The article presents results of research consisting in an attempt to assess the influence of temperature, heating time and cooling method on microstructure and residual strength properties of steel previously tempered during the production process. Simulated environmental conditions to which high-strength bolts, commonly used in steel construction, were subjected, were intended to reflect conditions of a natural fire that may occur in public facilities where the obligation to ensure safety of users and rescue teams is of key importance, also required by law. Furthermore, the tests carried out also comprised a simulated effect of a rescue and firefighting operation using shock, rapid cooling of some of the heated bolts. Samples cut out from the tested bolts, after they were properly prepared, were subjected to microstructural tests using light microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), phase analysis with the use of an X-ray diffractometer (XRD) and quantitative analysis of the microstructure involving, inter alia, measuring the surface area of grains, their equivalent diameter and mean diameter. As a result of the tests, considerable microstructure changes were identified occurring in the bolt material as a result of exposing it to fire conditions, leading to a change in key, from the point of view of structural safety, mechanical properties. The results of the microstructure tests were compared with the results of previous strength tests, including hardness of the material after the heat treatment and the residual tensile strength of the material Rm. A conducted comparative analysis showed a significant effect of all such factors as the temperature level of the simulated fire, its duration and the fire-fighting method on the mechanical properties of bolts. Results obtained were provided with required comments and the concept of using the microstructure for the post-fire assessment of steel structures was referred to.

It is important to realize the transformation behavior of wüstite because it greatly affects the final structure of the oxide layer and the surface quality of the steel products. In the present study, the transformation behaviors of the wüstite layer are examined under nearly-oxygen-free conditions, to simulate the cooling processes after the hot rolled strip is coiled. As the single phase wüstite was prepared at 950˚C, the 460˚C transformed oxide layer was composed of a mixture of iron and magnetite formed through eutectoid reactions. For the 750˚C-fabricated wüstite, only magnetite was observed after transformation, without iron precipitates and residual wüstite. It is speculated that the unusual transformation behavior of the low-temperature-made wüstite results from the pseudo-structural intermediate phase transformation between wüstite and magnetite. This pseudo-structure is a pre-transformed wüstite and of various concentration of ferrous ion, which is determined by the fabrication conditions. During the hot strip mill process, the so-called wet scale, wüstite, is produced continuously from finish mill to laminar flow sections and ended at 570˚C. Consequently, the final eutectoid transformation below 570˚C is dominantly controlled by the surface temperature ranged from 750˚C to 950˚C for low carbon steel.

Clinching is a manufacturing method of mechanical joining two or more materials without the use of heat or additional components. This process relies on high plastic deformation to create a secure bond. Clinching technology is widely used for joining various grades and thickness of materials. Especially in the automotive industry, clinching is an alternative to spot resistance welding. However, the load-bearing capacity of clinched joints is comparatively lower when compared to resistance spot welded joints. This research aimed to enhance the load-carrying capacity of clinched joints. Experimental tests were conducted on clinched joints with locally modified microstructures to optimize their placement within the joint. The microstructure distribution in the clinched joint region was analysed using light and scanning electron microscopy, as well as microhardness measurements. Two material grades, micro-alloyed steels HX420LAD+Z and dual-phase ferritic-martensitic steels HCT600X+Z, were tested. Each grade underwent five groups of ten samples, subject to identical experimental conditions of local heating by resistance spot welding (RSW) and clinching. The application of RSW to the clinched joint area resulted in increase of load-bearing capacity for both joined types of materials.

Despite significant advances in metallurgy and the potential to create high and very high-strength steel, all international specifications for steel design provided little information about the limits of slenderness for high-strength steel sections (HSSs) and didn’t give anything about the design of very high-strength steel sections (VHSSs). The American structural steel design specification covers circular hollow sections (CHS) of steel grades up to S690, while it isn't in ANSI/AISC 360-16 and ASTM A514/A514M. Euro code EN 1993-1-1 can be applicable only to steel grades up to S460. EN 1993-1-3 and EN 1993-1-12 contain supplementary rules for cold-formed members and HSS (S460- S700), respectively. Though ductility requirements for (HSS) are specifically established in EN 1993-1-12, it is largely a continuation of the normal-strength-steel design procedures standardized in EN 1993-1-1, where (HSSs) are largely treated as normal-strength steels in these rules, and the same design approaches are used. The behavior of high and very high-strength steel circular hollow sections under axial compression load is studied in this research. A total of 16 nonlinear finite-element (FE) models were generated to replicate stub column tests that were experimentally tested by others in previous research. Hence, a parametric study is conducted using forty FE models developed to investigate the local buckling behavior under various slenderness ratios comprehensively. The developed models cover slenderness ratios ranging from 20 to 1226 and steel grades S460 and S1100 with yield stress equal 460 MPa and 1152 MPa, respectively. The FE results were combined with 105 previously collected experimental results to assess the applicability of existing codified design methodologies in the Euro code and the North American codes of cold-formed CHS. Based on the results of this study, new cross-sectional slenderness limits and new design equations for more efficient simple designs were presented for high and very-high strength steel circular hollow sections and Compared with the results of experimental tests and FE models.

The effect of rare earth Pr6O11 on the microstructure and mechanical properties of high-strength steel weld metal was investigated by optical microscopy, scanning electron microscopy and mechanical testing. Three different contents of Pr6O11 were added to the flux-cored wires. The results showed that the addition of 1% Pr6O11 can promote the refinement and spheroidization of inclusions, refine the grains, form acicular ferrites, and significantly improve the toughness of weld metal. The addition of Pr6O11 promoted the formation of rare earth composite inclusions and acicular ferrites in the weld metal, refined the lath microstructure, inhibited the formation of martensite and bainite. The crack formation mode changed from the boundary cracking of the bainite clusters caused by the surface shear stress to the surface shear stress-induced decohesion of inclusion. However, excessive addition of Pr6O11 will reduce the number of inclusion nucleation and deteriorate the mechanical properties. The wire No.2 with 1% Pr6O11 had the good comprehensive mechanical properties, and the corresponding values were 835MPa of tensile strength and 72 J of impact toughness. These findings suggest that the control of Pr6O11 can be an effective way to improve the impact toughness of weld metal.

The effect of Pr6O11 on the microstructure and mechanical properties of high-strength steel weld metal was investigated by optical microscopy, scanning electron microscopy and mechanical testing. Three different contents of Pr6O11 were added to the flux-cored wires. The results demonstrate that the addition of 1% Pr6O11 can promote the refinement and spheroidization of inclusions, refine the grains, form acicular ferrites in the weld metal, and significantly improve the toughness. The addition of Pr6O11 promoted the formation of rare earth composite inclusions and acicular ferrites in the weld metal, refined the lath microstructure, inhibited the formation of martensite and bainite. The crack formation mode changed from the boundary cracking of the bainite clusters caused by the surface shear stress to the surface shear stress-induced decohesion of inclusion. Excessive addition of Pr6O11 will reduce the number of inclusion nucleation and deteriorate the mechanical properties. The wire No.2 with 1% Pr6O11 had the good comprehensive mechanical properties.

The use of new developed high-strength steel in concrete members can reduce steel bars congestion and construction costs. This research aims to study the behavior of concrete columns reinforced with new developed high-strength steel under eccentric loading. Ten reinforced concrete columns were fabricated and tested. The test variables are transverse reinforcement amount and yield strength, eccentricity, and longitudinal reinforcement yield strength. The failure patterns are compression and tensile failure for columns subjected to small eccentricity and large eccentricity, respectively. The same level of post-peak deformability and ductility only can be obtained with lower amount of transverse reinforcement when high-strength transverse reinforcements are used in columns subjected to small eccentricity. The high-strength longitudinal reinforcement can improve bearing capacity and post-peak deformability of concrete columns. Besides, three different equivalent rectangular stress block (ERSB) parameters in predicting bearing capacity of columns with high-strength steel were discussed based on test and simulated results. It is concluded that the Code of GB 50010-2010 overestimates the bearing capacity of columns with high-strength steel, whereas bearing capacities computed using Codes of ACI 318-14 and CSA A23.3-04 agree well with test results.

In some sour reservoirs and tertiary oil recovery blocks, SO₄^2- in solution can cause the corrosion and corrosion fatigue of the sucker rods. In this paper, the corrosion behaviors of super-strength sucker rod FG20 (16Mn2SiCrMoVTiA) steel in the well fluid are investigated by electrochemical measurements, and electron probe micro-analyzer (EPMA) analysis. The results show that FG20 steel has a favorable corrosion resistance in neural solutions. When the hydrogen ion content increases, the hydrolysis of SO₄^2- greatly accelerates the corrosion of FG20 steel. The energy dispersive X-ray(EDX)results demonstrate that the corrosion process of FG20 steel in neural well liquid is an oxygen concentration process, and the protective FeCO₃ and Fe₂O₃ on the surface of the samples can prevent further corrosion. With the increase of the acidity in the well liquid, the corrosion process converts into a sulphide concentration process, and the sloppy FeS and mackinawite film cannot provide effective protection for the specimens, resulting in the increase of corrosion rate.

With continuous increase in integration of the semiconductor devices, the requirements on size accuracy and surface quality of the etched lead frame are higher. The etchant is a key factor on etching process and etched surface quality, while effects of the difference in etchants on microscopic etched surface morphology of the Cu alloy have not been directly studied. In this study, the aqua regia, acidic FeCl3 and CuCl2 solutions were used as etchants, and the CuCrSn alloy specimens with different microstructure were etched and characterized. The results show that the etching rate in aqua regia is high, and the grain orientation, grain boundary (GB) and dislocation have significant influence on the local etching rate. The preferential etching of some atomic planes forms steps between grains with different orientations, and the preferential etching around the GB and dislocation group forms grooves, resulting in high surface roughness. For etching of the FeCl3 and CuCl2 etchants, the steps and grooves become blurred, and almost invisible on the surface etched by the CuCl2 etchant, thus the surface roughness is much lower. The CuCrSn alloy surface etched by the aqua regia is clean, with little Cr-rich particles, while high density Cr-rich particles are remained on the surfaces etched with the FeCl3 and CuCl2 etchants. For the same kind of etchant, the ion concentration can affect the etching mechanism and etching surface morphology.

Hybrid reinforcement in a composite material (CM), in many situations, allows better govern material mechanical properties. Polymer matrix CM plate is reinforced with small particles and macro-fibers. Particles are oil shale ash (OSA) powder, macro-fibers – basalt fiber threads im-pregnated by matrix material. With the goal to find out elastic properties of the matrix- polymer with OSA, samples with its different concentrations were experimentally fabricated and their elastic properties were experimentally measured. Obtained data were used in numerical model-ling. Was observed polymer matrix composite slab, reinforced with OSA and three-dimensional (3D) basalt fiber fabric. Fabric are forming threads impregnated by matrix (polymer resin mixed with OSA particles). Damage accumulation in the stretched slab was modelled. Impregnated thread, in the modelling, is observed as a macro-fiber (MF) with averaged elastic properties. With the load increase MF in the material began to break. At first, appeared isolated single breaks. A probabilistic sequential MF rupture accumulation model was accepted and numerical-ly realized. The geometry of the reinforcing knitted fabric was modeled using the Leaf and Glaskin approach. In the knitted fabric highly, stressed MF cross-sections are observed as po-tential location where thread breakage can occur. If one thread breaks, the cross-sections of the adjacent threads experience the overload caused by this rupture. More overloaded crossection in the adjacent overloaded thread breaks and we obtain two adjacent broken MF designated as a defect with the size j=2. The probabilities of obtaining defect consisting of at least 2, 3, … j adjacent broken MF in the plate were calculated. The calculations continued until the rupture process becomes unstable (j→∞). The overstresses on adjacent threads in the CM were calculat-ed using the FEM three-dimensional numerical approach. Analytical and stochastic methods were used for the load-carrying capacity determination and different size defects accumulation in the hybrid composite material (HCM) plate. Also, was calculated the probability of the plate rupture.

This study deals with two different aspects of the high-strength low-alloyed 1100 MC steel. The first is associated with the remarkable heterogeneity in the surface state produced during sheet rolling with respect to the sheet width. The variable-thickness surface layer exhibits a microstructure different from that of the deeper bulk. Variation of the thickness of the thermally softened near-surface region strongly affects Barkhausen noise, as well. This technique can be considered a reliable tool for monitoring the aforementioned heterogeneity. It can also be reported that the opposite sides of the sheet are different with respect to the surface state, heterogeneity distribution, and corresponding Barkhausen noise. These aspects indicate the different conditions during hot rolling followed by rapid quenching on the upper and lower rollers. The second aspect is related to the remarkable asymmetry of Barkhausen noise emission with respect to two consecutive bursts. This asymmetry is due to the presence of remnant magnetisation in the sheet produced during manufacturing. The remnant magnetisation is coupled to the magnetic field produced by the excitation coil of the Barkhausen noise sensor and strongly contributes to the aforementioned asymmetry. As soon as sufficient removal of this remnant magnetisation is carried out in the vanishing magnetic field (demagnetisation), the aforementioned remarkable asymmetry is fully lost.

Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) is developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) are comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibits a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at -20 ℃. In contrast, the HR-QT steel exhibits tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consists of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reaches 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared to the HR-QT process, the TMCP-DQP process results in finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieves the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilizes the RA through carbon enrichment, while the relaxation stage reduces a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminates internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.

China is facing the development requirements of the dual carbon goal and the construction needs of resilient cities. Currently, high-strength composite structural systems are a feasible solution, but their research and application in the construction field are insufficient, especially for the combination forms of concrete above C100 and steel above Q550. In response to this issue, this paper proposes a new high-performance structural system, namely the composite frame - high-strength steel plate wall core tube resilient structure system, which includes high-strength steel plate (Q550) - ultra-high strength concrete (C100) shear walls, replaceable energy dissipation coupling beams, and composite frames. Taking a 200 meter building as an example, this paper designs and establishes calculation models for a conventional reinforced concrete frame-core tube structure and a high-performance structure based on PKPM software, and establishes elastoplastic analysis models for both based on SAUSAGE software, and then conducts dynamic elastoplastic time history analysis and seismic resilience assessment of structures under design basis earthquakes (DBEs), maximum considered earthquake (MCEs) and extremely rare earthquakes (EREs). Research has shown that compared to conventional structures, new high-performance structures can effectively reduce the size of shear walls, reduce the self-weight of the structure, and enhance the space for building use; The story drift ratio has higher redundancy than specification limits, lower plastic damage and overall stiffness degradation of the structure, and better seismic performance; The seismic resilience has significantly improved, especially in the case of casualties, which can better ensure the safety of people's lives and property.

This paper presents a review on numerical and experimental methods to predict fracture of ad-vanced high strength steels (AHSS). AHSS are widely processed through sheet metal forming processes. Although being an excellent choice when lightweight, high strength and ductility are critical factors, their multi-phase microstructure accentuates forming challenges. To accurately model forming behavior, necking based failure criteria as well as direct fracture models require improvements. As a necking based failure model, the conventional forming limit diagram/curve (FLD/FLC) presents limitations such as in estimating direct fracture (surface cracks, edge cracks, shear cracks), as well as deformation histories under nonlinear strain paths. Thus, significant re-search efforts are being made towards the needs of advanced fracture constitutive models capa-ble of predicting fracture scenarios without necking, more frequently observed in the realm of AHSS. Scientific community research is divided into several directions aiming at improving the forming and fracture behavior accuracy of parts subjected to sheet metal forming operations. In this review paper, a comprehensive overview on ductile fracture modeling is presented. Firstly, the FLD/FLC limitations modeling fracture behavior in sheet metal forming operations are stud-ied. Followed by the recent trends in constitutive material modeling. Afterwards, material char-acterization methods advancements to cover a broad range of stress states are comprised. Final-ly, damage and fracture models predicting failure in AHSS are investigated. This review paper supplies relevant information on the current issues the sheet metal forming community is chal-lenged with due to the trend towards AHSS employment in the automotive industry.

This paper analyzed the main diseases of the friction high-strength bolt (FHSB) joints in order to study the characteristics of the corrosion products of the joints in steel bridge and the influence factors. Seven representative FHSB connection pairs and eight steel plate samples were selected from the Dongying Shengli Yellow River Bridge, which has been in operation for 33 years. Then Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS) and X-Ray Diffraction (XRD) were used to analyze the microscopic morphology and chemical composition of the corroded surface of the samples. Finally, this paper discussed the relationship between the corroded sample surface and the environmental corrosion. The research results showed that construction quality problems, such as non-standard hole expansion, segmental slab joint dislocation and contact surface pollution, accelerated corrosion of the contact surface. With the increase of corrosion degree of joints, the contact surface of aluminum spraying layer gradually changed from a rugged and dense state to a smooth and porous powder state. With the corrosion of the steel plate substrate, the contact surface gradually changed from a fluffy stratified state to a surface bonding state. It was inferred that the friction coefficient of the FHSB connection node on the corroded aluminum sprayed contact surface first decreased and then increased. The corroded node samples detected not only a large number of S and Cl elements, but also the oxides of Mn, Si and other elements as well as FeS. It was speculated that node corrosion was also related to atmospheric (acid rain) and industrial dust and other corrosive environments. Almost all samples detected the component SiO2 of the Yellow River soil, as well as Mg, Ca, K, Na and other elements at the same time, which is basically consistent with the component elements of the Yellow River soil. Therefore, it was inferred that it was related to the inclusion of the Yellow River soil.

In this study, the effect of hot stamping forming process on the properties change of compound layer in Al–Si coated high-strength steel sheet with different thickness was investigated. The coating layer in hot stamped high-strength steel sheet was composed of a diffusion layer and a compound layer. As the hot stamping temperature and holding time for forming increased, the thickness of the compound layer in the Al–Si coated high-strength steel sheet increased. The thickness of coating layer with the hot stamping for 500 sec at 890, 910 and 950 °C was obtained 8.9, 11.8, and 20.6 micrometer, respectively. The thickness of coating layer with hot stamping for 180, 500 and 550 sec at 910 ^oC was obtained 5.7, 11.8, and 17.8 micrometer, respectively. The compound layer in hot stamped high-strength steel sheet with Al–Si coating layer consists of Al_5.4Fe₂ and Fe₂Si phases. In the compound layer, Al and Si were irregularly distributed.

The microstructure and hardness along the thickness direction of a water quenched, high-strength thick plate with a thickness of 40 mm were investigated with three specimens from the thick plate: surface, 1/4t, and 1/2t (center) thickness, and the phase transformation behavior of the thick plate according to the cooling rate was analyzed through dilatometric experiments. Finally, the cooling rate for each thickness of the thick plate was estimated by comparing the microstructure and hardness of the thick plate along the thickness with those of the dilatometric specimens. Martensite microstructure was observed on the surface of the water quenched thick plate due to the fast cooling rate. On the other hand, an inhomogeneous microstructure was transformed inside the thick plate due to the relatively slow cooling rate and central segregation of Mn. A small fraction of bainite was shown at 1/4t thickness. A banded microstructure with martensite and bainite resulting from Mn segregation was developed at 1/2t; that is, the full martensite microstructure was transformed in the Mn-enriched area even at a slow cooling rate due to high hardenability, but a bainite microstructure was formed in the Mn-depleted area owing to relatively low hardenability. A portion of martensite with fine cementite at the surface and 1/4t was identified as auto-tempered martensite with a Bagaryatskii orientation relationship between the ferrite matrix and cementite. The microstructure and hardness as well as dilatation were investigated at various cooling rates through a dilatometric experiment, and a continuous cooling transformation (CCT) diagram was finally presented for the thick plate. Comparing the microstructure and hardness at the surface, 1/4t, and 1/2t of the thick plate with those of dilatometric specimens cooled at various cooling rates, it was estimated that the surface of the thick plate was cooled at more than 20 oC/s, whereas the 1/4t region was cooled at approximately 5 ~ 10 oC/s during water quenching.

Effects of oxygen content on microstructure and creep property of FGH96 superalloy were investigated. When oxygen content increased from 135ppm to 341ppm, prior particle boundary (PPB) rose from degree 2 to degree 3, and the size of γ′ phase on PPB enlarged from 1.07μm to 1.27μm, and MC carbide size grew from 77.4nm to 104.0nm. Meanwhile, the steady creep rate accelerated form 4.34×10-3 h-1 to 1.87×10-2 h-1, and the creep rupture life shortened from 176h to 94h, and the creep rupture mode transferred from intergranular and transgranular mixed fracture to along PPB fracture. During creep, the micro-twins formation and gliding will be restrained by ∑3 boundaries. FGH96 superalloy with higher oxygen content contains less ∑3 boundaries and its micro-twins cross slipped instead of single direction slip in lower oxygen content superalloy. Consequently, specimen with higher oxygen content creeped faster and raptured earlier.

Composites, and especially carbon fiber reinforced plastics (CFRPs), are increasingly used in the automotive, aerospace, and aviation industries, and as a result, CFRP production has increased dramatically, leading to a corresponding increase of waste. Landfill and incineration of waste are likely to be restricted as a result of the legislation, thus highlighting the need for efficient recycling methods for CFRPs. However, the recycling of CFRP is very challenging, mainly due to the difficulty of removing the thermosetting matrix. This study reports a pre-screening of the solvolysis recycling process for CFRPs based on the mechanical properties of the recovered fibers. To this end, solvolysis tests were conducted on unidirectional CFRP samples under supercritical and subcritical conditions using acetone and water. The solvolysis tests were conducted for various conditions of temperature, pressure, and reaction time. The efficiency of the recycling processes has been evaluated through a morphological and a mechanical characterization of the recovered fibers. In most cases, the decomposition efficiency of the epoxy resin, measured in terms of mass, ranged between 90 and 100%. Moreover, the scanning electron microscopy images of the recovered fibers showed negligible traces of resin residues and no detectable signs of physical damage or any changes in morphology with regard to diameter. Finally, the single-fiber tension tests revealed that that the recovered fibers retained more than 61% of their initial Young's modulus and 70% of their tensile strength.

The current paper aims to study the impact properties of additively manufactured Maraging steel (1.2709) using laser powder bed fusion (PBF-L) processing. The specimens were manufactured using 3Dsystems ProX 300 equipment under constant specific power input, or Andrew Number. The interactions between the build strategy and parameters, such as Hatch spacing and Scan speed was, and the impact strength and fracture were investigated. The Impact energy anisotropy was also investigated parallel and perpendicular to the build direction. Instrumented impact testing was performed, and the fractography supported that the fusion zone geometry dictated the fracture behaviour. The influence from gaseous elements such as Nitrogen, Oxygen and Hydrogen was found insignificant at the levels found in the printed material.

This study delves into the atmospheric corrosion behavior of chromium-free complex-phase steel (CP), specifically investigating the influence of wet/dry frequency and ratio in cyclic corrosion tests (CCT). The study employs a modified ISO 14993 standard CCT method, which involves salt spray, dry, and wet stages. After 15 and 30 CCT cycles, mass loss, maximum corrosion depth, and corrosion products were analyzed to gain insights into corrosion mechanisms. In general, increasing the frequency and wet/dry stage ratio in CCT extends the time for autocatalytic reactions to occur, leading to accelerated localized CP corrosion and increased pitting factors. However, as the rust layer thickens, uniform corrosion may also intensify, so careful considerations are necessary. This study underscores the importance of controlling the frequency and ratio of wet/dry stages in CCT for effectively analyzing localized corrosion behavior in specimens.

Joining of aluminium alloys to steels has been extensively studied, especially in the automotive sector. However, aluminium alloys are known to be difficult to join with steels when methods involving fusion welding are used because of hot cracking problem. Hence, a high strength joint between these dissimilar metals would be of benefit especially in reducing the weight of products. In this work the torch brazing method was applied to join AR500 steel with AA7075 aluminium alloy using Al-Si-Zn base filler metal at various flame times. The effect of the brazing work on the intermetallic phase formation and the mechanical strength of the joints were investigated. In this work, the maximum shear load obtained was 6460 N and the presence of the intermetallic phases had reduced the shear strength of the brazed joints. However, the torch brazing process using Al-Si-Zn filler metal had successfully facilitated the joining of these dissimilar metals.

The domestic ducks (Anas platyrhynchos domesticus) are resistant to most of the highly pathogenic avian influenza virus (HPAIV) infections. In this study, we characterized the lung proteome and phosphoproteome of ducks infected with HPAI H5N1 virus (A/duck/India/02CA10/2011/Agartala) at 12 hr, 48 hr and 5 days post infection condition. Total 2082 proteins were differentially expressed and 320 phosphorylation sites mapping to 199 phosphopeptides corresponding to 129 proteins were identified. Functional annotation of proteome data analysis reveals activation of RIG-I-like receptor and Jak-STAT signaling pathways, that lead to induction of interferon stimulated genes (ISGs) expression. The pathway analysis of phosphoproteome datasets also confirms the activation of RIG I, Jak-STAT signaling, NF-kappa B signaling and MAPK signaling pathways in the lung tissues. The induction of ISGs proteins (STAT1, STAT3, STAT5B, STAT6, IFIT5 and PKR) establishes protective antiviral immune response in duck lung tissue. Further, the protein-protein interaction network analysis identified proteins like AKT1, STAT3, JAK2, RAC1, STAT1, PTPN11, RPS27A, NFKB1 and MAPK1 as main hub proteins that might play important roles in disease progression in ducks. Together, functional annotation of proteome and phosphoproteome datasets reveals the molecular basis of the disease progression and disease resistance mechanism in ducks infected with HPAI H5N1 virus.

