spectrometry (IMS) and chiral amino acid analysis (AAA) should be considered among others.

Due to its built-up chemoresistance after prolonged usage, the demand for replacing platinum in metal-based drugs (MBD) is rising. The first MBD approved by the FDA for cancer therapy was cisplatin in 1978. Even after nearly four and a half decades of trials, there has been no significant improvement in osteosarcoma (OS) therapy. In fact, many MBD have been developed, but the chemoresistance problem raised by platinum remains unresolved. This motivates us to elucidate the possibilities of the copper and zinc (CuZn) combination to replace platinum in MBD. Thus, the anti-chemoresistance properties of CuZn and their physiological functions for OS therapy are highlighted. Herein, we summarise their chelators, main organic solvents, and ligand functions in their structures that are involved in anti-chemoresistance properties. Through this review, it is rational to discuss their ligands’ roles as biosensors in drug delivery systems. Hereafter, an in-depth understanding of their redox and photoactive function relationships is provided. The disadvantage is that the other functions of biosensors cannot be elaborated on here. As a result, this review is being developed, which is expected to intensify OS drugs with higher cure rates. Nonetheless, this advancement intends to solve the major chemoresistance obstacle towards clinical efficacy.

The fireproof design of geopolymer has intriguing increasing attention by adjusting multi-component metallurgical solid wastes, due to its low-carbon emission, cost-effectiveness, and environmental conservation. Herein, the effects of silica fume (SF) on the microstructure and mechanical properties of alkali-activated slag/FA (fly ash) pastes subjected to elevated temperatures (150, 500, 850, and 1200℃) are investigated, to clarify the fact that whether or not the SF generates positive roles in mechanical strength of slag/FA (slag: FA=30:70, wt.%) geopolymers during building fires. The results show that the replacement of FA with 10 wt% SF (silica fume) promotes the increasing pore volume with a diameter of 0.2~3 μm, leading to an increase in the compressive or flexural strength below 850℃, “right shifts” of the endothermic peak, appearing uniform and compact fracture surfaces. Meanwhile, the gehlenite and labradorite generate after exposure above 850℃. While the bloating effect of the SF-containing sample occurs at 1200℃, leading to a greater deformation, due to the further restructuring of the amorphous geopolymer chain N-A-S-H or N-(Ca)-A-S-H composed from the [SiO4]4− and [AlO4]5−. It explores an effective approach for improving geopolymer’s fireproof performance by adjusting the solid-waste formulation.

Recycling of metallurgical solid waste has intriguing increasing attention for fabricating cementitious materials, due to its low-carbon emission, cost-effectiveness, and environmental conservation. Herein, the effects of silica fume (SF) on the microstructure and mechanical properties of alkali-activated slag/FA (fly ash) pastes subjected to elevated temperatures (150, 500, 850, and 1200℃) are investigated, to clarify the fact that whether or not the SF generates positive roles in mechanical properties of slag/FA geopolymers. The results show that the replacement with 10 wt% SF (silica fume) promotes the increasing pore volume with a diameter of 0.2~3 μm at room temperature, leading to an increase in the compressive or flexural strength, “right shifts” of endothermic peak and the initial-final temperature of mass loss, presenting a denser and compact fracture surface. Meanwhile, the mineral phase of gehlenite and labradorite emerges after exposure above 850℃ from the XRD results. Furthermore, the bloating effect of the incorporated SF occurs due to the formation of a liquid phase altogether with the amorphous silicates after exposure to 1200℃, leading to a greater deformation and enhancement of restructuring involved in the [SiO4]4− and [AlO4]5−. It explores an effective recycling approach for fabricating paste binders using metallurgical solid wastes.

In the study, ground granulated blast furnace slag was activated with a wide variety of sodium salts to compare the effect of their pH and anion size on the hydration progress and compressive strength development of GGBFS pastes. Research was carried out on samples activated with twelve different sodium salts, cured for one year. Changes in their phase composition (XRD), loss on ignition at different temperatures, expansion and microstructure (SEM+EDS) were examined over the entire curing period. Studies have shown that the presence of sodium ions is more important than the pH of the system, as activation took place even in the case of compounds whose solutions are characterized by low pH, such as sodium tartrate or phosphate. The compressive strength of the pastes ranged from approximately 8 to 65 MPa after one year of curing.

