This paper proposes an innovative approach to address the challenge of softening deformation of thermal-curable thermosets during additive manufacturing. This approach involves the development of a composite powder composed of thermosetting materials with distinct curing temperatures, the utilization of Cold Spray Additive Manufacturing (CSAM) technology for 3D printing, and the application of a stepwise isothermal curing process. The corresponding effectiveness is validated by case studies. The results demonstrate that samples printed via CSAM maintain a solid state without deformation. During the post-curing process, each component of the composite material cures independently while the other components remain in a solid state, providing structural support for the whole material, thereby effectively reducing the softening deformation during the post-curing process. This approach offers a novel perspective for the additive manufacturing of thermal-curable thermosets.

In the present study, the corrosion resistance of amorphous coating and composite coatings in 3.5 wt.% NaCl, 0.5 M H₂SO₄ and 10 wt.% NaOH solution were studied. The composite coatings exhibit superior corrosion resistance. When the content of AT13 （Al₂O₃–13 wt.% TiO₂）was 15 wt.%, the composite coating has the lowest corrosion current density (1.75×10^-6 A cm^-2), which is 5.14×10^-5 A cm^-2 for Fe-based metallic glassy coating, and the highest corrosion potential (-411 mV), which is -580 mV for Fe-based metallic glassy coating. The breakdown potential of the passivation film in 3.5 wt.% NaCl solution was much higher than that of 316L.The long-time immersion corrosion tests carried out on different coatings showed that the corrosion protection effect of coating was enhanced with the increase of the amount of AT13 added.

Viral co-infections, where a host is infected by multiple viruses simultaneously, are common in the human population. Human viral co-infections can lead to complex interactions between viruses and the host immune system, affecting the clinical outcome and posing challenges for treatment. Understanding the types, mechanisms, impacts, and identification methods of human viral co-infections is crucial for the prevention and control of viral diseases. In this review, we first introduce the significance of studying human viral co-infections and summarize the current research progress and gaps in this field. We then classify human viral co-infections into four types based on the pathogenic properties and species of the viruses involved. Next, we discuss the molecular mechanisms of viral co-infections, focusing on virus-virus interactions, host immune responses, and clinical manifestations. We also summarize the experimental and computational methods for identifying viral co-infections, emphasizing the latest advances in high-throughput sequencing and bioinformatics approaches. Finally, we highlight the challenges and future directions in human viral co-infection research, aiming to provide new insights and strategies for the prevention, control, diagnosis, and treatment of viral diseases. This review provides a comprehensive overview of the current knowledge and future perspectives on human viral co-infections, and underscores the need for interdisciplinary collaborations to address this complex and important topic.

In this work, nitrite intercalated CaAl-LDH was firstly prepared in this work. Scanning electronic microscopy (SEM) coupled with the energy dispersive spectrometer (EDS) was used to characterize the morphology and element composition of the synthesized powder. Fourier transform infrared spectroscopy (FTIR) was used to characterize the chemical composition and X-ray diffraction (XRD) was used to analyze the structure. The nitrite release curve and the chloride concentration change curve were obtained to study the anion-exchange reaction. The corrosion protection effect of the CaAl-LDH loaded with nitrites towards the carbon steel was evaluated in 0.02 M NaCl solution by electrochemical impedance spectroscopy (EIS). Then the powder was added in the epoxy coating with a percentage of 2% (vs. epoxy resin). The coating morphology and roughness was evaluated by SEM and laser microscopy, and the corrosion protection effect was investigated by EIS in an immersion period of 21 d. Local electrochemical impedance spectra (LEIS) was used to characterize the corrosion development process in micro-corrosion sites. The corrosion product of the scratched area after salt spray exposure was analyzed by EDS and Raman spectroscopy. The corrosion protection mechanism of the CaAl-LDH loaded with nitrites was proposed based on the above experimental results.

Selection of efficient corrosion inhibitors requires detailed knowledge regarding interaction mechanism, which depends on the type and amount of functional groups within the inhibitor molecule. Position of functional groups between different isomers is often overlooked but not less important since factors like steric hinderance may significantly affect the adsorption mechanism. In this study we have presented how different dihydroxybenzene isomers interact with aluminium alloy 5754 surface, reducing its corrosion rate in bicarbonate buffer (pH = 11). We have shown the highest inhibition efficiency among tested compounds belongs to catechol at 10 mM concentration, although differences were moderate. Utilization of novel impedance approach to adsorption isotherm determination allowed to confirm that while resorcinol chemisorbs on aluminium surface, catechol and quinol follows ligand exchange model of adsorption. Unlike catechol and quinol, the protection mechanism of resorcinol is bound to interaction with insoluble aluminium corrosion products layer and was only found efficient at concentration of 100 mM (98.7%). The aforementioned studies were confirmed with scanning electron microscopy and x-ray photoelectron spectroscopy analyses. There is a significant increase of the corrosion resistance offered by catechol at 10 mM after 24 h exposure in electrolyte: from 63 to 98%, with only negligible changes in inhibitor efficiency observed for resorcinol at the same time. However, in the case of resorcinol a change in electrolyte color was observed. We have revealed that the differentiating factor is the keto-enol tautomerism. The NMR studies of resorcinol indicate the keto form in structure in presence of NaOH, while the chemical structure of catechol does not change significantly in alkaline environment.

Improvement of hydrophysical properties and corrosion resistance of self-compacting concrete to the effects of alternate freezing-thawing and aggressive soils of southern and central Kazakhstan is of interest to a wide range of researchers from the side of practical application of the obtained results in construction practice. It is proposed to form a spatially reinforced fine crystalline structure of cement matrix with maximum dense packing by using a complex modifier (Hyperplasticiser + Polymer + Microsilica + Fibro fibers) in the composition of self-compacting concretes (SCC). The introduction of the calculated amount of the above additives increases the operational reliability of the current SCC compositions, increasing the water resistance to W16, frost resistance to F=500, increasing the compressive strength by 20%, reducing the mass loss of samples during corrosion leaching to 50%. It has been experimentally established that the proposed addition of complex modifier (Hyperplasticiser + Polymer + Microsilica + Fiber fibers) to the SCC composition allows obtaining self-compacting concrete of high quality with improved performance characteristics (compressive strength, water resistance, frost resistance and corrosion resistance). Studies have shown that the complex modifier-modified SCC compositions have a high degree of resistance in aggressive environments and leaching corrosion. Based on the results of the conducted tests, it is possible to recommend the obtained SCC compositions for production of building products working in the zone of alternating freezing-thawing and aggressive soils.

Structural and functional materials are subjected to harsh oxidizing environments that lead to a rapid decline in their surface chemical stability. At high-temperatures, the diffusion of atoms is erratic; thus, the reactive elements (REs) get a chance to migrate to the surface and look for oxygen-reactive sites. Their migration from the lattice sites creates vacancies in the matrix and thus weakens the bond, making the material prone to environmental degrading factors. Subsequently, the inward diffusion of oxygen, sulfur, nitrogen, or carbon may occupy these vacancies, resulting in undesired precipitation at the grain boundary, which is usually brittle. The solubility and dissociation of attacking species and corrosion products play the most critical role in corrosion in high-temperature water. To evade such situations, Ti, Al, and Cr are added in Ni/Fe-based alloys, forming a dense oxide layer on the surface that impedes further surface migration of ions. The stability of the alloys is then determined by the capability of these oxide layers to heal or reform during spalling/cracking. This review attempts to understand the migration of REs at the interfaces to prepare structural materials in any unexpected set of oxidizing service conditions. This review will also try to establish the interaction mechanism of REs novel/conventionally added in the alloys with the oxidizing elements in the environments to design better degradation-resistant high-temperature alloys.

Present worldwide difficulties in healthcare and the environment have motivated the investigation and research of novel materials in an effort to find novel techniques to address the current chal-lenges and requirements. In particular, the use of nanomaterials has demonstrated a significant promise in the fight against bacterial infections and the problem of antibiotic resistance. Metal na-noparticles and carbon-based nanomaterials in particular have been highlighted for their excep-tional abilities to inhibit many types of bacteria and pathogens. In order for these materials to be as effective as possible, synthetic techniques are crucial. Therefore, in this review article, we high-light some recent developments in the design and synthesis of various nanomaterials, including metal nanoparticles (e.g., Ag, Zn, or Cu), metal hybrid nanomaterials, and the synthesis of mul-ti-metallic hybrid nanostructured materials. Following that, examples of these materials’ applica-tions in antimicrobial performance targeted at eradicating multi-drug resistant bacteria, material protection such as microbiologically influenced corrosion (MIC), or additives in construction ma-terials have been described.

Governments worldwide are actively committed to achieving their carbon emission reduction targets, and one avenue under exploration is harnessing the potential of hydrogen. Blending hydrogen with natural gas is emerging as a promising strategy to reduce carbon emissions, as it burns cleanly without emitting carbon dioxide. This blending could significantly contribute to emissions reduction in both residential and commercial settings. However, a critical challenge associated with this approach is the potential for Hydrogen Embrittlement (HE), a phenomenon wherein the mechanical properties of pipe steels degrade due to the infiltration of hydrogen atoms into the metal lattice structure. This can result in sudden and sever failures when the steel is subjected to mechanical stress. To effectively implement hydrogen-natural gas blending, it is imperative to gain a comprehensive understanding of how hydrogen affects the integrity of pipe steel. This necessitates the development of robust experimental methodologies capable of monitoring the presence and impact of hydrogen within the microstructures of steel. Key techniques employed for this assessment include microscopic observation, hydrogen permeation tests, and tensile and fatigue testing. In this study, samples from two distinct types of pipeline steels used in the natural gas distribution network underwent rigorous examination. To induce hydrogen absorption, an electrochemical charging process is employed in a solution rich in H+ ions. This charging process, accomplished by a potentiostat applying a constant current, prompts the hydrogen evolution reaction at the steel specimen, acting as the cathode of the charging cell. Immediate tensile and fatigue testing following the charging process enables the evaluation of mechanical properties in comparison to non-charged samples. Different charging current densities are employed to simulate various hydrogen blend scenarios. The findings from this research indicate that charged samples exhibit a discernible decline in fatigue and tensile properties. This deterioration is attributed to embrittlement and reduced ductility stemming from the infiltration of hydrogen into the steel matrix. The extent of degradation in fatigue properties is correlated not only to the hydrogen content but also to the hydrogen permeability and diffusion rate influenced by steel’s microstructural features, with higher charging current densities indicating a more significant presence of hydrogen in the natural gas pipeline blend.

A series of waterborne polyurethane (WBPU)/modified lignin amine (MLA) adhesives was prepared using modified lignin amine (MLA) as a chain extender by a prepolymer mixing process. A successful Mannich reaction was achieved during the synthesis of MLA by reacting lignin with bis(3-aminopropyl)amine. Higher tensile strength, Young’s modulus and thermal stability were recorded for WBPU/MLA adhesives with higher MLA contents. The WBPU/MLA adhesive materials were used to coat PVC substrates. The adhesive strength increased with increasing MLA content. More importantly, the MLA also enhanced the WBPU/MLA coating in terms of adhesive strength at moderately high temperatures as well as under natural weather exposed conditions. The adhesive strength was essentially unaffected with 6.48 mole% MLA in the WBPU/MLA coating after exposure to natural weather conditions for 180 days.

The key question for the understanding of corrosion phenomena of Si3N4-SiC material in Al reduction cell – whether corrosion by gases (and oxidation in particular) opens way for the corrosion by molten cryolite, or corrosion of Si3N4-SiC by cryolite plays its own role in degradation of the material in service. More probably the reactions of silicon carbide and silicon nitride with molten cryolite go after the stage of pre oxidation to silicon dioxide. The corrosion of Si3N4-SiC material in the reduction cell may take place by “gas-solid” reaction and by “liquid-solid” reaction. There are several variants of lab corrosion test for the evaluation of corrosion resistance of Si3N4-SiC material to cryolite. The results of investigation of Si3N4-SiC lab corrosion test give no direct evidence of selective dissolution of specific phase (Si3N4 or SiC, α-Si3N4 or β-Si3N4) in cryolite. The existing variants of lab corrosion testing require clarification.

This paper deals with the design and kinematic analysis of a novel mechanism for the elbow joint of an upper-limb exoskeleton, with the aim of helping operators, in terms of effort and physical resistance, in carrying out heavy operations. In particular, the proposed eight-bar el-bow joint exoskeleton mechanism consists of a motorized Watt I six-bar linkage and a suitable RP dyad, which connects mechanically the external parts of the human arm with the corre-sponding forearm by hook and loop velcro and thus, helping their closing relative motion for lifting objects during repetitive and heavy operations. This relative motion is not a pure rotation and thus, the upper part of the exoskeleton is fastened to the arm, while the lower part is not rigidly connected to the forearm, but through a prismatic pair which allows both rotation and sliding along the forearm axis. Instead, the human arm is sketched by means of a crossed four-bar linkage, which coupler link is considered as attached to the glyph of the prismatic pair, that is fastened to the forearm. Therefore, the kinematic analysis of the whole ten-bar mecha-nism, which is obtained by joining the Watt I six-bar linkage and the RP dyad to the crossed four-bar linkage, is formulated to investigate the main kinematic performance and for design purposes. The proposed algorithm has given several numerical and graphical results. Finally, a double-parallelogram linkage, as particular case of the Watt I six-bar linkage, was considered in combination with the RP dyad and the crossed four-bar linkage, by giving a first mechanical de-sign and a 3D printed prototype.