Selective laser melting (SLM) is a commonly used laser powder bed technique where the final properties are influenced by many different powder related properties, such as particle size distribution, chemical composition and flowability. In applications where high hardness, wear resistance, strength and good heat properties are required, high speed steels (HSS) are widely used today. HSS has high carbon content and are therefore considered as unweldable. The rapidly growing implementation of AM technologies has led to a growing range of new applications and demands for new alloys and properties. The interest in being able to manufacture HSS by SLM without cracking is therefore increasing. In SLM, it is possible to preheat the base plate to a few hundred degrees Celsius which has been used for HSS and proved successful due to reduced thermal gradients. In this study, the properties of SLM produced high speed steel PEARL Micro®2012 with a carbon content of 0.61 wt.-% have been investigated and compared to those of a forged and rolled PM-HIP counterpart ASP®2012.

Microscopic vision plays an important role in automated micro-assembly. However, some uncertain factors in the assembly process, such as occlusion and stains can lead to the mistakes of feature extraction. Herein, to solve the problem, the deep learning techniques are introduced into the feature recognition tasks, focusing on the attention mechanism and visualizing CNNs for DL-based microscopic vision. The main contributions are summarized as follows: The CBAM attention mechanism is combined with the YOLOv5 algorithm to improve the accuracy and robustness of feature extraction. The micropart feature occlusion experiment results show that at 70% occlusion degree, YOLOV5-CBAM can reach 97.9% [email protected], which is 4.6% higher than the original one. Visualization analysis of DL-based model is conducted using Grad-CAM to make the decision result more transparent and avoid potential visual detection risks during assembly. The heatmap matching degree between GT area and high-light area is increased by 27.81% on average, which further verify the effectiveness of attention mechanism in micropart feature localization. Additionally, micropart surface stain and droplet quality classification models based on ResNet50 are trained to replace the manual sorting. The visual results are consistent with human eye discernment and judgement, confirming the reliability of parts and droplets sorting.

The Eastern Kunlun Fault Zone (EKFZ) is located in a seismic blank area. This study investigates the hydrogeochemical characteristics of varied-temperature springs in the EKFZ to understand the relationship between fractures, fluids and earthquakes. It aids in establishing their induction mechanisms and assists in monitoring the earthquake precursors of the EKFZ. In this study, the main elements, trace elements, hydrogen and oxygen isotopes and strontium isotopes of 23 varied-temperature springs in the EKFZ were analyzed. The results reveal the source of groundwater recharge, hydrochemical types, mineral saturation, and for a select few springs indicative of geothermal activity, collected geothermal reservoir temperatures. The study also explores the relationship between earthquakes and springs, identifying sensitive chemical indicators. Based on continuous monitoring at Maqu Station, we found that before the occurrence of the Maerkang Ms 6.0 earthquake, the concentration of Cl− rose by 2.9 times, and 46 days before the Gande earthquake (Ms = 4.7), the concentrations of Na+ and SO42− significantly increased. Finally, a conceptual model of the hydrogeochemistry of springs is presented to describe the groundwater circulation in the study area. This research is of great significance for the analysis of fluid geochemistry in this area and for assessing the seismic hazards of the EKFZ.

Corrosion is considered as one of the main factors in the structural performance deterioration of steel members. In this study, experimental and numerical methods were used to assess the reduction in compressive strength of short tubular steel columns with local corrosion damage. The corrosion damage was varied with different depths (0, 1.5, 2, 3, 4, 4.5, and 6 mm), height (0, 20, 40, 60, 80, 100, 120, 140, 160, and 180 mm), circumference (0, 90, 180, 270, and 360°), and location along the column. A parametric numerical study was performed to establish a correlation between the residual compressive strength and the severity of corrosion damage. The results showed that as the corrosion depth, height and circumference increased, the compressive strength decreased linearly. As for the corrosion height, the residual compressive strength became constant after decreasing linearly when the corrosion height was greater than the half-wavelength of buckling of the short columns. An equation is presented to evaluate the residual compressive strength of short columns with local corrosion wherein the volume of the corrosion damage was used as a reduction factor in calculating the compressive strength. The percentage error using the presented equation was found to be within 11.4%.

This study investigates the impact of specimen size on the mechanical properties of wood, specifically focusing on compression strength, elastic modulus, and Poisson's ratio. Compression tests were conducted using three different specimen sizes (20mm×20mm×30mm, 40mm×40mm×60mm, 60mm×90mm×90mm) in the longitudinal, radial, and tangential directions. Mechanical parameters, failure mechanisms, load-displacement curves, and stress-strain relationships were systematically analyzed for each size. The study also evaluated the influence of specimen size on the accuracy of finite element numerical simulations by utilizing the obtained mechanical parameters. The results reveal a significant correlation between compressive strength and specimen size, indicating a decrease in compressive strength with increasing specimen size. Conversely, elastic modulus and Poisson's ratio exhibit less sensitivity to variations in specimen size. Notably, parameters derived from small-sized specimens (20mm×20mm×30mm) exhibited substantial errors, while those obtained from medium-sized (40mm×40mm×60mm) and large-sized specimens (60mm×90mm×90mm) demonstrated greater reliability, providing precise results in finite element numerical simulations.

This study aimed to evaluate the effects of Blazepod technology when incorporated with various training regimens on the essential elements of physical fitness in volleyball, such as agility, speed, visual response time, and vertical leap. Thirty-six participants (age :17.33±0.48 y, height: 183.78±6.34 cm, weight: 77.14±5.16 kg) were in-volved in this study. In randomized design, three equal groups with two experimental groups and one control group were involved in the study over a period of six weeks: (GE1) used Blazepod technology to workout at a low level; (GE2) used Blazepod technology to workout at a higher intensity; (CG) did not employ Blazepod technology, but it adhered to the same fundamental training curriculum. We conducted agility, speed, reaction time, and vertical jump tests before, midway and after the study to determine optimal training volume, intensity, and frequency. A significant main effect of time (P0.01), and time×group interaction (P>0.001) were found for all tests. Post hoc test showed that the two experimental groups gadget significantly improved in all performance variables (P

Enhancement in the strength of austenitic steels with a small content of carbon can be achieved by a limited number of methods, among which is the ultrafine-grained (UFG) structure formation, especially efficient with the use of severe plastic deformation (SPD) processing that enables increasing significantly the contribution of grain-boundary strengthening, and also involves a combination of other strengthening factors (work hardening, twins, etc.). In this paper, we demonstrate that the use of SPD processing combined with conventional methods of deformation treatment of metals, such as rolling, may lead to an additional strengthening of UFG steel. Analysis of the results of the study on the change of the microstructure and mechanical properties of the Cr-Ni stainless austenitic steel after a combined deformation reveals a substantial increase in the strength properties of this steel, resulting from a consecutive application of SPD processing via equal-channel angular pressing and rolling at a temperature of 400 С, yielding a strength more than 1.5 times higher that that produced by any of these two methods used separately.

The numerical simulation of entropy generation at mixed natural free and forced convection flow in a square lid-driven cavity filled with an eletrically conducting binary fluids saturated porous media in the presence of a magnetic field is performed in this investigation. Both the top and bottom horizontal walls of the cavity are kept at constant and different temperatures while the left and right vertical walls are adiabatic and insulated. The magnetic field is applied in normal direction to the cavity. The Darcy model, including Brinkman term relative to viscous effects and Forchheimer term due to inertial forces, is used for the momentum equations, and the SIMPLER algorithm, based on the control volume finite-element method approach is used to solve the pressure –velocity coupling. The flow pattern and the heat transfer characteristics inside the cavity are presented in the form of isotherms, streamlines and isentropic lines and average Nusselt number trend. The entropy generation rate is determined for various values of Darcy number (10^-3 ≤ Da ≤ 1) and for a range of Hartmann number (0 ≤ Ha ≤ 10²). This study is limited to Pr = 7 which corresponds to water. It is observed that entropy generation is very affected by the variations of dimensionless control parameters considered.

Soccer is the leading cause of all sports-related ocular injuries in Europe and Israel and leads to blindness at a disproportionately high rate, especially among children (Thompson et al., 2019). With soccer being the most popular sport in the world, it is surprising the only solution to ocular injuries are sports glasses which can cause direct damage to the eye and impair peripheral vision by 15%, calling for an alternative (Smith & Jones, 2020). This work, based on an imported facial model, focuses on both the qualitative and quantitative aspects of building a personalized, low-cost (through optimizing material needed), superior apparatus to conventional sports glasses. The quantitative side examines a modified and model-validated (through a SRS of thirty unique extrapolated points) multivariate linear regression equation, based on horizontal and vertical rotation angles (n=60) trained with residual and computer simulation data, that can accurately extrapolate and quantify ocular impact from all horizontal and vertical rotation angles and a modified Hertzian Contact Stress Equation to determine the thickness of the apparatus using the elasticity modulus, impact force, and geometrical facial and soccer-ball features. The qualitative side examines where firstly, ocular impact is most prevalent, and secondly, where most impact is seen from rotating the ball horizontally and vertically through analysis of Pearson’s Correlation Coefficient at the supraorbital, medial canthus, infraorbital, and lateral canthus regions from both regression equations as well as a cost-benefit analysis for comparison with conventional sports glasses. The findings discovered in this work lay the groundwork for future research to build a customized low-cost ocular injury prevention device which can simultaneously ensure complete ocular safety while enhancing athletic performance for over 250,000,000 players (Johnson & Garcia, 2022).

Fungal infection of grape berries (Vitis vinifera) by Botrytis cinerea frequently coincides with harvest, impacting both the yield and quality of grape and wine products. A rapid and non-destructive method for identifying B. cinerea infection in grapes at an early stage prior to harvest is critical to manage loss. In this study, zeolitic imidazolate framework-8 (ZIF-8) crystal was applied as an absorbent material for volatile extraction from B. cinerea-infected and healthy grapes in a vineyard followed by thermal desorption gas chromatography-mass spectrometry. The performance of ZIF-8 to absorb and trap targeted volatiles was evaluated with a standard solution of compounds and with a whole bunch of grapes enclosed in a glass container to maintain standard sampling conditions. Results from sampling methods were then correlated to B. cinerea infection in grapes as measured and determined by Genus specific antigen quantification. Trace levels of targeted compounds reported as markers of grape B. cinerea infection were successfully detected with in-field sampling. Peak area counts for volatiles 3-octanone, 1-octen-3-one, 3-octanol, and 1-octen-3-ol extracted using ZIF-8 were significantly higher than values achieved using Tenax®-TA from field testing and demonstrated good correlation with B. cinerea infection severities determined by B. cinerea antigen detection.

Supplementary cementitious materials (SCMs) are increasingly used in precast concrete industry to enhance concrete strength and durability. SCMs of large market share in precast concrete in-dustry include silica fume, also known as micro-silica and class C fly ash. The main objective of this research is to develop non-proprietary high strength concrete mixes for precast/prestressed concrete industry. Two SCMs are used simultaneously in partial replacement of portland cement to develop ternary mixes. Class c fly ash and silica fume incorporation in the mix design, in ad-dition to low water-to-powder ratio resulted in the successful development of high strength mixes with minimum 24-hour strength in excess of 70 MPa and a final compressive strength ex-ceeding 100 MPa at 28 days. Mechanical properties testing of developed concrete mixes showed that SCMs incorporation resulted in increased values for hardened concrete modulus of elasticity (MoE) and modulus of rupture (MoR). The enhanced concrete properties, mainly high early strength, are highly required in precast concrete industry as it allows for increased productivity of precast facilities and the possibility of pouring high strength slender sections for prestressed concrete applications

SiC ceramics are excellent materials applied at high temperatures because of their light weight, excellent high temperature strength, and high thermal shock resistance. For better engineering properties, we made SiC with fractal lattices. Stress-strain behavior and modulus changes from room temperature to 1,250oC were analyzed using LAMMPS S/W, a molecular dynamics program. As a result of this study, it was confirmed that the modulus of elasticity of SiC crystals changed in the range of about 475 GPa to 425 GPa as it increased from room temperature to 1,250 oC, The stress-displacement characteristics of SiC crystals, which could not be measured at a high temperature of 1,000 oC or higher, could be ensured.

Mutual exclusion algorithms are at the heart of concurrent, distributed/parallel, real-time and operating systems. It is well-known that such algorithms are very difficult to analyze and in the literature different conjectures about starvation-freedom and the number of by-passes (also said the overtaking factor), which in turn affects the (hopefully) bounded waiting time that a process competing for entering the critical section has to suffer before accessing the shared resource, have been formulated for specific algorithms. This paper proposes a novel modelling approach based on Timed Automata and the Uppaal toolset, which proves effective for studying all the properties of a mutual exclusion algorithm for N≥2 processes, by exhaustive model checking. Although the approach, as already confirmed by similar experiments reported in the literature, is not scalable due to state explosion problems, and can be practically applied until N≤5, it is of great value for revealing true properties of analyzed algorithms. For dimensions N>5 the statistical model checker of Uppaal can be used which, although based on simulations, can confirm properties by estimations and probabilities. The paper describes the proposed modelling and verification method and applies it to several mutual exclusion algorithms, thus retrieving known properties but also showing new results about properties often studied only by peer-review and intuitive reasoning.

