One mechanism by which fructose could exert deleterious effect in metabolism and inflammation is via its potency vis-à-vis de Maillard reaction. We employed simulated stomach and duodenum digestion of ovalbumin to test the hypothesis that indeed AGEs are formed by fructose during simulated digestion of an ubiquitous food protein with intrinsic allergenic potential and under model physiological conditions. Methods: OVA was subjected to simulated gastric and intestinal digestion using standard models, in presence of fructose or glucose (0-100 mM). Peptide fractions were analyzed by fluorescence spectroscopy and intensity at Excitation: λ370 nm, Emission: λ 440nm. Results: AGE adducts form between fructose and OVA which can be found in peptide fractions (< 5 kDa) at times (30 min) and concentration ranges (10 mM) plausibly found in the intestines, whereas no reaction occurs with glucose. The reaction is inhibited by chlorogenic acid at concentrations compatible with those found in the gut. The reaction is inhibited by AG, a specific antiglycation agent. Conclusion: Our proof of principle study shows that fructose-AGE formation on an ubiquitous allergenic protein indeed occurs in one hour and thereby may pave the way for the study of yet another mechanism by which the excess fructose in our Western diets is contributing to disease: intestinal AGE formation, absorption and RAGE engagement.

This study presents a comprehensive investigation into the spectrum and determinants of child abuse and neglect in Nkpor-Uno, a community in Anambra State, Nigeria. Through a descriptive surveys design, the study explores various forms of abuse and neglect experienced by children, as well as the underlying factors contributing to these phenomena. The population for the study consisted of 1000 parents/ caregivers who are residents of Nkpor-uno. The sample for the study consisted of 100 respondents, purposive sampling techniques was used for the study. The questionnaire was a self-designed structured questionnaire. Data collected were analyzed using frequency, mean and standard deviation. Findings reveal alarming prevalence rates of child maltreatment, including physical, emotional, sexual abuse, and neglect. Socioeconomic factors such as poverty, parental substance abuse, family dynamics, and inadequate sex education emerged as significant contributors to child maltreatment. The study underscores the urgent need for targeted interventions and support systems to address the root causes of abuse and neglect and safeguard the well-being and development of children in Nkpor-Uno. By raising awareness, enhancing access to resources, and promoting positive parenting practices, we can strive towards building a safer and healthier environment for children, ensuring they are protected from harm and given the opportunity to thrive.

Titanium alloys belong to the metal biomaterials that are one of the most widely used in medicine. In recent years, in order to reduce the use of vanadium, Ti6Al4V alloy is increasingly replaced by Ti6Al7Nb alloy. In addition, to ensure the best possible biocompatibility, its surface is subjected to appropriate modifications, for example, anodic oxidation. Despite the extensive use of anodic oxidation of titanium implants in orthopedics, there are few works focused on a detailed analysis of the chemical composition of the surface layers. In addition, the effect of treatments before anodic oxidation on the properties of the produced layer has not been analyzed. Thus, the purpose of this study was to analyze in detail the chemical composition of the passive layer of Ti6Al7Nb alloy obtained by anodic oxidation preceded by sandblasting. Moreover, the physicochemical properties of the analyzed surface affecting biocompatibility were determined. For this purpose, surface observation, wettability and roughness tests, microhardness tests, electrochemical tests and phase composition analysis were carried out. In addition, the preclinical suitability, of the surface modified in this way, was evaluated by cytotoxicity tests.

This review examines additive manufacturing for refractory tungsten (W) and its alloys. It emphasizes the primary challenges and determining factors involved in additive manufacturing pure W, W alloys, and composites. Our focus in this regard extends to both process and alloying strategies designed to address critical issues such as densification, micro-cracking, and mechanical properties in tungsten-based components produced through additive techniques. Throughout the review, we organize existing knowledge and insights into convenient tables, serving as valuable resources for researchers embarking on a deeper exploration of these topics.

The work presents a mathematical model of a thermogravimetric curve for the growth and simultaneous sublimation of scale on a metal or alloy surface. Reduction of the reaction area as a result of the formation of oxides of alloying elements (for obtaining the basic oxide) is considered for the alloy. For metals, the case where this area is increased as a result of powder metal crushing is also considered. The equations that were obtained are employed to explain the kinetic curves of the mass change of the samples.

A new model of gravity is presented here similar to the earlier work of Verlinde on Emergent Gravity but without the use of Verlinde's main assumption on the nature of gravity as an entropic force using the First Law of Thermodynamics. Instead, the model will be shown to be consistent with the Second Law of Thermodynamics as used in Black Hole Physics. Moreover, it does not use the Equipartition Theorem such that there is no need to define a thermal bath enclosed within a holographic screen. The theory uses $E=NE_{p}$, for the total energy of a massive object where $E_{p}$ is the Planck Energy while $N$ is the number of Planck Energy to represent the maximum possible density of information that can reside in matter. The theory uses also the Holographic Principle as the basis for an information-theoretic approach to the nature of gravity. It is shown here that gravity emerges whenever there is an updating of the information within a given volume of space by the presence of matter.

In this work we explored how solvents can affect olefin oxidation reactions catalyzed by MCM-bpy-Mo catalysts and whether their control can be made with those players. The results of this study evidenced that polar and apolar aprotic solvents modulated the reactions in different ways. Experimental data showed that acetonitrile (aprotic polar) could hinder largely the reaction rate whereas toluene (aprotic apolar) did not. In both cases product selectivity at isoconversion was not affected. Further insights were obtained by means of neutron diffraction experiments, which confirmed the kinetic data allowing to propose a model based on substrate-solvent crosstalk by means of hydrogen bonding. In addition, the model was also validated in the ring-opening reaction (overoxidation) of styrene oxide towards benzaldehyde, which progressed when toluene was the solvent (reaching 31% styrene oxide conversion) but was strongly hindered when acetonitrile was used instead (reaching only 7% conversion), due to the establishment of H-bonds in the latter. Although this model was confirmed and validated for olefin oxidation reactions, it can be envisaged that it may also be applied to other catalytic reaction systems where reaction control is critical, while widening its use.

Heat-treated aluminum-silicon (Al-Si)-based alloys have dominated the cast lightweight alloy industry for several decades. However, in the last decade, Al-Ce-based alloys have shown promise in replacing Al-Si alloys due to their ability to remove the need for costly heat treatments. Since the properties of Al-Ce alloys depend on the as-cast microstructure, it is important to characterize the solidification kinetics of these alloys. Therefore, this study focused on characterizing the solidification of a near eutectic Al-Ce alloy with additions of Ni and Mn. The alloy was cast in a wedge mold configuration, resulting in cooling rates between 0.18 and 14.27 °C/s. SEM coupled with EDS and DSC techniques characterized the evolution rate of solid phases. The SEM/EDS data revealed that an Al10CeMn2 phase is present at higher cooling rates. At lower cooling rates, near the center of the casting, a proeutectic Al23Ce4Ni6 phase was more present. It was observed that up to 2.6 at. % of Mn was dissolved in this proeutectic Al23Ce4Ni6 phase, thereby removing a large portion of the available Mn for forming the Al10CeMn2 phase. DSC analysis showed differences in the samples' liquidus temperatures which is indicative of compositional variations. Inductively coupled plasma atomic emission spectroscopy (ICP-OES) and Scheil solidification simulations correlated the compositional differences to phase formation, which agreed with the SEM and DSC results. This experimentation provides insight into novel Al-Ce-Ni-Mn alloys and where their potential lies in industrial applications.

MnO₂ nanoparticles are considered nanozymes with intrinsic peroxidase-like activity and there are several reports on their application in the field of nanozyme-based sensing and detection, however, up to now, there is no report on the investigation of their biochemical and kinetics properties toward enzyme-mediated oxidations. Hence, in this work, the MnO₂ nanozymes were synthesized and characterized with different characterization methods. Thereafter, their biochemical properties including pH stability, thermal stability, and salt stability as well as their kinetics perfromances were evaluated toward n-electron irreversible oxidation of 3,3’-diaminobezedine. The results showed that the as-prepared nanozymes reveal their maximal enzyme-like activity over a wide pH range of 3.0-6.0 at a temperature of 23-25 ℃ toward oxidation of 3,3’-diaminobezedine. Besides, the salt stability studies exhibited that the as-mentioned nanozymes can save their maximal activity over a wide range of high salt concentrations over 3-7 M of NaCl. Moreover, the kinetics studies revealed a K_m as low as 1.6 mM and a V_max as high as 47 nM sec^-1 for the MnO₂ nanozymes toward irreversible oxidation of DAB to produce the brown-colored polyDAB.

MgAl oxide coatings containing MgO and MgAl2O4 phases were doped with CeO2 particles using plasma electrolytic oxidation (PEO) of AZ31 magnesium alloy in 5 g/L NaAlO2 water solution, with CeO2 particles added at concentrations up to 8 g/L. They underwent extensive inve-stigation into their morphology, chemical and phase compositions, and most importantly, photoluminescent (PL) properties and photocatalytic-activity (PA) in photodegradation of methyl orange (10 cm3 of 8 mg/L). The concentration of CeO2 particles in the aluminate electrolyte influences the amount of CeO2 particles incorporated into MgAl oxide coatings, but CeO2 particles have no signi-ficant effect on the surface morphology, thickness, or phase structure of the coatings. The PL emi- ssion spectrum of MgAl oxide coating is divided into two bands: one in the 350-600 nm range related to structural defects in MgO, and another much more intense in the 600-775 nm range attributed to F+ centres in MgAl2O4. Incorporated CeO2 particles do not have a significant effect on the PL intensity of the band in the red spectral region, but the PL intensity of the first band increases with the concentration of CeO2 particles. PA of MgAl/CeO2 oxide coatings is higher than that of pure MgAl oxide coatings. The highest PA was observed for MgAl/CeO2 oxide coatings formed in aluminate electrolytes with the addition of 2 g/L of CeO2 particles. The MgAl/CeO2 oxide coatings remained chemically and physically stable across multiple cycles, indicating their potential for applications.

Carbon supported nanoparticles of monometallic Ni catalyst and binary Ni-Transition Metal (Ni-TM/C) electrocatalytic composites were synthesized via chemical reduction method, where TM stands for the doping elements Fe, Co, and Cu. The chemical composition, structure and morphology of the Ni-TM/C materials were characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffractometry (XRD), transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM) and energy-dispersive X-ray spectroscopy (EDS). The electrochemical properties towards hydrogen oxidation reaction in alkaline medium were studied using the rotating disc electrode and cycling voltammetry methods. A significant role of the TM dopant in the promotion of the hydrogen electrooxidation kinetics of the binary Ni-TM/C materials were revealed. A record-high in exchange current density value of 0.060 mA cm²_Ni was measured for Ni₃Fe₁/C, whereas the monometallic Ni/C counterpart has only shown 0.039 mA cm²_Ni. In order to predict the feasibility of the electrocatalysts for hydrogen chemisorption, density functional theory was applied to calculate the hydrogen binding energy and hydroxide binding energy values for bare Ni and Ni₃TM₁.

Ultra-high temperature oxidation-resistant alloys (UTORAs) have received a lot of attention due to the increased research demand for deep space exploration around the world. But UTORAs have the disadvantages of easy oxidation and chalking. So, in this study, a UTORA was prepared by hot-press sintering on VZrHfNbTa (HEA) substrate coated with hafnium. The bonding mechanism, resistance to high-temperature oxidation, and hardness of the sample tests were carried out. The results show that zirconium in the matrix will diffuse into the hafnium coating during the high-temperature sintering process and form the HfZr alloy transition layer, the coating thickness of the composite is about 120 μm, and the diffusion distance of zirconium in the hafnium coating is about 60 μm, this transition layer chemically combines the hafnium coating and the HEA substrate into a monolithic alloy composite. The results of high-temperature oxidation experiments show that the oxidation degree of the hafnium-coated VZrHfNbTa composite material was significantly lower than that of the VZrHfNbTa HEA after oxidation in air at 1600 °C for 5 h. The weight gain of the coated sample after oxidation is 56.56 mg/cm2, which was only 57.7 % compared to the weight gain of the uncoated sample (98.09 mg/cm2 for uncoated), and the surface of the uncoated HEA showed obvious dents, oxidation, and pulverization occurred on the surface and interior of the sample. In contrast, the coated composite alloy sample mainly underwent surface oxidation sintering to form a dense HfO2 protective layer, and the internal oxidation of the hafnium-coated VZrHfNbTa composite alloy was significantly lower than that of the uncoated VZrHfNbTa HEA.