The trace element copper (Cu) is part of our nutrition and essentially needed for several cuproenzymes that control redox status and support the immune system. In blood, the ferroxidase ceruloplasmin (CP) accounts for the majority of circulating Cu and serves as transport protein. Both Cu and CP behave as positive, whereas serum selenium (Se) and its transporter selenoprotein P (SELENOP) behave as negative acute phase reactants. In view that coronavirus disease (COVID-19) causes systemic inflammation, we hypothesized that biomarkers of Cu and Se status are regulated inversely, in relation to disease severity and mortality risk. Serum samples from COVID-19 patients were analysed for Cu by total reflection X-ray fluorescence and CP was quantified by a validated sandwich ELISA. The two Cu biomarkers correlated positively in serum from patients with COVID-19 (R=0.42, p&lt;0.001). Surviving patients showed higher mean serum Cu and CP concentrations in comparison to non-survivors ([mean+/-SEM], Cu; 1475.9+/-22.7 vs. 1317.9+/-43.9 µg/L; p&lt;0.001, CP; 547.2.5 +/- 19.5 vs. 438.8+/-32.9 mg/L, p=0.086). In contrast to expectations, total serum Cu and Se concentrations displayed a positive linear correlation in the patient samples analysed (R=0.23, p=0.003). Serum CP and SELENOP levels were not interrelated. Applying receiver operating characteristics (ROC) curve analysis, the combination of Cu and SELENOP with age outperformed other combinations of parameters for predicting risk of death, yielding an AUC of 95.0%. We conclude that the alterations in serum biomarkers of Cu and Se status in COVID-19 are not compatible with a simple acute phase response, and that serum Cu and SELENOP levels contribute to a good prediction of survival. Adjuvant supplementation in patients with diagnostically proven deficits in Cu or Se may positively influence disease course, as both increase in survivors and are of crucial importance for the immune response and antioxidative defence systems.

Friction stir alloying (FSA) of commercially pure Cu with Ni, Zn, and Mg is implemented in the current study. The successfully fabricated alloy structure has been scrutinized in terms of mechanical and micro-structural standpoints. Energy-dispersive X-ray spectroscopy revealed a uniform distribution of alloying elements and coalescence at the atomic level. The compositional and grain size heterogeneity is managed in the stir zone, which pave way for microstructural control using FSA. Thus, the present study carries significance for the development of novel materials whose fabrication requires temperature far below the melting point of base metals. Ultra-refinement of grains is found to accompany the alloying process, with ~ 440 nm being the smallest grain size. Maximum and average micro-hardness enhancement of 18.4 % and 6 % is observed for the fabricated alloy. Tensile properties have also been investigated and co-related with the micro-structural morphology. The shift towards grain bimodality has also been reported, which is a highly sought property in the present day, especially to overcome the strength-ductility trade-off.

CuAl8Fe5Ni4Zn4Sn1 (OF 2238) is a new lead-free copper alloy for plain bearing applications that was first officially presented in a scientific journal in 2020. Soon after its invention, the use of the alloy for connecting rod bushings in heavy duty internal combustion engines was promoted and validated with customers. The aim of this article is to describe the material properties of the new alloy in more detail than previously and explain how the advantageous properties of CuAl8Fe5Ni4Zn4Sn1 are generated. At the beginning of the article, the general development trends in the field of copper alloys for sliding applications are presented. This is followed by a presentation of the latest research results about CuAl8Fe5Ni4Zn4Sn, before concluding with a brief summary and future outlook, emphasizing on the fact that recent trends in copper-based sliding applications show great additional potential for further material developments.