Isothermal interrupted hot compression tests of 5754 aluminum were conducted on Gleeble-3500 thermo-mechanical simulator at temperature 350 °C and 450 °C, strain rate 0.1 s-1 and 1s−1. These tests simulated flat rolling to investigate how softening behaviors respond to controlled parameters, such as deformation temperature, strain rate and delay times. This data allowed the parameters for the hot rolling process to be optimized. The delay times during interrupted compression vary between 5s and 60s. The dynamic softening at each pass and metadynamic recrystallization at the intervals of deformation passes were analyzed in detail. 0.2% offset yield strength is applied to calculate the softening fraction undergoing metadynamic recrystallization. A kinetic model was developed to describe metadynamic recrystallization behaviors of the hot deformed 5754 aluminum alloy. Furthermore, the time constant for 50% recrystallization was expressed as functions related to the temperature and the strain rate. The experimental and calculated results were found to be in close agreement, which verified the developed model.

The purpose of the study is to establish compliance of the design of the modernized car with the requirements for safe operation. An option has been proposed for upgrading a passenger wagon to a Mobile Diagnostic Complex for transporting a combined vehicle equipped with appropriate flaw detection equipment intended for rail diagnostics. The authors have established the most optimal option for locating the diagnostic vehicle on board the Mobile Diagnostic Complex (MDC) wagon, taking into account the additional load from the vehicle. To achieve this goal, the article developed a three-dimensional model of the supporting structure of the wagon body, proposed a methodology and presented the results of a study of the stress-strain state of the wagon body, taking into account the additional weight of the wagon. The article develops a methodology for studying the natural frequencies of vibrations of the wagon body and develops a three-dimensional model of the wagon for calculating dynamic indicators in the Universal Mechanism software package. Taking into account the previously carried out strength calculations, as well as in order to maintain the factory life cycle indicators of the supporting structure of the wagon body, it is recommended to use the model in the first version.

The new slide roller burnishing (SRB) method has been developed to produce mirror-like surfaces. Unlike conventional roller burnishing (RB), SRB is implemented through a unique device that allows the axes of the deforming roller and the rotary workpiece to cross resulting in a relative sliding velocity that can be controlled (in magnitude and direction) by varying the crossing angle. In the present work, the effect of SRB on the fatigue behavior of AISI 316 steel fatigue specimens was investigated by comparing with a conventional RB using the basic correlation in surface engineering: finishing–surface integrity (SI)–operating behavior. To obtain a more representative picture of the comparison, we implemented each method (RB and SRB) with two combinations of governing factors: (A) a radius of the roller toroidal surface of 3 mm, a burnishing force of 250 N and feed rate of 0.05 mm/rev (RB-A and SRB-A) and (B) a radius of the roller toroidal surface of 4 mm, a burnishing force of 550 N and feed rate of 0.11 mm/rev (RB-B and SRB- B). Both SRB-A (crossing angle of –45°) and SRB-B (crossing angle of –30°) achieved mirror-finish surfaces. SRB-B lead to the greatest fatigue strength and, thus, the longest fatigue life among all tested processes. SRB-B created the deepest zone (>0.5 mm) with residual compressive macro-stresses and a clearly defined modified surface layer, whose thickness of more than 20 m is about twice that created by the other three processes.

In order to obtain the good match between yield strength and low-temperature toughness, the short-time partial austenitization (SPA) process was employed for V-microalloying 0.22C-5.24Mn steel. The initial microstructure after intercritical tempering was dual-phase ferrite and reversed austenite (RA), while the final microstructure was consisted of ferrite, RA and secondary martensite (SM) after subjected to SPA process. (V, Mo)C with disc-like morphology mainly precipitated during intercritial tempering, and the aspect ratio of particle decreased, leading to the appearance of near-spherical morphology. After subjected to SPA process, the resultant multiphase hierarchical microstructure (three layers: out layer of ferrite, interlayer of SM and inner layer RA) enabled high yield strength of 1097 MPa, total elongation of 14%, and impressive impact energy of 33.3 J at -20 °C. The strengthening contribution of (V, Mo)C precipitation was estimated about 108 MPa.

On-stream inspections are the most appropriate method for routine inspections during plant operation without going through production downtime. Ultrasonic inspection, one of the on-stream inspection methods, faces challenges when performed at high temperatures exceeding the recommended 52°C. This study aims to determine the ultrasonic velocity and attenuation with the known material grade, thickness, and temperatures by comparing theory calculation versus experiment with temperatures ranging between 30°C to 250°C on low carbon steel covering most petrochemical equipment material and working conditions. The theoretical analysis was to obtain Young's modulus, Poisson's ratio, and longitudinal velocity at different temperatures. The experiments validated the predicted results of ultrasonic change due to temperature increase and showed a maximum error of 3%. The experimental data of velocity and decibel change from the temperature range provide a reference for the future when dealing with unknown materials information on site that require a quick corrosion status determination.

This paper seeks to optimize the mechanical and durability properties of ultra-high performance concrete (UHPC). To meet this objective, concrete specimens were manufactured by using 1,100 kg/m3 of binder, water/binder ratio 0.20, silica sand and last generation of superplasticizer. Silica fume, metakaolin and two types of nano silica were used for improving the performances of the concrete. Additional mixtures included 13mm long OL steel fibers. Compressive strength, electrical resistivity, mercury intrusion porosimetry tests and differential and thermogravimetric thermal analysis were carried out. The binary combination of nano silica and metakaolin, and the ternary combination of nano silica with metakaolin and silica fume, led to the best performances of the UHPC, both mechanical and durable performances.

This paper presents the microstructural and mechanical properties of low and medium carbon advanced high-strength forging steels developed based on the third generation advanced high-strength sheet steels, in conjunction with those of conventional high-strength forging steels. Hot-forging followed by an isothermal transformation process considerably improved the mechanical properties of the forging steels. The improvement mechanisms of the mechanical properties were summarized by relating to the matrix structure, the strain-induced transformation of metastable retained austenite and/or a mixture of martensite and austenite.

Powdery mildew is a severe disease causing substantial yield losses in wheat production worldwide. The Chinese wheat landrace Changanhongmai (CAHM) exhibits high resistance to the physiological race E09 of powdery mildew. This study aims to characterize the powdery mildew resistance gene in CAHM, and develop molecular markers for marker-assisted selection of wheat. To investigate the genetic characteristics of this resistant gene, we developed F1 plants, F2 generation population, and F2:3 families from a cross between CAHM and SY225. Genetic analysis demonstrated that all F1 plants were resistant to the disease, while the ratio of resistant to susceptible plants was 3: 1 in both the F2 population and F2:3 families, indicating that CAHM is inherited in a manner of single dominant powdery mildew resistance gene, which was tentatively designated as PmCAHM. By using bulk segregation analysis, we constructed a genetic map encompassing Xgwm273, Xwmc626, Xgwm11, Xgwm18, Xgdm28, Xgpw7812, Xgpw5195, Xwmc694 and PmCAHM. Among these markers, Xgpw7812 and Xgpw5195 were flanking markers tightly linked to PmCAHM at a genetic distance of 2.5 cM and 8.4 cM, respectively. Furthermore, nullisomic-tetrasomic analysis revealed that PmCAHM is located on chromosome 1B. These results indicate that PmCAHM differs from the internationally recognized powdery mildew resistance genes in both location and source. In addition, a new germplasm/line NW1748 with large seeds and powdery mildew resistance was developed from the cross and back cross populations of Fengyou 1718 (FY1718)/CAHM//FY 1718. Therefore, PmCAHM can serve as a novel powdery mildew resistance source for breeding of wheat by using NW1748 as the donor in the future.

As Artificial Intelligence (AI) technology, particularly Machine Learning algorithms, becomes increasingly ubiquitous, our abilities to understand and interpret AI and machine learning algorithms are becoming increasingly desirable. Visualization has been used as a common tool to view and understand complex machine learning processes. In this paper, we will focus on developing a general framework for the visualization of machine learning models as a scalar valued multi-dimensional function to help users understand how the models behave over different viewing spaces. We first give a formal definition of the visualization problem. Interpolation-based morphing and subspace sampling techniques are applied to generate various renderings through projections and cross-sections of the model space as 3D surfaces or heatmap images. This method will be applied to two real-world datasets and applications: the diagnosis of Alzheimer's Disease (AD) using a human brain networks dataset and a real-world benchmark dataset for predicting home credit default risks. The visualizations show that different machine learning algorithms can behave quite differently under different conditions.

The fatigue strength of the hot work steel depends on various factors, including the mechanical, properties and behavior and bulk and the surface under layer, the microstructural features as well as heat treatments. The influence of a series of heat treatments on the fatigue strength of H13 hot work steel was investigated. Different preheating, quenching and tempering treatments were applied to four sets of specimens and fatigue tests were conducted at room temperature using a rotating bending test machine. All heat treatments resulted in a certain improvement of the fatigue strength. Highest fatigue strength obtained by applying a double tempering heat treatment (first tempering at 550 °C for two hours and second tempering at 610 °C for two hours) after initial preheating and quenching. One tempering treatment (550 °C for two hours after preheating and quenching) did not significantly improve the fatigue strength.

The study aimed to investigate the impact of incorporating deep learning strategies in mathematics instruction on students' problem-solving abilities, critical thinking skills, academic achievement, and mathematical skills development. The study population consisted of 280 students, with a sample size of 162 participants. Employing a purely quantitative approach, data collection utilized questionnaires and achievement tests as instruments. Data analysis involved simple linear regression, descriptive analysis, and Pearson correlation. The results of the study revealed that there was no significant enhancement observed in students' problem-solving abilities and critical thinking skills when deep learning strategies were incorporated into mathematics instruction. Additionally, students' attitudes towards deep learning activities in mathematics showed no effect on their academic achievement. Furthermore, students' engagement levels in deep learning activities did not impact their development of mathematical skills. Lastly, the frequency of deep learning activities in the mathematics classroom did not show a significant relationship with students' academic performance. These findings suggest that the implementation of deep learning strategies in mathematics instruction did not yield notable improvements in the specified areas based on the study outcomes.

Experimental quantification of retention factors related to post-fire strength as well as post-fire ductility of intentionally selected stainless steel grades applied in construction is the objective of research presented here. These steel grades are characterized by a two-phase austenitic-ferritic microstructure of the duplex type. In this context two mutually corresponding chromium-nickel-molybdenum steel grades have been subjected to analysis, namely X2CrNiMoN22-5-3 steel belonging to the standard duplex group (DSS 22% Cr) and X2CrMnNiN21-5-1 steel belonging to the lean duplex group (LDSS). The similarities and differences in the mechanical properties exhibited by these steel grades after effective cooling, following more or less prolonged simulated fire action conforming to several development scenarios, have been identified and indicated. The resistance of given steel grade to permanent structural changes induced by the heating program proved to be the critical factor determining these properties and resulting in many cases in increased susceptibility to brittle fracture.

Yttria stabilized zirconia materials are frequently used in mechanical engineering and biomedical applications. Demanding loading conditions require materials combining a high level of strength and fracture toughness. A ready to press alumina doped 2 mol% yttria stabilized zirconia powder was shaped by axial pressing and sintering in air at 1250 - 1500 °C for 2 h. The best combination of strength and toughness value of 7.8 MPa√m. Materials sintered in the middle of the chosen temperature range combine fully density, high transformability and small grain size. Toughness measurements by direct crack length measurements delivered unrealistically high fracture toughness values.

The objective of this study was to investigate the impact of athletes' respiratory muscle strength, as assessed through maximal inspiratory (MIP) and expiratory pressure (MEP), on aerobic endurance, as indicated by maximal oxygen consump-tion (Max VO2) kinetics. Respiratory muscle strength was assessed using a digital spirometer (Pony FX Cosmed, Italy), while maximal oxygen utilization capacity was measured using a breath-by-breath automatic portable gas analysis system (Cosmed K5, Italy). Statistical analysis was conducted utilizing SPSS 22.0. Based on the standardized regression coefficients (β), it was found that MEP (mean ± SD: 130.95 ± 42.82) and inspiratory diaphragmatic circumference values significantly influenced ventilatory equivalent (VE), oxygen consumption (VO2), and carbon dioxide pro-duction (VCO2). Conversely, the remaining predictor variables did not exhibit a sig-nificant effect on VE (mean ± SD: 134.80 ± 36.69), VO2 (mean ± SD: 3877.52 ± 868.47 ml), and VCO2 (mean ± SD: 4301.27 ± 1001.07 ml). In contrast, measurements of chest circumference (mean ± SD: 91.40 ± 10.72 cm), MEP, and diaphragmatic cir-cumference during inspiration (mean ± SD: 95.20 ± 10.21 cm) were found to signifi-cantly impact Max VO2 (mean ± SD: 58.52 ± 10.74 ml/kg/min), while the other pre-dictor variables did not demonstrate a significant effect on Max VO2. Conclusively, the study revealed that measured values of diaphragmatic circumference during inspiration and MEP exerted a notable influence on Max VO2, VE, VO2, and VCO2. Our findings underscore the importance of considering respiratory muscle strength in assessing and enhancing athletes' aerobic performance. These insights contribute to a deeper understanding of the interplay between respiratory function and exercise capacity, offering potential avenues for optimizing training regimens and perfor-mance outcomes in athletic contexts.

