Directed energy deposition (DED) parameters were determined for near-β alloy Ti-55511 by employing statistical design of experiments (DOE) methods. Parameters resulting in fully dense freeform deposits were identified using two sequential DOEs. Single laser tracks were printed with several laser power, traverse rate, and powder feed rate settings in an initial DOE to identify promising build parameters. Capture efficiency and effective deposition rate were used to characterize and rank the single track deposits. The best parameters were then used to print solid cube with various X-Y and Z-overlaps (different hatch spacing, HS, and layer thickness, ZS) in a second DOE. Suitable deposition parameters were selected based on cube density and microstructure and were used to fabricate larger tensile samples for mechanical testing. Multiple parameter sets were found to provide dense Ti-55511 deposits with acceptable mechanical properties and parametric models showed statistical significance.

Core-shell structured magnetic nanoparticles combine hard and a soft phases to improve energy efficiency. The mutual interaction of the two phases can lead to the exchange spring effect leading to higher magnetic energy. In this regard, synthesis of Nd2Fe14B based core-shell structured powders have proven to be elusive due to the relatively reactive nature of this phase. In this study, a process has been established for successfully coating the surface of Nd2Fe14B powders with FeCo layer using galvanic displacement method. Initially, a binary phase magnetic powder was synthesized containing Nd2Fe14B and Nd2Fe17 phase. Subsequently, the powders were coated using a Co precursor at 303 K. During coating the metastable Nd2Fe17 phase was dissolved and the Fe ions were released into the solution. Subsequently, the Fe ions deposited together with the Co ions on the surface of Nd2Fe14B powder to form a FeCo shell. The deposited layer thickness and composition was confirmed using TEM analysis.

With the rising cost of animal feed protein, finding affordable and effective substitutes is crucial. Walnut kernel cake, a polyphenols, fiber, protein and fat-rich byproduct of walnut oil extraction, has been underexplored as a potential protein replacement in pig feed. In this study, we found that feeding large Diqing Tibetan pigs walnut kernel cake promoted adipose deposition and improved pork quality during pig growth. Transcriptome analysis revealed the upregulation of genes ANGPTL8, CCNP, ETV4, and TRIB3, associated with adipose deposition. Pathway analysis highlighted enrichment in adipose-deposition-related pathways, including PPAR, Insulin, PI3K-Akt, Wnt, and MAPK signaling. Further analysis identified DEGs (differentially expressed genes) positively correlated with adipose-related traits, such as PER2 and PTGES. Single-cell transcriptome data pointed to the specific expression of CD248 and PTGES in adipocyte progenitor/stem cells (APSCs), pivotal for adipocyte differentiation and adipose deposition regulation. This study demonstrates walnut kernel cake's potential to substitute soybean cake in pig feed, providing high-quality protein and promoting adipose deposition. It offers insights into feed protein replacement, human functional food, fat metabolism, and related diseases, with marker genes and pathways supporting pig breeding and pork quality improvement.

The wide application of graphene in the industry requires the direct growth of graphene films on silicon substrates. In this study, we find a possible technique to meet the requirement above. Multilayer graphene thin films (MLG) are grown without a catalyst on Si/SiO2 by pulsed laser deposition (PLD). It was found that the minimum number of laser pulses that are required to produce fully covered (uninterrupted) samples is 500. This number of laser pulses resulted in samples that contain ~5 layers of graphene. The number of layers was not affected by the laser fluence and the sample cooling rate after the deposition. However, the increase of the laser flu-ence from 0.9 J/cm2 to 1.5 J/cm2, results in 2.5 fold reduction of the MLG resistance. The present study reveals that the PLD method is suitable to produce nanocrystalline multilayer graphene with electrical conductivity of the same magnitude as commercial CVD graphene samples.

Crystalline silver thin layers were obtained by high-energy pulsed laser ablation without heating of the deposition substrate. The fluid Plateau-Rayleigh (PRI), Rayleigh – Taylor (RTI) and Richtmyer – Meshkov (RMI) instabilities, as well as crown splash induced during pulsed laser deposition (PLD) in high energy regime, resulting in ring and pearl shaped structures, offer the benefit of increased sorption surface. These morphological structures obtained for the silver thin layers make them of interest for catalytic applications. The study presented with this work addresses both the fundamental and applied issues on the morphological structures obtained for the silver thin layer and their catalytic function in organic processes. In this sense, the catalytic action of the thin silver layer was highlighted by modifications of the Reactive Blue 21 dye (C.I.) in aqueous solution with sodium bicarbonate. Specific investigations and analyzes were carried out by electron microscopy and elemental analysis (SEM-EDX), atomic force microscopy (AFM) and profilometry, mass spectrometry, ablation plasma diagnosis, diffractograms (XRD), as well as IR spectroscopy (FTIR). In addition to the experimental investigation and analyzes, simulation of the ionization energy threshold was conducted in COMSOL for complementary evaluation on the involved processes and phenomena.

Cyclic olefin copolymer (COC) is a novel type of thermoplastic polymer gaining the attention of the scientific community in electronic, optoelectronic, biomedicine and packaging applications. Despite the benefits in the use of COC like undoubted optical transparency, chemical stability, good water-vapor barrier and biocompatibility, its original hydrophobicity restricts its wider applicability and optimization of its performances. Presently, we report on the optical, and morphological properties of the films of COC covered with Ti in selected areas. The layer of Ti on COC was deposited by pulsed lased deposition processing. The Ti/COC film was characterized by UV-Vis spectroscopy indicating that its transmittance in the visible region decreased by about 20% with respect to the pristine polymer. The quality of the deposited Ti was assessed with the morphology by scanning electron (SEM) and atomic force microscopies (AFM). The modification of the wettability was observed by the sessile drop method indicating a reduction of the native hydrophilicity.

Even though inhalation dosimetry is determined by three factors (i.e., breathing, aerosols, and the respiratory tract), the first two categories have been more widely studied than the last. Both breathing and aerosols are quantitative variables that can be easily changed, while respiratory airway morphologies are difficult to reconstruct, modify, and quantify. Despite several methods are available for model reconstruction and modification, developing an anatomically accurate airway model and morphing it to various physiological conditions remains labor-intensive and technically challenging. The objective of this study is to explore the feasibility of using an adjoint-CFD model to understand airway shape effects on vapor deposition and control vapor flux into the lung. A mouth-throat model was used, with the shape of the mouth and tongue being automatically varied via adjoint morphing, and the vapor transport being simulated using ANSYS Fluent coupled with a wall absorption model. Two chemicals with varying adsorption rates, Acetaldehyde and Benzene, were considered, which exhibited large differences in dosimetry sensitivity to airway shapes. For both chemicals, large shape deformations were explored to find the maximal possible morphing; both the maximal and intermediate deformations were simulated for morphology parametric studies. Results show that changing the mouth-tongue shape can alter the oral filtration by 3.2% for Acetaldehyde and 0.27% for Benzene under a given inhalation condition. This study demonstrates that the hybrid adjoint-CFD approach can be a practical and efficient method to investigate morphology-associated variability in inhalation dosimetry of vapors and nanomedicines.

This study aimed to elucidate the similarities and differences between amyloid-forming corpora amylacea (CA) in the prostate and lung, examine the nature of CAs in cystic tumors of the atrioventricular node (CTAVN), and clarify the distinctions between amyloid-forming CA and spheroid-type amyloid deposition. We conducted proteomics analyses using liquid chromatography–tandem mass spectrometry with laser microdissection and immunohistochemistry to validate the characteristics of CAs in the lung and prostate. Our findings revealed that CAs in these organs primarily consist of common proteins (β2-microglobulin and lysozyme) and locally produced proteins. Moreover, we observed a discrepancy between the histopathological and proteomic analysis results in CTAVN-associated CAs. In addition, while the histopathological appearance of amyloid-forming CAs and spheroid-type amyloid deposits were nearly identical, the latter deposition lacked β2-microglobulin and lysozyme, and exhibited evident destruction of surrounding tissue. A literature review further supported these findings. These results suggest that amyloid-forming CAs in the lung and prostate are formed through a shared mechanism, serving as waste containers (wasteosomes) and/or storage for excess proteins (functional amyloids). In contrast, we hypothesize that while amyloid-forming CA and spheroid-type amyloid deposits are formed, in part, through common mechanisms, the latter are pathological.

Asphaltene precipitation and deposition pose significant operational challenges in both reservoirs and surface facilities by inducing formation damage. To understand the kinetics involved in asphaltene particle nucleation, growth, and aggregation, this study employed confocal microscopy and centrifuge-based methods under a unified set of experimental parameters. The acquired time-resolved particle size images were analyzed using MIPAR image processing software, while asphaltene mass yield was quantitatively evaluated through centrifugation. Experimental conditions were varied to study the effects of heptane concentration, asphaltene concentration, and shear rate. Notably, this investigation introduces, for the first time, the parameter of particle count as an additional variable influencing asphaltene mass production. This study aims to discern how particle count correlates with asphaltene mass yield over time. Results indicate that the minimum mean particle diameter was observed to be 2 microns, which progressively grew up to 80 microns. The mean particle diameter exhibited a positive correlation with both asphaltene concentration and shear rate, whereas an inverse correlation was seen with heptane concentration. Furthermore, the asphaltene mass yield was found to increase with greater asphaltene and heptane concentrations, as well as with higher shear rates. The relationship between mean particle diameter and mass yield was found to be nonlinear. In the early stages, a higher prevalence of small particles contributed to a greater total particle count, while at later stages, particle aggregation led to the formation of larger particles that influenced the overall asphaltene mass. The insights gained from understanding the relationship between particle diameter, count, and mass yield are crucial for advancing the fundamental science of asphaltene precipitation and deposition. These findings may also guide future research that relies solely on particle counts for assessing asphaltene deposition.

We synthesized iron(II)-triazole spin crossover compounds of the type [Fe(atrz)3]X2 and incorporated and deposited them on electrospun polymer nanofibers. In view of possible applications, we chose iron(II)-triazole-complexes that are known to exhibit spin crossover close to ambient temperature. Therefore we used the complexes [Fe(atrz)3]Cl2 and [Fe(atrz)3](2ns)2 (2ns = 2Naphthalenesulfonate) and analyzed them with IR-, UV/Vis and Mossbauer spectroscopy and with a SQUID magnetometer. The synthesized complexes were then in one attempt deposited on fibers of polymethylmethacrylate (PMMA) and in another attempt incorporated into core-shell like PMMA fiber structures. This was done via two different electrospinning methods. Deposition was performed by uniaxial electrospinning and incorporation was performed by coaxial electrospinning. The obtained polymer-complex-composites were then further investitgated by the same methods as the pure complexes as well as by SEM pictures and EDX measurements. The analysis by UV/Vis spectroscopy, Mössbauer spectroscopy and temperature-depended magnetic measurements with the SQUID magnetometer showed that the spin crossover properties were maintained and were not changed after the electrospinning processes and that the complexes were not harmed during the procedure.

Additive Friction Extrusion Deposition (AFED) is a recently developed additive manufacturing technique that promises high deposition rates at low forces. Due to the novelty of the process, the underlying phenomena and their interactions are not fully understood, and in particular the processing strategy and tool design are still in their infancy. This work contributes to the state of the art of AFED through a comprehensive analysis of its working principles and an experimental program including a representative sample component. The working principle and process mechanics of AFED are broken down into their individual components. Forces, their origins and effects on the process are described, and measures of process efficiency and theoretical minimum energy consumption are derived. Three geometrical features of the extrusion die are identified as most relevant to the active material flow, process forces and deposition quality: the topography of the inner and outer circular surfaces and the geometry of its extrusion channels. Based on this, the experimental program investigates seven different tool designs in terms of efficiency, force reduction and throughput. The experiments using AA 6061-T6 as feedstock show that AFED is capable of both high material throughput (close to 550 mm³/s) and reduced substrate forces: For example, the forces for a run at 100 mm³/s remained continuously below 500 N, and for a run at 400 mm³/s below 3500 N. Material flow and microstructure of the AFED are assessed from the macrosections. Significant differences are found between the advancing and retracting sides for both process effects and material flow. Banded structures show strong similarities to other solid state processes. The fabrication of the sample components demonstrates that AFED is already capable of producing industrial grade components. In mechanical testing, interlayer bonding defects result in a more brittle failure behavior in the direction of the structure, in the microstructure show strong similarities to other solid-state processes. The manufacturing of the sample components demonstrates that AFED is already capable of producing industrial grade components. In mechanical tests, interlayer bonding defects result in a more brittle failure behavior in the direction of the structure, while in the horizontal direction of the structure mechanical properties corresponding to a T4 temper have been achieved.

