Search Results (227)

In vitro alternative therapy of human epidermoid squamous carcinoma (A431) by superparamagnetic hyperthermia (SPMHT) using Fe₃O₄ (magnetite) superparamagnetic nanoparticles (SPIONs) with an average diameter of 15.8 nm, bioconjugated with hydroxypropyl gamma-cyclodextrins (HP-γ-CDs) by means of polyacrylic acid (PAA) biopolymer, is presented in this paper. The therapy was carried out at a temperature of 43 °C for 30 min using the concentrations of Fe₃O₄ ferrimagnetic nanoparticles from nanobioconjugates of 1, 5, and 10 mg/mL nanoparticles in cell suspension, which were previously found by us to be non-toxic for healthy cells (cell viabilities close to 100%), according to ISO standards (cell viability must be greater than 70%). The temperature for the in vitro therapy was obtained by the safe application (without exceeding the biological limit and cellular damage) of an alternating magnetic field with a frequency of 312.4 kHz and amplitudes of 168, 208, and 370 G, depending on the concentration of the magnetic nanoparticles. The optimal concentration of magnetic nanoparticles in suspension was found experimentally. The results obtained after the treatment show its high effectiveness in destroying the A431 tumor cells, up to 83%, with the possibility of increasing even more, which demonstrates the viability of the SPMHT method with Fe₃O₄-PAA–(HP-γ-CDs) nanobioconjugates for human squamous cancer therapy. Full article

The detection of magnetic nanoparticles in a liquid medium and the quantification of their concentration have the potential to improve the efficiency of several relevant applications in different fields, including medicine, environmental remediation, and mechanical engineering. To this end, sensors based on the magneto-impedance effect have attracted much attention due to their high sensitivity to the stray magnetic field generated by magnetic nanoparticles, their simple fabrication process, and their relatively low cost. To improve the sensitivity of these sensors, a multidisciplinary approach is required to study a wide range of soft magnetic materials as sensing elements and to customize the magnetic properties of nanoparticles. The combination of magneto-impedance sensors with ad hoc microfluidic systems favors the design of integrated portable devices with high specificity towards magnetic ferrofluids, allowing the use of very small sample volumes and making measurements faster and more reliable. In this work, a magneto-impedance sensor based on an amorphous Fe_73.5Nb₃Cu₁Si_13.5B₉ wire as the sensing element is integrated into a customized millifluidic chip. The sensor detects the presence of magnetic nanoparticles in the ferrofluid and distinguishes the different stray fields generated by single-domain superparamagnetic iron oxide nanoparticles or magnetically blocked Co-ferrite nanoparticles. Full article

The aim of this study is the fabrication of unprecedented neuroelectrodes, replete with exceptional biological and electrical attributes. Commencing with the synthesis of polyethylene glycol and polyethyleneimine-modified iron oxide nanoparticles, the grafting of Dimyristoyl phosphatidylcholine was embarked upon to generate DMPC-SPION nanoparticles. Subsequently, the deposition of DMPC-SPIONs onto a nickel–chromium alloy electrode facilitated the inception of an innovative neuroelectrode–DMPC-SPION. A meticulous characterization of DMPC-SPIONs ensued, encompassing zeta potential, infrared spectroscopy, X-ray photoelectron spectroscopy, and X-ray diffraction analyses. Evaluations pertaining to hemolysis and cytotoxicity were conducted to ascertain the biocompatibility and biosafety of DMPC-SPIONs. Ultimately, a comprehensive assessment of the biocompatibility, electrochemical properties, and electrophysiological signal acquisition capabilities of DMPC-SPION neuroelectrodes was undertaken. These findings conclusively affirm the exemplary biocompatibility, electrochemical capabilities, and outstanding capability in recording electrical signals of DMPC-SPION neuroelectrodes, with an astounding 91.4% augmentation in electrode charge and a noteworthy 13% decline in impedance, with peak potentials reaching as high as 171 μV and an impressive signal-to-noise ratio of 15.92. Intriguingly, the novel DMPC-SPION neuroelectrodes herald an innovative pathway towards injury repair as well as the diagnosis and treatment of neurological disorders. Full article

This study aimed to develop multifunctional nanoplatforms for both cancer imaging and therapy using superparamagnetic iron oxide nanoparticles (SPIONs). Two distinct synthetic methods, reduction–precipitation (M_R/P) and co-precipitation at controlled pH (M_pH), were explored, including the assessment of the coating’s influence, namely dextran and gold, on their magnetic properties. These SPIONs were further functionalized with gadolinium to act as dual T1/T2 contrast agents for magnetic resonance imaging (MRI). Parameters such as size, stability, morphology, and magnetic behavior were evaluated by a detailed characterization analysis. To assess their efficacy in imaging and therapy, relaxivity and hyperthermia experiments were performed, respectively. The results revealed that both synthetic methods lead to SPIONs with similar average size, 9 nm. Mössbauer spectroscopy indicated that samples obtained from M_R/P consist of approximately 11–13% of Fe present in magnetite, while samples obtained from M_pH have higher contents of 33–45%. Despite coating and functionalization, all samples exhibited superparamagnetic behavior at room temperature. Hyperthermia experiments showed increased SAR values with higher magnetic field intensity and frequency. Moreover, the relaxivity studies suggested potential dual T1/T2 contrast agent capabilities for the coated SP_pH-Dx-Au-Gd sample, thus demonstrating its potential in cancer diagnosis. Full article