Fe-(9, 19, 28, 37)wt.% Cr alloys were corroded at 700 and 800 ^oC for 70 h under 1 atm of N₂, 1 atm of N₂/3.2%H₂O-mixed gas, and 1 atm of N₂/3.1%H₂O/2.42%H₂S-mixed gas. The corrosion rate of Fe-9Cr alloy increased with the addition of H₂O, and furthermore with the addition of H₂S in N₂ gas. Fe-9Cr alloy was always nonprotective. In contrast, Fe-(19, 28, 37) wt.%Cr alloys were protective in N₂ and N₂/H₂O-mixed gas because of formation of the Cr₂O₃ layer. They were, however, nonprotective in N₂/H₂O/H₂S-mixed gas because sulfidation dominated to form the outer FeS layer and the inner Cr₂S₃ layer containing some FeCr₂S₄.

Earth observation satellites can capture images of specific areas in Earth's orbit based on user requirements. Despite the high demand for satellite imagery, satellites remain a scarce resource. When there are many observation tasks that are large and dense, they may interfere with each other due to satellite mobility. To address this issue, a multi-satellite scheduling algorithm based on a task merging mechanism has been proposed. This paper proposes a two-stage approach to the problem: task merging phase and merging task scheduling phase. The task merging phase introduces two methods based on Mean Shift and Complete Graph to generate the merging task set. In the merging task scheduling phase, a multi-satellite scheduling algorithm based on merging tasks is employed to solve the problem. Finally, certain measurement experiments suggest the effectiveness of the algorithm.

Today, legislative framework addresses the metal alloys’ corrosion issues, demanding the re-striction of use of the probable carcinogenic, mutagenic and toxic for reproduction at humans (CMG) metals, like nickel, cobalt and chromium, and demand to develop new biomaterials. Therefore, the aim of this research is to evaluate and compare ion release of standard dental alloys and their hypoallergenic equivalents. Six types of orthodontic alloy wires (nickel-titanium (NiTi), coated NiTi, stainless steel (SS), Ni-free SS, cobalt-chromium (CoCr), and titanium-molybdenum (TMA) were immersed into artificial saliva of pH 5.5 and 6.6. Release of metal ions was measured by inductively coupled plasma-mass-spectrometry (ICP-MS) after 3, 7, 14 and 28 days. Data analyses were done using analysis of variance, results with P

For better understanding the corrosion and corrosion products behavior in the primary circuit of lead-bismuth eutectic (LBE) coolant reactor, the concentration distribution of soluble impurities and the transport of solid particles are investigated through finite-element method. An axisymmetric model of the primary circuit of LBE reactor was constructed to accelerate the calculation the thermal hydraulic filed of circuit. The saturation concentration of solute Fe, Cr and Ni in LBE coolant are identified through the equilibrium of their oxides and PbO. And the very different saturation concentrations of Fe/Cr/Ni in LBE will lead to significant element selective corrosion. The migration of solid oxides particles in the primary circuit is also investigated by the Euler-Lagrange tracing model. The simulation shows that driving force for the movement of particles >100 μm is buoyancy, which lets particles float on a free surface, while particles <10 μm tend to suspend in coolant. However, the behavior of particles also depends on the formation position, the particles formed above the core have the high possibility of re-entering in the core.

As high strength and ultra-high strength steels are widely used in all kinds of modern welded constructions, a lot of research is carried out to investigate the mechanical properties of weldments of these steels but there is a scarce information on such important characteristic as their corrosion behaviour. This research focuses on the corrosion behaviour of weld metal of weldments of S906QL and S700MC steels. Weld metal was tested electrochemically in a 3,5% NaCl aqueous solution via potentiodynamic scan to determine corrosion rate and its dependence on welding gap. No influence of welding gap on corrosion rate was found but the experimental results suggested that corrosion rate depended on the chemical composition of filler material and the microstructure of weld metal.

Although various atmospheric corrosion simulation models have been developed that give good results, industrial environments are still challenging. This paper aims to investigate the effect industrial atmospheres in Bor on the mechanical properties of structural steel S235JR and to create a constitutive model and also laboratory experimental conditions that will give the best results as an accelerated corrosion test. Atmospheric corrosion tests lasted six months, using sites close to the Electrolytic Refining Plant and Sulphuric Acid Plant, as well as air quality monitoring stations at a remote location in the city of Bor. The laboratory experiments included a salt chamber test lasting 120 h and 240 h and immersing the specimen in the electrolyte from the Electrolytic Refining Plant for 30 days. The results were compared with the standard specimens stored in the laboratory. The X-ray diffraction (XRD) method was used to identify the composition of corrosion products. The scanning electron microscopy (SEM) analysis was applied to analyze the fracture surfaces of the specimens. The use of the Complete Gurson Model (CGM) described the tensile characteristics of the corroded specimens. The study has shown that an enhanced acceleration model and conditions could be developed using numerical analysis of the test results.

By introducing environmental mediator, for avoiding randomness in selecting indicators and subjectivity in deciding interaction path coefficients to reveal interaction mechanism among forest industry, ecology and environmental capacity, structural Pressure–State–Impact–Response (PSIR) and quantitative Structural Equation Modeling (SEM) are utilized with data on thirty–one provinces of China. We can find that: (i) forest industry has a negative influence on ecology, whereas ecology has a positive influence on industry; (ii) the destructive influence that industry has on ecology is much greater than the positive effect ecology has on industry; and (iii) environmental capacity plays a partial mediating role between industry and ecology. According to these results we can conclude that: (i) forest industry and ecology are not in a symbiotic relationship and have not reached a level of ecological security; (ii) the interaction between industry and ecology is in a period of transition from antagonistic to beneficial; and (iii) industry dominates ecology. However, we prospect the following advice: (i) methods of forest industry should be changed; (ii) new modes of industrial integration and circular economy should be developed; and (iii) the ability of the environment to sustain itself should be enhanced. The level of forest ecological security to discuss the symbiotic mechanism of industry and ecology will propose to be measured in future.

Revealing the spatial distribution mechanism of the coupling effect between soil water and salt is essential for managing saline-alkali farmland. This study utilized the multifractal method to analyze soil water and salt under varying water content levels in arid saline-alkali farmland. Soil samples were collected on the second (S1), fifth (S2), eighth (S3), eleventh (S4), and fourteenth (S5) days after a rainfall event. The findings showed that a significant decrease in soil water content, contrasting with an increase in soil salt content throughout the soil layers post-rainfall. As water content decreased, the spatial variability of soil water initially increased from S1-3 and then decreased, while the spatial variability of soil salt decreased. The spatial distribution between soil water and salt exhibited a high correlation at S3-4 (with relative water content of soil ranging from 0.52 to 0.75) due to their coupling effect. However, soil salt was unevenly leached by rainfall at high water content levels (S1-2) and precipitated at low water content levels (S5), resulting in low spatial variability correlations between soil water and salt. This study elucidated the coupling process of soil water and salt, identifying their spatiotemporal distribution mechanism in dryland agricultural areas.

As a new plant slope protection technology, living stumps can effectively improve slope stability. The current study attemptes to investigate the mechanical characteristics of the root system of living stumps and their reinforcement mechanism on slopes by carrying out a three-dimensional living stump slope modeling test. Using ABS materials, a 3D model of a living elm stump was created by 3D printing and a slope model test was carried out. The reinforcement mechanism of the living stump was studied through a combination of model testing and numerical simulation. The results indicate that, due to the presence of living stumps in the lower and middle parts of the slope, the maximum shear stress area of the soil moved to a deeper direction. The stress state of the soil around the living stump was effectively improved due to the existence of the lateral root system.Living stumps in the lower part of the slope cross the potential sliding surface and transferred the soil shear stress gradually to the root system through root-soil interaction. Moreover, the tap roots and lateral roots of living stumps form a robust spatial structure that bears the shear stress of soil together, thus increasing the stability of the slope.

This study introduces a novel nanocomposite coating composed of PANI/CeO2 nanocomposite films, aimed at addressing corrosion protection needs. Analysis through FTIR spectra and XRD patterns confirms the successful formation of the nanocomposite films. Notably, the PANI/CeO2 nanocomposite films exhibit a hydrophilic nature. The bandgap energy of the PANI composite film measures at 3.74 eV, while the introduction of CeO2 NPs into the PANI matrix reduces the bandgap energy to 3.67 eV. Furthermore, the electrical conductivity of the PANI composite film is observed to be 0.40 S.cm-1, with the incorporation of CeO2 NPs leading to an increase in electrical conductivity to 1.07 S.cm-1. To evaluate its efficacy, electrochemical measurements were conducted to assess the corrosion protection performance. Results indicate a high protection efficiency of 92.25% for the PANI/CeO2 nanocomposite film.

Glioblastoma (GB) is the most aggressive and prevalent glioma within the Central Nervous System. GB exhibit a dismal 5-year survival rate (~6%) due to unfavorable prognosis and lack of viable treatment options. Therefore, novel therapies with plant-derived compounds emerge as very promising. This study aims to investigate the antitumor activity of 7α-acetoxy-6β-hydroxyroyleanone (Roy) in GB cell lines. Roy was isolated from Plectranthus hadiensis Schweinf. and its antitumor mechanism was assessed in a panel of five GB cell lines to mimic tumor heterogeneity. Metabolic activity was evaluated by Alamar Blue® assay, while cell death, cell cycle regulation, mitochondrial membrane potential, and activated caspase-3 were evaluated by flow cytometry. mRNA levels of target genes were measured by qPCR and protein expression was assessed by Western blotting. Cell uptake and impact on mitochondrial morphology were evaluated by confocal microscopy. Roy induced G2/M cell cycle arrest, mitochondrial fragmentation, and apoptosis by inhibiting the expression of anti-apoptotic proteins and increasing activated caspase-3 levels with concentration 6-9 fold lower than those of temozolomide, the first-line treatment. Roy demonstrated a robust antitumor activity against GB cells, without affecting non tumoral cells (microglia and astrocytes), being a promising natural lead compound for the development of novel chemotherapeutic approaches.

The existing methods of oil palm Fresh Fruit Bunch (FFB) evacuation from in-field to temporary collection point which typically apply medium to large tractors, often result in unexpected soil compaction. Meanwhile, smaller size equipment indicates low working capacity and unable to perform direct unloading to collection bin. This paper addresses the challenge of FFB evacuation by focusing on preventing soil compaction, increasing working capacity and enabling direct unloading to collection bin. For this purpose, a 6x6WD transporter prototype with a scissor lift mechanism was developed. With the design, the transporter could evacuate FFB in both steep mineral terrain and low ground pressure peatland, able to carry FFB with capacity of 750 kg and provide direct unloading into collection bin. The average field working capacity of the transporter was found to be 15 tons day-1. This research offers insights for future designs of medium-sized FFB transporters with advanced unloading mechanisms.

A method for accurately determining the chemical composition of deposits at the bottom of pores during the electrocoloring (e-coloring) of aluminum anodic oxide (AAO) layers in tin-based solutions is developed. The aluminum samples were AC e-colored after DC sulfuric anodization. Free-standing, tin e-colored aluminum oxide film was obtained by selective dissolution of the metallic aluminum from the AAO in copper chloride solution to access the deposit directly at the bottom of the pore. This allowed us to take XPS analysis directly from the deposits at pore bottoms without any interference from the base material or insulating barrier layer. The results revealed the presence of a mixture of tin oxide and metal in the deposits, which were richer in oxide content. Furthermore, a cyclic voltammetry experiment mimicking real polarization conditions during AC conditions was optimized and used to gain a deeper understanding of the electrochemical reactions that occur during AC electrocoloring. The comparison of CV results in tin-free and tin-containing electrolytes indicated that the tin deposited during a cathodic cycle is oxidized in the anodic cycle. The formation of tin based deposits radically changed the CV behavior. The XPS and cyclic voltammetry results consistently show that the deposits formed during e-coloring comprised a mixture of metallic and oxidic tin species richer in oxide content.

Banana wilt caused by Fusarium oxysporum f. sp. cubense tropical race 4 (Foc TR4) is a devastating fungal disease. Biocontrol strategies owned immense potential in inhibiting the spread of Foc TR4. Here, thirty actinobacteria were isolated from soils and screened for their antagonistic activity against Foc TR4. Strain SCA4-21T exhibited broad-spectrum antifungal activity against nine phytopathogenic fungi including Foc TR4. The strain was identified as the genus Streptomyces according to phenotypic characteristics and 16S rRNA gene phylogenetic analysis. Multi-locus sequence analysis based on five house-keeping gene alleles (atpD, gyrB, recA, rpoB, and trpB) revealed that strain SCA4-21T clustered into S. hygroscopicus subsp. hygroscopicus NBRC 13472T with 100% of bootstrap value. Average nucleotide identity and dDDH were 98.49% and 44.30% above the threshold of novel species. Hence, strain SCA 4-21T represented a novel species within the genus Streptomyces, named as Streptomyces luomodiensis sp. nov.. The type strain is SCA4-21T (=GDMCC4.340T= JCM36555T). By the CAZymes analysis, 348 carbohydrate-active enzymes were detected, including 15 chitinases and 8 β-1,3-glucanases. The fermentation broth of strain SCA4-21T showed high activities of chitinase and β-1,3-glucanase, contributing to the antifungal activity. Our results showed an innovative potential biocontrol agent for managing plant fungal diseases, specifically banana fusarium wilt.