Rapid solidification during metal additive manufacturing (AM) leads to non-equilibrium microsegregation, which can result in the formation of detrimental phases and cracking. Most of the microsegregation models, assume a Scheil-type solidification, where the solidification interface is planar and there exists local equilibrium at the interface along with either zero or infinite solute diffusion in the respective participating phases - solid and liquid. This assumption leads to errors in prediction. One has to account for finite solute diffusion and the curvature at the dendritic tip for more accurate predictions. In this work, we compare different microsegregation models that do and do not consider finite diffusion and dendrite tip kinetics against the experiments. We also propose a method to couple dendrite tip kinetics with the diffusion module (DICTRA®) implemented in Thermo-Calc®. The models which accounted for both finite diffusion and dendrite tip kinetics matched well with the experimental data.

In the article, we are trying to find a general law that describes the physical properties of a complex compound through the same physical properties of compound elements. For metal alloys operated under extreme conditions - neutron and proton irradiations and thermal heating, the mechanical properties of these alloys and their elements have been studied. It turned out that the ultimate tensile strength of tantalum alloys used in the design of space reactors can be expressed in terms of the weighted sum of the ultimate tensile strengths of its elements in the range of neutron doses: (0 - 0.96) displacement per atom (dpa) for Ta–10W alloy and (1.4 - 1.7) dpa for T–111 alloy with a neutron energy of more than 0.1 MeV. For tungsten binary alloys used in the design of fusion reactors, the Vickers hardness can also be expressed in terms of the weighted sum of the Vickers hardnesses of the alloy elements in the range of proton irradiation doses: (0 - 0.05) dpa for W-1%Re alloy, (0.05 - 0.2) dpa for W-3%Re alloy and (0.05 - 1) dpa for W-1%Ta with a proton energy of 1 MeV.

The direct methane to methanol (MTM) oxidation is a grand challenge in catalysis, with profound economical implications for the modern chemical industry. Bioinspired metal-organic frameworks (MOFs) with active iron and copper sites have been emerging very recently as innovative catalytic platforms to accomplish the MTM conversion under mild conditions. This review discusses the current state of the art regarding the application of MOFs with iron and copper catalytic centers to perform the MTM reaction, with a focus on the diverse spectroscopic techniques used to unveil the electronic and structural properties of the MOF catalysts at a microscopic level. We explore the synthetic strategies employed to incorporate iron and copper sites into different MOF topologies, the efficiency and selectivity of the iron- and copper-bearing MOF catalysts, and the ensuing MTM reaction mechanisms proposed on the basis of spectroscopic characterization supported by theory. In particular, we evidence how the combination of complementary spectroscopic tools probing different regions of the electromagnetic spectrum is particularly useful to reach a satisfactory understanding of the key reaction pathways and intermediates. Finally, we provide a critical perspective on future directions to advance the use of MOFs to accomplish the MTM reaction.

Solid oxide cells are capable of efficiently converting various chemical energy carriers to electricity and vice versa. The urgent challenge nowadays is the faster degradation rate compared with other fuel cell/electrolyzer technologies. To understand the degradation mechanisms, simulation of a solid oxide cell is helpful. Since most previous research developed models using commercial software, such as COMSOL and ANSYS Fluent, a gap for knowledge transfer is being gradually formed between academia and industry due to licensing issues. This paper introduces a multiphysics model, developed by a computational code, openFuelCell2. The code is implemented with an open-source library, OpenFOAM. It accounts for momentum transfer, mass transfer, electrochemical reactions and metal interconnect oxidation. The model can precisely predict I-V curves under different temperatures, fuel humidity and operation modes. Comparison between OpenFOAM and COMSOL simulations shows good agreement. The metal interconnect oxidation is modelled, which can predict the thickness of the oxide scale under different protective coatings. Simulations are conducted by assuming an ultra-thin film resistance on the rib surface. It is revealed that coatings fabricated by atmospheric plasma spraying can efficiently prevent metal interconnect oxidation, with a contribution of only 0.53 \% to the total degradation rate.

Carbazole is one of the typical heterocyclic aromatic compounds (NSO-HETs) observed in pol-luted urban atmosphere, which has become a serious environmental concern. The most im-portant atmospheric loss process of carbazole is the reaction with OH radical. The present work investigated the mechanism of OH-initiated atmospheric oxidation degradation of carbazole by using density functional theory (DFT) calculations at the M06-2X/6-311++G(3df,2p)//M06-2X/6-311+G(d,p) level. The rate constants were determined by the Rice-Ramsperger-Kassel-Marcus (RRKM) theory. The lifetime of carbazole determined by OH was compared with other typical NSO-HETs. The theoretical results show that the degradation of carbazole initiated by OH radical includes four types of reactions: OH additions to “bend” C atoms, OH additions to “benzene ring” C atoms, H abstractions from C-H bonds and the H ab-straction from N-H bond. The OH addition to C1 atom and the H abstraction from N-H bond are energetically favorable. The main oxidation products are hydroxycarbazole, dialdehyde, carba-zolequinone, carbazole-ol, hydroxy-carbazole-one and hydroperoxyl-carbazole-one. The calcu-lated overall rate constant of carbazole oxidation by OH radical is 6.52 × 10−12 cm3 molecule−1 s−1 and the atmospheric lifetime is 43.92 h under the condition of 298 K and 1 atm. The lifetime of carbazole determined by OH radical is similar with that of dibenzothiophene oxidation but longer than those of pyrrole, indole, dibenzofuran and fluorene. This work provides a better understanding of the reactivity of carbazole in the atmospheric environment, the formation of secondary organic aerosols, and the chemical degradation and removal of carbazole in the at-mospheric environment.

Rare earth rich magnesium alloys are used in aerospace and automotive fields because of their high specific strength and good castability. However, due to their low corrosion resistance, protective surface treatments, such as conversion coating or electroless plating are necessary, when they have to be used in humid or corrosive environments. The present study was aimed to evaluate the effect of Plasma Electrolytic Oxidation (PEO) and different surface roughness (Ra≈0.8 μm and Ra≈0.3 μm) on the rotating bending fatigue of an innovative Mg alloy, with a high content of Nd (up to 3.1 wt%) and Gd (up to 1.7 wt %). Fatigue tests revealed a 15% decrease in the fatigue strength of the PEO treated alloy (fatigue strength = 88 MPa) with respect to the bare alloy (fatigue strength = 103 MPa). The reduction of fatigue strength was mainly due to the residual tensile stresses induced by the PEO treatment. The effect of surface roughness on the bare alloy was, instead, negligible. The mechanisms of crack initiation were similar in the untreated and PEO treated alloy, with crack nucleation sites located in correspondence of large facets of the cleavage planes.

The microstructure evolution and grain refinement kinetics of a solution treated Cu – 0.1Cr – 0.06Zr alloy during equal channel angular pressing (ECAP) at a temperature of 673 K via route B_C were investigated. The microstructure change during plastic deformation was accompanied by the microband formation and an increase in the misorienations of strain-induced subboundaries. The refinement of initial coarse grains was considered as a result of continuous dynamic recrystallization. The dynamic recrystallization kinetics was discussed in terms of grain/subgrain boundary triple junction evolution. The strain dependence of the triple junctions of high-angle boundaries can be expressed by a modified Johnson-Mehl-Avrami-Kolmogorov relationship with a strain exponent of about 1.49. Severe plastic deformation by ECAP led to substantial strengthening of the Cu-0.1Cr-0.06Zr alloy. The yield strength increased from 60 MPa in the initial state to 445 MPa after the total strain of 12.

Microwave technology has a potential application in the extraction of zinc from sulphide ores, knowledge of the dielectric properties of these ores plays a major role in the microwave design and simulation for any process. The dielectric properties of zinc sulfide concentrate for two different apparent densities—1.54 and 1.63 g/cm³—have been measured by using the resonance cavity perturbation technique at 915 and 2450 MHz during the roasting process for the temperature ranging from room temperature to 850 °C. The variations of dielectric constant, the dielectric loss factor, the dielectric loss tangent and the penetration depth with the temperature, frequency and apparent density have been investigated numerically. The results indicate that the dielectric constant increases as the temperature increases and temperature has a pivotal effect on the dielectric constant, while the dielectric loss factor has a complicated change and all of the temperature, frequency and apparent density have a significant impact to dielectric loss factor. Zinc sulfide concentrate is high loss material from 450 to 800 °C on the basis of theoretical analyses of dielectric loss tangent and penetration depth, its ability of absorbing microwave energy would be enhanced by increasing the apparent density as well. The experimental results also have proved that zinc sulfide concentrate is easy to be heated by microwave energy from 450 to 800 °C. In addition, the experimental date of dielectric constant and loss factor can be fitted perfectly by Boltzmann model and Gauss model, respectively.

Semi-solid feedstock of AZ80 magnesium alloy modified by minor rare-earth Y element (0, 0.2, 0.4, 0.8 wt.%) were fabricated by strain induces melting activated (SIMA) in the form of extrusion and partial remelting. The effect of Y addition on the microstructure evolution of extruded and isothermal treated alloy was observed by optical microscope (OM), scanning electron microscope (SEM), X-ray diffraction (XRD) and quantitative analysis. The results show that the Y addition can refine the microstructure and make the β-Mg17Al12 phases agglomerating. During the subsequent isothermal treatment at 570℃, the average solid grain size, shape factor and liquid fractions increased with prolonged soaking time. Smaller spheroidal solid grains and the larger shape factor were obtained due to Y addition. The coalescence and Ostwald ripening of solid grains operated the coarsening process simultaneously. The coarsening rate constants of AZ80M1 (0.2 wt.% Y addition) of 164.22 μm3s-1 was approximately four times less than the un-modified AZ80 alloy of 689.44 μm3s-1. In contrast, the desirable semi-solid structure featured by fine, well globular solid grains and appropriate liquid fractions and shape factor was achieved in AZ80M1 alloy treated at 570℃ for 20-30 min.

This study concerns calculation and comparison of Fe, Co, Ni and Cu deposition rates in tungsten codeposition process based on electrodeposition of numerous tungsten alloys. 8 different tungsten alloys containing from 2 to 5 metals were electrodeposited in constant conditions in order to compare exact reduction rates. Calculated rates enabled control of the alloy composition precise enough to obtain a high-entropy WFeCoNiCu alloy with well-balanced composition. Introduction of copper to form the quinternary alloy was found to catalyze the whole process, increasing deposition rates of all components of the high-entropy alloy.

Isothermal interrupted hot compression tests of 5754 aluminum were conducted on Gleeble-3500 thermo-mechanical simulator at temperature 350 °C and 450 °C, strain rate 0.1 s-1 and 1s−1. These tests simulated flat rolling to investigate how softening behaviors respond to controlled parameters, such as deformation temperature, strain rate and delay times. This data allowed the parameters for the hot rolling process to be optimized. The delay times during interrupted compression vary between 5s and 60s. The dynamic softening at each pass and metadynamic recrystallization at the intervals of deformation passes were analyzed in detail. 0.2% offset yield strength is applied to calculate the softening fraction undergoing metadynamic recrystallization. A kinetic model was developed to describe metadynamic recrystallization behaviors of the hot deformed 5754 aluminum alloy. Furthermore, the time constant for 50% recrystallization was expressed as functions related to the temperature and the strain rate. The experimental and calculated results were found to be in close agreement, which verified the developed model.

It is well-known that the peroxidase enzyme catalyzes the oxidation of different substrates such as 3,3’,5,5’-thetramethylbenzidine, and 3,3’-diaminobenzidine, however, the affinity of different substrates to the enzyme and consequently and catalytic performances of the enzyme toward different substrates is not same, resulting in different kinetics indexes. As the BSA-gold nanozymes are considered artificial peroxidase enzymes, hence, the kinetics indexes of these nanozymes should also be varied by varying their substrate. Hence, in this work, a comparative study was performed on the kinetics performances of BSA-gold nanozymes for enzyme-mediated oxidations of 3,3’,5,5’-thetramethylbenzidine, and 3,3’-diaminobenzidine. The results showed that the Km value of BSA-gold nanozymes was 0.03 mM and 0.72 mM toward TMB and DAB, in order, to reveal the higher affinity (lower Km) of TMB for binding to nanozyme active nodes compared to its alternative substrate, DAB. In contrast, the Vmax was found to be 263 nM sec^-1 and 185 nM sec^-1 for nanozmye-mediated oxidation of TMB and DAB, respectively. The higher Vmax of the nanozyme-mediated oxidation of TMB revealed that the catalytic efficiency of BSA-Au nanozymes toward TMB oxidation is higher (about 1.5-fold) than that of the DAB oxidation. The difference between the kinetic indexes of TMB and DAB may be related to their different oxidation pathways and their different reactivity. In fact, the DAB oxidizes via an n-electron irreversible oxidation pathway to produce an indamine polymer. While TMB nanozyme-mediated oxidation has occurred upon a 2-electron reversible mechanism for the production of a cation radical. These different pathways resulted in different kinetic performances.