The analysis of particulate matter (PM) in dilute solutions is an important target for environmental, geochemical and biochemical researches. Here we show how the microdrop technology may allow to control, through the evaporation of small droplets, the deposition of insoluble materials dispersed in a solution on a well-defined area with a specific spatial pattern. Using this technology the superficial density of the deposited solute can be accurately controlled. In particular, it becomes possible to deposit an extremely reduced amount of insoluble material -in the order of few μg- on a confined area, thus allowing a relatively high superficial density to be reached within a limited time. In this work we quantitatively compare the microdrop technique for the preparation of particulate matter samples with the classical filtering technique. After having been optimized, the microdrop technique allows to obtain a more homogeneous deposition and limit sample consumption of a factor ~25. This method is potentially suitable for many novel applications in different scientific fields.

In recent years, antibacterial coatings have become a significant approach in the global fight against bacterial pathogens. Developments in materials science, chemistry and biochemistry have led to a plethora of materials and chemical compounds that have potential for creating antibacterial coatings. Nonetheless, there has been insufficient consideration given to the analysis of the techniques and technologies used to apply these coatings. Among the various inorganic coating techniques, Atomic Layer Deposition (ALD) is noteworthy. It enables the successful synthesis of high-purity inorganic nanocoatings on surfaces of complex shape and topography, while also providing precise control over their thickness and composition. ALD has various industrial applications, but its practical application in medicine is still limited. In recent years, a substantial number of papers have been published on the suggested implementation of thin films and coatings produced through ALD in medicine, notably those with antibacterial properties. The aim of this paper is to carefully evaluate and analyse the relevant literature on this subject. Simple oxide coatings, including TiO2, ZnO, Fe2O3, MgO, and ZrO2, were examined, as well as coatings containing metal nanoparticles such as Ag, Cu, Pt, and Au, and mixed systems such as TiO2-ZnO, TiO2-ZrO2, ZnO-Al2O3, TiO2-Ag, and ZnO-Ag. Through comparative analysis, we have been able to draw conclusions on the effectiveness of various antibacterial coatings of different compositions, including key characteristics such as thickness, morphology, and crystal structure. ALD has been analysed in its use for developing antibacterial coatings for various applications. Furthermore, assumptions regarding the most promising development areas have been presented.

Metallic masters can be used as a metallic mold to replicate polymeric pieces with high resolution. Metallic masters with high resolution were created by photolithography technique and nickel electrodeposition technique. AZ 9260 photoresists and SPR 220-7.0 photoresists were used to coat metallic substrates and to compare results. Steel substrate and nickel substrate were used as the metallic substrate to compare results. Two different nickel electrodeposition protocols were used to compare results. In the conclusion section, was determined the best photoresist, metallic substrate, and nickel electrodeposition protocol to fabricate metallic masters.

Chemical vapor deposition (CVD) is a vital process for depositing thin films of various materials with precise control over thickness, composition, and properties. Understanding the heat and mass transfer mechanisms during CVD is essential for optimizing process parameters and ensuring high-quality film deposition. This review provides an overview of recent advancements in the heat and mass transfer modeling for chemical vapor deposition processes. It explores innovative modeling techniques, recent research findings, emerging applications, and challenges in the field. Additionally, it discusses future directions and potential areas for further advancement in CVD modeling.

This study investigates the spatial and temporal distribution of litter at 7 beach sectors in Cadiz Bay, Southwest Spain. Two ten-day surveys carried out in autumn 2022 and spring 2023 revealed a total of 4,199 and 4,634 items, respectively, with plastic being the predominant material (71.13% in autumn, 88.39% in spring). Litter quantities varied significantly among beaches, La Puntilla showing the highest abundance with 0.48 ± 0.25 items m-1 in autumn and 1.34 ± 0.61 items m-1 in spring. The lowest abundance was recorded at sector 1 of Valdelagrana beach (0.08 ± 0.06 items m-1) during autumn and at El Castillito beach (0.08 ± 0.04 items m-1) during spring. Statistical analyses did not reveal significant differences in litter quantities between autumn and spring, however high significant interaction was shown considering both season and beach lo-cation. Seasonal differences were also observed in litter composition. Litter categories increased from 90 in autumn to 107 in spring. The top 10 litter categories varied between seasons and included cigarette butts, plastic fragments and plastic packaging. Cigarette butts were principally abundant in autumn because re-lated to summer beach users and wet wipes were particularly observed in spring because linked to wastewaters and river discharges especially relevant in winter months. Hydrodynamic and wind conditions were analyzed, revealing complex relationships with litter abundance.

The number of obese people worldwide is rising dramatically, with 51% of the global population expected to be obese or overweight by 2035. And it is usually involved in a variety of chronic diseases, including diabetes, hypertension, cardiovascular and cerebrovascular diseases. In the process of obesity, adipose tissue expands indefinitely, which induces metabolic dysfunction. Here, we confirm the role of succinate in the intervention of obesity. Through adding succinate to drinking water, high-fat diet induced obese mice were associated with the lower fat mass, and improved glucose tolerance and energy expenditure. These metabolic changes are accompanied by increased expression of lipolysis genes and decreased lipogenesis genes, especially in subcutaneous adipose tissue. In summary, supplement of succinate improves lipid deposition and metabolic health in obese mice.

In this paper, a novel synthesis for a chemical precursor for nanocrystalline VO2 coatings is elaborated. The compatibility of the precursor towards the substrate is optimized for spin coating. This is done by subjecting multiple solvents to contact angle measurements. A suitable thermal treatment is developed to densify the coating and to induce crystallization. Afterwards the microstructure of the coating is investigated using X-Ray diffraction, electron microscopy and ellipsometry techniques. To assess the thermochromic properties of the fabricated device, optical transmission experiments were conducted both at room temperature and at elevated temperature. A correlation between these thermochromic properties and coating thickness was investigated in order to obtain an optimized thermochromic device, where both high visual transparency and prominent thermochromic switching abilities are aimed for. In this work, an optimal coating thickness is proposed for a thermochromic coating with high switching ability and solar modulation.

Bending pipe is a common component of long distance pipeline. Accurately understanding the flow law of hydrate particles in elbow pipe is of great significance for optimizing pipeline design, improving production efficiency of gas transmission pipeline and ensuring pipeline safety. Taking the flow of hydrate particles in a Bending pipe as the object of study, the spiral flow attenuation and hydrate particle deposition under different bending pipe angles, different rate of bending pipe to diameter, different Reynolds number and different torsion were studied by numerical simulation method. The results show that the larger the swirl number, the higher the spiral flow intensity. When the fluid enters the bending pipe, the Angle of the bending pipe is larger, the torsional rate is smaller, and the Reynolds number is larger, the swirl number is larger, the intensity of the swirl flow is stronger, and the swirl number is larger at the same position. However, the larger the bending pipe to diameter ratio, the greater the change of the total swirl number and the weaker the strength at outflow, but the slower the change of swirl number, indicating that the spiral flow attenuation is slower. The larger the bending pipe Angle, the larger the bending pipe diameter rate, the smaller the torsion rate and the larger the Reynolds number, the smaller the deposition rate of the particles after flowing through the pipe. The results show that the spiral flow strength can be maintained in a proper way to reduce the deposition and ensure the safety of the conveying process.

The main purpose of this paper is to present a system to detect extrusion failures in Fused Deposition Modelling (FDM) 3D printers by sensing that the filament is moving forward properly. After several years using these kind of machines, authors detected that there is not any system to detect the main problem in FDM machines. Authors thought in different sensors and used the Weighted Objectives Method, one of the most common evaluation methods, for comparing design concepts based on an overall value per design concept. Taking into account the obtained scores of each specification, the best choice for this work is the optical encoder. Once the sensor is chosen, it is necessary to design de part where it will be installed without interfering with the normal function of the machine. To do it, photogrammetry scanning methodology was employed. The developed device perfectly detects the advance of the filament without affecting the normal operation of the machine. Also, it is achieved the primary objective of the system, avoiding loss of material, energy and mechanical wear, keeping the premise of making a low-cost product that does not significantly increase the cost of the machine. This development has made it possible to use the printer with remains coil filament, which were not spent because they were not sufficient to complete an impression and also printing models in two colours with only one extruder.

Abstract: Polylactic acid (PLA) is brittle in nature with extensive deformation property. For improvement of the end-use quality, it is of significant importance to enhance the producibility of fused deposition modeling (FDM)-printed objects in PLA. The purpose of this investigation is to boost toughness and to reduce the production cost of the FDM-printed tensile test samples with the desired part thickness. To attain the research purpose number of experiments are designed and analyzed by the Response Surface Method (RSM). The statistical analysis is performed to deal with this concern considering layer thickness, infill percentage, and extruder temperature as controlled factors. The tensile test specimens are printed based on the designed experiments, and the tensile strength tests are conducted by SANTAM 150 universal testing machine based on ASTM D638. The honeycomb internal fill pattern is applied for the production of light-weight and high-strength specimens. The area under Force- Extension curve up to fracture is acquired as the toughness of the printed specimens. This study also developed a modeling process using ANN and ANN-GA techniques for developing an accurate estimation for toughness, part thickness, and production cost as dependant variables. Results were evaluated by correlation coefficient and RMSE values. According to the modeling results, ANN-GA as a hybrid ML technique could successfully improve the accuracy of modeling about 7.5, 11.5 and 4.5 % for toughness, part thickness, and production cost, respectively, in comparison with those for the single ANN method. In the other side, the optimization results confirm that the optimized specimen is cost-effective and able to comparatively undergo deformation, which develops the usability of printed PLA objects. The research is accomplished under the constraints of PLA compatibility with existing fused deposition modeling setup without changing the functional hardware/software of the machine. Although the mechanical properties and dimensional accuracy of PLA have already been studied, there is little literature on the toughness of the printed PLA with honeycomb internal fill pattern.

The type of tail of sheep is an important economic trait. However, the candidate genes associated with the tail type are uncertain. The objective of this study was to identify the genetic region and genotype responsible for the tail type phenotype. Here we perform a genome-wide association study (GWAS) in 40 large tailed Han sheep and 40 Altay sheep as case and 40 Tibetan sheep as control. The results indicated that a total 31 genome-wide significant SNPs associated with type of tail traits were detected. For significant SNPS loci, determine its physical location, and screening of candidate genes within section. By combining information of previously reported and annotated biological functional genes, we identified SPAG17, Tbx15, VRTN, NPC2, BMP2 and PDGFD as the most promising candidate genes for type of tail traits. Based on the above identified candidate genes on type of tail traits, we selected BMP2 and PDGFD to conduct the genetic effect analysis in a large Altay sheep and Tibetan sheep population. Rs119 T>C in the exon1 of BMP2 gene and 1 SNPs in the exon4 (rs69 C>A) of PDGFD gene were detected, rs119 that located on exon1 of BMP2 gene was TT genotype in Altay sheep, while with CC genotype in Tibetan sheep. On rs69 of PDGFD gene, Altay sheep with CC genotype, however, Tibetan sheep with AA genotype. These results indicated that the significant associations of SNPs detected in GWAS were indirectly caused by the genetic effects of BMP2 and PDGFD on sheep tail fat deposition.

Cold gas dynamic spray (CS) is a unique technique to deposit material using high strain rate solid state deformation. A major challenge for this technique is its dependence on the powder properties and lack of standards to assess them between lots and manufacturers. The motivation of this research was to understand the variability in powder atomization techniques for stainless steel powders and their subsequent properties for their corresponding impact on CS. A drastic difference (~30%) was observed in deposition efficiencies (DE) of unaltered, spherical, and similar sized stainless steel (316) powders produced using centrifugal (C.A) and traditional gas atomization (G.A) techniques. The study highlights more on differences on precursor level. Using recent advancements in large scale statistical measurements like laser diffraction shape analysis, µCT scanning, traditional methods like EBSD, nano-indentation, an attempt is made to understand the powder property. Insights on powder size and shape are documented. Significant differences were observed between C.A and G.A powders in terms of grain size, fraction of higher angle grain boundaries (HAGB) and nano hardness. The outcomes of this study would be helpful to understand the commercialization of the cold-spray process for bulk manufacturing of powder precursors

This paper presents the results of the investigation of composite sinters W-TiB2 which were used as an electrode in the process of electro-spark deposition (ESD) and the examination of the deposited layers. The scope of the study includes detailed characteristics of powder mixtures, composite sinters made using the spark plasma sintering method (SPS) and layers deposited in the electro-spark process. The ESD process, using the W+30 vol.% TiB2 electrode, was carried out using an automated device. The substrates were made of copper and aluminium. The topography analysis of the surfaces of the composite layer and the evaluation of their wear resistance properties are also presented. The analysis of the results of research showed the possibility to obtain, using the SPS method, composite materials of good quality, which can be used as electrodes in the ESD process. The obtained layers had increased wear resistance in relation to the substrate material.