Nutrition therapy is the best solution to human chronic diseases, especially beer and barley which play an important role in human health and civilization. We demonstrated the actional mechanism of functional ingredients in beer and barley to combat chronic diseases, based on PubMed, google, CNKI, and ISI Web of Science databases from 1997 to 2024. Beer is rich in functional ingredients that is a complex of barley malt and hops; the health effect of beer against 26 chronic diseases is highly similar to that of barley, due to molecular mechanism of polyphenols (phenolic acids, flavonoids), melatonin, minerals, bitter acids, vitamins, and peptides. The ancient German Beer Purity Law provides much scientific basis today, especially indirectly supporting the human one cell disease theory. Low purine beer can be produced by enzymatic and biological degradation and adsorption of purines as well as dandelion addition. Functional beer with low purine and high active ingredients made from Beer Purity and barley malt as well as functional foods addition will be the key and important development direction, such as ginger beer and ginseng beer, especially coix-lily beer at the ancestors ca. 9000 years ago. This review paper not only reveals the actional mechanism of beer overcoming human chronic diseases, but also provides scientific basis for the development of functional beer for the prevention and treatment of human chronic diseases.

Dysferlinopathies comprise a spectrum of muscular dystrophies characterized by progressive muscle weakness and degeneration due to mutations in the DYSF gene, which encodes the dysferlin protein critical for muscle membrane repair. This review delves into the clinical spectra of dysferlinopathies, their molecular mechanisms, and the spectrum of emerging therapeutic strategies. We explore the phenotypic heterogeneity of dysferlinopathies, highlight the incomplete understanding of genotype-phenotype correlations, and discuss the implications of various DYSF mutations. Furthermore, we examine the utility of animal models in elucidating disease mechanisms and the potential of symptomatic, pharmacological, molecular, and genetic therapies in mitigating the disease's progression. We also consider the roles of diet and metabolism in managing dysferlinopathies, as well as the impact of clinical trials on treatment paradigms. By culminating the complexities inherent in dysferlinopathies, this article emphasizes the need for multidisciplinary approaches, precision medicine, and extensive collaboration in research and clinical trial design to advance our understanding and treatment of these challenging disorders.

The North China Plain is among the regions most afflicted by ground fissure disasters in China. Recent urbanization has accelerated ground fissure activity in the three counties of the northern North China Plain, posing significant threats to both the natural environment and socioeconomic sustainability. Despite the increased attention, a lack of comprehensive understanding persists due to delayed recognition and limited research. This study conducted field visits and geological surveys across 43 villages and 80 sites to elucidate the spatial distribution patterns of ground fissures in the aforementioned counties. By integrating these findings with regional geological data, we formulated a causative model to explain ground fissure formation. Our analysis reveals a concentration of ground fissures near the Niuxi and Rongxi faults, with the former exhibiting the most extensive distribution. The primary manifestations of ground fissures include linear cracks and patch-shaped collapse pits, predominantly oriented in east-west and north-south directions, indicating tensile failure with minimal vertical displacement. Various factors contribute to ground fissure development, including fault activity, ancient river channel distribution, bedrock undulations, rainfall, and ground settlement. Fault activity establishes a concealed fracture system in shallow geotechnical layers, laying the groundwork for ground fissure formation. Additionally, the distribution of ancient river channels and bedrock undulations modifies regional stress fields, further facilitating ground fissure emergence. Rainfall and differential ground settlement serve as triggering mechanisms, exposing ground fissures at the surface. This research offers novel insights into the causative mechanisms of ground fissures in the northern North China Plain, providing valuable scientific evidence for mitigating ground fissure disasters during the urbanization process in the region.

The iron roughneck is an automated equipment utilized for the connection and removal of drilling tools. This paper presents the design of an integrated iron roughneck, providing a detailed introduction to its clamp body structure, along with an analysis of its structural characteristics and performance requirements. The study delves into the integration mode and working characteristics of the clamping mechanism and spin buckle mechanism for the integrated upper clamp body structure of the iron roughneck. Additionally, this paper conducts an in-depth theoretical study on the spin buckle mechanism. Firstly, it analyzes the actual working condition of the spin buckle roller from two perspectives: contact theory and rolling friction theory, determining the structural form of the spin buckle roller. Secondly, it investigates the relative displacement between the spin buckle mechanism and the drilling tool, proposing a design method for the floating device mounted on the spin buckle roller and establishing the kinematic equation of the spin buckle roller under the influence of the floating device. Furthermore, the kinematic equations of the spin buckle roller under the influence of the floating device are established. Finally, a dynamics simulation experiment is performed to simulate the working process of the spin buckle mechanism under actual working conditions, analyzing the dynamics and kinematics of the spin buckle mechanism and obtaining the relevant parameter curves of the spin buckle mechanism and drilling tools. Through data comparison and analysis, the correctness of the theoretical analysis results and the rationality of the performance and structure of the spin buckle mechanism are verified.

Insulated Gate Bipolar Transistor (IGBT) may convey high current and sustain high breakdown voltages; it may provide high power control. In a sense, how IGBT demonstrates the capability of power control was not specifically described, and the equivalent bipolar junction transistors (BJT) activated by an applied bias to the insulated gate is intriguing. As seen in Figure 1, IGBT shows an equivalent circuit structure containing two types of BJT, (NPN-type Bipolar transistor and PNP-type Bipolar transistor), which can be modeled as diode-associated transistor. Apparently, as a bias applies to the controlling gate, the channel beneath the gate oxide gets strongly inversed and turns out to be conductive just like what happens on metal-oxide-silicon field effect transistor (MOSFET), which provides necessary igniting currents to both BJTs and thus causes high current gain flowing through them-selves from the bottom. A proposed and renewed formula provides addressing the above scenario and successfully fitting the measured data that forms the characteristic curves. Some parameters in the proposed formula, which includes size and mobility associated constant, threshold voltage, and Early-Voltage-related lambda for MOSFET, explain and explore the underlying physics. IGBT thus enjoy high input impedance and high current gain due to MOSFET (Insulated Gate) and BJT, respectively. This formula combines both merits of MOSFET and BJT in order to fit the measured data. Indeed, the formula intimately fits IGBT electrical characteristic curves, and thus may be qualified and served as a model. The new model is then advisable for designing power integrated circuit to exactly achieve power saving, power control, and power efficiency.

In this work, the inhibition properties of new bio-based lignine ILs on the corrosion of mild steel in an aqueous solution of 0.01 M NaCl were investigated by Potentiostatic Electrochemical Impedance Spectroscopy (PEIS), Cyclic Potentiodynamic Polarization (CPP). Moreover, the surface was characterized using SEM, EDS, and optical profilometry. The influence of cation and anion on the inhibitor properties and a possible synergistic effect were investigated. The IL choline syringate showed a promising performance, reducing the corrosion current after 24-hour immersion in 0.01 M sodium chloride, from 1.66 µA/cm2 for the control to 0.066 µA/cm2 with 10 mM of the IL present. In addition to the performance as a corrosion inhibitor, both components of this IL also meet or exceed current additional desired properties of such compounds, being readily available, economically efficient, and well tolerated in organisms and the environment.

New corrosion inhibitor derived from coumarin-3-amine namely 3-((2-chlorobenzylidene)amino)coumarin was synthesized and characterized by CHN elemental analysis in addition to Fourier transform infrared and nuclear magnetic resonance techniques. The anti-corrosion ability of 3-((2-chlorobenzylidene)amino)coumarin to inhibit the impacts of corrosion has been demonstrated and damage reduction of the mild steel also. 3-((2-chlorobenzylidene)amino)coumarin, has been employed as a good corrosion inhibitor for mild steel in HCL solution. The efficiency of the inhibition was figured according to weight loss method and it was 74.6%.

In recent years, with the development of the Internet of Things and distributed computing, the "server-edge device" architecture has been widely deployed. This study focuses on leveraging autoencoder technology to address the binary classification problem in network intrusion detection, aiming to develop a lightweight model suitable for edge devices. Traditional intrusion detection models face two main challenges when directly ported to edge devices: inadequate computational resources to support large-scale models and the need to improve the accuracy of simpler models. To tackle these issues, this research utilizes Extreme Learning Machine for its efficient training speed and compact model size to implement autoencoders. Two improvements over the latest related work are proposed: First, to improve data purity and ultimately enhance detection performance, this study partitions the data into multiple regions based on the prediction results of these autoencoders. Second, leveraging autoencoder characteristics to investigate further the data within each region. We used the public dataset NSL-KDD to test the behavior of the proposed mechanism. The experimental results show that when dealing with multi-class attacks, the model's performance was significantly improved, the accuracy and the F1-score are improved by 3.5% and 2.9%, respectively maintaining its lightweight nature.

At present, farmland abandonment（FA）is a severe phenomenon in China, imposing a serious restriction on agricultural production. In this context, it is of great significance to explore the logical relationship between high-standard farmland construction (HSFC) and FA to optimize land resource allocation and guarantee national food security. Based on 838 samples of farmers in the main rice production area of the Yangtze River Basin in China, this paper employs the Tobit model, the mediating effect model, and the moderated mediating effect model to analyze the impact of HSFC on FA at the micro level. The results show that (1) HSFC inhibits FA, and FA proportion decreases by 1.14% for every 1% increase in HSFC proportion, and the robustness test and endogeneity treatment also yield consistent conclusions. (2) Agricultural socialization services (ASS) play a positive mediating role in the influence path. HSFC promotes farmers' purchase of ASS, which in turn inhibits FA. (3) The agricultural labor transfer distance (ALTD) plays a positive moderating role in the relationship between HSFC and FA. The farther the distance, the more likely HSFC can promote farmers' purchase of ASS and inhibit FA. The results provide enlightenment on how to precisely implement HSFC policy, that is, to inhibit FA by improving the construction of high-standard farmland and the post-construction management as well as protection system. Moreover, this study helps guiding the development of ASS and optimizing the institutional environment for agricultural labor transfer, creating conditions for agricultural scale management.

This review paper aims to understand the current processing plant maintenance systems and further identify on-stream phased array corrosion mapping (PACM) to reduce turnaround maintenance (TAM) activity during plant operations. Reducing the TAM duration and extending the TAM interval are common goals of most researchers. Thus, a detailed review was performed to understand the maintenance systems and the problems faced. Furthermore, a review of the current PACM application and the possibility of applying it during on-stream inspection was also per-formed. PACM has better detectability for localized corrosion, and the results can be obtained for a range of thicknesses, which is the main advantage of this method. The challenge is to apply it to a surface with high temperatures, owing to the greater probe contact and the limitation of ultrasonic properties. This literature review provides a more precise direction for future research to evaluate PACM on piping that can be utilized in inspection during plant operation at elevated temperatures. Detecting and monitoring corrosion growth without shutdown.

This study delves into the atmospheric corrosion behavior of chromium-free complex-phase steel (CP), specifically investigating the influence of wet/dry frequency and ratio in cyclic corrosion tests (CCT). The study employs a modified ISO 14993 standard CCT method, which involves salt spray, dry, and wet stages. After 15 and 30 CCT cycles, mass loss, maximum corrosion depth, and corrosion products were analyzed to gain insights into corrosion mechanisms. In general, increasing the frequency and wet/dry stage ratio in CCT extends the time for autocatalytic reactions to occur, leading to accelerated localized CP corrosion and increased pitting factors. However, as the rust layer thickens, uniform corrosion may also intensify, so careful considerations are necessary. This study underscores the importance of controlling the frequency and ratio of wet/dry stages in CCT for effectively analyzing localized corrosion behavior in specimens.

Objective: This research was aimed to estimate the anti-fatigue effects of arecoline and elucidate its underlying mechanisms using a murine model of central fatigue precipitated by sleep deprivation (SD). Methods: Seventy-two male C57BL/6 mice were randomly allocated into six groups: a control group, a SD-induced fatigue model group, a group receiving Rhodiola Rosea capsules (2.5 mg/kg), and arecoline groups administered low, medium, and high doses (10, 20, and 40 mg/kg, respectively). Following 28 days of continuous administrations, the effects of arecoline on the mouse fatigue-related behaviors was assessed by the behavioral tests, including grip strength, rotarod performance, and weight-bearing swimming endurance. Enzyme-linked immunosorbent assays (ELISAs) were utilized to measure the levels of the relevant biochemical markers. Western blotting was employed to quantify the expression of nuclear factor erythroid 2-related factor (Nrf2), Kelch-like ECH-associated protein 1 (Keap1), heme oxygenase 1 (HO-1), sequestosome-1 (p62), and NADPH quinone oxidoreductase 1 (NQO1) in the gastrocnemius muscle. Results: Arecoline administration notably enhanced grip strength, delayed the onset of fatigue as evidenced by extended latencies in rotarod tests, and increased the duration of weight-bearing swimming in mice. In the elevated plus maze, arecoline significantly reduced both the number of entries and the total distance traveled in the open arms. Arecoline markedly decreased serum levels of creatine kinase, blood urea nitrogen, lactate dehydrogenase, triglycerides, and cholesterol, while elevated total testosterone, lactate dehydrogenase, and immunoglobulin G levels. Furthermore, it significantly increased superoxide dismutase(SOD), catalase(CAT), and glutathione peroxidase activity in the gastrocnemius muscle, reduced malondialdehyde levels, augmented hippocampal SOD and CAT activity, and elevated glycogen stores in both liver and muscle tissues. Neurotransmitter levels were significantly increased, cytokine levels were markedly reduced, and the expression of Nrf2, Keap1, NQO1, p62, and HO-1 in brain tissue was significantly upregulated. Conclusion: The current study for the first time demonstrated that arecoline has significant anti-fatigue activity, and its mechanism of action is related to elevate the levels of glucose and lipid metabolism, relieve oxidative stress damage, inhibit neuroinflammatory response, regulate neurotransmitter levels and Keap1/Nrf2/HO-1 signaling pathway. The current study provides a new insight into the potential of arecoline in prevention and improvement of fatigue.