Porous metals possess low bulk density, large specific strength, high stiffness and special thermal, electromagnetic and acoustic conductivity, so that porous metals are widely used in filtration and separation, flame retardant explosion-proof, biomedical application, etc. Compared with its corresponding dense metal, the presence of porous structures also leads to different corrosive performances of porous metal. So, some researches have utilized weight loss method, electrochemical impedance to evaluate porous metals’ corrosion behavior; however, the influence of pore structure on metal corrosion is still controversial, and present methods used for analyses of porous metals’ corrosion are statistical averages of the corrosion behavior of the entire porous material, which cannot accurately reflect the corrosion behavior inside the pore structure. Herein, we prepare porous copper samples with 0, 24, 72, 96 pores using mechanical process, and employ scanning kelvin probe combined with electrochemical polarization curve and impedance spectroscopy to test the corrosion performance of the porous copper in static and dynamic NaCl solution. The relevant results indicate that in static solution, the corrosion resistance of samples gradually increases with the rise of the number of pores. By contrast, the sample with 24 pores exhibits more susceptible to corrosion than the sample without pore.

Copper toxicity has been a selective pressure on the sea-ice bacteria due to its widespread occur-rence in Antarctica. Here, with a combined biochemical and metabolomic approach, the Cu2+ ad-aptation mechanisms of Antarctic bacteria were analyzed. Heavy metal resistance pattern of Pb2+ > Cu2+ > Cd2+ > Hg2+ > Zn2+ was observed. Copper treatment did increase the activity of antioxidants and enzymes, maintaining cellular redox state balance and normal cell division and growth. Metabolomics analysis demonstrated that fatty acids, amino acids, and carbohydrates played dominant roles in copper stress adaptation. The results indicated that the adaptation mechanisms of strain O5 to copper stress included protein synthesis and repair, accumulation of organic per-meable substances, up-regulation of energy metabolism, and formation of fatty acids. This study increases the resistance mechanism understanding of Antarctic strains to heavy metals in extreme environments.

Heavy metals contamination in groundwater often occurs in various industrial processes. Stud-ies have confirmed that polysulfide could reduce hexavalent chromium to trivalent chromium, achieving the effect of in-situ stabilization. For other heavy metals contamination in groundwa-ter, whether polysulfide also had a stabilizing ability to achieve in-situ remediation. This re-search focused on heavy metals except for chromium that often contaminated in groundwater, including lead, nickel, zinc, copper, and cadmium to explore the feasibility of using calcium polysulfide (CaSx) as an in-situ stabilization technology for these heavy metals contamination groundwater. Results showed that CaSx had a great removal efficiency for heavy metals lead, nickel, zinc, copper, and cadmium. However, for nickel, zinc, copper and cadmium, when CaSx was added excessively, complexes would be formed, causing the result of re-dissolve and this would also reduce the removal efficiency. Since it is difficult to accurately control the dosage of agents for in-situ groundwater remediation, the concentration of re-dissolved nickel, zinc, cop-per, and cadmium may not be able to meet the groundwater control standards. CaSx had high lead removal efficiency, and it would not cause re-dissolution due to excessive CaSx dosing. CaSx can be used as an in-situ stabilization technique for lead contaminated groundwater.

Researchers from around the world are looking for better and cheaper ozone production. One of the methods increasing the efficiency of ozone production is the use to a rotating electrode presented in this paper. Experiments were carried out which shows that the most important parameters are the materials used on the electrodes and the condition of its surface. The metallographic investigations of the electrodes after continuous monthly work was made, which show how the raids layers are formed. As a result of working in a highly oxidizing environment, the electrode is oxidized in the process of chemical corrosion. It is obvious that the layer of corrosion products created during the work of the plasma reactor isolates the surface of the electrode, which reduces the intensity of the electric field, causing a decrease in the amount of plasma generated, which is a direct cause of lowering the concentration of ozone during this process. The dynamics of plasma generation process and the type of electrode material working in changing process conditions are the decisive factors influencing the concentration of ozone produced. The influence of the medium, which is the electrode material, depends mainly on its resistance to corrosion in the environment of dynamically changing conditions, e.g. electrode rotation, oxygen flow through the rotating electric field and the long monthly working time of the plasma reactor.