Optical and mechanical properties of multilayer coatings depend on the selected layer materials and the deposition technology; therefore, knowledge of the performances of thin films is essential. In the present work, titanium dioxide (TiO2) and silicon dioxide (SiO2) thin films have been prepared by plasma ion-assisted deposition (PIAD). The optical, structural, and mechanical properties of thin films have been investigated using spectrometer/ellipsometer, X-ray diffraction (XRD), atomic force microscopy (AFM), and laser interferometer. The results show that TiO2 film fabricated by PIAD induces a high refractive index, wide optical band gap, amorphous structure, smooth surface, and tensile stress. In the case of SiO2 film, high bias voltage leads to dense structure and compressive stress. As an application, a three-wavelength high reflectance at 632.8, 808, and 1550nm is optimized and deposited. The dependence of total stress in the multilayer on the substrate temperature is studied as well. In conclusion, it is demonstrated that PIAD is an effective method for the preparation of ultralow stress TiO2/SiO2 multilayer films. The achieved stress is as low as 1.4Mpa. The result could provide guidance to the stress optimization of most optical components without prefiguring, backside coating, and post-deposition treatments.

In this study, the effects of grain size and gradation of riprap, overtopping flow depth and downstream slope of embankment on scouring and deposition characteristics at the downstream toe of the embankment was investigated. For the experiment, three different downstream slopes (1:2, 1:3, and 1:4), three different overflow depths (1, 2, and 3 cm), and three different sizes (d₅₀ of 16.41 mm, 8.48 mm, and 3.39 mm herein referred as No.5, 6 and 7 respectively) of riprap particles, respectively, were used in the laboratory. The experimental results demonstrated that the scour depth and deposition height increased with increasing energy head for each downstream slope condition. Among the three particle sizes, for No. 5 size particle shows the lowest scour depth and highest deposition height. For the 1:2 slope, the No. 5 particle size could resist scour 62% and 75% less than that of the No. 6 and No. 7 particles, respectively. For the 1:3 slope case, this was 31% and 46%, and for the 1:4 slope case, this was 39% and 49% less than the No. 6 and No. 7 size particles, respectively.

In this study, the potential of Fe3Al coating material as an environmentally friendly alternative to coatings containing critical elements for brake discs was investigated. A buffer layer of Cr-Mo steel (Ferro 55) was applied to enhance coating quality and prevent the formation of hot cracks during solidification. Microstructural analysis of the cross-section of the coating showed that the buffer layer diffused into the Fe3Al coating, forming a combination of Fe3Al, Fe, and Fe3AlC0.5 phases. The tribological properties of the Fe3Al coating were evaluated by pin-on-disc tests using two different copper-free friction materials extracted from commercial brake pads. The wear results showed a coefficient of friction comparable to that of an uncoated disc, but with a reduction in Particulate Matter (PM) emissions, an interesting aspect that is gaining increasing importance in view of the upcoming international standards..

Focused electron beam induced deposition is a versatile tool for the direct fabrication of complex-shaped nanostructures with unprecedented shape fidelity and resolution. While the technique is well-established for various materials, the direct electron beam writing of silver is still in its infancy. Here, five different silver carboxylates, three fluorinated: [Ag2(µ-O2CCF3)2], [Ag2(µ-O2CC2F5)2], [Ag2(µ-O2CC3F7)2] and two containing hydrogen: [Ag2(µ-O2CCMe2Et)2] and [Ag2(µ-O2CtBu)2] were examined and compared as potential precursors for focused electron beam induced deposition. All of the compounds show high sensitivity to electron dissociation and efficient dissociation of Ag-O bonds. The as-deposited materials showed high silver content from 42 at.% to above 70at.% and silver nano-crystal formation with impurities of carbon and fluorine incorporated between metal grains. A correlation of the number of carbon atoms in the precursor ligands and silver content of the deposited structures was found. The highest silver contents were achieved for compounds with the shortest CF chains. The deposited silver content depends on the balance of electron induced ligand co-deposition and thermal ligand desorption. Low electron flux is advantageous for high silver content. Our findings demonstrate that silver carboxylates constitute a promising group of precursors for focused electron beam nanoprinting of high silver content materials.

The possibility of using additive manufacturing (AM) in the medicine area has created a new opportunities in health care. This has contributed to a sharp increase in demand for 3D printers, their systems and materials that are adapted to strict medical requirements. We described herein a medical-grade thermoplastic polyurethane (S-TPU), which was developed and then formed into a filament for Fused Deposition Modeling (FDM) 3D printers during a melt-extrusion process. S-TPU consisting of aliphatic hexamethylene 1,6-diisocyanate (HDI), amorphous α,ω-dihydroxy(ethylene-butylene adipate) (PEBA) and 1,4 butandiol (BDO) as a chain extender, was synthesized without the use of a catalyst. The filament properties were characterized by rheological, mechanical, physico-chemical and in vitro biological properties. The tests showed biocompatibility of the obtained filament as well as revealed no significant effect of the filament formation process on its properties. This study may contribute to expanding the range of medical-grade flexible filaments for standard low-budget FDM printers.

Polylactic Acid (PLA) is an organic polymer commonly used in fused deposition (FDM) printing and biomedical scaffolding that is biocompatible and immunologically inert. However, variations in source material quality and chemistry make it necessary to characterize the filament and determine potential changes in chemistry occurring as a result of the FDM process. We used several spectroscopic techniques, including laser confocal microscopy, Fourier-Transform Infrared (FTIR) spectroscopy and photoacousitc FTIR spectroscopy, Raman spectroscopy, and X-ray photoelectron Spectroscopy (XPS) in order to characterize both the bulk and surface chemistry of the source material and printed samples. Scanning Electron Microscopy (SEM) and Differential Scanning Calorimetry (DSC) were used to characterize morphology, crystallinity, and the glass transition temperature following printing. Analysis revealed calcium carbonate-based additives which were reacted with organic ligands and potentially trace metal impurities, both before and following printing. These additives became concentrated in voids in the printed structure. This finding is important for biomedical applications as carbonate will impact subsequent cell growth on printed tissue scaffolds. Results of chemical analysis also provided evidence of the hygroscopic nature of the source material and oxidation of the printed surface, and SEM imaging revealed micro and sub-micron scale roughness that will also impact potential applications.

Weathering and erosion transport minerals and organics toward the sea or lake bottoms over geologic time. The finest solids are deposited in lower, less turbulent areas, such as lake bottoms and continental shelves. They sometimes stack up to thicknesses of kilometers, and begin compacting. These sediment sections are called shales, and as initially deposited in water, shales can have porosities up to 50-80{\%} water, As they are buried, many alteration products from oil to slate are produced due to overburden and temperature increasess, making them important to study. A preceeding paper \cite{1} showed that pressure solution is the primary mechanism for porosity reduction, with possible mechanical compaction at shallow depths. Without naming the mineral(s) involved, it postulated that the greater the product of the water and pore interfaces, the faster the reaction would proceed. This term is $ \varphi^{4m/3}(1-\varphi)^{4n/3}$ , where $\varphi$ is porosity and m and n are numbers close to unity. The large exponents, {\em 4/3}, recognize that the reaction occurs at the molecular scale at which the surfaces are rough. A second term, $\exp^{(-E/RT)}$ , indicates that the reaction is impeded by a quantum energy barrier, E, with diminished impeding power as increased available thermal energy, represented by the absolute temperature, T, becomes available at greater depths in the Earth. These two factors combine to allow porosity $\varphi$ to reduce with time, or equivalently for the fraction of solids, $(1-\varphi)$, to increase with time,$\left. \frac{\partial(ln(1-\varphi) ) }{\partial t } \right |_{\sigma} = (\varphi )^{4m/3}( 1-\varphi )^{4n/3}Ae^{-E/(RT)}$. { \em Here it is shown that this equation can cover quantitatively any actual deposition rates which may have been experienced by the six sections studied, the actual deposition rates being unknown for these cases. Hence a time-depth depositional history for any new shale section, known in detail, would allow determination of the parameters m, n, E and a lumped proportionality constant A. This was accomplished by showing that, for a wide range of depositional rates, r, the range of E for any of the studied sections is small compared to laboratory measurements of quartz solution\cite{2}, 24+-15kJ/mol. Results were obtained over this range of r's using the previously determined m and n, and porosity and temperature profiles. The presently existing porosity profiles necessarily incorporate any overpressure or underpressure conditions that may have existed in the past or currently, as the net difference between overburden and pore pressure is a primary driving force for pressure solution. $SiO_2$ usually comprises 20-50{\%} of shales. In conclusion, pressure solution of quartz can account for vertical compaction of shales quantitatively in the studied examples. Separately, a quasi-eqivalent method for discussing reduced porosities in Macron 2 versus Macron 1 as increased vertical stress, rather than additional horizontal stress, is illustrated. Experiments are suggested to clarify the pressure solution mechanism. The role of horizontal forces is discussed. From a global point of view, shale compaction by pressure solution is a quantified step in the cycling of continental rocks, beginning with rifting.

Vertical graphene nanowalls (VGNWs) have emerged as a highly promising material in recent years due to their exceptional properties, such as a high specific surface area, excellent electrical conductivity, scalability, and compatibility with transition metal compounds. These attributes make VGNWs a compelling candidate for various applications, including energy storage, catalysis, and sensing, fostering great interest in their use in next future commercial graphene-based sensors like optoelectronic and plasmonic devices, energy storage electrodes, and catalytic systems. Among the diverse graphene synthesis methods, plasma-enhanced chemical vapor deposition (PECVD) has proven to be a robust technique for producing large-scale graphene films and creating VGNWs on diverse substrates. However, despite substantial progress in optimizing growth conditions to achieve micrometer-sized graphene nanowalls, the outcomes are often obtained through empirical approaches, and a comprehensive understanding of the underlying physicochemical mechanisms governing nanostructure formation remains elusive. In particular, a deeper exploration of atomic-level phenomena, such as nucleation, carbon precursor adsorption, and surface diffusion of adatoms, is imperative to exert precise control over the growth process. Concerning the synthesis of VGNWs, hydrogen plays a dual role in the graphene growth process, acting as both a co-catalyst and an etchant for the nanowalls. Nevertheless, a thorough comprehension of the intricate growth process is still required. To address these knowledge gaps, this review paper aims to investigate the nucleation and growth of VGNWs using PECVD, with a specific focus on exploring the temperature effect on the graphene growth ratio and nucleation density across a wide range of temperatures. By providing valuable insights into the PECVD process, our objective is to enable the optimization of growth conditions for tailoring VGNWs' properties, thereby facilitating their application in energy storage, catalysis, and sensing fields.

In the fashion field, the use of electroplated small metal parts such as studs, clips and buckles is widespread. The plate is often made of precious metal, such as gold or platinum. Due to the high cost of these materials, it is strategically relevant and of primary importance for manufacturers to avoid any waste by depositing only the strictly necessary amount of material. To this aim, Companies need to be aware of the overall number of items to be electroplated so that it is possible to properly set the parameters driving the galvanic process. Accordingly, the present paper describes a Machine Vision-based method able to automatically count small metal parts arranged on a galvanic frame. The devised method relies on the definition of a proper acquisition system and on the development of image processing-based routines. Such a system is then implemented on a counting machine is meant to be adopted in the galvanic industrial practice to properly define a suitable set or working parameters (such as current, voltage and deposition time) for the electroplating machine and, thereby, to assure the desired plate thickness from one side and to avoid material waste on the other.

We report on the fabrication and electrical characteristics of zinc-oxide (ZnO) based metal-insulator-semiconductor (MIS) type Schottky barrier diodes (SBHs). ZnO thin layer on the p-type silicon substrate was fabricated by atomic layer deposition (ALD). The structure and surface properties of the thin film were characterized by X-ray diffraction (XRD), atomic force microscope (AFM) and secondary ion mass spectrometer (SIMS). The current-voltage (I-V) characteristics of Al/ALD-grown ZnO/p-Si diodes were measured under dark at room temperature. The electrical parameters such as ideality factor (n), series resistance (R_s) and barrier height (ϕ_b) of the diodes were analyzed using standard thermionic emission (TE) theory, Norde and Cheung method. The barrier height value obtained from I-V and Cheung method was found to be 0.73 eV and 0.76 eV, respectively. The interface state density (Dit) of the diodes was determined from the I-V characteristics. The nonideal behavior of measured parameters suggested the presence of interface states. The obtained results showed that the prepared diode can be used for NIR Schottky photodetector applications.

The rational design of magnetic carbon composites, encompassing both composition and microstructure, holds significant potential for achieving exceptional electromagnetic wave absorbing materials (EAMs). In this study, FeCo@CM composites was efficiently fabricated through an advanced microwave plasma assisted reduction chemical vapor deposition (MPARCVD) technique, offering high efficiency, low cost, and energy-saving benefits. By depositing graphitized carbon microspheres, the dielectric properties were significantly enhanced, resulting in improved electromagnetic wave absorption performances through optimized impedance matching and a synergistic effect with magnetic loss. A systematic investigation revealed that the laminar-stacked structure of FeCo exhibited superior properties compared to its spherical counterpart, supplying a higher number of exposed edges and enhanced catalytic activity, which facilitated the deposition of uniform and low-defect graphitized carbon microspheres. Consequently, the dielectric loss performance of the FeCo@CM composites was dramatically improved due to increased electrical conductivity and the formation of abundant heterogeneous interfaces. At a 40 wt% filling amount and a frequency of 7.84 GHz, the FeCo@CM composites achieved a minimum reflection loss value of -58.2 dB with an effective absorption bandwidth (fE) of 5.13 GHz. This study presents an effective strategy for developing high-performance EAMs.