This paper presents an investigation of the oxidation of Alloy X-750 containing 5% Fe in a simulated boiling water reactor (BWR) environment. To mimic the conditions in which the bare metal is exposed to the reactor water the samples were not pre-oxidized. The specimens were exposed for durations ranging from 2 to 840 hours, and the development of the oxide microstructure was mainly studied using electron microscopy. The results showed that the oxide scale consisted of blocky crystals of trevorite on top of a porous inner layer rich in Ni and Cr. After the longest exposure time, the trevorite crystals completely covered the specimen surface. The study further revealed that the speed at which the oxide grew and the metal dissolved both decreased with time. Additionally, the metal thinning process was found to be sub-parabolic. Given the significant variation in iron content in the X-750 specification, the influence of this element on the material's corrosion performance in BWR was examined by comparing the results from this investigation with those from previous work on material containing 8 wt% Fe. The study demonstrated that the oxide growth, metal dissolution and metal thinning were slower in the material with higher Fe content, indicating the importance of this element in limiting the degradation of Alloy X-750 in BWR environments.

Keywords: liquid alloys, microstratification, dispersed particles, spontaneous dispersion, criteria for true (entropic) spontaneous dispersion, mechanisms of quasi-spontaneous dispersion, methods and results for assessing size of dispersed particles.

: TiAl6V4 alloy is widely used in selective laser melting and direct laser melting. In turn, works devoted to the issue of how the track stacking scheme affects the value of mechanical properties is not enough. The influence of the Ti6Al4V alloy track trajectories on the microstructure and mechanical properties during direct laser deposition is studied in this article for the first time. The results were obtained on the influence of «parallel» and «perpendicular» technique of laying tracks in direct laser synthesis. All studied samples have a microstructure typical of the hardened two-phase condition titanium. It is shown that the method of laying tracks and the direction of load application during compression testing relative to the location of the tracks leads to a change in the ultimate strength of the Ti-6Al-4V alloy from 1794 to 1910 MPa. The plasticity of the Ti-6Al-4V alloy obtained by direct laser alloying can vary from 21.3 to 33.0% depending on the direction of laying the tracks and the direction of the compression test. The hardness of alloys varies in the range from 409 to 511 HV and depends on the method of laying the tracks and the direction of hardness measurements.

Ti-Al alloy phase layer/Ti-Al carburizing composite coating was prepared on the surface of titanium alloy by the stepwise coating method of hot dip aluminization and then carburizing. The weight gain results of the composite coating showed that the titanium alloy coated with the composite coating had long-term stability (≥16 days) at 800oC. The microstructure, phase structure and composition of the composite coating were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS).The composite coating is composed of an alloy phase layer and a carburized layer. The natural transition of four phases (Ti3Al/TiAl/TiAl2/TiAl3) in the alloy phase layer, significantly improves the interfacial bonding between the coating and the substrate, and slows down the propagation of microcracks through the coating.Al2O3, TiC and C in the carburizing layer improve the surface hardness of the coating, and TiAl2 and Al2O3 also have excellent oxidation resistance at high temperature.

The present study aimed to investigate the effect of cold deformation on the precipitation kinetics of a binary CuSc alloy containing 0.4 wt.% scandium using the experimental analysis method of differential scanning calorimetry (DSC). Non-deformed and 75% cross-section reduced cold-rolled, supersaturated specimens were tested at non-isothermal DSC runs at up to five different heating rates. The DSC results showed that cold deformation significantly accelerated the precipitation process in the binary alloy, leading to a decrease in the initial and peak temperatures of the exothermic reactions. The activation energies calculated with the Kissinger method, indicated that the precipitation activation energy decreased with increasing cold deformation. The findings of this study provide worthy implications to further optimize the processing of Cu-Sc alloys with improved mechanical properties.

Microcrystalline and near nanocrystalline AlCrFeCoNi high-entropy alloy (HEA) coatings were applied on Inconel 718 superalloy using air plasma spraying (APS) process. High-temperature oxidation behavior of the microcrystalline and near nanocrystalline AlCrFeCoNi HEA coated superalloy were examined at 110°C under the air atmosphere for 50 cycles under cyclic heating and cooling (1 h for each cycle). The oxidation kinetics of both nanocrystalline and microcrystalline coated superalloy was accordingly analyzed by weight change measurement. It was noticed that the uncoated and coated followed the parabolic rate law of the oxidation. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), energy dispersive X-ray analysis (EDS), and elemental mapping techniques were used to analyze the oxidized coated and uncoated samples. In the HEA coated superalloy, Fe, Ni, Co, and Al were oxidized in the inter-splat region, whereas the splats which consist mainly of Ni and Cr remained unoxidized. Because of the formation of compact and adhesive thin NiO, CoO oxides, and spinels together with the Al2O3 oxide scale on the surface of the coating during oxidation, the developed nanocrystalline HEA coating shows better oxidation resistance than the microcrystalline HEA coating.

Crystal structures of simple metals and binary alloy phases based on the face-centered cubic (fcc) structure are analyzed within the model of Fermi sphere – Brillouin zone interactions to understand the stability of original cubic structure and derivative structures with distortions, superlattices and vacancies. Examination of the Brillouin-Jones configuration in relation to the nearly-free electron Fermi sphere for several representative phases reveals significance of the electron energy contribution to the phase stability. Representation of complex structures in the reciprocal space clarifies their relationship to the basic cubic cell.

With the evolution of toxic chemicals continuing to progress, developing methods for the destruction of chemical warfare agents (CWAs) has become an increasingly important research topic. Metal-organic frameworks (MOFs) are a class of porous crystalline solids that have sparked interest in this area. Due to their exceptional porosities and large surface areas, MOFs possess superior adsorption, reactivity, and catalytic abilities, making them structurally ideal candidates for the capture and decomposition of target species. Additionally, the tunable networks of MOFs allow their chemical functionalities to be customized for various applications and operating conditions, making them practicable in personal protective equipment and adjustable to dynamic environments. This paper reviews experimental and computational studies on CWA removal by MOFs, with a special emphasis on nerve agent (GB, GD, and VX) removal via hydrolysis and sulfur mustard (HD) removal via selective photooxidation. With extraordinary structural stability and reusability, zirconium-based MOFs are the most promising materials for hydrolytic and photooxidative degradation of CWAs and are thus the primary focus of this work. First-principles approximations of the intrinsic catalytic reaction mechanisms towards different agents in Zr-MOFs are summarized, and developments in the structure-property relationships governing Zr-MOF design rules for efficient degradation in the aqueous and solid phases are discussed. We also examine recent progress in tuning and functionalizing MOFs to promote practical CWA removal under realistic battlefield conditions.

The poor oxidation resistance of refractory high-entropy alloys (RHEAs) is a major obstacle for their use in high-temperature engineering applications. Anti-oxidation coating technology is an effective method for improving the oxidation resistance. In this paper, the Si-20Cr-20Fe coating was prepared on MoNbTaTiW RHEA by a fused slurry method. The microstructural evolution and compositions of the silicide coating under high-temperature oxidation environment were studied. The results show that the silicide coating could effectively prevent the oxidation of the MoNbTaTiW RHEA. The initial silicide coating had a double-layer structure; a high silicon-content layer mainly composed of MSi2 as the outer layer and a low silicon-content layer mainly contained M5Si3 as the inner layer. Under high-temperature oxidation conditions, the silicon element diffused from the silicide coating to the RHEA substrate while the oxidation of the coating occurred. After oxidation, the coating was composed of an outer oxide layer and an inner silicide layer. The silicide layer moved toward the inside of the substrate, led to the increase of its thickness. Compared with the initial silicified layer, its structure did not change significantly. The structure and compositions of the oxide layer on the outer surface strongly depended on the oxidation temperature. This paper provides a strategy for protecting RHEAs from oxidation at high-temperature environments.

The objective of this study was to investigate the impact of athletes' respiratory muscle strength, as assessed through maximal inspiratory (MIP) and expiratory pressure (MEP), on aerobic endurance, as indicated by maximal oxygen consump-tion (Max VO2) kinetics. Respiratory muscle strength was assessed using a digital spirometer (Pony FX Cosmed, Italy), while maximal oxygen utilization capacity was measured using a breath-by-breath automatic portable gas analysis system (Cosmed K5, Italy). Statistical analysis was conducted utilizing SPSS 22.0. Based on the standardized regression coefficients (β), it was found that MEP (mean ± SD: 130.95 ± 42.82) and inspiratory diaphragmatic circumference values significantly influenced ventilatory equivalent (VE), oxygen consumption (VO2), and carbon dioxide pro-duction (VCO2). Conversely, the remaining predictor variables did not exhibit a sig-nificant effect on VE (mean ± SD: 134.80 ± 36.69), VO2 (mean ± SD: 3877.52 ± 868.47 ml), and VCO2 (mean ± SD: 4301.27 ± 1001.07 ml). In contrast, measurements of chest circumference (mean ± SD: 91.40 ± 10.72 cm), MEP, and diaphragmatic cir-cumference during inspiration (mean ± SD: 95.20 ± 10.21 cm) were found to signifi-cantly impact Max VO2 (mean ± SD: 58.52 ± 10.74 ml/kg/min), while the other pre-dictor variables did not demonstrate a significant effect on Max VO2. Conclusively, the study revealed that measured values of diaphragmatic circumference during inspiration and MEP exerted a notable influence on Max VO2, VE, VO2, and VCO2. Our findings underscore the importance of considering respiratory muscle strength in assessing and enhancing athletes' aerobic performance. These insights contribute to a deeper understanding of the interplay between respiratory function and exercise capacity, offering potential avenues for optimizing training regimens and perfor-mance outcomes in athletic contexts.

Intermetallic compounds are increasingly being expected to utilize in tribological environments, but to date the works are hindered by insufficient ductility at low and medium temperature. This paper presents a novel multiphase intermetallic alloy with the chemical composition of Mo-40Ni-13Si (at.%). Microstructure characterization reveals that a certain amount of ductile Mo phases formed during the solidification process of ternary Mo-Ni-Si alloy melt, which is undoubtedly beneficial to the ductility improvement of intermetallic alloy. Tribological properties of the designed alloy, including wear resistance, friction coefficient and metallic tribological compatibility, were evaluated under dry sliding wear test conditions at room temperature. Results suggested that the multiphase alloy possesses an excellent property for room-temperature wear applications, which is attributed to the unique microstructural features and thereby good combination in hardness and ductility. The corresponding wear mechanism is also reported by observing the worn surface, subsurface and wear debris of alloy, which to be found is soft abrasive wear.

To realize the utilization of peanut shell, this study investigates the combustion behavior, chemical kinetics, and thermodynamic parameters of peanut shell using TGA under atmospheric air. Results indicate that increasing the heating rate leads to higher ignition, burnout, and peak temperatures, as observed in the TG/DTG curves shifting to the right. Analysis of combustion performance parameters suggest that higher heating rates can enhance combustion performances. Kinetic analysis using two model-free methods, KAS and FWO, shows that the activation energy (Eα) ranges from 93.30 to 109.65 kJ/mol for FWO and 89.72 to 103.88 kJ/mol for KAS. The data fit well with coefficient of determination values (R2) close to 1. Pre-exponential factors using FWO range from 2.19×106 to 8.06×107 s–1, and for KAS range from9.72×105 to 2.25×107 s–1. Thermodynamic analysis indicates a low-energy barrier (≤ ±6 kJ/mol) between activation energy and enthalpy changes, suggesting easy reaction initiation. Furthermore, variations in enthalpy (ΔH), Gibbs free energy (ΔG), and entropy (ΔS) upon conversion (α) suggest that peanut shell combustion is endothermic and non-spontaneous, with the generation of more homogeneous or well-ordered products as combustion progresses. These findings offer a theoretical basis and data support for the further utilization of agricultural biomass.

The developed microstructure features a long with mechanical properties in vacuum brazing of commercially pure Ti-alloy using Ti₂₀Zr₂₀Cu_60-x-Ni_x (x=10, 20, 30, 40 and 50) metallic filler. Brazing temperatures and holding times employed in this study were 1240-1279 K (967-1006^oC) for a period of 10 min, respectively. The mechanical properties of brazed joints were evaluated by nanoindention at a constant peak load of 5000 μN and tensile tests. The number of intermetallic phase, such as NiTi₂, Ti₂Cu, (Ti, Zr)₂Cu, (Ti, Zr)₂Ni, β(Ti, Zr), α-Ti and NiTi. The solid solution matrix have been identified at 1279 K out of these different regions the NiTi₂ rich region had the highest nanohardness of 17 GPa, It is interesting to note that among five different glasses, the Ti₂₀Zr₂₀Cu₁₀Ni₅₀ has the highest yield strength of 17 GPa, which is mainly due to NiTi₂ phase. Based on the tensile test results all cracks propagate along the brittle intermetallic compounds like NiTi₂ in the reaction layer the reduction of the strength of the joints and fracture behaviour upon propagation of the crack, which shows the morphological cleavage including facets characteristics.