Superparamagnetic iron oxide nanoparticles (SPION) have attracted great attention not only for therapeutic applications but also as an alternative magnetic resonance imaging (MRI) contrast agent that helps visualize liver tumors during MRI-guided stereotactic body radiotherapy (SBRT). SPION can provide functional imaging of liver parenchyma based upon its uptake by the hepatic resident macrophages or Kupffer cells with a relative enhancement of malignant tumors that lack Kupffer cells. However, the radiomodulating properties of SPION on liver macrophages are not known. Utilizing human monocytic THP-1 undifferentiated and differentiated cells, we characterized the effect of ferumoxytol (Feraheme^®), a carbohydrate-coated ultrasmall SPION agent at clinically relevant concentration and therapeutically relevant doses of gamma radiation on cultured cells in vitro. We showed that ferumoxytol affected both monocytes and macrophages, increased the resistance of monocytes to radiation-induced cell death and inhibition of cell activity, and supported the anti-inflammatory phenotype of human macrophages under radiation. Its effect on human cells depended on the duration of SPION uptake and was radiation dose-dependent. The results of this pilot study support a strong mechanism-based optimization of SPION-enhanced MRI-guided liver SBRT for primary and metastatic liver tumors, especially in patients with liver cirrhosis awaiting a liver transplant. Full article

Nanoparticles composed of inorganic boron-containing compounds represent a promising candidate as ¹⁰B carriers for BNCT. This study focuses on the synthesis, characterization, and assessment of the biological activity of composite nanomaterials based on boron carbide (B₄C). Boron carbide is a compelling alternative to borated molecules due to its high volumetric B content, prolonged retention in biological systems, and low toxicity. These attributes lead to a substantial accumulation of B in tissues, eliminating the need for isotopically enriched compounds. In our approach, B₄C nanoparticles were included in composite nanostructures with ultrasmall superparamagnetic nanoparticles (SPIONs), coated with poly (acrylic acid), and further functionalized with the fluorophore DiI. The successful internalization of these nanoparticles in HeLa cells was confirmed, and a significant uptake of ¹⁰B was observed. Micro-distribution studies were conducted using intracellular neutron autoradiography, providing valuable insights into the spatial distribution of the nanoparticles within cells. These findings strongly indicate that the developed nanomaterials hold significant promise as effective carriers for ¹⁰B in BNCT, showcasing their potential for advancing cancer treatment methodologies. Full article

Chlorpyrifos (CP) is a globally used pesticide with acute toxicity. This work studied the photocatalytic degradation of CP using TiO₂, ZnO nanoparticles, and nanocomposites of TiO₂ and ZnO supported on SPIONs (SPION@SiO₂@TiO₂ and SPION@SiO₂@ZnO). The nanocomposites were synthesized by multi-step incipient wetness impregnation. The effects of the initial pH, catalyst type, and dose were evaluated. The nanocomposites of SPION@SiO₂@TiO₂ and SPION@SiO₂@ZnO showed higher CP photodegradation levels than free nanoparticles, reaching 95.6% and 82.3%, respectively, at pH 7. The findings indicate that iron oxide, as a support material for TiO₂ and ZnO, extended absorption edges and delayed the electron–hole recombination of the nanocomposites, improving their photocatalytic efficiency. At the same time, these nanocomposites, especially SPION@SiO₂@TiO₂, showed efficient degradation of 3,5,6-trichloropyridinol (TCP), one of the final metabolites of CP. The stability and reuse of this nanocomposite were also evaluated, with 74.6% efficiency found after six cycles. Therefore, this nanomaterial represents an eco-friendly, reusable, and effective alternative for the degradation of chlorpyrifos in wastewater treatment. Full article