Polymeric composites such as Poly-ether-ether-ketone (PEEK)/carbon fiber (CF) have been widely utilized due to outstanding performances such as high specific strength and specific modulus. The PEEK/CF components via powder-bed fusion additive manufacturing usually show brittle fracture behaviors induced by their poor interfacial affinity and inner voids. These defects are strongly associated with powder packing quality upon deposition. The particle dynamic model has been widely employed to study the interactions of particle motions. Powder property, bulk material property, and interfacial features of composite powders are key factors in the particle dynamic model. In this work, an efficient and systematic material evaluation is developed for composite powders to investigate their deposition mechanism. The discrete element method is utilized to simulate the dynamic behaviors of PEEK/CF composite powders. The powder properties, bulk material properties, and interfacial features of powders are calibrated and justified by experimental measurement, numerical simulation, and design of experiments. The particle dynamic model can well explain the powder flow behaviors and interactions. It reveals that the addition of short CF particles can assist the flow of PEEK powders and improve the packing quality of the composite powders.

Mechanical robustness, biocompatibility, and antibacterial performances are key features for materials suitable to be used in tissue engineering applications. In this work, we investigated the link existing between structural and functional properties of TiCu(Ag) thin films deposited by physical vapor deposition magnetron sputtering on Si substrates. The thin films were characterized by X-ray diffraction (XRD), nanoindentation, atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS). The TiCu(Ag) thin films showed complete amorphous structure and improved mechanical properties in comparison with pure Ti films. However, for contents in excess of 20% Ag, we observed the appearance of nanometric Ag crystallite. The TiCu(Ag) thin films displayed excellent biocompatibility properties, allowing adhesion and proliferation of the human fibroblasts MRC-5 cell line. Moreover, all the investigated TiCu(Ag) alloy display bactericidal properties, preventing the growth of both Pseudomonas aeruginosa and Staphylococcus aureus. Results obtained from biological tests have been correlated to the surface structure and microstructure of films. The excellent biocompatibility and bactericidal properties of these multifunctional thin films opens to their use in tissue engineering applications.

The present work proposes a novel manufacturing technique based on the combination of Laser Metal Deposition, Laser Beam Machining and Laser Polishing processes for the complete manufacturing of complex parts. Therefore, the complete process is based on the application of a laser heat source both for the building of the preform shape of the part by additive manufacturing and for the finishing operations. Their combination enables to manufacture near-net-shape parts and afterwards, remove the excess material via laser machining, which has resulted to be capable of eliminating the waviness resulting from the additive process. Besides, surface quality is improved via laser polishing to reduce the roughness of the final part. Therefore, conventional machining operations are eliminated, what results in a much cleaner process. In order to validate the capability of this new approach, the dimensional accuracy and surface quality of the resulting parts are evaluated. The process has been validated on an Inconel 718 test part, where a previously additively built up part has been finished by means of laser machining and laser polishing.

The control of the fine particle emission from the coal-fired power plants has been a big challenge in china. Either the conventional electrostatic precipitator or the fabric filter has some shortages. The electrostatic precipitator is hard to keep high efficiency for the submicron particles. The fabric filter could keep high efficiency but with very high pressure drop. One solution is to combine them together. Several types of hybrid particle collectors (HPC) combining the electrostatic precipitator and the fabric filter together have been developed and applied in a number of projects in China. In recent years, numerical simulation technology has been widely used in the design of the collectors. In this paper, an unsteady numerical model is used to investigate the particle deposition characteristics in a scale hybrid collector. The fluid field is modeled by using incompressible Navier-Stokes equations with the RNG turbulence equations. The corona discharge is solved by using a finite volume method. The particle charging is modeled by using a filed-diffusing combined model. And an unsteady cake formation model is used to simulate the filtration process.

The mechanism of vapor-gas deposition of vinyltrimethoxysilane (VS) and ethylene glycol (EG) from azeotropic solutions is investigated, which allows to reduce the evaporation temperature of the components of working mixtures. The need for such studies is associated with the development of a new direction in the technology of vapor-gas deposition of polymer coatings. Methods have been developed for monitoring the chemical composition of working solutions in evaporators using optical spectroscopy, which allow calculating the partial pressures of vapor phase components. Based on these studies, compositions of working solutions are proposed that allow to equalize the partial pressures of the components of working mixtures with a large difference in boiling point. A new method of vapor-gas deposition of non-volatile powder inhibitors on metals is proposed. Chemical compositions of siloxane coatings were determined using XPS and mechanisms of interaction of VS with polymerization promoters ethylene glycol and 1-hydroxy ethylidene-1,1-diphosphonic acid (HEDP) were proposed.

Despite huge effort has been devoted to the design of the initiators and reaction conditions, it remains challenging to synthesize high molecular weight polypeptides with conventional solution phase synthesis. In this work, surface-initiated vapor deposition polymerization (SI-VDP) was utilized to graft synthetic polypeptides poly (γ-benzyl L-glutamate) (PBLG) from polystyrene (PS) resin beads by ring-opening polymerization of N-carboxyanhydrides (NCAs). It was demonstrated for the first time that high molecular weight bulk PBLG (> 500,000) could be readily obtained within one hour via solvent-free synthetic method which paves the way for the synthesis of copolypeptides with high molecular weight.

Magnetron sputtering was used for producing Titanium Vanadium Nitride (TiVN) coatings on a variety of substrates. In this research, we investigate how changing the sputtering power and nitrogen: argon (N2:Ar) gas ratio affects the structural and tribological properties of TiVN coatings. Scanning Electron Microscope (SEM) technique was used to examine TiVN coating surface morphology. Both variants showed a gradual increase in the intensity of the TiVN coating's (111) and (222) peaks. TiVN coating's tribological properties were examined using a pin-on-disc tribometer with varying loads, speeds, and sliding distances. The wear rates of TiVN-coated brass pins were in the range of 2.5×10-4 to 9.14×10-4 mm3/Nm depending on load, sliding distance, and gas ratio variation, when compared to the wear rates of TiVN-coated brass pins deposited at various power, which ranged from 1.76×10-3 to 5.87×10-3 mm3/Nm.

Electrochemical deposition of silicon at room temperature is problematic due to intrinsically low conductivity of the deposits. This study reports the photoelectrochemical (PEC) deposition of silicon (Si) and silicon–carbon (Si–C) layers from an ionic liquid at temperature 40 oC using silicon tetrachloride (SiCl4) as a silicon precursor. Amorphous layers are deposited on p-type silicon (p-Si), p-type gallium arsenide (p-GaAs), and aluminum–copper alloy AA2024. The semi-conductor substrates are activated by white LED illumination, which generated photoelectrons, thereby making the substrate conductive with respect to the cathodic reaction. Photoresponsive-ness of the deposits is proven by the light-induced photocurrents on an optically inactive substrate made of the alloy AA 2024. The proposed method paves the way for the electrochemical modifica-tion of semiconductors and metals with Si and Si–C structures, which are applicable in various fields, such as; batteries, anti-corrosion coatings, photovoltaics, or PEC electrodes for hydrogen production.

In this study the formation of thin-film barrier coatings based on a highly-conducting Bi1.60Er0.4O3 (EDB) solid electrolyte on supporting Ce0.8Sm0.2O1.9 (SDC) electrolyte substrates is implemented for the first time using electrophoretic deposition (EPD). Electrokinetic properties of EDB-based suspensions in a non-aqueous dispersion medium of isopropanol modified with small additions of polyethyleneimine (PEI, 0.26 g/L) and acetylacetone (0.15 g/L), as well as in a mixed isopropanol/acetylacetone (70/30 vol.%) medium are studied. The dependences of the thickness of EDB coatings on voltage and deposition time are obtained using deposition on a model Ni-foil electrode. Preliminary synthesis of a conductive polypyrrole (PPy) polymer film is used to create surface conductivity of non-conductive SDC substrates. The efficiency of using a modified dispersion medium based on isopropanol to obtain a continuous EDB coating 12 μm thick, sintered at a temperature of 850 °C for 5 h, is shown. The microstructure and morphology of the surface of the EDB coating are studied. Pt/SDC/EDB/Pt cell is used to characterize the coating conductivity. The EPD method is shown to be promising for the formation of barrier coatings based on doped bismuth oxide. The developed method can be used for creating cathode barrier layers in SOFC technology.

In this work, the manufacture of thin walls with sharp corners has been optimized by adjusting the limits of a 3-axis cartesian kinematics through data recorded and analyzed off-line, such as axis speed, acceleration and the positioning of the X and Y axes. The study was carried out with two powder materials (SS316L and IN718) using the directed energy deposition process with laser. 1 mm thick walls were obtained with only one bead per layer and straight/sharp corners at 90º. After adjusting the in-position parameter G502 for positioning precision on the FAGOR 8070 CNC system, it has been possible to obtain walls with minimal accumulation of material in the corner, and with practically constant layer thickness and height, with a radii of internal curvature between 0.11 and 0.24 mm for two different precision configuration. The best results have been obtained by identifying the correct balance between the decrease in programmed speed and the precision in the positioning to reach the point defined as wall corner, with speed reductions of 29% for a programmed speed of 20 mm/s and 61% for a speed of 40 mm/s. The walls show minimal defects such as residual porosities, and the microstructure is adequate.

Rats fed a high-fat diet with a single streptozotocin (STZ) injection developed obesity, prediabetes, cardiac hypertrophy and diastolic dysfunction. Here we aimed to explore the renal consequences of prediabetes in the same groups of rats. Male Long-Evans rats were fed normal chow (CON; n = 9) or high-fat diet containing 40% lard and were administered STZ at 20 mg/kg (i.p.) at week four (prediabetic rats, PRED, n = 9). At week 21 cardiac functions were examined (Koncsos et al., 2016) and blood and urine samples were taken. Kidney samples were collected for histology, immunohistochemistry and for analysis of gene expression. High-fat diet and streptozotocin increased body weight gain and visceral adiposity, and plasma leptin, elevated fasting blood glucose levels, impaired glucose and insulin tolerance, despite hyperleptinemia, plasma C-reactive protein concentration decreased in PRED rats. Immunohistochemistry revealed elevated collagen IV protein expression in the glomeruli, and Lcn2 mRNA expression increased, while Il-1β mRNA expression decreased in both the renal cortex and medulla in PRED vs. CON rats. Kidney histology, urinary protein excretion, plasma creatinine, glomerular Feret diameter, desmin protein expression and cortical and medullary mRNA expression of TGF-β1, Nrf2, PPARγ were similar in CON and PRED rats. Reduced AMPKα phosphorylation of the autophagy regulator Akt was the first sign of liver damage, while serum lipid and liver enzyme levels were similar. In conclusion, glomerular collagen deposition and increased lipocalin-2 expression were the early signs of kidney injury, while most biomarkers of inflammation, oxidative stress and fibrosis were negative in the kidneys of obese, prediabetic rats with mild heart and liver injury.

In this study, silver-strontium doped hydroxyapatite (AgSr-HA)/chitosan composite coatings were deposited on stainless steel (SS) substrate via electrophoretic deposition (EPD) technique. The EPD parameters such as the concentration of Ag Sr-HA particles in the suspension, applied voltage and deposition time were optimized on by the Taguchi Design of Experiment (DoE) approach. DOE approach elucidated that the “best” coating was obtained at; the deposition voltage of 20V, deposition time of 7 minutes, and at 5 g/L of Ag Sr-HA particles in the suspension. The optimum coatings were characterized by using scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) spectroscopy. SEM images confirmed the deposition of chitosan/Ag Sr-HA on the SS substrate. The wettability studies indicated the hydrophilic nature of the chitosan/Ag Sr-HA coatings, which confirmed the suitability of the developed coatings for orthopedic applications. The average surface roughness of the chitosan/Ag Sr-HA coatings was in a suitable range for the attachment of bone marrow stromal cells. Chitosan/Ag Sr-HA coatings showed a potent antibacterial effect against the Gram-Positive and Gram-negative bacteria.