Abstract: An Al-Co-Y diffusion coating was prepared on a TiAl alloy by pack cementation process at a low temperature range of 650-720 ℃. The influence of different activators and co-deposition temperatures on the coating’s microstructure and formation process, and high temperature oxida-tion performance was studied. The results showed that NaF was a more suitable activator for preparing the Al-Co-Y diffusion coating on TiAl alloy compared to NH4Cl and AlCl3. A more compact coating structure can be obtained when deposition was performed at 680 ℃ using NaF as the activator. The coating was mainly composed of a TiAl3 outer layer, a TiAl2 inner layer, and a thin Al-rich TiAl inter-diffusion layer. The growth of the coating exhibited a positive linear correlation between coating thickness increase and the square root of deposition time. The high-temperature oxidation tests showed that a dense scale mainly composed of Al2O3 and a small amount of TiO2 formed on the coating after oxidation at 950 ℃ for 100 h. The scale possessed excellent high-temperature oxidation resistance, with a parabolic rate constant of the oxidation weight gain approximately 4.9×10-3 mg2/cm4 h, which is lower than that of the TiAl substrate by about three orders of magnitude, and lower than that of the pure Al diffusion coating more than one order of magnitude.

Although composting has many advantages in the treatment of organic waste, there are still many problems and challenges associated with emissions, like NH3, VOCs, and H2S, as well as greenhouse gases such as CO2, CH4, and N2O. One promising approach to enhancing composting conditions is used of novel analytical methods bad on artificial intelligence. To predict and optimize the emissions (CO, CO2, H2S, NH3) during composting process kinetics thought mathematical models (MM) and machine learning (ML) models were utilized. Data about everyday emissions from laboratory composting with compost’s biochar with different incubation (50, 60, 70 °C) and biochar doses (0, 3, 6, 9, 12, 15% d.m.) were used for MM and ML models selections and training. MM has not been very effective in predicting emissions, (R2 0.1 - 0.9), while ML models such as acritical neural network (ANN, Bayesian Regularized Neural Network; R2 accuracy CO:0,71, CO2:0,81, NH3:0,95, H2S:0,72)) and decision tree (DT, RPART; R2 accuracy CO:0,693, CO2:0,80, NH3:0,93, H2S:0,65) have demonstrated satisfactory results. For the first time the ML models to predict CO and H2S during composting were demonstrated. Further research in a semi-scale and field study composting with biochar is needed to improve the accuracy of developments models.

Biopolymers are of growing interest, but to improve some of their poor properties and performance, it is required the formulation of bio-based blends and/or adding of nanoparticles. For this purpose, in this work, two different metal oxides, such as zinc oxide (ZnO) and titanium dioxide (TiO2), at different concentrations (0.5, 1 and 2 %wt.) have been added in polylactic acid (PLA) and polylactic acid/polyamide 11 (PLA/PA11) blends to establish their effects on solid-state properties, morphology, melt behaviour, and photo-oxidation resistance. It seems that the addition of ZnO in PLA leads to a significant reduction of its rigidity probably due to an inefficient dispersion in the melt state, while the addition of TiO2 does not penalise PLA rigidity. Interestingly, the addition of both ZnO and TiO2 in PLA/PA11 blend has a positive effect on the rigidity because of blend morphology refinement and leads to a slight increase in film hydrophobicity. The photo-oxidation resistance of neat PLA and PLA/PA11 blend is significantly reduced due to the presence of both metal oxides, and this must be considered when designing the potential applications. The last results suggest that both metal oxides could be considered as photo-sensitive degradant agents for biopolymer and biopolymer blends.

A dynamic impact test was performed on as-rolled AZ31 alloy with gradient microstructure under various strains. The microstructural evolution and mechanical properties were systematically investigated. As the strain rate gradually increases, an increasing number of twins are formed, facilitating dynamic recrystallization (DRX), and the mechanical properties are also gradually improved as well. The microstructure becomes heterogeneous at higher strain rates, but the peak stress decreases. The impact process results in significantly higher performance due to microstructural refinement, work hardening by dislocations and precipitates. In addition, both the adiabatic shear band and the adjacent crack experience a temperature rise that exceeds the recrystallization temperature of the alloy. This observation also explains the presence of ultrafine recrystallized grains within the adiabatic shear band and the appearance of molten metal around the crack.

A new Mg-Zn-Zr-Ca alloy in powder state was obtained via mechanical alloying method, from pure elemental powder. Further, the obtained powder-alloy was processed by selective laser melting (SLM) procedure to obtain 3D printed samples for small biodegradable implants. A series of microstructural, mechanical and corrosion analysis were performed. The SEM analysis of powder-alloy reveal a good dimensional homogeneity, with uniform colored, no agglutinated and almost rounded particles, suitable for selective laser melting procedure. Further, the SLM samples reveal a robust and unbreakable morphology, with a suitable porosity and without undesirable balling effect. The tested Young’s modulus of the SLM samples, of 42 GPa, is close to cortical bone one, of 30 GPa. The corrosion tests performed in PBS (Phosphate-buffered saline) solution show that the corrosion parameters have a satisfactory evolution.

Human serum albumin (HSA) corona formation at polymer microparticles of a spheroidal shape was studied using dynamic light scattering and laser Doppler velocimetry (LDV). Physicochemical characteristics of the albumin comprising, the zeta potential and the isoelectric point were determined as a function of pH for various ionic strengths. Analogous characteristics of the polymer particles were carried out. The adsorption of albumin on the particles was monitored by electrophoretic mobility measurements (LDV). The stability of the HSA functionalized particle suspensions under various pHs and their electrokinetic properties were determined. The deposition kinetics of the particles on mica, silica and gold sensors were determined in situ by optical microscopy, AFM and by the quartz microbalance (QCM) under diffusion and flow conditions. The obtained results were interpreted in terms of the coarse-grained random sequential adsorption model that allowed to estimate the range of applicability of QCM for determining deposition kinetics of virus and bacteria at abiotic surfaces.

Ti and its alloys are the most commonly used materials for biomedical applications. However, bacterial infection after implant placement is still one of the significant rising complications. Therefore, the application of the antimicrobial agents into implant surfaces to prevent implant-associated infection has attracted lots of attention. Scientific papers have shown that inorganic antibacterial metal element (e.g. Ag, Cu, Zn) can be introduced to implant surfaces with the addition of metal nanoparticles or metallic compounds into electrolyte via micro-arc oxidation (MAO) technology. In this review, the effects of the composition and concentration of electrolyte and process parameters (e.g. voltage, current density, oxidation time) on morphological characteristics (e.g. surface morphology, bonding strength), antibacterial ability and biocompatibility of MAO antimicrobial coating were discussed in detail. Anti-infection and osseo-integration can be simultaneously accomplished with the selection of the proper antibacterial elements and operating parameters. Besides, MAO assisted by magnetron sputtering (MS) to endow Ti-based implant materials with superior antibacterial ability and biocompatibility was also discussed. Finally, the development trend of MAO technology in the future was forecasted.

The continuous casting process of helical fiber reinforced metal matrix composites was proposed, and the experimental equipment was designed and manufactured. The relationship model be-tween the process parameters and the helical shape of the fibers in the metal matrix is analyzed by differential geometry. Helical carbon fiber reinforced lead matrix composites were prepared under different conditions. When the melting temperature and cooling intensity were increased, the helical radius of helical carbon fiber in lead matrix was increased. When the fiber rotation speed was increased, the helical radius was decreased, and the helical pitch was de-creased proportionally. The experimental results are consistent with the process model. Carbon fiber rein-forced aluminum composites were prepared. Scanning electron microscopy showed that the infiltration between the aluminum matrix and the carbon fiber was not complete. As the volume fraction of carbon fiber which was added in composites is too small, the mechanical properties of the composites have not been significantly improved.

The aim of this study was to examine the oxidation of human serum albumin (HSA) caused by oxidative stress after an exhaustive exercise such as ultra-marathon race. Thus, blood samples from 12 adult runners who underwent a 103 km mountain ultra-marathon race were collected pre- and 24, 48 and 72 h post race. HSA was partially purified using affinity chromatography and then was subjected to Western blot analysis for disulfide dimers determination, indicating oxidation. The results were correlated with those from a previous study in which the same samples were analyzed using different oxidative stress markers and a good correlation with protein carbonyls (PC) at all time points was observed. Moreover there was a significant correlation with static oxidation-reduction potential (sORP) at 24 h, and a negative correlation with capacity oxidation-reduction potential (cORP) at 24 and 48 h. In addition, an individual analysis of albumin dimers exhibited great inter-individual differences. This inter-individual variability in the oxidation of HSA may suggest different interventions (e.g. through diet) in order to confront the effects on athletes’ organism after a strenuous exercise. In conclusion, this study supported the importance of the assessment of albumin dimers as a predictive marker for exercise-induced oxidative stress.

Turner syndrome (TS) is caused by a complete or partial absence of an X or Y chromosome, including chromosomal mosaicism, affecting 1 in 2,500 female live births. Sister chromatid exchange (SCE) is used as a sensitive indicator of spontaneous chromosome instability. Cells from mosaic patients constitute useful material for SCE evaluations as they grow under the influence of the same genetic background and endogenous and exogenous factors. We evaluated proliferation dynamics and SCE frequencies of 45,X and 46,XN cells of 17 mosaic TS patients. In two participants, 45,X cells exhibited a proliferative disadvantage in relation to 46,XN cells after 72h of cultivation. The analysis of mean PI showed significant differences between 45,X and 46,XN lineages; however there were no intraindividual differences. On the other hand, mean SCE frequencies showed no differences between the two lineages, but there were intraindividual differences in 5 patients. The absence of mean SCE frequency differences between 45,X and 46,XN lineages may indicate that both were equally unstable, as more than 70% of the 46,XN lineages had an anomalous karyotype. However, 46,XN had a higher mean PI, suggesting that the amount of cells with a karyotype distinct from 45,X may increase with time in mosaic TS women.

Organic electrophoretic coatings have gained significant attention due to their ability to provide a uniform and controlled coating thickness, high coating adhesion, and excellent corrosion protection properties. In this work, to investigate the aging behaviors of an organic electrophoretic coating for magnesium alloys, water absorption kinetics curves of the coatings after immersion in 3.5 wt.% NaCl at 20℃ and 40℃ were measured, and parameters such as the saturated water absorption and saturation time of the free film coatings were fitted to determine the densification evolution of the organic coatings. A tensile test was used to test the tensile strength of the organic coating during service to determine the evolution of the strength and toughness of the organic coating. The evolution of wet adhesion of organic coatings with service time was tested by ASTM D4541-02. The impedance spectra of the organic coatings under the above conditions were detected by EIS, and finally, the failure behavior of the organic coatings under immersion was analyzed.

Weathering and erosion transport minerals and organics toward the sea or lake bottoms over geologic time. The finest solids are deposited in lower, less turbulent areas, such as lake bottoms and continental shelves. They sometimes stack up to thicknesses of kilometers, and begin compacting. These sediment sections are called shales, and as initially deposited in water, shales can have porosities up to 50-80{\%} water, As they are buried, many alteration products from oil to slate are produced due to overburden and temperature increasess, making them important to study. A preceeding paper \cite{1} showed that pressure solution is the primary mechanism for porosity reduction, with possible mechanical compaction at shallow depths. Without naming the mineral(s) involved, it postulated that the greater the product of the water and pore interfaces, the faster the reaction would proceed. This term is $ \varphi^{4m/3}(1-\varphi)^{4n/3}$ , where $\varphi$ is porosity and m and n are numbers close to unity. The large exponents, {\em 4/3}, recognize that the reaction occurs at the molecular scale at which the surfaces are rough. A second term, $\exp^{(-E/RT)}$ , indicates that the reaction is impeded by a quantum energy barrier, E, with diminished impeding power as increased available thermal energy, represented by the absolute temperature, T, becomes available at greater depths in the Earth. These two factors combine to allow porosity $\varphi$ to reduce with time, or equivalently for the fraction of solids, $(1-\varphi)$, to increase with time,$\left. \frac{\partial(ln(1-\varphi) ) }{\partial t } \right |_{\sigma} = (\varphi )^{4m/3}( 1-\varphi )^{4n/3}Ae^{-E/(RT)}$. { \em Here it is shown that this equation can cover quantitatively any actual deposition rates which may have been experienced by the six sections studied, the actual deposition rates being unknown for these cases. Hence a time-depth depositional history for any new shale section, known in detail, would allow determination of the parameters m, n, E and a lumped proportionality constant A. This was accomplished by showing that, for a wide range of depositional rates, r, the range of E for any of the studied sections is small compared to laboratory measurements of quartz solution\cite{2}, 24+-15kJ/mol. Results were obtained over this range of r's using the previously determined m and n, and porosity and temperature profiles. The presently existing porosity profiles necessarily incorporate any overpressure or underpressure conditions that may have existed in the past or currently, as the net difference between overburden and pore pressure is a primary driving force for pressure solution. $SiO_2$ usually comprises 20-50{\%} of shales. In conclusion, pressure solution of quartz can account for vertical compaction of shales quantitatively in the studied examples. Separately, a quasi-eqivalent method for discussing reduced porosities in Macron 2 versus Macron 1 as increased vertical stress, rather than additional horizontal stress, is illustrated. Experiments are suggested to clarify the pressure solution mechanism. The role of horizontal forces is discussed. From a global point of view, shale compaction by pressure solution is a quantified step in the cycling of continental rocks, beginning with rifting.

