Sendust is a magnetic metal powder that was invented by Hakaru Masumoto at Tohoku Imperial University in Sendai, Japan circa 1936 as an alternative to permalloy in inductor applications for telephone networks. Sendust composition is typically 85% iron, 9% silicon and 6% aluminium. The powder is sintered into cores to manufacture inductors. Sendust cores have high magnetic permeability (up to 140 000)[clarification needed], low loss, low coercivity (5 A/m) good temperature stability and saturation flux density up to 1 T[clarification needed].
Due to its chemical composition and crystallographic structure Sendust exhibits simultaneously zero magnetostriction and zero magnetocrystalline anisotropy constant K1.
Sendust is harder than permalloy, and is thus useful in abrasive wear applications such as magnetic recording heads.
See also
External links
- Comparison of molybdenum permalloy with sendust as energy storage inductors (PDF file)
- Sendust properties
 | This alloy-related article is a stub. You can help Wikipedia by expanding it. |
This page was last edited on 7 September 2023, at 16:40