In this work, the possibility of fabrication magneto-optical ceramics by vacuum sintering of compacts prepared by electrophoretic deposition (EPD) from suspensions of (Ho0.95La0.05)2O3 (HoLa) nanopowders made by self-propagating high-temperature synthesis and (Y0.9La0.1)2O3 (YLa) nanopowders made by laser synthesis was systematically investigated. The processes of the formation of bulk one- and two-layer compacts by the EPD method from non-aqueous suspensions of nanopowders was studied. The use of acetylacetone and polyvinyl butyral (PVB) was shown to make it possible to obtain stable alcohol suspensions of the nanopowders characterized by high zeta potential values (+29…+80 mV) and to carry out a stable EPD process. One-layer compacts were made from the YLa and HoLa nanopowders with a density of 30–43%. It was found out that the introduction of PVB into the suspension leads to a decrease in the mass and thickness of the green bodies deposited, but does not significantly affect their density. A possibility to make two-layers (YLa/HoLa) compacts with a thickness of up to 2.6 mm and a density of up to 46% was demonstrated. Sintering such compacts in a vacuum at a temperature of 1750°C for 10 hours leads to the formation of ceramics with a homogeneous boundary between the YLa/HoLa layers and thickness of the interdiffused ions layer of about 30 μm.

Titanium dioxide (TiO2) thin films have been widely used in transparent optoelectronic devices owing to their excellent optical properties also is used in photocatalysis, cosmetics, and many other biomedical applications. However, a lack of studies was published on microstructure and adherence comparison of the TiO2 deposited on both AISI substrates. In this work, TiO2 thin films were deposited onto AISI 304 and AISI 316L stainless steel (SS) substrates via atomic layer deposition. Its heterostructure, morphology, and adhesion were compared in both substrates looking for synergistic and multifunctional properties. Raman spectroscopy mapping and X-ray diffraction using the Rietveld refinement method showed that the films are composed of anatase and rutile phases in different percentages. Scratching tests were used to analyze the film adher-ence and friction between a diamond tip and TiO2 film, showing well adhered in both substrates.

The composition of fine-ground lead zirconate-titanate powder Pb(Zr_0.52Ti_0.48)O₃, suspended in PZT and bismuth titanate (BiT) solutions, is deposited on the curved surface of IN718 and IN738 nickel-based supper alloy substrates up to 100 µm thickness. Photochemical metal organic and infiltration techniques are implemented to produce smooth, semi-dense, and crack-free random orientated thick piezoelectric films as piezo-sensors, free of any dopants or thickening polymers. Every single layer of the deposited films is heated at 200 °C with 10 wt.% excess PbO, irradiated by UV lamp (365 nm, 6 watt) for 10 minutes, pyrolyzed at 400 °C, and subsequently annealed at 700 °C for one hour. This process is repeated successively until reaching the desired thickness. Au and Pt thin films are deposited as the bottom and top electrodes using evaporation and sputtering methods, respectively. PZT/PZT and PZT/BiT composite films are then characterized and compared to similar PZT and BiT thick films deposited on the similar substrates. The effect of composition and deposition process is also investigated on the crystalline phase development and microstructure morphology as well as dielectric, ferroelectric and piezoelectric properties of piezo-films. The maximum remnant polarization of P_r = 22.37 ± 0.01, 30.01 ± 0.01 µC/cm², the permittivity of ε_r = 298 ± 3, 566 ± 5 and piezoelectric charge coefficient of d₃₃ = 126, 148 m/V were measured versus the minimum coercive field of E_c = 50, 20 kV/cm for the PZT/PZT and PZT/Bit thick films, respectively. The thick film piezo-sensors are developed to be potentially used at frequency bandwidth of 1–5 MHz for rotary structural health monitoring and also in other industrial or medical applications as a transceiver.

We used a metal-organic chemical vapor deposition technique to synthesize a boron-doped reduced graphene oxide (B-rGO) material with various electrical characteristics, dependent on simultaneous reduction and doping procedures. The effect of the doping level on the B bonding in the reduced graphene oxide (rGO) layer controlled by the annealing temperature was investigated using X-ray photoelectron spectroscopy (XPS). The XPS data indicated that the B-rGO layer had a higher B concentration and a considerable number of O-B bonds as a result of the appreciable annealing temperature, which resulted in a decreased work function and Schottky contact between B-rGO and n-type Si. Owing to the higher proportion of B-C and B-C3 bonding in the B-rGO device than that in the rGO/Si device, the lower Schottky barrier height of the B-rGO/n-Si vertical junction photodetector resulted in a higher responsivity. This work suggests a facile method of B doping to alter the electrical properties of graphene materials.

Magneto-electrochemistry (MEC) is a unique paradigm in science, where electrochemical experiments are carried out as a function of an applied magnetic field, creating a new horizon of potential scientific and technological applications. Over the time, detailed understanding of this research domain was developed to identify and rationalize the possible effects exerted by a magnetic field on the various microscopic processes occurring in an electrochemical system, such as: electrolyte properties governed by charge-transfer process (electric conductivity, viscosity, and diffusivity), mass transfer, electrochemical kinetics and on the structure/quality of products formed either at the working electrode or in the electrochemical cell. Particularly, magnetic field controlled chiral architecture obtained from deposited metal, alloys and catalyst and their excellent enantio-recognition in experimental frame is highly appealing. Interestingly, Hall effect was also demonstrated in electrolytic medium via an impressive experimental technique which is being employed for further theoretical understanding in the field of magneto-electrochemical science. Later, a highly reproducible local temperature variation was observed in electrochemical electrolytes exposed to perpendicular magnetic and electric fields. However, until recent studies, none of the above mentioned reports considered the possibility of a spin-dependent related charge-transfer process. Recent experimental and theoretical studies reveal that electron’s transmission through chiral molecules is spin-selective and this effect has been referred to as chiral-induced spin-selectivity (CISS) effect. The CISS effect pave the way for the building up of a system characterized by a net magnetic moment exploiting the spin-filtering ability of chiral molecules. This interplay between chirality and magnetism may shed light on fundamental scientific aspects underlying the enantio-recognition and highly efficient electron-transfer that occurs in biological process.

Walls-like structured monoclinic WO3 thin films were obtained by spray deposition method for further integration in gas sensors. For sensing applications, it is very important to achieve a high surface-to-volume ratio surface together with a proper thin films structure. The present communication reports on the effect of the sprayed solution volume variation (as a thickness variation element) on the detailed Raman spectroscopy for WO3 thin films with different thicknesses grown from precursor solutions with two different concentrations. Detailed analysis of the two series of samples shows that the growing thickness strongly affects the films morphology while their crystalline structure is only slightly affected. The Raman analysis contribute to refining the structural features clarifications. It was observed that, for both concentrations, the increase in thickness seems to slightly affect the stoichiometry of material and, in association with surface morphology variations, provide new possibilities for fine tuning of films properties towards enhanced as sensing applications. Further studies are ongoing.

Spray penetration into citrus canopies is critical for adequate coverage and deposition to ensure effective pest control. However, mismatch of air assistance to target canopy characteristics can lead to unintended spray loss through over penetration. To evaluate the effect of air assistance on on-target deposition, two sprayers (surrogates for airflow rates) were used to apply a fluorescent tracer dye solution @ target concentration of 300 ppm to 16 medium foliage density tree blocks in a commercial mandarin orchard. The complete factorial experiment in three replications comprised two ground speeds (1.6 and 4.8 km/h), two disc-core nozzles (TeeJet® D3-25 and D6-45), and either one or two nozzle rows to obtain a wide range of application rates (496 to 9,719 L/ha). Dye deposition significantly decreased with canopy depth (p=<0.001) by nearly 7 times across the 3.4-m-wide canopies but was not significant over 1.2 to 2.2 m sampling height (p=0.867). Deposition obtained with the low airflow rate sprayer was significantly greater (p=<0.001) than that obtained with the high airflow rate sprayer over the dose range likely due to too much air pushing out spray droplets. This study underscores the importance of matching the air assistance of orchard sprayers to the target canopy.

Laser-Powder Directed Energy Deposition (DED-LB/Powder) is an additive manufacturing process that is gaining popularity in the manufacturing industry due to its numerous advantages, particularly in repairing operations. However, its application is often limited to case studies due to some critical issues that need to be addressed, such as the degree of internal porosity. This paper investigates the effect of the most relevant process parameters of the DED-LB/Powder process on the level and distribution of porosity. Results indicate that, among the process parameters examined, porosity is less affected by travel speed and more influenced by powder mass flow rate and laser power. Additionally, a three-dimensional finite element transient model was introduced, which was able to predict the development and location of lack-of-fusion pores along the building direction.

Polymer-derived ceramic (PDC) based coatings like Si-C-N and their derivatives are gaining importance day by day in N/MEMS and aerospace due to their thermos-mechanical stability and conductivity. The crystallized, amorphous, and near amorphous morphology of SiCN nanocomposite coatings based on deposition conditions requires thorough investigation for appropriate utilization as they lead to differences in mechanical properties (quantified using nanoindentation in this case). A 4-stage model was proposed based on Raman spectroscopy due to the N₂-Ar pressure variations during the deposition process of SiCN coatings by magnetron sputtering. The integral intensity of the G (graphitic), disorder (D), and tetrahedral (T) peaks namely I_G, I_D, and I_T were calculated after the deconvolution of the spectra. The sp² domain size and defect parameters were evaluated and correlated with the hardness and different bond formation involving Si, C, and N. Image analysis revealed the atomic migration involved during the growth process leading to crystallization along with the formation of voids and defects. The observations were supported by FTIR and TEM-SAED analysis. The outcomes provide a foundation causing an urge to develop similar models with further elemental additions and correlate with various physical properties.

This article describes the synthesis of hydroxyapatite (HAp) flakes through a microwave-assisted hydrothermal method. These flakes are intended for use as substrates for depositing titanium dioxide (TiO2) films using chemical vapor deposition with metal–organic precursors (MOCVD). The results reveal the formation of crystalline hydroxyapatite characterized by a uniform mor-phology. Additionally, we demonstrated the successful deposition of TiO2 coatings on the hy-droxyapatite flakes, resulting in a distinctive faceted prism morphology. Our findings affirm the effective synthesis of the HAp/TiO2 composite material. To further explore the material’s practical applications, we recommend assessing the photocatalytic activity of these composite membranes in future research.

Having garnered significant attention in the scientific community over the past decade, Wire Arc Directed Energy Deposition (arc-DED) technology is at the heart of this investigation into additive manufacturing parameters. Singularly focused on invar as the selected material, the primary objective revolves around devising an indirect cord height measurement approach. This innovative methodology involves the seamless integration of internal signals and sensors, enabling the derivation of crucial measurements sans the requirement for direct physical interaction or conventional measurement methodologies. Through the course of this research, meticulous alteration of deposition parameters is undertaken to thoroughly scrutinize their influence on the ultimate cord dimensions. The fusion of cutting-edge manufacturing techniques with advanced sensor technology constitutes the essence of this endeavor, offering substantial potential to augment precision and efficiency in additive manufacturing processes. Remarkably cost-effective, this solution circumvents the need for intricate measurements and significantly contributes to the proper layer-by-layer growth process.

Laser direct writing allows for the fabrication of complex structures, which is particularly advantageous in micro-optic applications. However, the increasing demand for optics quality requires the lowest optical power loss, which can occur from unwanted reflections. This research demonstrates the possibility of forming an anti-reflective coating on hybrid-polymer micro-lenses fabricated by employing laser direct writing (LDW), without changing their geometry. Such coating deposited by atomic layer deposition (ALD) decreased the reflection from 3.3 % to 0.1 % at the wavelength of 633 nm for one surface of SZ2080™.

Accurate measurement of low-level thoron gas and high-accuracy calibration of thoron measurement devices are essential for assessing and preventing thoron radiological risks. This study aimed to develop a thoron gas measurement technique using an airflow-through scintillation cell for both low-level measurement and high-accuracy calibration. To achieve this, a compartment model was developed to estimate the influence of progeny deposition and accumulation on the wall of the scintillation cell to prevent overestimation of thoron. A self-developed scintillation cell was utilized to implement and validate this technique. The lower detection limit and measurement uncertainty were then evaluated to assess the feasibility of the technique for low-level measurement and high-accuracy calibration. The results showed that the compartment model effectively addressed the influence of the progeny deposition. The measurement technique achieved a lower detection limit below 100 Bq m-3 even with the coexistence of 100 Bq m-3 of radon and attained a measurement uncertainty (k = 2) below 10% when the concentration of thoron exceeded 1,000 Bq m-3. In summary, this study developed a reliable and practical thoron gas measurement technique using an airflow-through scintillation cell with consideration for progeny deposition, and is expected to contribute to the assessment and prevention of thoron radiological risk.

Laser Powder Directed Energy Deposition (LP-DED) is an Additive Manufacturing process in which a laser beam is used to generate a melt pool onto a substrate. The additional material, in form of powder material, is fed into the generated melt pool and a raised track is obtained. The LP-DED process is very powerful for different applications such as the repair operations and the production of functionally graded material, however the application is still limited and one of the main reasons is related to the lack of knowledge in the physics of the process mechanisms. The process is influenced by a huge number of parameters and three main mechanisms can be identi-fied. These mechanisms are the powder flow, the generation of the molten pool and the solidifica-tion process and for each of these mechanisms the process parameters have a different relevance. In this paper, a review of the main mechanisms and the relationship between the process parame-ters and the outcome of each step of the process is presented.