An analysis of the processes of plastic deformation and acoustic relaxation in a high-entropy alloy Al0.5CoCrCuFeNi was carried out. The following have been established: dominant dislocation defects; types of barriers that prevent the movement of dislocations; mechanisms of thermally activated movement of various elements of dislocation lines through barriers at room and low temperatures. Based on modern dislocation theory, quantitative estimates have been obtained for the most important characteristics of dislocations and their interaction with barriers.

The effects of rare earth Ce on the microstructure and properties of cast pure copper were investigated through thermodynamic calculations, XRD analysis, mechanical testing, metallographic microscopy, and scanning electron microscopy (SEM). The experimental results demonstrate that the reaction between rare earth Ce and oxygen as well as sulfur in copper exhibits a significantly negative Gibbs free energy value, indicating a strong thermodynamic driving force for deoxidation and desulfurization reactions. Ce is capable of removing trace amounts of O and S from copper. Moreover, the maximum solid solubility of Ce in Cu falls within the range of 0.009% to 0.01%. Furthermore, Ce can refine columnar grains while enlarging equiaxed grains in as-cast copper.Upon addition of rare earth Ce, the tensile strength increased by 8.45%, elongation increased by 12.1%, and microhardness rose from 73.5HV to 81.2HV-an increase of 10.5%. Overall, rare earth Ce has been found to enhance both the microstructure and mechanical properties of cast pure copper.

This paper addresses the input coupling problem for the shape memory alloy (SMA) actuated parallel platform with completely unknown nonlinear dynamics. The problem means that in a parallel platform with multiple SMA actuators acting together, the displacement of one of the actuators will simultaneously affect the remaining actuators to change. Due to the coupling problem and nonlinear characteristics of the SMA actuators, it is not easy to control the platform to achieve bi-directional swing with completely unknown nonlinear dynamics. Therefore, a model-free adaptive sliding mode control method is proposed to improve the control accuracy of the complex motion of the platform, avoiding the complex modeling process of the SMA actuated parallel platform. Based on the model-free adaptive control (MFAC) theory, a multiple input and multiple output (MIMO) dynamic linearized mathematical model of the parallel platform is established using the online input and output data of the system. Then, a sliding mode controller is designed based on the dynamic model. A rigorous theoretical analysis proves that the proposed model-free adaptive sliding mode controller is able to stably control the SMA actuated parallel platform, and its tracking error is uniformly ultimately bounded (UUB). Finally, experiments are conducted on the established SMA actuated parallel platform. The results show that the proposed model-free controller is feasible and effective, and can control the system well to achieve the complex motion of bi-directional swing.

This study investigates the effects of Zinc (4wt.%) and severe plastic deformation on the mechanical properties of AZ61 magnesium alloy through the stir-casting process. The severe plastic deformation (equal channel angular pressing (ECAP)) has been done followed by T4 heat treatment. The microstructural examinations revealed that the addition of 4wt.%Zn enhances the uniform distribution of β-phase, contributing to a more uniformly corroded surface in corrosive environments. Additionally, dynamic recrystallization (DRX) significantly reduces the grain size of as-cast alloys after undergoing ECAP. The attained mechanical properties demonstrate that after a single ECAP pass, AZ61 + 4wt.%Zn alloy exhibits optimal yield strength (YS), ultimate compression strength (UCS), and hardness. This research highlights the promising potential of AZ61 + 4wt.%Zn alloy for enhanced mechanical and corrosion-resistant properties, offering valuable insights for applications in diverse engineering fields.

Among the various types of gas sensors, the chemoresistive gas sensors based on metal oxides are considered the most attractive ones due to their simple operation, low costs and miniaturization. Thin films of V2O5 undoped and doped with TiO2 were studied as nitrogen dioxide, methane and hydrogen sensors. The experimental kinetics of the electrical conductivity changes due to introduction and removal of gas on metal oxide gas sensors were successfully explained in terms of the Langmuir adsorption theory.

Structural and functional materials are subjected to harsh oxidizing environments that lead to a rapid decline in their surface chemical stability. At high-temperatures, the diffusion of atoms is erratic; thus, the reactive elements (REs) get a chance to migrate to the surface and look for oxygen-reactive sites. Their migration from the lattice sites creates vacancies in the matrix and thus weakens the bond, making the material prone to environmental degrading factors. Subsequently, the inward diffusion of oxygen, sulfur, nitrogen, or carbon may occupy these vacancies, resulting in undesired precipitation at the grain boundary, which is usually brittle. The solubility and dissociation of attacking species and corrosion products play the most critical role in corrosion in high-temperature water. To evade such situations, Ti, Al, and Cr are added in Ni/Fe-based alloys, forming a dense oxide layer on the surface that impedes further surface migration of ions. The stability of the alloys is then determined by the capability of these oxide layers to heal or reform during spalling/cracking. This review attempts to understand the migration of REs at the interfaces to prepare structural materials in any unexpected set of oxidizing service conditions. This review will also try to establish the interaction mechanism of REs novel/conventionally added in the alloys with the oxidizing elements in the environments to design better degradation-resistant high-temperature alloys.

The grain-to-grain stress vertically in sediments is given by the overburden less the pore fluid pressure, σ, divided by the fraction of the horizontal area which is the supporting matrix , (1 − φ), where φ is the porosity. It is proposed that the fractional reduction of this ratio, Λ, with time is given by the product of φ 4m/3 , (1 − φ) 4n/3 , and one or more Arrhenius functions A exp(−E/RT ) with m and n close to 1. This proposal is tested for shale sections in six wells from around the world for which porosity-depth data are available. Good agreement is obtained above 30-40 C and porosities less than 0.5. Single activation energies for each well are obtained in the range 15-33 kJ/mole, close to pressure solution of quartz, 24 kJ/mol. Values of m and n are in the range 1 to 0.8, indicating nearly fractal pore-matrix spaces and water-wet interfaces. Results are independent of over- or under-pressure of pore water. This model explains shale compaction quantitatively. Given porosity-depth data and accurate activation energy, E, one can infer paleo-geothermal-gradient and from that organic maturity, thus avoiding unnecessary drilling.

Bobbin Tool Friction Stir Welding (BTFSW) is a variant of FSW process using the special two shoulder tool that forms the top and bottom weld surface. As such, a significant simplification of welding setup is achieved. One of the dominant parameters of BTFSW process is the interference between tool shoulder pinch gap and weld metal thickness. In this research, the influence of interference of the square pin tool with convex shoulders on process temperature, microstructure, tensile, impact and bend performance were studied, and appropriate correlations were devised. The base metal was aluminum-magnesium alloy, with the interference varied in the range of 0.1 to 0.5 mm. The worm defects and irregularities were found in all specimens except in specimen welded with 0.4 mm interference. Optimal interference of 0.4 mm resulted in the highest mechanical properties, which, in terms of tensile strength and reduction of area were similar to the base metal. Furthermore, impact strength was significantly higher, which was attributed to grain refinement effect in the nugget zone.

Semisolid casting can provide excellent castings, but the nature of the pore-forming mechanisms has not been properly clarified. In the current communication, it was suggested that hydrogen precipitated during slurry making might have a decisive role in the formation of both gas and shrinkage porosity. Intensive stirring at the end of the slurry making process may act as a degassing step. Without the intense stirring, structures of primary slurry particles form around the hydrogen pores, strongly affecting pore formation and feeding during the intensification stage.

Heavy metal pollution poses a significant threat to ecosystems and human health worldwide. In response to this pressing issue, bioremediation has emerged as a promising approach for mitigating contamination. This paper adopts a bibliographic method to explore the key techniques and applications of bioremediation. Furthermore, we delve into the most prominent threats to human environmental health and the corresponding remediation methods. Additionally, we discuss the future trajectory of bioremediation research, with a particular focus on the integration of big data and machine learning technologies. These advanced methodologies hold great potential for enhancing the effectiveness and efficiency of environmental remediation efforts in the face of escalating pollution challenges.

With continuous increase in integration of the semiconductor devices, the requirements on size accuracy and surface quality of the etched lead frame are higher. The etchant is a key factor on etching process and etched surface quality, while effects of the difference in etchants on microscopic etched surface morphology of the Cu alloy have not been directly studied. In this study, the aqua regia, acidic FeCl3 and CuCl2 solutions were used as etchants, and the CuCrSn alloy specimens with different microstructure were etched and characterized. The results show that the etching rate in aqua regia is high, and the grain orientation, grain boundary (GB) and dislocation have significant influence on the local etching rate. The preferential etching of some atomic planes forms steps between grains with different orientations, and the preferential etching around the GB and dislocation group forms grooves, resulting in high surface roughness. For etching of the FeCl3 and CuCl2 etchants, the steps and grooves become blurred, and almost invisible on the surface etched by the CuCl2 etchant, thus the surface roughness is much lower. The CuCrSn alloy surface etched by the aqua regia is clean, with little Cr-rich particles, while high density Cr-rich particles are remained on the surfaces etched with the FeCl3 and CuCl2 etchants. For the same kind of etchant, the ion concentration can affect the etching mechanism and etching surface morphology.

In this paper we present magnetoelectric properties of metal/metal-oxide/metal junctions. We use Ti and Fe as metallic layers separated by the porous metal-oxides of iron or titanium formed with the anodization method. This allowed to prepare double junctions with at least one ferromagnetic layer. Here we show magnetoresistance and current-voltage characteristics of the junctions together with their magnetic characteristics. We found positive or negative magnetoresistance depending on junction composition. We discuss also the nature of differential resistance calculated from I-V characteristics. Our findings show that the strongest influence on observed behaviour has a top metallic layer and the interface between this layer and anodized oxide where strong interatomic diffusion is expected.

Pure titanium is limited to be used in biomedical applications due to its lower mechanical strength compared to its alloy counterpart. To enhance its properties and improve medical implants feasibility, advancements in titanium processing technologies are necessary. One such technique is equal channel angular pressing (ECAP) for its severe plastic deformation (SPD). This study aimed to surface modify commercially pure titanium using micro arc oxidation (MAO) technology and mineral solutions containing Ca and P. The composition and shape of the changed surface were characterized using X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The weight % of Ca and P in the coating was determined using Energy Dispersive Spectroscopy (EDS), and the corrosion resistance was evaluated through potentiodynamic measurement. The behavior of human dental pulp cell and periodontal cell behavior was also studied through a biomedical experiment over a period of 1-, 3-, and 7-days using trypsin as the culture medium and ELISA as the observation method. This study showed that the mechanical grain refinement method and surface modification significantly improved the biomechanical properties of commercially pure (CP) Titanium. Although the results showed variations in the absorbance values of cells cultured on different surfaces, this study provides valuable insights into pulp cell behavior and advances the field of biomedical research.

The alcoholic fermentation process with agitation/static, followed by the acetic fermentation submerged in banana was evaluated. Kinetics parameters of alcoholic fermentation for the maximum ethanol/glycerol metabolites in agitated process was 29 and 27 h, and in static 47 and 45 h, respectively. For acetic fermentation, the kinetics parameters were medium time of 39.9 h, acetic acid yield of 53.1% and acetic acid productivity of 0.216 g/Lh. Wines from agitated/static process presented 5.73 and 6.81% (v/v) of alcohol content, respectively. Wine obtained by the static process presented higher concentrations of volatile compounds. The vinegar showed 49.2 g/L of acetic acid and the esters concentrations were higher than in wine. The wine and vinegar minerals were consistent with amount observed in the pulp, with an increase in sulphur concentration after alcoholic fermentation and decrease after acetic fermentation. Products showed chemical and composition of sensory and nutritional interest.