We have successfully developed curcumin nanosuspension aimed for oral delivery. The main purpose is to improve bioavailability through enhancing its solubility. The nanoparticles were stabilized using various stabilizers including polyvinyl pyrrolidone (PVP), polyvinyl alcohol (PVA), sodium carboxymethylcellulose (Na-CMC), d-alpha tocopheryl polyethylene glycol 1000 succinate (TPGS), and sodium dodecyl sulfate (SDS). The average diameter of particles, microscopic appearance, and sedimentation of each preparation was observed and compared. Each stabilizer demonstrated different degree of inhibition of particle aggregation under electrolyte-containing simulated gastrointestinal (GIT) fluid. Non-ionic stabilizers (PVA, PVP, and TPGS) has shown to preserve the nanosuspension stability against electrolytes. In contrast, strong ionic surfactants such as SDS were found to be very sensitive to electrolytes. The results can provide useful information for the formulators to choose the most suitable stabilizers by considering the nature of stabilizers and physiological characteristics of target site of the drug.

Sea cucumber peptides are small molecular peptides with biological function obtained from fresh sea cucumber as feedstock, which were hydrolyzed by protease, separated ,and purified. As the main product of sea cucumber refinement, it more accurately expresses the nutritional effect of sea cucumber and has a wide range of potential applications. It has been demonstrated that sea cucumber has a certain value-added effect on bone mineral density regulation, but the differences in bone mineral density regulation of extracts from different parts of sea cucumber and the techniques contributing to the efficient isolation of bone sea cucumber peptides have not been reported. Firstly, the aim of this study was to reveal the differences in osteogenic activities of enzymatic peptides from three major parts of sea cucumber: the body wall, the egg protein, and the intestinal protein. Then, the bone-enhancing sea cucumber peptides were isolated based on the characteristics of the dif-ferences in molecular weight distribution, hydrophilicity, and ionisation degree of sea cucumber, and to explore the possible mechanisms of their action. The findings indicated that sea cucumber peptides extracted from three distinct sites exhibited a dose-dependent enhancement of osteoblast proliferation and differentiation. Upon evaluating the three methods of sea cucumber peptide separation based on molecular weight distribution, hydrophilicity, and ionization, it was observed that the fraction isolated by hydrophobicity and

Aluminum base alloys containing chromium (Cr) and zinc (Zn) were produced using extrusion and heat treated powder metallurgy. Cr addition ranged between 5 to 10 wt. % while Zn was added in an amount between 0 to 20 wt. %. Heat treatment processes were performed during powder metallurgy process at different temperatures followed by water quenching. Similar alloys were extruded, with an extrusion ratio of 4.6 to get proper densification. Optical microscopy was used for microstructure investigations of the produced alloys. The element distribution microstructure study was carried out using the Energy Dispersive X-ray analysis method. Hardness and tensile properties of the investigated alloys have been examined. Wear resistance tests were carried out and the results were compared with these of the Al-based bulk alloys. Results showed that the aluminum base alloys containing 10wt. % Chromium and heat treated at 500°C for one hour followed by water quenching exhibited the highest wear resistance and better mechanical properties.

The corrosion inhibition behavior of cetyl pyridinium chloride (CPC) on mild steel (MS) in 0.5 M H₂SO₄ solution was examined using the weight loss method and potentiodynamic polarization method. The experimented MS surface was characterized by Fourier Transform Infrared Spectroscopy (FTIR), Field Emission Scanning Electron Microscopy (FESEM), and Atomic Force Microscopy (AFM). Corrosion rate and corrosion efficiency was calsulated via weight loss and potentiodynamic polarization methods where the corrosion rate in 0.5 M H₂SO₄ , 0.000192 M, and 0.0077 M of CPC solution was 12.09×10^-3, 8.23×10^-3, 6.63×10^-5 (mm/Year), respectively and the inhibition efficiency of 94.42% and 98.54%. FESEM studies demonstrated the corrosion attack on MS surface. Also, the EDX showed the presence of nitrogen of CPC. Thus, CPC acts as an important corrosion inhibitor.

Corrosion inhibitors are the natural or synthetic compounds that have the ability to inhibit the average of corrosion and reduce the damage of the mild steel. Enormous organic inhibitors nowadays employed in the corrosion domain but excluded due to costly. Comparatively cheap, and stable organic compound, namely 3-((4-nitrobenzylidene)amino)coumarin, have been utilized as an excellent corrosion inhibitor in hydrochloric acid for mild steel. The inhibition efficiency has been figured regarding to weight loss method. The corrosion inhibitor was identified according to spectroscopic techniques namely Fourier transform infrared and nuclear magnetic resonance in addition to micro-elemental analysis. Inhibition efficiency for the studied inhibitor was 71.4% that, at the highest studied concentration.

To enhance the corrosion resistance of molybdenum metal in molten zinc, this study successfully fabricated TiB2 coatings on molybdenum substrates using the molten salt electrophoretic deposition technique and investigated their corrosion resistance in molten zinc. Initially, TiB2 nanoparticles with a size ranging from 50 to 150 nm were synthesized using the borothermal reduction method in NaF-AlF3 molten salts at 1238 K. Subsequently, electrophoretic deposition experiment was conducted by applying a cell voltage of 1.2 V (corresponding to an electric field of 0.6V/cm) for 1 h in the molten salts containing TiB2 nanoparticles, resulting in a uniform, continuous, and dense TiB2 coating with a thickness of 35 μm on the molybdenum substrate. Moreover, the corrosion resistance of the TiB2 coated molybdenum metal to molten zinc was tested through continuous immersion. After 120 h of immersion, the TiB2 coating showed no signs of cracking or peeling off, successfully protecting the molybdenum metal substrate from corrosion by molten zinc. The results confirm that the molten salt electrophoretic deposition technique can be used to prepare TiB2 coatings with good resistance to molten zinc corrosion on molybdenum metal.

Information taken from David A. Scott’s book “Copper and Bronze in Art” was crucial for research on copper corrosion products in Stuttgart. Examples discussed are the nature and variability of ‘Black Spots’ (aka ‘Brown Fuzzies’); cupric hydroxide by cleaning, patination, and pigment synthesis; the wondrous phenomenon of curly malachite; chalconatronite formed by contact to soda glass; the formation of copper formates by glass-induced metal corrosion; and synthesis and X-ray diffraction of basic copper acetates (‘verdigris’).

it still undergoes corrosion when exposed to corrosive environments. This paper proposes an evaluation method for assessing the corrosion level of SPCC steel specimens using traditional eddy current testing (ECT), along with two different machine learning approaches. The objective is to classify the corroded state of the specimens into two states: a less corroded state (state-1) and a highly corroded state (state-2). Generative and discriminative models were implemented for classification. The generative classifier was based on the Gaussian mixture model (GMM), while the discriminative model was based on the logistic regression model. The models used features based on the absolute maximum of the perturbation magnetic field components at two different frequencies. The performance of the classifiers was evaluated using metrics such as absolute error, accuracy, precision, recall, and F1 score. The results indicate that high classification accuracy can be achieved based on both methods using traditional eddy current testing.

Nano-titanium has excellent corrosion resistance and can be widely used in the field of corrosion resistant coatings. This paper introduces nano-weight titanium modified phenolic resin coatings and their anti-corrosion properties to explore the principle of nano-titanium modification and the mechanism of anti-corrosion to further develop more advanced corrosion resistant coatings. The article uses scanning electron microscopy, Fourier transform infrared spectroscopy, Raman spectroscopy and UV-Vis spectrophotometer to characterise the morphology and structure of the nano-titanium modified phenolic resin coatings and to determine the corrosion resistance properties of the modified phenolic resin coatings. The results show that the 4% nano-titanium modified phenolic resin coating, nano-titanium powder and phenolic resin will maximize the dispersion and combination, and the structure is good; nano-titanium grafted on phenolic resin, the successful preparation of nano-titanium modified phenolic resin; modified nano-titanium added to improve the coating's ability of UV absorption. The corrosion resistance of the coating is much better than that of the unmodified phenolic resin coating.

Plasma Electrolytic Oxidation (PEO) is a surface treatment, similar to anodizing, that produces thick oxide films on the surface of metals. In the present work, PEO coatings were obtained on zinc-aluminized (ZA) carbon steel using as electrolyte a solution containing sodium silicate and potassium hydroxide, and working with high current densities and short treatment times in DC mode. The surface morphology resulted the typical one of PEO layers, with the presence of a lot of pores and micro-cracks. Considering the cross section, the thickness of the coating was strongly influenced by the process parameters, with different dissolution grades of the ZA layer depending on the current density and treatment time. The PEO layer resulted mainly composed by aluminum and zinc oxides and silicates. The corrosion resistance was remarkable increased in the samples with the PEO coating.

The Shimensi super-large tungsten polymetallic deposit is located in Late Jurassic- Early Cretaceous Porphyry-Skarn tungsten ore belt in the south Yangtze metallogenic belt. There are 3 types of mineralization: veinlet-disseminated type, thick quartze vein type and hydrothermal crypto-explosive breccia type. Based on geological studies, this paper presents new petrographic, microthermometric, laser Raman spectroscopic and hydrogen and oxygen isotope research of the fluid inclusions from the deposit. The results show that there are five different types of fluid inclusions: liquid-rich inclusions, vapor-rich inclusions, pure liquid inclusions, pure vapor inclusions, and fluid inclusions containing a solid crystal. The homogenization temperatures of the fluid inclusion range from 140℃-270℃, the salinities are 3%-5% NaCleq and the densities of ore-forming fluid range from 0.64 g/cm3 to 0.99 g/cm3. For the analyses of Laser Raman spectroscopic, the ore-forming fluids can be approximated by a Ca2+-Na+-SO42--Cl- fluid system with small amount of CO2, CH4 and N2. Otherwise, the datas of the pressure, pH and Eh show a fluid metallogenic environment of low pressure, weak acid and weak reduction. The values of the homogenization temperature in 3 types of orebodies suggest that the mineralization is characterized by the decrease of the temperature under the condition of the fluid immiscibility. The H-O isotope values are interpreted to indicate that the ore-forming fluids are mainly composed of magmatic water, and also the meteoric water was added with the process of the magma rising.

This study aimed to investigate the fatigue performance and interfacial strengthening mechanisms of Al6061-to-Cu dissimilar lap joints via electromagnetic pulse welding (EMPW). The load-bearing capacity of the joints at discharge voltages of 14 kV and 16 kV was superior to that of 12 kV. Furthermore, the fatigue life of the 14 kV joints was one order of magnitude higher compared to the 12 kV joints. SEM observation of the fatigue fracture surface revealed the presence of typical "tire-mark" fatigue striations only in the 14 kV joint, indicating higher ductility and the ability to withstand extended plastic deformation. Notably, ultra-fine nanocrystalline Al2Cu phase, amorphous phase, and numerous dislocations hindered EBSD acquisition in the transition zone. Nevertheless, dense low-angle grain boundaries (LAGBs) and refined grains were examined at the bonding interface. This suggests that the high-velocity collision caused severe plastic deformation and led to the formation of substructures. The interfacial strength was attributed not only to the "wave-like" or "inverted hook-like" diffusion layer but also to the presence of refined grains along the interface and nanocrystalline Al2Cu in the transition zone. Furthermore, the hybrid nanocrystalline-amorphous microstructure strengthened the joint by regulating the balance between strength and ductility.

Hierarchical tungsten oxide assemblies such as spindle-like, flowers with sharp petals, nanowires and regular hexagonal structures are successfully synthesized via a solvothermal reduction method by simply adjusting the reaction conditions. On the basis of the experimental results, it is determined that the reaction time significantly influences the phase transition, microstructure and photocatalytic activity of the prepared samples. The possible mechanisms for the phase transition and morphology evolution process have been systematically proposed. Moreover, the as-prepared products exhibit significant morphology-depended photocatalytic activity. The flower-like W18O49 prepared at 6 h possesses large specific surface area (150.1 m²g^-1), improved separation efficiency of electron-hole pairs and decreased electron-transfer resistance by the photoelectrochemical measurements. As a result, the flower-like W₁₈O₄₉ prepared at 6 h exhibits the highest photocatalytic activity for the degradation of Methyl orange aqueous solution. The radical trap experiments showed that the degradation of MO was driven mainly by the participation of h⁺ and •O²⁻ radicals.

A flow chart is presented depicting coupling in ocean-atmosphere system, initiated by solar decadal variability that involves El Niño Southern Oscillation (ENSO). Possible mechanisms for Canonic ENSO, Modoki ENSO and Canonic-Modoki ENSO are proposed considering their relevance to the decadal variation of Hadley, Walker circulation and mid-latitude jets. It also discusses subsequent teleconnections by ENSO on Indian Summer Monsoon (ISM) with a special emphasis on later two decades of the last century. Possible mechanisms relating to a disruption of the usual ENSO-ISM teleconnection for those decades are emphasised; the role of volcanos and the change in the sun- NAO (North Atlantic Oscillation) connection were attended. The regional Hadley circulation, via the NAO in the northern hemisphere and Indian Ocean Dipole in the southern hemisphere, during that period, may have a role in the change in ISM behaviour- which though captured in observation but missed by models. The representation of flow chart helps to improve understanding of various types of ENSO in both temporal as well as spatial scale. The overall study subsequently can benefit the modelling community by not only improved the representation of ENSO in models but also better representation of ISM teleconnection via regional Hadley cell.