Directed Energy Deposition (DED) is a process that enables high-speed deposition with a sub-millimeter thickness using laser technology. Thus far, defect studies on additive manufacturing, including DED, have focused mostly on preventing pores and crack defects that reduce fatigue strength. On the other hand, evaporation products, fumes and spatters, generated by the high energy have often been neglected despite being some of the main causes of porosity and defects. In high-quality metal deposition, the problems caused by evaporation products are difficult to solve, but they have not yet caught the attention of metallurgists and physicists. This review examines the effect of the laser, material, and process parameters on the evaporation products to help obtain a high-quality metal film layer in thin-DED.

: TiAl6V4 alloy is widely used in selective laser melting and direct laser melting. In turn, works devoted to the issue of how the track stacking scheme affects the value of mechanical properties is not enough. The influence of the Ti6Al4V alloy track trajectories on the microstructure and mechanical properties during direct laser deposition is studied in this article for the first time. The results were obtained on the influence of «parallel» and «perpendicular» technique of laying tracks in direct laser synthesis. All studied samples have a microstructure typical of the hardened two-phase condition titanium. It is shown that the method of laying tracks and the direction of load application during compression testing relative to the location of the tracks leads to a change in the ultimate strength of the Ti-6Al-4V alloy from 1794 to 1910 MPa. The plasticity of the Ti-6Al-4V alloy obtained by direct laser alloying can vary from 21.3 to 33.0% depending on the direction of laying the tracks and the direction of the compression test. The hardness of alloys varies in the range from 409 to 511 HV and depends on the method of laying the tracks and the direction of hardness measurements.

Structure quality of LuFeO3 epitaxial layers grown by pulsed-laser deposition on sapphire substrates with and without platinum interlayers has been investigated by in-situ high-resolution x-ray diffraction (reciprocal-space mapping). The parameters of the structure such as size and misorientation of mosaic blocks have been determined as functions of the thickness of LuFeO3 during the PLD growth and for different platinum interlayers thicknesses up to 40 nm. The x-ray diffraction results combined with ex-situ scanning electron microscopy and high-resolution transmission electron microscopy demonstrate that the Pt interlayer significantly improves the structure of LuFeO3 by reducing the misfit of the LuFeO3 lattice with respect to the material underneath.

An amorphous silicon carbide (SiC) membrane with H2 permeance of 1.2E-7 mol･m^-2･s^-1･Pa^-1 and excellent H₂/CO₂ selectivity of 2600 at 673 K was successfully synthesized on a Ni-gamma-alumina-coated alpha-alumina porous support by counter diffusion chemical vapor deposition (CDCVD) using silacycrobutane (SCB) at 788 K. The dominant permeation mechanism for He and H₂ in the temperature range 323-673 K was activated diffusion. The SiC active layer was formed in Ni-gamma-Al₂O₃ intermediate layer. The thermal expansion coefficients mismatch between SiC active layer and Ni-gamma-Al₂O₃-coated alpha-Al₂O₃ porous support was eased by the low decomposition temperature of SiC source and membrane structure.

Cotton fiber development transition from elongation to secondary cell wall biosynthesis is a critical growth shifting phase that affects cotton fiber final length, strength and other properties. Morphological dynamic analysis indicates that an asynchronous fiber developmental pattern between two cotton species. The critical time point for Gh and Gb fiber elongation termination is, respectively, 23 and 27 days post-anthesis (dpa). The temporal changes of protein expression at three representative development periods (15–19, 19–23, 23–27 dpa) were examined in both species with iTRAQ technics. Strikingly, a large proportion of differentially expressed proteins (DEPs) was identified at 19–23 dpa in Gh or at 23–27 dpa in Gb, corresponding to their fiber developmental transition timing from elongation to secondary cell wall biosynthesis. To better understand fibers transitional development, we comparatively analyzed those DEPs in 19–23 dpa of Gh vs. in 23–27 dpa of Gb, and noted that these cotton species indeed share fundamentally similar fiber development features under the biological processes. It also showed that there have limited overlaps in both specific upregulated and downregulated proteins between the two species, suggesting specie-specific protein regulations in development. Proteomic profiling revealed dynamic changes of several key proteins and biological processes that potentially correlate with fiber development transition. During the transition, upregulated proteins mainly involved in carbohydrate/energy metabolism, oxidation-reduction, cytoskeleton, protein turnover, Ca²⁺ signaling etc, whereas important downregulated proteins mostly concentrated in phenylpropanoid and flavonoid secondary metabolism pathways. Several changed proteins in this key stage were also validated by qRT-PCR. Overall, the present study provides accurate pictures of the regulatory networks of functional proteins during the fiber developmental transition.

Hot stamping dies include cooling channels to treat the formed sheet. The optimum cooling channels of dies & molds should adapt to the shape and surface of the dies, so that a homogeneous temperature distribution and cooling are guaranteed. Nevertheless, cooling ducts are conventionally manufactured by deep drilling, attaining straight channels unable to follow the geometry of the tool. Laser Metal Deposition (LMD) is an additive manufacturing technique capable to fabricate nearly free-form integrated cooling channels and therefore shape the so-called conformal cooling. The present work investigates the design and manufacturing of conformal cooling ducts, which are additively built up on hot work steel and then milled in order to attain the final part. Their mechanical performance and heat transfer capability has been evaluated, both experimentally and by means of thermal simulation. Finally, conformal cooling conduits are evaluated and compared to traditional straight channels. The results show that LMD is a proper technology for the generation of cooling ducts, opening the possibility to produce new geometries on dies & molds and, therefore, new products.

Hf1-xZrxO2 (HZO) thin films are versatile materials suitable for advanced ferroelectric semiconductor devices. Previous studies have shown that the ferroelectricity of HZO thin films, can be stabilized by doping them with group III elements at low concentrations. While doping with Y improves the ferroelectric properties, there has been limited research on Y-HZO thin films fabricated using atomic layer deposition (ALD). In this study, we investigated the effects of Y doping cycles on the ferroelectric and electrical properties of as-deposited Y-HZO thin films with vaying compositions fabricated through ALD. The Y-HZO thin films were stably crystallized without the need for post-thermal treatment and exhibited transition behavior depending on the Y-doping cycle and initial composition ratio of the HZO thin films. These Y-HZO thin films offer several advantages, including enhanced dielectric constant, leakage current density, and improved endurance. Moreover, the optimized Y-doping cycle induced a phase transformation that resulted in Y-HZO thin films with improved ferroelectric properties, exhibiting stable behavior without fatigue for up to 1010 cycles. These as-deposited Y-HZO thin films show promise for applications in semiconductor devices that require high ferroelectric properties, excellent electrical properties, and reliable performance with a low thermal budget.

Ti-6Al-4V (TC4) titanium alloy parts were successfully fabricated by laser melting deposition (LMD)technology in this study. Proper normalizing temperatures were presented in detailed for bulk LMD specimens. Optical microscope, scanning electron microscopy, X-ray diffraction and electronic universal testing machine were used to characterize the microstructures, phase compositions, the tensile properties and hardness of the TC4 alloy parts treated using different normalizing temperature. The experimental results showed that the as-fabricated LMD speceimens microstructures mainly consisted of α-Ti phase with a small amount of β-Ti phase. After normalizing treatment, in the area of α-Ti phase, the recrystallized length and width of α-Ti phase both increased. When normalizing in the (α+β) phase field, the elongated primary α-Ti phase in the as-deposited state was truncated due to the precipitation of β-Ti phase and became a short rod-like primary α-Ti phase. In as-fabricated microstructure, the β-Ti phase was precipitated between different short rod-shaped α-Ti phases distributed as basketweave. After normalizing treatment at 990 for two hours with subsequent air cooling, the TC4 titanium alloy had significant different microstructures from original sample produced by LMD. Moreover, the mismatch of tensile and hardness property was mitigated in this heat treatment. So the normalizing treatment methods and temperature can be qualified as a prospective heat treatment of titanium alloy fabricating by laser melting deposition.

The fusion of surface-modified steel with tungsten carbide (WC) and NiCrBSi powder through laser metal deposition has emerged as a formidable strategy for fortifying components against wear and corrosion in extreme operating environments. Meticulous selection of WC content, innovative pre-alloying techniques, and precise control of laser metal deposition profoundly influence the mechanical properties and microstructural evolution of WC-NiCrBSi coatings applied to surface-enriched commercial alloy steel (805M2, 832M13, and 827M40). These tailored coatings exhibit exceptional resilience, ideal for harsh industrial settings in Oil and gas drilling, petrochemical, and Mining sectors. Advanced materials testing techniques, including scanning electron microscopy, light optical microscopies, and microhardness testing, unveil the innate hardness attributes, with findings highlighting the unassailable fortitude of the Mixed matrix layer's side face. The amalgamation of these testing methodologies with laser metal deposition promises an unparalleled path to extend the operational lifespan of critical components in challenging working conditions. The research horizon for WC-NiCrBSi coatings remains broad, with the potential to enhance durability, operational efficiency, and cost-effectiveness across diverse applications.

This article addresses the need to know the thermal conductivity in different filaments that this FDM technology uses. Because there are multiple applications that these additive manufacturing products play in the field of thermal insulation. For the study of thermal conductivity, the DTC-25 commercial conductivity measurement bench is used, where the tests will be carried out on a set of seven different materials with 100% fabrication density. From base materials such as acrylonitrile butadiene styrene (ABS) or polylactic acid (PLA), materials of high mechanical and thermal resistance, polyether ether ketone (PEEK) and high-performance polyetherimide thermoplastic (ULTEM), to materials with metal inclusions (aluminum 6061) that would later be subjected to thermal aftertreatments. The study shows how the parts manufactured with aluminum inclusion have a higher thermal conductivity, 0.40 ±0.05 W/m·K, compared to another material, such as TPU, of high mechanical and thermal resistance, with a conductivity of 0.26 ±0.05 W/m·K.

This paper investigates the impact of sediment deposition and inflow conditions on horizontal impact pressure and frequency analysis of bridge deck vibrations during flooding. Flooding-induced pressure and vibrations contribute to bridge collapse, and sediment deposition influences water flow and impact pressure. The study explores the relationship between sediment deposition height and impact pressure, revealing a significant increase as sediment approaches 50% of bridge deck clearance. Sediment amplifies impact pressure response to flow velocity changes. The dimensionless sediment deposition height has a greater influence on impact pressure compared to the inflow Froude number. Two distinct frequencies, dominant and secondary, are identified for impact pressure and water level fluctuations. Dominant frequencies positively correlate with sediment deposition height and Froude number, indicating an increasing trend. Secondary frequencies remain stable (0.31-0.58 Hz). These findings enhance understanding of flow dynamics and bridge-flow interaction in sediment-deposited channels, providing theoretical support for evaluating and managing disasters related to bridges in such environments. Overall, this research contributes to the field of bridge engineering and supports improved design and maintenance practices for bridges exposed to sediment-deposited channels.

Delayed atomic layer deposition (ALD) of ZnO, i.e., area selective (AS)-ALD, was successfully achieved on silicon wafers (Si/SiO2) terminated with tris(dimethylamino)methylsilane (TDMAMS). This resist molecule was deposited in a home-built, near atmospheric pressure, flow-through , gas-phase reactor. TDMAMS has been shown to react with Si/SiO2 in a single cycle/reaction and to drastically reduce the number of silanols that remain at the surface. ZnO was deposited in a commercial ALD system using dimethylzinc (DMZ) as the zinc precursor and H2O as the coreactant. Deposition of TDMAMS was confirmed by spectroscopic ellipsometry (SE), X-ray photoelectron spectroscopy (XPS), and wetting. ALD of ZnO, including its selectivity on TDMAMS – terminated Si/SiO2 (Si/SiO2/TDMAMS), was confirmed by in situ ellipsometry, ex situ SE, XPS, and/or high sensitivity – low energy ion scattering (HS-LEIS). The thermal stability of the TDMAMS resist layer, which is an important parameter for AS-ALD, was investigated by heating Si/SiO2/TDMAMS in air and nitrogen at 330 ºC. ALD of ZnO takes place more readily on Si/SiO2/TDMAMS heated in the air than in N2, suggesting greater damage to the surface heated in the air. To better understand the in situ ALD of ZnO, the data were also plotted as the normalized growth per cycle and to show the selectivity. Even one, short pulse of TDMAMS effectively passivates Si/SiO2. TDMAMS can be an effective small molecule inhibitor of ALD of ZnO on Si/SiO2 surfaces.