Green synthesis using plant extracts has emerged as an eco-friendly, clean, and viable strategy alternative to chemical and physical approaches. The leaf, stem, and root extracts of Lannea discolor was utilized as a reducing and stabilizing agent in the synthesis of gold (AuNPs) and copper (CuNPs) nanoparticles. The formation of AuNPs and CuNPs confirmed by their color change, was characterised by UV–Vis Spectroscopy (UV- Vis), Scanning electron microscopy analysis and energy dispersive x-ray (SEM-EDX), Transmission Electron Microscopy (TEM), and Fourier Transform Infrared Spectroscopy (FTIR), coupled with minimum concentration inhibitory (MIC) antibacterial assays. AuNFs, NPs and CuNPs peaked at wavelengths in the ranges of 316, 544 and 564 nm respectively. TEM showed unexpected nanoflowers (30 – 97 nm) in the leaf extracts and spherical NPs (10 -33 nm; 9.3 – 37.5) from stem and root extracts, while spherical CuNPs (20 – 104 nm), were observed from all the extracts. EDX was able to confirm the presence of metal salts and FTIR revealed stable capping agents. AuNPs and NFs from L. discolor extracts showed appreciable antibacterial activity against Staphylococcus aureus, Escherichia coli, Pseudomonas aeruginosa, Klebsiella pneumoniae and Bacillus subtilis, when compared to the plant extracts, while none was observed from the CuNPs. These AuNPs and CuNPs are particularly appealing in a variety of applications in the biomedical as well as conductivity manufacturing, due to their shapes and sizes and economical and environmentally friendly production.

Macroautophagy/autophagy plays an important role in cellular copper clearance. The means by which the copper metabolism and autophagy pathways interact mechanistically is vastly unexplored. Dysfunctional ATP7B, a copper-transporting ATPase, is involved in the development of monogenic Wilson disease, a disorder characterized by disturbed copper transport. Using in silico prediction, we found that ATP7B contains a number of potential binding sites for LC3, a central protein in autophagy pathway, so-called LC3 interaction regions (LIRs). The conserved LIR3, located at the C-terminal end of ATP7B, was found to directly interact with LC3B in vitro. Replacing the two conserved hydrophobic residues W1452 and L1455 of LIR3 significantly reduced interaction. Furthermore, autophagy was induced in normal human hepatocellular carcinoma cells (HepG2) leading to enhanced colocalization of ATP7B and LC3B on the autophagosome membranes. By contrast, HepG2 cells deficient of ATP7B (HepG2 ATP7B-/-) showed autophagy deficiency at elevated copper condition. This phenotype was complemented by heterologous ATP7B expression. These findings suggest a cooperative role of ATP7B and LC3B in autophagy-mediated copper clearance.

The airflow carried by artificial aeration provides oxidant O2 for microbial growth and mineral dissolution in heap bioleaching. To investigate the effect of forced aeration rate on bioleaching of low-grade copper sulfide ores, column bioleaching experiments with six columns were conducted in the aeration range of 0~150 L/h at 30~45 ℃. The results showed that when the aeration rate was higher than 95 L/h, the proportions of heap settlement and fine particles mass were much greater than that without aeration. The final total Fe concentration and bacterial cell numbers in pregnant leach solution increased with the increase of aeration rate.The final concentrations of Cu2 + in the mother liquor under aeration conditions of 60-150 L / h were 1.411, 1.432, 1.498, 1.491 and 1.583 g / L, respectively, which were higher than 1.345 g / L under non-aeration conditions. When the aeration rate was 150 L / h, the final Cu leaching rate was 80.1 %, which was 11.4 % higher than that without aeration ( 68.7 % ). Furthermore, in the early stage of leaching, copper leaching rate with 95 L/h aeration rate remained the highest. 结论Artificial aeration accelerates the bioleaching of low-grade copper sulfide ores by improving porosity structure, temperature range of bacterial activity and microbial catalyzed dissolution of targeted minerals.