This study provides an in-depth review of the available literature on metal composite material machining, focusing on traditional machining operations such as turning, milling, shaping, drilling, and grinding. The motivation for the study is that this composite type has emerged as a vital material in applications requiring functionality, resilience, cost-effective operation, low consumption of energy and lightweight. Despite its superior characteristics, the manufacturing complexity and poor machinability of metal matrix composites have been the primary barriers to its adoption. Nevertheless, there is a reduction of exceptional efficiency, increase in surface roughness, tool wear and so on in metal matrix composites throughout machining. As a result, this review gives a comprehensive investigation of metal matrix composite machining and effect on process parameters and procedures. Furthermore, this study distinguishes metal matrix composites towards sustainable manufacturing and the metals employed by the researchers, as well as the gaps discovered for future recommendations in metal-based composites.

Cu₆Sn₅ whiskers precipitated in Sn3.0Ag0.5Cu/Cu interconnection in concentrator silicon solar cells solder layer were found and investigated after reflow soldering and during aging. Ag₃Sn fibers can be observed around Cu₆Sn₅ whiskers in the matrix microstructure, which can play an active effect on the reliability of interconnection. Different morphologies of Cu₆Sn₅ whiskers can be observed, and hexagonal rod structure is the main morphology of Cu₆Sn₅ whiskers. A hollow structure can be observed in hexagonal Cu₆Sn₅ whiskers, and a screw dislocation mechanism was used to represent the Cu₆Sn₅ growth. Based on mechanical property testing and finite element simulation, Cu₆Sn₅ whiskers were regarded as having a negative effect on the durability of Sn3.0Ag0.5Cu/Cu interconnection in concentrator silicon solar cells solder layer.

An eight-sided prism sample, obtained from a hot-rolled AZ31 magnesium alloy sheet, was compressed at room temperature along the transverse direction to investigate the influence of local strain on twinning behavior using electron backscatter diffraction (EBSD) measurements. The octagonal surface of the sample was divided into distinct regions based on hardness distribution and metallographic observations. The EBSD maps of different areas show significant variations, suggesting that these areas experienced different local strain conditions. The EBSD measurements provided detailed data from three distinct regions, with the strain state known in two regions and uncertain in the third. The combined analysis of the Schmid factor (SF) and the strain compatibility factor (m') was employed to study twin variant selection. The comparison of twinning behavior in different regions showed that the strain compatibility factor offered a more comprehensive explanation for the observed twinning pattern in the region with local shear strain.

From the theory of relativistic chemical kinetics [M. W. Baig, Int. J. Mod. Phys. B 31, 1750177 (2017)] relativistic thermodynamics and kinetics for electrode processes have been developed to explain time dilation for electrode processes. For a moving observer moving at fractions of the speed of light, cell potential is observed to decrease. This results in the slower oxidation and reduction of ions at the respective electrodes. The newly formulated Lorentz transformation of the electrode and cell potential is explained in terms of generation of spin 2-boson “gravitons” from fusion of spin-1 boson “virtual-photons” mediating electrostatic force of attraction between ions and electrodes. It is postulated that birth of spin 2-boson i.e. gravitons is followed by their eventual escape in any of higher 4+n dimensions. To demonstrate the effectiveness of the present theory, the Daniel cell is considered as a numerical example.

For some persistent pollutants, such as recalcitrant pesticides, the polluted water (urban, agricultural and/or industrial) treated by conventional wastewater treatment plants is in some cases insufficient to achieve the legally required level of purity. This issue is of particular concern in areas where low rainfall does not provide sufficient water resources to meet the needs of agriculture, requiring increased reuse of water from wastewater treatment plants. In this context, Advanced Oxidation Processes (AOPs) hold great promise for the removal of organic pollutants. This study first evaluates the effectiveness of UV/S2O8= compared to heterogeneous photocatalysis using UV/TiO2 processes on the degradation of two commonly used herbicides (terbutylazine and isoproturon) in aqueous solutions using a photoreactor. In addition. the effect of UV wavelength on the degradation efficiency of both herbicides was investigated. Although degradation rate was higher under UV-254/S2O8= nm than under UV-365/S2O8= nm, complete degradation of the herbicides (0.2 mg L-1) was achieved within 30 min under UV-366 nm using a Na2S2O8 dosage of 250 mg L-1 in the absence of inorganic anions. To assess the impact of water matrix, the individual and combined effects of sulphate, bicarbonate and chloride were evaluated. They can react with hydroxyl and sulphate radicals formed during AOPs to form new radicals with a lower redox potential. The results showed negligible effects of sulphate, while the combination of bicarbonate and chloride seemed to be the key for the decrease in herbicide removal efficiency found when working with complex matrices. Finally, the main intermediates detected during the photodegradation process were identified and the likely pathways are proposed and discussed.

To enhance the applicability of dual-phase high-entropy alloys (HEAs) like Fe32Cr33Ni29Al3Ti3, fabricated via selective laser melting (SLM), a focus on improving their mechanical properties is essential. As part of this effort, heat treatment was explored. This study compares the microstructure and mechanical properties of the as-printed sample with those cooled in water after undergoing heat treatment at temperatures ranging from 1000 to 1200 ℃ for 1 hour. Both pre- and post-treatment samples reveal a dual-phase microstructure comprising FCC and BCC phases. Although heat treatment led to a reduction in tensile and yield strength, it significantly increased ductility compared to the as-printed sample. This strength-ductility trade-off is related to changes in grain sizes with ultrafine grains enhancing strength and micron grains optimizing ductility, also the influence of the content of FCC/BCC phases and dislocation density. In particular, the sample heat-treated at 1000 °C for 1 hour and then water-cooled exhibited a better combination of strength and ductility, a yield strength of 790 MPa, and an elongation of 13%. This research offers innovative perspectives on crafting dual-phase HEA of Fe32Cr33Ni29Al3Ti3, allowing for tailorable microstructure and mechanical properties through a synergistic approach involving SLM and heat treatment.

A better understanding of high temperature processes in slags contributes to facilitate knowledge based design of the solidified product. Here, a slag analogue with a nominal composition of 17 wt% LiMnO2 and 83 wt% Ca2SiO4 was synthesized encountering fairly high cooling rates. The Mn species from 1223 K to 1773 K was simulated using a thermodynamic model assuming a homogeneous melt. The micro-composition including the Mn species of the solidified slag was determined experimentally and was used as basis for molecular dynamics (MD) simulation. The MD simulation provides information on structure and viscosity at high temperatures, otherwise difficult to access. These parameters significantly influence oxidation state of redox-active elements and the solidified product. The micro-composition analyzed by electron probe micro analysis (EPMA) and synchrotron based micro-X-ray fluorescence (micro-XRF) showed that Mn-rich and Ca-Si-rich phases are separated. While the Mn-O phases did not contain noticeable Ca, the Ca2SiO4 phase had incorporated 0.6 wt% of Mn. The slag solidified into round shaped and droplet shaped grains of a Li-Mn-oxide, some Mn3O4 and Ca2SiO4. The powder X-ray diffraction (PXRD) confirmed the formation of larnite, the identity of the Li-Mn-oxide however remained inconclusive. The Mn oxidation state (OS) was identified using synchrotron based micro-X-ray absorption near edge spectroscopy (micro-XANES). The Mn-O grains, matched well with Li-Mn-oxides and a Mn OS: +3 e.g. LiMn3+O2. Small areas matching Hausmannite (Mn2+Mn23+O4) were also identified. The OS of Mn in the silicate phase could not be identified. For comparison a slowly cooled slag analogue with similar composition however higher Si content, was also subjected to micro-XANES. The slowly cooled slag formed long Mn-rich needles in a matrix of large calcium silicate crystals. The Mn-rich crystals matched well with the XANES spectrum of a Mn3+ Li-oxide like LiMn3+O2. At the rim of the needles the Mn-spectra matched well the Hausmannite (Mn2+Mn23+O4) reference. In the silicate phases Mn had a OS: +2, unambiguously. The melt structure at different temperatures of two compositions i.e. LiMn3+O2 and Ca2SiO4 was simulated using molecular dynamics (MD). They serve as model compositions assuming a heterogeneous melt. The results show significant different degrees of polymerization and viscosity. Information from MD simulations can support the identification of potentially different oxygen permeability and with that prediction of oxidation states. The bulk composition was identified by inductively coupled plasma optical emission spectrometry (ICP-OES), bulk structure by PXRD and bulk species by lab-XANES. The synchrotron micro analysis including micro-XRD were performed at the microfocus beamline I18 at the Diamond Light Source. Pure reference compounds were prepared and characterized with the same multi-modal approach.

This paper presents a review on numerical and experimental methods to predict fracture of ad-vanced high strength steels (AHSS). AHSS are widely processed through sheet metal forming processes. Although being an excellent choice when lightweight, high strength and ductility are critical factors, their multi-phase microstructure accentuates forming challenges. To accurately model forming behavior, necking based failure criteria as well as direct fracture models require improvements. As a necking based failure model, the conventional forming limit diagram/curve (FLD/FLC) presents limitations such as in estimating direct fracture (surface cracks, edge cracks, shear cracks), as well as deformation histories under nonlinear strain paths. Thus, significant re-search efforts are being made towards the needs of advanced fracture constitutive models capa-ble of predicting fracture scenarios without necking, more frequently observed in the realm of AHSS. Scientific community research is divided into several directions aiming at improving the forming and fracture behavior accuracy of parts subjected to sheet metal forming operations. In this review paper, a comprehensive overview on ductile fracture modeling is presented. Firstly, the FLD/FLC limitations modeling fracture behavior in sheet metal forming operations are stud-ied. Followed by the recent trends in constitutive material modeling. Afterwards, material char-acterization methods advancements to cover a broad range of stress states are comprised. Final-ly, damage and fracture models predicting failure in AHSS are investigated. This review paper supplies relevant information on the current issues the sheet metal forming community is chal-lenged with due to the trend towards AHSS employment in the automotive industry.

The rational design of magnetic carbon composites, encompassing both composition and microstructure, holds significant potential for achieving exceptional electromagnetic wave absorbing materials (EAMs). In this study, FeCo@CM composites was efficiently fabricated through an advanced microwave plasma assisted reduction chemical vapor deposition (MPARCVD) technique, offering high efficiency, low cost, and energy-saving benefits. By depositing graphitized carbon microspheres, the dielectric properties were significantly enhanced, resulting in improved electromagnetic wave absorption performances through optimized impedance matching and a synergistic effect with magnetic loss. A systematic investigation revealed that the laminar-stacked structure of FeCo exhibited superior properties compared to its spherical counterpart, supplying a higher number of exposed edges and enhanced catalytic activity, which facilitated the deposition of uniform and low-defect graphitized carbon microspheres. Consequently, the dielectric loss performance of the FeCo@CM composites was dramatically improved due to increased electrical conductivity and the formation of abundant heterogeneous interfaces. At a 40 wt% filling amount and a frequency of 7.84 GHz, the FeCo@CM composites achieved a minimum reflection loss value of -58.2 dB with an effective absorption bandwidth (fE) of 5.13 GHz. This study presents an effective strategy for developing high-performance EAMs.

Directed energy deposition (DED) parameters were determined for near-β alloy Ti-55511 by employing statistical design of experiments (DOE) methods. Parameters resulting in fully dense freeform deposits were identified using two sequential DOEs. Single laser tracks were printed with several laser power, traverse rate, and powder feed rate settings in an initial DOE to identify promising build parameters. Capture efficiency and effective deposition rate were used to characterize and rank the single track deposits. The best parameters were then used to print solid cube with various X-Y and Z-overlaps (different hatch spacing, HS, and layer thickness, ZS) in a second DOE. Suitable deposition parameters were selected based on cube density and microstructure and were used to fabricate larger tensile samples for mechanical testing. Multiple parameter sets were found to provide dense Ti-55511 deposits with acceptable mechanical properties and parametric models showed statistical significance.

This letter presents a dual-frequency terahertz amplitude modulator based on a cross-shaped structure and U-shaped metal patches. Its structural unit is a typical metal-substrate structure. The top metal consists of a cross-shaped structure and U-shaped metal patches, and the bottom substrate layer is made of quartz. Amplitude modulation is achieved by adjusting the temperature of the vanadium dioxide (VO2) patches. The modulation depth can be approximately 75%. The mechanism of the resonance frequency is explained by the equivalent circuit model. The proposed structure shows good amplitude modulation capability at different incidence and azimuth angles by changing the location of the VO2 patches. The dual-frequency terahertz amplitude modulator can be used in terahertz communication, imaging, etc.