The photocatalytic biohydrogen generation using ZnO with the aid of simultaneous deposition of copper from an aqueous biomass-derivative glycerol solution was investigated. The effects of concentration of glycerol solution, Cu ion concentration and reaction temperature on biohydrogen generation were investigated. The photocatalytic biohydrogen production rate increased with increasing the concentration of aqueous glycerol solution, and the observed data could be fitted to the Langmuire-Hinshelwood kinetic models. The photocatalytic H2 production efficiency with ZnO could be significantly improved by simultaneous Cu deposition. The photocatalytic biohydrogen production rate was dependent on temperature, and increased with the increasing temperature. The possible mechanisms for oxidation of glycerol solution and photocatalytic hydrogen generation were proposed.

Over the last decade, a significant literature has emerged that advocates the potential of different Additive manufacturing (AM) technologies and printable polymeric materials. Nevertheless, large scale printing and complex geometric shapes, with curvatures and non-planar layer deposition, are a challenging process for the traditional gantry-based machine. The 3 degrees of freedom cartesian configuration restricted their capability to planar layered printing and restricted part dimensions. To date, many researchers have used industrial robots to overcomes this limitation. This review gives the reader a good overview of the FDM technique due to its scalability, cost efficiency and a wide range of material printability. A strong emphasis is laid on the PLA and PLA-based composites as promising materials for the FDM process applications. The second part of this paper links the successful use of these materials in the traditional printing process to large scale printing using the robot-based FDM process. This survey presents representative setups for robot-based AM and works that have been used these setups for non-planar material deposition. Finally, we conclude this paper by identifying opportunities for realizing new functional capabilities by exploiting robot-based AM, and we also present the future trends in this area.

The development of high complexity geometry parts is one of the main goals of the additive manufacturing technology. However, the failure of printed structures and the joining of different parts to create complex assemblies represents a real challenge in the research of efficient and sustainability techniques for the permanent assembly of polymers. Laser welding processes have been used as a single step method to join metals until years ago. Nowadays, the growing trend in the use of thermoplastics for additive manufacturing has led to the need to adapt this technique to materials with a very specific nature and more sensitive to thermal effects. Also, the possibility of transmitting the laser beam through transparent polymer layers allows to focus the energy supply on internal sections of the assembled components. In this research, an infrared laser marking system was used to join two different samples of polylactic acid manufactured by fused deposited modeling technology. In order to increase the effectiveness of the bonding process, a transparent and a dark sample have been used as assembly material, focusing the laser beam on the interface area of the two parts. By means of tensile tests, dimensional measurement and the use of optical microscopy techniques, a basis was established that links the supplied energy by laser to the joining performance.

Metal 3D printing technology is a promising manufacturing method. The quality of the printed product can pass for mechanical application, if the anisotropy of the microstructure, imperfections, deformation, and residual stress of the printed sample could be lower than the appropriate level or if they are fully illuminated. Thermal stress is one of the significant reasons for deformation in the 3D printed samples. Thermal stresses are the direct consequence of the local temperature gradient. In this research, the effect of the temperature printer’s chamber (from room temperature to 900 C) was studied on thermal stress and subsequent total deformation in the printed sample. The printed sample is a six-layers-printed walk, which could be considered as a building block of other complex shapes and give us inside about deformation. The computational results show a meaningful reduction in thermal stress and deformation at the higher temperature of the printer’s chamber. The lower final deformation of the printed sample is an important subject, especially for samples with complex shapes.

A conventional 2D numerical model is improved by incorporating three submodels to consider different effects of secondary flow and a module for cohesive sediment transport. The model is applied to a meandering reach of Yangtze River to investigate secondary flow effects on cohesive sediment deposition, and a preferable submodel is selected based on the flow simulation results. Sediment simulation results indicate that the improved model predictions are in better agreement with the measurements in planar distribution of deposition as the increased sediment deposits caused by secondary current on the convex bank have been well predicted. Secondary flow effects on predicted amount of deposition become more obvious during the period when the sediment load is low and velocity redistribution induced by the bed topography is evident. Such effects vary with the settling velocity and critical shear stress for deposition of cohesive sediment. The bed topography effects can be reflected by the secondary flow submodels.

Electrodeposition of cadmium telluride (CdTe) on fluorine doped tin oxide (FTO) using two electrode configuration was successfully achieved with the main focus on the growth temperature. The electroplating temperatures explored ranges between (55 and 85)℃ for aqueous electrolytes containing 1.5 M cadmium nitrate tetrahydrate (Cd(NO3)2 •4H2O) and 0.002 M tellurium oxide (TeO2). The ensuing CdTe thin-films were characterised using X-ray diffraction (XRD), UV-Vis spectrophotometry, scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and photoelectrochemical (PEC) cell measurements. The electroplated CdTe thin-films exhibit a dominant (111) CdTe cubic structure, while the crystallite size increases with the increase in the electroplating temperature. The internal strain, dislocation density and the number of crystallites per unit area decrease with increasing growth temperature. The optical characterization depicts that the CdTe samples show comparable absorbance and a resulting bandgap of 1.51±0.03 eV for as-deposited CdTe layers. A marginal increase in the bandgap and reduction in the absorption edge slope towards lower deposition temperatures were also revealed. The annealed CdTe thin-films showed improvement in energy bandgap as it tends towards 1.45 eV while retaining the aforementioned absorption edge slope trend. Scanning electron microscopy shows that the underlying FTO layers are well covered with increasing grain size observable relative to the increase in the deposition temperature. The energy dispersive X-ray analyses show an alteration in the Te/Cd relative to the deposition temperature. Higher Te ratio with respect to Cd was revealed at deposition temperature lower than 85℃. The photoelectrochemical cell study shows that both p- and n-type CdTe can be electroplated and that deposition temperatures below 85℃ at 1400 mV results in p-type CdTe layers.

The use of the LMD technology as a manufacturing and repairing technique in industrial sectors like the die and mold and aerospace is increasing within the last decades. Research carried out in the field of LMD process situates argon as the most usual inert gas, followed by nitrogen. Some leading companies have started to use helium and argon as carrier and shielding gas, respectively. There is therefore a pressing need to know how the use of different gases may affect the LMD process due to there is a lack of knowledge with regard to gas mixtures. The aim of the present work is to evaluate the influence of a mixture of argon and helium on the LMD process by analyzing single tracks of deposited material. For this purpose, special attention is paid to the melt pool temperature, as well as to the characterization of the deposited clads. The increment of helium concentration in the gases of the LMD processes based on argon will have three effects. The first one is a slightly reduction of the height of the clads. Second, an increase of the temperature of the melt pool. Last, smaller wet angles are obtained for higher helium concentrations.

A controlled ammonia (NH₃) release experiment was performed at a grassland site to quantify the effect of dry deposition, at the field scale between the source and the receptors (NH₃ measurement locations), on the estimates of emission rates by means of inverse dispersion modelling. NH₃ was released for 3 hours at a constant rate of Q = 6.29 mg s⁻¹ from a grid of 36 orifices spread over an area of 250 m². The increase in line-integrated NH₃ concentration was measured with open-path optical miniDOAS devices at different locations downwind of the artificial source. Using a backward Lagrangian stochastic (bLS) dispersion model (bLSmodelR), the fraction of the modelled release rate to the emitted NH₃ (Q_bLS/Q) was calculated from the measurements of the individual instruments. Q_bLS/Q was found to be systematically lower than 1, on average between 0.69 and 0.91, depending on the location of the receptor. We hypothesized that NH₃ dry deposition to grass and soil surfaces was the main factor responsible for the observed depletion of NH₃ between source and receptor. A dry deposition algorithm based on a deposition velocity approach was included in the bLS modelling. Model deposition velocities were evaluated from a ‘big‑leaf’ canopy resistance analogy. Canopy resistances (generally termed Rc) that provided Q_bLS/Q = 1 ranged from 75 to 290 s m⁻¹, showing that surface removal of NH₃ by dry deposition can plausibly explain the original underestimation of Q_bLS/Q. The inclusion of a dry deposition process in dispersion modelling is crucial for emission estimates, which are based on concentration measurements of depositing tracers downwind of homogeneous area sources or heterogeneously distributed hot spots, such as e.g. urine patches on pastures in the case of NH₃.

A simple and effective surface modification of polyester fabrics with sulfuric acid to improve the interfacial deposition of polypyrrole was presented in our work. A range of sulfuric acid concentrations were analyzed by studying water contact angle. Effect of sulfuric acid modification on the deposition of polypyrrole was investigated by sheet resistance and color depth of fabric samples. Polyester fabrics coated with polypyrrole layer were confirmed by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-Ray diffraction spectra (XRD), Fourier transform infrared spectroscopy (FTIR). XPS showed that sulphur containing functional groups were obviously appeared on the polyester fiber surface after modification, which were advantageous to promote the deposition of polypyrrole onto polyester fabrics. The improved deposition increased electrical conductivity of fabric samples.

The Review examines studies aimed at the organization of energy (non-mechanical) control of high-speed flow/flight using spatially multi-component plasma structures and combined energy deposition. The Review covers selected works on experimental obtaining and numerical modeling multi-component plasma structures and use of sets of actuators based on the plasma of such a spatially type for the purposes of control of shock wave/bow shock wave – energy source interaction, as well as control of shock wave – boundary layer interaction. A series of works on repetitive multiple laser pulse plasma structures is also analyzed from the point of view of examining shock wave/bow shock wave boundary layer interaction. Self-sustained theoretical models for laser dual-pulse, multi-mode laser pulses and self-sustained glow discharge are also considered. Separate sections are devoted to high-speed flow control using combined physical phenomena and numerical prediction of flow control possibilities using thermal longitudinally layered plasma structures. The wide possibilities for organization and applying spatially multi-component structured plasma for the purposes of high-speed flow control are demonstrated.

Hybrid manufacturing processes that combine additive and machining operations are gaining relevance in modern industry thanks to the capability of building complex parts with minimum material and, many times, with process time reduction. Besides, as the additive and subtractive operations are carried out in the same machine, without moving the part, dead times are reduced and higher accuracies are achieved. However, it is not clear whether the direct material deposition after the machining operation is possible or intermediate cleaning stages are required because of the possible presence of residual cutting fluids. Therefore, different LMD tests are performed on a part impregnated with cutting fluid, both directly and after the removal of the coolant by techniques such as laser vaporizing and air blasting. The present work studies the influence of the cutting fluid in the LMD process and the quality of the resulting part. Resulting porosity is evaluated and it is concluded that if the part surface is not properly clean after the machining operation, deficient clad quality can be obtained in the subsequent laser additive operation.

Cell sheet (CS) engineering using human MSC is of significant interest for regenerative medicine and this rapidly growing field translates to clinical use in a number of indications. Nevertheless, little is known of factors that define the timing of CS assembly from primary cultures which is important for planning treatments in both – autologous and allogeneic modes of use. We used a comparative in vitro approach with primary donors’ (n=14) adipose-derived MSC and evaluated the impact of healthy subject’s characteristics (age and sex), MSC culture features (population doubling time and lag-phase) and extracellular matrix (ECM) composition along with factors related to connective tissue formations (-SMA and FAP-) on CS assembly duration.

A self-protective metal/ liquid microcapsule composite plating coating has been prepared in our previous research. The release speed of liquid core material from microcapsules is crucial for the coating surface properties. The aim of this paper is to study the permeability rule of liquid microcapsules within composite coatings. According to permeability experimental data’s linear characteristics, multiple linear regression is firstly used to set up permeability model of liquid microcapsules. The results show that a reliable mathematical model about membrane porosity, viscosity of core material and membrane thickness is established under ambient temperature and moisture. Meanwhile, the predictive capacity and reliability of this model are analyzed carefully.

Obesity is a problem in the last decades since the development of different technologies forced the submission of a faster pace of life, resulting in nutrition style changes. In turn, domestic pigs are an excellent animal model in recognition of adiposity-related processes, corresponding to the size of individual organs, the distribution of body fat in the organism, and similar metabolism. The present study applied the next-generation sequencing method to identify adipose tissue (AT) transcriptomic signals related to increased fat content by identifying differentially expressed genes (DEGs), included long-non coding RNA molecules. The Freiburg RNA tool was applied to recognise predicting hybridisation energy of RNA-RNA interactions. The results indicated several long non-coding RNAs (lncRNAs) whose expression was significantly positively or negatively associated with fat deposition. lncRNAs play an essential role in regulating gene expression by sponging miRNA, binding transcripts, facilitating translation, or coding other smaller RNA regulatory elements. In the pig fat tissue of obese group, increased expression of lncRNAs corresponding to human MALAT1 was observed that previously recognised in the obesity-related context. Moreover, hybridisation energy analyses pinpointed numerous potential interactions between identified differentially expressed lncRNAs, and obesity-related genes and miRNAs expressed in AT.

Detection of formaldehyde is very important in terms of life protection, as it can cause serious injury to eyes, skin, mouth and gastrointestinal function if indirectly inhaled and hence researchers are putting effort in developing novel and sensitive device. In this work, we have fabricated an electro-chemical sensor in the form of a field effect transistor (FET) to detect formaldehyde over wide range (10 nM to 1 mM). For this, ZnO nanosheets (NS) were first synthesized by hydrothermal method with in-situ deposition on cleaned SiO₂ coated Si (100) substrate. The synthesized materials were characterized for morphology and purity and surface area (31.718 m²/g). The developed device was tested for formaldehyde detection at room temperature that resulted in a linear response with concentration (96%), sensitivity value of 0.27 mA/M/cm² and a low detection limit of 210 nM, and a high 0.93194 return.