Cancer is a disease that continues to greatly impact our society. Developing new and more personalized treatment options is crucial to decreasing the cancer burden. In this study, we combined magnetic polysaccharide microparticles with a Pluronic thermoresponsive hydrogel to develop a multifunctional, injectable drug delivery system (DDS) for magnetic hyperthermia applications. Gellan gum and alginate microparticles were loaded with superparamagnetic iron oxide nanoparticles (SPIONs) with and without coating. The magnetic microparticles’ registered temperature increases up to 4 °C upon the application of an alternating magnetic field. These magnetic microparticles were mixed with drug-loaded microparticles, and, subsequently, this mixture was embedded within a Pluronic thermoresponsive hydrogel that is capable of being in the gel state at 37 °C. The proposed DDS was capable of slowly releasing methylene blue, used as a model drug, for up to 9 days. The developed hydrogel/microparticle system had a smaller rate of drug release compared with microparticles alone. This system proved to be a potential thermoresponsive DDS suitable for magnetic hyperthermia applications, thus enabling a synergistic treatment for cancer. Full article

Superparamagnetic iron oxide nanoparticles (SPIONs) have emerged as cutting-edge materials, garnering increasing attention in recent years within the fields of chemical and biomedical engineering. This increasing interest is primarily attributed to the distinctive chemical and physical properties of SPIONs. Progress in nanotechnology and particle synthesis methodologies has facilitated the fabrication of SPIONs with precise control over parameters such as composition, size, shape, stability, and magnetic response. Notably, these functionalized materials exhibit a remarkable surface-area-to-volume ratio, biocompatibility, and, most importantly, they can be effectively manipulated using external magnetic fields. Due to these exceptional properties, SPIONs have found widespread utility in the medical field for targeted drug delivery and cell separation, as well as in the chemical engineering field, particularly in wastewater treatment. Magnetic separation techniques driven by magnetophoresis have proven to be highly efficient, encompassing both high-gradient magnetic separation (HGMS) and low-gradient magnetic separation (LGMS). This review aims to provide an in-depth exploration of magnetic field gradient separation techniques, alongside a comprehensive discussion of the applications of SPIONs in the context of drug delivery, cell separation, and environmental remediation. Full article

Superparamagnetic iron oxide nanoparticles (SPIONs) have gathered tremendous scientific interest, especially in the biomedical field, for multiple applications, including bioseparation, drug delivery, etc. Nevertheless, their manipulation and separation with magnetic fields are challenging due to their small size. We recently reported the coupling of cooperative magnetophoresis and sedimentation using quadrupole magnets as a promising strategy to successfully promote SPION recovery from media. However, previous studies involved SPIONs dispersed in organic solvents (non-biocompatible) at high concentrations, which is detrimental to the process economy. In this work, we investigate, for the first time, the magnetic separation of 20 nm and 30 nm SPIONs dispersed in an aqueous medium at relatively low concentrations (as low as 0.5 g·L⁻¹) using our custom, permanent magnet-based quadrupole magnetic sorter (QMS). By monitoring the SPION concentrations along the vessel within the QMS, we estimated the influence of several variables in the separation and analyzed the kinetics of the process. The results obtained can be used to shed light on the dynamics and interplay of variables that govern the fast separation of SPIONs using inexpensive permanent magnets. Full article

The need for stable and well-defined magnetic nanoparticles is constantly increasing in biomedical applications; however, their preparation remains challenging. We used two different solvothermal methods (12 h reflux and a 4 min microwave, MW) to synthesize amine-functionalized zinc ferrite (ZnFe₂O₄-NH₂) superparamagnetic nanoparticles. The morphological features of the two ferrite samples were the same, but the average particle size was slightly larger in the case of MW activation: 47 ± 14 nm (Refl.) vs. 63 ± 20 nm (MW). Phase identification measurements confirmed the exclusive presence of zinc ferrite with virtually the same magnetic properties. The Refl. samples had a zeta potential of −23.8 ± 4.4 mV, in contrast to the +7.6 ± 6.8 mV measured for the MW sample. To overcome stability problems in the colloidal phase, the ferrite nanoparticles were embedded in polyvinylpyrrolidone and could be easily redispersed in water. Two PVP-coated zinc ferrite samples were administered (1 mg/mL ZnFe₂O₄) in X BalbC mice and were compared as contrast agents in magnetic resonance imaging (MRI). After determining the r1/r2 ratio, the samples were compared to other commercially available contrast agents. Consistent with other SPION nanoparticles, our sample exhibits a concentrated presence in the hepatic region of the animals, with comparable biodistribution and pharmacokinetics suspected. Moreover, a small dose of 1.3 mg/body weight kg was found to be sufficient for effective imaging. It should also be noted that no toxic side effects were observed, making ZnFe₂O₄-NH₂ advantageous for pharmaceutical formulations. Full article