Nowadays, Multi-needle electrospinning has used to be an efficient method for producing nanofiber membranes. But in the process, the fluctuation errors in electrospinning fluid flow rate have directly influence the membrane quality, which bringing instability and still have not been solved yet. For finding out the solution to the inaccurate flow control in multi-needle, it is necessary to develop a multi-stage flow runner spinneret for large-scale production of nanofiber membrane. At first, the paper uses the finite element software COMSOL to numerically simulate the polymer flow in the runner of spinneret. Based on it, the velocity field distribution curve was draw and the velocity instability coefficient of the polymer flow was attained, which are providing theoretical guidance for the optimal design of spinneret. Next, the response surface analysis method (RSM) was used to establish a regression model between the average diameter of the nanofiber membrane and the process parameters. Then, above regression model used to perform variance data processing between the average diameter and the process parameter configuration. After that, the 2D and 3D response surface profiles and the significance analysis were completed. Finally, the stability of the nanofibers production was improved, which attained the optimal adjustment of process configuration in multi-needle electrospinning.

The multifarious internal workings of organisms are difficult to reconcile with a single feature defining a state of ‘being alive’. Indeed, definitions of life rely on emergent properties (growth, capacity to evolve, agency) only symptomatic of intrinsic functioning. Empirical studies demonstrate that biomolecules including ratcheting/rotating enzymes, ribozymes and pigment molecules undergo repetitive conformation state changes driven by energy absorption, excitation and relaxation. They exhibit disparate structures, but govern processes relying on directional physical motion (DNA transcription, translation, ATP synthesis, cytoskeleton transport, photosynthetic resonance energy transfer) and share the principle of repetitive uniplanar conformation changes driven by thermodynamic gradients, producing dependable unidirectional motion: ‘heat engines’ exploiting thermodynamic disequilibria to perform work. Recognition that disparate biological molecules share a heat engine principle governing directional motion, working in self-regulating networks, allows a mechanistic definition: life is a self-regulating process whereby matter undergoes cyclic, uniplanar conformation state changes that convert thermodynamic disequilibria into directed motion, performing work that locally reduces entropy. ‘Living things’ are structures including autonomous networks of units operating on the heat engine principle. Death is loss of integrated heat engine function. These principles are independent of any specific chemical environment, and can be applied to other biospheres.

Microscopic vision plays an important role in automated micro-assembly. However, some uncertain factors in the assembly process, such as occlusion and stains can lead to the mistakes of feature extraction. Herein, to solve the problem, the deep learning techniques are introduced into the feature recognition tasks, focusing on the attention mechanism and visualizing CNNs for DL-based microscopic vision. The main contributions are summarized as follows: The CBAM attention mechanism is combined with the YOLOv5 algorithm to improve the accuracy and robustness of feature extraction. The micropart feature occlusion experiment results show that at 70% occlusion degree, YOLOV5-CBAM can reach 97.9% [email protected], which is 4.6% higher than the original one. Visualization analysis of DL-based model is conducted using Grad-CAM to make the decision result more transparent and avoid potential visual detection risks during assembly. The heatmap matching degree between GT area and high-light area is increased by 27.81% on average, which further verify the effectiveness of attention mechanism in micropart feature localization. Additionally, micropart surface stain and droplet quality classification models based on ResNet50 are trained to replace the manual sorting. The visual results are consistent with human eye discernment and judgement, confirming the reliability of parts and droplets sorting.

This article utilized electrodeposition technology to fabricate Zn and Zn-Y₂O₃-Al₂O₃ composite coatings on Q235 steel plates. The composite coatings were obtained by adding Y₂O₃/Al₂O₃ nanoparticles (0, 5, 10, and 15 g/L) to acidic chloride solutions. This study then examined the impact of these nanoparticles on the microstructure, morphology, microhardness, hydrophobicity, and corrosion resistance of the composite coatings. The results indicate that the addition of the nanoparticles increased the nucleation sites on the surface of the coating, thereby refining the grain size and reducing the roughness of the coating surface. When 10g/L of Y₂O₃ and 10g/L of Al₂O₃ nanoparticles were added, the hardness of the composite coating (369 Hv) was 2.49 times higher than that of the pure Zn coating (148 Hv), which was attributed to the dispersion strengthening and grain refinement effects of the nanoparticles. The corrosion resistance of the Zn and Zn-Y₂O₃-Al₂O₃ composite coatings was studied using linear sweep voltammetry and AC impedance spectroscopy. The addition of the nanoparticles improved the corrosion resistance of the composite coating, and the composite coating prepared in an electrolyte containing 10 g/L of Y₂O₃ and 10 g/L of Al₂O₃ nanoparticles exhibited the best corrosion resistance. Meanwhile, the composite coating exhibited good hydrophobicity, with a contact angle of 120.9°, 1.94 times that of the pure Zn coating (62.2°). The Zn-Y₂O₃-Al₂O₃ nanocomposite coating material has significant potential advantages in the field of steel corrosion.

The 70/30 copper–nickel alloy is mainly used in critical parts with more demanding conditions in marine settings. There is a need for innovative methods that offer fast production and cost-effectiveness to supplement current copper–nickel alloy manufacturing processes. In this study, we employ wire-arc additive manufacturing (WAAM) to fabricate the 70/30 copper–nickel alloy. The as-built microstructure is characterized by columnar grains with prominent dendrites and chemical segregation in the inter-dendritic area. The aspect ratio of the columnar grain increases with increasing travel speed (TS) at the same wire feed speed (WFS). This is in contrast to an equiaxed grain structure with a more random orientation of conventional sample. The sample built with a WFS of 8 m/min, TS of 1000 mm/min, and a track distance of 3.85 mm exhibits superior corrosion properties in the 3.5 wt% NaCl solution compared to the conventional one, as evidenced by a higher film resistance and breakdown potential, along with a lower passive current density of the WAAM sample. The corrosion morphology reveals the critical roles played by the nickel element unevenly distributed between the dendrite core and inter-dendritic area.

The study’s objective is to analyse the mechanical properties of steel pipe piles as a part of a trestle bridge subjected to five years of natural marine corrosion degradation. Sixteen tensile specimens were extracted from the steel pipe piles in the splash, tidal, and immersion zones. The experimental tensile test results are used to establish regression equations defining elastic modulus, yield strength, strain hardening index, and strength coefficient for the true stress-strain curves of the three regions. A non-linear time-dependent mathematical model is exploited to identify the corrosion degradation using the data from one single corrosion degradation measurement campaign. The analysis indicated that the splash zone experiences the most severe corrosion degradation, and there are progressive losses in the mechanical properties of each zone as the corrosion degradation progresses. The established relationships of the mechanical properties, as a function of the ratio of corroded plate thickness to the as-built one, can be used as a fast-engineering approach to identify the mechanical properties of severely corroded piles. The corrosion degradation allowance is also defined using the First Order Reliability Method, accounting for existing uncertainties covered by the partial safety factors. By examining the impact of marine corrosion on the mechanical properties of marine structures and developing predictive models to assess the corrosion’s effect on material strength and corrosion allowance, the study aims to improve offshore structures’ safety, design, and maintenance.

The development of Al-Ni alloys with a controlled microstructure has had a great impact on the field of study of aluminum-based alloys. In the present research, the influence of thermal parameters on the grain structures resulting from the directional solidification process of Al-Ni alloys with different alloy content has been studied. It has also been evaluated how different structures and the distribution of second phases influence the corrosion behavior and microhardness of alloys. The columnar-to-equiaxed transition (CET) was observed to occur when the temperature gradient in the melt decreased to values between 1.3 to 2.9 ° C/cm. In addition, a small increase in the microhardness values was observed as a function of the Ni-content. When the Ni-content increase, the resistance to polarization decreases for samples with equiaxed grain structure, throughout the range of compositions studied. Furthermore, the equiaxed grain structure presents higher resistance to polarization values than the columnar grain zone, for alloys with a composition equal to or lower than the eutectic composition.

This study aims to investigate the interfacial tension, emulsion stability, and the impact on oil displacement effectiveness of mixed systems containing nonionic surfactants and amphoteric surfactants at different ratios. To achieve this, three different emulsion stability formulations were prepared by mixing betaine and nonionic surfactants in ratios of 1:1, 3:2, and 3:1 respectively. By adjusting the proportions of betaine and nonionic surfactants, variations in interfacial tension and emulsion formation among the three mixed systems were studied to analyze the mechanism of interaction between betaine and nonionic surfactants and evaluate their effects on crude oil displacement and enhanced oil recovery in reservoirs. Subsequently, microscopic and macroscopic oil displacement experiments were conducted on the three mixed systems, along with experiments on emulsion flow resistance. The aim was to verify the oil displacement effectiveness of different mixed systems and further understand their potential applications in reservoirs. By comprehensively analyzing the experimental results, optimal ratios and conditions for the mixed systems were determined. The experimental results indicate that the emulsification system formed by mixing betaine and nonionic surfactants at a ratio of 3:1 achieves molecular synergies through electrostatic interactions and mixed adsorption with betaine, resulting in a compact arrangement of interface membranes and demonstrating a synergistic effect in reducing interfacial tension to an ultra-low value of 10 -4 mN/m. Additionally, as the proportion of betaine surfactant increases, the viscosity of the aqueous phase liquid film increases, the rate of thinning of the liquid film slows down, the rate of water release slows down, and the stability of the emulsion increases. Microscopic oil displacement experiments verified that the three mixed systems increase oil washing efficiency through low interfacial tension and emulsification stripping action, thereby increasing the oil displacement mechanism's coefficient. Emulsion flow resistance experiments demonstrated that as the proportion of betaine surfactant increases, the system exhibits better plugging ability. However, macroscopic oil displacement experiments revealed differences in compatibility between different emulsion stability solutions and rocks with different permeabilities. The mixed system of betaine and nonionic surfactants at a ratio of 3:1 exhibits the best emulsification plugging ability in rocks with a permeability of 109mD, while the 1:1 mixed system performs best in rocks with a permeability of 12mD. This holds significant theoretical and practical significance for reservoir development and enhanced production.

Cellular automata (CA) models have emerged as a valuable tool in corrosion management. This manuscript provides an overview of the application of cellular automata models in corrosion research, highlighting their benefits and contributions to understanding the complex nature of corrosion processes. Cellular automata models offer a computational approach to simulate corrosion behavior at the microscale, capturing the intricate interactions between electrochemical reactions, material properties, and environmental factors generating a new vision of predictive maintenance. It discusses the key features of cellular automata, such as the grid-based representation of the material surface, the definition of state variables, and the rules governing cell-state transitions. The ability to model local interactions and emergent global behavior makes cellular automata particularly suitable for simulating corrosion processes. Finally, cellular automata models offer a powerful and versatile approach to studying corrosion processes, expanding models that can continue to enhance our understanding of corrosion and contribute to the development of effective corrosion prevention and control strategies.

Addressing real-time aircraft target detection in microsatellite-based visible light remote sensing video imaging requires considering the limitations of imaging payload resolution, complex ground backgrounds, and the relative positional changes between the platform and aircraft. These factors lead to multi-scale variations in aircraft targets, making high-precision real-time detection of small targets in complex backgrounds a significant challenge for the detection algorithms. Hence, this paper introduces a real-time aircraft target detection algorithm for remote sensing imaging using an improved lightweight attention mechanism that relies on the YOLOv7 framework (SE-CBAM-YOLOv7). The proposed algorithm replaces the standard convolution (Conv) with a lightweight convolutional SEConv to reduce the computational parameters and accelerate the detection process of small aircraft targets, thus enhancing real-time onboard processing capabilities. Besides, the SEConv-based SPPCSPC (Spatial Pyramid Pooling and Connected Spatial Pyramid Convolution) module extracts image features. It improves detection accuracy while the feature fusion section integrates the CBAM hybrid attention network, forming the CBAMCAT module. Furthermore, it optimizes small aircraft target features in channel and spatial dimensions, improving the model's feature fusion capabilities. Experiments on public remote sensing datasets reveal the proposed SE-CBAM-YOLOv7 improves detection accuracy by 3% and mAP value by 4.2% compared to YOLOv7, significantly enhancing the detection capability for small-sized aircraft targets in satellite remote sensing imaging.