Copper oxide nanoparticles (CuONPs) were synthesized using an eco-friendly method and their antimicrobial and biocompatibility properties were determined. The supernatant and extract of the fungus Ganoderma sessile yielded small, quasi-spherical NPs with an average size of 4.5 ± 1.9 nm and 5.2 ± 2.1 nm, respectively. CuONPs showed antimicrobial activity against Staphylococcus aureus, Escherichia coli and Pseudomonas aeruginosa. Minimum inhibitory concentration (MIC) for E. coli and S. aureus was 15.9 µg/mL for nanoparticles (NPs) using the supernatant (CuONPs-S) and 16.5 µg/ml for NPs using the extract (CuONPs-E). Lower concentrations were required for P. aeruginosa inhibition. Ultrastructural analysis revealed the presence of the small CuONPs all through the bacterial cells. Finally, the toxicity of CuONPs was analyzed in three mammalian cell lines: hepatocytes (AML-12), macrophages (RAW 264.7) and kidney (MDCK). Low concentrations (<15 µg/ml) of CuONPs-E were non-toxic to kidney cells and macrophages, and the hepatocytes were the most susceptible to CuONPs-S. The results obtained suggest that the CuONPs synthesized using the extract of the fungus G. sessile, could be further evaluated for the treatment of superficial infectious diseases.

This work aimed to carry out a bioremediation study to evaluate the resistance of Penicillium sp. isolated from kefir grains for the treatment of copper. The fungal culture medium was prepared using a 2% malt-agar medium at pH 7.0 in which Penicillium sp. was inoculated. Penicillium sp. growing in a liquid medium showed a decrease in biomass in presence of Cu(NO3)2 (800 mg.L-1), suggesting that the metal impacts the growth rate of the fungus. Moreover, the combined factors of pH and the presence of the inorganic contaminant impacted the radial growth of the fungus, causing inhibition of 73% at pH 4.0, 75% at pH 7.0, and 77% at pH 9.0 in liquid medium compared to control. However, images obtained with scanning electron microscopy showed the integrity of the fungus cell, even at high doses of copper in the medium. Therefore, it can be concluded that Penicillium sp. isolated from kefir grain can bioremediate the environment and that the harmful effects of heavy metals can be minimized as a result biosorption. Although the growth of Penicillium sp. is inhibited, such retardation requires high doses of copper nitrate, thus ensuring the use of this microorganism for protection against the harmful effects of non-essential copper in the environment.

The color of a thin copper oxide layer formed on a copper plate was transformed from reddish-brown into blue-purple by irradiation with 5 keV Ar+ ions to a fluence as low as 1 1015 Ar+ cm–2. In the unirradiated copper oxide layer, the copper valence state of Cu2+ as well as Cu+ and/or Cu0 was included as indicated by the presence of a shake-up satellite line in a photoemission spectrum. While for the irradiated one, the satellite line decreased in intensity, indicating that irradiation resulted in the reduction from Cu2+ to Cu+ and/or Cu0. Furthermore, nuclear reaction analysis using a 16O(d, p)17O reaction with 0.85 MeV deuterons revealed a significant loss of oxygen (51015 O atoms cm–2) in the irradiated layer. Thus, the chromatic change observed in the present work originated in the irradiation-induced reduction of a copper oxide.

Compelling epidemiologic data support the critical role of dietary fructose in the epidemic of obesity, metabolic syndrome and nonalcoholic fatty liver disease (NAFLD). The metabolic effects of fructose on the development of metabolic syndrome and NAFLD are not completely understood. High fructose intake impairs copper status, and copper-fructose interactions have been well documented in rats. Altered copper-fructose metabolism leads to exacerbated experimental metabolic syndrome and NAFLD. A growing body of evidence has demonstrated that copper levels are low in NAFLD patients. Moreover, hepatic and serum copper levels are inversely correlated with the severity of NAFLD. Thus, high fructose consumption and low copper availability are considered two important risk factors in NAFLD. However, the causal effect of copper-fructose interactions as well as the effects of fructose intake on copper status remain to be evaluated in humans. The aim of this review is to summarize the role of copper-fructose interactions in the pathogenesis of the metabolic syndrome and discuss the potential underlying mechanisms. This review will shed light on the role of copper homeostasis and high fructose intake and point to copper-fructose interactions as novel mechanisms in the fructose induced NAFLD.