Currently, in some domestic and foreign mines, the backfill drilling pipeline experience a rupture phenomenon even when the wear degree is low. This results in a delay in production due to the filling becoming 'sick'. This paper presents, for the first time, the damage mechanism from a mechanical perspective and re-derives the anti-extrusion strength model of the backfill drilling pipeline. We investigate the influence of law on the anti-extrusion strength of pipelines from the perspective of stratum and cement ring. We then verify the theoretical and simulation results through engineering examples. The results demonstrate that the Mises stress criterion is a suitable modification principle for the anti-extrusion strength model of the backfill drilling pipeline. The anti-extrusion strength of the pipeline is related to the elastic modulus and Poisson's ratio of the stratum, and the thickness of the cement ring. It is negatively affected by the depth of the stratum. For hard strata, a cement ring with a smaller elastic modulus is suitable, while for soft stratum, a cement ring with a larger elastic modulus is recommended. When the missing angle of the cement ring is less than 60°, the stress concentration factor increases up to 2.2. The stress unloading capacity of the cement ring ranges from 32.7% to 37.8%, and optimal performance of the cement ring is achieved when it has high strength and low rigidity. The backfill filling pipeline of a copper mine abroad was destroyed due to external extrusion force exceeding its anti-extrusion strength value. The modified pipeline anti-extrusion strength model is 18.2% higher than the casing API strength value. This finding can inform the design of the backfill filling pipeline for China's kilometer-deep wells in the future.

3D printing is a non-traditional additive manufacturing process. It is different from the traditional subtractive manufacturing process. It offers exceptional rapid prototyping capabilities and results that traditional subtractive manufacturing methods cannot attain, especially in applications involving curved or intricately shaped components. Despite its advantages, metal 3D printing will face porosity, warpage, and surface roughness issues. These issues will affect the future practical application of the parts indirectly, for example, the structural strength and the parts assembly ca-pability. Therefore, this study compares the qualities of the warpage, weight, and surface rough-ness after milling and grinding processes under the same materials (316L stainless steel) between general rolled steel and 3D additive steel. Experimental results show that 3D printing parts are approximately 13% to 14% lighter than the general rolled steel. The surface roughness performance of 3D printing steel is better than general rolled steel under the same material after milling or grinding processing. The hardness of the 3D printing steel is better than that of the gen-eral rolled steel. The research verifies that 3D additive manufacturing can use surface processing to optimize surface performance and achieve the functions of lightness and hardness.

In this paper, a new method by combining cold drawing and martensitic transformation was proposed to produce ultrahigh-strength steel wire, and the effect of austenitizing heating rate on microstructure and mechanical properties was studied. Compared with Muffle furnace heating, salt bath heating has a much higher austenitizing heating rate, which is beneficial to obtain ultrafine-grained martensite for steel wire with a larger section. By salt bath hardening and low-temperature tempering, an ultrahigh strong (strength of 2.48 GPa) and tough (elongation of 6.0%) steel wire was produced. Moreover, to explore whether is it possible to replace long-time low-temperature tempering with short-time tempering at elevated temperatures to improve the tempering efficiency, the effect of tempering time on the evolution of microstructure and mechanical properties of the steel wires tempered at 350 °C was systematically studied. The results demonstrate that tempering at 350 °C for 30 s can endow the steel wire with comparable mechanical properties to that of the one tempered at 250 °C for 2 h. With tempering time prolonging, the strength decreases gradually with the precipitated phase transition from χ-Fe5C2 carbide into θ-Fe3C carbide and coarsening, which plays a major role in the strength decrease.

The statistical analysis of impact of the top 50 solar flares of X-class (1997-2023) on the global seismic activity, as well as on the earthquake preparation zones located in illuminated part of the globe and in the area of 5000 km radius around the subsolar point was carried out. It is shown by a method of epoch superposition that for all cases the increase of seismicity is observed, especially in the region around the subsolar point (up to 38%) during 10 days after the solar flare in comparison with preceding 10 days. The case study of aftershock sequence of strong M=9.1 earthquake (Su-matra-Andaman Islands, 26.12.2004) after the solar flare of X7.2 class (20.01.2005) demonstrated that the number of aftershocks with magnitude M≥2.5 increases more than 20 times after the solar flare with a delay of 7 days. For the case of the Darfield earthquake (M=7.1, 04.09.2010, New Zealand) it was shown that strong solar flares of class X and M probably triggered two strong aftershocks (M>6) with the same delay of 6 days on the Port Hills fault, which is the most sensitive to external electromagnetic impact from point of view of the fault electrical conductivity and orientation. Based on the obtained results the possible application of natural electromagnetic triggering of earthquakes is discussed for a short-term earthquake prediction using confidently recorded strong external electromagnetic triggering impacts on the specific earthquake preparation zones, as well as ionospheric perturbations due to aerosol emission from the earthquake sources recorded by satellites.

The performance of OpenFOAM in strong scaling tests on HPC systems with AMD EPYC processors exhibits a pronounced superlinear speedup. Simple test cases show superlinear speedups of over 300%, which significantly impacts the efficient use of computing resources. With the last generation of HPC architectures, a superlinear speedup of about 10% to 20% was well expected and accepted by CFD users. The measured superlinear speedup is much more pronounced and withstands the communication overhead to even larger scales. A detailed performance analysis of OpenFOAM follows, employing various High-Performance Computing (HPC) architectures, including AMD, ARM and Intel systems. The performance metric FVOPS (Finite VOlumes solved Per Second) is introduced to compare the performance of Computational Fluid Dynamics (CFD) applications when varying the grid size, as occurs in a strong scaling test. The achievable FVOPS depends on various factors, including the simulation type, boundary conditions, and especially the grid size of a use case. Analysing FVOPS on a single node level with varying grid size shows a significant difference in performance and cache utilization, which explains the large superlinear speedups seen in the strong scaling tests. Furthermore, FVOPS can be used as a simple benchmark to determine the optimal number of grid elements per rank to simulate a given use case at peak efficiency on a given platform, resulting in time, energy, and cost savings. The FVOPS metric also facilitates the direct comparison between different HPC architectures. The tests using AMD, ARM, and Intel processors show a peak in performance when employing around 10,000 grid elements per core. The presence of a large L3 cache on AMD processors is particularly advantageous, as indicated by L3 cache miss rates observed on AMD EPYC processors. Our results suggest that future HPC architectures with larger caches and higher memory bandwidth would benefit the CFD community.

By using hydrogen quench continuous annealing technology, Stelco Inc. has developed a suite of Advanced High Strength Steel (AHSS) grades with tensile strength greater than 1000MPa to meet standard automotive specifications and for unique customer requirements. These grades were optimized by correlating chemical composition and processing parameters with microstructures and mechanical properties. Dual-Phase 980 (Stelco trademarked STELMAXTM 980DP), Multi-Phase 1180 (STELMAXTM 1180MP), Martensitic Steel 1300 (STELMAXTM 1300M) and 1500 (STELMAXTM 1500M) products met strength and formability requirements with excellent flatness and surface quality. Hydrogen quench continuous annealing technology not only ensures all developed AHSS grades have consistent mechanical properties across the entire strip length (from strip head to tail) and width (from edge to edge), but also produces high product yield compared with other continuous annealing processes.

A proposed low-temperature forging method aims to enhance stainless steel bearings by creating a martensitic subsurface layer, significantly boosting bearing fatigue life due to increased surface hardness. This technique induces beneficial residual stresses, particularly in axial bearings, streamlining their construction and improving machine elements. Challenges persist, especially with radial bearings, but simplicity in axial bearing forging promotes compact, resource-efficient facility construction. Future research will focus on applying this technique to axial bearing washers, potentially replicating success in other bearing components. Despite the energy ex-penditure for cooling during forging, the substantial increase in bearing fatigue life offsets this, enhancing overall longevity and reliability of critical machine components. Integration of this forging technique into bearing fabrication appears seamless, offering a promising trade-off be-tween energy use and enhanced performance.

Based on the dynamic strength variation mechanism of concrete under complex loading conditions, two approaches were devised: numerical testing and CT scanning, guided by the principle of minimizing energy dissipation. A methodology for calculating concrete's failure area and measuring its strength was developed. The analysis delves into the mechanisms behind failure patterns and variations in concrete specimen strength, focusing on crack initiation, development, and the resultant failure surface formed by crack propagation, along with the stress distribution in concrete specimens subjected to diverse loading conditions. Through evaluating the strength and computed failure area of concrete specimens, it is evident that the loading method influences both the strength and failure area of concrete specimens. In general, a larger failure area correlates with a higher measured strength.

The dilatometer curves of continuous cooling transformation of 12Mn steel were measured with Formastor-FⅡthermal mechanical simulator．The steel's undercooled austenite phase continuous cooling transformation curves ( CCT curves) were established by means of the dilatometer method and the metallographic-hardness measurement method． The effect of cooling rate on microstructure and hardness of the steel was studied． CCT curve of test steel was simulated by JMatPro. The results show that the Ac1 and Ac3 of the experimental steel are 692 ℃ and 855 ℃ ; the microstructure obtained is made of ferrite，pearlite and bainite．The ferrite transformation and pearlite transformation occur at a slower cooling rate，in which the ferrite is dominant. When the cooling rate is greater than 4.25 ℃ / s bainite transformation happens．As the cooling rate increases，microstructure or grains become finer．The hardness of the tested steel with increasing cooling rate shows a trend of first fast increase and soon decrease．The simulation results are consistent with the measured CCT law. The high temperature mechanical properties of 12mn steel round billet were tested by gleeble-1500d thermal / mechanical simulator. The tensile strength, reduction of area and stress-strain curves of the billet were obtained in the range of 600-1300 ℃.

TiC–high Mn steel-bonded carbide with a cellular structure was designed and fabricated by powder metallurgy techniques using coarse and fine TiC particles as the hard phase. This preparation process was carefully investigated and optimized. The microstructure of the TiC steel-bonded carbide was observed using a scanning electron microscope. Results showed that there are two types of microstructures in the TiC steel-bonded carbide: the coarse-grained TiC and fine-grained TiC. The transverse rupture strength and impact toughness of the alloy reach maximum values 2231 MPa and 12.87 J/cm2, respectively when the starting weight ratio of MP-A (containing coarse TiC particles) to MP-B (containing fine TiC particles) is 60:40. Hence, this study serves as a feasible example of how to prepare a high-strength and high-toughness TiC–high Mn steel-bonded carbide.

In recent years, in addition to the commonly known wire-based processes of Directed Energy Deposition using lasers, a process variant using the electron beam has also developed to industrial market maturity. The process offers particular potential for processing highly conductive, reflective or oxidation-prone materials. However, for industrial usage there is a lack of comprehensive data on performance, process limits and possible applications. The present study deals with this problem using the example of the high-strength aluminum bronze CuAl8Ni6. Multi-stage test welds are used to determine the physically possible process limits and draw conclusions about the suitability of the parameters for additive manufacturing. For this purpose, optimal ranges for energy input, possible welding speeds and the scalability of the process were investigated. Finally, additive test specimens in the form of cylinders and walls are produced and the hardness profile, microstructure and mechanical properties are investigated. It is found that the material CuAl8Ni6 can be well processed by wire electron beam additive manufacturing. The microstructure is similar to a cast structure, the hardness profile over the height of the specimens is constant and the tensile strength and elongation at fracture values achieved correspond to the specification of the raw material.

In steel structures, oblique thin steel plates serve as panel zones in structures spanning large spaces (e.g., warehouses and gymnasiums). Considerable research has been conducted on the shear buckling of panels due to seismic loads acting on a structure. Conversely, under snow or wind loads, the panel zone may experience compressive and tensile stresses simultaneously from two directions. Considering the economic preference for thin steel plates, evaluating the elastic critical local buckling stresses in the panel zone under biaxial normal stress may provide essential information to structural engineers. In this study, an elastic buckling analysis based on the energy method is performed to clarify the impact of panel geometry and boundary conditions on the elastic local buckling stresses of oblique panel zones. As confirmed, the buckling stresses derived from the energy method could simulate the local buckling stresses with accuracy comparable to that of finite element analysis, and an engineer-friendly design formula was proposed. Finally, we determined the correlation of the buckling stresses under biaxial stresses and presented a method for evaluating this correlation. Engineers can utilize the provided design equations to more efficiently and accurately calculate buckling loads, facilitating safer and more economical design of structures with oblique plates.