Our investigations show that electrochemical corrosion of copper is faster than electrochemical corrosion of aluminium at temperatures below 100oC. Literature data analysis shows that the Al atoms diffuse faster than the Cu atoms at temperatures higher than 475oC, Al rich intermetallic compounds (IMCs) are formed faster in the Cu-Al system, and the Kirkendall plane shifts toward Al side. Electrochemical corrosion occurs due to electric current and due to diffusion. An electronic devise working time, for example, depends on initial copper cover thickness on aluminium wire, connected to the electronic devise, temperature, and volume and dislocation pipe diffusion coefficients, so copper, iron, and aluminium electrochemical corrosion rates are investigated experimentally at room temperature and at temperature 100oC. Intrinsic diffusivities ratios of copper and aluminium at different temperatures and diffusion activation energies in the Cu-Al system are calculated by proposed here methods using literature experimental data. Dislocation pipe and volume diffusion activation energies of pure iron are calculated separately by earlier proposed method using literature experimental data. Aluminium dissolved into NaCl solution as the Al3+ ions at room temperature and at temperature 100oC, iron dissolved into NaCl solution as the Fe2+ (not Fe3+) ions at room temperature and at temperature 100oC, copper dissolved into NaCl solution as the Cu+ ions at room temperature and as the Cu+ and the Cu2+ ions at temperature 100oC. It is founded experimentally that copper corrosion is higher than aluminium corrosion, and ratio of electrochemical corrosion rates, kCu/kAl>1, decreases with temperature increasing, although iron electrochemical corrosion rate doesn’t depend on temperature below 100oC. It is obvious, because melting point of iron is more higher then melting point of copper or aluminium. It is calculated that copper electrochemical corrosion rate is approximately equal to aluminium electrochemical corrosion at temperature about 300oC, so copper can dissolve into NaCl solution mostly as the Cu2+ ions at temperature about 300oC. Ratio of intrinsic diffusivities, DCu/DAl <1, increases with temperature increasing, and intrinsic diffusivity of aluminium could be approximately equal to intrinsic diffusivity of copper at temperature about 460oC.

As one of the typical deposits in Sichuan-Yunnan-Guizhou Pb-Zn metallogenic province, the Daliangzi Pb-Zn deposit has a close genetic relation with the structural system of “black/fracture zone” formed under the action of NWW-approx. EW strike-slip structures in the metallogenic province, but the mechanism of rock and ore-controlling action of the structural system remains unclear. Based on detailed analysis of tectonite-mineralized alteration lithofacies of R1 “black/fracture zone”, the tectonite-mineralized alteration lithofacies zones can be divided into 4 types in succession outward from the Pb-Zn mineralization center, i.e., ① brecciated and stockwork-like Pb-Zn mineralization-complex breccia facies zone, ② stockwork-like Pb-Zn mineralization-simple breccia and cataclasite facies zone, ③ veined pyrite-sulfide-dolomitic cataclasite facies zone, and ④ fine-veined calcite-black carbonized dolomite facies zone; Cl- and SO42--rich high-temperature oxidizing ore-bearing fluid mixes with reducing fluid in Zone ① while migration and precipitation occur in Zone ④. With the evolution of ore-forming fluid, the homogenization temperature decreases from Zone ① to Zone ④, the salinity increases from Zone ① to Zone ② and then decreases to Zones ③ and ④, and the fluid density has little change on the whole; the contents of Zn, Pb, Cu, Ga, Ge, Cd, Ag, and other metallogenic elements, the Zn/Pb ratio, and the CaO/MgO mole ratio decrease gradually from Zone ① to Zone ④; and REE fractionation, calcilization, silicification, and pyritization enhance gradually from Zone ① to Zone ④. This series of changes are the product of diapirism (cryptoexplosion) of strike-slip structures and “black/fracture zone”, among which the second-order structures (F5, F100, and other faults) derived from NWW-approx. EW striking dextral shear-tension faults F1 and F15 control the brecciated and stockwork-like Pb-Zn mineralized complex breccia facies zones and the stockwork-like Pb-Zn mineralized simple breccia and cataclasite facies zones. Therefore, this paper establishes the zoning mode of tectonite-mineralized alteration lithofacies of “black/fracture zone” and proposes that Zones ① and ② are important prospecting criteria. conclusions.

In this paper, the mechanism of combined process of ion beam sputtering (IBS) and HF acid etching on the chemical structure defects of fused silica and its laser damage resistance perfor-mance were investigated. During the removal process of surface material, the sputtering effect causes lattice atoms to detach from their original positions, forming a large number of unsaturated structures on silica surface, which improves the chemical activity of Si and O atoms, accelerates the chemical reaction process between surface atoms and water molecules, increases the content of hydroxyl (OH-) groups in the shallow layer, and enhances the photothermal weak absorption intensity. However, the presence of OH- groups reduces the bonding strength of Si-O, destroys the spatial network structure of silica bulk, and reduces the mechanical strength of silica surface, resulting in a decrease in its laser damage resistance performance. The paper reveals for the first time the mechanism of IBS to change the structure characteristics of silica material, accelerate the surface hydroxylation process, and thereby reduces the laser damage resistance performance. This work provides technical guidance for effectively suppressing chemical structure defects on silica surface and improving laser damage resistance performance of optical components under high-flux laser irradiation.

In this paper we overview all analytical engineering solutions for corrosion problems in pressure vessels delivered over the past 60 years. We briefly detail strengths and weaknesses of existing approaches, thus demonstrating the need for novel uniform corrosion analysis methods for both current and new applications. To complement the review, we also present a new analytical model allowing to estimate the lifetime of pressured elastic vessels with mechanically assisted corrosion. Both internal/external pressure and internal/external corrosion are captured and dissolution driven corrosion is also considered. The readily implemented method improves existing analytical approaches and is shown to be effective for thin and thick shells, as well as various loading and corrosion intensity and geometrical conditions.

The acoustic emission (AE) technique was applied to monitor the pitting corrosion of carbon steel in NaHCO₃ + NaCl solutions. The open circuit potential (OCP) measurement and the corrosion morphology in-situ capturing using optical microscope were conducted during AE monitoring. The corrosion micromorphology was characterized with scanning electron microscope (SEM). The propagation behavior and AE features of natural pitting on carbon steel were investigated. After the performing of signal processing including pre-treatment, shape preserving interpolation and denoising for raw AE waveforms, three types of AE signals can be classified in the correlation diagrams of new waveform parameters. Finally, a 2D pattern recognition method was established to calculate the similarity of different continuous AE graphics, which is quite effective to distinguish the localized corrosion from uniform corrosion.

Petrochemical plants use on-stream inspection more often to detect and monitor the corrosion on the equipment and piping system. Compared to ultrasonic thickness gauging and pulse-echo A-scan, phased array corrosion mapping has better coverability and can scan a large area to detect general and localized corrosion. This paper's objective is to obtain documentary evidence on the accuracy of corrosion detection from 30°C to 250°C on A36 low-carbon steel by carrying out simulation experiments every 10°C steps. A minimum of three sets of phased array corrosion mapping data in each temperature were collected to study and evaluate the detectability. The data evidence could enhance the confidence level of the plant's end users to use the phased array mapping in the future during an inspection. The experiments were found to be insufficiently thorough despite addressing the initial concerns, leaving more area for discussion in further studies, such as expanding the investigation to thicker carbon steel, stainless steel, and wedge materials.

Worldwide the steel corrosion is one of the greatest deterioration problems for reinforced concrete structures. Comparing some literature experimental results with a complex FEM model, the present paper points out the principal aspects those characterize the static behavior of RC elements damaged by corrosion. Moreover, the non-dimensional abaci defined for some specific case studies finalized to the evaluation of the residual flexural strength of corroded elements highlight the dangerousness of the corrosion degradation if the failure of the element is governed by the steel

Conventional heat treatment is not capable of converting a sufficient amount of retained austenite into martensite in high-carbon or high-carbon and high-alloyed iron alloys. Cryogenic treatment induces the following alterations in the microstructures: (i) a considerable reduction in the retained austenite amount, (ii) formation of refined martensite coupled with an increased number of lattice defects, such as dislocations and twins, (iii) changes in the precipitation kinetics of nano-sized transient carbides during tempering, and (iv) an increase in the number of small globular carbides. These microstructural alterations are reflected in mechanical property improvements and better dimensional stability. A common consequence of cryogenic treatment is a significant increase in the wear resistance of steels. The current review deals with all the mentioned microstructural changes as well as the variations in strength, toughness, wear performance, and corrosion resistance for a variety of iron alloys, such as carburising steels, hot work tool steels, bearing and eutectoid steels, and high-carbon and high alloyed ledeburitic cold work tool steels.

Isothermal interrupted hot compression tests of 5754 aluminum were conducted on Gleeble-3500 thermo-mechanical simulator at temperature 350 °C and 450 °C, strain rate 0.1 s-1 and 1s−1. These tests simulated flat rolling to investigate how softening behaviors respond to controlled parameters, such as deformation temperature, strain rate and delay times. This data allowed the parameters for the hot rolling process to be optimized. The delay times during interrupted compression vary between 5s and 60s. The dynamic softening at each pass and metadynamic recrystallization at the intervals of deformation passes were analyzed in detail. 0.2% offset yield strength is applied to calculate the softening fraction undergoing metadynamic recrystallization. A kinetic model was developed to describe metadynamic recrystallization behaviors of the hot deformed 5754 aluminum alloy. Furthermore, the time constant for 50% recrystallization was expressed as functions related to the temperature and the strain rate. The experimental and calculated results were found to be in close agreement, which verified the developed model.

Two polyurethanes (PUs) were similarly synthesized by reacting a cycloaliphatic isocyanate with 1,4 butanediol and two polyols of different nature (polyester, polycarbonate diol) with molecular weights of 1000 Da. The PU made with polycarbonate diol polyol (YCD) was the only showing intrinsic self-healing at 20 °C. For assessing the mechanism of intrinsic self-healing of YCD, a structural characterization by molecular weights determination, infrared and X-ray photoelectronic spectroscopies, differential scanning calorimetry, X-ray diffraction, thermal gravimetric analysis and dynamic mechanical thermal analysis was carried out. It was concluded that the self-healing at 20 °C of YCD was due to non-covalent dynamic exchange interactions among the carbonate groups of the soft segments. Therefore, the chemical nature of the polyol played a key role in developing PUs with intrinsic self-healing at 20 °C.

Two austenitic stainless steel (ASS) plates, 304L and 316L, were cold-rolled (304R and 316R) with a 10 % reduction in thickness then subjected to laser welding. Cold-rolling caused a slight surface hardening and introduced residual tensile stress into the ASS plates. The susceptibility to stress corrosion cracking (SCC) of the welds (304RW and 316RW) was determined using the U-bend test pieces in a salt spray. To highlight the stress concentration at the weld’s fusion boundary (FB), the top weld reinforcement was not ground off before bending. Moreover, micro-shot peening (MSP) was performed to mitigate the SCC of the welds by imposing high residual compressive stress and forming a fine-grained structure. Cold-rolling increased the susceptibility of the 304R specimen to pitting corrosion (PTC) and intergranular (IG) microcracking. Moreover, PTC and SCC were found more often at the FBs of the 304RW. The corrosion pits of the peened 304RW (304RWSP) were finer but greater in amount than the un-peened one. The results also indicated that the 316L ASS welds with MSP was resistant to the incidence of PTC and SCC in a salt spray. The better reliability and longer service life of dry storage canister could be achieved by using 316L ASS for construction and application of MSP on it.

Porous metals possess low bulk density, large specific strength, high stiffness and special thermal, electromagnetic and acoustic conductivity, so that porous metals are widely used in filtration and separation, flame retardant explosion-proof, biomedical application, etc. Compared with its corresponding dense metal, the presence of porous structures also leads to different corrosive performances of porous metal. So, some researches have utilized weight loss method, electrochemical impedance to evaluate porous metals’ corrosion behavior; however, the influence of pore structure on metal corrosion is still controversial, and present methods used for analyses of porous metals’ corrosion are statistical averages of the corrosion behavior of the entire porous material, which cannot accurately reflect the corrosion behavior inside the pore structure. Herein, we prepare porous copper samples with 0, 24, 72, 96 pores using mechanical process, and employ scanning kelvin probe combined with electrochemical polarization curve and impedance spectroscopy to test the corrosion performance of the porous copper in static and dynamic NaCl solution. The relevant results indicate that in static solution, the corrosion resistance of samples gradually increases with the rise of the number of pores. By contrast, the sample with 24 pores exhibits more susceptible to corrosion than the sample without pore.

Concrete is the most utilized construction material worldwide. In the marine environment, it is subject to chemical degradation through reactions with chloride (the most important ion), sulfate and magnesium ions in seawater and to biodeterioration resulting from biological (initially microbiological) activities, principally acid production. These two types of corrosion are reviewed and the failure of attempts to predict the degree of deterioration resulting from each is noted. Chemical (abiotic) corrosion is greatest in the splash zone of coastal constructions, while phenomenological evidence suggests that biodeterioration is greatest in tidal zones. There have been no comparative experiments to determine the rates and types of microbial biofilm formation in these zones. Both chemical and microbiological concrete deterioration are complex and have not been successfully modeled. The interaction between abiotic corrosion and biofilm formation is considered. EPS can maintain surface hydration, potentially reducing abiotic corrosion. The early marine biofilm contains relatively specific bacterial colonizers, including cyanobacteria and proteobacteria; these change over time, producing a generic concrete biofilm, but adhesion of microorganisms to concrete in the oceans is little investigated. The colonization of artificial reefs is briefly discussed. Concrete appears to be a relatively prescriptive substrate, with modifications necessary to increase colonization for the required goal of increasing biological diversity.