Quasi-solid composited electrolytes were produced by LiFSI initiated polymerized poly-(Dioxolane) (PDOL) with garnet-LLZO (Li7La2Zr3O12) nanofibers and used in lithium-metal batteries. Linear sweep voltammetry shows that the initial oxidation voltage of 4.6 V for Gel-10% (G10, 10% wt. LLZO in PDOL) vs Li/Li+. EIS test of stainless steel// stainless steel symmetric cells for Gel-1% (G1), Gel-5% (G5) and Gel-10% (G10) show ion conductivity (5*10-5 S/cm). Li/G10/Li symmetric cells have stable stripping-plating cycling performance over 1300 hours continuously with the current density of 0.1 mA/cm2 at 25 oC, indicating a good interface contact and stable lithium-ion transport pathway through the composite electrolytes. LFP/G10/Li batteries have stable charge-discharge plateau, low polarization voltage of 0.07-volt, energy efficiency of 95% and coulombic efficiency of ~99% at current density of 26.3 mA/g at 25 oC for over 100 cycles.

Despite the successful introduction of oral cholera vaccines, Zambia continues to experience multiple, sporadic, and protracted cholera outbreaks in various parts of the country. While vaccines have been useful in staying the cholera outbreaks, the ideal window for re-vaccinating individual’s resident in cholera hotspot areas remains unclear. Using a prospective cohort study design, 225 individuals were enrolled, re-vaccinated with two doses of Shanchol™ regardless of previous vaccination and followed-up for 90 days. Bloods collected at baseline before re-vaccination, at day 14 prior to second dosing and subsequently on days 28, 60, and 90. Vibriocidal assay was performed on samples collected at all five time points. Our results showed that anti-LPS and vibriocidal antibody titers increased at day 14 after re-vaccination and decreased gradually at 28, 60 and 90 across all the groups. Seroconversion rates were generally comparable in all treatment arms. We therefore conclude that vibriocidal antibody titers generated in response to re-vaccination still wane quickly irrespective of previous vaccination status. However, despite the observed decline, the levels of vibriocidal antibodies remained elevated over baseline values across all groups, an important aspect for Zambia where there is no empirical evidence as to the ideal time for re-vaccination.

Today, legislative framework addresses the metal alloys’ corrosion issues, demanding the re-striction of use of the probable carcinogenic, mutagenic and toxic for reproduction at humans (CMG) metals, like nickel, cobalt and chromium, and demand to develop new biomaterials. Therefore, the aim of this research is to evaluate and compare ion release of standard dental alloys and their hypoallergenic equivalents. Six types of orthodontic alloy wires (nickel-titanium (NiTi), coated NiTi, stainless steel (SS), Ni-free SS, cobalt-chromium (CoCr), and titanium-molybdenum (TMA) were immersed into artificial saliva of pH 5.5 and 6.6. Release of metal ions was measured by inductively coupled plasma-mass-spectrometry (ICP-MS) after 3, 7, 14 and 28 days. Data analyses were done using analysis of variance, results with P

Hydrogen storage in general is an indispensable prerequisite for the introduction of a hydrogen energy based infrastructure. In this respect, high-pressure metal hydride (MH) tank systems appear to be one of the most promising hydrogen storage techniques for automotive applications using proton exchange membrane (PEM) fuel cells. These systems bear the potential of achieving a beneficial compromise of comparably large volumetric storage density, a wide working temperature range, comparably low liberation of heat, and increased safety. The debatable term unstable metal hydride stands in the literature short for metal hydrides with high dissociation pressure at comparably low temperature. Such compounds may help to improve the merit of high-pressure MH tank systems. Consequently, in the last few years, some materials for possible on-board applications in such tank systems have been developed. This review summarizes the state-of-the-art developments of these metal hydrides, mainly including intermetallic compounds and complex hydrides and gives some guidelines for future developments. Since typical laboratory hydrogen uptake measurements are limited to 200 bar, a possible threshold for defining unstable hydrides could be a value of their equilibrium pressure of peq > 200 bar for T < 100°C. However, these values would mark a technological future target and most current materials, and those reported in this review, do not fulfill these requirements and need to be seen as current stages of development towards the intended target. For each of the aforementioned categories in the review, special care was taken not only to covers the pioneering and classical research, but also to portrait the current status and latest advances. For intermetallic compounds, key aspects focus on the influence of partial substitution on absorption/desorption plateau pressure, hydrogen storage capacity and hysteresis properties. For complex hydrides, the preparation procedures, thermodynamics and theoretical calculation are presented. Besides, challenges, perspectives, and development tendency of this field are also discussed.

Keywords: friction stir processing; additive manufacturing; wire; titanium alloy; material transfer; microstructure; microhardness

This review describes major advances in the use of functionalized molecular metal oxides (polyoxometalates, POMs) as water oxidation catalysts under electrochemical conditions. The fundamentals of POM-based water oxidation are described together with a brief overview of general approaches to designing POM water oxidation catalysts. Next, the use of POMs for homogeneous, solution-phase water oxidation is described together with a summary of theoretical studies shedding light on the POM-WOC mechanism. This is followed by a discussion of heterogenization of POMs on electrically conductive substrates for technologically more relevant application studies. Stability of POM water oxidation catalysts are discussed on selected examples where detailed data is already available. The review finishes with an outlook on future perspective and emerging themes in electrocatalytic polyoxometalate-based water oxidation research.

Surface initiated atom transfer radical polymerization (SI-ATRP) is one of the most versatile technique to modify the surface properties of material. Recent developed metal free SI-ATRP makes such technique more widely applicable. Herein photo-induced metal-free SI-ATRP of methacrylates, such as methyl methacrylate, N-isopropanyl acrylamide, and N,N- dimethylaminoethyl methacrylate, on the surface of SBA-15 was reported to fabricate organic-inorganic hybrid materials. SBA-15 based polymeric composite with adjustable graft ratio was obtained. The structure evolution during the SI-ATRP modification of SBA-15 was monitored and verified by FT-IR, XPS, TGA, BET, and TEM. The obtained polymeric composite showed enhanced adsorption ability for the model compound toluene in aqueous. This procedure provides a low cost, ready availability, and facile modification way to synthesize the polymeric composites without the contamination of metal.

In this work, two plasmonic structures with two different periodic nanostructures (nanodisk and nanostrip arrays) separated from the gold layer by an ultrathin dielectric Al2O3 layer are proposed, and their optical properties are simulated as 3-dimensional models using COMSOL Multiphysics software tool. The optical responses, such as the amplification of the electric field and the scattering, absorption and extinction cross sections of the two structures, are investigated and compared. The results show that both structures show strong field enhancement in their gap layer, and the structure with the periodic array of metal nanodisks shows stronger field enhancement and larger absorption, extinction, and scattering cross sections in its dipole resonance wavelength, which is defined as a bright plasmonic mode. In addition, some weaker resonant modes are observed for both structures and the reason for their generation is dis-cussed. The analysis of different possible modes in such structures is crucial for their application in various fields.

Magnetogenetics emerges as a transformative approach for modulating cellular signaling pathways through the strategic application of magnetic fields and nanoparticles. This technique leverages the unique properties of magnetic nanoparticles (MNPs) to induce mechanical or thermal stimuli within cells, facilitating the activation of mechano- and thermosensitive proteins without the need for traditional ligand-receptor interactions. Unlike traditional modalities that often require invasive interventions and lack precision in targeting specific cellular functions, magnetogenetics offers a non-invasive alternative with the capacity for deep tissue penetration and the potential for targeting a broad spectrum of cellular processes. This review underscores magnetogenetics' broad applicability, from steering stem cell differentiation to manipulating neuronal activity and immune responses, highlighting its potential in regenerative medicine, neuroscience, and cancer therapy. Furthermore, the review explores the challenges and future directions of magnetogenetics, including the development of genetically programmed magnetic nanoparticles and the integration of magnetic field-sensitive cells for in vivo applications. Magnetogenetics stands at the forefront of cellular manipulation technologies, offering novel insights into cellular signaling and opening new avenues for therapeutic interventions.

Colombia is the world's leading producer of mild washed arabica coffee and produces 12.6 million bags of green coffee, but at the same time 784,000 tons of waste biomass are dumped in open fields, of which only 5% is recovered or used. The objective of this project was to evaluate the production of platform chemicals from these coffee wastes. To achieve this, biomass characterization was carried out using proximate analysis, ultimate analysis and structural analysis. Hydrothermal valorization was carried out at a temperature range of 120-180 °C (LHW) and 180-260 °C (HTC) for one hour, the platform chemicals obtained were quantified by HPLC-IR, monitored by pH and conductivity, and the solid fraction was characterized by monitoring the functional groups in IR spectroscopy, and elemental analysis. Hydrolysis processes were obtained from 150 °C, production of platform chemicals from 180 °C and maximum concentration at 180 °C-4h, over 200 °C degradation of the products in the liquid fraction starts to take place. Homogeneous basic and acid catalysts were used to improve the yields of the reaction. The kinetics of the hydrolysis of lignocellulosic structures to sugars were also analyzed and described, and reaction orders of 1 (LHW), 3 (HTC) and their respective reaction rate equations were reported.

This study aimed to evaluate the impact of Candida albicans on subgingival biofilm formation on dental implant surfaces. Scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM) were used to compare biofilm structure and microbial biomass in the presence and absence of the fungus after periods of 24, 48, and 72 h. Quantitative polymerase chain reaction (qPCR) was used to quantify the number of viable and total micro-organisms for each of the biofilm-forming strains. A general linear model was applied to compare CLSM and qPCR results between control and test conditions. The biofilm developed with C. albicans at 72 h had a higher bacterial biomass, with a significantly higher cell viability (p &lt; 0.05). After both 48 and 72 h of incubation, in the presence of C. albicans, there was a significant increase in counts of Fusobacterium nucleatum and Porphyromonas gingivalis and in the cell viability of Streptococcus oralis, Aggregatibacter actinomycetemcomitans, F. nucleatum, and P. gingivalis. Using a dynamic in vitro multispecies biofilm model, C. albicans exacerbated the development of the biofilm grown on dental implant surfaces, significantly increasing the number and cell viability of periodontal bacteria.

Objective: This study aimed to assess the impact of artificial intelligence (AI)-driven noise reduction algorithms on metal artifacts and image quality parameters in cone-beam computed tomography (CBCT) images of the oral cavity. Materials and Methods: This retrospective study included 70 patients, 61 of whom were analyzed after excluding those with severe motion artifacts. CBCT scans, performed using a Hyperion X9 PRO 13 × 10 CBCT machine, included images with dental implants, amalgam fillings, orthodontic appliances, root canal fillings, and crowns. Images were processed with ClariCT. AI deep learning model (DLM) for noise reduction. Objective image quality was assessed using metrics such as the differentiation between voxel values (ΔVVs), the artifact index (AIx), and the contrast-to-noise ratio (CNR). Subjective assessments were performed by two experienced readers, who rated overall image quality and artifact intensity on predefined scales. Results: Compared with native images, DLM reconstructions significantly reduced the AIx and increased the CNR (p<0.001), indicating improved image clarity and artifact reduction. Subjective assessments also favored DLM images, with higher ratings for overall image quality and lower artifact intensity (p<0.001). However, the ΔVV values were similar between the native and DLM images, indicating that while the DLM reduced noise, it maintained the overall density distribution. Orthodontic appliances produced the most pronounced artifacts, while implants generated the least. Conclusion: AI-based noise reduction using ClariCT. AI significantly enhances CBCT image quality by reducing noise and metal artifacts, thereby improving diagnostic accuracy and treatment planning. Further research with larger, multicenter cohorts is recommended to validate these findings.

Green synthesis offers a superior alternative to traditional methods for producing metal and metal oxide nanoparticles. This approach is not only benign and safe but also cost-effective, scalable, and straightforward, operating under ambient conditions. Notable metals and metal oxide nanoparticles, such as manganese oxides, iron oxides, silver, and gold, have been produced using various bio-reductants derived from plant extracts. These biological agents not only expedite the reduction process but also stabilize the nanoparticles, serving dual roles as reducing and capping agents. This review presents the green synthesis of nanoparticles (NPs) obtained from biogenic wastes and plant extracts. The green-synthesized nanostructured MnO2 are evaluated as a potential photocatalyst for water treatment and as an electrode material in lithium-ion batteries and supercapacitors. The green-derived iron oxide nanoparticles are examined as promising antioxidant, anti-inflammatory, and anti-diabetic agents. Additionally, this review discusses the green synthesis of precious metal nanoparticles, specifically silver (Ag NPs) and gold (Au NPs), highlighting their potential medical applications in areas like antiviral treatments and cancer therapy.