This paper presents the deformation of the joined sheet after the clinch-riveting process. The DX51D steel sheet with zinc coating was used. The samples to be joined with clinch riveting technology had a thickness of 1±0.05 mm and 1.5±0.1 mm. The sheet deformation was measured before and after the joining process. The rivet was pressed in the sheets with the same dimension between the rivet axis and three sheet edges: 20, 30 and 40 mm. For fixed segments of the die, from the rivet side close to the rivet, the sheet deformation was greater than that of the area with movable segments. The movement of die sliding element caused more sheet material to flow in the space between the fixed part of the die and movable segments. Hence, the sheet deformation in these places was smaller than for the die fixed element – sheet material was less compressed. For sheets thickness 1.5 mm and width 20 mm, the bulk of the sheet was observed. For a sheets width of 20 mm, it was observed that the deformation of the upper and lower sheets in the area of the rivet is greater than for sheets width of 30 or 40 mm.

The swelling behavior of titanium-modified austenitic stainless steel 15-15Ti was investigated by pre-implantation of He at room temperature followed by Ni irradiation at 580 °C to peak doses of 120, 240 and 400 dpa. Relatively smaller cavities were observed in the zone of helium implantation while large cavities appeared in the region near the damage peak. A correction formula of the dpa curve was proposed and applied for samples with large swelling. It is found that the steady-state swelling rate of 15-15Ti keeps at ~1% /dpa even to high doses. By comparing the swelling data of the helium-implanted and helium-free regions at same doses, 70 dpa and 122 dpa, the suppression of excessive helium on swelling can be deduced at such doses.

Mobile elevating work platforms (MEWPs) consist of a work platform, extending structure, and chassis, and are used to move persons to working positions. MEWPs are useful but are composed of pieces of equipment, and accidents do occur owing to equipment defects. Among these defects, accidents caused by the fracture of bolts fixed to the extension structure and swing system are increasing. This paper presents a failure analysis of the fixing bolts of MEWP. Standard procedure for failure analysis was employed in this investigation. Visual inspection, chemical analysis, tensile strength measurement, and finite element analysis (FEA) were used to analyze the failure of the fixing bolts. Using this failure analysis approach, we found the root cause of failure and proposed a means for solving this type of failure in the future. First, the chemical composition of the fixing bolt is obtained by a spectroscopy chemical analysis method, which determined that the chemical composition matched the required standard. The tensile test showed that the tensile and yield strengths were within the required capacity. The stress analysis was carried out at five different boom angles, and it was determined that the fixing bolt of MEWP can withstand the loads at all the boom angles. The outcomes of the fatigue analysis revealed that the fixing bolt fails before reaching the design requirements. The results of the fatigue analysis showed primarily that the failure of the fixing bolt was due to fatigue. A visual inspection of the fractured section of the fixing bolt also confirmed the fatigue failure. We propose a method to prevent failure of the fixing bolt of the MEWP from four different standpoints: the manufacturer, safety certification authority, safety inspection agency, and owner.

Monitoring of structures is one of the engineering challenges of the 21st century. At the same time, as a result of changes in the conditions of use, design errors, many building structures require strengthening. The article presents research on the development of the external strengthening carbon fiber textile with an option of self-sensing. The idea is based on the pattern of resistive strain gauge, where thread is provided in a zig-zag of parallel lines. Already the first laboratory tests showed the high efficiency of the system in the measurement of strains, but also revealed the sensitivity of measurement to environmental conditions. The article presents studies on the influence of temperature and humidity on the measurement. To separate those effects, resistance changes were tested on unloaded concrete and wooden samples. The models were placed in a climatic chamber and the daily cycle of temperature and humidity changes was simulated. The results of the research confirm preliminary observations. Resistivity growths with the temperature. This effect is more visible on concrete samples, presumably due to its greater natural humidity. The strain measurement with carbon fibers is very sensitive to temperature changes and application of this method in practice requires compensation.

The wealth of data obtained during the past 20 years using Laser-Induced Breakdown Spectroscopy (LIBS) indicates that the technique is very promising to detect small chemical contents of alloying elements. The potential of LIBS was looked more seriously during the past two decades or so as more data were obtained on Aluminum and steel to study the phenomena in the condition of local thermodynamic equilibrium and time-delay between a Q-switch laser and an intensified CCD camera. Since the past decade, some data on compounds were also shown to be useful in determining small concentrations of harmful elements. This manuscript is intended to show that the technique of LIBS performance is very promising in fields such as micro-machining, in alloying element analysis, surface cleaning and environmental applications even with lightweight spectrometers having a relatively low resolution, which can potentially be air-borne.

In this paper, through high-temperature tensile tests of 55NiCrMoV7 steel, the high-temperature fracture behavior, microstructure evolution and carbide distribution characteristics of both thermal-mechanical coupling zone (fracture zone) and thermal stress zone (clamping zone) at different temperatures were studied. Intrinsic relationship between high temperature fracture and carbides types, distribution and size were revealed and evolution mechanism of microstructure near cracks in 55NiCrMoV7 hot-working die steel during high temperature deformation was clarified. Samples were stretched at different temperatures from 25 °C to 700 °C, and microscopic examinations were carried out by using SEM and TEM. The results showed that: With the increase of temperature, tensile strength and yield strength decreased, elongation and reduction of area increased, and fracture mode changed from brittle fracture to ductile fracture by transition temperature at about 400℃. During high temperature deformation, the grain dislocation density decreased, the tempered martensite decomposed, recovered, recrystallized, and then grain grew. M7C3 and M23C6 carbides precipitated and grew along the grain boundary, and a small amount of fine granular MC carbides were dispersed in the grain. The work done by the external force on the deformation zone would cause the temperature of it to be higher than tensile temperature, which provides thermodynamic conditions for the re-dissolution of small carbides near the fracture zone and the grain growth of large carbides, resulting in the decrease of small carbides and increase of large carbides in thermal-mechanical coupling zone.

This research investigated high-temperature corrosion (500 °C) of Cr-Mo steel processed using water jet peening or multifunction cavitation (MFC), and the suitability of such steel for high-temperature boilers and reaction vessels. High-temperature corrosion was induced using an embedment test and a coating test using sulfide-type K2SO4-Na2SO4 powder. To measure the relaxation of the residual stress due to the decrease in work hardening caused by an increase in specimen temperature and the difference in thermal shrinkage between the surface and interior of the specimen, a thermal cycling test was conducted. For the MFC-processed specimen, the oxide film that formed on the surface suppressed mass loss, prevented crack formation, and reduced the compressive residual stress caused by high-temperature corrosion. MFC-processed Cr-Mo steel is thus suitable for a high-temperature corrosion environment.

In this paper, the synthesis of two novel luminescent Eu3+ ion complexes [Eu(TFT)3(phen) (1) and Eu(TFT)3(bpy)•Hex (2)] based on the combination of 2-(2,2,2-trifluoroethyl)-1-tetralone (TFT), containing n-donor ligands (1,10-phenanthroline or 2,2'-Bipyridine) and Eu3+ ion is reported herein, and their structural features are discussed on the basis of X-ray crystallographic and thermal analyses. We observed that the ligands transfer energy effectively to the metal center by fluorescence, IR and UV spectrograms studies. The structures and properties of complexes 1-2 were optimized by the DFT theoretical calculation, and the calculation results were consistent with the experimental X-ray structure data and spectral analysis.

This study aimed to use biomineralization technology to improve the bond strength of fiber-reinforced lightweight aggregate concrete (LWAC) after exposure to temperatures of 300 °C and 500 °C. The specimens of a control group (Group A) and two experimental groups (Group B and Group C) were prepared. These specimens healed themselves in different ways after exposure to high temperatures and pull-out tests. The self-healing method of Group A involved placing the specimen into an incubator. The self-healing method of Group B was the same as that of Group A. The self-healing method of Group C involved immersing the specimen in a mixed solution of urea and calcium acetate for two days, then taking it out and placing it in an incubator for two days. A cycle of four days was undertaken until the desired age was reached. After the specimens were healed to the planned age, the first and secondary pull-out tests and repair compound identification were carried out. After exposure to a temperature of 300 °C and self-healing for 90 days, compared with the specimens in Group A, the relative bond strength ratios of the secondary pull-out tests of the specimens in Group C increased by 20.3%. This indicates that biomineralization can effectively improve the bond strength of LWAC after high-temperature damage.

In this paper, we focus on the impact of financial liberalization on stability of emerging stock market. We identify crises in a group of Latin American (Argentina, Brazil and Chile) and Asian countries (Philippines, Korea, Taiwan and Thailand) during 1975–2005. This paper aims to apply the methodology of CMAX method. Our results indicate that liberalization triggers more unstable stock market in the short run and generate several crises. Still, liberalization seems to generate more stable financial markets in the long run. Financial liberalization does not increase the frequency of crises in emerging countries and at long-term, crises are less several.

The effects of environmental media on the corrosion fatigue fracture behavior of 25CrMo steel were investigated. The media include air, and a 3.5 wt.% and a 5.0 wt.% NaCl solutions. Experimental results indicate that the media induces the initiation of corrosion fatigue cracks at multiple sites. The multi-cracking sites cause the changes in the crack growth directions, the crack growth rate during the coupling action of the media and the stress amplitude. The coupling effects are important for engineering applications and research. The probability and predictions of the corrosion fatigue characteristic life can be estimated using the 3-parameter Weibull distribution function.

Concrete contributes 8% of all global carbon emissions making the need to find substitute critical for environmental sustainability. Research has indicated the potential for recycled plastics to be used as concrete substitutes. This study extends existing research by investigating the use of polycarbonate (PC) in plastic sand bricks as a mechanical equivalent to concrete. PC has high compressive strength, durability, impact strength, thermal resistivity, clarity, fatigue resistance, and UV resistance. This work provides a method and mold to produce a matrix of sand-plastic sample compositions with dimensions adhering to ASTM D695 standard for compressive properties of rigid-plastic. Compositions of 0% (control), 20%, 30%, 40%, and 50% sand by weight were tested. Samples were tested for compressive strength until yield and stress-strain behaviors plotted. The results for 100% PC demonstrated an average and maximum compressive strength of 71 MPa and 72 MPa, respectively. The 50% PC and 50% sand composition yielded an average and maximum compressive strength of 71 MPa and 73 MPa respectively with an increase in compressive stiffness, and transition to shear failure resembling cement. With a composite density of 1.86 g/cm3 against concrete’s average 2.4 g/cm3, and a compressive strength exceeding commercial concrete demands of 23.3 MPa to 30.2 MPa, this lightweight alternative meets the strength demands of concrete, reduces the need for new construction materials, and provides an additional recycling opportunity for nonbiodegradable waste plastic.

The present work investigates primarily the morphology evolution of the body-centered-cubic (BCC)/B2 phases in AlxNiCoFeCr high-entropy alloys (HEAs) with increasing Al content, which has been neglected so far. There exist two types of microscopic morphologies of BCC and B2 phases in this HEA series: one is the weave-like morphology induced by the spinodal decomposition, and the other is the microstructure of a spherical disordered BCC precipitation on the ordered B2 matrix that appears in HEAs with a much higher Al content. The shape of coherent precipitates is found to be closely related to the lattice misfit between BCC and B2 phases, which is sensitive to Al. The mechanical properties, including the compressive yielding strength and microhardness of the AlxNiCoFeCr HEAs, are also discussed in light of the concept of the valence electron concentration (VEC).

In this paper, low circumferential reciprocating load foot-scale tests were performed on two truncated PHC B 600 130 tubular piles with bearing nodes to characterize the damage process and morphology of the specimens and to investigate the load-carrying performance of the members. The test results reveal that under the action of tensile-bending-shear loading, the bearing concrete in the node area buckles and is damaged, the anchored reinforcement in the node area yields, the constraint is weakened, an articulation point is formed, and the node rotational capacity increases. When the embedment depth increases from 200 mm to 300 mm, the ultimate bearing capacities of the positive and negative nodes increase by 57.60% and 54.60%, respectively. A numerical simulation is used to verify the test results. Considering the three types of piles with truncated nodes, the numerical simulation is used to analyze the node-bearing capacity at different embedment depths. Finally, two preferred node types are proposed as follows: pipe pile core-filled longitudinal reinforcement anchored into the bearing node and pipe pile body longitudinal reinforcement anchored into the bearing node + pipe pile core-filled longitudinal reinforcement anchored into the bearing node, with preferred embedment depths of 350 mm and 200 mm, respectively.