Adsorption is a popular technique and has been investigated with many different materials for removing synthetic dyes from textile wastewater. This study compares the methylene blue (MB) adsorption capabilities of surface-modified superparamagnetic iron oxide nanoparticles, (SPION) using polyvinyl alcohol (PVA) and chitosan (CS), combined with two carbon materials, activated carbon (AC) and graphite (GR), respectively. After 9 days, depending on the initial MB loading concentration (0.015 mg/mL, 0.02 mg/mL, and 0.025 mg/mL), the MB adsorption capacities onto SPION/PVA/CS/AC and SPION/PVA/CS/GR were 7.6 ± 0.2–22.4 ± 0.05 and 6.9 ± 0.02–22.4 ± 0.05 mg/g, respectively. The cumulative release percentages of SPION/PVA/CS/AC and SPION/PVA/CS/GR after 30 days were 63.24 ± 8.77%–22.10 ± 2.59% and 91.29 ± 12.35%–24.42 ± 1.40%, respectively. Additionally, both SPION/PVA/CS/AC and SPION/PVA/CS/GR can both fit the Freundlich isotherm model. The adsorption and desorption kinetics can be fitted to the pseudo-second-order linear and zeroth-order models, respectively. At 0.020 mg/mL MB initial loading, out of SPION/PVA/CS/AC, SPION/PVA/CS/GR, and SPION/PVA/CS/GO, SPION/PVA/CS/AC is the most economical adsorbent. Compared to SPION/PVA/AC, SPION/PVA/CS/AC is less economical. Since CS has antimicrobial properties, antimicrobial activities should be investigated to conclude which adsorbent is more promising: SPION/PVA/AC or SPION/PVA/CS/AC. Full article

The potential of standard methods of radiation therapy is limited by the dose that can be safely delivered to the tumor, which could be too low for radical treatment. The dose efficiency can be increased by using radiosensitizers. In this study, we evaluated the sensitizing potential of biocompatible iron oxide nanoparticles coated with a dextran shell in A172 and Gl-Tr glioblastoma cells in vitro. The cells preincubated with nanoparticles for 24 h were exposed to ionizing radiation (X-ray, gamma, or proton) at doses of 0.5–6 Gy, and their viability was assessed by the Resazurin assay and by staining of the surviving cells with crystal violet. A statistically significant effect of radiosensitization by nanoparticles was observed in both cell lines when cells were exposed to 35 keV X-rays. A weak radiosensitizing effect was found only in the Gl-Tr line for the 1.2 MeV gamma irradiation and there was no radiosensitizing effect in both lines for the 200 MeV proton irradiation at the Bragg peak. A slight (ca. 10%) increase in the formation of additional reactive oxygen species after X-ray irradiation was found when nanoparticles were present. These results suggest that the nanoparticles absorbed by glioma cells can produce a significant radiosensitizing effect, probably due to the action of secondary electrons generated by the magnetite core, whereas the dextran shell of the nanoparticles used in these experiments appears to be rather stable under radiation exposure. Full article

Superparamagnetic iron oxide nanoparticles (SPIONs) have garnered significant attention in the medical sector due to their exceptional superparamagnetic properties and reliable tracking capabilities. In this study, we investigated the immunotoxicity of SPIONs with a modified surface to enhance hydrophilicity and prevent aggregate formation. The synthesized SPIONs exhibited a remarkably small size (~4 nm) and underwent surface modification using a novel “haircut” reaction strategy. Experiments were conducted in vitro using a human monocytic cell line (THP-1). SPIONs induced dose-dependent toxicity to THP-1 cells, potentially by generating ROS and initiating the apoptotic pathway in the cells. Concentrations up to 10 μg/mL did not affect the expression of Nrf2, HO-1, NF-κB, or TLR-4 proteins. The results of the present study demonstrated that highly hydrophilic SPIONs were highly toxic to immune cells; however, they did not activate pathways of inflammation and immune response. Further investigation into the mechanisms of cytotoxicity is warranted to develop a synthetic approach for producing effective, highly hydrophilic SPIONs with little to no side effects. Full article

Methylene blue (MB) is one of the toxic synthetic dyes that are being discharged heavily into water supplies. Hence, MB removal is one of the most important tasks for a cleaner water supply. By using inexpensive, abundant, and easy-to-synthesize materials, superparamagnetic iron oxide nanoparticles, which were synthesized using the co-precipitation method with polyvinyl alcohol and graphite (SPION/PVA/GR), can be used to adsorb MB. The adsorbent was characterized using FE-SEM, FTIR, XRD, VSM, and BJH. The entrapment efficiency of MB on SPION/PVA/GR after 12 days was 33.96 ± 0.37–42.55 ± 0.39%, at 333.15, 310.15, and 298.15 K, and the initial concentration of MB was 0.017–0.020 mg/mL. The adsorption process can be considered spontaneous, endothermic, chemisorption, heterogeneous, or multilayer adsorption. When releasing MB at 298.15 K and a pH of 3.85 after 7 days, the release percentage ranged from 11.56 ± 0.33 to 22.93 ± 5.06 depending on the initial loading conditions and mainly the releasing temperature following the Higuchi kinetic model. Since this is a novel SPION-based MB adsorbent, optimization, and different forms of adsorbent (i.e., thin film composite) should be further researched. Full article