Alumina dispersion-strengthened copper, Glidcop, is used widely in high-heat-load ultra-high-vacuum components for synchrotron light sources (absorbers), accelerator components (beam intercepting devices) and in nuclear power plants. Glidcop has similar thermal and electrical properties to OFE (oxygen free electrical) copper, but has superior mechanical properties, thus making it a feasible structural material; its yield and ultimate strength are equivalent to those of mild-carbon steel. The purpose of this work has been to develop a brazing technique to join Glidcop to Mo, using a commercial Cu-based alloy. The effects of the excessive diffusion of the braze along the grain boundaries on the interfacial chemistry and joint microstructure, as well as on the mechanical performance of the brazed joints, has been investigated. In order to prevent the diffusion of the braze into the Glidcop alloy, a copper barrier layer has been deposited on Glidcop by means of RF-sputtering.

Carbonous nanomaterials are promising additives for composite coatings for heat-dissipation materials because of their excellent thermal conductivity. Here, copper/carbonous nanomaterial composite coatings were prepared using nanodiamond (ND) as the carbonous nanomaterial. The copper/ND composite coatings were electrically deposited onto copper substrates from a continuously stirred copper sulfate coating bath containing NDs. NDs were dispersed by ultrasonic treatment, and the initial bath pH was adjusted by adding sodium hydroxide solution or sulfuric acid solution before electrodeposition. The effects of various coating conditions—the initial ND concentration, initial bath pH, stirring speed, electrical current density, and the amount of electricity—on the ND content of the coatings were investigated. Furthermore, the surface of the NDs was modified by hydrothermal treatment to improve ND incorporation. A higher initial ND concentration and a higher stirring speed increased the ND content of the coatings, whereas a higher initial bath pH and a greater amount of electricity decreased it. The electrical current density showed a minimum ND content at approximately 5 A/dm². Hydrothermal treatment, which introduced carboxyl groups onto the ND surface, improved the ND content of the coatings. A copper/ND composite coating with a maximum of 3.85 mass% ND was obtained.

This research paper focuses on the synthesis and characterization of Cu-doped Mg-Co ferrites with varying compositions (Mg_0.6-xCo_0.4Cu_xFe₂O₄, where x = 0.0, 0.1, 0.2, and 0.3) using a solid-state reaction method. This paper also investigates the structural, morphological, magnetic, and electrical characteristics of synthesized Mg_0.6-xCo_0.4Cu_xFe₂O₄, where x = 0.0, 0.1, 0.2, and 0.3. The X-ray diffraction (XRD) technique confirms the ferrites spinel structure in the Fd-3m space group, with average crystallite sizes ranging from 57.29 to 48.57 nm. Fourier Transform Infrared (FTIR) spectroscopy verifies chemical and structural changes, while scanning electron microscopy (SEM) reveals cubic crystal growth with an average grain size of 1 to 1.5 μm. DC electrical resistivity decreases with increasing temperature and Cu²⁺ substitution, ranging from 1.4 x 10⁶ Ω-cm to 6.7 x 10⁵ Ω-cm. The study suggests a correlation between resistivity and Cu²⁺ concentration. Magnetic behaviour, studied using a Vibrating Sample Magnetometer (VSM), shows dependence on dopant concentration, with coercivity ranging from 157 Oe to 256 Oe. The results indicate potential applications in magnetic storage devices, antennas, transformers, and high-frequency electronics.