: In the automotive industry, high-strength plates have been increasingly used to reduce the vehicle body weight due to stringent regulations on fuel economy and safety. Such plates achieve tensile strengths as high as 1.5 GPa owing to the hot-stamping process. However, these plates suffer from scale generation and surface decarburization because of the surface oxidation of the material. Recently, studies on materials subjected to high-frequency induction heating have reported strength improvement owing to the coil shape and cooling method. This study presents the surface temperature changes, mechanical properties, and microstructures of boron steels subjected to longitudinal heating, which uses eddy currents generated from high-frequency induction heating. The surface temperature data were analyzed under different high-frequency induction heating powers (15, 18, 21, 24, 27, and 30 kW) and distances from the specimen (6, 9, and 15 mm). The mechanical properties and microstructures were also analyzed in different high-frequency induction heating coil directions. The correlations between the high-frequency induction heating power and the distance from the specimen with the maximum tensile strength were determined.

Solid waste management in Accra is a major challenge to the Metropolitan Authorities and inhabitants. The rapidly increasing population coupled with poor capacity of the municipal and private waste management companies to management waste effectively has created issues of environmental concern. Due to poor waste managements systems, most household dispose waste indiscriminately leading to floods and health issues. The study showed that about 60% of household waste is organic materials which has the potential to be converted to compost for agriculture purpose. Meanwhile plastics and rubbers which litters the environment as well as blocking major storm drains and gutters hence creating huge environmental hazard is made of 11% of the total component of most household waste generated daily. The study also revealed that among the methods of disposing waste, dumping waste in skip containers located at authorized places was the preferred means of disposing waste by household though others also dispose waste by other means such as burying and burning. Inadequate skip containers per population of household in an area coupled with irregularity of tracks picking these containers makes skip containers dumping site ugly scene, hence creating health issues. Among the constraints that impact negatively on sustainable waste management in Accra Metropolis, economic constraints was perceived as the main challenge which affect efficient waste management. Currently the country is going through serious economic challenges so government does not release money timely to fund projects which waste management is key. Most donor partners that use to support the government with funds have either reduced or redrawn their services as they have no confidence in the state of Ghana economy. Aside the constrains, the study also indicated that factors such as poor public attitude towards waste management, poor enforcement of sanitation by-laws, inadequate and untimely release of government funds were also seen as the main factors affecting waste management.

Based upon Maxwell's equations, it has long been established that oscillating electromagnetic (EM) fields incident upon a metal surface decay exponentially inside the conductor, leading to a virtual EM vacuum at sufficient depths. Magnetic resonance imaging (MRI) utilizes radiofrequency (r.f.) EM fields to produce images. Here we present the first visualization of a virtual EM vacuum inside a bulk metal strip by MRI, amongst several novel findings. We uncover unexpected MRI intensity patterns arising from two orthogonal pairs of faces of a metal strip, and derive formulae for their intensity ratios, revealing differing effective elemental volumes (voxels) underneath these faces. Further, we furnish chemical shift imaging (CSI) results that discriminate different faces (surfaces) of a metal block according to their distinct nuclear magnetic resonance (NMR) chemical shifts, which holds much promise for monitoring surface chemical reactions noninvasively. Bulk metals are ubiquitous, and MRI is a premier noninvasive diagnostic tool. Combining the two, the emerging field of bulk metal MRI can be expected to grow in importance. The fundamental nature of results presented here may impact bulk metal MRI and CSI across many fields.

In this study, an alternative method to conventional production methods involving thin section copper permanent mould casting (rapid solidification), hot rolling and heat treatment processes to manufacture AISI DC 53 cold work tool steel, has been investigated. In this new method, solidification of the AISI DC 53 was done in the thin section copper mould instead of traditional ingot casting. After solidification, thin slabs obtained was homogenized to 1150 ^oC and hold at this temperature for one hour and then hot rolling was be applied. During hot rolling process, about % 30 reduction in thickness of slab was obtained. After hot rolling, heat treatment (austenitizing, quenching and tempering) have been applied to thin slab. The samples have been taken as cast, as rolled and as heat treated (austenitized and tempered) and the microstructural analysis, hardness tests, retained austenite quantity measurement by XRD method have been performed. The heat treatment and tests have been performed for a commercially available AISI DC 53 which is manufactured by thick section ingot casting and rolling. Hardness values of the AISI DC 53 steels produced by traditional route is in the range of 52-54 HRC after austenitization at 1025 ^oC for one hour and quenched in compressed air and tempered twice at 525 ^oC for 120 mins. On contrary the permanent mould cast AISI DC 53 after homogenization at 1150 ^oC and immediately hot rolling then air cooling and austenitized at 1025 ^oC for one hour then quenched by compressed air and tempered twice at 525 ^oC for 120 mins have hardness valeus in the range of 55-57 HRC. Experiments have revealed that the properties of new rapid solidified steel in permanent copper mould are better than the commercially available steel and have a more refined microstructure than commercially produces alternative. Therefore, the new proposed method can be used as an alternative manufacturing method for cold-work tool steels.

The Gleeble-1500D thermal simulation test machine was used to conduct the isothermal compression test on 21-4N at the strain rate ( ) of 0.01-10s-1, the deformation temperature (T) of 1273-1453K and the maximum deformation is 0.916. The data of the stress-strain ( - )were obtained. Based on the - data, the Johnson-Cook (J-C), modified J-C, Arrhenius and Back-Propagation Artificial Neural Network (BP-ANN) models were established. The accuracy of four models were verified, analyzed and compared. The results show that J-C model has a higher accuracy only under reference deformation conditions. When the deformation condition changes greatly, the accuracy of J-C model is significantly reduced. The coupling effect of T and of modified J-C model is considered, and the prediction accuracy is greatly improved The Arrhenius model introduces Zener-Hollomon (Z) to represent the coupling effect of T and , it has a fairly high prediction accuracy. And it can predict flow stress ( ) accurately at different conditions. The accuracy of BP-ANN model is the highest, but its learning rate is low, the learning and memory are unstable. It has no memory for the weights and thresholds of the completed training. So, there are certain limitations of it in use. Finally, a FEM of the isothermal compression experiment for four models were established, and the distribution of the equivalent stress field, equivalent strain field and temperature field with the deformation degree of 60% were obtained.

Evidence suggests that COVID-19 infection can cause lasting health consequences. Multidiscipli-nary rehabilitation services have been recommended to reduce the sequalae. However, the effec-tiveness of physical exercise interventions remains insufficiently documented. The aim of this study was to develop and implement a specific and well tolerated protocol-based, intervention to reduce muscle weakness in older adults impacted by COVID-19. Forty six older adults random-ized into Intervention and Control Groups. Isometric and isokinetic strength assessments were conducted for selected muscle groups using JBA Staniak® torquemeter and Biodex System 3 dy-namometer. Functional abilities were evaluated with the Time Up and Go test and Chair Stand Tests. Men in intervention group demonstrated a significant improvement in static conditions for knee flexors (KF), trunk extensors (TE) and trunk flexors (TF) and in dynamic conditions for knee extensors (KE). Women in intervention group showed significant improvement in static condition for EF, KF, TE and TF and in dynamic for a KE and for a KF. The interaction GROUP x TESTING SESSION was significant for Chair test (s) and Chair test (n). Our results demonstrate the effec-tiveness of a well-tolerated, protocol-based approach that can be used to diminish long lasting functional deficits in post-covid survivors.

In this research, a design method for the graded triply periodic minimal surface (TPMS) structures with lightweight, high-strength, and high sound absorption properties is proposed. The graded TPMS structures are controlled by linear, quadratic, and sine functions. Uniform TPMS and graded TPMS were manufactured by laser powder bed fusion (LPBF) with AlSi7Mg powder, and an acoustic impedance tube test, compression test, and digital image correlation (DIC) test were ap-plied to obtain the sound absorption and compression properties. The sound absorption coefficient of a uniform Gyroid increases as the number of layers and surface thickness increase, and it in-creases as element size decreases. The sound absorption peak shifts to low frequencies as the number of layers increases. The sound absorption property of Type-Ⅰ graded TPMS is superior to the Type-Ⅱ, and the G-LinearⅠ has the highest sound absorption properties among the three functions. It reveals that the graded TPMS has superior sound absorption performance at low and medium frequencies. The compression and DIC results of graded TPMS also show excellent mechanical properties and energy absorption characteristics.

Powder and SLM additively manufactured parts of X5CrNiCuNb17-4 maraging steel were systematically investigated by electron microscopy to understand the relationship between the properties of the powder grains and the microstructure of the printed parts. We prove that satellites, irregularities and superficial oxidation of powder particles can be transformed into an advantage through the formation of nanoscale (AlMnSiTiCr)-oxides in the matrix during the printing process. The nano-oxides showed extensive stability in terms of size, spherical morphology, chemical composition and crystallographic disorder upon in situ heating up to 950°C in the scanning transmission electron microscope. Their presence thus indicates a potential for oxide-dispersive strengthening of this steel, which may be beneficial for creep resistance at elevated temperatures. The nucleation of copper clusters and their evolution into nanoparticles as well as the precipitation of Ni and Cr particles upon in situ heating have as well been systematically documented.

Modular steel buildings (MSBs) interlocking inter-module connections (IMCs) have piqued researchers’ interest. However, the existing literature has not yet studied the optimisation of its plate thicknesses. This paper, therefore, focuses on optimising interlocking (IMCs) plate thickness in (MSBs), leveraging previous experimental and numerical simulation methodologies. Various numerical models for four MSBs interlocking (IMCs) with plate thicknesses (4 mm, 6 mm, 10 mm, and 12 mm) were developed under compression loading conditions. The study’s novelty lay in its comprehensive parametric analysis, which evaluated the slip phenomenon in (MSBs) connections and introduced a slip prediction model validated against empirical data. Further innovative machine learning approach was utilised to predict slip values based on applied force through a random forest regression model trained using the 'Treebagger' function. Sensitivity analysis and comparisons with alternative methods were utilised to underscore the reliability and applicability of the findings. The results showed that 11.03 mm was the optimal plate thickness for interlocking (IMCs) in modular steel buildings, with up to 8.08% reduced material costs. Increasing plate thickness boosts its deformation resistance by up to 50.75%. ‘TreeBagger’ random forest for anomaly detection and machine learning improves slip prediction up to 7% at higher force levels.

Concrete being one of the most frequently used construction materials in the field of construction. The use of concrete has increased with the passage of time as the more and more construction activities are taking place around the globe. Different materials have been added in to the concrete mix to provide the concrete more strength and make it more durable and long lasting. This paper looks into a detailed comparison of concrete strength when casted with in the presence of carbon fibers, steel fibers and glass fibers. The compressive strength for cubes and cylinder with carbon fibers is the highest as compare to steel fibers as well as glass fibers. The compressive strength of concrete is measured on 3 day, 7 day, 14 day and 28 day strength. The compressive strength of cube on 28th day strength is 37.52 MPa for carbon fiber steel, for steel fiber it is 34.22 MPa and with glass fiber the strength is 29.335 MPa whereas the compressive strength of cylinder with carbon fibers the 34.88 MPa, with steel fiber it is 34.22 MPa and with glass fiber the strength is 27.447 MPa. For the cubes the maximum difference between different fibers inducted concrete sample is 28% approximately and for cylinder it is 27%, respectively. On the other hand, the tensile strength of concrete was also gained with the carbon fiber. It was determined that carbon fiber provided about 16% and 12.8% tensile strength higher than glass and steel fibers respectively.

High-strength wastewaters from a variety of sources, including the food industry, domestic septage and landfill leachate, are often hauled to municipal wastewater treatment plants (WWTPs) for co-treatment. Due to their high organic loadings, these wastewaters can cause process upsets in both the WWTP’s liquid and solids treatment trains and consume organic treatment capacity, leaving less capacity available to service customers in the catchment area. A novel pre-treatment method, the Waste Activated Sludge-High Rate (WASHR) process, is proposed to optimize the co-treatment of high-strength wastewaters. The WASHR process combines the contact stabilization and sequencing batch reactor processes. It utilizes waste activated sludge from the municipal WWTP as its biomass source, allowing rapid start-up. Bench scale treatment trials of winery wastewater confirm the WASHR process can reduce loadings on the downstream WWTP’s liquid treatment and solids treatment trains. A case study approach is used to confirm the economic viability and environmental sustainability of the WASHR process compared to direct co-treatment using life cycle cost analyses and greenhouse gas emissions estimates.