Inclusions in steels and alloys are known as factors that could lower deformation, mechanical, corrosion and other properties. Study of inclusions in nickel based alloys is important since these materials could suffer from corrosion degradation in harsh operational conditions, where inclusions could lead to a pitting initiation. For estimation of a harmful effect of different inclusions on corrosion resistance of Ni-based alloys, inclusion characteristics (such as composition, morphology, size, number and location) on film filter and dissolution of metal matrix around different inclusions on surfaces of metal samples after electrolytic extraction (EE) were investigated in two samples of industrial Ni-based alloys (alloy 718 and EP718). It was found that both Ni-based alloys have various inclusions: carbides (large size NbTi-C and small multicomponent carbides), nitrides TiNb-N and sulfides (TiNb-S in EP718 alloy). The higher harmful effect on corrosion resistance of metal was detected around sulfides and small carbides containing Mo, W, Cr. Dissolution effect was also observed around large carbides and nitrides, especially around inclusions having size more than 10 µm. Moreover, the dissolution of metal matrix around inclusions and clusters located on the grain boundaries is 2.1-2.7 times larger compared to that for those inclusions inside of grains of the given alloy samples.

1) Background: The objective was to evaluate the corrosion resistance of different commercially pure ultrafine-grained (UFG) titanium and its alloys with acid etched surface processed by equal-channel angular pressing (ECAP); 2) Methods: Coarse-grained and UFG titanium samples were investigated using polarization resistance technique. Surface characteristics of the native oxidized layer were evaluated by TEM and XRD. Electrochemical tests were under physiological electrolyte at a rate of 1 and 10 mV/s. Weight loss tests were performed after immersion into HCl solution for up to 3 years; 3) Results: UFG titanium was less susceptible to corrosion which was identified under lower rates and at higher polarization resistance than its coarse grain counterparts. Titanium Grade 2 and Grade 4 demonstrated similar corrosion susceptibility. Titanium Grade 5 revealed a thin and tightly adhered native oxide layer with adequate corrosion resistance; 4) Conclusions: ECAP process imposed a more compact and adhered oxidized layer. Surface etching techniques delivered a thicker native TiO₂ layer, being both grain refinement and surface etching techniques responsible for the improved corrosion resistance of Titanium samples under physiological environment after 3 years of observation.

In this work, we investigated the effects of heat treatment on the microstructure, hydrogen storage characteristics and corrosion rate of a Ti₃₄V₄₀Cr₂₄Fe₂ alloy. The arc melted alloy was divided into three samples, two of which were separately quartz-sealed under vacuum and heated to 1000 °C for 1 h; one of these samples was quenched and the other furnace cooled to ambient temperature. The crystal structures of the samples were studied via X-ray diffractometry and scanning electron microscopy. Absorption/desorption characteristics were investigated using a Sievert apparatus. Potentiostat corrosion tests on the alloys were performed using an AutoLab^® corrosion test apparatus and electrochemical cell. All samples exhibited a mixture of body-center-cubic (BCC) and Laves phase structures. The corrosion rate, maximum absorption, and useful capacities increased after both heat treatments. The annealed sample had the highest absorption and reversible capacity. The plateau pressure of the as-cast alloy increased after quenching. The corrosion rate increased from 0.0004 mm/y in as-cast sample to 0.0009 mm/y after annealing and 0.0017 mm/y after quenching, due to a decrease in the Cr-content of the C14 phase.

It is important to realize the transformation behavior of wüstite because it greatly affects the final structure of the oxide layer and the surface quality of the steel products. In the present study, the transformation behaviors of the wüstite layer are examined under nearly-oxygen-free conditions, to simulate the cooling processes after the hot rolled strip is coiled. As the single phase wüstite was prepared at 950˚C, the 460˚C transformed oxide layer was composed of a mixture of iron and magnetite formed through eutectoid reactions. For the 750˚C-fabricated wüstite, only magnetite was observed after transformation, without iron precipitates and residual wüstite. It is speculated that the unusual transformation behavior of the low-temperature-made wüstite results from the pseudo-structural intermediate phase transformation between wüstite and magnetite. This pseudo-structure is a pre-transformed wüstite and of various concentration of ferrous ion, which is determined by the fabrication conditions. During the hot strip mill process, the so-called wet scale, wüstite, is produced continuously from finish mill to laminar flow sections and ended at 570˚C. Consequently, the final eutectoid transformation below 570˚C is dominantly controlled by the surface temperature ranged from 750˚C to 950˚C for low carbon steel.

The nickel-chromium-molybdenum alloy 625 exhibits an excellent combination of mechanical properties and corrosion resistance. However, the high temperature plastic deformation process and the heat treatment represent critical aspects and the adoption of non-optimal parameters can result in excessive grain coarsening and loss in mechanical strength. This detrimental behavior is worsened by the presence of a narrow region of temperatures and strain rates for complete recrystallization and the absence of phase transformation temperatures. In this alloy, the presence of sufficient amounts of niobium, titanium and aluminum permits slow age-hardening response upon single-aging treatments. Therefore, when the soft- or solution-annealed condition is associated with insufficient mechanical properties, this potentiality can be exploited to improve the mechanical strength and prevent waste of material and resources. Since the precipitation kinetic of the hardening γ^'' phase can be accelerated by prior nucleation treatment, different time-temperature combinations of double aging at 732 °C and 621 °C are investigated to reduce the overall heat treatment time. However, the simultaneous formation of Cr-rich carbides can dramatically affect the intergranular corrosion resistance. For this reason, a performance map is developed to compare all the tested conditions and identify the best compromise in terms of mechanical strength and corrosion rate.

The corrosion resistance of two cast CoCr based alloys, with different amounts of chromium and with different alloying elements in the bulk composition of the alloy, was assessed. Herewith, we investigated the corrosion behavior of Co21Cr8Mo7W and Co29Cr7W by open circuit potential (OCP), potentiodynamic polarization (PP) and electrochemical impedance spectroscopy (EIS) in 0.1 M phosphate buffer solution (PBS) at 37°C for long time immersion. After 1000 hours of immersion, the corrosion current density (icor), estimated from anodic polarization tests, is lower for Co21Cr8Mo7W (i.e. 49 nA cm-2) alloy compared to Co29Cr7W alloy (180 nA cm-2). As regards the corrosion potential (Ecor), a nobler value was observed for Co21Cr8Mo7W (i.e. -59 mV vs. Ag/AgCl) compared to Co29Cr7W (i.e. -114 mV vs. Ag/AgCl). These findings suggest a better corrosion resistance of the film formed on the alloy containing lower amount of Cr and two alloying elements, namely Mo and W. These results are promising ones in terms of medical applications because they open new strategies in obtaining alloys with lower content of chromium and with higher protective properties against corrosion attack.

Activated Corrosion Products (ACPs) formation and deposition pose a critical safety issue for nuclear fusion reactors. The working fluid transports the ACPs towards regions accessible to worker personnel. Predicting ACPs formation deposition and transport is fundamental for source term identification, reduction of radiation exposure assessment, maintenance plan definition, design optimization, and waste management. The code OSCAR-Fusion has been developed by the CEA (France) to evaluate the ACPs generation and transport in closed water-cooled loops for fusion application. This work aims at assessing the impact of water chemistry on the transport, precipitation, and deposition of corrosion products for the EU-DEMO divertor Plasma Facing Unit Primary Heat Transfer System. Sensitivity analyses and uncertainty quantification are needed due to the multi-physics phenomena involved in ACPs formation and transport. The OSCAR-Fusion/RAVEN code coupling developed by the Sapienza University of Rome and ENEA has been used. This work presents the perturbation results of different parameters chosen for a closed water-cooled loop considering a continuous scenario of 1888 days. The aim of this work is to assess the variation of build-up of ACPs, perturbing the alkalizing agent concentration into the coolant and the corrosion and release rates of different materials.

The corrosion morphology in grade 2205 duplex stainless steel wire has been studied to understand the nature of pitting and the causes of the ferrite phase's selective corrosion in acidic NaCl solution. It is shown that the corrosion mechanism is always pitting, which either manifests lacy cover perforation or densely-arrayed selective cavities developing on the ferrite phase. Pits with a lacy metal cover form in concentrated chloride solutions, whereas the ferrite phase's selective corrosion develops in diluted electrolytes, showing dependency on the chloride-ion concentration. The pit perforation is probabilistic and occurs on both austenite and ferrite grains. The lacy metal covers collapse in concentrated solutions but remain intact in diluted electrolytes. The collapse of the lacy metal cover happens due to hydrogen embrittlement. Pit evolution is deterministic and occurs selectively in the ferrite phase in light chloride solutions.

An analysis of the physical and chemical phenomena accompanying the electrical discharges was carried out, principal factors inactivating microorganisms is studied. Characteristic factors of an electric discharge in cavitation mode providing a synergistic effect when disinfecting water with a discharge and chemical reagents are identified in order of importance. As a result of the integral action of cavitation, the inactivation of bacteria is intensified both due to the emergence of chem-ically active particles and due to local shock waves, acoustic currents and ultraviolet radiation in the area of cavitating bubbles. The similarity of cavitation processes in water systems implemented by underwater electric discharges and with the ultrasound has been experimentally proved. The main advantage of electric discharge cavitation in comparison with ultrasonic one is the wide band of ultrasonic frequencies of radiation inherent in electric discharge, high intensity and power of cav-itation processes, and, accordingly, the possibility of a significant increase in the volume of the disinfected liquid. The study enable better understanding and prediction of the effects that occur during a high-voltage underwater electrical discharge and have a bactericidal effect.

Asymmetric lithium salts, such as Lithium (difluoromethanesulfonyl)(trifluoromethanesulfonyl)imide (LiDFTFSI), have been demonstrated to surpass traditional symmetric lithium salts with improved Li+ conductivity and the capacity to generate stable solid electrolyte interphase (SEI) while maintaining compatibility with aluminum (Al0) current collector. However, the intrinsic reductive mechanism through which LiDFTFSI influences battery performance remains unclear and under debate. Herein, the detailed SEI reactions of LiDFTFSI-based electrolytes were investigated by combining density functional theory and molecular dynamics, aiming to clarify the formation process and atomic structure of SEI. Our results show that asymmetric DFTFSI– weakens the interaction between carbonate solvents and Li+, and substantially alter the solvation structure, exhibiting a well-balanced coordination capacity to bis(trifluoromethanesulfonyl)imide (TFSI–). Nanoseconds hybrid molecular dynamics simulation further reveals that the preferential decomposition of LiDFTFSI produces sufficient LiF and Li2O to facilitate a robust SEI. Moreover, the abundant F– generated from LiDFTFSI decomposition accumulates on the Al surface and subsequently combines with Al3+ from the current collector to form AlF3, potentially inhibiting corrosion of the current collector. Overall, these findings elucidate how LiDFTFSI regulates the solvation sheath and SEI structure, advancing the development of high-performance electrolytes compatible with current collector.

Diatomite (DME) consists of natural ordered porous structures that are excellent candidates as microcontainers. However, to the best of our knowledge, the application of DME loaded with corrosion inhibitors in anti-corrosion coatings has not hitherto been reported. In this study, DME has been used as a source of microcontainers to load benzotriazole (BTA) inhibitor by an immersion method. In order to prevent unwanted early release of the small molecule BTA inhibitor from the DME microcontainers, inspired by the adhesion characteristics of catechol and amine in mussel adhesion protein, polydopamine (PDA) was coated on their surfaces to generate BTA@DME/PDA microcapsules. Because of the depolymerization characteristics of PDA at low pH, the synthesize microcapsules showed a controllable release function. The SEM morphology, chemical structure, and loading capacity of the synthesized BTA@DME/PDA microcapsules were characterized. The corrosion resistances of epoxy coatings with different contents of BTA@DME/PDA microcapsules were compared by saline immersion and electrochemical impedance tests. A scratched coating with 5wt.% BTA@DME/PDA microcapsules showed the best anti-corrosion effect.

This research investigated high-temperature corrosion (500 °C) of Cr-Mo steel processed using water jet peening or multifunction cavitation (MFC), and the suitability of such steel for high-temperature boilers and reaction vessels. High-temperature corrosion was induced using an embedment test and a coating test using sulfide-type K2SO4-Na2SO4 powder. To measure the relaxation of the residual stress due to the decrease in work hardening caused by an increase in specimen temperature and the difference in thermal shrinkage between the surface and interior of the specimen, a thermal cycling test was conducted. For the MFC-processed specimen, the oxide film that formed on the surface suppressed mass loss, prevented crack formation, and reduced the compressive residual stress caused by high-temperature corrosion. MFC-processed Cr-Mo steel is thus suitable for a high-temperature corrosion environment.

Grain trade plays a pivotal role in international trade, serving not only as a primary component of the global agricultural market but also as a crucial factor in ensuring global food security and price stability. This study utilizes panel data from Russia, one of the largest players in the grain market, to investigate the determinants of cereal exports. The results of the gravity model estimation reveal a positive impact of demand factors, population differences, and the level of economic openness of importing countries, while distance and tariffs exert a negative influence on exports. The findings also indicate that Russia possesses significant untapped potential for cereal export growth, which has only increased in the context of geopolitical instability. The paper identifies regions with potential for export expansion and outlines the conditions necessary for realizing this potential. The results of this study contribute to the development of evidence-based policies aimed at enhancing the sustainability of regional export flows in global systems.

Cordycepin has good antitumor activity, but its clinical application is limited due to the easy deamination of N6 in structure. In this study, a large lipopolysis group was introduced at the cordycepin N6 to improve the problem, Cordycepin derivatives(3a-4c) were synthesized, and biological evaluation of compounds were studied. In the study, the vitro antitumor activity of the compounds against MCF7 cells, HepG2 cells and SGC-7901 cells was evaluated by MTT assay. In the results, compound 4a showed the most obvious inhibitory effect on MCF7 cells with IC50 value of 27.566±0.52 μM, which was much lower than cordycepin. Compound 4a showed high selectivity between MCF7 and normal MCF-10A cells. Further biological evaluation showed that compound 4a promoted apoptosis and blocked the cell cycle in G0/G1 phase. Then, Western Blot was used to detect related apoptotic proteins. It was found that Compound 4a could down-regulate the expression of Bcl-2 protein and up-regulate the expression of p53, Bax, Caspase-3, and Caspase-9 proteins. The mitochondrial membrane potential decreased continuously and the positive expression rate decreased. It was speculated that compound 4a induced the apoptosis of MCF7 cells through the mitochondrial pathway.