The direct methane to methanol (MTM) oxidation is a grand challenge in catalysis, with profound economical implications for the modern chemical industry. Bioinspired metal-organic frameworks (MOFs) with active iron and copper sites have been emerging very recently as innovative catalytic platforms to accomplish the MTM conversion under mild conditions. This review discusses the current state of the art regarding the application of MOFs with iron and copper catalytic centers to perform the MTM reaction, with a focus on the diverse spectroscopic techniques used to unveil the electronic and structural properties of the MOF catalysts at a microscopic level. We explore the synthetic strategies employed to incorporate iron and copper sites into different MOF topologies, the efficiency and selectivity of the iron- and copper-bearing MOF catalysts, and the ensuing MTM reaction mechanisms proposed on the basis of spectroscopic characterization supported by theory. In particular, we evidence how the combination of complementary spectroscopic tools probing different regions of the electromagnetic spectrum is particularly useful to reach a satisfactory understanding of the key reaction pathways and intermediates. Finally, we provide a critical perspective on future directions to advance the use of MOFs to accomplish the MTM reaction.

Mining and processing tailings often contain significant amounts of valuable metals, that can represent valuable sources of secondary raw materials. Especially this is case in early-stage operations, in which the head grades were higher, and the tailings were higher grade. These tailings can also present a substantial risk to the environment. Serbia has copper deposits which have been exploited since ancient times, and these operations have generated large amounts of mineral processing tailings. The main objective of this study is to show how valuables can be recovered from chemically and mineralogically challenging tailings. After detailed chemical and mineralogical characterization, the laboratory scale flotation tests focused on evaluating the effect of particle size, different types of collectors, pH, and pulp potential. Based on the test work, copper and gold can be recovered effectively into pyrite concentrate

One of the largest in the archipelago silver-copper mineralisation at Mount Sigurdf′ellet in West Spitsbergen Island was found in 1990 by Russian geologists. Firstly genesis was caused exclusively with hydrothermal ore migration of a substance from the enclosing sandstone and siltstone of the Devonian age. But subsequent work on the ore and nearest rocks of the basement gave a new factual material on the geochemical characteristics of potential sources of metals and found new for this mineral occurrence - gold mineralization. Similarity of geochemical associations of Sigurd ore occurrence with nearby upper Proterozoic marble as the first likely source of ore substance and the second - caused by carbonate-containing streaks in Low Devonian sediments. Ore-formation, probably due to repeated hydrothermal processes and was completed in a period of tectono-magmatic activity in Jurassic-Cretaceous time.

: In Chile, most tailings impoundments are in Northern and Central Chile, 20% of them are abandoned. Municipal budgets to manage these environmental liabilities are very limited and the use of native and endemic plant species to remove heavy metals from tailings is a low-cost alternative. Ex-situ phytoremediation experiments were conducted over seven months to evaluate the potential of Lycium chilense and Haplopappus foliosus to remove copper and lead from mine tailings. The results indicate that both species can concentrate high levels of both elements and they present removal efficiencies for Cu close to 50%. The best performance was presented by Haplopappus foliosus, accumulating higher concentrations of both metals than Lycium chilense. Also, it presents a bioconcentration over 1.

Sulfate attack is one of the main factors affecting the durability of concrete structures. In recent years, multi-walled carbon nanotubes (MWCNTs) have attracted the attention of scholars for their excellent mechanical properties and durability performance. In this paper, the influence of sulfate attack and dry-wet cycles on the performance of multi-walled carbon nanotube-lithium slag concrete (MWCNTs-LSC) with varied MWCNTs content (0wt%, 0.05wt%, 0.10wt% and 0.15wt%) and varied water-cement ratios (0.35, 0.40 and 0.45) were investigated. Besides, scanning electron microscopy (SEM) and X-ray computed tomography (CT) tests were conducted to analyze the microstructure and pore structure of the concrete. The results show that concrete incorporated with MWCNTs could effectively mitigate sulfate attack The resistance to sulfate attack of concrete is negatively related to the water-cement ratio when the dry-wet cycle is fixed. The MWCNTs-LSC showed the best compressive strength at the water-cement ratio of 0.35 and 0.10 wt% MWCNTs. The SEM test results showed that the MWCNTs both filled the pores and cracks within the specimen and formed bridges between the cracks, enhancing the resistance to sulfate attack. The CT test results also showed that the addition of MWCNTs could reduce the porosity of concrete, refine the pore size and inhibit the generation and development of cracks, thus optimizing the internal structure of concrete and improving its resistance to sulfate attack.