In the context of the COVID-19 epidemic, and on the basis of the Theory of Dynamical Systems, we propose a simple model for the expansion of contagious diseases, with a particular focus on viral respiratory tracts. The infection develops through contacts between contagious and exposed people, with a rate proportional to contact duration and turnover, inversely proportional to the efficiency of protection measures, and balanced by the average immunological response. The obvious initial exponential increase is readily hindered by the size reduction of the exposed population. The system converges towards a stable attractor whose value is expressed in terms of the ratio C/D of contamination vs decay factors. Decreasing this ratio below a critical value leads to a tipping point beyond which the epidemic is over. By contrast, significant values of C/D may bring the system through a bifurcating hierarchy of stable cycles up to a chaotic behaviour.

This work investigated the isothermal holding time dependence of the densification, microstructure, weight loss and tensile properties of Fe-Mn-Si powder compacts. Elemental Fe, Mn and Si powder mixtures with a nominal composition of Fe-28Mn-3Si (in weight percent) were ball milled for 5h and subsequently pressed under a uniaxial pressure of 400 MPa. The compacted Fe-Mn-Si powder mixtures were sintered at 1200 ℃ for 0, 1, 2 and 3 h, respectively. In general, the density, weight loss and tensile properties increased with the increase of isothermal holding time. A significant increase in density, weight loss and tensile properties occurred in the compacts isothermally holding for 1 h, as compared to those with no isothermal holding. However, further extension of isothermal holding time (2 and 3 h) only played a limited role in promoting the density and tensile properties. The weight loss of the sintered compacts was mianly caused by the sublimation of Mn in Mn depletion region on the surface layer of the sintered Fe-Mn-Si compacts. The length of the Mn depletion region increased as isothermal holding time increased. A single α-Fe phase was detected on the surface of all the sintered compacts, and the locations beyond the Mn depletion region were comprised of a dual dominant γ-austenite and minor ε-martensite.

SiC is a material with excellent mechanical and thermal properties, but with a high production cost. Obtaining SiC by reactive infiltration is an attractive method and at a much lower cost than the traditional sintering process. However, the reactive infiltration process presents a serious problem, which is the high residual silicon content, which decreases its range of application. The replacement of silicon with silicides is a widely used alternative. The present investigation shows the good mechanical properties of the SiC/IrSi₃ composite material obtained by reactive infiltration of SiC/C preforms with Ir-Si alloys. The thermomechanical analysis shows a high compatibility of silicide with SiC. The presence of the silicide shows a substantial improvement against the oxidation of the SiC/Si composites.

Peptides, both natural and synthetic, are well suited for a wide range of purposes and offer versa-tile applications in different fields such as biocatalysts, injectable hydrogels, tumor treatment, and drug delivery. The rising prominence of therapeutic peptides encompasses anticancer, antiviral, antimicrobial, and anti-neurodegenerative properties. The metals Na, K, Mg, Ca, Fe, Mn, Co, Cu, Zn, and Mo are ten of the twenty elements that are considered essential for life. Crucial for under-standing the biological role of metals is the exploration of metal-bound proteins and peptides. Aside from essential metals, there are other, non-essential metals that also interact biologically, exhibiting either therapeutic or toxic effects. Irregularities in metal binding contribute to diseases like Alzheimer’s, neurodegenerative disorders, Wilson's, and Menkes disease. Certain metal com-plexes have potential applications as radiopharmaceuticals. The examination of these complexes was done by preforming UV-Vis, IR, EPR, NMR spectroscopy, and X-ray analysis.

This investigation mainly focused on the microstructural analysis of Al based hybrid metal matrix composites. Aluminium as base metal and reinforced with 2% B4 C, ZrO2 (2%,4%,6%), SiC (4%,8%,12%). Specimens were manufactured by using conventional stir casting technique. Hybrid metal matrix composites were examined by using Scanning electron microscope. This research explained XRD, EDS and Fractography analysis. This investigation shows the reinforced material has given better results in all aspects than pure Al6061 alloy and homogeneous dispersion of particles inside the matrix. Porosity, delamination, cracks, particle distributions were observed through microstructural analysis. Additionally determined the crystal size of pure Aluminium 6061 alloy and hybrid composites.

In this study, an extensive data set was based on existing literature records in order to enable the suitability of several predictive models, from Multiple Linear Regression (MLR) to Neural Networks (NN). The main objective was to, through regression analyses, generate model computations to correlate tensile properties (UTS- Ultimate Tensile Strength, YTS – Yield Tensile Strength and EF – Elongation-to-Fracture) to a given alloy composition and microstructural spacing. This investigation led to positive results, as the highest accuracies of the trained modules (in 80% of the database) were found to be above ~82% (UTS and EF) and a maximum of ~98% (YTS), when analyzing the results to a test data set. Later, these models were used to define trends for possible next solder alloy commercial compositions. Overall, using the standard model’s setup, the Random Forest and Decision Tree models showed the highest accuracy results, with 0.958 for YTS as opposed to 0.907 for MLR. Moreover, Multilayer Perceptron (MLP)-optimized models yielded the best results for each variable, with the highest increases in accuracy associated with the YTS and EF. The present contribution might imply an important milestone towards alloy design research based on data science guidelines to unlock the full potential of former experiments and their extensive set of results.

In this paper, 6063 aluminum alloy for common building profiles is used as the research object. By adding a new Al-Ti-C-La composite alloy, the effect of 6063 aluminum alloy on the microstructure and properties of 6063 aluminum alloy is studied. The results show that Al-Ti-C-La composite alloy has obvious effect on grain refinement of 6063 aluminum alloy. With the addition of Al-Ti-C-La composite alloy, the grain size decreased significantly. When the addition amount of Al-Ti-C-La composite alloy is 1%, the grain size is reduced from 482 μm to 121 μm. Rare earth La is mainly distributed near the Mg2Si phase and β-AlFeSi, and complex compounds such as AlFeSiMgLa are formed. After aging for 270 days on the basis of T6 heat treatment, the tensile strength and elongation of 6063 aluminum alloy augmented with the addition of Al-Ti-C-La composite alloy, and the Vickers hardness gradually diminished. When the addition amount of Al-Ti-C-La composite alloy is 1%, the tensile strength, elongation and Vickers hardness of 6063 aluminum alloy reach 177.2 MPa, 17.8% and 60.9 HV, respectively, and the tensile strength is increased by 16.3%. The elongation is increased by 50.8%, the Vickers hardness is reduced by 15.4%, and the fracture of the alloy is mainly ductile fracture.

To fulfil a need of limitation automotive emissions the reduction of vehicle weight is widely recommended and achieved in many ways, both by the construction of individual elements of the vehicle, and by the selection of light materials including Al alloys. Connecting these elements with each other and with elements made of iron alloys can be realized, inter alia, by welding or stir welding. However, the quality of the welds obtained varies widely and depends on many design, operational and environmental factors. The present study focused on a review of various welding technics used to joint both similar and dissimilar Al alloys utilized in automotive industry, the effect of various process parameters on welds quality, and phenomena appeared in such welds..

Micro satellites must survive severe mechanical conditions during their launch phase. Therefore, structural design requirements are imposed on the micro satellites. These requirements are the strength requirement and the stiffness requirement. Usually, the structural design of a micro satellite is performed using the internal stress analysis and the natural frequency analysis, which are based on a Finite Element Method (FEM). The validity of this structural design is evaluated through vibration tests. In an early stage of development, which has a FEM model of a satellite in the process of creation, presumption of the natural frequency of a satellite may be difficult. In this study, a simple method for determining the longitudinal and lateral minimum natural frequencies of the micro satellites during the ascent phase was clarified. The structure of the micro satellites used in this research is made of aluminum alloy, and they have a monocoque structure. The Young's modulus and moment of inertia of area used to calculate the minimum natural frequencies were determined using the area ratio of the monocoque structure to the entire satellite. When this method is used, the estimated minimum natural frequencies of the longitudinal direction and the lateral direction are in agreement with the measured values acquired by the vibration tests. In order to shorten the process of micro satellites development, this paper describes a practical estimation method of the minimum natural frequency for micro satellites.

Direct Energy Deposition (DED) is a versatile and efficient method in metal additive manufacturing. However, humping, caused by abnormal dynamics in the melt pool (MP), poses a significant threat to the geometric integrity of manufactured products. Current state-of-the-art (SOTA) methods primarily detect humping by analyzing late-stage spatial abnormalities, such as MP detachment. This approach is fundamentally reactive, leading to a tendency to miss early humping spatiotemporal dynamics, like cyclic elongation of the MP. This study introduces a novel, proactive indicator named VIMPS (Variability of Instantaneous MP Solidification-Front Speed), a physics-based tool designed to quantify early abnormal fluctuations in MP solidification speed. The experiments demonstrate VIMPS correlation with humping-induced geometric inaccuracies. By capturing early spatiotemporal dynamics of the MP, VIMPS reduces detection latency by 30 seconds compared to existing SOTAs that focus solely on spatial abnormalities. This significant improvement transforms detection from reactive to proactive, providing the time needed for corrective actions to enhance the overall productivity and quality of the DED process.

Asphaltene precipitation and deposition pose significant operational challenges in both reservoirs and surface facilities by inducing formation damage. To understand the kinetics involved in asphaltene particle nucleation, growth, and aggregation, this study employed confocal microscopy and centrifuge-based methods under a unified set of experimental parameters. The acquired time-resolved particle size images were analyzed using MIPAR image processing software, while asphaltene mass yield was quantitatively evaluated through centrifugation. Experimental conditions were varied to study the effects of heptane concentration, asphaltene concentration, and shear rate. Notably, this investigation introduces, for the first time, the parameter of particle count as an additional variable influencing asphaltene mass production. This study aims to discern how particle count correlates with asphaltene mass yield over time. Results indicate that the minimum mean particle diameter was observed to be 2 microns, which progressively grew up to 80 microns. The mean particle diameter exhibited a positive correlation with both asphaltene concentration and shear rate, whereas an inverse correlation was seen with heptane concentration. Furthermore, the asphaltene mass yield was found to increase with greater asphaltene and heptane concentrations, as well as with higher shear rates. The relationship between mean particle diameter and mass yield was found to be nonlinear. In the early stages, a higher prevalence of small particles contributed to a greater total particle count, while at later stages, particle aggregation led to the formation of larger particles that influenced the overall asphaltene mass. The insights gained from understanding the relationship between particle diameter, count, and mass yield are crucial for advancing the fundamental science of asphaltene precipitation and deposition. These findings may also guide future research that relies solely on particle counts for assessing asphaltene deposition.

In this study, 12 organic waste materials were subjected to TG/DTG thermogravimetric analysis and DSC calorimetric analysis. These analyses provided basic information about thermochemical transformations and degradation rates during organic waste pyrolysis. Waste materials were chosen to cover the most abundant waste that can be found in the municipal solid waste stream. Based on TG results, kinetic parameters according to Coats–Redfern method were determined. The pyrolysis activation energy was the highest for cotton 134.5 kJ∙(mol∙K)-1 and the lowest for leather 25.2 kJ∙(mol∙K)-1. The DSC analysis showed number of transformations occurred during pyrolysis for each material. For each transformation, normalized energy required for transformation, or released during transformation were determined and then summarized to present energy balance. The study found that only for three waste materials: PET (-220.1 J⸱g-1), leather (-66.9 J⸱g-1), and chicken meat (-130.3 J⸱g-1) energy balance was negative, while the highest positive balance value was found for potato peelings (367.8 J⸱g-1). The obtained results may be applied for the modelling of energy and mass balance of municipal solid waste pyrolysis.

The reaction kinetics of burnt lime (CaO) in contact with sea water has been elucidated and compared to its behaviour in fresh water. In the first minutes of contact between burnt lime and water, it "slaked" as CaO reacted with water to yield calcium hydroxide (Ca(OH)2). Subsequently, calcium hydroxide reacted with magnesium, sulphate and carbonate from the sea water to yield magnesium hydroxide (Mg(OH)2), calcium sulphate dihydrate (gypsum, CaSO4·2H2O) and calcium carbonate (CaCO3), respectively. In a closed system of 1% CaO in natural sea water (where the supply of sulphate, magnesium and carbonate is limited), more than 90% reacted within the first 5 hours. It is foreseen that in an open system, like a marine fjord, it will react even faster. The pH 8 of sea water close to the CaO particle surface will immediately increase to a theoretical value of about 12.5 but will, in an open system with large excess of sea water, rapidly fall back to pH 10.5 being equilibrium pH of magnesium hydroxide. This is further reduced to < 9 due to the common ion effect of dissolved magnesium in sea water and then be diluted to the sea water background pH, about 8. Field test dosing CaO particles to sea water showed that the pH of water between the particles stayed around 8.