Biofilms are usually defined as surface-associated microbial communities, surrounded by an extracellular polymeric substance matrix. There are three major steps that are observed in biofilm formation: initial attachment events, microcolony formation and construction of mushroom-like structure with secretion of extracelluar polymeric substances. These substances can be considered a mechanism to protect the bacterial community from external insults.Biofilms, significantly increase the ability of the pathogen to evade both host defenses and antibiotics and they are being implicated in the pathogenesis and also clinical manifestation of several infections. They cause a variety of persistent infections, such as native valve endocarditis, osteomyelitis, dental caries, middle ear infections, ocular implant infections, urinary tract infections and cystic fibrosis. Established biofilms can tolerate antimicrobial agents at concentrations of 10–1000-times that needed to kill genetically equivalent planktonic bacteria, and are also resistant to phagocytosis, making biofilms extremely difficult to eradicate from living hosts. Consequently, biofilm-related infections that appear to respond to a therapeutic course of antibiotics may relapse weeks or even months later, making surgical removal and replacement of the infected tissue or medical device a frequent and unfortunate necessity.Several pathogens associated with chronic infections, including Pseudomonas aeruginosa in cystic fibrosis pneumonia, Haemophilus influenzae and Streptococcus pneumoniae in chronic otitis media and Enteropathogenic Escherichia coli in recurrent urinary tract infections, are linked to biofilm formation.

Focusing on the problem of identifying and classifying aero-engine models, this paper measures the infrared spectrum data of aero-engine hot jets using a telemetry Fourier transform infrared spectrometer. Simultaneously, infrared spectral data sets with the six different types of aero-engines are created. For the purpose of classifying and identifying infrared spectral data, a CNN architecture based on the continuous wavelet transform peak seeking attention mechanism (CWT-AM-CNN) is suggested. This method calculates the peak value of middle wave band by continuous wavelet transform, and the peak data is extracted by the statistics of the wave number locations with high frequency. Attention mechanism is used for the peak data, and the attention mechanism is weighted to the feature map of the feature extraction block. The training set, vali-dation set and prediction set are divided in the ratio of 8:1:1 for the infrared spectral data sets. For three different data sets, CWT-AM-CNN proposed in this paper is compared with the classical classifier algorithm based on CO2 feature vector and the popular AE, RNN and LSTM spectral processing networks. The prediction accuracy of the proposed algorithm in the three data sets is as high as 97%, and the lightweight network structure design not only guarantees high precision, but also has a fast running speed, which can realize the rapid and high-precision classification of the infrared spectral data of the aero-engine hot jets.

Marked changes in temperature, pH, dissolved oxygen (DO) content, and nutrient content typically occur in marine thermoclines, which are key factors that affect the corrosion of metals. Offshore platforms have required marine metals to be exposed to deep-sea environments and have thus increased their penetration into the marine thermocline. This study investigates the galvanic corrosion of E690 steel in a marine thermocline using a simulated marine thermocline (SMT). Specifically, the corrosion of E690 steel was analyzed using the wire beam electrode (WBE) technique, linear polarization (LP), corrosion morphology, and weight loss measurement. Results indicated that the SMT had a stable multilayer structure, and the variations of temperature, DO, pH and nutrient concentration in the SMT were similar to those in the natural marine thermocline. Galvanic corrosion occurred after the intrusion of E690 steel into the marine thermocline. The driver of galvanic corrosion was the of E690 steel at various depths of the marine thermocline. The Ecorr of E690 steel was influenced by the temperature, pH and DO of seawater, and the order was DO >> T > pH. The continuous reduction of Ecorr with depth contributed to the large-scale galvanic corrosion, and the oscillation variation of Ecorr with depth was the reason for small-scale galvanic corrosion. The primary anodic regions of galvanic corrosion were located in the area with the fastest temperature variation in the thermocline. The proportion of galvanic corrosion in the average corrosion rate could increase up to approximately 80% in the stable anodic region. There were many deep corrosion pits in the long-term and stable anodic region of galvanic corrosion.

Corrosion is considered as one of the main factors in the structural performance deterioration of steel members. In this study, experimental and numerical methods were used to assess the reduction in compressive strength of short tubular steel columns with local corrosion damage. The corrosion damage was varied with different depths (0, 1.5, 2, 3, 4, 4.5, and 6 mm), height (0, 20, 40, 60, 80, 100, 120, 140, 160, and 180 mm), circumference (0, 90, 180, 270, and 360°), and location along the column. A parametric numerical study was performed to establish a correlation between the residual compressive strength and the severity of corrosion damage. The results showed that as the corrosion depth, height and circumference increased, the compressive strength decreased linearly. As for the corrosion height, the residual compressive strength became constant after decreasing linearly when the corrosion height was greater than the half-wavelength of buckling of the short columns. An equation is presented to evaluate the residual compressive strength of short columns with local corrosion wherein the volume of the corrosion damage was used as a reduction factor in calculating the compressive strength. The percentage error using the presented equation was found to be within 11.4%.

Metal corrosion poses a significant challenge for industries by decreasing the lifespan of materials and escalat-ing maintenance and replacement costs. This study is critically important as it assesses the corrosion resistance properties of annealed steel wire electrodes coated with manganese, employing chronoamperometry and linear voltammetry techniques. The electrodes were immersed in an electrolyte solution and subjected to chronoam-perometry at various voltages (-0.55 V, -0.60 V, and -0.70 V) and durations (60 seconds and 1800 seconds). Sub-sequently, linear voltammetry was performed over a potential range from -0.8 V to 0.8 V to generate Tafel plots. The Butler-Volmer equation was applied to the data obtained to determine the corrosion current density. The re-sults indicate that the optimal conditions for forming a highly effective protective manganese layer occur at a potential of -0.70 V for 1800 seconds. Under these conditions, the electrodes exhibited superior corrosion re-sistance. The study also revealed that shorter durations and less negative potentials led to less effective manga-nese coatings, with higher corrosion rates and reduced stability. These findings are significant for developing ef-ficient corrosion protection methods in industrial and research applications, providing clear parameters for op-timizing the manganese electrodeposition process on annealed steel.

MoS2 lithium-based grease is suitable for lubrication protection between bearings at high temperatures and loads due to its excellent tribological properties. However, there is little research on the influence of different addition methods of MoS2 additive on the tribology and corrosion properties of lithium grease. In this work, vegetable oil with low toxicity, high biodegradation rate, and low cost was selected as the base oil, lithium 12-hydroxystearate as the thickener, and MoS2 as the additive. The effects of different adding modes of MoS2 on the tribology and corrosion properties of lithium grease were studied. The experimental results showed that adding 0.01wt% MoS2 before thickening was more conducive to improving the tribological properties of lithium grease. The average friction coefficient was 0.034, and the average spot diameter was reduced by 0.16mm. After grinding and adding 0.01wt% MoS2, the corrosion inhibition efficiency of the steel sheet was as high as 96.97%. The main reason was that the longer stirring and grinding were conducive to the uniform distribution of MoS2 in the grease, and the protective film formed by MoS2 and GCr15-bearing steel improved the lubrication performance and corrosion inhibition performance of the friction system.

Although 4Ce4YSZ has high corrosion resistance, it faces challenges concerning sinterability and ionic conductivity. Therefore, we studied destabilization behavior caused by corrosion and oxygen vacancy ordering according to ZnO doping. The powders of (4Ce4YSZ)1-x(ZnO)x (x=0.5, 1, 2, 4 mol%) were synthesized through the sol-gel method. With the addition of ZnO, the cubic phase increased, and secondary phases were not observed. The (111) peak showed a higher angle shift in ZnO-doped 4Ce4YSZ compared to 4Ce4YSZ, and TEM-SAED revealed a reduction in the spacing of the (011)t plane, suggesting lattice contraction due to the substitution of the smaller Zn2+ (60 Å) for Zr4+ (84 Å) in the lattice. The local atomic structure analysis was conducted using EXAFS to investigate the oxygen vacancy ordering behavior. Zr K-edge Fourier-transform data revealed a decrease in the Zr-O1 peak intensity with an increasing amount o ZnO doping, indicating an increase in oxygen vacancies. The Zr-O1 peak position shifted to the right, leading to an increase in the Zr-O1 interatomic distance. In the Y K-edge Fourier-transform data, the Y-O1 peak intensity did not decrease, and there was little variation in the Y-O1 interatomic distance. These results suggest that the oxygen vacancies formed due to ZnO doping are located in the neighboring oxygen shell of Zn, rather than in the neighboring oxygen shells of Y and Zr. Impedance measurements were conducted to measure the conductivity, and as the amount of ZnO doping increased, the total conductivity increased, while the activation energy decreased. The increase in oxygen vacancies by ZnO doping contributed to the enhancement of conductivity and it is considered that these created oxygen vacancies did not interact with Zn2+ and did not form defect associations. Fluoride-based molten salts were introduced to the specimens to assess corrosion behavior in a molten salt environment. Yttrium depletion layers (YDLs) were formed on the surfaces of all specimens due to the leaching of yttrium. However, Ce remained relatively stable at the interface according to EDS line scans, suggesting a reduction in the phase transformation (cubic, tetragonal to monoclinic) typically associated with yttrium leaching in YSZ.

Molten LiCl-KCl salt and liquid cadmium are proposed as the electrolyte and the reactive cathode for the electrorefining of spent nuclear fuels. Corrosion testing of existing alloys is mandatory to ensure the service life of the electrorefiner vessel and electrode assemblies. Haynes C276, Inconel 600, AISI 316L stainless steel, and 42CrMo low alloy steel were exposed to LiCl-KCl melt at 500°C for 500 h in an argon atmosphere. All alloys suffered from dissolution attacks with the presence of oxide islands or porous oxide layer on the surface. AISI 316L, T91 steel and tungsten specimens were also submitted to corrosion tests in liquid cadmium at 500°C for 120 h. Corrosion of AISI 316L and T91 stainless steel were predominated by chemical oxidation with additional severe Ni dealloying occurred on AISI 316L. Tungsten only suffered from dissolution attack in comparison.

Zn–Ni plating is indispensable in various industries because of its high corrosion resistance. However, Ni has been reported to trigger allergies; thus, an alternative Ni-free plating is desired. Zn–Fe plating is considered to be a promising candidate, albeit its corrosion resistance still needs to be improved. The corrosion resistance of Zn–Fe plating is expected to increase by the addition of Mo as the third alloying element as it is more noble than Zn and Fe. In this study, Zn–Fe–Mo plating with a corrosion resistance nearly equivalent to that of the Zn–Ni plating was fabricated. Zn–Fe–Mo plating was electrically deposited from continuously agitated plating baths prepared by mixing ZnSO₄, FeSO₄, Na₂MoO₄, Na₃C₆H₅O₇, and Na₂SO₄ using Fe or Ni plates as the substrate. The surface morphology, composition, crystal phase, and electronic state of Mo of the platings were investigated by SEM-EDS, XRD, and XPS. The anti-corrosion performance was evaluated by Tafel extrapolation method. Formation of plating comprising a Mo containing alloy phase was found to be crucial for improving corrosion resistance. The Zn–Fe–Mo plating demonstrates promise for replacing anti-corrosion Zn–Ni platings.

The effects of environmental media on the corrosion fatigue fracture behavior of 25CrMo steel were investigated. The media include air, and a 3.5 wt.% and a 5.0 wt.% NaCl solutions. Experimental results indicate that the media induces the initiation of corrosion fatigue cracks at multiple sites. The multi-cracking sites cause the changes in the crack growth directions, the crack growth rate during the coupling action of the media and the stress amplitude. The coupling effects are important for engineering applications and research. The probability and predictions of the corrosion fatigue characteristic life can be estimated using the 3-parameter Weibull distribution function.

The study is devoted to the issues of mathematical modeling and simulating the sport differential mechanism (DM) with controllable torque redistribution. The issue is caused by the elaboration of ADAS systems with the automated torque vectoring for transmissions of all-wheel-drive (AWD) vehicles and the inclusion of such devices in the combined autonomous vehicle trajectory control scheme. At the article's beginning, the use of devices for redistributing traction forces is reasoned by analyzing the curvilinear vehicle motion, where they could ensure the accuracy of vehicle steerability. The literature review highlights modern developments in the field of modeling and researching such DMs. Considering the vehicle turn with a minimum radius, the conditions corresponding to passing greater torque over the outrunning rear axle are determined. All the mechanism's components and loads acting between them are described in detail. To form an original method of mathematical description of the mechanism functioning, the system of differential equations, systems of kinematic and force connections are considered separately. The article details the mathematical approach to generalize the way for automating the equation compilation for rotational mechanical systems such as vehicle transmissions. In the simulation section, a Simulink model reflecting the functional components and calculation procedures is presented. A series of testing and simulations on the DM operation with forcible torque distribution is carried out. Modeling data are presented, and the analysis of simulation results is performed. In the completion, conclusions are made regarding the scope and use of this model and the prospects for further developing the method proposed to automate the formation of equation systems.