Among all the active confinement techniques, the use of pre-tensioned stainless steel straps has recently gained much attention. The flexibility of the stainless steel straps allows us to bend and pass them through the thickness of the masonry, thus creating a three-dimensional strengthening system between the two opposite facings. The use of the same perforation for the passage of several straps closed in a loop generates a continuous strengthening system that prevents parts of the structure from falling and injuring the occupants during seismic events. However, the perforations can nullify the in-plane strengthening, as they act as cylindrical hinges and make the reinforcement system labile for certain strap arrangements. Diagonal compression tests on square masonry panels performed in the present study show that the straps improve neither strength nor ductility when running along the mortar head and bed joints, arranged in square meshes. Conversely, they improve both strength and ductility when the straps make angles of 45° with the mortar joints. Furthermore, the experimental results show that the straps exert an anisotropic effect that decreases the apparent in-plane Poisson ratio. They also provide new insights into the diagonal compression test and allow formulating a new proposal for the pseudo-ductility factor.

Extensive experimental and theoretical research over the past several decades has culminated in the understanding of the mechanisms behind nanoparticle-mediated enhancements on the mechanical properties of hydrogels. This information is not only crucial to realizing applications that directly benefit from developing hydrogels with high mechanical strength, but also to guide the development of strategies to further enhance hydrogel properties by combining different approaches. In our study, we investigated the effect of combining two approaches – addition of nanoparticles and crosslinking two different polymers (to create double-network hydrogels) – on the mechanical properties of hydrogels. Our studies revealed that these approaches may be combined to synthesize hydrogel composites with enhanced properties; however, both polymers in the double-network hydrogel must strongly interact with the nanoparticles to fully benefit from the addition of nanoparticles. Moreover, the concentration of hydrogel monomers used for the preparation of the double-network hydrogels had a significant effect on the extent of nanoparticle-mediated enhancements; double-network hydrogel nanocomposites prepared using lower monomer concentrations showed higher enhancements in elastic moduli compared to those prepared using high monomer concentrations. Collectively, these results demonstrate that the hypotheses previously developed to understand the role of nanoparticles on the mechanical properties of hydrogel nanocomposites may be extended to double-network hydrogel systems and guide the development of next generation hydrogels with extraordinary mechanical properties through a combination of orthogonal approaches.

Currently, one of the biggest issues when developing an ODS alloy is the competition established between the different oxide precursors during the precipitation of oxides which nature depends on their chemical composition. In the presence of various precursors, usually the one with the highest affinity to oxygen leads to the absence of the other oxides. In this work, a new process to equilibrate the local concentration of species and to decrease the competition among them is explained. A unique compound, containing the diverse oxide precursors as one complex oxide, is introduced in a prealloyed 14Cr Steel powder via mechanical alloying. Thus, generating environments enriched in Y, Ti and Zr which, after consolidation, refine the oxides precipitation improving the thermal stability of the alloy. SPS were used as consolidation technique to guarantee shorter sintering times and to maintain the nanostructure obtained. Mechanical properties were tested by tensile tests and Vickers microhardness.

Concrete cracks and local damage can affect the bond performance between concrete and steel bars, thereby reducing the durability of reinforced concrete structures. Compared with general concrete crack repair methods, biomineralization repair not only has effective bonding capabilities but is also particularly environmentally friendly. In view of this, this study aimed to apply biomineralization technology to repair damaged fiber-reinforced lightweight aggregate concrete (LWAC). Two groups of LWAC specimens were prepared. The control group used lightweight aggregates (LWAs) without bacterial spores and nutrient sources, and the experimental group used LWAs containing bacterial spores and nutrient sources. These specimens were first subjected to compression tests and pull-out tests, respectively, and thus were damaged. After the damaged specimen healed itself in different ways for 28 days, secondary compression and pull-out tests were conducted. The self-healing method of the control group involved placing the specimens in an incubator. The experimental group was further divided into experimental group I and experimental group II. The self-healing method of experimental group I was the same as that of the control group. The self-healing method of experimental group II involved soaking the specimen in a mixed solution of urea and calcium acetate for two days, and then taking it out and placing it in an incubator for two days, with a cycle of four days. The test results showed that, compared with the control group specimens, the relative bond strength ratio of the experimental group II specimens increased by 17.9%. Moreover, the EDS and XRD analysis results confirmed that the precipitate formed at the crack was calcium carbonate, which improved the compressive strength and bond strength after self-healing. This indicates that the biomineralization maintenance method used in experimental group II is more effective.

At different heat treatment temperatures, the hardness and flexural strength of M2 high-speed steel selective laser melting (SLM) parts show mixed trends. When the heat treatment temperature is 260°C, the hardness and flexural strength of the M2 high-speed steel SLM part are decreased, but the hardness difference between the upper and lower surfaces of the M2 high-speed steel SLM part is also reduced. When the heat treatment temperature is 560°C, the hardness and flexural strength of the M2 high-speed steel SLM part are almost close to that of the original M2 high-speed steel SLM part, and the performance gradient in the sample is improved, and the overall structure is uniform. When the subsequent heat treatment temperature is 860 °C, the hardness of the SLM parts reaches a minimum, with an average value of 24 HRC. However, the flexural strength exceeds that of the original SLM parts. Moreover, the microstructure of the sample is uniform, which significantly improves the anisotropy of performance.

Abstract: High step-up voltage gain nonisolated DC-DC converter have attracted much attention in photovoltaic, fuel cells and other renewable energy system applications. In this paper, by combining input current ripple-free boost cell with coupled-inductor voltage-doubler cell, an input current ripple-free high voltage gain nonisolated converter is proposed. In addition, passive lossless clamp circuit is adopted to recycle the leakage inductor energy and to reduce the voltage spike across the power switch. By utilizing voltage-doubler cell consisting of diode and capacitor, the voltage stress of switch is further reduced and the resonance between the leakage inductor and the stray capacitor of the output diode is eliminated. A low switch-on-resistance low-voltage-rated MOSFET can therefore be employed to reduce the conduction loss and cost. The reverse recovery loss of output diode is reduced, and the efficiency of converter can be improved. Furthermore, the proposed converter can achieve nearly zero input current-ripple and make the design of electromagnetic interference (EMI) filter easy. Steady state analysis and operation mode of the converter is performed. Finally, experimental results are presented to verify the analysis results of the proposed converter.

A PLS-based quality prediction method is proposed for batch processes using two-dimensional extended windows. To realize the adoption of information in the direction of sampling time and batch, a new definition region of support (ROS), k-i-back-extended region of support (KIBROS), is proposed to establish the extended window, which including the data of the previous sampling times in the same batch, the data of the same sampling time in the historical batches, the data of the previous sampling times in the historical batches and the data of the later sampling times in the historical batches. According to these regions of support, extended windows are established, and different models are proposed based on the extended windows for batch processes quality prediction. Further, using a typical batch process as an example, the injection molding process, the proposed quality prediction method is experimentally verified, proving that the proposed methods have higher prediction accuracy than the traditional method and the prediction stability is also improved.

In the process of oil and gas development and production, when the flow rate in the wellbore is large, the materials underground will be eroded, causing the operation to be unable to proceed smoothly and reducing the efficiency of oil and gas production. Therefore, optimizing the anti-erosion coating under high-speed flow conditions in wellbore is a very interesting thing. It can greatly improve operational efficiency. In this paper, laser cladding was used to prepare the new coating used in the PDC drill bit. Then, the effects of tungsten carbide and multi-layer graphene on the microstructure and properties of the tungsten carbide coating were studied. The research results indicate that, for new coatings, 60% tungsten carbide and 0.3% graphene are the optimal ratios. After adding WC, the hardness has significantly improved. However, when the WC content further increases more than 30%, the increase in hardness is relatively small. In addition, when the content of graphene is more than 0.3%, the branched structure became thicker, and not only the segregation of Cr, Si and W became very obvious again, but also the segregation of Fe occurred at the Ni enrichment site. The research results contribute to improving oil and gas production and operational efficiency under high-speed fluid flow conditions in the wellbore.

Although various atmospheric corrosion simulation models have been developed that give good results, industrial environments are still challenging. This paper aims to investigate the effect industrial atmospheres in Bor on the mechanical properties of structural steel S235JR and to create a constitutive model and also laboratory experimental conditions that will give the best results as an accelerated corrosion test. Atmospheric corrosion tests lasted six months, using sites close to the Electrolytic Refining Plant and Sulphuric Acid Plant, as well as air quality monitoring stations at a remote location in the city of Bor. The laboratory experiments included a salt chamber test lasting 120 h and 240 h and immersing the specimen in the electrolyte from the Electrolytic Refining Plant for 30 days. The results were compared with the standard specimens stored in the laboratory. The X-ray diffraction (XRD) method was used to identify the composition of corrosion products. The scanning electron microscopy (SEM) analysis was applied to analyze the fracture surfaces of the specimens. The use of the Complete Gurson Model (CGM) described the tensile characteristics of the corroded specimens. The study has shown that an enhanced acceleration model and conditions could be developed using numerical analysis of the test results.

This paper introduces an innovative Particle Swarm Optimization (PSO) Algorithm in-corporating Sobol and Halton Random number samplings. It evaluates the enhanced PSO's performance against conventional PSO employing Monte Carlo Random Number Samplings. The comparison involves assessing the algorithms across nine benchmark problems and the renowned Travelling Salesman Problem (TSP). The re-sults reveal consistent enhancements achieved by the enhanced PSO utilizing Sob-ol/Halton samplings across the benchmark problems. Particularly noteworthy are the substantial improvements demonstrated by the enhanced PSO in solving the Travel-ling Salesman Problem. These findings underscore the efficacy of employing Sobol and Halton random number generation methods in enhancing algorithm efficiency.

Aluminum wire is a common material for wire bonding due to its resistance to oxidation and low price. It does not melt when becoming a free air ball (FAB) during the electronic flame-off (EFO) process with wettability, and is applied by wedge bonding. This study used 20μm Zn-Coated Al-0.5wt.%Si (ZAS) wires to improve the FAB shape after the EFO process, while maintaining stability of the mechanical properties, including the interface bonding strength and hardness. In order to test circuit stability after ball bonding, the current-tensile test was performed. During the experiment, it was found that 80nm ZAS with wire bonding has lower resistance and higher fusing current. For the bias tensile test, the thicker Zn film diffused into the Al-Si matrix easily, after which the strength was reduced. The ball-bond interfaces had no change in their condition before and after the bias. Accordingly, ZAS could be a promising candidate for ball bonding in the future.

Background: The maximal one-repetition test (1-RM) is widely used in scientific research; however, there are conflict results regarding its reproducibility in elderly population. The present study aimed to analyze the reproducibility the test both before and after a 12 week training period by using the bench press and leg press 45° 1-RM tests in the elderly taking into consideration the training experience and strength level of the women. Methods: Elderly women (n = 376; age, 68.5 ± 14.1 years; height, 162.7 ± 5.5 cm; body mass, 71.2 ± 16.0 kg) who underwent ≥3 months of resistance training performed an initial week of familiarization and a second week of testing and retest, with a 48–72 hour interval. Results: The results showed maximal and relative load strength of 39.3 kg and 0.59 kg/body mass for lower limbs and 20.9 kg and 0.31 kg/body mass for upper limbs. The Kappa indices were 0.93 and 0.95, and the intraclass correlation coefficients were 0.99 and 0.99 for the lower and upper limbs, respectively. Conclusion: Therefore, the present study confirms that the 1-RM test has high reliability and reproducibility in the elderly, for both upper and lower limbs.

The mechanism underlying microbiologically induced carbonate precipitation have not been thoroughly characterized, although numerous scholars and experts have specifically investigated questions regarding minerals induced by bacteria. The study of the precipitation of carbonate minerals induced by halophilic bacteria has aroused wide concern. The present study aimed to investigate the characterization and process of biomineralization in high salt systems by a halophilic bacterium, Chromohalobacter israelensis strain LD532 (GenBank: KX766026), which was isolated from the Yinjiashan Saltern in China. Carbonate minerals induced by LD532 were investigated in several sets of comparative experiments that employed magnesium sulfate and magnesium chloride as Mg resources. Magnesium calcite and aragonite were induced by LD532 bacteria, whereas these minerals did not appear in the control group. The mineral phases, micromorphologies, and crystal structures were analysed using X-ray powder diffraction, scanning electron microscopy, and energy dispersive X-ray detection. The carbonic anhydrase and urease secreted by strain LD532 through metabolism increased the pH value of the liquid medium and promoted the process of carbonate precipitation. Further study using high resolution transmission electron microscopy, energy dispersive X-ray detection and analysis of ultrathin slices showed that the nucleation sites of carbonate minerals were located on extracellular polymeric substances and the membranes of intracellular vesicles of LD532 bacteria, which provided favourable conditions for the growth of carbonate mineral crystals. The morphologies and compositions of minerals formed in solutions of MgSO₄ and MgCl₂ display significant differences, indicating that different sources of Mg²⁺ may also affect the physiological and biochemical activities of microorganisms and thus mineral deposition. This study will be of some interest for the interpretation of carbonate biomineralization in natural salt environments and has some value as a reference in understanding sedimentary carbonates in ancient marine environments, such as tidal flats.