We report on the development of chemical vapour deposition (CVD) based graphene field effect transistor (GFET) immunosensors for the sensitive detection of Human Chorionic Gonadotropin (hCG), a glycoprotein risk biomarker of certain cancers. The GFET sensors were fabricated on Si/SiO₂ substrate using photolithography with evaporated chromium and sputtered gold contacts. GFET channels were functionalized with a linker molecule to immobile anti-hCG antibody on the surface of graphene. Binding reaction of the antibody with varying concentration levels of hCG antigen demonstrated the limit of detection of the GFET sensors to be below 1 pg/mL using four-probe electrical measurements. We also show annealing can significantly improve the carrier transport properties of GFETs and shift the Dirac point (Fermi level) with reduced p-doping in back-gated measurements. The developed GFET biosensors are generic and could find applications in a broad range of medical diagnostics in addition to cancer, such as neurodegenerative (Alzheimer’s, Parkinson’s and Lewy body) and cardiovascular disorders.

This paper investigates the effects of various process parameters, specifically the substrate temperature, on weld track geometry in Directed Energy Deposition (DED) processes. A specialized experimental setup integrated within a DED machine facilitates controlled thermal conditioning of sample sheets. Through Design of Experiments (DoE) methods, individual weld marks are generated and analysed to assess geometric characteristics. Regression models are constructed to predict machine parameters for desired weld geometry at different substrate temperatures. Validation experiments confirm the accuracy and reliability of the regression models. Results show a consistent trend towards target geometric features across a broad range of substrate temperatures. Despite deviations in measured values, successful fabrication is achieved, demonstrating robust bonding between weld and substrate. Contact angle predictions exhibit precision within a partial temperature range for proper deposition. The developed model offers insights for optimizing DED process parameters to achieve desired weld characteristics, advancing the capabilities and reliability of additive manufacturing technology. Future work aims to refine the regression model and explore additional mathematical relationships for enhanced accuracy. An implication of this work is the potential to vary the local mechanical properties of parts by controlling the temperature profile while maintaining consistent geometric characteristics. By manipulating the substrate temperature, it may be possible to tailor the microstructure and mechanical properties of fabricated components in the future to meet specific requirements in different regions of the part.

Severe respiratory syncytial virus (RSV) infections in early life have been linked to the development of chronic airway disease. RSV is a potent inducer of reactive oxygen species (ROS) which contributes to inflammation and enhanced clinical disease. NF-E2-related factor 2 (Nrf2) is an evolutionary conserved redox-responsive protein that helps to protect cells and whole organisms from oxidative stress and injury. The role of Nrf2 in the context of viral-mediated chronic lung injury is not known. Herein, we show that RSV experimental infection of adult Nrf2 deficient BALB/c mice (Nrf2-/-; Nrf2 KO) is characterized by enhanced disease, increased inflammatory cell recruitment to the bronchoalveolar compartment, and a more robust upregulation of innate and inflammatory genes and proteins, compared to wild type Nrf2+/+ competent mice (WT). These events that occur at very early time points, lead to increased peak RSV replication in Nrf2 KO compared to WT mice (day 5). To evaluate longitudinal changes of the lung architecture, mice were scanned weekly by high-resolution micro-computed tomography (micro-CT) imaging up to 28 days after initial viral inoculation. Based on micro-CT qualitative 2D imaging and quantitative reconstructed histogram-based analysis of lung volume and density, we found that RSV infected Nrf2 KO mice developed significantly greater and prolonged fibrosis compared to WT mice. Results of this study underscore the critical role of Nrf2-mediated protection from oxidative injury not only in acute pathogenesis of RSV infection, but also in its long-term consequences of chronic airway injury.

This report describes the collection of a large dataset (6930 measurement) on dimensional error in the fused deposition modeling (FDM) additive manufacturing process for full-density parts. Three different print orientations were studied, as well as seven raster angles (0°, 15°, 30°, 45°, 60°, 75°, and 90°) for the rectilinear infill pattern. All measurements were replicated ten times on ten different samples to ensure a comprehensive dataset. Eleven polymer materials were considered: acrylonitrile butadiene styrene (ABS), polylactic acid (PLA), high-temperature PLA, wood-composite PLA, carbon-fiber-composite PLA, copper-composite PLA, aluminum-composite PLA, high-impact polystyrene (HIPS), polyethylene terephthalate glycol-enhanced (PETG), polycarbonate, and synthetic polyamide (nylon). The samples were ASTM-standard impact testing samples, since this geometry allows the measurement of error on three different scales; the nominal dimensions were 3.25mm thick, 63.5mm long, and 12.7mm wide. This dataset is intended to give engineers and product designers a benchmark for judging the accuracy and repeatability of the FDM process for use in manufacturing of end-user products.

This study investigated the characteristics of radio-frequency middle-pressure argon plasma used in the atomic layer deposition (ALD) of Al2O3 films. Based on the electrical characteristics, that is current, voltage, and phase shift between them, and stability of plasma plume, the optimum plasma power, allowing reliable switching on the plasma for any step of an ALD cycle, was determined. Spectral measurements were performed to determine the gas temperature and reactive species that could be important in the ALD process. The density of metastable argon atoms was estimated using tunable laser absorption spectroscopy. It was concluded that plasma heating of substrates did not affect film growth and proposed that the crystallization-enhancing effect of plasma was due to the action of OH radicals, produced in the plasma.

Fat has a high energy density and excessive fatness has been recognized as a problem for egg production and the welfare of chickens. The identification of a genetic polymorphism controlling fat deposition would be helpful to select against excessive fatness in the laying hen. This study aimed to estimate genomic heritability and identify the genetic architecture of abdominal fat deposition in a population of chickens from a Dongxiang blue-shelled local breed crossbred with the White Leghorn. A genome-wide association study wase conducted on abdominal fat percentage, egg production and body weights using a sample of 1534 hens genotyped with a 600K Chicken Genotyping Array. The analysis yielded a heritability estimate of 0.19 ± 0.04 for abdominal fat percentage, 0.56 ± 0.04 for body weight at 72 weeks, 0.11 ± 0.03 for egg production and 0.24 ± 0.04 for body weight gain. The genetic correlation of abdominal fat percentage with egg production between 60 and 72 weeks of age was 0.35 ± 0.18. This implies a potential trade-off between these two traits related to allocation of resource. Strong positive genetic correlations were found between fat deposition and weight traits. A promising locus close to COL12A1 on chromosome 3, associated with abdominal fat percent, was found in the present study. The other region located around HTR2A on chromosome 1, where allele substitution was predicted to be associated with body weight gain, accounted for 2.9% of phenotypic variance. Another region located on chromosome 1, but close to SOX5, was associated with egg production. These results may be used to influence the balanced genetic selection for laying hens.

Functionally graded materials (FGM) have attracted considerable attention in the field of composite materials and rekindled interest in research on composite materials, due to their unique mechanical response achieved through material design and optimization. Compared to conventional composites, FGMs offer several advantages and exceptional properties, including improved deformation resistance, improved toughness, lightness properties, and excellent recoverability. This study focused on the production of functionally graded (FG) polymer materials by additive manufacturing (AM) method. FG structures were produced by the Fused Deposition Modeling (FDM) method using Acrylonitrile benzidine styrene (ABS) and Polylactic acid (PLA) materials and tensile tests were performed according to ASTM D638. The effects of different layer thicknesses, volume ratios, and total thicknesses on mechanical behavior were investigated. In addition, tensile tests were carried out by producing single-layer samples at certain volume ratios to create a numerical model with the Finite element method to verify the experimental data. As a result of this study, it is presented that the FG structure produced with FDM improves mechanical behavior.

Directed energy deposition (DED) is an efficient method to fabricate functionally graded materials (FGMs) with gradient composition and complex structures, allowing for local tailoring of properties instead of the costly need for extraneous welds and joints. In this study, a FGM from stainless steel to Inconel alloy was successfully fabricated using the powder-based laser DED. A very refined grain structure has been observed in at the composition with 75 wt.% Inconel alloy content, which also exhibits the highest (entropy). For the first time, the post heat treatments, microstructure and aging precipitation behaviors of FGMs were systematically studied via experimental characterization and computation, to elucidate their effects on the gradient smoothing and mechanical properties. The diffusion and segregation of Ni, Nb and Ti elements underly the transformation mechanism between Laves, δ, γ’ and γ’’ phases during precipitation. Homogenization on FGMs not only eliminates the heterogeneity inherited from the AM process, but also provides a practical way to smoothen the gradient on composition and microstructure for the eventual good gradient properties. It has a direct influence on the following precipitation behaviors in the FGM, which highly relies on the diffusion degree of the elements in the matrix and grain boundaries. The high-throughput thermodynamic modeling and kinetic modeling were exploited to evaluate the experimental microstructure and address computational uncertainty using different thermodynamic conditions and databases, which enables an accelerated design through local tailoring of process-structure-property relationships to develop new functional materials.

This case report describes a 71-year-old female with multiple comorbidities who presented with symptoms suggestive of stroke and was subsequently found to have severe acute kidney injury (AKI) due to acute interstitial nephritis (AIN). The patient has normal kidney function at baseline. She has been on hydrochlorothiazide and metoprolol succinate for hypertension for several years. Due to severe acute kidney injury, a kidney biopsy was performed, revealing severe Acute Interstitial Nephritis secondary and multiple intratubular oxalate crystals. The patient's renal function improved after withdrawing HCTZ, volume repletion and initiating prolonged prednisone taper. We attempt to provide some insights through our paper into the mechanism of acute renal failure from crystal nephropathy and its management.

Airborne microplastic (MP) is an emerging pollutant, still under-characterised and insufficiently understood. Detailed description of MP air pollution is crucial as it has been identified in human lungs and remote locations, highlighting atmosphere as medium of MP dispersion and transportation. The lack of standardization of methods for measuring and further monitoring of the MP pollution is an obstacle towards the assessment of health risks. Since the first recognition of MP presence in the atmosphere of Krakow in 2019, this research was conducted to further characterise and develop the methods for qualitative and quantitative analysis of airborne MP (ATR-FTIR, Pyr-GC-MS, SEM-EDS) and pre-treatment of samples.The data was gathered in seven cycles, from June 2019 to February 2020. Methods used in the study allowed the identification and analysis of the changing ratio of the different types of synthetic polymers identified in the atmospheric fallout (LDPE, Nyl-66, PE, PET, PP, PUR). Observations of interactions between MP particles and environment were made with analyses of surface changes due to the degradation. Mineral phases attached to the MPs’ surfaces, with some of the inorganic contaminants transported on these surfaces, determined to also be of anthropogenic origin.Methodology proposed in this study, allows further characterisation of MP from multiple locations to provide highly comparable data, leading to the identification of the sources of this phenomenon, as well as seasonal changes.

Laser metal deposition with wire (LMD-w) is a developing additive manufacturing (AM) technology that has a high deposition material rate and efficiency, and is suitable for fabrication of large aerospace components. However, control of material properties, geometry, and residual stresses is needed before LMD-w technology can be widely adopted for the construction of critical structural components. In this study, we investigated the effect of interlayer cooling time, clamp constraints, and tool path strategy on part distortion and residual stresses in large-scale laser additive manufactured Ti-6Al-4V components using finite element method (FEM). The simulations were validated with the temperature and the distortion measurements obtained from a real LMD-w process. We found that a shorter interlayer cooling time, full clamping constraints on the build plates, and a bidirectional tool path with 180⁰ rotation minimized part distortion and residual stresses and resulted in symmetric stress distribution.

As a photo-catalytic titanium oxide film deposition process, thermal spray is hoped to be utilized practically on the condition that it is relatively easy to deposit anatase rich films. However, because of its high equipment and feedstock powder costs, it is very difficult to introduce thermal spray equipment into small companies. In this study, to develop a low cost thermal spray system, low power atmospheric suspension plasma spray equipment with titanium hydroxide suspension created by hydrolysis of titanium tetra iso butoxide using Ar, N2 as working gases. For avoiding sedimentation of the hydroxide particles in the suspension, mechanical milling of the suspension was conducted to create colloidal suspension before using it as feedstock. Moreover, an Ultrasonic wave container was used to keep the suspension particles moving while the spray process was conducted. After the film deposition, with As for the coating, anatase rich TiO2 film could be obtained. For characterization of the film, microstructure observation by optical microscope and X-ray diffraction was carried out. Consequently, by creation of colloidal suspension, deposition could be conducted without sedimentation of the hydroxide particle in the suspension during operation. Besides, it was proved the film had enough photo-catalytic property to decolor methylene-blue droplet